CN101293753A - Resin sand special for probe core body and high-performance structure sublance composite probe made thereof - Google Patents
Resin sand special for probe core body and high-performance structure sublance composite probe made thereof Download PDFInfo
- Publication number
- CN101293753A CN101293753A CNA2008100993589A CN200810099358A CN101293753A CN 101293753 A CN101293753 A CN 101293753A CN A2008100993589 A CNA2008100993589 A CN A2008100993589A CN 200810099358 A CN200810099358 A CN 200810099358A CN 101293753 A CN101293753 A CN 101293753A
- Authority
- CN
- China
- Prior art keywords
- probe
- core body
- sand
- probe core
- sampling box
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to resin sand specially used for probe cores and a high-efficient structural sublance dual probe made of the resin sand. The resin sand specially used for the probe cores improves the whole temperature tolerance property and the intensity of the resin sand by adding a proper amount of high-temperature sand in the quartz sand with low heat resistance. The probe core made of the resin sand can be used in the high-temperature and high-pressure working condition of a converter and also has appropriate brittleness; therefore, when a probe falls into a platform bucket which is lower than 20 meters, a coupon can be crashed automatically and the coupon can be sent to carry out a spectroscopic analysis directly without needing workers to beat by a hammer, thereby relieving the labor intensity of the workers, shortening detection time and increasing steel-making speed. The high-efficient structural sublance dual probe directly moulds a die cavity to form a sample box containing cavity, a fixed carbon chamber and a molten steel flow passage in the probe cores made of the resin sand. The fixed carbon chamber has no metal pieces and the resin sand has good adiathermancy, thereby slowing down the freezing rate of iron and steel solution in the fixed carbon chamber and increasing the precision of the fixed carbon. According to the actual analysis and comparison, the precision of the fixed carbon can be steadily improved to be above the standard grade; simultaneously, the sublance dual probe saves a plurality of spare parts, which leads the whole manufacturing cost to be reduced by more than 30 percent.
Description
Technical field
The present invention relates to a kind of resin sand special for probe core body and with the high-performance structure sublance composite probe of its making.
Background technology
In the smelting process of iron and steel, for guaranteeing quality product, the preceding need of coming out of the stove carry out sampling, thermometric repeatedly to the iron and steel liquation and decide oxygen and decide carbon, this work is to take a sample by temperature, oxygen level and the carbon content of iron and steel liquation in the collection of the sublance composite probe in the converter stove and to the iron and steel liquation, show to reach by secondary instrument again the sample piece is carried out spectroscopic analysis, obtain the various constituent datas of iron and steel.Particularly detect very key at the carbon of deciding for the last time that faces before coming out of the stove, the speed of should seeking quickness, refinement is true again.Over nearly 30 years, the Iron And Steel Industry fast development, production technology is upgraded and is accelerated, and equipment enlarging, industrial automatization improve, and adopt the component content and the temperature of the multi-functional probe on-line quick detection of sublance steel in the smelting steel process, to enhance productivity.The domestic beginning after Baosteel goes into operation used, and becomes the strong technical support that improves STEELMAKING PRODUCTION efficient but just begin large scale application after constantly having mammoth conveter to put into production the beginning of this century.The flow process of modern steel production is: the working continuously of converter smelting---external refining---continuous casting ejection, the most basic feature is the strict coupling synchronously of the time of operation, at first require the converter timing, decide composition, fixed temperature for steel, require the strict control of converter smelting cycle, the sample of the terminal point (before the tapping) that is taken out by auxiliary lance probe must be sent to the laboratory fast, obtains result of laboratory test fast.
At present, steelmaking process has been realized automatization control, do not fall stove, do not carry out auxiliary lance probe probe temperature, carbon content, oxygen level and sampling etc. under the situation of blow off, after auxiliary lance probe detects success automatically, the useless probe of the automatic exhausted of the mechanical manipulator of furnace roof transfers to the waste material bucket, directly fall to the platform bucket below more than 20 meters, the workman takes out the back and breaks the pottery head into pieces with hammer, take out the sample piece, blow to the spectrum chamber through airduct and to analyze, only require to conform to various chemical element contents on being presented at screen and just can come out of the stove in its result.Existing multi-functional sublance composite probe has multiple, as TCS (be thermometric, decide carbon and sampling) type, TSO (be thermometric, sampling and decide oxygen) type, TCSO (be thermometric, decide carbon, sampling and decide oxygen) type or the like.(be thermometric wherein with TCSO; decide carbon; sampling and decide oxygen) the multi-functional sublance composite probe function of type is the most complete; structure is the most complicated; its essential structure generally includes probe pipe shaft part and pottery head; temperature sensor; decide oxygen element (tubular zirconium-oxide) and high temperature resistant protective tube thereof; sampling box; silica tube and tin hat; sampling box is provided with the cavity avris by two centres and has the irony disk that level lets slip a remark and involute; intermediate formation standard shape chamber; the level synthetic fluid inlet of leting slip a remark; silica tube is inserted in the fluid inlet; the head of making pottery is made by refractory materials; injection moulding; burn till through high temperature; the common front end of shape becomes the frustum of a cone; and the other end is provided with boss formation rank shoulder; boss diameter and outer paper tube internal orifice dimension running fit; the raised head face center is provided with a sampling box location die cavity; die cavity center, location is provided with the sampling jack that connects vertically to a front end of making pottery; the both sides of a pottery front end sampling jack are provided with the installation jack of temperature sensor and tubular zirconium-oxide and high temperature resistant protective tube thereof; high temperature resistant protective tube is set in outside the tubular zirconium-oxide; described sampling box is arranged in the die cavity of location; the sampling box fluid inlet is inserted in the sampling jack; be inserted with silica tube in the liquid-inlet pipe; the silica tube front end is exposed at outside the front end face of making pottery; the outer sheathed ferule of silica tube; it is outer simultaneously as the outer electrode temperature sensor that the ferule front end is exposed at the probe core body front end face; tubular zirconium-oxide and high temperature resistant protective tube thereof fixedly are plugged in respectively in separately the installation jack; the tubular zirconium-oxide front end passes from high temperature resistant protective tube and exposes; temperature sensor; the pin of tubular zirconium-oxide and outer electrode thereof is connected with signal lead and causes in the outer paper tube; outside a front end face of making pottery, place and be provided with tubular zirconium-oxide; high temperature resistant protective tube; temperature sensor and the sampling box fluid inlet annular recess that matches with protection marginal ridge mouth in being looped around, protection marginal ridge mouth are embedded in annular recess temperature sensor and tubular zirconium-oxide and liquid-inlet pipe are covered on wherein.The probe pipe shaft partly comprises middle paper tube, outer paper tube and the docking apparatus that flexibly connects with the sublance plug, in middle paper tube, also be provided with and decide the carbon assembly, that decides that the carbon assembly comprises irony cylindricly decides carbon iron cup and front and back plug and decides the carbon thermopair, decides the carbon thermopair and is arranged on and decides carbon cup center.
Existing multi-functional sublance composite probe has also exposed some defectives in the process of using: 1, because the head of making pottery is to be made by firm refractory materials, the workman is very difficult when breaking pottery head taking-up sample piece into pieces with hammer, therefore the piece demoulding of taking a sample is time-consuming, usually want 3-4 consuming time minute, also just only need thirties minutes altogether and smelt one heat steel, therefore reach the earth and restricted steel-making efficient, hindered the raising of output.2, since decide in the carbon assembly decide the carbon cup and the front and back plug is a ferrous material, quickened to decide the iron and steel liquation crystallization speed in the carbon cup, causing deciding the carbon degree reduces, existing multi-functional sublance composite probe does not generally reach standard level promptly ± 0.05% for its accuracy of detection of steel of carbon containing 20%-50%, and generally can not reach standard level promptly ± 0.02% for its accuracy of detection of steel of carbon containing 20%.3, part is many, complex structure, and the assembling difficulty causes multi-functional sublance composite probe production and material cost very high.4, it is not high always to survey into rate, about 90%.The problems referred to above are perplexing the scientific worker of this area for a long time, can't solve well always.
Summary of the invention
The objective of the invention is to provides a kind of resin sand special for probe core body of high-performance structure sublance composite probe for overcoming the deficiencies in the prior art, the probe core body made from this resin sand can adapt to furnace high-temperature highly compressed working conditions, and the useless probe of exhausted transfers to the waste material bucket when the mechanical manipulator of furnace roof is incited somebody to action, and when weighing down to the platform bucket below more than 20 meters, probe core body can be pulverized voluntarily, and the sampling piece need not the workman and strikes with a hammer.
The objective of the invention is to reach by the following technical programs: 1, a kind of resin sand special for probe core body, comprise quartz sand and Resin adhesive, it is characterized in that: described resin sand comprises that also heatproof is at the high temperature resistant sand more than 1700 ℃, wherein the granularity of quartz sand is 70 orders-140 orders, weight percent content is 50-54, the granularity of high temperature resistant sand is 140 orders-200 orders, and weight percent content is 44-48, and the weight percent content of Resin adhesive is 2.0-2.6.Its compound method comprises following step:
A, join sand---with quartz sand and high temperature resistant husky the mixing, stir then, when stirring, temperature is heated to 180 ℃-200 ℃, continue to be stirred to the no temperature difference;
B, add glue---add Resin adhesive in the sand after stir, and stir;
C, going out sand---the resin sand for preparing is spread out, and the blowing cooling is cooled to room temperature;
D, screening---screen cooled resin sand with 60 purpose sieves, remove the coarse grain of granularity more than 60 orders.
This resin sand is by having added an amount of high temperature resistant sand in the lower quartz sand of heatproof, improved the whole heat resistance of resin sand, and because the granularity of high temperature resistant sand is enough thin, fully filled the gap between the quartz sand particle, be issued to enough intensity in Resin adhesive bonding, the probe core body of making can adapt to furnace high-temperature highly compressed working conditions, but because the interior temperature of stove is higher than the heatproof value of quartz sand, make quartz sand become fragile, therefore, the useless probe of exhausted transfers to the waste material bucket when the mechanical manipulator of furnace roof is incited somebody to action, and when weighing down to the platform bucket below more than 20 meters, the probe core body that resin sand is made will be pulverized voluntarily, and the sample piece need not the workman and strikes with a hammer just can directly send to again and carry out spectroscopic analysis, has alleviated working strength of workers to a great extent, shortened detection time widely, every stove can shorten more than 10% tap to tap time, has improved steel-making speed, has huge social benefit and economic benefit.
Another object of the present invention be for overcome the deficiencies in the prior art provide a kind of sample piece to need not that the workman strikes with a hammer and simple in structure, cost is low, decide carbon accuracy of detection height, high-performance structure sublance composite probe that the rate of always surveying into is high.
For achieving the above object; the invention provides a kind of high-performance structure sublance composite probe; comprise probe pipe shaft part and temperature sensor; tubular zirconium-oxide and high temperature resistant protective tube thereof; sampling box; silica tube and tin hat; the probe pipe shaft partly comprises middle paper tube; outer paper tube and the docking apparatus that flexibly connects with the sublance plug; described sampling box is provided with cavity by two centres; avris has the irony disk that level lets slip a remark and involutes; intermediate formation standard shape chamber; the level synthetic fluid inlet of leting slip a remark; silica tube is inserted in the fluid inlet; it is characterized in that: the probe core body front end becomes the frustum of a cone; the rear end is the cylinder shape boss; the boss diameter is takeed on than the little formation of frustum of a cone rank; described probe core body front end face upper edge be axially arranged with cross-sectional shape respectively with temperature sensor; decide two installation jacks that the oxygen element matches; temperature sensor; deciding the oxygen element fixedly is plugged in respectively in separately the installation jack; the cylinder shape boss inside of described probe core body forms molten steel runner and the sampling box cavity volume that is provided with vertically and decides the carbon chamber; the sampling box cavity volume is than deciding the more close front end in carbon chamber; described sampling box is arranged in the sampling box cavity volume; the sampling box liquid inlet port is towards the rear end; described molten steel runner and sampling box liquid inlet port reach decides carbon chamber rear end UNICOM; deciding the carbon thermopair is inserted into from front end and decides the carbon chamber; described boss is provided with inlet opening and described molten steel runner UNICOM; molten steel runner turning point is with arc transition; the boss diameter cooperates with outer paper tube internal orifice dimension and is inserted on the outer paper tube front end; during being arranged on, docking apparatus also places outer paper tube in the paper tube together; also be provided with wire casing on the described probe core body boss; described temperature sensor; the guide line of deciding the oxygen element and deciding the carbon thermopair is connected with docking apparatus through wire casing; probe core body integral body is made by resin sand; described resin sand hill is drawn together quartz sand; heatproof is at the high temperature resistant sand more than 1700 ℃; wherein the granularity of quartz sand is 70 orders-140 orders; weight percent content is 50-54; the granularity of high temperature resistant sand is 140 orders-200 orders; weight percent content is 44-48, and the weight percent content of Resin adhesive is 2.1-2.6.
Compared with prior art, because this high-performance structure sublance composite probe is directly to decide carbon chamber, sampling hut by mold the die cavity formation in the husky probe core body of making of resin, thermometric is decided oxygen and fluid inlet.That has save steel decides carbon cup, steel sampling cup and front and back plug and other numerous parts.And resin sand has heat insulating ability preferably, has slowed down the crystallization velocity of deciding iron and steel liquation in the carbon chamber, has improved the precision of deciding carbon, and contrast is analyzed on the border factually, and the precision of deciding carbon can be stablized and is increased to more than the standard level, and has improved the rate always surveyed into; What simultaneously this high-performance structure sublance composite probe had been save irony decides carbon cup and front and back plug and other numerous parts, and other dissimilar sonde configurations also have simplification in various degree, and maximum reaches 50%, and whole cost has been descended more than 30%.
For achieving the above object; the present invention also provides another kind of high-performance structure sublance composite probe; comprise probe pipe shaft part and temperature sensor; tubular zirconium-oxide and high temperature resistant protective tube thereof; sampling box; silica tube and tin hat; the probe pipe shaft partly comprises middle paper tube; outer paper tube and the docking apparatus that flexibly connects with the sublance plug; described sampling box is provided with cavity by two centres; avris has the irony disk that level lets slip a remark and involutes; intermediate formation standard shape chamber; the level synthetic fluid inlet of leting slip a remark; silica tube is inserted in the fluid inlet; it is characterized in that: described high-performance structure sublance composite probe is provided with probe core body; the probe core body front end becomes the frustum of a cone; the rear end is the cylinder shape boss; the boss diameter is takeed on than the little formation of frustum of a cone rank; described probe core body boss is provided with caulking groove or the die cavity that matches with sampling box; the thickness of caulking groove or die cavity cooperates with the thickness zero of sampling box box body; the bottom of caulking groove or die cavity is provided with and connects to the probe core body front end; the sampling jack of diameter and liquid-inlet pipe running fit; on the described probe core body front end face jack both sides be provided with vertically cross-sectional shape respectively with temperature sensor; decide two installation jacks that the oxygen element matches; the jack bottom is installed is provided with the fairlead that leads to the rear end; temperature sensor and decide the oxygen element and be plugged in respectively in separately the installation jack; temperature sensor passes with docking apparatus from fairlead respectively with the guide line of deciding the oxygen element and is connected; described sampling box is embedded in caulking groove or die cavity; the liquid-inlet pipe front end is from the sampling jack, and the silica tube in the liquid-inlet pipe passes from the sampling jack.
The invention will be further described below in conjunction with the accompanying drawings and the specific embodiments.
Description of drawings
Accompanying drawing 1 is sublance composite probe specific embodiment 1 structure sectional view of the present invention;
Accompanying drawing 2 is sublance composite probe specific embodiment 2 structure sectional views of the present invention;
Accompanying drawing 3,4 is a probe core body different angles schematic perspective view in the specific embodiment of the invention 2;
Accompanying drawing 5 is a probe core body structure sectional view in the specific embodiment of the invention 2;
Embodiment
Resin sand special for probe core body is by quartz sand, heatproof is formed at high temperature resistant sand more than 1700 ℃ and Resin adhesive, the weight percent content of Resin adhesive is 2.1-2.6, wherein the granularity of quartz sand can not be thick excessively, will be between 70 orders-140 order, crossing thick words can influence the compressive strength of probe core body, 70 orders preferably, the weight percent content of quartz sand is 50-54, the granularity of high temperature resistant sand is less than the granularity of quartz sand, fully be filled in the gap between the quartz sand particle, make probe core body reach enough intensity down in the bonding of Resin adhesive, be generally 140 orders-200 order, 140 orders preferably, the weight percent content of high temperature resistant sand is 44-48, and the content of high temperature resistant sand can not be too much, otherwise probe core body can too firmly can't be broken into pieces, high temperature resistant sand can be selected red corundum for use, black corundum or white fused alumina a kind of or their mixture, the heatproof of probe core body is relevant with proportioning between them.The method of preparation resin sand is characterized in that comprising following step:
A, join sand---with quartz sand and high temperature resistant husky the mixing, stir then, generally stirred 15-30 minute, when stirring, temperature is heated to 180 ℃-200 ℃, preferably 185 ℃;
B, add glue---add Resin adhesive in the sand after stir, and continue to stir;
C, going out sand---the resin sand for preparing is spread out as early as possible, prevent the husky bonding of resin, the blowing cooling is cooled to room temperature;
D, screening---screen cooled resin sand with 60 purpose sieves, remove the coarse grain of granularity more than 60 orders.
Specific embodiment 1:
With TCSO (is thermometric; decide carbon; sampling and decide oxygen) high-performance structure sublance composite probe of type is example; as shown in Figure 1; comprise probe pipe shaft part and probe core body 1 and temperature sensor 2; tubular zirconium-oxide 3 and high temperature resistant protective tube 4 thereof; sampling box 5 and tin hat 6 reach decides carbon thermopair 7; paper tube 8 during the probe pipe shaft partly comprises; outer paper tube 9 and the docking apparatus 10 that flexibly connects with the sublance plug; described sampling box 5 is provided with cavity by two centres; avris has the irony disk that level lets slip a remark and involutes; intermediate formation standard shape chamber; the level synthetic fluid inlet of leting slip a remark is inserted with silica tube 11 to prevent the molten steel adhesion in the liquid-inlet pipe.Probe core body 1 front end becomes the frustum of a cone; the rear end is the cylinder shape boss; the boss diameter is takeed on than the little formation of frustum of a cone rank; probe core body 1 front end face upper edge be axially arranged with cross-sectional shape respectively with temperature sensor 2; the temperature sensor that tubular zirconium-oxide 3 and high temperature resistant protective tube 4 thereof match is installed by jack 12 and tubular zirconium-oxide is installed jack 13; temperature sensor 2; tubular zirconium-oxide 3 and high temperature resistant protective tube 4 thereof fixedly are plugged in respectively in separately the installation jack; high temperature resistant protective tube 4 is enclosed within outside the tubular zirconium-oxide 3; tubular zirconium-oxide 3 front ends pass from high temperature resistant protective tube 4 and expose; the cylinder shape boss inside of probe core body 1 forms the sampling box cavity volume 14 of molten steel runner 16 and setting vertically and decides carbon chamber 15; sampling box cavity volume 14 is than deciding carbon chamber 15 more close front ends; sampling box cavity volume 14 shapes and sampling box 5 match; sampling box 5 is arranged in the sampling box cavity volume 14; sampling box 5 liquid inlet ports are towards the rear end; decide carbon chamber 15 for cylindrical; deciding carbon thermopair 7 is inserted into from front end and decides the carbon chamber 15; molten steel runner 16 is with sampling box 5 liquid inlet ports and decide carbon chamber 15 rear end UNICOMs; the boss cylinder is provided with inlet opening 17 and described molten steel runner 16 UNICOMs; molten steel runner 16 turning points with arc transition to reduce resistance to molten steel; the boss diameter preferably is inserted on outer paper tube 9 front ends with outer paper tube 9 internal orifice dimension transition fit; during being arranged on, docking apparatus 10 also places the rear side of outer paper tube 9 probe core bodies 1 in the paper tube 8 together; the boss of probe core body 1 preferably also is provided with the shoulder rank that match with middle paper tube 8 internal diameters; paper tube 8 is pegged graft with the boss shoulder rank of probe core body 1 in making; also be provided with wire casing 18 on the described probe core body 1 boss cylinder; temperature sensor 2; the guide line of deciding the oxygen element and deciding carbon thermopair 7 causes outside surface internally and is connected with docking apparatus 10 through wire casing 18; probe core body 1 integral body is made by aforementioned resin sand, and probe core body 1 is formed by two slit bamboo or chopped woods or the merging of three slit bamboo or chopped woods.
Specific embodiment 2:
With TSO (is thermometric; sampling and decide oxygen) high-performance structure sublance composite probe of type; as shown in Figure 2; comprise probe pipe shaft part and probe core body 1 and temperature sensor 2; tubular zirconium-oxide 3 and high temperature resistant protective tube 4 thereof; sampling box 5 and tin hat 6; paper tube 8 during the probe pipe shaft partly comprises; outer paper tube 9 and the docking apparatus 10 that flexibly connects with the sublance plug; described sampling box 5 is provided with cavity by two centres; avris has the irony disk that level lets slip a remark and involutes; intermediate formation standard shape chamber; the level synthetic fluid inlet of leting slip a remark preferably is inserted with silica tube 11 to prevent the molten steel adhesion in the liquid-inlet pipe.Shown in Fig. 3-5; described probe core body 1 front end becomes the frustum of a cone; the rear end is the cylinder shape boss; the boss diameter is takeed on than the little formation of frustum of a cone rank; described probe core body 1 boss is provided with caulking groove or the die cavity that matches with sampling box 5; the thickness of caulking groove or die cavity cooperates with the thickness zero of sampling box 5 box bodys; the bottom of caulking groove or die cavity is provided with and connects to probe core body 1 front end; the sampling jack 20 of diameter and liquid-inlet pipe running fit; on described probe core body 1 front end face jack both sides be provided with vertically cross-sectional shape respectively with temperature sensor 2; the temperature sensor that tubular zirconium-oxide 3 and high temperature resistant protective tube 4 thereof match is installed by jack 12 and tubular zirconium-oxide is installed jack 13; temperature sensor 2; tubular zirconium-oxide 3 and high temperature resistant protective tube 4 thereof fixedly are plugged in respectively in separately the installation jack; high temperature resistant protective tube 4 is enclosed within outside the tubular zirconium-oxide 3; tubular zirconium-oxide 3 front ends pass from high temperature resistant protective tube 4 and expose; temperature sensor 2 passes with docking apparatus 10 from fairlead respectively with the guide line of deciding the oxygen element and is connected; described sampling box 5 is embedded in caulking groove or die cavity; the liquid-inlet pipe front end is from the sampling jack; silica tube 11 in the liquid-inlet pipe passes from the sampling jack; silica tube 11 outer sheathed ferules, it is outer simultaneously as outer electrode that the ferule front end is exposed at the probe core body front end face.
The external form of above-mentioned probe core body 1 is not unique, can not have step yet, so long as can be fitted in front end mutually just passable with outer paper tube; In addition, the combined probe in the specific embodiment 1 is save and is decided carbon thermopair 7 and choked flow behind the molten steel runner 16 of deciding carbon chamber 15, also can constitute the high-performance structure sublance composite probe of TSO type.
Claims (7)
1, a kind of resin sand special for probe core body, comprise quartz sand and Resin adhesive, it is characterized in that: described resin sand comprises that also heatproof is at the high temperature resistant sand more than 1700 ℃, wherein the granularity of quartz sand is 70 orders-140 orders, weight percent content is 50-54, the granularity of high temperature resistant sand is 140 orders-200 orders, and weight percent content is 44-48, and the weight percent content of Resin adhesive is 2.1-2.6.
2, a kind of method of preparing the described resin sand special for probe core body of claim 1 is characterized in that comprising following step:
A, join sand---with quartz sand and high temperature resistant husky the mixing, stir then, when stirring, temperature is heated to 180 ℃-200 ℃, continue to be stirred to the no temperature difference;
B, add glue---add Resin adhesive in the sand after stir, and stir;
C, going out sand---the resin sand for preparing is spread out, and the blowing cooling is cooled to room temperature;
D, screening---screen cooled resin sand with 60 purpose sieves, remove the coarse grain of granularity more than 60 orders.
3; high-performance structure sublance composite probe; comprise probe pipe shaft part and temperature sensor; tubular zirconium-oxide and high temperature resistant protective tube thereof; sampling box; silica tube and tin hat; the probe pipe shaft partly comprises middle paper tube; outer paper tube and the docking apparatus that flexibly connects with the sublance plug; described sampling box is provided with cavity by two centres; avris has the irony disk that level lets slip a remark and involutes; intermediate formation standard shape chamber; the level synthetic fluid inlet of leting slip a remark; silica tube is inserted in the fluid inlet; it is characterized in that: described high-performance structure sublance composite probe is provided with probe core body; the probe core body front end becomes the frustum of a cone; the rear end is the cylinder shape boss; the boss diameter is takeed on than the little formation of frustum of a cone rank; described probe core body front end face upper edge be axially arranged with cross-sectional shape respectively with temperature sensor; decide two installation jacks that the oxygen element matches; temperature sensor; deciding the oxygen element fixedly is plugged in respectively in separately the installation jack; the cylinder shape boss inside of described probe core body forms molten steel runner and the sampling box cavity volume that is provided with vertically and decides the carbon chamber; the sampling box cavity volume is than deciding the more close front end in carbon chamber; described sampling box is arranged in the sampling box cavity volume; the sampling box liquid inlet port is towards the rear end; described molten steel runner and sampling box liquid inlet port reach decides carbon chamber rear end UNICOM; deciding the carbon thermopair is inserted into from front end and decides the carbon chamber; described boss is provided with inlet opening and described molten steel runner UNICOM; molten steel runner turning point is with arc transition; the boss diameter cooperates with outer paper tube internal orifice dimension and is inserted on the outer paper tube front end; during being arranged on, docking apparatus also places outer paper tube in the paper tube together; also be provided with wire casing on the described probe core body boss; described temperature sensor; the guide line of deciding the oxygen element and deciding the carbon thermopair is connected with docking apparatus through wire casing; probe core body integral body is made by resin sand special for probe core body; described resin sand special for probe core body comprises quartz sand; heatproof is at the high temperature resistant sand more than 1700 ℃; wherein the granularity of quartz sand is 70 orders-140 orders; weight percent content is 50-54; the granularity of high temperature resistant sand is 140 orders-200 orders; weight percent content is 44-48, and the weight percent content of Resin adhesive is 2.1-2.6.
4, high-performance structure sublance composite probe according to claim 3 is characterized in that: described probe core body is formed by two slit bamboo or chopped woods or the merging of three slit bamboo or chopped woods.
5, high-performance structure sublance composite probe according to claim 4 is characterized in that: also be inserted with silica tube in the liquid-inlet pipe.
6; a kind of high-performance structure sublance composite probe; comprise probe pipe shaft part and temperature sensor; tubular zirconium-oxide and high temperature resistant protective tube thereof; sampling box; silica tube and tin hat; the probe pipe shaft partly comprises middle paper tube; outer paper tube and the docking apparatus that flexibly connects with the sublance plug; described sampling box is provided with cavity by two centres; avris has the irony disk that level lets slip a remark and involutes; intermediate formation standard shape chamber; the level synthetic fluid inlet of leting slip a remark; it is characterized in that: described probe core body front end becomes the frustum of a cone; the rear end is the cylinder shape boss; the boss diameter is takeed on than the little formation of frustum of a cone rank; described probe core body boss is provided with caulking groove or the die cavity that matches with sampling box; the thickness of caulking groove or die cavity cooperates with the thickness zero of sampling box box body; the bottom of caulking groove or die cavity is provided with and connects to the probe core body front end; the sampling jack of diameter and liquid-inlet pipe running fit; on the described probe core body front end face jack both sides be provided with vertically cross-sectional shape respectively with temperature sensor; decide two installation jacks that the oxygen element matches; the jack bottom is installed is provided with the fairlead that leads to the rear end; temperature sensor and decide the oxygen element and be plugged in respectively in separately the installation jack; temperature sensor passes with docking apparatus from fairlead respectively with the guide line of deciding the oxygen element and is connected; described sampling box is embedded in caulking groove or die cavity, and the liquid-inlet pipe front end passes from the sampling jack.
7, high-performance structure sublance composite probe according to claim 6 is characterized in that: be inserted with silica tube in the liquid-inlet pipe, and the outer sheathed ferule of silica tube, it is outer simultaneously as outer electrode that the ferule front end is exposed at the probe core body front end face.