CN101280799A - Method for producing high strength nut - Google Patents
Method for producing high strength nut Download PDFInfo
- Publication number
- CN101280799A CN101280799A CNA2008100614597A CN200810061459A CN101280799A CN 101280799 A CN101280799 A CN 101280799A CN A2008100614597 A CNA2008100614597 A CN A2008100614597A CN 200810061459 A CN200810061459 A CN 200810061459A CN 101280799 A CN101280799 A CN 101280799A
- Authority
- CN
- China
- Prior art keywords
- high strength
- nut
- production method
- strength nut
- galvanizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Disclosed is a method for producing high intensity nuts. The producing method comprises steps as follows: (1) blanking and preprocessing; (2) cold heading and piercing; (3) quenching; (4) galvanizing; (5) tapping and obtaining the high intensity nuts. The invention provides a method that can enhance the intensity and quality of nuts for producing high intensity nuts.
Description
Technical field
The present invention relates to a kind of production method of the high strength nut of making by carbon steel.
Background technique
In high strength carbon steel nut production process, the Chang Yinwei technological problems causes the nut Material Strength to reduce, and sliding tooth takes place nut in use destroys.
Summary of the invention
For the deficiency that nut strength is lower, nut is second-rate of the production method that overcomes existing high strength nut, the invention provides a kind of production method that can strengthen nut strength, improve the high strength nut of nut quality.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of production method of high strength nut, described production method may further comprise the steps: (1), blanking and pretreatment; (2), cold-heading, punching; (3), quench; (4), galvanizing by dipping; (5), tapping, make high strength nut.
As preferred a kind of scheme: in described step (3), described heat treatment is 860~870 ℃ of quenchings, cools off in the CL-1 quenching medium.
As preferred another scheme: in described step (4), described galvanizing by dipping is the low temperature galvanizing by dipping, and its temperature range is 455~480 ℃.
Beneficial effect of the present invention mainly shows: compare with existing plain nut production technology, have the cost increase less, characteristics that nut strength is high.
Description of drawings
Fig. 1 is the flow chart of the production method of high strength nut.
Embodiment
Below in conjunction with accompanying drawing the present invention is further described.
With reference to Fig. 1, a kind of production method of high strength nut, described production method may further comprise the steps: (1), blanking and pretreatment; (2), cold-heading, punching; (3), quench; (4), galvanizing by dipping; (5), tapping, make high strength nut.
In described step (3), described heat treatment is 860~870 ℃ of quenchings, cools off in the CL-1 quenching medium.
In described step (4), described galvanizing by dipping is the low temperature galvanizing by dipping, and its temperature range is 455~480 ℃.
Compare with existing plain nut production technology, have the cost increase less, the nut strength height Advantage.
Claims (3)
1, a kind of production method of high strength nut is characterized in that: described production method may further comprise the steps: (1), blanking and pretreatment; (2), cold-heading, punching; (3), quench; (4), galvanizing by dipping; (5), tapping, make high strength nut.
2, the production method of a kind of high strength nut as claimed in claim 1 is characterized in that: in described step (3), described heat treatment is 860~870 ℃ of quenchings, cools off in the CL-1 quenching medium.
3, the production method of a kind of high strength nut as claimed in claim 1 or 2 is characterized in that: in described step (4), described galvanizing by dipping is the low temperature galvanizing by dipping, and its temperature range is 455~480 ℃.