CN101280123A - 一种中温型环保分散染料组合物 - Google Patents
一种中温型环保分散染料组合物 Download PDFInfo
- Publication number
- CN101280123A CN101280123A CNA200810061830XA CN200810061830A CN101280123A CN 101280123 A CN101280123 A CN 101280123A CN A200810061830X A CNA200810061830X A CN A200810061830XA CN 200810061830 A CN200810061830 A CN 200810061830A CN 101280123 A CN101280123 A CN 101280123A
- Authority
- CN
- China
- Prior art keywords
- formula
- dye
- dye monomer
- parts
- monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种中温型环保分散染料组合物，主要包括10～90份如式(1－1)所示的染料单体A和如式(1－2)所示的染料单体B的混合物，10～50份如式(2)所示的染料单体C。本发明分散染料组合物配伍性极好，且在染色时pH值的适应范围比较宽广、提升力高、得色量高、匀染性好、各项牢度均好，是一只综合性能优越的中温型环保分散染料组合物。
Description
技术领域
本发明涉及一种中温型分散染料组合物，特别是适用于涤纶及混纺织物染色和印花。
背景技术
现有的分散染料品种繁多，型号各异，有高温型、中温型、低温型。每只型号的性能各异，若一种组合物同时含有两种或两种以上的型号，其配伍性肯定不好，在印染操作中会带来一定的难度，而且印染出来的产品的牢度有一定的影响。
发明内容
本发明提供了一种配伍性能极佳的中温型环保分散染料。此组合物是由中温型染料复配而成，各项牢度指标均优异，且非常经济实用。
一种中温型环保分散染料组合物，以重量份计，包括：
10～90份如式(1-1)所示的染料单体A和如式(1-2)所示的染料单体B的混合物：
10～50份如式(2)所示的染料单体C：
一种优化的中温型环保分散染料组合物，包括：10～80份如式(1-1)所示的染料单体A和如式(1-2)所示的染料单体B的混合物，10～50份如式(3-3)所示的染料单体C，2～40份一种或多种如式(3-1)、(3-2)、(3-3)、(3-4)、(3-5)、(3-6)所示的染料单体D：
染料单体D可增加产品牢度性能，提高染料在染色时的增深性能。
一种更优化的中温型环保分散染料组合物，包括：10～80份如式(1-1)所示的染料单体A和如式(1-2)所示的染料单体B的混合物，10～50份如式(2)所示的染料单体C，2～35份一种或多种如式(3-1)、(3-2)、(3-3)、(3-4)、(3-5)、(3-6)所示的染料单体D，2～10份如式(4)所示的染料单体E：
染料单体E有助于调节色光，增加牢度。
染料单体A和染料单体B在生产时为混合物状态。
本发明的分散染料组合物，应用时一般需要加入助剂。所述的助剂为分散染料复配时常用的分散剂、扩散剂及其表面活性剂等，优选包括下列之一或其混合物：萘磺酸甲醛缩合物、木质素磺酸盐、烷基萘磺酸甲醛缩合物。如甲基萘磺酸甲醛缩合物(分散剂MF)、萘磺酸甲醛缩合物(扩散剂NNO)、苄基萘磺酸甲醛缩合物(扩散剂CNF)、木质素磺酸钠(木质素85A、83A)等。通常，助剂与原染料重量之比为0.8～5∶1。
本发明所述的分散染料组合物可用以下方法制备：将染料单体的原染料按比例混合后，在助剂、水或其它表面活性剂存在下用砂磨机或研磨机等粉碎机进行微粒子化，然后喷雾干燥。上述染料单体均可采用市售产品。
本发明所述的分散染料组合物，微粒子化后可为液状，喷雾干燥后可为粉状、颗粒状。此染料复合物的配伍性极好，且在染色时pH值的适应范围比较宽广、提升力高、得色量高、匀染性好、各项牢度均好，是一只综合性能优越的中温型环保分散染料组合物。
具体实施方式
下面结合实施例对本发明作进一步说明，但本发明的保护范围并不限于此。
实施例1～18
根据表1所示数据，将染料单体A、染料单体B、染料单体C、染料单体D、染料单体E与甲基萘磺酸甲醛缩合物(分散剂MF)、萘磺酸甲醛缩合物(扩散剂NNO)、木质素磺酸钠(木质素85A、83A)加水拼混后，用砂磨进行研磨分散，然后进行喷雾干燥。
其中染料单体A和染料单体B可选用浙江闰土股份有限公司生产的C.I.DISP BLUE291：3#，染料单体C可选用浙江闰土股份有限公司生产的分散橙288#，染料单体D可选用浙江闰土股份有限公司生产的C.I.DISPBLUE 291#，分散蓝291：5#，分散蓝291：4#，染料单体E可选用浙江闰土股份有限公司生产的C.I.DISP YELLOW 119#。
表1
| 7 | (1-1)(1-2) | 1213 | (2) | 41 | (3-1)(3-3)(3-5) | 41515 | ---- | 0 | 85A | 150 |
| 8 | (1-1)(1-2) | 2726 | (2) | 17 | (3-2) | 30 | ---- | 0 | 83A | 200 |
| 9 | (1-1)(1-2) | 1822 | (2) | 25 | (3-3) | 25 | (3) | 10 | 分散剂MF | 200 |
| 10 | (1-1)(1-2) | 3040 | (2) | 25 | (3-1)(3-6) | 14 | ---- | 0 | 扩散剂NNO | 200 |
| 11 | (1-1)(1-2) | 5030 | (2) | 18 | (3-4) | 2 | ---- | 0 | 分散剂MF | 200 |
| 12 | (1-1)(1-2) | 258 | (2) | 25 | (3-3)(3-5) | 78 | ---- | 0 | 扩散剂NNO | 200 |
| 13 | (1-1)(1-2) | 355 | (2) | 30 | (3-5)(3-6) | 1015 | (3) | 5 | 85A | 150 |
| 14 | (1-1)(1-2) | 55 | (2) | 47 | (3-1)(3-3) | 1520 | (3) | 8 | 分散剂MF | 200 |
| 15 | (1-1)(1-2) | 238 | (2) | 42 | (3-3)(3-6) | 99 | (3) | ---- | 83A | 170 |
| 16 | (1-1)(1-2) | 1718 | (2) | 50 | (3-5) | 12 | (3) | 3 | 扩散剂NNO | 200 |
| 17 | (1-1)(1-2) | 2040 | (2) | 30 | (3-2)(3-5) | 12 | (3) | 7 | 83A | 150 |
| 18 | (1-1)(1-2) | 1535 | (2) | 40 | (3-1)(3-2)(3-3)(3-4)(3-5)(3-6) | 221122 | ---- | 0 | 85A | 150 |
将上述实施例制得的分散染料、助剂、水混合后制得的染料复合物进行性能测试，测试方法如下：
各取0.5克实施例1～18制得的分散染料，用水分别配制成浓度为0.5g/500ml的分散染料悬浮液，取20ml与80ml的水混合，用醋酸调节染浴pH到5，然后升温到60℃，同时分别放入2g聚酯纤维进行高温高压染色，在35分钟内升温到130℃，保温30分钟，冷却到80℃时取样。
观察布样色光并采用GB/T3921-1997、GB/T3920-1997、GB/T5718-1997测定其染色牢度。测定结果见表2。
表2 单位：级
| 实施例名称 | 提升力 | 水洗牢度 | 摩擦牢度 | 升华牢度(180℃) |
| 实施例1 | A | 4-5 | 4-5 | 4-5 |
| 实施例2 | A | 4 | 4 | 4-5 |
| 实施例3 | A | 4 | 4-5 | 4-5 |
| 实施例4 | A | 4 | 4 | 4-5 |
| 实施例5 | A | 4-5 | 4-5 | 4-5 |
| 实施例6 | A | 4-5 | 4-5 | 4-5 |
| 实施例7 | A | 4-5 | 4-5 | 4-5 |
| 实施例8 | A | 4-5 | 4-5 | 4-5 |
| 实施例9 | A | 4-5 | 4-5 | 4-5 |
| 实施例10 | A | 4-5 | 4-5 | 4-5 |
| 实施例11 | A | 4-5 | 4-5 | 4-5 |
| 实施例12 | A | 4-5 | 4-5 | 4-5 |
| 实施例13 | A | 4-5 | 4-5 | 4-5 |
| 实施例14 | A | 4-5 | 4-5 | 4-5 |
| 实施例15 | A | 4-5 | 4-5 | 4-5 |
| 实施例16 | A | 4-5 | 4-5 | 4-5 |
| 实施例17 | A | 4-5 | 4-5 | 4-5 |
| 实施例18 | A | 4-5 | 4-5 | 4-5 |
Claims (3)
1、一种中温型环保分散染料组合物，以重量份计，包括：
10～90份如式(1-1)所示的染料单体A和如式(1-2)所示的染料单体B的混合物：
10～50份如式(2)所示的染料单体C：
2、如权利要求1所述的中温型环保分散染料组合物，其特征在于：包括：10～80份如式(1-1)所示的染料单体A和如式(1-2)所示的染料单体B的混合物，10～50份如式(2)所示的染料单体C，2～40份一种或多种如式(3-1)、(3-2)、(3-3)、(3-4)、(3-5)、(3-6)所示的染料单体D：
3、如权利要求2所述的中温型环保分散染料组合物，其特征在于：包括：10～80份如式(1-1)所示的染料单体A和如式(1-2)所示的染料单体B的混合物，10～50份如式(2)所示的染料单体C，2～35份一种或多种如式(3-1)、(3-2)、(3-3)、(3-4)、(3-5)、(3-6)所示的染料单体D，2～10份如式(4)所示的染料单体E：