CN101250658A - 铜镍铁合金 - Google Patents

铜镍铁合金 Download PDF

Info

Publication number
CN101250658A
CN101250658A CNA2008100201823A CN200810020182A CN101250658A CN 101250658 A CN101250658 A CN 101250658A CN A2008100201823 A CNA2008100201823 A CN A2008100201823A CN 200810020182 A CN200810020182 A CN 200810020182A CN 101250658 A CN101250658 A CN 101250658A
Authority
CN
China
Prior art keywords
nickel
copper
steel
iron
alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100201823A
Other languages
English (en)
Inventor
陈平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGZHOU WUFAN ALLOY Co Ltd
Original Assignee
CHANGZHOU WUFAN ALLOY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGZHOU WUFAN ALLOY Co Ltd filed Critical CHANGZHOU WUFAN ALLOY Co Ltd
Priority to CNA2008100201823A priority Critical patent/CN101250658A/zh
Publication of CN101250658A publication Critical patent/CN101250658A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种采用二次资源含铜、含镍废料重熔制备的铜镍铁合金,其各组份的重量百分含量是:铜45~60%;镍15~25%;不可避免的杂质总量≤2.0%;铁为余量,且通过急冷浇铸等措施而制得成品。具有熔点低,在钢水中扩散性能好,制取成本低,和炉前合金化处理操作简便等特点。是一种冶炼耐热钢、耐候钢和其它合金钢的合金添加剂。

Description

铜镍铁合金
技术领域
本发明涉及一种铜镍铁合金,具体涉及一种采用二次资源含铜含镍废料重熔制取的铜镍铁合金。属于合金技术。
背景技术
铜、镍是冶炼耐热钢、耐侯钢和其它合金钢的炉前合金处理的添加剂。传统的炉前合金化处理技术,是将切割成块的电解铜和电解镍,通过高位仓自流加入钢水中的。无疑,这种已有技术的处理成本高,炉前装备复杂,操作比较麻烦,尤其是由于镍的熔点高,在待处理钢水中的扩散性差,如果处理时搅拌不均匀,就会严重影响镍在合金钢中的均匀固溶性,而直接影响合金钢的质量。
中国专利授权公告号CN1221679C和CN1224727C以及公开号CN1908212A,分别公开了“易碎的镍铜铁合金”,“镍铜硅铁合金”和“铜镍硅铁合金”,虽然都能在一定程度上,克服传统技术用电解铜、电解镍作钢水合金化处理所存在的众多技术不足。但终究由于其为了易于破碎,而都含有4~15%的硅,给合金钢质量造成严重的不利影响。
业内人士都知道,虽然硅具有优于锰而低于铝的脱氧效果,但其成渣粘度高,不易从钢水内部上浮而被去掉。而何况在钢水进入合金化处理工序前,已经作了有效的脱氧、除杂处理。也就是说,待合金化处理的钢水,一般都是洁净钢水,因此不必再用硅来脱氧。且除了冶炼含硅钢种外,其它钢种都不希望有硅元素存在,尤其是轿车薄钢板,更是如此。
发明内容
本发明旨在提供一种不含硅的铜镍铁合金,以克服已有技术的诸多不足。
本发明的技术方案是:
一种铜镍铁合金,含有铜、镍、铁,以及不可避免的杂质,其创新点在于,各组份的重量百分含量是:
铜:45~60%
镍:15~25%
不可避免的杂质总量:≤2.0%
铁:余量
这里应当说明的是,所给出的铜镍铁合金,所存在的不易破碎的问题,可以通过所述合金浇铸时,采取急冷等措施,予以有效解决。
本发明优选的各组份的重量百分含量是:
铜:50~60%
镍:20~25%
不可避免的杂质总量:≤1.0%
铁:余量。
本发明在其制备过程中,不可避免地存在碳、磷、硫等杂质。而所述杂质总量通过处理,严格控制其重量百分含量为≤2%
本发明十分重视有害杂质磷、硫的低含量处理,而主张其硫的重量百分含量≤0.05%,磷的重量百分含量≤0.10%。
上述技术方案得以实施后,本发明具有熔点低,在钢水中扩散性能好,制取成本低和炉前合金化处理操作简便等特点,是显而易见的。与已技术相比,具有突出的实质性特点和显著进步。
具体实施方式
以0.5t中频电炉且每批总投料量为500kg为例。
1、本发明的制取先按以下重量配料备用:
含镍95%以上的废镍材料(如镍网)         132kg;
含铜95.5%以上的废紫铜材(如废铜线)     315kg;
废钢(低碳钢)                           53kg;
2、本发明的制取工艺过程按如下步骤进行:
(1)加入废钢升温熔化;
(2)加入废镍并使其尽快熔化;
(3)分批加入废紫铜材,待其全部熔化后搅拌除渣;
(4)出炉铸块。粒径为8~100mm。
按上述配料且经由上述工艺过程所制取的镍铜铁合金,经化验它的各组份重量百分含量是:
镍:24.5%
铜:59.2%
碳磷硫不可避免的杂质的总量为0.195%;
铁:余量。
通过调整配料,可获得铜和镍在其所述重量百分含量范围内不同铜、镍含量的本发明。
本发明不排除采用电解铜、电解镍和废钢重熔制备铜镍铁合金。
试验例:其初样经钢厂试用表明,采用钢水包人工直接加入法,操作简捷方便;铜和镍的收得率均在98.5%以上。

Claims (3)

1. 一种铜镍铁合金,含有铜、镍、铁,以及不可避免的杂质,其特征在于,
各组份的重量百分含量是:
铜:45~60%
镍:15~25%
不可避免的杂质总量:≤2.0%
铁:余量
2. 根据权利要求1所述的铜镍铁合金,其特征在于,各组份的重量百分含量是:
铜:50~60%
镍:20~25%
不可避免的杂质总量:≤1.0%
铁:余量
3. 根据权利要求2所述的铜镍铁合金,其特征在于,杂质硫≤0.05%,磷≤0.10%。
CNA2008100201823A 2008-03-28 2008-03-28 铜镍铁合金 Pending CN101250658A (zh)