CN101239483A - Source-saving type moisture-proof working board, 9mm thicknesses board, cabinet board, door board, tabletop board, floor, ceiling board and square board - Google Patents
Source-saving type moisture-proof working board, 9mm thicknesses board, cabinet board, door board, tabletop board, floor, ceiling board and square board Download PDFInfo
- Publication number
- CN101239483A CN101239483A CNA2006101679570A CN200610167957A CN101239483A CN 101239483 A CN101239483 A CN 101239483A CN A2006101679570 A CNA2006101679570 A CN A2006101679570A CN 200610167957 A CN200610167957 A CN 200610167957A CN 101239483 A CN101239483 A CN 101239483A
- Authority
- CN
- China
- Prior art keywords
- board
- deck
- slab
- plate
- sub
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Moisture-resist board, nine-cm board, cabinet board, door board, desktop board, floor board, and square board are manufactured using corn powder, rice shell, paring sheet, corn flour sheet, river sand or rock powder mixing with waterproof glue to semi-wet state, and then loaded into quantitatively mould and formed by rolling and pressing. The two surfaces of the board is paved with a layer of board sheets, fire-resist sheet, or board sheets when manufacturing, and then lay a nylon strengthen net in the board sheets, fire-resist sheet, or board sheets. Pave a layer of board on the four margins of the square board, and pave a layer of nylon strength net in the board sheet, and pave a layer of nylon strength net in the middle of the square board. The board and the sheet is stable in quality, moisture-resisting and not burning, saving the wood resource so that it is a good alternative for wood board and wood square board. Moisture resisting shed board is made using cement corn powder, rice shell, fine stove ash or powder coal ash mixing with water to semi-wet state, and then loaded into quantitatively mould and formed by rolling and pressing. Both surfaces of the board is paved with a layer of nylon strengthen net. The board surface will not crack or yellow after shaving for a long time.
Description
Technical field
Technology at present internal and international is, employing timber is raw material, through poach, rotary-cut and steam drying, again plate two-sided with milky white adhesive or all-purpose adhesive paste on the slab, fire prevention leather or floor leather, processing and fabricating worker plate, nine lis of plates, cabinet board, door-plate, desktop, floor and prescriptions, complex process not only, cost height, be subject to humidity, the distortion and inflammablely do not prevent fires of rotting, and waste timber resources.
Summary of the invention
Adopting sub flat, sub-bar of wood shavings in Yu Mi Grains end, rice husk and corn nest bar is raw material, adds marine glue and mixes to half wet not dried shape, roll extrusion making source-saving type moisture-proof working board, nine lis of plates, cabinet board, door-plate, desktop and floors in the quantitative mould of packing into.At two-sided one deck slab, fire prevention leather or the floor leather respectively laid of plate, in slab, fire prevention leather or floor leather, respectively lay one deck nylon reinforcing network during making.Make the more solid and high resilience of plate matter, the plate light weight, cost hangs down moisture proof without putrefaction, indeformable, and fire prevention is not burnt, and saves timber resources.
On batching, an amount of river sand (stone powder) of admixture expands and pushes a unreal difficult problem to solve sub flat, sub-bar of wood shavings in Yu Mi Grains end, rice husk and corn nest bar.Cut out to cut with iron hard iron and all can at plate face nailing nail.Be the substitute products on wooden worker's plate, nine lis of plates, cabinet board, door-plate, desktop and floors.
When making the source-saving type moisture-proof prescription, four limit faces at prescription respectively enclose shop one deck slab, respectively enclose shop one deck nylon reinforcing network in slab, and the middle one deck nylon reinforcing network that overlays in prescription, to increase the intensity and the pulling force of prescription, be the substitute products of timber system prescription.
With adopting cement, Yu Mi Grains end and thin ashes quarrels (flyash) is raw material, adds water and mixes to half wet not dried shape, and moistureproof refractory slab is made in roll extrusion in the quantitative mould of packing into.At two-sided one deck nylon reinforcing network of respectively laying of plate, make plate matter solid more durable during making, on the plate face, scrape Da Bai, year nondiscolouring, not crack of a specified duration.Be the substitute products of two Thistle boards, and solved the drawback of on two Thistle board faces, scraping big Bai Nianjiu flavescence and crack.
Description of drawings
1, the two ends handle of iron plate formulation amount mould 2, mould
3, pressing plate iron plate 4, pressing plate iron plate handle
Accompanying drawing 2 is made the quantitative mould elevation of nine lis of plates of source-saving type moisture-proof and refractory slab for roll extrusion: (is unit with the millimeter)
1, the two ends handle of iron plate formulation amount mould 2, mould
3, pressing plate iron plate 4, pressing plate iron plate handle
The specific embodiment
The specification of source-saving type moisture-proof working board, nine lis of plates, cabinet board, door-plate, desktop, floor, refractory slab and prescriptions:
1, moisture-proof working board: 240cm * 120cm * 1.8cm
2, moistureproof nine lis of plate: 240cm * 120cm * 0.9cm
3, moistureproof cabinet board: 240cm * 120cm * 1.8cm
4, moistureproof door-plate: 200cm * 90cm * 4.5cm
185cm×80cm×4.5cm
5, moistureproof desktop: 240cm * 120cm * 2.5cm
100cm×100cm×2.5cm
6, moisture-proof floor: 100cm * 15cm * 1.5cm (with lock mouthful)
120cm * 20cm * 2cm (with lock mouthful)
7, moistureproof refractory slab: 240cm * 120cm * 0.9cm
8, moistureproof prescription: 3m * 3cm * 5cm
3m×4cm×6cm
The distribution of source-saving type moisture-proof working board, nine lis of plates, cabinet board, door-plate, desktop, prescription:
1, the proportioning of Yu Mi Grains end, river sand (stone powder) is 1.5: 1, adds marine glue and mixes to half wet not dried shape.
2, the proportioning of flat, the river sand (stone powder) of rice husk is 1.5: 1, adds marine glue and mixes to half wet not dried shape.
3, the proportioning of Yu Mi Grains end, the sub-bar of wood shavings, river sand (stone powder) adds marine glue and mixes to half wet not dried shape at 2: 1: 1.5.
4, the proportioning of Yu Mi Grains end, corn nest bar, river sand (stone powder) adds marine glue and mixes to half wet not dried shape at 2: 1: 1.5.
5, the distribution on 1.5: 1.5: 2 source-saving type moisture-proof floors of proportioning of sub flat, the river sand (stone powder) in Yu Mi Grains end, rice husk:
1, the proportioning of Yu Mi Grains end, river sand (stone powder) adds marine glue and mixes to half wet not dried shape at 1.5: 1.
2, the proportioning of Yu Mi Grains end, the sub-bar of wood shavings, river sand (stone powder) adds marine glue and mixes to half wet not dried shape at 2: 1: 1.5.
The distribution of moistureproof refractory slab:
1, cement, Yu Mi Grains proportioning last, thin ashes quarrels (flyash) add water and mix to partly wet not dried shape at 1: 2: 1.
2, the proportioning of flat, the thin ashes quarrels of cement, rice husk (flyash) adds water and mixes to half wet not dried shape at 1: 2: 1.
3, the proportioning of cement, Yu Mi Grains end, sub flat, the thin ashes quarrels of rice husk (flyash) is 1: 1: 1: 1 adds water mixes to half wet not dried shape.
The preparation method of source-saving type moisture-proof working board, nine lis of plates, cabinet board, door-plate, desktop:
At first supporting plate by being placed in the flat unwheeling of four-wheel, (flat frame is equipped with lifting and roller bearing) again mould by being placed on the supporting plate, lay one deck slab or fire prevention leather on the supporting plate in mould, on slab and fire prevention leather face, all respectively brush one deck marine glue, on slab or fire prevention leather, lay one deck nylon reinforcing network again, charging, material is filled to exceeds mould 2cm, 1cm, 4cm or 2.5cm, on material, respectively lay one deck nylon reinforcing network, re-laying slab or the fire prevention leather that brushes marine glue on the aspect on the nylon reinforcing network, before being pushed into machine, push the roll extrusion platform roll extrusion of multi-functional unburned brick and tile dividing plate compacting (roll extrusion) machine again, connect holder with the flat unwheeling of four-wheel behind the machine, the roll extrusion pusher is to vacant lot or canopy, by putting a block pressur plate iron plate, level is lifted mould, removes pressing plate iron plate again on the plate face.The supporting plate plate is lifted to rack-layer, and source-saving type moisture-proof working board, nine lis of plates, cabinet board, door-plate, desktops are made.
Can reach intensity in 15 days, at four limit faces of plate marine glue pasting boards leather or fire prevention leather edge sealing bar.Just can sell use two days later.
The preparation method on source-saving type moisture-proof floor:
At first supporting plate by being placed in the flat unwheeling of four-wheel, 1 * 10 moisture-proof floor assembling die, by being placed on the supporting plate, all brushing marine glue on the 10 floor leather faces, put into each mould lattice, all lay one deck nylon reinforcing network on slab of various places, charging is filled to material and exceeds mould 1.5cm, on material, all re-lay one deck nylon reinforcing network, before all re-laying the floor leather that brushes marine glue on the aspect on the nylon reinforcing network, being pushed into machine, push the roll extrusion of roll extrusion platform, behind the machine with the flat bridge joint holder of four-wheel, the roll extrusion pusher is to vacant lot or canopy, on every floor face, all respectively by putting a block pressur plate iron plate, level is lifted mould, remove pressing plate iron plate again, the supporting plate floor is lifted to rack-layer, 10 moisture-proof floors are made.Four limit faces on the floor after 15 days are pasted the edge sealing bar with marine glue, just can sell use two days later.
The preparation method of moistureproof refractory slab:
At first holding in the palm by being placed in the flat unwheeling of four-wheel, mould by being placed on the supporting plate, lay one deck nylon reinforcing network on the supporting plate in mould, charging, material be filled to exceed mould 1cm, on material, re-lay one deck nylon reinforcing network, be pushed into machine before, push the roll extrusion of roll extrusion platform, connect holder with the flat unwheeling of four-wheel behind the machine.The roll extrusion pusher is to vacant lot or canopy, and by putting a block pressur plate iron plate, level is lifted mould, removes pressing plate iron plate again, and the supporting plate refractory slab is lifted to rack-layer on the refractory slab face, and moistureproof refractory slab is made.The health of spraying water after 48 hours, every day, three healths were seven days, amounted to 20 days, can reach intensity and just can sell use.
The preparation method of source-saving type moisture-proof prescription:
At first supporting plate by being placed in the flat unwheeling of four-wheel, again the assembling die of 1 * 20 prescription by being placed on the supporting plate, in each mould lattice, all enclose slab that brushes marine glue on one aspect of shop, in slab, respectively enclose shop one deck nylon reinforcing network, charging, material is filled to a half, one deck nylon reinforcing network again tiles on material, again material is filled to and exceeds mould 3cm, nylon wire is surrounded again slab is surrounded, be pushed into machine before, push the roll extrusion of roll extrusion platform, connect holder with the flat unwheeling of four-wheel behind the machine, the roll extrusion pusher presses 20 prescription iron plate all by being placed on each prescription face to vacant lot or canopy.Level is lifted mould, removes to press prescription iron plate again, and 20 source-saving type moisture-proof prescriptions are made.Intensity can be reached in 15 days, and just use can be sold.
Annotate: beautiful rice Grains need be ground into the end, and rice husk need be rolled into flat, wood shavings and corn nest need the pulverizing sliverings (1.5cm * 0.5cm).
The marine glue that the marine glue need are used with the stickup waterproof roll.But 10: 1 milky white adhesive of marine glue admixture is with the setting rate of the marine glue that slows down.
Cement 500#.
Claims (10)
1. adopt that Yu Mi Grains is last, sub flat, the sub-bar of wood shavings of rice husk, corn nest bar, river sand (stone powder) and marine glue be raw material, processing and fabricating source-saving type moisture-proof working board and nine lis of plates.During making,, in slab, respectively lay one deck nylon reinforcing network at two-sided one deck slab of respectively laying of plate.
2. adopt that Yu Mi Grains is last, sub flat, the sub-bar of wood shavings of rice husk, corn nest bar, river sand (stone powder) and marine glue be raw material, processing and fabricating source-saving type moisture-proof cabinet board.At two-sided one deck fire prevention leather of respectively laying of plate, in the fire prevention leather, respectively lay one deck nylon reinforcing network during making.
3. adopt that Yu Mi Grains is last, sub flat, the sub-bar of wood shavings of rice husk, corn nest bar, river sand (stone powder) and marine glue be raw material, processing and fabricating source-saving type moisture-proof door-plate and desktop.At two-sided one deck slab of respectively laying of plate, in slab, respectively lay one deck nylon reinforcing network during making.
4. adopting Yu Mi Grains end, the sub-bar of wood shavings, river sand (stone powder) and marine glue is raw material, processing and fabricating source-saving type moisture-proof floor.At two-sided one deck floor leather of respectively laying of plate, in the leather of floor, respectively lay one deck nylon reinforcing network during making.
5. adopting cement, Yu Mi Grains end, the sub flat and thin ashes quarrels of rice husk (flyash) is raw material, adds water and mixes to half wet not dried shape the moistureproof refractory slab of processing and fabricating.During making at two-sided one deck nylon reinforcing network of respectively laying of plate.
6. adopt Yu Mi Grains end, the sub-bar of wood shavings, river sand (stone powder) and marine glue are raw material, processing and fabricating source-saving type moisture-proof prescription and balustrade.Four limit faces at prescription or balustrade during making respectively enclose shop one deck slab, respectively enclose shop one deck nylon reinforcing network in slab, and the middle one deck nylon reinforcing network that overlays in prescription or balustrade.
7. adopt that Yu Mi Grains is last, sub flat, the sub-bar of wood shavings of rice husk, corn nest bar, river sand (stone powder) and marine glue be raw material, processing and fabricating source-saving type moisture-proof clothes closet plate and bed board.At two-sided one deck slab of respectively laying of plate, in slab, respectively lay one deck nylon reinforcing network during making.
8. adopt that Yu Mi Grains is last, sub flat, the sub-bar of wood shavings of rice husk, corn nest bar, river sand (stone powder) and marine glue be raw material processing and fabricating source-saving type moisture-proof panel, chopping board and the black plate of engineering.At two-sided one deck slab of respectively laying of plate, in slab, respectively lay one deck nylon reinforcing network during making.
9. adopting Yu Mi Grains end, the sub-bar of wood shavings, river sand (stone powder) and marine glue is raw material processing and fabricating source-saving type moisture-proof mast peculiar to vessel.Respectively enclose shop one deck slab during making in two semicircle masts, respectively lay five layers of nylon reinforcing network more than slab, make the back and with marine glue two semicircle masts fastenings are sticked together, spacing 50cm respectively bores a hole, penetrates with lead screw, reinforces with screw.
10. adopting cement, Yu Mi Grains end, river sand (stone powder) is raw material, adds water and mixes to half wet not dried shape, makes sculpture goods and stair circular abutment railing.At two-sided one deck nylon reinforcing network of respectively laying of two half sculpture goods or two semicircle post and rails, make the back and two half sculpture goods or two semicircle post and rails fastenings are sticked together during making with marine glue.