CN101191030A - Water-based anti-sticking dope and producing method thereof - Google Patents
Water-based anti-sticking dope and producing method thereof Download PDFInfo
- Publication number
- CN101191030A CN101191030A CNA2006100703638A CN200610070363A CN101191030A CN 101191030 A CN101191030 A CN 101191030A CN A2006100703638 A CNA2006100703638 A CN A2006100703638A CN 200610070363 A CN200610070363 A CN 200610070363A CN 101191030 A CN101191030 A CN 101191030A
- Authority
- CN
- China
- Prior art keywords
- emulsion
- weight part
- interfacial agents
- weight portions
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an aqueous antisticking paint and a preparation method thereof. The aqueous antisticking paint comprises the components that: 50-80 weight potions of emulsion, 2-20 weight portions of interfacial agent, 0.1-0.5 weight portions of defoaming agent, 0.1-0.6 weight portions of preservative, 2-4 weight portions of film-forming additive, and 0.2-0.7 weight potions of thickening agent. The preparation method is that: according to the given weight portions, under the condition of slowly stirring, the emulsion, the defoaming agent, the film-forming additive, the interfacial agent and the preservative are added in sequence, and well stirred, and then thickening agent is added to form proper viscosity, then filtered, thus obtaining the aqueous antisticking paint. The invention does not comprise organic solvent, does not do harm to human and natural environment, has good hydrophobicity and can be wildly used for the surfaces of concrete, plasterboard, wood and metal.
Description
Technical field
The invention belongs to a kind of chemistry painting industry, relate in particular to a kind of aqueous, environmental protective Antisticking coating.
Background technology
Along with rapid economy development and people continuous increase to information requirement, all kinds of unrest are signposted and are continued to bring out, these disorderly paste small advertisement and are difficult for tearing, become extremely discordant city " psoriasis ", therefore be necessary to produce a kind of non-setting adhesive barrier coating that is applicable to building surface, the phenomenon of stopping on buildings, at will to put up non-setting adhesive
At present, both at home and abroad the non-setting adhesive barrier coating generally adopts organic resin to mix with Wax since in the material in a large number with an organic solvent, understand to environment and human body working the mischief and pollute in the brushing process; And this class material ventilation property is relatively poor, also is not suitable for the surface of brushing at buildingss such as concrete.CN200510045871.6 discloses a kind of Antisticking coating as the Chinese invention patent publication number, it carries out stirring heating with polyethylene wax 3～11, paraffin 2～10, Microcrystalline Wax 0.5～10, natural resin 6～8, dimethylbenzene 40～60, ethanol 10～15, petroleum naphtha 10～40, ethylene glycol monobutyl ether 10～35 mixing, and the homogeneous reaction post-treatment forms.The object plane of coating Antisticking coating has than low surface tension, and there is self-cleaning action on the patellate surface, and dirt tumbles naturally, can come off easily after self-adhesive paper sticks.But this Antisticking coating in a large number with an organic solvent, pollutes for environment and human body and endanger.
Summary of the invention
The present invention is for solving existing non-setting adhesive barrier coating in a large number with an organic solvent, pollutes for environment and human body and endangers, and a kind of pollution-free, harmless aqueous, environmental protective Antisticking coating is provided; The production method of this aqueous, environmental protective Antisticking coating is provided simultaneously
For addressing the above problem, water-based anti-sticking dope of the present invention is composed of the following components
Emulsion 50-80 weight part, interfacial agents 2-20 weight part, defoamer 0.1-0.5 weight part, sanitas 0.1-0.6 weight part, film coalescence aid 2-4 weight part, thickening material 0.2-0.7 weight part.
Emulsion wherein is a kind of in ACRYLIC EMULSION, phenylpropyl alcohol (cinnamic acrylic ester) copolymer emulsion, vinyl acetate between to for plastic-tertiary carbon acid esters copolymer emulsion and the organosilicon crylic acid latex at least.
It is the super-hydrophobicity interfacial agents that interfacial agents wherein requires.
Remaining defoamer, sanitas, film coalescence aid and thickening material are coating raw material commonly used.
The preparation method of this Antisticking coating is: the parts by weight according to setting, under the situation of stirring at low speed, add emulsion, defoamer, film coalescence aid, interfacial agents and sanitas successively, and stir, add thickening material again and be modulated into appropriate viscosity and filter and get final product.
The present invention compared with prior art has following advantage: the anti-paste coating of the present invention is the aqueous, environmental protective product, there is not organic solvent, can not work the mischief to human body and physical environment, has extraordinary hydrophobic performance, common non-setting adhesive and dust are not easy to be attached on the coating, produce simple, superior performance, but widespread use and concrete, plasterboard, timber, metallic surface.
Embodiment
Below in conjunction with preferred embodiment the present invention is done further auspicious stating:
Prescription is: 80 kilograms of (total amount is 100 kilograms of meters) organosilicon crylic acid latexs, 15 kilograms of interfacial agents, 0.3 kilogram of defoamer, 0.2 kilogram of sanitas, 4 kilograms of film coalescence aid, 0.5 kilogram of thickening material.
The blending process step is: at first disperse to add emulsion in the cylinder at stainless steel, start stirrer, add defoamer, film coalescence aid, interfacial agents and sanitas under the stirring at low speed situation, stirred 5 minutes, and slowly added thickening material again, stirred 10 minutes, filter with vibratory screening apparatus, packing gets final product.
Interfacial agents wherein is the LD super-hydrophobicity interfacial agents that Architectural Science Design Inst. of Zhejiang Prov. produces.
Wherein state the NXZ that defoamer can be a Henkel company.
Sanitas wherein can be that Rhom and Hass produces
Sterilant; The Hua Ke-981 that Shanxi Petro-Chemical Design Inst. produces.
Film coalescence aid wherein can be the TEXANOL that Eastman Chemical Company produces.
Thickening material wherein can be the ACRYSOL that Rhom and Hass produces
TMASE-60 and ACRYSOL
TMRM-8W.
Claims (1)
1. water-based anti-sticking dope, it is mixed by following component:
Emulsion 50-80 weight part, interfacial agents 2-20 weight part, defoamer 0.1-0.5 weight part, sanitas 0.1-0.6 weight part, film coalescence aid 2-4 weight part, thickening material 0.2-0.7 weight part;
Emulsion wherein is a kind of in ACRYLIC EMULSION, phenylpropyl alcohol (cinnamic acrylic ester) copolymer emulsion, vinyl acetate between to for plastic-tertiary carbon acid esters copolymer emulsion and the organosilicon crylic acid latex at least, and it is the super-hydrophobicity interfacial agents that interfacial agents wherein requires;
Its preparation method is: the parts by weight according to setting, under the situation of stirring at low speed, add emulsion, defoamer, film coalescence aid, interfacial agents and sanitas successively, and stir, add thickening material again and be modulated into appropriate viscosity and filter and get final product.