CN101153366A - 孕育处理改善离心铸造气缸套金相组织的方法 - Google Patents
孕育处理改善离心铸造气缸套金相组织的方法 Download PDFInfo
- Publication number
- CN101153366A CN101153366A CNA2006100964002A CN200610096400A CN101153366A CN 101153366 A CN101153366 A CN 101153366A CN A2006100964002 A CNA2006100964002 A CN A2006100964002A CN 200610096400 A CN200610096400 A CN 200610096400A CN 101153366 A CN101153366 A CN 101153366A
- Authority
- CN
- China
- Prior art keywords
- graphite
- metallographic structure
- cylinder cover
- gestating
- processing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种孕育处理改善离心铸造气缸套金相组织的方法，它适用于发动机气缸套达A型石墨、高耐磨、使用寿命长的需求。本发明应用孕育处理改善离心铸造气缸套金相组织的方法，使气缸套金相组织得到分布均匀细片状的A型石墨，其基体为珠光体。对铁水进行瞬时孕育处理，可以消除缸套组织中的晶间石墨，提高抗拉强度，降低硬度。经过瞬时孕育处理，在铁液中存在的碳、硅的浓度起伏和温度起伏的微观区域大量的石墨核心在这些微观区域内形成均匀分布的A型。
Description
所属技术领域
本发明涉及一种孕育处理改善离心铸造气缸套金相组织的方法，它适用于发动机气缸套达A型石墨、高耐磨、使用寿命长的需求。
背景技术
传统的合金铸铁材质气缸套，其毛坯由金属模具离心铸造而成，由于冷却速度大，使金相组织容易形成D和E型石墨，导致抗拉强度低，硬度升高，给加工带来一定困难。同时其性能降低，发动机使用寿命短。
发明内容
本发明应用孕育处理改善离心铸造气缸套金相组织的方法，使气缸套金相组织得到分布均匀细片状的A型石墨，其基体为珠光体。
对铁水进行瞬时孕育处理，可以消除缸套组织中的晶间石墨，提高抗拉强度，降低硬度。
经过瞬时孕育处理，在铁液中存在的碳、硅的浓度起伏和温度起伏的微观区域大量的石墨核心在这些微观区域内形成均匀分布的A型。
A型石墨对基体的破坏作用减少，所以抗拉强度增高。其化学成分中的硅有相当一部分已成为石墨结晶的核心，对基体的固溶强化作用大大减弱，因此硬度没有未孕育处理的缸套高。
其孕育剂采用75Si或硅钡孕育剂，硅是强烈促进石墨化元素，能使Fe-C合金的共晶点左移共晶温度升高，利于碳原子在铁液中扩散、聚集、使石墨长大。
硅量增加，缸套的抗拉强度降低，这是因为硅含量增加，引起石墨片粗大，增多。石墨越多，基体承载面积减少，石墨片越粗大，其缺口效应越强烈，使基体在受到拉伸载荷时，越容易产生应力集中。因此在孕育时一定要控制好硅的含量。
附图说明
见附图中说明。
具体实施方式
1.电炉熔炼时控制原始硅1.4％左右；
2.按运转铁水包容量配置一次孕育剂含量(硅含量控制在1.7％～1.8％之间)；
3.将孕育剂放入运转包底；
4.运转铁水包中进铁水；
5.铁水净化2-3分钟；
6.化验；
7.二次孕育在浇包中进行；
8.根据浇包的容量配置二次孕育剂含量(硅含量控制在2.0％～2.2％之间)；
9.将二次孕育剂放入浇包中；
10.将运转包中的铁水倒入浇包中；
11.浇注。
Claims (3)
1.本发明涉及一种孕育处理改善离心铸造气缸套金相组织的方法，它适用于发动机气缸套达A型石墨、高耐磨、使用寿命长的需求。
2.根据权利要求书1所述的其特征是：本发明应用应用孕育处理改善离心铸造气缸套金相组织的方法，使气缸套金相组织得到分布均匀细片状的A型石墨，其基体为珠光体。。
3.根据权利要求书1所述的其特征是：对铁水进行瞬时孕育处理，可以消除缸套组织中的晶间石墨，提高抗拉强度，降低硬度。