CN101134652A - Cement floor hardening agent and construction technique thereof - Google Patents
Cement floor hardening agent and construction technique thereof Download PDFInfo
- Publication number
- CN101134652A CN101134652A CNA2006101123201A CN200610112320A CN101134652A CN 101134652 A CN101134652 A CN 101134652A CN A2006101123201 A CNA2006101123201 A CN A2006101123201A CN 200610112320 A CN200610112320 A CN 200610112320A CN 101134652 A CN101134652 A CN 101134652A
- Authority
- CN
- China
- Prior art keywords
- cement
- hardening agent
- cement floor
- agent
- floor hardening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides one kind of cement floor curing agent and its construction process. The cement floor curing agent is prepared with interface agent in 18 kg, Portland cement in 2 kg, and aqueous color paste specially for paint in 50-100 ml, and through mixture. The construction process with the cement floor curing agent includes the steps of: cleaning floor, wetting floor, mixing the cement floor curing agent and water in the same weight, painting to floor, and drying. The cement floor curing agent can cure the surface layer of concrete and cement mortar, fill the cracks and ensure environmental sanitation.
Description
Technical field
The present invention relates to the tackiness agent in the material of construction, relate in particular to a kind of solidifying agent and construction technology thereof that is used for indoor cement flooring.
Background technology
At present domestic a large amount of new dwelling house all is to pay the house purchaser with the form of rough house, when rough house is carried out indoor fine fitment, usually will be to ground water silt particle slurry plaster leveling, cause ground coarse, be prone to phenomenons such as crackle, crack, a sand, an ash, the working-yard is difficult to carry out hygiene, is difficult to more guarantee that construction environment reaches technology and technical requirements, can not satisfy the requirement of civilized construction.Therefore family room's interior finish work is to be hard nut to crack with filthy working-yard always, and this has become the industry common fault.
Summary of the invention
Existing in order to overcome to causing the defective of environmental pollution in the construction of rough house cement flooring, the object of the present invention is to provide a kind of cement floor hardening agent, a kind of construction technology that adopts this solidifying agent also is provided, has not only ensured construction quality, but also created excellent environmental protection construction environment.
The technical solution adopted for the present invention to solve the technical problems is: cement hardener is that main component and be mixed in proportion with special-purpose aqueous mill base of coating and inert matter forms with the interfacial agents.Its prescription is: 18 kilograms of interfacial agents, 2 kilograms of silicate cements, 50～100 milliliters of the special-purpose aqueous mill bases of coating.Through mixing and fully being formed into material after the stirring, pack with bucket, stand-by.
Adopt the construction technology step of cement hardener of the present invention to be: (1) cleaning ground; (2) dip in water with mop, clean and moistening ground; (3) become material and clear water to stir, form spendable solidifying agent by 1: 1 mixed; (4) with solidifying agent roller coating cement flooring; (5) add at positions such as corners and be coated with solidifying agent; (6) survive after the drying.
The invention has the beneficial effects as follows, adopt solidifying agent roller coating cement flooring, after the brushing, owing to the solidification to concrete and sand-cement slurry coat of plaster surface, the ground sand-lime is cured fully, crack and crackle are filled, when in construction, cleaning the ground health, no longer include dust and sand grains, guaranteed the construction environment health effectively, and can as prior art, directly not use the sand-cement slurry plaster leveling, cause environmental pollution.
Embodiment
It is main component that cement hardener of the present invention is to use with the interfacial agents, and interpolation water-based pigment and inert matter are mixed in proportion and form, and its prescription is: 18 kilograms of interfacial agents, 2 kilograms of silicate cements, 50～100 milliliters of the special-purpose aqueous mill bases of coating.In practice of construction, according to the difference of selected color, can suitably adjust the ratio of the special-purpose aqueous mill base of coating in the prescription, be advisable with 100 milliliters usually, then should choose 50～80 milliliters for special color such as red, orange and be advisable.To after fully stirring, be formed into material according to the composite batching of above-mentioned prescription, pack with bucket, stand-by.Silicate cement can be selected the P32.5 ordinary Portland cement for use.Interfacial agents is to handle a kind of tackiness agent of the increase sticking power of building concrete and sand-cement slurry coat of plaster surface usefulness, and it can carry out surface cure to concrete and sand-cement slurry coat of plaster.Interfacial agents is water white liquid, added the special-purpose aqueous mill base of cement inert matter and coating in proportion, mix the back and form cement hardener, rapid permeability can not take place in brushing when concrete and sand-cement slurry coat of plaster surface, and can form the integrally curing film, thereby can ground be cured in the mode of big area brushing, improve the construction environment health, reduced the pollution of dust and sand-lime construction environment.
The construction technology step of cement hardener of the present invention is: (1) cleaning ground; (2) dip in water with mop, clean and moistening ground; (3) become material and clear water to stir, form spendable solidifying agent by 1: 1 mixed; (4) with solidifying agent roller coating cement flooring; (5) add at positions such as corners and be coated with solidifying agent; (6) survive after the drying.So construction creates civilized construction, the environment of environmental protection construction.Because cement hardener added color, make construction ground more attractive in appearance, form carpet or mulch film effect, perfect civilized construction image.
Claims (4)
1. cement floor hardening agent is characterized in that, described cement hardener is that main component and be mixed in proportion with special-purpose aqueous mill base of coating and inert matter forms with the interfacial agents.
2. cement floor hardening agent as claimed in claim 1 is characterized in that, the prescription of described cement hardener is: 18 kilograms of interfacial agents, 2 kilograms of silicate cements, 50～100 milliliters of the special-purpose aqueous mill bases of coating;
To after fully stirring, be formed into material according to above-mentioned prescription blended batching, pack with bucket, stand-by.
3. cement floor hardening agent as claimed in claim 2 is characterized in that, described silicate cement can be selected No. 32.5 ordinary Portland cements of P for use.
4. one kind is adopted the construction technology step of the described cement floor hardening agent of claim 1 to be:
(1) cleaning ground;
(2) dip in water with mop, clean and moistening ground;
(3) become material and clear water to stir, form spendable solidifying agent by 1: 1 mixed;
(4) with solidifying agent roller coating cement flooring;
(5) add at positions such as corners and be coated with solidifying agent;
(6) survive after the drying.