CN101131032A - Moulded glass fibre reinforced plastic grille and manufacturing method thereof - Google Patents
Moulded glass fibre reinforced plastic grille and manufacturing method thereof Download PDFInfo
- Publication number
- CN101131032A CN101131032A CN 200610086257 CN200610086257A CN101131032A CN 101131032 A CN101131032 A CN 101131032A CN 200610086257 CN200610086257 CN 200610086257 CN 200610086257 A CN200610086257 A CN 200610086257A CN 101131032 A CN101131032 A CN 101131032A
- Authority
- CN
- China
- Prior art keywords
- resin
- reinforced plastic
- plastic grille
- glass
- bed die
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to one kind of molded GRP grille and its production process, and features that the molded GRP grille is produced with resin as basic material, and through adding proper amount of promoter and curing agent and glass fiber as reinforcing material, molding and curing. The resin may be one of three kinds of resin, including vinyl resin, etc; the promoter is cobalt isozincate in 0.5-3 wt% of resin; and the curing agent is butanone peroxide in 0.5-3 wt% of resin. The molded GRP grille has high strength and easy edge trimming.
Description
Technical field
The present invention relates to a kind of glass-fiber reinforced plastic grille, specifically a kind of have high-intensity glass-fiber reinforced plastic grille and a production method thereof.
Background technology
Relevant by retrieval patent documentation does not retrieve moulded glass fibre reinforced plastic grille identical with the present invention and production method thereof at present as yet.Existing glass-fiber reinforced plastic grille is owing to resin, glass fiber and production technology, and the glass-fiber reinforced plastic grille of producing generally can only be used as places such as platform, floor, trench cover plate.For the high occasion of requirement of strength as: high boat deck, highrise building then are difficult to satisfy its requirement, thus be necessary mining inetesity height, the better glass-fiber reinforced plastic grille kind of performance, to satisfy the needs of high strength use occasion.
Summary of the invention
The objective of the invention is to provide a kind of employing mold pressing, have the intensity height, can be used for the glass-fiber reinforced plastic grille of high boat deck, highrise building.
Another object of the present invention is that a kind of method of producing above-mentioned moulded glass fibre reinforced plastic grille will be provided.
The object of the present invention is achieved like this:
Moulded glass fibre reinforced plastic grille is characterized in that: being base material with the resin, adding an amount of accelerator, curing compound, is that reinforcing material forms through molded curing with the glass fiber yarn; Described resin is wherein a kind of of adjacent benzene resin, isophthalic resin, vinylite.
An amount of accelerator of described adding is meant that the weight group of adding is: the different cobalt green of amount of resin 0.5-3%.
An amount of curing compound of described adding is meant that the weight group of adding is: the methyl ethyl ketone peroxide of amount of resin 0.5-3%.
A kind of method of producing above-mentioned moulded glass fibre reinforced plastic grille may further comprise the steps:
1. with special-purpose bed die preheating, and maintain the temperature at 30-45 ℃;
2. get quantity of resin, add an amount of accelerator, curing compound in proportion, and stir;
3. the 2. made resin colloid of step is cast in the step mold cavity 1.;
4. on bed die evenly around the cloth glass fiber yarn;
5. step is 2. made resin glue casts in the step mold cavity 4., and compacting, and glass fiber yarn is fully flooded;
6. repeating step 4., step 5., successively evenly around cloth glass fiber yarn, casting resin colloid to the bed die height, compacting, glass fiber yarn is fully flooded;
7. with the mold gland on bed die, mold and bed die compress, pressure is: 100～180bar;
8. mold, bed die are heated together with the good glass-fiber reinforced plastic grille of casting, its resin is fully solidified, temperature remains on 30-45 ℃;
9. withdraw from mould, take out the glass-fiber reinforced plastic grille that is cured;
10. the 9. described glass-fiber reinforced plastic grille of step is repaired, got finished product.
The present invention compared with prior art has following remarkable advantage:
1, is base material owing to taking resin glue, and adds accelerator, curing compound, make mixed resin glue have good adhesive property.
2, because the high-intensity glass fiber yarn of employing is a reinforcing material, and form, make the glass-fiber reinforced plastic grille of producing have very high intensity, and the finishing corner is convenient through molded curing.
3, adopt curing compound, accelerator, manufacturing process keeps certain temperature simultaneously, can make resin solidification rapid.
4, the glass-fiber reinforced plastic grille reliable in quality of producing owing to this method, the intensity height is so can be used for occasions such as high boat deck, highrise building.
Description of drawings
Below with reference to accompanying drawing the present invention is further described:
Accompanying drawing 1 is the flow chart of moulded glass fibre reinforced plastic grille of the present invention and production method thereof;
Accompanying drawing 2 is structural representations of the bed die in moulded glass fibre reinforced plastic grille of the present invention and the production method thereof;
Accompanying drawing 3 is structural representations of the mold in moulded glass fibre reinforced plastic grille of the present invention and the production method thereof;
The specific embodiment
With reference to accompanying drawing 1, accompanying drawing 2, accompanying drawing 3, moulded glass fibre reinforced plastic grille of the present invention is a base material with the resin, adds an amount of accelerator, curing compound, is that reinforcing material forms through molded curing with the glass fiber yarn; Described resin is wherein a kind of of adjacent benzene resin, isophthalic resin, vinylite.An amount of accelerator of described adding is meant that the weight group of adding is: the different cobalt green of amount of resin 0.5-3%, the different cobalt green that present embodiment adds weight resin 2% is an accelerator.An amount of curing compound of described adding is meant that the weight group of adding is: the methyl ethyl ketone peroxide of amount of resin 0.5-3%, the methyl ethyl ketone peroxide that present embodiment adds weight resin 2% is a curing compound.
A kind of method of producing above-mentioned moulded glass fibre reinforced plastic grille may further comprise the steps:
1. with special-purpose bed die preheating, and maintain the temperature at 30-45 ℃, present embodiment maintains the temperature at 40 ℃:
2. get quantity of resin, add an amount of accelerator, curing compound according to the above ratio, and stir;
3. the 2. made resin colloid of step is cast in the step mold cavity 1.;
4. on bed die evenly around the cloth glass fiber yarn;
5. step is 2. made resin glue casts in the step mold cavity 4., and compacting, and glass fiber yarn is fully flooded;
6. repeating step 4., step 5., successively evenly around cloth glass fiber yarn, casting resin colloid to the bed die height, compacting, glass fiber yarn is fully flooded;
7. with the mold gland on bed die, mold and bed die compress, pressure is: 100～180bar, present embodiment pressure are 120bar;
8. mold, bed die are heated together with the good glass-fiber reinforced plastic grille of casting, its resin is fully solidified, temperature remains on 30-45 ℃, and present embodiment maintains the temperature at 40 ℃;
9. withdraw from mould, take out the glass-fiber reinforced plastic grille that is cured;
10. the 9. described glass-fiber reinforced plastic grille of step is repaired, got finished product.
Claims (4)
1. moulded glass fibre reinforced plastic grille, it is characterized in that: being base material with the resin, adding an amount of accelerator, curing compound, is that reinforcing material forms through molded curing with the glass fiber yarn; Described resin is wherein a kind of of adjacent benzene resin, isophthalic resin, vinylite.
2. moulded glass fibre reinforced plastic grille according to claim 1 is characterized in that: an amount of accelerator of described adding is meant that the weight group of adding is: the different cobalt green of amount of resin 0.5-3%.
3. moulded glass fibre reinforced plastic grille according to claim 1 is characterized in that: an amount of curing compound of described adding is meant that the weight group of adding is: the methyl ethyl ketone peroxide of amount of resin 0.5-3%.
4. method of producing the described moulded glass fibre reinforced plastic grille of claim 1 may further comprise the steps:
1. with special-purpose bed die preheating, and maintain the temperature at 30-45 ℃;
2. get quantity of resin, add an amount of accelerator, curing compound in proportion, and stir;
3. the 2. made resin colloid of step is cast in the step mold cavity 1.;
4. on bed die evenly around the cloth glass fiber yarn;
5. step is 2. made resin glue casts in the step mold cavity 4., and compacting, and glass fiber yarn is fully flooded;
6. repeating step 4., step 5., successively evenly around cloth glass fiber yarn, casting resin colloid to the bed die height, compacting, glass fiber yarn is fully flooded;
7. with the mold gland on bed die, mold and bed die compress, pressure is: 100～180bar;
8. mold, bed die are heated together with the good glass-fiber reinforced plastic grille of casting, its resin is fully solidified, temperature remains on 30-45 ℃;
9. withdraw from mould, take out the glass-fiber reinforced plastic grille that is cured;
10. the 9. described glass-fiber reinforced plastic grille of step is repaired, got finished product.