CN101117420A - High-performance abrasion-proof rubber cushion - Google Patents
High-performance abrasion-proof rubber cushion Download PDFInfo
- Publication number
- CN101117420A CN101117420A CNA2007102008900A CN200710200890A CN101117420A CN 101117420 A CN101117420 A CN 101117420A CN A2007102008900 A CNA2007102008900 A CN A2007102008900A CN 200710200890 A CN200710200890 A CN 200710200890A CN 101117420 A CN101117420 A CN 101117420A
- Authority
- CN
- China
- Prior art keywords
- rubber cushion
- proof rubber
- parts
- shares
- performance abrasion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-performance wear-resistant rubber pad, comprising the following weight part compositions of ingredients: 7.0-8.7 shares of natural rubber, 3.0-4.3 shares of cis-1,4-polybutadiene rubber, 30-40 shares of multipolymer of ethane and vinyl acetate, 2.0-3.5 shares of light calcium, 5-9 shares of carbon black, 0.6-0.75 shares of stearic acid, 0.4-0.7 shares of accelerant, 1.8-2.0 shares of zinc oxide, 0.7-0.9 shares of vesicant and 0.8-1.2 shares of engine oil. The invention is made by common technique. The invention has the advantages of wear-resistance and small weight, which can be widely applied on occasions where high requirements on wear-resistance are needed and prolongs the service life of components or equipment.
Description
Technical field
The present invention relates to a kind of rubber pad, particularly relate to a kind of high performance abrasion-proof rubber cushion.
Background technology
In daily life and work place,,, can cause the destruction of object outward appearance even lose original performance effect along with the growth of fraction time owing to do not stop friction between object.Such as sole, need possess wear resisting property, could the underwriter after sports such as every day walking even running, be not easy worn out, the wear resisting property of sole is good more, and work-ing life is long more, if add in light weight, will be comfortable and easy to wear, can satisfy users' demand.Though sole in the market has wear resisting property, also have lightweightly, performance is different, and result of use has nothing in common with each other.Therefore, develop a kind of wear resisting property excellence, lightweight rubber pad, help applying at sole and other mat industries.
Summary of the invention
The objective of the invention is to, provide a kind of new wear resisting property good, and lightweight rubber pad.
Technical scheme of the present invention: a kind of high-performance abrasion-proof rubber cushion, it is characterized in that: this high-performance abrasion-proof rubber has the following materials of weight proportions of using, 7.0~8.7 parts of natural rubbers, 3.0~4.3 parts of cis-butadiene cements, 30~40 parts of ethylene vinyl acetates, 2.0~3.5 parts of fine particle calcium carbonates, 5~9 parts of carbon blacks, 0.6~0.75 part of hard ester acid, 0.4~0.7 part of promotor, 1.8~2.0 parts in zinc oxide, 0.7~0.9 part of whipping agent, 0.8~1.2 part in machine oil adopt conventional manufacture craft to make.
Above-mentioned high-performance abrasion-proof rubber cushion, described natural rubber are the 3L natural rubbers.
Aforesaid high-performance abrasion-proof rubber cushion, described machine oil is 46
#Machine oil.
Aforesaid high-performance abrasion-proof rubber cushion, described carbon black are N330 carbon black and N220 sooty mixture, and wherein N330 carbon black and N220 carbon black usage ratio are N330 carbon black 60%~80%, N220 carbon black 20%~40%.
Aforesaid high-performance abrasion-proof rubber cushion, described whipping agent are the AC-3000 whipping agents.
Aforesaid high-performance abrasion-proof rubber cushion, described promotor are DCP promotor.
Aforesaid high-performance abrasion-proof rubber cushion, described ethylene vinyl acetate are the mixtures of EVA-180 and EVA-600, and wherein the usage ratio of EVA-180 and EVA-600 is EVA-18025%~50%, EVA-60050%~75%.
Compared with prior art, the present invention has obtained following effect: with the ethylene vinyl acetate resin is main component, adopt proper raw material proportioning, the present invention possesses better wear resisting property, and in light weight, therefore, the sole wear resisting property excellence that the present invention makes, life-span is long, and is in light weight, comfortable and easy to wear; The high-performance abrasion-proof rubber cushion of making can be widely used in the workplace that wear resisting property is had requirement, thereby greatly improves the work-ing life of workpiece or equipment etc.
Embodiment
Embodiments of the invention 1: adopt conventional manufacture craft to make high-performance abrasion-proof rubber cushion with following materials of weight proportions, and in grinding tool, be hot pressed into sole.0.8 part of 7.5 parts of 3L natural rubbers, 3.5 parts of cis-butadiene cements, ethylene vinyl acetate 34 parts of (18012 parts of EVA, 60022 parts of EVA), 3 parts of fine particle calcium carbonates, carbon black 7 parts of (5 parts of N330 carbon blacks, 2 parts of N220 carbon blacks), 0.67 part of hard esters acid, 0.5 part of DCP promotor, 1.9 parts in zinc oxide, AC-3000 whipping agent, 46
#1 part in machine oil.This sole has the good wear resistance energy, has used the shoes of this sole, has prolonged work-ing life, and in light weight, comfortable and easy to wear.
Embodiments of the invention 2: adopt conventional manufacture craft to make high-performance abrasion-proof rubber cushion with following materials of weight proportions.0.9 part of 8.5 parts of 3L natural rubbers, 4.3 parts of cis-butadiene cements, ethylene vinyl acetate 40 parts of (24 parts of EVA-18016 part, EVA-600), 2.0 parts of fine particle calcium carbonates, carbon black 9 parts of (6 parts of N330 carbon blacks, 3 parts of N220 carbon blacks), 0.6 part of hard esters acid, 0.7 part of DCP promotor, 1.8 parts in zinc oxide, AC-3000 whipping agent, 46
#1.2 parts in machine oil.Be used for equipment, the bottom of furniture etc. prevents that the bottom surface from being swiped, and wear resisting property makes this mat big leap ahead in work-ing life, and in light weight.
Claims (7)
1. high-performance abrasion-proof rubber cushion, it is characterized in that: this high-performance abrasion-proof rubber cushion has the following materials of weight proportions of using, 7.0~8.7 parts of natural rubbers, 3.0~4.3 parts of cis-butadiene cements, 30~40 parts of ethylene-vinyl acetate copolymers, 2.0~3.5 parts of fine particle calcium carbonates, 5~9 parts of carbon blacks, 0.6~0.75 part of hard ester acid, 0.4~0.7 part of promotor, 1.8~2.0 parts in zinc oxide, 0.7~0.9 part of whipping agent, 0.8~1.2 part in machine oil adopt conventional manufacture craft to make.
2. high-performance abrasion-proof rubber cushion according to claim 1 is characterized in that: described natural rubber is the 3L natural rubber.
3. high-performance abrasion-proof rubber cushion according to claim 1 is characterized in that: described machine oil is 46# machine oil.
4. high-performance abrasion-proof rubber cushion according to claim 1, it is characterized in that: described carbon black is N330 carbon black and N220 sooty mixture, and wherein N330 carbon black and N220 carbon black usage ratio are N330 carbon black 60%~80%, N220 carbon black 20%~40%.
5. high-performance abrasion-proof rubber cushion according to claim 1 is characterized in that: described whipping agent is the AC-3000 whipping agent.
6. high-performance abrasion-proof rubber cushion according to claim 1 is characterized in that: described promotor is DCP promotor.
7. high-performance abrasion-proof rubber cushion according to claim 1, it is characterized in that: described ethylene-vinyl acetate copolymer is the mixture of EVA-180 and EVA-600, and wherein the usage ratio of EVA-180 and EVA-600 is EVA-180 25%~50%, EVA-600 50%~75%.