CN101096558A - UV varnish - Google Patents

UV varnish Download PDF

Info

Publication number
CN101096558A
CN101096558A CNA2006100362510A CN200610036251A CN101096558A CN 101096558 A CN101096558 A CN 101096558A CN A2006100362510 A CNA2006100362510 A CN A2006100362510A CN 200610036251 A CN200610036251 A CN 200610036251A CN 101096558 A CN101096558 A CN 101096558A
Authority
CN
China
Prior art keywords
varnish
grams
efka3034
uv7605b
efka3777
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2006100362510A
Other languages
Chinese (zh)
Inventor
袁春来
邓燕
马迎娜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitac Precision Technology Shunde Ltd
Original Assignee
Mitac Precision Technology Shunde Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitac Precision Technology Shunde Ltd filed Critical Mitac Precision Technology Shunde Ltd
Priority to CNA2006100362510A priority Critical patent/CN101096558A/en
Publication of CN101096558A publication Critical patent/CN101096558A/en
Pending legal-status Critical Current

Abstract

The invention discloses a UV varnish, which comprises the following parts: 25-45% monomer, 50-70% photographic resin, 4-7% photo-initiation agent, 0.7-1.7% adjuvant and 40-60% solvent, wherein the monomer consists of TMPTA and DPHA; the photographic resin is aliphatic PUA, which contains UV7605B and 621A-8; the photographic resin includes Irgacure184 and the adjuvant contains EFKA3777, EFKA3034 and OB (optical brightener); the solvent contains toluene and acetic ester. The invention matches high hardness resin and high hardness active diluent with OB to realize the uniformity of high hardness and low yellow changing rate, which reduces cost with good economic benefit.

Description

A kind of UV varnish
Technical field
The present invention relates to a kind of UV coating, particularly relate to a kind of UV varnish that is used for the application plastic bottom material.
Background technology
UV coating is to utilize uviolizing to produce chemical action and hardened coating, its main component is made up of photosensitive resin, reactive thinner, light trigger and auxiliary agent, this coating with high-octane UV-light as solidifying the energy, absorb ultraviolet luminous energy by the light trigger in the coating and form free radical, cause photosensitive resin and reactive thinner molecule, and then the generation chain polymerization, making films reaches curing.
UV coating has advantages such as curing speed is fast, energy-conservation, ambient cure, superior performance, environmental protection, ray velocity is fast on it, rete luminance brightness height, face firm surface heat-resisting, that can make ground in dry back is very bright, level and smooth, refractive power is effective, make ground produce the sense of intensive main body, be widely used in fields such as chemical industry, machinery, electronics, light industry, communication.Just because of these advantages make its application in recent years more and more widely, the high-tech high added value electronic product of fast development behind the UV Lacquer finish, looks that light is gorgeous beautiful more especially day by day, and therefore marketable value is also promoted greatly.
Plastic bottom material does not in the market have some obvious defects with UV varnish, and is high as: hardness, behind ultra violet lamp and the xanthochromia that causes etc.It is also big to become the high often caused xanthochromia of resin of connection density, makes UV varnish be difficult on high rigidity and the low-yellowing and unifies.
Summary of the invention
The object of the present invention is to provide a kind of UV varnish, the method that it adopts high hardness resin and high rigidity reactive thinner to arrange in pairs or groups is added white dyes OB simultaneously, to realize the system on high rigidity and the low-yellowing
For achieving the above object, UV varnish provided by the invention mainly comprises following component, and its content is expressed as with parts by weight:
Monomer 25~45
Photosensitive resin 50~70
Light trigger 4~7
Auxiliary agent 0.7~1.7
Solvent 40~60
Wherein, described monomer comprises TMPTA and DPHA etc.
Described photosensitive resin is aliphatics PUA, and it comprises UV7605B and 621A-80 etc.
Described light trigger comprises Irgacure184 etc.
Described auxiliary agent comprises EFKA3777, EFKA3034, white dyes OB etc.
Described solvent comprises toluene, ethyl acetate etc.
Therefore, the screening formulation of UV varnish of the present invention is expressed as with parts by weight:
TMPTA 10~20
DPHA 15~25
UV7605B 40~50
621A-80 10~20
Irgacure184 4~7
EFKA3777 0.5~1.0
EFKA3034 0.1~0.2
OB 0.1~0.5
Toluene 20~30
Ethyl acetate 20~30
UV varnish of the present invention mainly is applicable to the application plastic bottom material, and its superior performance has realized the unification on high rigidity and the low-yellowing, and its cost is lower, has considerable economic.
Embodiment
Embodiment 1
By following set of dispense side all raw materials are mixed dissolving:
TMPTA 20 grams
DPHA 15 grams
UV7605B 40 grams
621A-80 15 grams
Irgacure184 5 grams
EFKA3777 1.0 grams
EFKA3034 0.2 gram
OB 0.5 gram
Toluene 25 grams
Ethyl acetate 25 grams
Then it is sprayed on the plastic basis material, adopts the 1KW high voltage mercury lamp to solidify with the UV-irradiation of 80W.cm-1 illumination, adopt relatively this base material spraying front and back aberration of color difference meter then, the gained result is:
Figure A20061003625100041
L=-1.095;
Figure A20061003625100042
a=0.021?
Figure A20061003625100043
b=0.207;
Figure A20061003625100044
E=1.115。And then it is filmed carries out the test of hardness and sticking power, its result is respectively its pencil hardness be 2H and do not have impression, none lattice of hundred lattice separately peel off.
Embodiment 2
By following set of dispense side all raw materials are mixed dissolving:
TMPTA 15 grams
DPHA 15 grams
UV7605B 45 grams
621A-80 10 grams
Irgacure184 4 grams
EFKA3777 0.5 gram
EFKA3034 0.2 gram
OB 0.5 gram
Toluene 25 grams
Ethyl acetate 25 grams
Then it is sprayed on the plastic basis material, adopts the 1KW high voltage mercury lamp to solidify with the UV-irradiation of 80W.cm-1 illumination, adopt relatively this base material spraying front and back aberration of color difference meter then, the gained result is:
Figure A20061003625100051
L=-0.891;
Figure A20061003625100052
A=0.015
Figure A20061003625100053
B=0.371; E=0.965.And then it is filmed carries out the test of hardness and sticking power, its result is respectively its pencil hardness be 2H and do not have impression, none lattice of hundred lattice separately peel off.
Embodiment 3
By following set of dispense side all raw materials are mixed dissolving:
TMPTA 20 grams
DPHA 15 grams
UV7605B 40 grams
621A-80 20 grams
Irgacure184 5 grams
EFKA3777 1.0 grams
EFKA3034 0.2 gram
OB 0.5 gram
Toluene 25 grams
Ethyl acetate 25 grams
Then it is sprayed on the plastic basis material, adopts the 1KW high voltage mercury lamp to solidify with the UV-irradiation of 80W.cm-1 illumination, adopt relatively place near the steps base material spraying front and back aberration of color difference meter then, the gained result is:
Figure A20061003625100055
L=-1.147; A=0.057
Figure A20061003625100057
B=0.281;
Figure A20061003625100058
E=1.182.And then it is filmed carries out the test of hardness and sticking power, its result is respectively its pencil hardness be 2H and do not have impression, none lattice of hundred lattice separately peel off.

Claims (7)

1. UV varnish, this varnish mainly comprises following component, its content is expressed as with parts by weight:
Monomer 25~45;
Photosensitive resin 50~70;
Light trigger 4~7;
Auxiliary agent 0.7~1.7;
Solvent 40~60.
2. UV varnish according to claim 1 is characterized in that described monomer comprises TMPTA and DPHA.
3. UV varnish according to claim 1 is characterized in that, described photosensitive resin is aliphatics PUA, and it comprises UV7605B and 621A-80.
4. UV varnish according to claim 1 is characterized in that, described light trigger is Irgacure184.
5. UV varnish according to claim 1 is characterized in that, described auxiliary agent comprises EFKA3777, EFKA3034 and white dyes OB.
6. UV varnish according to claim 1 is characterized in that described solvent comprises toluene and ethyl acetate.
7. according to the described UV varnish of claim 1-6, it is characterized in that the screening formulation of this UV varnish is expressed as with parts by weight:
TMPTA 10~20;
DPHA 15~25;
UV7605B 40~50;
621A-80 10~20;
Irgacure184?4~7;
EFKA3777 0.5~1.0;
EFKA3034 0.1~0.2;
OB 0.1~0.5;
Toluene 20~30;
Ethyl acetate 20~30.
CNA2006100362510A 2006-06-30 2006-06-30 UV varnish Pending CN101096558A (en)