CN101078180A - Antibiotic radiation proof treatment method for fabric and clothes - Google Patents
Antibiotic radiation proof treatment method for fabric and clothes Download PDFInfo
- Publication number
- CN101078180A CN101078180A CN 200610081487 CN200610081487A CN101078180A CN 101078180 A CN101078180 A CN 101078180A CN 200610081487 CN200610081487 CN 200610081487 CN 200610081487 A CN200610081487 A CN 200610081487A CN 101078180 A CN101078180 A CN 101078180A
- Authority
- CN
- China
- Prior art keywords
- clothes
- fabric
- solution
- radiation proof
- mixed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention provides a antibacterial and radiation protection processing method for the textile and clothing, it can realize as follows, adding 10%-20% CuSO4 and 2%-4% AgNO3 to the water solution to get the mixture, getting some cell polysaccharide to the acetum to get the concentration of 0.003-0.01g/ml mixture, then mixing the two mixture as the ratio 1:3-3:1, at last adding 2-6% dispersant. The pH value of the solution is 3.5-4.5 by the sodium hydrate and acetum. The textile or clothing can be infused into the mixture for 20-60min, then put into the high temperature stream room for 15-20min at 80-100deg.C, at last the clothing or textile was washed, dehydrated and dried to get the complex antibacterial textile and clothing. The processing clothing and textile has stronger antibacterial and radiation protection function, and it is good for the health of human body.
Description
Technical field:
The present invention relates to the processing method of a kind of fabric and clothes thereof, is a kind of processing method with fabric and clothes of antibiotic radiation proof function specifically.
Background technology:
Along with the development of application of electronic technology, increasing electromagnetic radiation appears in the living environment, such as mobile phone, computer etc., and people's health is caused increasing harm.On the other hand, along with increasing the weight of of environmental pollution, procreation of bacterium and propagation are also threatening human life day by day.Bacterium and radiation have become in people's daily life two harm greatly to health.Clothes are more and more shouldered the important task that the protection health is avoided encroaching on as the first road barrier with human body and environment isolation.Along with development of science and technology, multiple antibiotic radiation proof technology begins to occur, and uses in various fields, but since people to the clothes comfortableness, requirements such as portability, and clothes need the often characteristic of washing cause the raising of the difficulty that antibiotic anti-spoke technology uses.
Goal of the invention:
The bright antibiotic radiation proof treatment method that aims to provide a kind of fabric and clothes of this law is applicable to soft materials such as fabric and clothes, and fabric of handling and clothes have stronger antibiotic radiation proof effect, help human body health.
Summary of the invention:
The present invention is achieved through the following channels, and the processing method of a kind of fabric and clothes antibiotic radiation proof comprises the steps:
1, the silver nitrate stirring and dissolving that adds copper sulphate, the 2%-4% of 10%-20% in the aqueous solution makes copper sulphate and silver nitrate makes mixed solution.Get an amount of shitosan and be dissolved in the dilute acetic acid solution mixing, being mixed with concentration is the shitosan dilute acetic acid solution of 0.003-0.01g/ml.The solution of producing is pacified 1: 3-3: 1 mixed.The dispersant that adds 2-6% at mixed liquor.Regulate ph value of mixture to 3.5-4.5 by sodium hydroxide solution and spirit of vinegar.
2, fabric and clothes are immersed in the mixed liquor, soaked 20-60 minute, put into the high-temperature vapour chamber and under the 80-100 degree, fumigated 15-20 minute.
3, will fumigate obtain fabric and clothes wash, dewater, dry acquisition composite antibiosis fabric and clothes.
Aforesaid fabric and clothes antibiotic radiation proof treatment method is characterized in that described dispersant is polyvinylether and methyl trichlorosilane.
Aforesaid fabric and clothes antibiotic radiation proof treatment method, the finishing agent of adding fabric weight 80%-100% in the immersion process
The specific embodiment:
Below in conjunction with example the specific embodiment of this patent of invention is described, but not as the qualification to this summary of the invention.
Embodiment 1
The processing method of a kind of fabric and clothes antibiotic radiation proof comprises the steps:
1, in the aqueous solution, add 10% copper sulphate, 2% silver nitrate stirring and dissolving makes copper sulphate and silver nitrate makes mixed solution.Get an amount of shitosan and be dissolved in the dilute acetic acid solution mixing, being mixed with concentration is the shitosan dilute acetic acid solution of 0.005g/ml.With 1: 3 the mixed of producing of solution peace.Polyethylene of dispersing agent ether and methyl trichlorosilane in mixed liquor adding 2%.Regulate ph value of mixture to 3.5 by sodium hydroxide solution and spirit of vinegar.
2, fabric and clothes are immersed in the mixed liquor, the finishing agent that adds fabric weight 80% in the immersion process soaked 30 minutes, put into the high-temperature vapour chamber and fumigated 15 minutes under 80 degree.
3, will fumigate obtain fabric and clothes wash, dewater, dry acquisition composite antibiosis fabric and clothes.
Embodiment 2
The processing method of a kind of fabric and clothes antibiotic radiation proof comprises the steps:
1, in the aqueous solution, add 15% copper sulphate, 3% silver nitrate stirring and dissolving makes copper sulphate and silver nitrate makes mixed solution.Get an amount of shitosan and be dissolved in the dilute acetic acid solution mixing, being mixed with concentration is the shitosan dilute acetic acid solution of 0.0081g/ml.With 1: 1 the mixed of producing of solution peace.Polyethylene of dispersing agent ether and methyl trichlorosilane in mixed liquor adding 4%.Regulate ph value of mixture to 4 by sodium hydroxide solution and spirit of vinegar.
2, fabric and clothes are immersed in the mixed liquor, the finishing agent that adds fabric weight 90% in the immersion process soaked 50 minutes, put into the high-temperature vapour chamber and fumigated 20 minutes under 90 degree.
3, will fumigate obtain fabric and clothes wash, dewater, dry acquisition composite antibiosis fabric and clothes.
Embodiment 3
The processing method of a kind of fabric and clothes antibiotic radiation proof comprises the steps:
1, in the aqueous solution, add 20% copper sulphate, 4% silver nitrate stirring and dissolving makes copper sulphate and silver nitrate makes mixed solution.Get an amount of shitosan and be dissolved in the dilute acetic acid solution mixing, being mixed with concentration is the shitosan dilute acetic acid solution of 0.01g/ml.With 3: 1 the mixed of producing of solution peace.Polyethylene of dispersing agent ether and methyl trichlorosilane in mixed liquor adding 6%.Regulate ph value of mixture to 4.5 by sodium hydroxide solution and spirit of vinegar.
2, fabric and clothes are immersed in the mixed liquor aforesaid fabric and clothes antibiotic radiation proof treatment method, the finishing agent of adding fabric weight 100% in the immersion process.Soaked 60 minutes, and put into the high-temperature vapour chamber and under 100 degree, fumigated 20 minutes.
3, will fumigate obtain fabric and clothes wash, dewater, dry acquisition composite antibiosis fabric and clothes.
Claims (3)
1, the processing method of a kind of fabric and clothes antibiotic radiation proof comprises the steps:
1) the silver nitrate stirring and dissolving that adds copper sulphate, the 2%-4% of 10%-20% in the aqueous solution makes copper sulphate and silver nitrate makes mixed solution.Get an amount of shitosan and be dissolved in the dilute acetic acid solution mixing, being mixed with concentration is the shitosan dilute acetic acid solution of 0.003-0.01g/ml.The solution of producing is pacified 1: 3-3: 1 mixed.The dispersant that adds 2-6% at mixed liquor.Regulate ph value of mixture to 3.5-4.5 by sodium hydroxide solution and spirit of vinegar.
2) fabric and clothes are immersed in the mixed liquor, soaked 20-60 minute, put into the high-temperature vapour chamber and under the 80-100 degree, fumigated 15-20 minute.
3) will fumigate obtain fabric and clothes wash, dewater, dry acquisition composite antibiosis fabric and clothes.
2, fabric according to claim 1 and clothes antibiotic radiation proof treatment method is characterized in that described dispersant is polyvinylether and methyl trichlorosilane.
3, fabric according to claim 1 and clothes antibiotic radiation proof treatment method is characterized in that in the immersion process adding the finishing agent of fabric and clothes weight 80%-100%.