CN101062769A - Artificial diamond purification technique - Google Patents
Artificial diamond purification technique Download PDFInfo
- Publication number
- CN101062769A CN101062769A CN 200710054425 CN200710054425A CN101062769A CN 101062769 A CN101062769 A CN 101062769A CN 200710054425 CN200710054425 CN 200710054425 CN 200710054425 A CN200710054425 A CN 200710054425A CN 101062769 A CN101062769 A CN 101062769A
- Authority
- CN
- China
- Prior art keywords
- diamond
- acid
- ball milling
- graphite
- sulfuric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a process to purify diamond, which comprises the following steps: grinding diamond synthesized block into particles; putting into autoclave; adding into the water solution of sulfuric acid or azotic acid or alcaine with density at 10-20%; reacting at normal temperature for 36-48 h; stripping metal; balling; sluicing; clearing black lead; drying; getting the purified diamond. This method does not use concentrated nitric sulfuric mixed acid and can eliminate a good deal of yellow acid mist, which can improve the safety in industrial process.
Description
Technical field
The invention belongs to the synthetic purification techniques field of superhard material, is a kind of artificial diamond purification technique.
Background technology
In technique known, purification for superhard materials such as powder method diamond synthesis piece or cubic boron nitrides, generally adopt the nitric-sulfuric acid reaction method of high density, utilize the strong oxidizing property and the impurity reactions such as metal in the superhard material and graphite of nitric-sulfuric acid, reach the purpose that removal of impurities is purified.There is the problem of following several respects in this processing method:
1, contained metal and strong acid form surface passivation easily in the diamond synthesis block in reaction process, need react → ball milling → elutriations → more than ten cyclical operation processes repeatedly such as reaction, take a lot of work, time-consuming, take and expect.
2, contained impurity such as graphite also are to remove by the oxidizing reaction of nitric-sulfuric acid in the diamond synthesis block, therefore, need to consume a large amount of concentrated nitric acid and the vitriol oil.
3, in whole synthetic purification process, the Qu Yunong nitric-sulfuric acid participates in reaction, produces the yellow waste gas of a large amount of nitre sulfuric acid, and production environment and atmospheric environment are caused severe contamination, poisons HUMAN HEALTH, easily the operator is worked the mischief, even leads to the accident of burning.
4, discharge a large amount of spent acid solutions, severe contamination soil property, water quality, cost of sewage disposal height behind diamond synthesis block and the concentrated acid reaction.
Summary of the invention
The purpose of this invention is to provide and a kind ofly can avoid environmental pollution, reduce the artificial diamond purification technique of raw materials consumption and cost of labor.
Realize that the technical scheme that purpose of the present invention is taked is: undertaken by following purifying technique step:
(1) fragmentation: it is the particle that is not more than 2mm that diamond synthesis block is broken into particle diameter;
(2) reaction removes metal: the ground grains material is put into reactor, add then in the sulfuric acid or nitric acid or aqueous hydrochloric acid of 10～20% concentration, the weight proportion of feed liquid is a material: sulfuric acid liquid or nitric acid liquid or hydrochloric acid solution=and 1: 5, reacted at normal temperatures 36～48 hours, waste reaction solution is emitted, take out reaction mass;
(3) ball milling: reaction mass was added in the ball mill ball milling 2～3 hours, and ball, material were by 2: 1 weight proportion;
(4) eluriate clear graphite: the material behind the ball milling is eluriated clean Ex-all graphite extremely fully with clear water, draw wet diamond;
(5) oven dry: will eluriate clean diamond and put into baking oven and dry, the taking-up sorting of sieving promptly gets high purity diamond finished product.
Because contained metal, graphite and diamond is equally distributed on substantially in the diamond synthesis block, by adopting the metal reaction in dilute sulphuric acid or rare nitric acid or dilute hydrochloric acid and the synthetic piece, remove the metal in the synthetic piece earlier, remaining diamond and graphite will be fluffy naturally, by ball milling, elutriation, remove graphite, the diamond after obtaining purifying.The chemical formula of reaction is: M+2H
+→ M
2++ H
2In the present invention, because to the diamond synthesis block employing is dilute sulphuric acid or rare nitric acid or dilute hydrochloric acid reaction, these diluted acids and graphite do not react substantially, can effectively reduce purification process Central Plains material usage thus, and dilute sulphuric acid or rare nitric acid or dilute hydrochloric acid do not have volatility basically, acid mist can be do not produced, pollution can be eliminated environment.
According to processing method of the present invention the synthetic piece of man-made diamond is purified, its beneficial effect is: can eliminate fully and adopt a large amount of yellow acid mist that produces in the dense nitric-sulfuric acid production process, eliminate the pollution of purification process to environment.And in the purification process, only need carry out ball milling, eluriate operation, circulating reaction, ball milling, elutriation repeatedly, compared with prior art, processing method of the present invention reduces with the acid amount more than 70% than original method, reduce artificial consumption more than 50%, and do not use the vitriol oil, concentrated nitric acid, can improve the security of production process greatly.
Embodiment
Man-made diamond method of purification of the present invention is: diamond synthesis block is broken for the particle that particle diameter is not more than 2mm, put into reactor, add then in the sulfuric acid or nitric acid or aqueous hydrochloric acid of 10～20% concentration, the feed liquid weight ratio is a material: sulfuric acid liquid or nitric acid liquid or hydrochloric acid solution=and 1: 5, reacted at normal temperatures 36～48 hours, the metal in the synthetic material is peeled off fully, enter in sulfuric acid liquid or nitric acid liquid or the hydrochloric acid solution, the venting spent acid solution takes out reaction mass then.Dispeling of graphite is in the diamond synthesis block: reaction mass was added in the ball mill ball milling 2～3 hours, and ball, material weight ratio are 2: 1; Material behind the taking-up ball milling is eluriated with clear water, and the graphite in the Ex-all material draws wet diamond; The diamond that will wet is at last put into baking oven dries, and the sorting of sieving promptly gets the high purity diamond.
Embodiment 1
Processing method according to above-mentioned diamond synthesis is purified is broken into small-particle with diamond synthesis block earlier, puts into reactor, adds sulfuric acid or the nitric acid or the aqueous hydrochloric acid of 10% concentration, reacts at normal temperatures 48 hours, removes metal.Take out reaction mass then, remove graphite through ball milling, elutriation, the sorting of sieving after the oven dry promptly gets the diamond finished product.
Embodiment 2
Processing method according to above-mentioned diamond synthesis is purified is broken into small-particle with diamond synthesis block earlier, puts into reactor, adds sulfuric acid or the nitric acid or the aqueous hydrochloric acid of 15% concentration, reacts at normal temperatures 42 hours, removes metal.Take out reaction mass then, remove graphite through ball milling, elutriation, the sorting of sieving after the oven dry promptly gets the diamond finished product.
Embodiment 3
Processing method according to above-mentioned diamond synthesis is purified is broken into small-particle with diamond synthesis block earlier, puts into reactor, adds sulfuric acid or the nitric acid or the aqueous hydrochloric acid of 20% concentration, reacts at normal temperatures 40 hours, removes metal.Take out reaction mass then, remove graphite through ball milling, elutriation, the sorting of sieving after the oven dry promptly gets the diamond finished product.
Claims (1)
1, a kind of artificial diamond purification technique, it is characterized in that: it comprises the following steps:
(1) fragmentation: it is the particle that is not more than 2mm that diamond synthesis block is broken into particle diameter;
(2) reaction removes metal: the ground grains material is put into reactor, add then in the sulfuric acid or nitric acid or aqueous hydrochloric acid of 10～20% concentration, the weight proportion of feed liquid is a material: sulfuric acid liquid or nitric acid liquid or hydrochloric acid solution=and 1: 5, reacted at normal temperatures 36～48 hours, waste reaction solution is emitted, take out reaction mass;
(3) ball milling; Reaction mass was added in the ball mill ball milling 2～3 hours, and ball, material were by 2: 1 weight proportion;
(4) eluriate clear graphite: the material behind the ball milling is eluriated clean Ex-all graphite extremely fully with clear water, draw wet diamond;
(5) oven dry: will eluriate clean diamond and put into baking oven and dry, the taking-up sorting of sieving promptly gets high purity diamond finished product.