CN101041460A - Method for preparation of nano titanium dioxide micro latex - Google Patents
Method for preparation of nano titanium dioxide micro latex Download PDFInfo
- Publication number
- CN101041460A CN101041460A CN 200710011154 CN200710011154A CN101041460A CN 101041460 A CN101041460 A CN 101041460A CN 200710011154 CN200710011154 CN 200710011154 CN 200710011154 A CN200710011154 A CN 200710011154A CN 101041460 A CN101041460 A CN 101041460A
- Authority
- CN
- China
- Prior art keywords
- titanium dioxide
- nano titanium
- cosurfactant
- microemulsion
- hexyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a chemical materials preparing method of nanometer titanium oxide microemulsion, which comprises the following steps: setting TrionX-100 as surface activator; making cyclohexane as oil phase; choosing miscible liquids of regular butyl alcohol and regular hexyl alcohol as cosurfactant; making bulk factor of cosurfactant regular butyl alcohol and regular hexyl alcohol at 0.8:1. The invention emphasizes composition and proportion, which can drop cost.
Description
Technical field
The present invention relates to a kind of preparation method of industrial chemicals, particularly relate to a kind of method for preparing nano titanium dioxide micro latex.
Background technology
Current preparation nano titanium oxide (TiO
2) method numerous, but big multi-method can cause the material partial concn too high, easily reunite or shortcomings such as the reactor pattern has higher requirements are developed be restricted.Advantages such as micro-emulsion method for preparing nano titanium dioxide is simple to operate with it, size is controlled, particle good dispersity and receiving much concern.Microemulsion generally is divided into two kinds of w/o types and O/W type, and the w/o type microemulsion is meant that with water-fast organic solvent be dispersion medium, and water is the dispersion system of disperse phase, and its dispersed phase distribution is even, transparent, each homogeny owing to the existence of tensio-active agent makes.The disperse phase of w/o type microemulsion " pond " is a kind of special nanometer (nm) space, and its size can be controlled at several nanometers to tens nanometers, and yardstick is little and separated from one another, is the ideal reactor, can obtain the controlled nanoparticle of particle diameter as reactor.Therefore can micro-emulsion method for preparing nano titanium dioxide key of success be configure the stable microemulsion liquid system, and its stable range is the bigger the better.Shi Liyi etc. are that tensio-active agent, hexanaphthene are that oil phase, n-hexyl alcohol are cosurfactant, titanium tetrachloride (TiCl with Triton X-100 (TrionX-100)
4) prepared in reaction nano-TiO
2, obtaining 25nm anatase titanium dioxide powder 650 ℃ of calcinings, 1000 ℃ of calcinings obtain 54nm nano rutile-type powder.The used n-hexyl alcohol price of this method is more expensive, and the cost height is unfavorable for producing in enormous quantities.Therefore the popularization of method is restricted.
Summary of the invention
The object of the present invention is to provide and a kind ofly prepare nano titanium oxide from microemulsion system, lay particular emphasis on the composition and the proportioning of this microemulsion system, compare with existing microemulsion system, the present invention can reduce cost, and the gained microemulsion system also can be prepared the fine nano titanium oxide simultaneously.
The objective of the invention is to be achieved through the following technical solutions:
A kind of method for preparing nano titanium dioxide micro latex is that tensio-active agent, hexanaphthene are oil phase with TrionX-100, and the mixed solution of having selected propyl carbinol and n-hexyl alcohol for use is as cosurfactant; The compound method of its microemulsion is: the proportioning of cosurfactant propyl carbinol and n-hexyl alcohol is 0.8: 1 volume ratio.
Advantage of the present invention and effect are:
For reducing cost, the gained microemulsion system also can be prepared the fine nano titanium oxide during batch process, the mixed solution that adopts propyl carbinol and n-hexyl alcohol is as cosurfactant, and the propyl carbinol price is about n-hexyl alcohol half, thereby can reduce cost greatly.
Embodiment
Below the present invention is described in detail.
Present method adopts the mixed solution of propyl carbinol and n-hexyl alcohol as cosurfactant, TrionX-100 is that tensio-active agent, hexanaphthene are that oil phase has prepared the stable microemulsion liquid system: get 5 milliliters of hexanaphthenes (ml), water 15ml, TrionX-100 5ml, mix, under ultrasonic concussion to propyl carbinol that wherein drips 0.8: 1 (volume ratio) and n-hexyl alcohol mixed solution, until certain unexpected clear in a flash.Under the magnetic agitation of gentleness, with a certain amount of TiCl
4Slowly splash in the above-mentioned microemulsion, microemulsion gradually becomes translucent until white opacity occurring by clear, after fully stirring 4～5 hours again, the mixed solution that adds acetone-water, separate static a moment, takes supernatant liquor away, use acetone repetitive scrubbing throw out again, suction filtration obtains colourless spawn, 70 ℃ of following vacuum-dryings 12 hours, obtains hydration TiO then
2, for buff powder (presoma), again the presoma that obtains is placed muffle furnace, 550 ℃ of following roastings 4 hours, obtain the anatase type nano TiO of complete in crystal formation
2Powder.Its specific performance index and liquid state and solid-state sample are seen accompanying drawing (the strict GB GB/T 19591-2004 standard of carrying out of detection method).A kind of compound method of novel cheap microemulsion in the micro-emulsion method for preparing nano titanium dioxide.It is with TrionX-100 be tensio-active agent, hexanaphthene be the propyl carbinol of oil phase, 0.8: 1 (volume ratio) and n-hexyl alcohol mixed solution as cosurfactant, successfully make the stable microemulsion liquid system.Utilize this microemulsion to adopt literature method can prepare the nanometer titanium dioxide body that meets national standard.
The performance index of microemulsion gained nano titanium oxide
| Item compared | Performance index | |
| GB | This experiment product | |
| Titanium dioxide massfraction/% Electronic Speculum median size/nm≤specific surface area/(m 2/ g) mass fraction/% of reunion index≤moisture≤pH value bulk density≤ | 90 100 90 100 2 6～8 0.5 | 95 50 55 80 1.2 7.4 0.74 |
Claims (1)
1. a method for preparing nano titanium dioxide micro latex is characterized in that with TrionX-100 being that tensio-active agent, hexanaphthene are oil phase, and the mixed solution of having selected propyl carbinol and n-hexyl alcohol for use is as cosurfactant; The compound method of its microemulsion is: the proportioning of cosurfactant propyl carbinol and n-hexyl alcohol is 0.8: 1 volume ratio.