CN101029462A - Method for penetrating and coating ink-jet printing material - Google Patents
Method for penetrating and coating ink-jet printing material Download PDFInfo
- Publication number
- CN101029462A CN101029462A CN 200710063661 CN200710063661A CN101029462A CN 101029462 A CN101029462 A CN 101029462A CN 200710063661 CN200710063661 CN 200710063661 CN 200710063661 A CN200710063661 A CN 200710063661A CN 101029462 A CN101029462 A CN 101029462A
- Authority
- CN
- China
- Prior art keywords
- coating
- paper
- color
- ink
- silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
The contrast scope (density) of rice paper | ||||||||
C | M | Y | K | |||||
Rice paper | Be not coated with | Be coated with | Be not coated with | Be coated with | Be not coated with | Be coated with | Be not coated with | Be coated with |
0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 |
3.00 | 0.01 | 0.03 | 0.02 | 0.03 | 0.04 | 0.01 | 0.04 | 0.03 |
7.00 | 0.06 | 0.07 | 0.07 | 0.06 | 0.10 | 0.08 | 0.08 | 0.08 |
10.00 | 0.08 | 0.09 | 0.08 | 0.09 | 0.12 | 0.11 | 0.11 | 0.11 |
15.00 | 0.13 | 0.15 | 0.14 | 0.15 | 0.16 | 0.16 | 0.18 | 0.18 |
20.00 | 0.19 | 0.20 | 0.19 | 0.19 | 0.21 | 0.21 | 0.24 | 0.24 |
25.00 | 0.24 | 0.24 | 0.25 | 0.26 | 0.26 | 0.26 | 0.31 | 0.30 |
30.00 | 0.28 | 0.30 | 0.30 | 0.30 | 0.30 | 0.30 | 0.37 | 0.37 |
40.00 | 0.38 | 0.42 | 0.44 | 0.42 | 0.37 | 0.39 | 0.51 | 0.50 |
50.00 | 0.47 | 0.52 | 0.54 | 0.51 | 0.43 | 0.47 | 0.61 | 0.62 |
60.00 | 0.57 | 0.64 | 0.65 | 0.65 | 0.52 | 0.57 | 0.72 | 0.76 |
70.00 | 0.68 | 0.76 | 0.74 | 0.76 | 0.58 | 0.69 | 0.78 | 0.94 |
80.00 | 0.79 | 0.92 | 0.87 | 0.93 | 0.73 | 0.92 | 0.87 | 1.16 |
90.00 | 0.94 | 1.13 | 0.99 | 1.11 | 0.97 | 1.33 | 0.91 | 1.42 |
95.00 | 1.04 | 1.33 | 1.03 | 1.28 | 1.06 | 1.43 | 0.99 | 1.60 |
100.00 | 1.13 | 1.34 | 1.17 | 1.25 | 1.31 | 1.45 | 1.09 | 1.63 |
C | M | |||||||||||
Rice paper | Be not coated with | Be coated with | Be not coated with | Be coated with | ||||||||
L | a | b | L | a | b | L | a | b | L | a | b | |
0 | 92.1 | 0.1 | 7.0 | 94.5 | 1.4 | -0.9 | 92.1 | 0.1 | 7.0 | 94.5 | 1.4 | -0.9 |
3 | 91.5 | -1.7 | 5.0 | 93.5 | 0.1 | -2.8 | 91.1 | 2.9 | 5.5 | 92.7 | 3.9 | -2.7 |
7 | 89.8 | -4.4 | 2.5 | 91.7 | -2.1 | -5.6 | 87.1 | 6.5 | 3.3 | 91.2 | 7.4 | -3.6 |
10 | 88.7 | -6.3 | 0.8 | 90.5 | -3.9 | -6.7 | 87.5 | 9.2 | 2.6 | 89.8 | 10.0 | -5.0 |
15 | 86.7 | -9.1 | -1.9 | 88.7 | -6.9 | -9.7 | 85.3 | 14.6 | -0.6 | 86.9 | 15.4 | -6.5 |
20 | 85.2 | -12.1 | -5.3 | 86.3 | -9.4 | -12.8 | 81.6 | 18.5 | -2.6 | 84.7 | 19.6 | -7.9 |
25 | 83.5 | -14.7 | -7.9 | 84.4 | -11.8 | -15.3 | 75.2 | 22.7 | -4.5 | 81.5 | 24.0 | -9.8 |
30 | 81.8 | -166 | -10.5 | 81.3 | -13.6 | -18.0 | 78.0 | 28.3 | -6.1 | 79.6 | 27.8 | -9.9 |
40 | 77.8 | -210 | -15.9 | 78.6 | -17.6 | -23.5 | 72.5 | 37.1 | -8.4 | 74.8 | 35.9 | -11.4 |
50 | 75.0 | -23.2 | -19.7 | 74.8 | -19.3 | -28.1 | 68.9 | 41.7 | -8.6 | 71.3 | 40.9 | -11.2 |
60 | 71.4 | -25.1 | -24.5 | 70.7 | -21.4 | -32.5 | 65.0 | 47.2 | -9.0 | 66.8 | 47.1 | -11.4 |
70 | 67.8 | -25.9 | -28.6 | 65.6 | -22.1 | -36.2 | 62.1 | 50.4 | -8.4 | 63.2 | 52.1 | -11.0 |
80 | 64.2 | -26.1 | -33.2 | 62.9 | -22.6 | -41.2 | 58.7 | 53.6 | -7.4 | 59.0 | 56.3 | -9.1 |
90 | 59.9 | -24.6 | -36.9 | 57.7 | -22.0 | -44.8 | 55.9 | 56.2 | -5.6 | 54.8 | 60.2 | -6.9 |
95 | 56.7 | -231 | -38.3 | 52.8 | -20.0 | -47.9 | 53.9 | 56.9 | -4.2 | 52.0 | 61.4 | -4.2 |
100 | 53.4 | -19.7 | -41.7 | 52.6 | -19.3 | -47.8 | 51.5 | 56.6 | -2.3 | 51.5 | 61.2 | -3.7 |
Y | K | |||||||||||
Rice paper | Be not coated with | Be coated with | Be not coated with | Be coated with | ||||||||
L | a | b | L | a | b | L | a | b | L | a | b | |
0 | 92.1 | 0.1 | 7.0 | 94.5 | 1.4 | -0.9 | 92.1 | 0.1 | 7.0 | 94.5 | 1.4 | -0.9 |
3 | 92.6 | -1.0 | 11.1 | 94.0 | 0.9 | 0.3 | 89.1 | 0.0 | 8.7 | 92.3 | 2.4 | -1.1 |
7 | 92.3 | -1.9 | 16.6 | 93.5 | -0.6 | 8.4 | 86.0 | -0.5 | 8.7 | 87.3 | 1.2 | 0.9 |
10 | 92.3 | -2.4 | 18.8 | 94.0 | -1.4 | 11.0 | 83.9 | -1.2 | 7.7 | 86.1 | 1.0 | 0.6 |
15 | 92.0 | -3.2 | 22.8 | 93.7 | -2.4 | 16.7 | 79.3 | -0.4 | 6.5 | 81.1 | 1.9 | 0.2 |
20 | 91.9 | -3.8 | 27.5 | 93.5 | -3.7 | 22.0 | 74.0 | -1.1 | 5.9 | 77.1 | 0.8 | 0.1 |
25 | 91.7 | -4.5 | 31.8 | 93.4 | -4.0 | 26.3 | 70.4 | -0.6 | 5.1 | 73.1 | 1.9 | -1.1 |
30 | 90.3 | -4.9 | 33.5 | 93.3 | -4.8 | 30.6 | 67.1 | -0.7 | 4.1 | 69.0 | 2.4 | -1.5 |
40 | 91.6 | -5.7 | 41.4 | 93.0 | -5.8 | 38.0 | 59.5 | 0.3 | 2.6 | 62.2 | 2.6 | -2.5 |
50 | 91.0 | -6.0 | 46.2 | 92.6 | -6.3 | 44.0 | 54.4 | 0.8 | 0.9 | 56.0 | 2.5 | -2.3 |
60 | 91.1 | -6.5 | 52.0 | 92.4 | -6.9 | 51.2 | 50.3 | 0.6 | 0.6 | 49.6 | 3.3 | -2.6 |
70 | 90.3 | -6.4 | 57.0 | 91.8 | -7.1 | 59.0 | 47.3 | 0.0 | 0.7 | 43.7 | 3.9 | -2.5 |
80 | 90.2 | -6.5 | 63.8 | 91.3 | -6.9 | 70.6 | 44.5 | 0.5 | 0.4 | 37.6 | 3.8 | 0.2 |
90 | 90.1 | -6.0 | 74.9 | 90.4 | -4.7 | 86.3 | 41.6 | -1.7 | 2.0 | 31.6 | 3.8 | 3.3 |
95 | 89.5 | -5.0 | 78.3 | 90.2 | -4.0 | 88.5 | 40.4 | -1.0 | 2.3 | 28.9 | 3.4 | 1.8 |
100 | 89.1 | -3.1 | 85.4 | 90.1 | -4.0 | 88.7 | 36.8 | -2.5 | 2.5 | 28.1 | 3.7 | 1.7 |
C | M | Y | K | X | Y | Z | L | a | | |||
G | 2A9 | |||||||||||
100 | 0 | 100 | 0 | 11.64 | 18.47 | 9.71 | 50.06 | -37.61 | 15.89 | |||
| 2Q9 | 0 | 0 | 100 | 0 | 67.36 | 71.81 | 9.45 | 87.88 | -4.1 | 81.96 | |
| S1 | 0 | 100 | 100 | 0 | 30.68 | 20.24 | 7.85 | 52.1 | 47.79 | 26.1 | |
| 2R9 | 0 | 100 | 0 | 0 | 30.96 | 18.99 | 17.34 | 50.68 | 54.98 | -3.96 | |
B | 119 | 100 | 100 | 0 | 0 | 11.4 | 10.3 | 19.03 | 38.38 | 11.03 | -28.91 | |
| 2S9 | 100 | 0 | 0 | 0 | 16.78 | 21.07 | 43.43 | 53.03 | -18.35 | -42 | |
G | 2A9 | 100 | 0 | 100 | 0 | 11.64 | 18.47 | 9.71 | 50.06 | -37.61 | 15.89 |
C | M | Y | K | X | Y | Z | L | a | | |||
G | 2A9 | |||||||||||
100 | 0 | 100 | 0 | 8.49 | 15.01 | 6.83 | 45.65 | -43.29 | 19.11 | |||
| 2Q9 | 0 | 0 | 100 | 0 | 66.83 | 71.63 | 8.73 | 87.79 | -4.88 | 84.34 | |
| S1 | 0 | 100 | 100 | 0 | 28.68 | 17.22 | 5.21 | 48.53 | 55.62 | 31.61 | |
| 2R9 | 0 | 100 | 0 | 0 | 31.43 | 18.03 | 18.65 | 49.53 | 61.65 | -8.86 | |
| I19 | 100 | 100 | 0 | 0 | 7.78 | 6.06 | 15.78 | 29.57 | 19.62 | -36.67 | |
| 2S9 | 100 | 0 | 0 | 0 | 15.91 | 20.14 | 47.79 | 52 | -18.84 | -49.49 | |
| 2A9 | 100 | 0 | 100 | 0 | 8.49 | 15.01 | 6.83 | 45.65 | -43.29 | 19.11 |
C | M | Y | K | |||||
Thin,tough silk | Be not coated with | Be coated with | Be not coated with | Be coated with | Be not coated with | Be coated with | Be not coated with | Be coated with |
0 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 | 0.00 |
3 | 0.03 | 0.05 | 0.05 | 0.06 | 0.04 | 0.05 | 0.01 | 0.05 |
7 | 0.06 | 0.08 | 0.09 | 0.09 | 0.09 | 0.11 | 0.05 | 0.09 |
10 | 0.09 | 0.11 | 0.11 | 0.12 | 0.11 | 0.13 | 0.07 | 0.12 |
15 | 0.14 | 0.16 | 0.18 | 0.17 | 0.14 | 0.19 | 0.14 | 0.18 |
20 | 0.19 | 0.22 | 0.20 | 0.21 | 0.18 | 0.25 | 0.20 | 0.23 |
25 | 0.24 | 0.26 | 0.25 | 0.27 | 0.22 | 0.27 | 0.26 | 0.30 |
30 | 0.29 | 0.30 | 0.30 | 0.32 | 0.24 | 0.32 | 0.32 | 0.36 |
40 | 0.37 | 0.41 | 0.41 | 0.42 | 0.30 | 0.41 | 0.43 | 0.48 |
50 | 0.46 | 0.51 | 0.49 | 0.52 | 0.36 | 0.50 | 0.52 | 0.60 |
60 | 0.57 | 0.62 | 0.57 | 0.64 | 0.41 | 0.59 | 0.61 | 0.74 |
70 | 0.65 | 0.76 | 0.65 | 0.74 | 0.48 | 0.70 | 0.69 | 0.90 |
80 | 0.74 | 0.90 | 0.74 | 0.93 | 0.58 | 0.92 | 0.70 | 1.08 |
90 | 0.87 | 1.09 | 0.84 | 1.09 | 0.81 | 1.30 | 0.76 | 1.32 |
95 | 0.91 | 1.29 | 0.88 | 1.26 | 0.91 | 1.37 | 0.80 | 1.47 |
100 | 0.99 | 1.32 | 0.98 | 1.29 | 1.08 | 1.37 | 0.86 | 1.47 |
C | M | |||||||||||
Thin,tough silk | Be not coated with | Be coated with | Be not coated with | Be coated with | ||||||||
L | a | b | L | a | b | L | a | b | L | a | b | |
0 | 92.7 | -0.2 | 4.9 | 93.3 | -0.6 | 6.2 | 92.7 | -0.2 | 4.9 | 93.3 | -0.6 | 6.2 |
3 | 91.5 | -2.0 | 4.2 | 93.0 | -2.0 | 4.1 | 91.6 | 2.6 | 4.4 | 92.3 | 1.8 | 3.3 |
7 | 90.5 | -4.3 | 1.8 | 91.2 | -4.0 | 1.9 | 89.5 | 6.3 | 1.8 | 90.9 | 4.9 | 2.7 |
10 | 89.1 | -5.8 | 0.7 | 90.3 | -5.8 | -0.5 | 88.3 | 8.7 | 1.4 | 87.4 | 7.3 | 1.4 |
15 | 87.3 | -8.6 | -2.6 | 88.2 | -8.5 | -3.1 | 85.4 | 14.0 | -1.4 | 86.7 | 12.6 | 0.3 |
20 | 85.8 | -11.1 | -5.5 | 86.1 | -11.1 | -6.5 | 83.8 | 17.7 | -3.2 | 84.7 | 16.0 | -1.0 |
25 | 83.7 | -13.6 | -8.0 | 84.3 | -13.4 | -9.1 | 80.8 | 22.9 | -5.0 | 82.0 | 21.2 | -2.9 |
30 | 82.9 | -15.2 | -11.9 | 82.5 | -15.7 | -11.2 | 78.7 | 26.7 | -6.9 | 79.7 | 24.6 | -3.0 |
40 | 79.3 | -18.7 | -16.3 | 78.6 | -18.7 | -17.4 | 74.1 | 34.6 | -8.9 | 75.3 | 32.1 | -5.4 |
50 | 76.2 | -21.6 | -20.3 | 74.6 | -21.0 | -22.4 | 70.1 | 40.3 | -9.1 | 71.5 | 37.9 | -5.3 |
60 | 72.7 | -23.0 | -23.9 | 71.0 | -22.4 | -27.2 | 66.7 | 44.6 | -9.3 | 66.9 | 43.9 | -5.9 |
70 | 69.9 | -24.4 | -28.6 | 67.4 | -23.3 | -31.3 | 64.4 | 47.8 | -9.5 | 63.1 | 48.0 | -5.8 |
80 | 67.0 | -24.6 | -32.2 | 63.5 | -23.4 | -35.3 | 61.0 | 51.1 | -8.5 | 59.1 | 53.9 | -4.7 |
90 | 62.4 | -24.0 | -36.3 | 57.9 | -22.9 | -41.0 | 58.3 | 52.9 | -7.1 | 55.2 | 57.8 | -3.0 |
95 | 60.9 | -23.3 | -37.2 | 52.6 | -20.4 | -44.1 | 56.8 | 53.4 | -5.9 | 50.4 | 57.9 | -1.5 |
100 | 57.8 | -21.1 | -38.0 | 53.2 | -21.1 | -44.1 | 54.2 | 54.4 | -5.0 | 49.9 | 57.9 | -1.2 |
Y | K | |||||||||||
Thin,tough silk | Be not coated with | Be coated with | Be not coated with | Be coated with | ||||||||
L | a | b | L | a | b | L | a | b | L | a | b | |
0 | 92.7 | -0.2 | 4.9 | 93.3 | -0.6 | 6.2 | 92.7 | -0.2 | 4.9 | 93.3 | -0.6 | 6.2 |
3 | 92.6 | -1.1 | 9.1 | 93.6 | -1.0 | 7.2 | 90.4 | -0.3 | 6.4 | 91.7 | 0.1 | 5.1 |
7 | 92.5 | -1.9 | 13.6 | 93.5 | -2.5 | 14.3 | 87.0 | -0.8 | 6.2 | 88.1 | -1.1 | 8.2 |
10 | 92.4 | -2.4 | 15.3 | 93.4 | -3.1 | 16.0 | 84.7 | -1.3 | 5.6 | 85.9 | -1.1 | 7.6 |
15 | 92.4 | -3.1 | 19.1 | 93.2 | -4.0 | 22.3 | 80.3 | -0.7 | 4.4 | 81.1 | -0.5 | 7.0 |
20 | 92.4 | -3.6 | 22.5 | 92.7 | -4.5 | 27.1 | 76.2 | -2.1 | 4.7 | 77.2 | -1.8 | 6.6 |
25 | 92.4 | -4.1 | 25.4 | 93.0 | -5.2 | 30.5 | 72.1 | -1.9 | 3.5 | 73.0 | -0.6 | 4.9 |
30 | 92.3 | -4.6 | 27.9 | 92.9 | -5.8 | 34.4 | 69.0 | -1.6 | 2.3 | 67.6 | -0.5 | 4.3 |
40 | 92.0 | -5.3 | 33.6 | 92.5 | -6.5 | 41.6 | 62.0 | -0.9 | 1.6 | 62.3 | -0.3 | 2.8 |
50 | 91.9 | -5.4 | 38.4 | 92.2 | -7.3 | 48.2 | 56.9 | -0.2 | 0.2 | 55.9 | -0.3 | 2.3 |
60 | 91.9 | -6.1 | 43.8 | 91.5 | -7.7 | 54.1 | 53.7 | -0.1 | -1.0 | 49.7 | 0.8 | 1.5 |
70 | 91.8 | -6.6 | 49.4 | 90.5 | -7.7 | 60.4 | 50.8 | -0.3 | -1.7 | 44.0 | 1.0 | 1.7 |
80 | 91.2 | -6.7 | 55.1 | 89.4 | -7.3 | 70.8 | 49.6 | 0.7 | -1.9 | 37.5 | 1.6 | 3.0 |
90 | 90.8 | -6.2 | 68.8 | 90.2 | -5.2 | 87.2 | 47.3 | -1.0 | 0.4 | 32.1 | 1.4 | 4.5 |
95 | 90.4 | -6.0 | 73.0 | 89.8 | -4.6 | 88.3 | 46.0 | -0.5 | 0.5 | 28.7 | 0.7 | 2.7 |
100 | 89.8 | -4.4 | 79.9 | 87.7 | -4.9 | 86.4 | 43.4 | -1.5 | 2.4 | 30.0 | 0.9 | 2.9 |
C | M | Y | K | X | Y | Z | L | a | | |||
G | 2A9 | |||||||||||
100 | 0 | 100 | 0 | 14.79 | 23.3 | 12.04 | 55.38 | -40.02 | 17.7 | |||
| 2Q9 | 0 | 0 | 100 | 0 | 65.42 | 70.5 | 11.2 | 87.24 | -5.65 | 75.2 | |
| S1 | 0 | 100 | 100 | 0 | 32.98 | 22.4 | 9.29 | 54.45 | 46.01 | 24.88 | |
| 2R9 | 0 | 100 | 0 | 0 | 35.19 | 23.17 | 23.03 | 55.25 | 50.2 | -7.88 | |
| I19 | 100 | 100 | 0 | 0 | 13.56 | 12.27 | 22.18 | 41.64 | 11.58 | -29.71 | |
| 2S9 | 100 | 0 | 0 | 0 | 20.38 | 25.66 | 45.75 | 57.71 | -19.86 | -37.24 | |
| 2A9 | 100 | 0 | 100 | 0 | 14.79 | 23.3 | 12.04 | 55.38 | -40.02 | 17.7 |
C | M | Y | K | X | Y | Z | L | a | | |||
G | 2A9 | |||||||||||
100 | 0 | 100 | 0 | 9.42 | 16.3 | 7.28 | 47.37 | -42.89 | 20.22 | |||
| 2Q9 | 0 | 0 | 100 | 0 | 64.08 | 68.95 | 9.11 | 86.48 | -5.39 | 80.75 | |
| S1 | 0 | 100 | 100 | 0 | 27.63 | 16.62 | 4.91 | 47.78 | 54.73 | 31.87 | |
| 2R9 | 0 | 100 | 0 | 0 | 30.23 | 17.83 | 16.68 | 49.29 | 58.25 | -4.8 | |
| I19 | 100 | 100 | 0 | 0 | 8.22 | 6.85 | 14.82 | 31.47 | 15.42 | -31.02 | |
| 2S9 | 100 | 0 | 0 | 0 | 16.84 | 21.69 | 44.08 | 53.69 | -20.93 | -42.14 | |
| 2A9 | 100 | 0 | 100 | 0 | 9.42 | 16.3 | 7.28 | 47.37 | -42.89 | 20.22 |
Claims (5)