CN101012624A - Staining method of tip brush silk - Google Patents
Staining method of tip brush silk Download PDFInfo
- Publication number
- CN101012624A CN101012624A CN 200710019961 CN200710019961A CN101012624A CN 101012624 A CN101012624 A CN 101012624A CN 200710019961 CN200710019961 CN 200710019961 CN 200710019961 A CN200710019961 A CN 200710019961A CN 101012624 A CN101012624 A CN 101012624A
- Authority
- CN
- China
- Prior art keywords
- spinning cake
- mill base
- color
- painted
- pointed bristles
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a dyeing method for neb brushing wire, comprising following procedures that stocks are mixed equally into color paste, whose PH value is among 1-9; the color paste is coated on the neb end of yarn cake or the neb end is used to fetch color paste; then it is sent into the coloring equipment and it is colored for 1-60 minutes in maintaining temperature of 100-200deg.C; and then the yarn cake is taken out from coloring equipment, residual color slurry is washed by water, it is dried or baked, it is packaged into finished product. Stocks are matched with following components of 5-25 share of disperse dyes by wt, 15-35 share of warm water with 50-60deg.C by wt and 40-80 share of original paste by wt. The invention adopts color slurry to dye neb brushing wire, conquers capillarity phenomena of dye, solves problems of uneven color, fixed length and location dyeing, at the same time solves color difference problem and advances the grade of production.
Description
Technical field:
The present invention relates to brush the colouring method of silk, be specifically related to the colouring method of pointed bristles.
Background technology:
At present, no matter be tack or pointed bristles, its dyeing all is to need dyeing part to immerse in the dye liquor brush silk, painted formation under certain temperature and time condition, and there is capillarity in the brush silk in dye liquor in dyeing course, make the position do not immersed in the dye liquor also by in various degree look, it immerses the position and also has painted irregular phenomenon, and simultaneously, the aberration phenomenon is heavier between every batch, cause the dyeing product class that obtains lower, can not be used to make high-grade toothbrush.
Summary of the invention:
The technical problem to be solved in the present invention provides a kind of colouring method of brushing silk, even dyeing, and no color differnece, and can realize fixed length dyeing.
The present invention is achieved through the following technical solutions:
A kind of colouring method of pointed bristles comprises the following steps:
(1), converts into mill base through mixing to transfer: DISPERSE DYES 1-25 part, 50-60 ℃ of warm water 15-35 part, former paste 40-80 part by following materials of weight proportions; The pH value of mill base is between 1-9;
(2) pointed bristles is packaged into spinning cake;
(3) mill base that step (1) is obtained is coated on the tip end of step (2) spinning cake with brush or scraper, or with the spinning cake tip end of step (2) perpendicular to the mill base face, put into the mill base libation at an ancient wedding ceremony and get mill base;
(4) spinning cake that step (3) is obtained was put into coloring apparatus, 100-220 ℃ of insulation painted 1-60 minute;
(5) the painted back spinning cake that step (4) is obtained takes out coloring apparatus, and the residual mill base of water flush away dries or dries and can be packaged as finished product.
Described coloring apparatus was a rapid steamer, and described spinning cake is put into rapid steamer, 100-200 ℃ of insulation painted 10-60 minute; Described coloring apparatus is hot melt, curer, and described spinning cake is put into hot melt, curer, and insulation is painted 1-35 minute in 170-220 ℃.
Described spinning cake is that polyester is through melt spinning, and after HEAT SETTING, wrap outside again and twine film or cover film formation tow, tow is cut into spinning cake, again spinning cake is put into water and made pointed bristles with the treatment fluid that finishing agent is converted, through clean, oven dry, the formation of integer packing back, the perhaps pointed bristles made from other method again.With the pointed bristles that the described method of another application case of the inventor is made, spinning cake only need remove the polytetrafluoroethylene (PTFE) dressing of external packing before cleaning, all need not remove packing film in cleaning, the drying course, and the finished product after the oven dry can directly enter dyeing process.
Described former paste can be that plant amylum and derivative thereof are made or chemical oar material etc.
Can in mill base, add deep-dyeing agent, reduction inhibitor agent and light stabilizer etc. according to painted needs.
Beneficial effect:
One, the present invention adopts mill base that the brush silk is dyeed, because mill base concentration is bigger, therefore, no matter be or draw together the tip end that cutter is coated to mill base spinning cake with brush, still the libation at an ancient wedding ceremony in the tip end immersion mill base is got mill base, all can overcome the capillarity of dye liquor dyeing, solve look irregular and fixed length, positioning dyeing problem.
Two, the present invention is owing to be mill base to be taken out be coated on the most advanced and sophisticated head surface of spinning cake, and therefore, all brush silks that a batch of material dyes do not have the aberration phenomenon.
Three, the present invention can repeatedly apply the mill base of inequality or different colours to spinning cake tip end, and controls the length of dyeing part, and repeatedly circulation is redyed, and can produce the effect of polychrome on a rhizoid, has promoted the class of product, forms high value added product.
The specific embodiment:
Described former paste can be that plant amylum and derivative thereof are made or chemical oar material etc., gets wherein any.
Embodiment 1
Obtain red pointed bristles as need, then get 5 parts of dispersive red dyes, 15 parts in 50-60 ℃ of warm water, former paste is transferred routinely for 40 parts and is converted mill base, and the pH value of mill base is 1; Pointed bristles is packaged into spinning cake with film or cloth; Length requirement according to dyeing quantitatively takes out mill base with spoon, and mill base is coated on the tip end (using scraper in the present embodiment) of spinning cake with scraper or brush; Then spinning cake is put into rapid steamer, painted 60 minutes of 100 ℃ of insulations; Again painted back spinning cake is taken out rapid steamer, the residual mill base of water flush away can be packaged as finished product after the oven dry.
Embodiment 2
Get 12 parts of dispersive red dyes, 25 parts in 50-60 ℃ of warm water, former paste is transferred routinely for 60 parts and is converted mill base, and the pH value of mill base is 4; Spinning cake is put into rapid steamer, painted 10 minutes of 200 ℃ of insulations.All the other are implemented as embodiment 1.
Embodiment 3
Get 25 parts of dispersive red dyes, 35 parts in 50-60 ℃ of warm water, former paste is transferred routinely for 80 parts and is converted mill base, and the pH value of mill base is 9; Spinning cake is put into rapid steamer, painted 45 minutes minutes of 150 ℃ of insulations.All the other are implemented as embodiment 1.
Embodiment 4
Get 5 parts of dispersive red dyes, 15 parts in 50-60 ℃ of warm water, former paste is transferred routinely for 40 parts and is converted mill base, and the pH value of mill base is 1; Spinning cake is put into hot melt, cured, and insulation is painted 35 minutes in 170 ℃.All the other are implemented as embodiment 1.
Embodiment 5
Get 25 parts of dispersive red dyes, 35 parts in 50-60 ℃ of warm water, former paste is transferred routinely for 80 parts and is converted mill base, and the pH value of mill base is 4; Spinning cake is put into hot melt, cured, and insulation is painted 20 minutes in 190 ℃.All the other are implemented as embodiment 1.
Embodiment 6
Get 12 parts of dispersive red dyes, 25 parts in 50-60 ℃ of warm water, former paste is transferred routinely for 60 parts and is converted mill base, and the pH value of mill base is 9; Spinning cake is put into hot melt, cured, and insulation is painted 1 minute in 220 ℃.All the other are implemented as embodiment 1.
Claims (4)
1, a kind of colouring method of pointed bristles is characterized in that: comprise the following steps:
(1), converts into mill base through mixing to transfer: DISPERSE DYES 1-25 part, 50-60 ℃ of warm water 15-35 part, former paste 40-80 part by following raw materials in weight portion; The pH value of mill base is between 1-9;
(2) pointed bristles is packaged into spinning cake;
(3) mill base that step (1) is obtained is coated on the tip end of step (2) spinning cake with brush or scraper, or with the spinning cake tip end of step (2) perpendicular to the mill base face, put into the mill base libation at an ancient wedding ceremony and get mill base;
(4) spinning cake that step (3) is obtained was put into coloring apparatus, 100-220 ℃ of insulation painted 1-60 minute;
(5) the painted back spinning cake that step (4) is obtained takes out coloring apparatus, and the residual mill base of water flush away dries or dries and can be packaged as finished product.
2, the colouring method of a kind of pointed bristles as claimed in claim 1 is characterized in that: described coloring apparatus was a rapid steamer, and described spinning cake is put into rapid steamer, 100-200 ℃ of insulation painted 10-60 minute;
3, the colouring method of a kind of pointed bristles as claimed in claim 1 is characterized in that: described coloring apparatus is hot melt, curer, and described spinning cake is put into hot melt, curer, and insulation is painted 1-35 minute in 170-220 ℃.
4, the colouring method of a kind of pointed bristles as claimed in claim 1 is characterized in that: described spinning cake is the pointed bristles spinning cake that Polyester Filament is made.