CN101007454A - Composite resin ornamental board - Google Patents
Composite resin ornamental board Download PDFInfo
- Publication number
- CN101007454A CN101007454A CN 200610002611 CN200610002611A CN101007454A CN 101007454 A CN101007454 A CN 101007454A CN 200610002611 CN200610002611 CN 200610002611 CN 200610002611 A CN200610002611 A CN 200610002611A CN 101007454 A CN101007454 A CN 101007454A
- Authority
- CN
- China
- Prior art keywords
- resin
- plank
- minutes
- stir
- curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention involves a resin composite decorative plate, it mainly consists of wood plate and resin coating the plate. Its characteristics are that it is prepared through the following method: daubing ceresin wax on the base seat and frame, wiping until dry; adding accelerator, color paste and curing agent into resin, stirring uniformly, pumping the foam fully; pouring the resin into frame on said base seat plate, laying and forming solidified resin layer; then pouring stirred materials on the solidified resin layer in frame, laying wood plate and curing; pouring stirred materials on the wood plate to making the gap between the wood plate and the frame is full of stirred materials and the a stirred materials layer is formed on the wood plate, laying and curing; then pouring the stirred materials on the solidified layer and covering transparent cladding paper, strickling and curing; putting it into oasthouse drying and demolding. The resin composite decorative plate is completely waterproof, and has high planeness, good brightness and no seams, the surface can beproduced for any pattern, it can be used in architectural and indoor and outdoor decorative areas as decorative sheet materials widely.
Description
Technical field
The present invention relates to a kind of composite resin ornamental board, relate to a kind of building material sheet material that reaches waterproof, decorative purpose with the resin-coating plank specifically.
Technical background
At present, along with the raising of people's living standard, the demand of decorative building material is also become rich and varied, existing sheet material mostly is natural wood sheet material, sheet metal, composite board.Though natural boards exists environmental protection, easy characteristics such as processing,, in actual use, it is big to be affected by the external environment, and moisture-sensitive is out of shape in wet environment especially, easier being damaged by worms and damaging; Sheet metal can not make moist distortion, damaged by worms, but its heaviness, the cost height, easy-to-rust is difficult for cutting, can not be widely used; Composite board light weight, but poor with the other materials conformability only can be used separately, in decoration, is difficult to separately to use as the sheet material of door and window etc., and easily aging distortion.For this reason, a kind of environmental protection of urgent need on the market, the sheet material that color is changeable, conformability is good.
Summary of the invention
The object of the present invention is to provide that a kind of cost is low, light weight, environmental protection, utilize timber to be base material, the composite resin ornamental board that the outside is resin-coated is to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this, and it mainly is made up of plank and the peripheral resin that coats thereof, and it is characterized in that it prepares by following method:
1. on base plate, evenly smear paraffin, spend 10～20 minutes and dry;
2. go out framework with cradle around the base plate, and be fixed on the base plate with clamp greater than plank 1～2mm;
3. evenly smear paraffin at frame inner wall, spend 10～20 minutes and dry, stand-by;
4. pour resin into mixing drum, the ratio with 1 kilogram of 5～20ml adds promoter again, and adds mill base, stir, the ratio with 1 kilogram of resin 6～20ml adds curing agent then, stirs to make to stir material, vacuumized again 3～5 minutes, the bubble that stirs in the material is taken out to the greatest extent;
5. it is interior thick to 0.5～1.5mm to stir the framework of expecting to pour on the said base flat board, places to form curing resin layer;
6. pour again that to stir material thick to 0.5～1mm on the curing resin layer in framework into, put plank then, place and solidify;
7. on plank, pour into and stir material, make the space between plank and framework fill up and on plank, form the thick one deck of 0.5～2mm, place and solidify;
8. will stir material and be poured on the cured layer, and cover transparent tectorial paper, wipe off, solidify;
9. put into drying room and heated up after 20 minutes to 60～80 ℃ by room temperature, constant temperature was placed 1 hour, lowered the temperature 30 minutes again to room temperature, and the demoulding promptly gets composite resin ornamental board.
Wherein, resin requires shrinkage little, solidifies back hardness height.Preferred unsaturated-resin.
Wherein, curing agent is preferably consolidated oxidation first and second bronze medals.
Wherein, the preferred cobalt iso-octoate of promoter.
Wherein, plank is selected flatness height, good permeability, the sheet material that the surface is slightly rough.
Wherein, base plate can be and is glass, plank, metallic plate, plastic plate, resin plate etc.The surface must be smooth smooth, but if any special shape die sinking tool.As needing decorative pattern, can stick stencil paper or film stencil paper on flat board, but this stencil paper or film stencil paper must not absorb resin on the composite resin ornamental board, high temperature resistant more than 50 ℃, veneer must be smooth.
Wherein, lath is bonding jumper, adhesive tape, plastic strip, batten, resin streak etc., and requires not absorb resin and surface smoothing.The thickness of lath must be identical with the thickness of the composite resin ornamental board of being done, and if any special shape, also the strip bending can be done decorative pattern as need, one side can be at the stencil paper that sticks of lath.
Wherein, transparent tectorial paper can be that good brightness such as plastic paper, flatness are good, does not absorb the paper of resin.As the need decorative pattern, available stencil paper.Transparent tectorial paper needs high temperature resistant more than 50 ℃, and preferred thickness is 0.5～1mm.
The compared with prior art complete waterproof of the present invention, flatness height, good brightness, no seam, any decorative pattern can be made in the surface, can be used as decorative plate and is widely used in building and indoor and outdoor decoration field.In the past few years by multiple performance check test, as corrosion resistance test, accelerated aging test, Wind-Pressure Resistance test or the like, no matter be overcast and rainy continuous, still The sun is shining fiercely or high moist environment, confirmed that all its " durability ", " security ", " reliability " shows that fully this plate has remarkable combination property.
The specific embodiment
Further specify the present invention below in conjunction with embodiment
Embodiment 1
1. on base plate, evenly smear paraffin, spend 10 minutes and dry;
2. go out framework with cradle around the base plate, and be fixed on the base plate with clamp greater than plank 1mm;
3. evenly smear paraffin at frame inner wall, spend 10 minutes and dry, stand-by;
4. pour 1 kilogram of resin into mixing drum, add the promoter of 5ml again, and add red mill base, stir, add the 6ml curing agent again, stir to make and stir material, vacuumized again 3 minutes, the bubble that stirs in the material is taken out to the greatest extent;
5. it is interior thick to 0.5mm to stir the framework of expecting to pour on the said base flat board, places to form curing resin layer;
6. pour on the curing resin layer in framework again to stir and expect to 0.5mm thickly, put plank then, place and solidify;
7. on plank, pour into and stir material, make the space between plank and framework fill up and on plank, form the thick one deck of 0.5mm, placement curing;
8. will stir material and be poured on the cured layer, and cover transparent tectorial paper, wipe off, solidify;
9. put into drying room and heated up after 20 minutes to 60 ℃ by room temperature, constant temperature was placed 1 hour, lowered the temperature 30 minutes again to room temperature, and the demoulding promptly gets the red resin composite decorating board.
Embodiment 2
1. on the glass pedestal flat board, evenly smear paraffin, spend 20 minutes and dry;
2. go out framework with the laths of metal frame around the glass pedestal flat board, and be fixed on the glass pedestal flat board with clamp greater than plank 2mm;
3. evenly smear paraffin at frame inner wall, spend 20 minutes and dry, stand-by;
4. pour 1 kilogram of unsaturated-resin into mixing drum, add the cobalt iso-octoate of 20ml again, and add green mill base, stir, add solid oxidation first and second bronze medals of 20ml again, stir to make and stir material, vacuumized again 5 minutes, the bubble that stirs in the material is taken out to the greatest extent;
5. it is interior thick to 1.5mm to stir the framework of expecting to pour on the above-mentioned glass pedestal flat board, places to form curing resin layer;
6. pour on the curing resin layer in framework again to stir and expect to 1mm thickly, put plank then, place and solidify;
7. on plank, pour into and stir material, make the space between plank and framework fill up and on plank, form the thick one deck of 2mm, placement curing;
8. will stir material and be poured on the cured layer, and cover plastic paper, wipe off, solidify;
9. put into drying room and heated up after 20 minutes to 80 ℃ by room temperature, constant temperature was placed 1 hour, lowered the temperature 30 minutes again to room temperature, and the demoulding promptly gets the green resin composite decorating board.
Embodiment 3
1. on the metal base flat board, evenly smear paraffin, spend 15 minutes and dry;
2. go out framework with the plastic slat frame around the metal base flat board, and be fixed on the metal base flat board with clamp greater than plank 1.5mm;
3. evenly smear paraffin at frame inner wall, spend 15 minutes and dry, stand-by;
4. pour 1 kilogram of unsaturated-resin into mixing drum, add the cobalt iso-octoate of 12ml again, and add yellow mill base, stir, add solid oxidation first and second bronze medals of 13ml again, stir to make and stir material, vacuumized again 4 minutes, the bubble that stirs in the material is taken out to the greatest extent;
5. it is interior thick to 1mm to stir the framework of expecting to pour on the above-mentioned metal base flat board, places to form curing resin layer;
6. pour on the curing resin layer in framework again to stir and expect to 0.7mm thickly, put plank then, place and solidify;
7. on plank, pour into and stir material, make the space between plank and framework fill up and on plank, form the thick one deck of 1.5mm, placement curing;
8. will stir material and be poured on the cured layer, and cover grain of rice paper, wipe off, solidify;
9. put into drying room and heated up after 20 minutes to 70 ℃ by room temperature, constant temperature was placed 1 hour, lowered the temperature 30 minutes again to room temperature, and the demoulding promptly gets yellow composite resin ornamental board.
Test report:
Environmental protection test: zero formaldehyde, put it in the fish jar 2000 hours, fish is still dynamic.
Superpower protection against the tide, water resistance test: place it in that continuous dipping ANOMALOUS VARIATIONS can not take place in 2000 hours in the water.
Superpower stable, be difficult for the deformation performance test: under the zero temperature 60 degree to 80 degree above freezing, humidity 95%, test use 3 years indeformable;
Anticorrosion mothproof performance test: place it in the termite population 2000 hours, no any vestige of damaging by worms.
Claims (4)
1, composite resin ornamental board, it mainly is made up of plank and the peripheral resin that coats thereof, and it is characterized in that it prepares by following method:
1. on base plate, evenly smear paraffin, spend 10～20 minutes and dry;
2. go out framework with cradle around the base plate, and be fixed on the base plate with clamp greater than plank 1～2mm;
3. evenly smear paraffin at frame inner wall, spend 10～20 minutes and dry, stand-by;
4. pour resin into mixing drum, the ratio with 1 kilogram of 5～20ml adds promoter again, and adds mill base, stir, the ratio with 1 kilogram of resin 6～20ml adds curing agent then, stirs to make to stir material, vacuumized again 3～5 minutes, the bubble that stirs in the material is taken out to the greatest extent;
5. it is interior thick to 0.5～1.5mm to stir the framework of expecting to pour on the said base flat board, places to form curing resin layer;
6. pour again that to stir material thick to 0.5～1mm on the curing resin layer in framework into, put plank then, place and solidify;
7. on plank, pour into and stir material, make the space between plank and framework fill up and on plank, form the thick one deck of 0.5～2mm, place and solidify;
8. will stir material and be poured on the cured layer, and cover transparent tectorial paper, wipe off, solidify;
9. put into drying room and heated up after 20 minutes to 60～80 ℃ by room temperature, constant temperature was placed 1 hour, lowered the temperature 30 minutes again to room temperature, and the demoulding promptly gets composite resin ornamental board.
2, composite resin ornamental board according to claim 1, resin are unsaturated-resin.
3, composite resin ornamental board according to claim 1, curing agent is solid oxidation first and second bronze medals.
4, composite resin ornamental board according to claim 1, promoter are cobalt iso-octoate.