CN100591818C - Fibrilia spinning method and yarn thereof - Google Patents
Fibrilia spinning method and yarn thereof Download PDFInfo
- Publication number
- CN100591818C CN100591818C CN200710143317A CN200710143317A CN100591818C CN 100591818 C CN100591818 C CN 100591818C CN 200710143317 A CN200710143317 A CN 200710143317A CN 200710143317 A CN200710143317 A CN 200710143317A CN 100591818 C CN100591818 C CN 100591818C
- Authority
- CN
- China
- Prior art keywords
- yarn
- handled
- flax fibre
- health
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A spinning method of bast fibers is provided, which comprises the following steps: (a) wetting the bast fibers; (b) subjecting the wetted bast fibers to opening, carding and drawing treatments to obtain bast stripes; (c) wetting the bast stripes; and (d) spinning the wetted bast stripes to make yarns. A yarn spun from the bast fibers is also provided. The yarn is produced by wetting the bast fibers, opening, carding, drawing, wetting again and spinning. The yarn made of bast fibers has the advantages of low rate of fiber breakage, high efficiency and good product quality.
Description
Technical field
The present invention relates to a kind of fibrilia spinning method and yarn thereof, particularly relate to a kind of fibrilia spinning method and yarn thereof that comprises secondary health treatment process.
Background technology
Because flax fibre has sucting wet air permeability, low static behaviour and good antibacterial characteristics preferably, the crudefiber crop textiles more and more is subjected to people's favor.But because the content of lignin is higher in the flax fibre, particularly tossa, therefore big than the rigidity of other fibers such as cotton fiber, fiber is more crisp, easily fracture.In the prior art, though can carry out the humidification health to flax fibre usually before spinning handles, to improve the pliability of flax fibre, but in the processed process of flax fibre, moisture loss is fast, becomes dry easily, and the phenomenon of fracture easily takes place in the spinning process, such as in the traditional handicraft of flax fibre and other fiber blends, when the spinning fineness is 12
sThe time, end breakage rate can reach every equipment 300-400 time/hour, and the difficulty that this has increased the flax fibre spinning has greatly reduced operating efficiency and product quality that flax fibre spins.
Summary of the invention
For this reason, technical problem to be solved by this invention be to provide that a kind of step is simple, efficient is high, low fibrilia spinning method and the yarn thereof of end breakage rate during spinning.
For solving the problems of the technologies described above, technical scheme of the present invention is: a kind of spinning method of flax fibre may further comprise the steps:
A. flax fibre being carried out a humidification health handles;
B. will be through the flax fibre opening or cleaning after a humidification health is handled, combing, drafting to form ramie stripes;
C. ramie stripes being carried out the secondary health handles;
D. the ramie stripes after the secondary health being handled is spun into yarn.
The spinning method of above-mentioned flax fibre, the temperature that described secondary health is handled is 30 ℃-80 ℃.
The spinning method of above-mentioned flax fibre, the relative humidity that described secondary health is handled is 80-100%.
The spinning method of above-mentioned flax fibre, the time that described secondary health is handled is 2-14 hour.
The spinning method of above-mentioned flax fibre, described flax fibre are one or more in jute, gombo hemp or the hemp.
The spinning method of above-mentioned flax fibre, the weight percentage of jute is 20%-100% in the described flax fibre.
The yarn that a kind of flax fibre is spun into, described yarn are by flax fibre being carried out the yarn that spinning forms after the secondary health is handled again behind a humidification health processing, opening or cleaning, combing, the drafting.
Above-mentioned yarn, described flax fibre are one or more in jute, gombo hemp or the hemp.
Above-mentioned yarn, the weight percentage of jute is 20%-100% in the described flax fibre.
Technique scheme of the present invention compared with prior art has the following advantages: the technology that fibrilia spinning method of the present invention adopts the secondary health to handle, make flax fibre when spinning, can have higher pliability, greatly increased the spinning property of flax fibre, having improved the operating efficiency and the product quality of flax fibre spinning, is 12 such as working as the spinning fineness
sThe time, adopt the end breakage rate of method flax fibre of the present invention can be reduced to every equipment 150-200 time/hour.
The specific embodiment
Embodiment 1
Tossa is carried out a humidification health by prior art to be handled; Then will be through the tossa after a humidification health is handled by the method opening or cleaning of prior art, combing, drafting to form ramie stripes; Ramie stripes is carried out the secondary health handle, the temperature that described secondary health is handled is 30 ℃, and relative humidity is 85%, and the time is 2 hours; Ramie stripes after then the secondary health being handled is spun into yarn.Adopt the yarn of the method spinning of present embodiment, when the spinning fineness is 12
sThe time, through 100 sampling tests, every equipment of end breakage rate average out to 200 times/hour.
Embodiment 2
Tossa is carried out a humidification health by prior art to be handled; Then will be through the tossa after a humidification health is handled by the method opening or cleaning of prior art, combing, drafting to form ramie stripes; Ramie stripes is carried out the secondary health handle, the temperature that described secondary health is handled is 80 ℃, and relative humidity is 90%, and the time is 14 hours; Ramie stripes after then the secondary health being handled is spun into yarn.Adopt the yarn of the method spinning of present embodiment, when the spinning fineness is 12
sThe time, through 100 sampling tests, every equipment of end breakage rate average out to 161 times/hour.
Embodiment 3
Tossa is carried out a humidification health by prior art to be handled; Then will be through the tossa after a humidification health is handled by the method opening or cleaning of prior art, combing, drafting to form ramie stripes; Ramie stripes is carried out the secondary health handle, the temperature that described secondary health is handled is 50 ℃, and relative humidity is 100%, and the time is 4 hours; Ramie stripes after then the secondary health being handled is spun into yarn.Adopt the yarn of the method spinning of present embodiment, when the spinning fineness is 12
sThe time, through 100 sampling tests, every equipment of end breakage rate average out to 176 times/hour.
Embodiment 4
The gombo hemp fiber is carried out a humidification health by prior art to be handled; Then will be through the gombo hemp fiber after a humidification health is handled by the method opening or cleaning of prior art, combing, drafting to form ramie stripes; Ramie stripes is carried out the secondary health handle, the temperature that described secondary health is handled is 40 ℃, and relative humidity is 95%, and the time is 3 hours; Ramie stripes after then the secondary health being handled is spun into yarn.Adopt the yarn of the method spinning of present embodiment, when the spinning fineness is 12
sThe time, through 100 sampling tests, every equipment of end breakage rate average out to 182 times/hour.
Embodiment 5
Linen fibre is carried out a humidification health by prior art to be handled; Then will be through the linen fibre after a humidification health is handled by the method opening or cleaning of prior art, combing, drafting to form ramie stripes; Ramie stripes is carried out the secondary health handle, the temperature that described secondary health is handled is 60 ℃, and relative humidity is 85%, and the time is 6 hours; Ramie stripes after then the secondary health being handled is spun into yarn.Adopt the yarn of the method spinning of present embodiment, when the spinning fineness is 12
sThe time, through 100 sampling tests, every equipment of end breakage rate average out to 154 times/hour.
Embodiment 6
Hemp is carried out a humidification health by prior art to be handled; Then will be through the hemp after a humidification health is handled by the method opening or cleaning of prior art, combing, drafting to form ramie stripes; Ramie stripes is carried out the secondary health handle, the temperature that described secondary health is handled is 70 ℃, and relative humidity is 80%, and the time is 10 hours; Ramie stripes after then the secondary health being handled is spun into yarn.Adopt the yarn of the method spinning of present embodiment, when the spinning fineness is 12
sThe time, through 100 sampling tests, every equipment of end breakage rate average out to 168 times/hour.
Embodiment 7
Being 90% jute with the jute weight percentage carries out a humidification health by prior art and handles with the flax fibre that mixes of gombo hemp fiber; Then will be through the mixing flax fibre after a humidification health is handled by the method opening or cleaning of prior art, combing, drafting to form ramie stripes; Ramie stripes is carried out the secondary health handle, the temperature that described secondary health is handled is 60 ℃, and relative humidity is 95%, and the time is 8 hours; Ramie stripes after then the secondary health being handled is spun into yarn.Adopt the yarn of the method spinning of present embodiment, when the spinning fineness is 12
sThe time, through 100 sampling tests, every equipment of end breakage rate average out to 151 times/hour.
Embodiment 8
Being 20% jute with the jute weight percentage carries out a humidification health by prior art and handles with the flax fibre that mixes of hemp; Then will be through the mixing flax fibre after a humidification health is handled by the method opening or cleaning of prior art, combing, drafting to form ramie stripes; Ramie stripes is carried out the secondary health handle, the temperature that described secondary health is handled is 70 ℃, and relative humidity is 90%, and the time is 12 hours; Ramie stripes after then the secondary health being handled is spun into yarn.Adopt the yarn of the method spinning of present embodiment, when the spinning fineness is 12
sThe time, through 100 sampling tests, every equipment of end breakage rate average out to 150 times/hour.
Obviously, the foregoing description only is for example clearly is described, and is not the qualification to embodiment.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here need not also can't give exhaustive to all embodiments.And conspicuous variation of being extended out thus or change still are among the protection domain of the invention.
Claims (9)
1, a kind of spinning method of flax fibre is characterized in that, may further comprise the steps:
A. flax fibre being carried out a humidification health handles;
B. will be through the flax fibre opening or cleaning after a humidification health is handled, combing, drafting to form ramie stripes;
C. ramie stripes being carried out the humidification health second time handles;
D. the ramie stripes after the humidification health is handled for the second time is spun into yarn.
2, spinning method according to claim 1 is characterized in that: the temperature that the described humidification health second time is handled is 30 ℃-80 ℃.
3, spinning method according to claim 1 is characterized in that: the relative humidity that the described humidification health second time is handled is 80-100%.
4, spinning method according to claim 1 is characterized in that: the time that the described humidification health second time is handled is 2-14 hour.
5, according to arbitrary described spinning method among the claim 1-4, it is characterized in that: described flax fibre is one or more in jute, gombo hemp or the hemp.
6, spinning method according to claim 5 is characterized in that: the weight percentage of jute is 20%-100% in the described flax fibre.
7, the yarn that is spun into of a kind of flax fibre is characterized in that: described yarn is to spin the yarn that forms by flax fibre being carried out handle the back through the humidification health second time again behind a humidification health processing, opening or cleaning, combing, the drafting.
8, yarn according to claim 7 is characterized in that: described flax fibre is one or more in jute, gombo hemp or the hemp.
9, yarn according to claim 8 is characterized in that: the weight percentage of jute is 20%-100% in the described flax fibre.