CN100582204C - Highly effective energy-saving nano anti-wearing agent and its preparation method and uses - Google Patents
Highly effective energy-saving nano anti-wearing agent and its preparation method and uses Download PDFInfo
- Publication number
- CN100582204C CN100582204C CN200810079682A CN200810079682A CN100582204C CN 100582204 C CN100582204 C CN 100582204C CN 200810079682 A CN200810079682 A CN 200810079682A CN 200810079682 A CN200810079682 A CN 200810079682A CN 100582204 C CN100582204 C CN 100582204C
- Authority
- CN
- China
- Prior art keywords
- nano
- antiwear agent
- parts
- agent
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a high-efficiency energy-saving nano anti-wear agent, a preparation method and application thereof. The nano anti-wear agent is made by the following raw materials in weight proportion: 1 to 500 portions of nano metal particles, 100 to 10,000 portions of detergent dispersant, 100 to 10,000 portions of antioxidant, 100 to 5,000 portions of organic high polymer, and 80,000 to 500,000 portions of diluting agent, wherein the nano metal particles are mixture of two or more than two of metal particle molybdenum, boron, chromium, vanadium, titanium, aluminum and cerium. The compositions are mixed according to the proportion, are stirred to react at a specified temperature, are circularly sprayed and dispersed for a plurality of hours through a high-pressure plunger pump, and then form a steady nano-metal eutectic ion organic compound colloid by the dispersion of a high-power ultrasonic device. The nano anti-wear agent has the advantages of good service performance, simple preparation method, and broad application, and can form novel lubricating oil series products with lubricating oil.
Description
Technical field
The present invention relates to a kind of nano antiwear agent, the invention still further relates to the preparation method and the application of this nano antiwear agent.
Background technology
Nano material has been subjected to extensive concern owing to its special physics and chemical property, and has obtained Preliminary Applications at numerous areas.In tribological field, people have carried out big quantity research at the nanoparticle lubricating oil additive.Have found that multiple nano metal particulate all can improve the antifriction of oil product, wear-resistant and extreme pressure property effectively as additive.It should be noted that, in lubricating oil storage and use, has high chemically reactive and surface-active nano metal particulate additives is difficult to keep for a long time chemical physical stability, and the easy reunion characteristic of nano metal particulate makes it be difficult to keep for a long time dispersion stabilization in lubricating oil, and this just makes the application of nano metal particulate lubricating oil additive be subjected to very big restriction.Forefathers studies show that, by means of the chemisorption characteristic of organic molecule part to solid surface, can introduce the organic molecule decorative layer at the nano metal microparticle surfaces, thereby make its dispersion stabilization in lubricating oil significantly improve by giving its surface hydrophobicity oil-wet behavior; The chemical physical stability of the nano metal particulate after meanwhile, surface modification is handled also significantly improves.Therefore, the surface finish nano metal particle has huge application potential as lubricating oil additive.CN1206737A discloses a kind of antifriction lubricant of nanometer metal micropowder, and it is made through certain process conditions and production stage by nanometer metal micropowder and solvent.CN1552833A discloses a kind of nano metal antifriction antiwear reinforcer of water based lubrication, and it is a kind of colloidal sol of metal nanoparticle, and the reinforcer composition is made up of nano-metal particle, dispersion medium and auxiliary agent.CN1528870A discloses a kind of nano antiwear agent and its production and application, nano antiwear agent is made up of polyisobutene and carbon nanotube, CN101113383A discloses a kind of ester flame-proof hydraulic-oil and production method that contains nano abrasion-resistant additive, the weight proportion of its raw material is as follows: synthesizing ester compound basis oil: 90～95%, the composite multifunction additive: 1.0～5.0%, nano abrasion-resistant additive: 1.0～5.0%.How these technology improve its use properties for the present invention there is no directive significance.
Summary of the invention
Technical problem to be solved by this invention is, a kind of high-efficiency energy-saving nano antiwear agent is provided, and this nano antiwear agent has good use properties, and the preparation method is simple, is widely used, and can form novel lubricating oil series product with lubricating oil.
For this reason, another technical problem to be solved by this invention is, a kind of preparation method and application of above-mentioned nano antiwear agent are provided.
For solving the problems of the technologies described above, the technical solution used in the present invention is as follows:
A kind of high-efficiency energy-saving nano antiwear agent, its technical scheme are that it is made by the following weight proportion raw material:
1～500 part of nano metal particulate
100～10000 parts of detergent-dispersant additives
100～10000 parts in oxidation inhibitor
100～5000 parts of organic polymers
80000～500000 parts of thinners
Wherein, above-mentioned nano metal particulate is two kinds or a two or more mixture in metal particle molybdenum, chromium, vanadium, titanium, aluminium, the cerium; Detergent-dispersant additive is the combination of wherein a kind of in middle base number calcium mahogany sulfonate, sulfur phosphorization polyisobutylene titanate salt, calcium sulfenyl phenolate, mono butonediimide ashless, the many succimides of polyisobutene, the middle basicity alkyl calcium salicylate or two kinds; Oxidation inhibitor is the combination of wherein a kind of in the two octyl group basic zinc salt of sulphur phosphorus, 2,6 ditertiary butyl p cresol, thiadiazoles derivative, p-tert-butylphenol, tri-isopropanolamine, the two octadecyl esters of thio-2 acid or two kinds; Organic polymer is the combination of wherein a kind of in ethylene-propylene copolymer, polyacrylic ester, polyisobutene, the polymethacrylate or two kinds; Thinner is the combination of wherein a kind of in 150ZN base oil, 200ZN base oil, 150SN base oil, the 200SN base oil or two kinds.
In the technique scheme, it is made described nano antiwear agent by following preferred weight proportion raw material:
250～300 parts of nano metal particulates
Earn 5000～6000 parts of dispersion agents clearly
5000～6000 parts in oxidation inhibitor
3000～4000 parts of organic polymers
200000～300000 parts of thinners.
The particle diameter of above-mentioned nano metal particulate is 1～100nm.The molecular weight of organic polymer can be for 200～5000 (also can not only select certainly in this scope, as select 200～500000 or other value).
The method for preparing described high-efficiency energy-saving nano antiwear agent, its technical scheme is that it may further comprise the steps: (1) places reactor with nano metal particulate, detergent-dispersant additive, oxidation inhibitor, organic polymer, thinner by above-mentioned weight proportion, heat to 45 ℃～120 ℃ stirring reaction 1～3.5 hour; (2) be that 2～100Mpa, flow are the high pressure plunger pump of 10～160L/min with the reactant operating pressure, circulation high-voltage high-speed jet spread 1～3.5 hour; (3) be that the ultrasonic drilling machine of 800～2000W disperses with output rating again, the time be 0.5～5 hour promptly.
Make the lubrication oil antiwear agent with described high-efficiency energy-saving nano antiwear agent, according to weight ratio, the nano antiwear agent with 10% mixes with 90% lubricating oil, and stirring through heating forms.
Make the extreme pressure gear oil anti-wear agent with described high-efficiency energy-saving nano antiwear agent, according to weight ratio, the nano antiwear agent with 20% mixes with 80% lubricating oil, and stirring through heating forms.
With the water-soluble anti-wear agent of extreme pressure that described high-efficiency energy-saving nano antiwear agent is made, according to weight ratio, the nano antiwear agent with 15% mixes with 85% lubricating oil, and stirring through heating forms.
High-efficiency energy-saving nano antiwear agent of the present invention is made up of multiple nano metal particulate, detergent-dispersant additive, oxidation inhibitor, organic polymer, thinner.These compositions mix by a certain percentage, and stirring reaction under specified temperature disperses a few hours through the high pressure plunger pump cyclic spray, disperse to form stabilized nano metal eutectic ion organic compound colloid through the high-power ultrasonics machine again.
Compare with traditional nano antiwear agent, nano antiwear agent of the present invention has the following advantages: (1) commercially available prod density is all greater than 1.1g/cm
3, and the little (0.950～1.065g/cm of nano antiwear agent proportion of the present invention
3), good dispersity is difficult for precipitation.(2) commercially available prod require the idling for internal combustion engine running more than 30 minutes temperature reach more than 80 ℃ and add under the situation, the hot activation film forming, film forming speed is slow, wear-resistant anti-extreme pressure can be poor.Nano antiwear agent of the present invention all can add in the lubricating oil at high and low temperature environment, high-strength infiltration, moment film forming, the wear-resistant anti-extreme pressure effect of moment performance product, it is energy-conservation, fall throat, cooling, reduction exhaust emissions effect are obvious.(3) commercially available prod carrying, anti-extreme pressure can be a little less than.Nano antiwear agent anti-extreme pressure of the present invention can be greater than 630,000 pounds/square inch, and anti-wear effect is 210 times of plain oil, are applicable to the mechanical means and the high and low temperature environment that need liquid lubrication.(4) commercially available prod high loading wheel casing, big load machinery, the high-power engine suggestion adds 10%.Nano antiwear agent suggestion of the present invention is added 5% and is got final product.(5) commercially available prod high-temperature behavior instability, shutting down at locomotive, machine oil is the meat jelly shape when longer.Nano antiwear agent high and low temperature of the present invention stable performance is fit to varying environment and uses, and has good cold start-up function.(6) commercially available prod does not have the cleaning of off-gas function, and nano antiwear agent of the present invention makes in the tail gas CO content descend more than 40%, and HC content descends more than 40%.(7) vehicle fuel about 0～4% is saved in the commercially available prod.Nano antiwear agent of the present invention is saved fuel oil more than 15%, and the economize on electricity of heavy loading running machinery is more than 10%, and textile manufacturing machine economizes on electricity more than 10%.(8) commercially available prod high loading, low-speed running machinery fuel-economizing, economize on electricity are not obvious.Nano antiwear agent of the present invention utilizes the eutectic metal, and the change sliding friction is rolling resistance, reduces frictional coefficient, and high loading, the fuel-economizing of low-speed running machinery, economize on electricity are obviously.(9) the commercially available prod shear ability is poor, general 150 hours (6 days) abrasion resistance complete losses.Nano antiwear agent anti-shear ability of the present invention is strong, and (365 days) safe life was long in 8000 hours, and abrasion resistance is good, and it is little to wear and tear.(10) the commercially available prod price is at 360～1200 yuan/kilogram, and the commercially available price of nano antiwear agent of the present invention is 160 yuan/kilogram, and cost performance is higher, has tangible price advantage.(11) from effect, use the nano antiwear agent of invention every energy-conservation 1%, the comprehensive benefit of generation is 10% of enterprise's pure profit, compares with scrap build type power-economizing method, its direct investment only is 2%, and saves ample resources, changes enterprise management idea.(12) nano antiwear agent of the present invention can prolong equipment life more than one times, saves a large amount of accessory expenses, pipe expense, upkeep cost, improves equipment availability, creates more multiple-effect benefit.
In sum, nano antiwear agent density of the present invention is lower, and nanometer particle size is little, and adding proportion (addition) is very low, water soluble base lubricating agent, oil, fat, the lubricating oil of being prepared, agent deposit do not reunite in several years, layering, precipitation.This anti-wear agent makes an addition in the lubricant medium; form nano metal eutectic ionic compound protective membrane; under overweight anti-extreme pressure condition, have good anti-wear and wear-resistant performance, thus reach reduce mechanical friction loss, reduce noise, improve output rating, prolong equipment life, the purpose of energy-saving and environmental protection.It has good use properties.Raw material of the present invention is cheap and easy to get, nontoxic, harmless, non-corrosiveness, and the preparation method is simple, three-waste free discharge.It is widely used, and can form novel lubricating oil (agent) series product with multiple lubricating oil (agent), can be mixed with different lubricant mediums and form new high-efficiency energy-saving nano antiwear agent, oily product innovation, is suitable for large-scale industrial production, application.
Embodiment
Embodiment 1: nano antiwear agent of the present invention is made by the following weight proportion raw material: nano metal particulate 250 grams, detergent-dispersant additive 5000 grams, oxidation inhibitor 5000 grams, organic polymer 3000 grams, thinner 200000 grams.Wherein, above-mentioned nano metal particulate is two kinds or a two or more mixture (i.e. two kinds or two or more combinations) in metal particle molybdenum, chromium, vanadium, titanium, aluminium, the cerium, and the particle diameter of nano metal particulate is 1～100nm.For example, the nano metal particulate can be the combination of metal particle chromium, vanadium, also can be the combination of metal particle titanium, aluminium, cerium.The particle diameter of nano metal particulate can be 40～60nm.Detergent-dispersant additive is the combination of wherein a kind of in middle base number calcium mahogany sulfonate, sulfur phosphorization polyisobutylene titanate salt, calcium sulfenyl phenolate, mono butonediimide ashless, the many succimides of polyisobutene, the middle basicity alkyl calcium salicylate or two kinds.For example, detergent-dispersant additive can be middle base number calcium mahogany sulfonate, can also be the combination of many succimides of polyisobutene and middle basicity alkyl calcium salicylate.Oxidation inhibitor is the combination of wherein a kind of in the two octyl group basic zinc salt of sulphur phosphorus, 2,6 ditertiary butyl p cresol, thiadiazoles derivative, p-tert-butylphenol, tri-isopropanolamine, the two octadecyl esters of thio-2 acid or two kinds.For example, oxidation inhibitor can be p-tert-butylphenol, can also be the combination of tri-isopropanolamine and the two octadecyl esters of thio-2 acid.Organic polymer is the combination of wherein a kind of in ethylene-propylene copolymer, polyacrylic ester, polyisobutene, the polymethacrylate or two kinds.For example, organic polymer can be polyacrylic ester, can also be the combination of ethylene-propylene copolymer and polymethacrylate.The molecular weight of organic polymer can be 200～5000.Thinner is the combination of wherein a kind of in 150ZN base oil, 200ZN base oil, 150SN base oil, the 200SN base oil or two kinds.For example, thinner can be the 200ZN base oil, can also be the combination of 150ZN base oil and 200SN base oil.
The method for preparing high-efficiency energy-saving nano antiwear agent may further comprise the steps: (1) places reactor with nano metal particulate, detergent-dispersant additive, oxidation inhibitor, organic polymer, thinner successively by above-mentioned weight proportion, heats to 80 ℃ stirring reaction 2 hours.(2) be that 60Mpa, flow are the high pressure plunger pump of 100L/min with the reactant operating pressure, the circulation high-voltage high-speed is from pump outlet nozzle jet spread 2 hours (described nozzle diameter can be 0.3～1.0 millimeter).(3) again with output rating be 1500W (watt) ultrasonic drilling machine disperse, the time be 3 hours promptly, product forms stabilized nano metal eutectic ion organic compound colloid.
Embodiment 2: nano antiwear agent of the present invention is made by the following weight proportion raw material: nano metal particulate 50 grams, detergent-dispersant additive 100 grams, oxidation inhibitor 100 grams, organic polymer 300 grams, thinner 90000 grams.Wherein, above-mentioned nano metal particulate is two kinds or a two or more mixture (i.e. two kinds or two or more combinations) in metal particle molybdenum, chromium, vanadium, titanium, aluminium, the cerium, and the particle diameter of nano metal particulate is 1～100nm.For example, the nano metal particulate can be the combination of metal particle chromium, vanadium, titanium, aluminium.The particle diameter of nano metal particulate can be 70～80nm, perhaps can be 10～30nm.Detergent-dispersant additive is the combination of wherein a kind of in middle base number calcium mahogany sulfonate, sulfur phosphorization polyisobutylene titanate salt, calcium sulfenyl phenolate, mono butonediimide ashless, the many succimides of polyisobutene, the middle basicity alkyl calcium salicylate or two kinds.For example, detergent-dispersant additive can be sulfur phosphorization polyisobutylene titanate salt, can also be the combination of calcium sulfenyl phenolate and mono butonediimide ashless.Oxidation inhibitor is the combination of wherein a kind of in the two octyl group basic zinc salt of sulphur phosphorus, 2,6 ditertiary butyl p cresol, thiadiazoles derivative, p-tert-butylphenol, tri-isopropanolamine, the two octadecyl esters of thio-2 acid or two kinds.For example, oxidation inhibitor can be 2,6 ditertiary butyl p cresol, can also be the combination of thiadiazoles derivative and p-tert-butylphenol.Organic polymer is the combination of wherein a kind of in ethylene-propylene copolymer, polyacrylic ester, polyisobutene, the polymethacrylate or two kinds.For example, organic polymer can be polymethacrylate, can also be the combination of polyacrylic ester and polyisobutene.The molecular weight of organic polymer can be 200～5000.Thinner is the combination of wherein a kind of in 150ZN base oil, 200ZN base oil, 150SN base oil, the 200SN base oil or two kinds.For example, thinner can be the 150SN base oil, can also be the combination of 200ZN base oil and 150SN base oil.The method for preparing high-efficiency energy-saving nano antiwear agent may further comprise the steps: (1) places reactor with nano metal particulate, detergent-dispersant additive, oxidation inhibitor, organic polymer, thinner by above-mentioned weight proportion, heat to 45 ℃ (can also select 120 ℃ for use) stirring reaction 1 hour (can also select for use 3.5 hours).(2) be that 2Mpa (can also select 100Mpa for use), flow are the high pressure plunger pump of 10L/min (can also select 160L/min for use) with the reactant operating pressure, the circulation high-voltage high-speed is from pump outlet nozzle jet spread 1 hour (can also select for use 3.5 hours).(3) be that the ultrasonic drilling machine of 800W (can also select 2000W for use) disperses with output rating again, the time be 0.5 hour (can also select for use 5 hours) promptly, product forms stabilized nano metal eutectic ion organic compound colloid.
Embodiment 3: nano antiwear agent of the present invention is made by the following weight proportion raw material: nano metal particulate 500 grams, detergent-dispersant additive 10000 grams, oxidation inhibitor 9000 grams, organic polymer 3500 grams, thinner 400000 grams.Its preparation method is with embodiment 1 (perhaps with embodiment 2).
Embodiment 4: nano antiwear agent of the present invention is made by the following weight proportion raw material: nano metal particulate 1 gram, detergent-dispersant additive 150 grams, oxidation inhibitor 200 grams, organic polymer 150 grams, thinner 80500 grams.Its preparation method is with embodiment 1 (perhaps with embodiment 2).
Embodiment 5:A, make the lubrication oil antiwear agent with nano antiwear agent of the present invention, according to weight ratio, the nano antiwear agent with 10% mixes with 90% lubricating oil, and (add temperature can be 70 ℃～80 ℃) stirs through heating and form.Nano antiwear agent is the stabilized nano metal eutectic ion organic compound colloid of the present invention's preparation.Lubricating oil adopts 350SN base oil, 500SN basis wet goods.B, make nano lubricating oil again with the lubrication oil antiwear agent of making in the present embodiment 5, according to weight ratio, the lubrication oil antiwear agent with 0.6% mixes with 99.4% lubricating oil, and stirring through heating forms.
Embodiment 6:A, make the extreme pressure gear oil anti-wear agent with nano antiwear agent of the present invention, according to weight ratio, the nano antiwear agent with 20% mixes with 80% lubricating oil, and stirring through heating forms.B, make extreme pressure gear oil again with the extreme pressure gear oil anti-wear agent of making in the present embodiment 6, according to weight ratio, the extreme pressure gear oil anti-wear agent with 0.8% mixes with 99.2% lubricating oil, and stirring through heating forms.
Embodiment 7:A, make the water-soluble anti-wear agent of extreme pressure with nano antiwear agent of the present invention, according to weight ratio, the nano antiwear agent with 15% mixes with 85% lubricating oil, and stirring through heating forms.B, make the water-soluble machining oil of extreme pressure again with the water-soluble anti-wear agent of making in the present embodiment 7 of extreme pressure, according to weight ratio, the water-soluble anti-wear agent of 0.6% extreme pressure is mixed with 99.4% lubricating oil, stirring through heating forms.
Nano antiwear agent the key technical indexes of the present invention sees Table 1.
Table 1 high-efficiency energy-saving nano antiwear agent the key technical indexes
After testing, its every technical indicator meets the technical requirements of company standard.
Claims (8)
1, a kind of high-efficiency energy-saving nano antiwear agent is characterized in that it is made by the following weight proportion raw material:
1～500 part of nano metal particulate
100～10000 parts of detergent-dispersant additives
100～10000 parts in oxidation inhibitor
100～5000 parts of organic polymers
80000～500000 parts of thinners
Wherein, above-mentioned nano metal particulate is two kinds or a two or more mixture in metal particle molybdenum, chromium, vanadium, titanium, aluminium, the cerium; Detergent-dispersant additive is the combination of wherein a kind of in middle base number calcium mahogany sulfonate, sulfur phosphorization polyisobutylene titanate salt, calcium sulfenyl phenolate, mono butonediimide ashless, the many succimides of polyisobutene, the middle basicity alkyl calcium salicylate or two kinds; Oxidation inhibitor is the combination of wherein a kind of in the two octyl group basic zinc salt of sulphur phosphorus, 2,6 ditertiary butyl p cresol, thiadiazoles derivative, p-tert-butylphenol, tri-isopropanolamine, the two octadecyl esters of thio-2 acid or two kinds; Organic polymer is the combination of wherein a kind of in ethylene-propylene copolymer, polyacrylic ester, polyisobutene, the polymethacrylate or two kinds; Thinner is the combination of wherein a kind of in 150ZN base oil, 200ZN base oil, 150SN base oil, the 200SN base oil or two kinds.
2, nano antiwear agent according to claim 1 is characterized in that it is made by the following weight proportion raw material:
250～300 parts of nano metal particulates
5000～6000 parts of detergent-dispersant additives
5000～6000 parts in oxidation inhibitor
3000～4000 parts of organic polymers
200000～300000 parts of thinners.
3, nano antiwear agent according to claim 1 and 2, the particle diameter that it is characterized in that above-mentioned nano metal particulate is 1～100nm.
4, nano antiwear agent according to claim 1 and 2, the molecular weight that it is characterized in that above-mentioned organic polymer is 200～5000.
5, a kind of method for preparing the described high-efficiency energy-saving nano antiwear agent of claim 1 is characterized in that it may further comprise the steps:
(1) nano metal particulate, detergent-dispersant additive, oxidation inhibitor, organic polymer, thinner are placed reactor by above-mentioned weight proportion, heat to 45 ℃～120 ℃ stirring reaction 1～3.5 hour;
(2) be that 2～100Mpa, flow are the high pressure plunger pump of 10～160L/min with the reactant operating pressure, circulation high-voltage high-speed jet spread 1～3.5 hour;
(3) be that the ultrasonic drilling machine of 800～2000W disperses with output rating again, the time be 0.5～5 hour promptly.
6, a kind of lubrication oil antiwear agent of making of the described high-efficiency energy-saving nano antiwear agent of claim 1 is characterized in that according to weight ratio, the nano antiwear agent with 10% mixes with 90% lubricating oil, and stirring through heating forms.
7, a kind of extreme pressure gear oil anti-wear agent of making of the described high-efficiency energy-saving nano antiwear agent of claim 1 is characterized in that according to weight ratio, the nano antiwear agent with 20% mixes with 80% lubricating oil, and stirring through heating forms.
8, a kind of water-soluble anti-wear agent of making of the described high-efficiency energy-saving nano antiwear agent of claim 1 of extreme pressure is characterized in that according to weight ratio, the nano antiwear agent with 15% mixes with 85% lubricating oil, and stirring through heating forms.