CN100569983C - 一种Cr-Mn-Ti齿轮钢的制备方法 - Google Patents
一种Cr-Mn-Ti齿轮钢的制备方法 Download PDFInfo
- Publication number
- CN100569983C CN100569983C CNB2008100148751A CN200810014875A CN100569983C CN 100569983 C CN100569983 C CN 100569983C CN B2008100148751 A CNB2008100148751 A CN B2008100148751A CN 200810014875 A CN200810014875 A CN 200810014875A CN 100569983 C CN100569983 C CN 100569983C
- Authority
- CN
- China
- Prior art keywords
- steel
- refining
- furnace
- pinion
- vacuum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
牌号 | C | Si | Mn | Cr | S | P | Ti |
20CrMnTiH | 0.17~0.23 | 0.17~0.37 | 0.8~1.15 | 1.0~1.35 | ≤0.035 | ≤0.035 | 0.04~0.10 |
试样编号 | C | Si | Mn | Cr | S | P | Ti |
1 | 0.20 | 0.21 | 0.86 | 1.03 | 0.007 | 0.011 | 0.030 |
2 | 0.21 | 0.23 | 0.88 | 1.05 | 0.008 | 0.009 | 0.035 |
3 | 0.20 | 0.27 | 0.90 | 1.09 | 0.005 | 0.014 | 0.033 |
20CrMnTiH | 0.20 | 0.26 | 0.92 | 1.09 | 0.008 | 0.013 | 0.062 |
试样编号 | 初炼温度,℃ | 精炼温度,℃ | 精炼时间,min | 真空度,Pa | 真空时间,min | 开轧温度,℃ | 终轧温度,℃ |
1 | 1645 | 1575 | 33 | 140 | 20 | 1220 | 900 |
2 | 1630 | 1560 | 35 | 140 | 20 | 1200 | 896 |
3 | 1650 | 1665 | 30 | 140 | 20 | 1205 | 890 |
Claims (1)