CN100560850C - Environment protection spinning thread wax ring and preparation method thereof

Info

Publication number: CN100560850C
Application number: CNB2007100277404A
Authority: CN
Inventors: 杨建�
Original assignee: Individual
Current assignee: Individual
Priority date: 2007-04-24
Filing date: 2007-04-24
Publication date: 2009-11-18
Anticipated expiration: 2027-04-24
Also published as: CN101050596A

Abstract

Environment protection spinning thread wax ring of the present invention and preparation method thereof belongs to fiber, yarn, the physical treatment field of line, in vegetalitas wax, make by adding heating paraffin, in vegetalitas wax, pass through to add the paraffin of different proportion, neither too hard, nor too soft, good mouldability is arranged, can not form little powder, vegetalitas wax 0.1%-99.9%, paraffin 0.1%-99.9%, vegetable oil 0%-99.8%, said components is put into no pressure by weight percentage, in the unsealed container of heating, be warmed to, all in the dissolving back perfusion wax ring mould at 60～110 ℃, taking-up can be packed use after being cooled to normal temperature, the present invention can satisfy the textile machine instructions for use, and compliance with environmental protection requirements makes the knitted cloth of producing, blast hole obviously reduces, cost-saved, improve the knitted cloth percentage of A-class goods, cost performance is more apparent superior.

Description

Environment protection spinning thread wax ring and preparation method thereof

Technical field

Environment protection spinning thread wax ring of the present invention and preparation method thereof belongs to the physical treatment field to fiber, yarn, line, particularly relates to a kind of spinning thread wax ring that uses in the fabrication processes such as knitting, woolens that acts on.

Background technology

Spinning thread wax ring is used to turn over the cotton that is climbed on the yarn machine, make the cotton surface contain the paraffin of certain deal, many one deck barrier films between cotton and contactant, reduce cotton generation of static electricity in running, reduce the workshop and fly hair and the generation of knitting process broken string phenomenon, make the knitted cloth of producing, blast hole reduces.The spinning thread wax ring that tradition is used is to make with high melting-point paraffin adding LMP paraffin or industrial wax; paraffin is the high more product of molten point in principle; the also corresponding raising of softening point and hardness; if want the high LMP paraffin of additional proportion or a large amount of grease deliquescing to get terrible; be difficult to meet the requirement of production; in turning over the cotton process, change because of temperature; low temperature particularly; the weather of low humidity forms little powder easily and can not adhere to well on the cotton; depending merely on paraffin does lubricatedly can not to satisfy production requirement; the oily wax circle that spins that the mineral grease is made appears adding; but mineral lubricating oil all has in order to improve the instructions for use that winter or cold district reduce condensation point; add the pour point depression additive; and the mineral oil that has added the pour point depression additive dissolves in the add-back paraffin once more; the oily wax circle of producing that spins; can make that paraffin can only become small crystal in the product; stop it to get together alternately and form the network structure ability; it is loosely organized; the moulding rate variance; can't add OIL IN LUBRICATING OIL PRODUCTION in a large number especially; can not adhere to well on the cotton so in turning over the cotton process, form little powder easily; and in use major part can become small powder and is scattered on ground and the knitting machine; particularly on loom pinprick and the electronic detectors; increase the knitting machine outage rate; cloth defect rate and workman's clearing times; reduce generation efficient and increase labor strength again; use a large amount of paraffin simultaneously; be unfavorable for environmental protection, influence the quality of knitted cloth.

Summary of the invention

The objective of the invention is to avoid the deficiencies in the prior art part and provide a kind of mixture that adheres on the cotton comparatively even, not playing powder again is scattered on ground and the loom, save cost, improve the knitted cloth percentage of A-class goods, play reduce yarn in knitting process with the environment protection spinning thread wax ring of coefficient of friction between metal or the pottery and preparation method thereof.

The objective of the invention is to reach by following measure, the present invention makes by adding heating paraffin in vegetalitas wax, and is by adding the paraffin of different proportion, neither too hard, nor too soft in vegetalitas wax, and good mouldability is arranged, and can not form little powder.

The percentage by weight of vegetalitas wax and paraffin is formed,

Vegetalitas wax 0.1%-99.9%,

Paraffin 0.1%-99.9%,

Vegetable oil 0%-99.8%,

Said components is put into no pressure, the unsealed container of heating by weight percentage, be warmed to 60～110 ℃, all in the dissolving back perfusion wax ring mould, take out after cooling to room temperature and can pack use.

Vegetalitas wax adopts palm wax, can be stearic acid, double pressed stearic acid, triple pressed stearic acid, also can be palmitic acid.

Paraffin adopts complete concise paraffin wax white, half concise paraffin wax white, grain wax, food packing wax, also can be industrial wax, saponified wax, and soft wax at least a can be used separately, also can combined hybrid use.In paraffin, also can add the appearance color that various nontoxic dyes change environmental protection wax circle, be convenient to identification and use.

Vegetable oil adopts margarine, can be at least a of artificial white (Huang) cream, shortening, plant butter, palm oil, rapeseed oil, soybean oil, cottonseed oil and corn oil, can use separately, also can combined hybrid use.

Turning over the cotton that environment protection spinning thread wax ring climbed on the yarn machine, because palm wax hardness height, softening point is also high, can not change the whole solution temperature of environmental protection wax circle again, so can add a large amount of greases solves spinning thread wax ring and only can not add grease in a large number and come collaborative lubrication by paraffin, because of palm wax has this characteristic, but the also higher LMP saponified wax of the additional proportion soft durometer of regulating environmental protection wax circle, viscosity is increased, the mixture that adheres on the cotton is comparatively even, not playing powder again is scattered on ground and loom and the pinprick, make the wax lipoprotein mixture barrier film that has one deck thicker between cotton and contactant, more can reduce coefficient of friction, reduce cotton generation of static electricity in running, reduce the workshop and fly hair and the generation of knitting process broken string phenomenon, the knitted cloth blast hole ratio of producing is obviously reduced.Cost-saved like this, improve the knitted cloth percentage of A-class goods, cost performance is more apparent superior.The present invention more plays help to ecological spinning, environmental protection weaving and the Huaihe River authentication of organic cotton weaving mark, can improve the human contaminated environment life style that relies on oil and byproduct thereof again.

The present invention is 20～30 ℃ of room temperatures, and the vegetalitas wax that result of use is best and the percentage by weight of paraffin are formed,

Vegetalitas wax 26～33%,

Paraffin 37～45%,

Vegetable oil 25～35%,

Vegetalitas wax adopts palm wax, with palm wax 26～33%, and the paraffin wax white 26～33% in 37～45% the paraffin wherein; Saponified wax 8～11%; Soft wax 0.9～1.4%, the wherein artificial yellow cream 18～25% in 25～35% the vegetable oil; Artificial white butter 7～10%, said components is put into no pressure, the unsealed container of heating by Different Weight percentage, be warmed at 80～85 ℃, all in the dissolving back perfusion wax ring mould, take out after cooling to room temperature and can pack use, when using room temperature to be 20～30 ℃, can obtain the environment protection spinning thread wax ring of top performance.

The present invention can satisfy the textile machine instructions for use, compliance with environmental protection requirements, with vegetable raw material is main production, reduce raw mineral materials and use, reduce cotton generation of static electricity, minimizing workshop in running and fly hair and the generation of knitting process broken string phenomenon, make the knitted cloth of producing earth pollution, blast hole obviously reduces, cost-saved, improve the knitted cloth percentage of A-class goods, cost performance is more apparent superior.

The specific embodiment

The invention will be further described below in conjunction with embodiment.

Embodiment 1:

The present invention forms vegetal palm wax 60% and paraffin 40% by weight percentage, wherein adopt paraffin wax white 19.5%, saponified wax 20%, soft wax 0.5% to mix and form in 40% the paraffin, said components is put into no pressure, the unsealed container of heating by weight percentage, be warmed at 60 ℃, all in the dissolving back perfusion wax ring mould, take out after cooling to room temperature and can pack use.

Embodiment 2:

The present invention forms vegetal palm wax 70% and paraffin 30% by weight percentage, wherein adopt paraffin wax white 9% in 30% the paraffin, saponified wax 20%, soft wax 1% mixes to be formed, said components is put into no pressure, the unsealed container of heating by weight percentage, be warmed at 80 ℃, all in the dissolving back perfusion wax ring mould, take out after cooling to room temperature and can pack use.

Embodiment 3:

The present invention forms vegetal palm wax 60% and paraffin 40% by weight percentage, wherein adopt paraffin wax white 10% in 40% the paraffin, saponified wax 30% is mixed and is formed, said components is put into no pressure, the unsealed container of heating by weight percentage, be warmed at 110 ℃, all in the dissolving back perfusion wax ring mould, take out after cooling to room temperature and can pack use.

Embodiment 4:

The present invention is with vegetal palm wax 30%, paraffin 35%, margarine 35% is formed by weight percentage, and paraffin wax white 24.75% is wherein adopted in available artificial white butter or artificial yellow cream manufacturing in 35% the paraffin, saponified wax 9.75%, soft wax 0.5% mixes to be formed, and said components is put into no pressure, the unsealed container of heating by weight percentage, is warmed at 85 ℃, all in the dissolving back perfusion wax ring mould, take out after cooling to room temperature and can pack use.

Embodiment 5:

The present invention is with vegetal palm wax 31%, paraffin 39.40%, margarine 29.60% is formed by weight percentage, wherein adopt paraffin wax white 28.35% in 39.40% the paraffin, saponified wax 9.78%, soft wax 1.27% mixes to be formed, wherein adopt artificial white butter 7.40% in 29.60% the margarine, artificial yellow cream 22.2% mixes to be formed, said components is put into no pressure, the unsealed container of heating by weight percentage, be warmed at 85 ℃, all in the dissolving back perfusion wax ring mould, take out after cooling to room temperature and can pack use.

Embodiment 6:

The present invention is with vegetal palm wax 30%, paraffin 38%, margarine 32% is formed by weight percentage, wherein adopt paraffin wax white 31% in 38% the paraffin, saponified wax 6%, soft wax 1% mixes to be formed, wherein adopt artificial yellow cream 30% in 32% the margarine, palm oil or rapeseed oil 2% mix to be formed, said components is put into no pressure, the unsealed container of heating by weight percentage, be warmed at 85 ℃, all in the dissolving back perfusion wax ring mould, take out after cooling to room temperature and can pack use.

Claims

1, a kind of environment protection spinning thread wax ring is characterized in that the percentage by weight composition,

Vegetalitas wax 26～33%,

Paraffin 37～45%,

Vegetable oil 25～35%,

Vegetalitas wax is palm wax,

Paraffin is at least a of complete concise paraffin wax white, half concise paraffin wax white, saponified wax, soft wax, and vegetable oil is a margarine, shortening, plant butter, palm oil, rapeseed oil, soybean oil, cottonseed oil, corn oil at least a.

2, environment protection spinning thread wax ring according to claim 1 is characterized in that

Vegetalitas wax adopts palm wax, the paraffin wax white 26～33% in the paraffin, saponified wax 8～11%, soft wax 0.9～1.4%, the artificial yellow cream 18～25% in the vegetable oil, artificial white butter 7～10%.

3, a kind of preparation method of environment protection spinning thread wax ring, vegetalitas wax 26～33%, paraffin 37～45%, vegetable oil 25～35%, said components is put into no pressure, the unsealed container of heating by weight percentage, be warmed to, all in the dissolving back perfusion wax ring mould at 60～110 ℃, take out after cooling to room temperature and can pack use

Vegetalitas wax is palm wax, and paraffin is at least a of complete concise paraffin wax white, half concise paraffin wax white, saponified wax, soft wax, and vegetable oil is a margarine, shortening, plant butter, palm oil, rapeseed oil, soybean oil, cottonseed oil, corn oil at least a.

4, the preparation method of environment protection spinning thread wax ring according to claim 3 is characterized in that vegetalitas wax adopts palm wax, the paraffin wax white 26～33% in the paraffin, saponified wax 8～11%, soft wax 0.9～1.4%, the artificial yellow cream 18～25% in the vegetable oil, artificial white butter 7～10%.