CN100557060C - C-Mn-Ti系热轧高强度高磁感性能钢的制造方法 - Google Patents
C-Mn-Ti系热轧高强度高磁感性能钢的制造方法 Download PDFInfo
- Publication number
- CN100557060C CN100557060C CNB2007100512527A CN200710051252A CN100557060C CN 100557060 C CN100557060 C CN 100557060C CN B2007100512527 A CNB2007100512527 A CN B2007100512527A CN 200710051252 A CN200710051252 A CN 200710051252A CN 100557060 C CN100557060 C CN 100557060C
- Authority
- CN
- China
- Prior art keywords
- hot
- steel
- magnetic induction
- manufacture method
- rolled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
C-Mn-Ti系热轧高强度高磁感性能钢的制造方法,它涉及微合金化钢制造领域。为解决现有技术所存在的成本较高,以及对轧制和卷取设备损害较大的问题,本发明所述热轧高强度高磁感性能钢的各组分的重量百分比为C:0.03%~0.15%、Si:≤0.15%、Mn:0.50%~1.40%、P:≤0.025%、S:≤0.015%、Ti:0.05%~0.15%、Al:0.02%~0.10%、N:≤0.010%,其余为Fe。其制造方法按下述步骤进行:a、铁水脱硫;b、转炉顶底复合吹炼;c、炉后吹氩气处理;d、浇注成板坯;e、热连轧机控轧控冷:选用热连轧机组设备,先将步骤d所制得的板坯加热至1230~1280℃;然后粗轧,粗轧结束温度为≥1100℃;然后精轧,终轧温度为850~930℃;钢板轧后采用层流冷却后卷取,卷取温度为580~650℃,制得热轧板卷。
Description
技术领域
本发明涉及微合金化钢制造领域,具体地指一种适应于大型水轮发电机转子磁轭部分所需的具备高强度(ReL≥600MPa)和高磁感性能的钢的制造方法。
背景技术
随着电力供需矛盾的日益突出,作为清洁无污染、可再生的水电已经成为我国解决能源问题的重要举措。随着我国西部大开发的深入,一大批三峡级的大型、巨型水电项目将在未来几十年内陆续开工建设,这些大型、巨型水电项目均需要单机容量70~80万千瓦级别的大型水轮发电机组,这就对其中发电机转子磁轭部分用钢提出了高强度、高磁感性能的要求。在本发明申请之前,专利号为98800888.2的中国发明专利记载了一种“基于低温板坯加热法生产具有高磁感应强度的晶粒择优取向电工钢板的方法”,其成分和工艺制度不足之处在于产线较长,从热轧钢板退火成冷轧钢板,最后还需要进行脱碳处理,生产周期长,能耗大,而且钢板含有较高含量的硅(Si)或者一定量的铜(Cu)、镍(Ni)、铬(Cr)、硼(B),合金成本较高,同时该发明涉及品种不具备高的拉伸强度。申请号为200480002119.7的中国发明专利介绍了一种“超高强度热轧钢及生产带材的方法”,其成分和工艺制度不足之处在于含有0.5%~1.0%的铬(Cr),而且生产工艺中需要将轧制温度控制在低于950℃,然后冷却至400℃或更低温度,其间保持在800℃与700℃之间的大于50℃/S的冷却速率,最后在250℃或更低温度下卷绕,这对于轧机和卷取设备的能力要求极高,且对设备损害较大,没有可操作性,同时该专利涉及品种不具备高的磁感性能。
发明内容
为解决现有技术所存在的成本较高,以及对轧制和卷取设备损害较大的问题,本发明提供了一种能满足高单机容量的大型水轮发电机转子中磁轭部分使用的屈服强度ReL≥600MPa,磁感性能B50≥1.5T的C-Mn-Ti系高强度高磁感性能钢的制造方法。
为实现上述目的,本发明所设计的C-Mn-Ti系热轧高强度高磁感性能钢,它由碳(C)、硅(Si)、锰(Mn)、磷(P)、硫(S)、钛(Ti)、铝(Al)、氮(N)和铁(Fe),各组分的重量百分比为C:0.03%~0.15%、Si:≤0.15%、Mn:0.50%~1.40%、P:≤0.025%、S:≤0.015%、Ti:0.05%~0.15%、Al:0.02%~0.10%、N:≤0.010,其余为Fe及不可避免的夹杂。
本发明的C-Mn-Ti系热轧高强度高磁感性能钢中各合金成份的作用机理如下:
本发明的碳(C)含量为0.03%~0.15%,碳是钢中不可缺少的提高钢材强度的元素之一,同时可以与钢中Ti作用形成微合金碳化物,起到析出强化作用,碳含量过高会影响到钢的磁感性能。将碳含量限定在0.03~0.15%,既可提高钢的强度,保证钢的磁感性能,又适合生产操作。
本发明的锰(Mn)含量为0.50%~1.40%,可降低奥氏体转变成铁素体的相变温度,扩大热加工温度区域,有利于细化铁素体晶粒尺寸,提高钢的屈服强度和抗拉强度。
本发明的磷(P)含量≤0.025%、硫(S)含量≤0.015%,磷在钢中具有容易造成偏析、降低磁感性能等不利影响。硫易与锰结合生成MnS夹杂,影响钢的磁感性能和塑性。因此,本发明应尽量减少磷、硫元素对钢性能的不利影响,通过对铁水进行深脱硫预处理等手段,控制磷、硫含量,从而减轻其不利影响。
本发明的硅(Si)含量≤0.15%,硅对热连轧板卷表面质量有不利影响,因此本发明应尽量降低钢中硅含量。
本发明的钛(Ti)含量为0.08%~0.18%,钛是一种强烈的碳化物和氮化物形成元素,在钢重新加热中阻止奥氏体晶粒长大,在高温奥氏体区粗轧时TiN和TiC析出,可有效抑制奥氏体晶粒长大,同时析出的TiN和TiC可以有效的提高钢板强度。
本发明的铝(Al)含量为0.02~0.10%,其主要作用是脱去钢水中的氧,防止钛被氧化而失效。
本发明的氮(N)含量≤0.01%,属于转炉钢中正常残余,可以与钢中钛(Ti)结合形成TiN析出,起到抑制奥氏体晶粒长大和析出强化作用。
上述C-Mn-Ti系热轧高强度高磁感性能钢的制造方法按下述步骤进行:a、铁水脱硫;b、转炉顶底复合吹炼;c、炉后吹氩气处理;d、浇注成板坯;e、热连轧机控轧控冷。其中,所述热连轧控轧控冷在热连轧机组进行,先将步骤d所制得的板坯加热至1230~1280℃;然后粗轧,粗轧结束温度为≥1100℃;然后精轧,终轧温度为850~930℃;钢板轧后采用层流冷却后卷取,卷取温度为580~650℃,制得热轧板卷。
本发明所述C-Mn-Ti系热轧高强度高磁感性能钢,不含有铜(Cu)、镍(Ni)、铬(Cr)、硼(B)等成份,大大节约原料成本;且轧制温度和卷取温度较高,可以降低钢板形变抗力,在轧制薄规格(1.6~5mm)高强度(ReL≥600MPa)钢过程中减小设备负荷,减少了对轧制设备和卷取设备的损害。试验表明,本发明的C-Mn-Ti系热轧高强度高磁感性能钢的屈服强度ReL≥600MPa,抗拉强度Rm≥700MPa,磁感性能B50≥1.50T,可以满足大型水轮发电机转子磁轭用高强度高磁感性能钢的需求。
具体实施方式
以下结合具体实施例对本发明的C-Mn-Ti系热轧高强度高磁感性能钢及其生产方法作进一步的详细描述:
表1本发明钢的化学成分,wt%
成份 | C | Si | Mn | P | S | Ti | Al | N |
1 | 0.064 | 0.03 | 0.769 | 0.016 | 0.005 | 0.063 | 0.034 | 0.007 |
2 | 0.074 | 0.022 | 0.776 | 0.011 | 0.004 | 0.077 | 0.047 | 0.008 |
3 | 0.10 | 0.022 | 0.533 | 0.015 | 0.005 | 0.079 | 0.057 | 0.007 |
表1列出了本发明可用于大型水轮发电机转子磁轭用钢的几种具体实例的化学成份。
这几种高强度高磁感性能用钢的制造方法如下:首先,采用铁水深脱硫技术,在转炉上进行顶底复合吹炼,使铁水中的S≤0.005%,钢水在炉后吹氩气处理过程中,进行微合金化,使钢中的化学成份满足表1的要求,余量为Fe及不可避免的夹杂;然后,将满足表1要求的钢水浇注成200~300mm×900~1550mm断面的板坯;最后,将该板坯在热连轧机上采用控轧控冷处理的热连轧生产工艺,将其轧制成热轧板。
采用控轧控冷处理的热连轧生产工艺时,为充分发挥微合金元素在钢中的作用和保证钢板的尺寸规格、表面质量,利用大功率轧机(3/4连续式热带钢轧机组,单机架最大功率为5000kw以上)的设备能力,减少轧制道次,提高道次压下率。先将板坯加热至1230~1280℃。粗轧累计压下率为80~90%,粗轧结束温度为≥1100℃。粗轧后进行精轧,终轧温度为850~930℃;经层流冷却后进行卷取,卷取温度为550~620℃,制得板厚为1.6~5mm的热轧板。
本发明C-Mn-Ti系热轧高强度高磁感性能钢的热轧板的生产工艺参数和试验结果见表2。
表2本发明钢热连轧板制备方法及试验结果
注:表2的成份1、2、3与表1中的成份1、2、3为对应关系。
实施例列举了三种成份的C-Mn-Ti系热轧高强度高磁感性能钢,分别对应于表1中的成份1、2、3。试验按热轧板工艺生产,其中成份1轧制了较厚和较薄的两种规格。从表2反映出的性能来看,各成份的1.6~5mm热轧板都能满足屈服强度ReL≥600MPa,磁感性能B50≥1.50T。
Claims (4)
1、一种C-Mn-Ti系热轧高强度高磁感性能钢的制造方法,其特征在于,钢由C、Si、Mn、P、S、Ti、Al、N和Fe组成,各组分的重量百分比为C:0.03%~0.15%、Si:≤0.15%、Mn:0.50%~1.40%、P:≤0.025%、S:≤0.015%、Ti:0.05%~0.15%、Al:0.02%~0.10%、N:≤0.010%,其余为Fe;
上述钢的制造方法按下述步骤进行:a、铁水脱硫;b、转炉顶底复合吹炼;c、炉后吹氩气处理;d、浇注成板坯;e、热连轧机控轧控冷;其中,所述热连轧控轧控冷在热连轧机组进行,先将步骤d所制得的板坯加热至1230~1280℃;然后粗轧,粗轧结束温度为≥1100℃;然后精轧,终轧温度为850~930℃;钢板轧后采用层流冷却后卷取,卷取温度为580~650℃,制得热轧板卷。
2、根据权利要求1所述的C-Mn-Ti系热轧高强度高磁感性能钢的制造方法,其特征在于各组分的重量百分比为C:0.064%、Si:0.03%、Mn:0.769%、P:0.016%、S:0.005%、Ti:0.063%、Al:0.034%、N:0.007%,其余为Fe。
3、根据权利要求1所述的C-Mn-Ti系热轧高强度高磁感性能钢的制造方法,其特征在于各组分的重量百分比为C:0.074%、Si:0.022%、Mn: 0.776%、P:0.011%、S:≤0.004%、Ti:0.077%、Al:0.047%、N:0.008%,其余为Fe。
4、根据权利要求1所述的C-Mn-Ti系热轧高强度高磁感性能钢的制造方法,其特征在于各组分的重量百分比为C:0.10%、Si:0.022%、Mn:0.533%、P:0.015%、S:0.005%、Ti:0.079%、Al:0.057%、N:0.007%,其余为Fe。