CN100537167C - Process of forming grooves in the bottom and side of anode carbon block for aluminium electrolysis - Google Patents
Process of forming grooves in the bottom and side of anode carbon block for aluminium electrolysis Download PDFInfo
- Publication number
- CN100537167C CN100537167C CNB2006100445250A CN200610044525A CN100537167C CN 100537167 C CN100537167 C CN 100537167C CN B2006100445250 A CNB2006100445250 A CN B2006100445250A CN 200610044525 A CN200610044525 A CN 200610044525A CN 100537167 C CN100537167 C CN 100537167C
- Authority
- CN
- China
- Prior art keywords
- moulding
- piece
- template
- fluting
- bayonet socket
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention is process of producing prebaked anode block with grooves in bottom or side through die pressing under vibrating condition. The production process includes mainly a vertical paste distributing step capable of maintaining the flowability of the paste and a secondary cooling step to meet the requirement of demolding on the paste curing state. The production process has easy demolding, low power consumption and high production efficiency.
Description
Technical field
The present invention relates to a kind of grooving technology of material with carbon element anode, particularly relate to the die methods grooving technology of a kind of used for aluminium electrolysis pre-baked anode carbon blocks bottom or sidepiece.
Background technology
Aluminum electrolysis industry all need be with pre-baked anode carbon blocks as anode electrolytic cell both at home and abroad.The anode carbon block bottom of adopting at present extensively all is flat, thereby exists programming rate slow and have bigger anode bottom air film resistance, increases power consumption.After using the anode carbon block of bottom or sidepiece trough of belt, it is fast and have pre-baked anode carbon blocks than primary anode bottom air film resistance to obtain programming rate, thereby reduces power consumption and the charcoal piece consumes.
The anode carbon block of bottom or sidepiece trough of belt, fluting is generally vertical or horizontal perforation 1～3 road, and the bottom equidistantly is provided with, and groove width is about 10mm, and the groove height is 1/3 of a charcoal tile height, about 200mm, the high 5～30mm of the comparable other end of groove one end.
Charcoal piece bottom slot technology is after the living piece roasting of prebaked anode becomes ripe at present, re-uses plant equipment such as milling cutter or circular saw, slots in the anode bottom.Because the material with carbon element hardness after the high-temperature roasting is big especially, hot property is good especially, and product itself does not allow water cooling, so it is carried out machining, power consumption is big, cost is high, efficient is low.
Summary of the invention
Technical problem to be solved by this invention provides a kind of anode carbon block for aluminium electrolysis bottom or sidepiece die methods grooving technology, under the prerequisite that does not influence product quality and performance, processing object changes living piece into by ripe, and grooving processes is energy-saving and cost-reducing, output is big, efficient is high.
Anode carbon block for aluminium electrolysis of the present invention bottom or sidepiece grooving technology, it is characterized in that in vibration shape machine moulding moulding box, placing the fluting template, moulding moulding box opposed inside wall has bayonet socket, the bayonet socket of at least one side connects sidewall, the fluting template is engaged in the bayonet socket of moulding moulding box, and at least one end of fluting template passes sidewall by the bayonet socket that the moulding moulding box connects, the moulding thickener of suitable temperature with becoming band distributed uniform, cloth is spread on the shaping mould case vertically, vibration shape machine die head and tup are deep in the moulding moulding box then, with the moulding moulding box, the fluting template is vibrated together, make the thickener moulding piece of making a living, vibration shape machine die head and tup are mentioned then, the moulding moulding box is mentioned, giving birth to piece is shifted onto on the living piece pallet by push pedal together with the fluting template, send into rapidly in 15～50 ℃ of cooling waters and cooled off 50～100 seconds, the fluting template is extracted in water outlet rapidly out from give birth to piece, give birth to piece and pallet thereof at last and send into secondary cooling in the cooling water, qualified living piece carries out the ripe piece of high-temperature roasting and is qualified products.
Preferably have hole or groove on the above fluting template.
It is slightly high that one end of fluting template cans be compared to the other end most, general high 5～30mm, and the fluting template is preferably extracted out from give birth to piece from high-end, and the madial wall bayonet socket of the moulding moulding box of the high-end correspondence of the template of therefore slotting is for connecting the bayonet socket of sidewall.The fluting template is passed from sidewall, and the template that is very beneficial for slotting is extracted out from sidepiece, thereby can guarantee product quality.
Because general mould grooving technology has certain influence to product quality,, porosity closely knit as bulk density, compression strength, bight, resistivity, non-oxidizability, heat resistanceheat resistant are shaken, outward appearance etc.In the vibration moulding process, the thermoplasticity thickener is kept certain flowability, could guarantee the product inherent quality; Have certain cure profile, could guarantee the product appearance quality.After vibration moulding moulding box bottom was provided with the fluting template, the bottom surface was separated, and the flowing space reduces, infringement thickener flowability; The demoulding of fluting template need be vibrated thickener and be cured to a certain degree, and flowability disappears substantially, otherwise very easily causes demoulding scuffing of moulding green compact and plastic deformation.Because can there be above problem in the mould grooving technology, so the present invention fully considers, has carried out technological improvement at above problem.
The one, use formed in mould method, under the vibration pressure condition, the prebaked anode that is shaped as bottom and sidepiece trough of belt is given birth to piece.
The 2nd, adopt banded vertically even thickener distributing method, to keep the thickener flowability; Adopt secondary cooling method, to satisfy the requirement of demoulding action to the thickener solid state.Hole or groove that different shape can be arranged on the fluting template are as the thickener flow channel.The groove that mould is opened can connect with charcoal piece bottom surface, also can not connect.Do not connect, can be left to follow-up reprocessing.
The 3rd, the fluting template can be from the sidepiece demoulding, also can be from the bottom demoulding.The fluting template can coat paper, aluminium foil, plastic foil etc. and prevent adhesion and scuffing, conveniently stripped material.
The 4th, for the template demoulding facility of slotting, the moulding moulding box of vibration shape machine carried out adapting to improved.
The slot material of template of the present invention can be a metal material, also can be nonmetal combustible material, as plank, fiberboard, particieboard and other resin material etc.Nonmetallic materials flutings template can not carried out the demoulding, directly send to divide after the high-temperature roasting and takes off scarfing cinder then.This promptly is second kind of scheme of the present invention: after living piece cools off for the first time, do not need to extract out the fluting template, directly carry out the cooling second time, roasting then.
Living piece carries out high-temperature roasting and carries out according to the prior art mode.
Outstanding advantage of the present invention is: time saving and energy saving, substantially do not change the moulding process of original flat prebaked anode, processing object changes living piece into by ripe, manufacturing process changes mould molding into by machining, simple, the demoulding is easy and convenient, reliable in quality, expense is low, and is energy-saving and cost-reducing, output is big, efficient is high.
Description of drawings
Fig. 1 is the prebaked anode side cut away view;
Fig. 2 is the prebaked anode end view;
Fig. 3 is a vibration shape forming machine mould schematic diagram;
Fig. 4 is the A portion structural representation among Fig. 3.
Among the figure: 1 anode block side, 2 through slots, 3 anode block end faces, 4 tups, 5 die heads, 6 moulding boxs, 7 conduction oils 8 fluting templates, the 9 vibration shape machines platform 10 bayonet sockets 11 oil pressure die clamps that shake
The specific embodiment
Fig. 1, prebaked anode shown in Figure 2 are the prior art product.
Vibration shape forming machine mould as shown in Figure 3 is known technology equipment except the shaping mould box structure improves to some extent, comprise bilateral oil pressure die clamp shown in Figure 4.
Moulding moulding box 6 is that the madial wall in relative both sides has bayonet socket 10, and wherein the bayonet socket of a side connects sidewall, right side as shown in Figure 3.One end of fluting template 8 is higher than the other end (30mm), the right side of high-end corresponding moulding moulding box.
Below be concrete operations technology:
(1) vibration shape machine moulding moulding box 6 promotes, and leaves the vibration shape machine platform 9 that shakes, and hovers in the vibration shape machine platform top that shakes;
(2) on vibration shape machine shakes platform 9, place fluting template 8 (can fix), and be positioned over the position of regulation by mark by aid;
(3) vibration shape machine moulding moulding box 6 falls, moulding moulding box bayonet socket 10 interlocks fluting template 8, and the fluting template embeds the moulding moulding box smoothly;
(4) vibration shape machine moulding moulding box secondary hovers;
(5) vibration shape machine moulding moulding box 6 continues to drop to vibration shape machine and shakes on the platform 9, and the position is errorless, and moulding moulding box and fluting template thereof are forced to be combined in vibration shape machine by the oil pressure die clamp 11 of vibration shape machine bilateral and shaken on the platform, and form one;
(6) the moulding thickener of suitable temperature (chuck on moulding box 6 walls in conduction oil temperature remain on 110 ℃-250 ℃), after metering, the distribution that becomes band, equably, vertically, cloth is spread on the shaping mould case in accordance with regulations;
(7) vibration shape machine die head 5 and tup 4 falls deeply to the moulding moulding box, and vibration shape machine running, and vibration shape machine die head and tup, moulding moulding box, fluting template tied together about 100 seconds (being generally 90～120 seconds) of vibration makes its moulding piece of making a living in accordance with regulations;
(8) vibration shape machine die head and tup are mentioned, and the moulding moulding box is mentioned, and give birth to piece and are shifted onto on the living piece pallet by push pedal (vibration shape machine other be provided with parts) together with the fluting template, and mark was also sent in 30 ℃ of cooling waters cooling rapidly 60 seconds;
(9) water outlet is extracted the fluting template out from giving birth to the piece sidepiece rapidly;
(10) give birth to piece and pallet thereof and send into secondary cooling in 30 ℃ of cooling waters rapidly, and to stipulating requirement, qualified living piece rolls off the production line;
(11) are qualified anode carbon block after the assay was approved through the ripe piece of 1150 ℃ of high-temperature roastings.
Can be provided with as if a hole or groove (omitting among the figure), as the thickener flow channel on the fluting template 8.
If the fluting template adopts nonmetal combustible material (plate, fiberboard, particieboard and other resin material etc.), above-mentioned steps (nine) can be omitted (can certainly extract the fluting template out), is burnt through high-temperature roasting fluting template, and the cleaning residue gets final product.
Claims (5)
1, anode carbon block for aluminium electrolysis bottom or sidepiece grooving technology, it is characterized in that in vibration shape machine moulding moulding box, placing the fluting template, moulding moulding box opposed inside wall has bayonet socket, the bayonet socket of at least one side connects sidewall, the fluting template is engaged in the bayonet socket of moulding moulding box, and at least one end of fluting template passes sidewall by the bayonet socket that the moulding moulding box connects, the moulding thickener of suitable temperature with becoming band distributed uniform, cloth is spread on the shaping mould case vertically, vibration shape machine die head and tup are deep in the moulding moulding box then, with the moulding moulding box, the fluting template is vibrated together, make the thickener moulding piece of making a living, vibration shape machine die head and tup are mentioned then, the moulding moulding box is mentioned, giving birth to piece is shifted onto on the living piece pallet by push pedal together with the fluting template, send into rapidly in 15～50 ℃ of cooling waters and cooled off 50～100 seconds, the fluting template is extracted in water outlet rapidly out from give birth to piece, give birth to piece and pallet thereof at last and send into secondary cooling in the cooling water, qualified living piece carries out the ripe piece of high-temperature roasting and is qualified products.
2, grooving technology according to claim 1 is characterized in that having hole or groove on the described fluting template.
3, grooving technology according to claim 1, it is characterized in that slotting an end of template than the high 5～30mm of the other end, the madial wall bayonet socket of the moulding moulding box of the high-end correspondence of fluting template is for connecting the bayonet socket of sidewall, and the fluting template is extracted out from give birth to piece from high-end.
4, anode carbon block for aluminium electrolysis bottom or sidepiece grooving technology, it is characterized in that in vibration shape machine moulding moulding box, placing the fluting template, the fluting template adopts nonmetal and combustible material, moulding moulding box opposed inside wall has bayonet socket, the bayonet socket of at least one side connects sidewall, the fluting template is engaged in the bayonet socket of moulding moulding box, and at least one end of fluting template passes sidewall by the bayonet socket that the moulding moulding box connects, the moulding thickener of suitable temperature with becoming band distributed uniform, cloth is spread on the shaping mould case vertically, vibration shape machine die head and tup are deep in the moulding moulding box then, with the moulding moulding box, the fluting template is vibrated together, make the thickener moulding piece of making a living, vibration shape machine die head and tup are mentioned then, the moulding moulding box is mentioned, giving birth to piece is shifted onto on the living piece pallet by push pedal together with the fluting template, send into rapidly in 15～50 ℃ of cooling waters and cool off 50～100 seconds, and then send into secondary cooling in the cooling water, qualified living piece carries out the ripe piece of high-temperature roasting and is qualified products.
5, grooving technology according to claim 4 is characterized in that having hole or groove on the described fluting template.