CN100531988C - Method for joining golf club head - Google Patents
Method for joining golf club head Download PDFInfo
- Publication number
- CN100531988C CN100531988C CNB2006101278999A CN200610127899A CN100531988C CN 100531988 C CN100531988 C CN 100531988C CN B2006101278999 A CNB2006101278999 A CN B2006101278999A CN 200610127899 A CN200610127899 A CN 200610127899A CN 100531988 C CN100531988 C CN 100531988C
- Authority
- CN
- China
- Prior art keywords
- assembly
- club head
- glof club
- scolder
- joint method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a joining method for a golf club head. Joining operation is conducted with hard brazing joining manufacture procedure and the method comprises a first component step, a second component step, a step in which a layer of active metal is covered on the first component and the second component and the active metal is suitable for joining with active metal welding material, and a step about joining operation of the first component and the second component, therefore, the first component is joined with the second component while shaping up. When implementing and using the joining method for the golf club head provided by the invention, processing cost of inlet protective gas and metal welding material can be effectively reduced and high temperature oxidation of the golf club head can be avoided, meanwhile, the golf club head can be processed in a continuous furnace, and therefore, whole capacity and yield can be effectively increased.
Description
Technical field
The present invention relates to a kind of joint method of glof club head, particularly relevant for a kind of joint method that can cut down finished cost and increase the glof club head of overall throughput and yield.
Background technology
Known golf clubs head structure mostly utilize be embedded cooperate or different welding manner in conjunction with a batting panel, yet above-mentioned combination has many shortcomings, for example, be embedded cooperation and cause the batting panel distortion easily, if the rod head noumenon of welding xenogenesis material and batting panel then can produce the compatible not enough problem of welding, and if use is known as the solder technology higher than the fusing point of weldment, more have or not method to keep its original machining accuracy before engaging, and the body of this glof club head and the composition surface of batting panel are difficult for smooth and bright and clean, in addition, the tissue property of body and batting panel is susceptible to also, and then cause stress concentrate and deflection big, so can't keep the structure machining accuracy before engaging, moreover, the body of this glof club head and the composition surface of batting panel are failed well bright and clean, so thereby need to use the shaping of finishing glof club head in the following process shaping.
Disappearance for the batting panel combined structure that overcomes known above-mentioned glof club head, known technology development the technology of directly utilizing the combination of high-intensity resin gluing at normal temperatures, yet, owing to be subject to the upper limit of high-intensity resin gluing bond strength, so though rod head noumenon and batting panel utilization gluing combination can be quickened processing procedure, but in the time of can't providing rod head noumenon to combine, has the stress of enough bond strengths for the supporting batting with batting panel.
So the rod head noumenon and the batting panel of known glof club head; also there is hard solder to close processing procedure as the worker's method that engages the two; but at present the hard solder connection process for as the utilization titanium as the material of glof club head; and when carrying out the hard solder connection process; because the scolder of easy high-temperature oxydation of workpiece itself and use contains titanium elements isoreactivity element again; so must add argon gas at vacuum drying oven or gas stove just can carry out with the oxidation of protection workpiece; yet the hard solder connection process uses vacuum drying oven or gas stove to do the hard solder connection process at present; promptly be for avoiding workpiece or scolder oxidation; if because workpiece or scolder oxidation; then both just can't produce the purpose that reaction reaches the hard solder combination; and when public hard solder connection process is done to engage for titanium; because of need vacuumizing just, vacuum drying oven can carry out the hard solder connection process; so it is not only time-consuming and reduce production capacity and the process that vacuumizes and be difficult for keyholed back plate; when being arranged slightly, gas leakage can't use with regard to making the workpiece oxidation stain in the whole vacuum drying oven; moreover; because gas stove must add argon shield and avoid workpiece or scolder oxidation to carry out the hard solder connection process smoothly; so cause the cost of argon shield that gas stove uses high; again; no matter be vacuum drying oven or gas stove is because of being all closed stove; so neither continuous oven height of its output as semi open model; select for use the titaniferous reactive metal scolder that needs vacuum or argon shield also expensive for process what is more, it is many to make that cost also increases.
Therefore, when known glof club head utilization titanium engages with the hard solder connection process as material, being subject to known hard solder connection process has the inferior position of easy oxidation for titanium, so have output minimizing and cost also to increase many, known joining technique has many bonding and molding disappearances simultaneously, so how to redesign a kind of joint method of glof club head, it can be the target of dealer's research and development in order to avoid easy oxidation of workpiece and increase output and to reduce cost.
Summary of the invention
Problem in view of above-mentioned known technology, the present invention is a kind of joint method of glof club head, in order to solve the glof club head of known titanium material, when doing to engage operation with the hard solder connection process, need to feed the higher argon gas of cost to prevent the inferior position of high-temperature oxydation, also overcome simultaneously known technology and be subject to and in vacuum drying oven or argon gas stove, process, can't increase the whole production capacity and the shortcoming of yield.
In order to achieve the above object, the present invention proposes a kind of joint method of glof club head, utilization hard solder connection process engages operation, and wherein, the joint method of this glof club head comprises:
One first assembly is provided, and this first assembly is made by the titanium material and is had a composition surface;
One second assembly is provided, and this second assembly is made by metal material and is had a composition surface;
The suitable nickel metal of doing to engage with a reactive metal scolder of the one deck that is covered is in this first assembly and this second assembly, and the surface of this first assembly and this second assembly is coated with one deck respectively and is suitable for this nickel metal that engages for this reactive metal scolder work; And
Carry out this first assembly and engage operation with this second assembly, this first assembly finished with this second assembly assembling and add this reactive metal scolder and engage with this second assembly for this first assembly, and place a continuous oven or a gas stove, and in this continuous oven or this gas stove, feed nitrogen gas, utilize and feed nitrogen gas in this first assembly of heating and this second assembly, make this solder fusing in the composition surface process of this first assembly and this second assembly, make this first assembly and this second assembly bonding and molding.
The joint method of above-mentioned glof club head, wherein, first assembly is a body, and this second assembly is batting panel, bulb top cover.
The joint method of above-mentioned glof club head, wherein, this first assembly is batting panel, bulb top cover, and this second assembly is a body.
The joint method of above-mentioned glof club head, wherein, the section shape of this batting panel is roughly cup-shaped.
The joint method of above-mentioned glof club head, wherein, the side that this first assembly does not comprise a striking surface or this first assembly striking surface that is shaped, and this second assembly is a balancing weight.
The joint method of above-mentioned glof club head, wherein, the side that this second assembly does not comprise a striking surface or this second assembly striking surface that is shaped, and this first assembly is a balancing weight.
The joint method of above-mentioned glof club head, wherein, this reactive metal scolder is not further for containing the scolder of titanium elements.
The joint method of above-mentioned glof club head, wherein, this reactive metal scolder is Ni-based scolder, money base scolder or copper parent metal.
The joint method of above-mentioned glof club head, wherein, the suitable nickel metal of doing to engage with a reactive metal scolder of this one deck that is covered is in this first assembly and this second assembly step, and surface-coated this nickel metal thickness of this first assembly and this second assembly is 0.1 μ m～10 μ m.
Above-mentioned glof club head joint method, wherein, this one deck that is covered is suitable for the nickel metal doing to engage with a reactive metal scolder in this first assembly and this second assembly step, and the surface-coated mode of this first assembly and this second assembly is physical vapor deposition lining method, chemical vapor deposition lining method, electroplate the lining method, electroless plating is covered method, thermal spraying is covered method.
The joint method of above-mentioned glof club head, wherein, the weld tabs that this reactive metal scolder is a solid, welding rod or half aqueous soldering paste.
Utilize the enforcement of the joint method of a kind of glof club head of the present invention, can reach following effect at least:
1. the present invention is a kind of joint method of glof club head, utilization hard solder connection process engages operation, utilize the joint method of this glof club head to implement utilization, can use continuous oven to do the joint operation of body and batting panel, so can more knownly increase the production capacity of making the glof club head finished product, and can promote the acceptance rate of glof club head finished product with vacuum drying oven or gas stove.
2. the present invention is a kind of joint method of glof club head; utilization hard solder connection process engages operation; utilize the joint method of this glof club head to implement utilization; because workpiece has lining one deck nickel metal coating workpiece; make and only need to use nitrogen protection thereby can high temperature and oxidation in the hard solder cooperation industry process of follow-up glof club head; event is more known to reduce many costs with argon gas as protective gas; and can re-use the scolder that do not contain titanium elements scolder as titanium hard solder connection process; the titaniferous scolder that therefore also can more known need just can apply at the environment of vacuum or argon shield more reduces whole processing cost.
Description of drawings
Fig. 1 is the joint method one embodiment flow chart of glof club head of the present invention;
Fig. 2 engages glof club head first structural representation of finishing for the joint method of glof club head of the present invention;
Fig. 3 engages glof club head second structural representation of finishing for the joint method of glof club head of the present invention;
Fig. 4 engages glof club head the 3rd structural representation of finishing for the joint method of glof club head of the present invention.
The specific embodiment
For making purpose of the present invention, structural feature and function thereof there are further understanding, cooperate related embodiment and accompanying drawing to be described in detail as follows:
At first, as shown in Figure 1, the present invention is a kind of joint method of glof club head, utilization hard solder connection process engages operation, joint method S1 one embodiment of this glof club head comprises, and the nickel metal that provide one first assembly (step S10), provide one second assembly (step S20), the one deck that is covered is suitable for to be engaged with reactive metal scolder work is in first assembly and second assembly (step S30) and carry out first assembly and the operation (step S40) of second assembly joint.
As shown in Figures 1 and 2, the present invention is a kind of joint method of glof club head, utilization hard solder connection process engages operation, joint method S1 one embodiment of this utilization glof club head, one first assembly (step S10) is provided earlier, this first assembly 10 is made by the titanium material and is had a composition surface, moreover, one second assembly (step S20) is provided, this second assembly is made by metal material and is had a composition surface, wherein the first above-mentioned assembly 10 of present embodiment is a body, and second assembly is a bulb top cover 21, certainly this second assembly also can be batting panel 22, and this batting panel 22 further is cup-shaped, shown in the 3rd figure, perhaps, this second assembly can be balancing weight 23 again, and its first assembly 10 does not comprise a striking surface or the one side striking surface 11 that is shaped, as shown in Figure 4, certainly this first assembly 10 also can be batting panel, the bulb top cover, and second assembly is a body, perhaps second assembly does not comprise a striking surface or the one side striking surface that is shaped, and first assembly is a balancing weight, follow-up, the suitable nickel metal of doing to engage with a reactive metal scolder of the one deck that is covered is in first assembly and second assembly (step S30), the surface-coated nickel metal that has one deck to be suitable for and to engage with reactive metal scolder work of this first assembly 10 and second assembly, present embodiment, the thickness of the surface-coated nickel metal of first assembly 10 and second assembly is 0.1 μ m～10 μ m, at last, carry out first assembly and second assembly and engage operation (step S40), first assembly 10 finished with second assembly assembling and add the reactive metal scolder and engage with second assembly for first assembly 10, and place a continuous oven or a gas stove, and in continuous oven or gas stove, feed nitrogen gas, utilize and feed nitrogen gas in heating first assembly 10 and second assembly, make solder fusing in the composition surface process of first assembly 10 and second assembly, make first assembly 10 and the second assembly bonding and molding, one glof club head 1.
The present invention is a kind of joint method of glof club head, utilization hard solder connection process engages operation, joint method S1 one preferred embodiment of this glof club head, the suitable nickel metal of doing to engage with a reactive metal scolder of the one deck that is covered is in first assembly and second assembly (step S30), the surface-coated mode of its first assembly and second assembly is a physical vapor deposition lining method, chemical vapor deposition lining method, electroplate the lining method, electroless plating lining method, thermal spraying lining method, above-mentioned in addition reactive metal scolder is not further for containing the scolder of titanium elements, it perhaps is Ni-based scolder, money base scolder or copper parent metal, and the above-mentioned reactive metal scolder weld tabs that is solid, welding rod or half aqueous soldering paste.
As shown in Figure 1, the joint method of a kind of glof club head of the present invention, utilization hard solder connection process engages operation, joint method S1 one preferred embodiment of this glof club head comprises, and the nickel metal that provide one first assembly (step S10), provide one second assembly (step S20), the one deck that is covered is suitable for to be engaged with reactive metal scolder work is in first assembly and second assembly (step S30) and carry out first assembly and the operation (step S40) of second assembly joint.
As depicted in figs. 1 and 2, the joint method of a kind of glof club head of the present invention, utilization hard solder connection process engages operation, joint method S1 one embodiment of this utilization glof club head, one first assembly (step S10) is provided earlier, this first assembly 10 is made by the titanium material and is had a composition surface, moreover, one second assembly (step S20) is provided, this second assembly is made by metal material and is had a composition surface, wherein the first above-mentioned assembly 10 of present embodiment is a body, and second assembly is a bulb top cover 21, certainly this second assembly also can be batting panel 22, and this batting panel 22 further is cup-shaped, system as shown in Figure 3, perhaps, this second assembly can be balancing weight 23 again, and its first assembly 10 does not comprise a striking surface or the one side striking surface 11 that is shaped, as shown in Figure 4, certainly this first assembly 10 also can be batting panel, the bulb top cover, and second assembly is a body, perhaps second assembly does not comprise a striking surface or the one side striking surface that is shaped, and first assembly is a balancing weight, follow-up, the suitable nickel metal of doing to engage with a reactive metal scolder of the one deck that is covered is in first assembly and second assembly (step S30), the surface-coated nickel metal that has one deck to be suitable for and to engage with reactive metal scolder work of this first assembly 10 and second assembly, present embodiment, the thickness of the surface-coated nickel metal of first assembly 10 and second assembly is 0.1 μ m～10 μ m, at last, carry out first assembly and second assembly and engage operation (step S40), first assembly 10 finished with second assembly assembling and add the reactive metal scolder and engage with second assembly for first assembly 10, and place a continuous oven or a gas stove, and in continuous oven or gas stove, feed nitrogen gas, utilize and feed nitrogen gas in heating first assembly 10 and second assembly, make solder fusing in the composition surface process of first assembly 10 and second assembly, make first assembly 10 and the second assembly bonding and molding, one glof club head 1.
The present invention is a kind of joint method of glof club head, utilization hard solder connection process engages operation, joint method S1 one embodiment of this glof club head, the suitable nickel metal of doing to engage with a reactive metal scolder of the one deck that is covered is in first assembly and second assembly (step S30), the surface-coated mode of its first assembly and second assembly is a physical vapor deposition lining method, chemical vapor deposition lining method, electroplate the lining method, electroless plating lining method, thermal spraying lining method, above-mentioned in addition reactive metal scolder is not further for containing the scolder of titanium elements, it perhaps is Ni-based scolder, money base scolder or copper parent metal, and the above-mentioned reactive metal scolder weld tabs that is solid, welding rod or half aqueous soldering paste.
Certainly; the present invention also can have other various embodiments; under the situation that does not deviate from spirit of the present invention and essence thereof; being familiar with those of ordinary skill in the art ought can make various corresponding changes and distortion according to the present invention, but these corresponding changes and distortion all should belong to the protection domain of the appended claim of the present invention.
Claims (11)
1. the joint method of a glof club head uses the hard solder connection process to engage operation, it is characterized in that the joint method of this glof club head comprises:
One first assembly is provided, and this first assembly is made by the titanium material and is had a composition surface;
One second assembly is provided, and this second assembly is made by metal material and is had a composition surface;
The suitable nickel metal of doing to engage with a reactive metal scolder of the one deck that is covered is in this first assembly and this second assembly; And
Carry out this first assembly and engage operation with this second assembly, this first assembly finished with this second assembly assembling and add this reactive metal scolder and engage with this second assembly for this first assembly, and place a continuous oven or a gas stove, and in this continuous oven or this gas stove, feed nitrogen gas, utilize and feed nitrogen gas in this first assembly of heating and this second assembly, make this solder fusing in the composition surface process of this first assembly and this second assembly, make this first assembly and this second assembly bonding and molding.
2. the joint method of glof club head according to claim 1 is characterized in that, first assembly is a body, and this second assembly is batting panel, bulb top cover.
3. the joint method of glof club head according to claim 1 is characterized in that, this first assembly is batting panel, bulb top cover, and this second assembly is a body.
4. according to the joint method of claim 2 or 3 described glof club heads, it is characterized in that the section shape of this batting panel is roughly cup-shaped.
5. the joint method of glof club head according to claim 1 is characterized in that, the side that this first assembly does not comprise a striking surface or this first assembly striking surface that is shaped, and this second assembly is a balancing weight.
6. the joint method of glof club head according to claim 1 is characterized in that, the side that this second assembly does not comprise a striking surface or this second assembly striking surface that is shaped, and this first assembly is a balancing weight.
7. the joint method of glof club head according to claim 1 is characterized in that, this reactive metal scolder is not further for containing the scolder of titanium elements.
8. the joint method of glof club head according to claim 1 is characterized in that, this reactive metal scolder is Ni-based scolder, money base scolder or copper parent metal.
9. the joint method of glof club head according to claim 1, it is characterized in that, the suitable nickel metal of doing to engage with a reactive metal scolder of this one deck that is covered is in this first assembly and this second assembly step, and surface-coated this nickel metal thickness of this first assembly and this second assembly is 0.1 μ m～10 μ m.
Glof club head according to claim 1 joint method, it is characterized in that, this one deck that is covered is suitable for the nickel metal doing to engage with a reactive metal scolder in this first assembly and this second assembly step, and the surface-coated mode of this first assembly and this second assembly is physical vapor deposition lining method, chemical vapor deposition lining method, electroplate the lining method, electroless plating is covered method, thermal spraying is covered method.
11. the joint method of glof club head according to claim 1 is characterized in that, the weld tabs that this reactive metal scolder is a solid, welding rod or half aqueous soldering paste.