CN100509329C - 仿卵石生态混凝土预制件及其制备方法 - Google Patents
仿卵石生态混凝土预制件及其制备方法 Download PDFInfo
- Publication number
- CN100509329C CN100509329C CNB2006100413160A CN200610041316A CN100509329C CN 100509329 C CN100509329 C CN 100509329C CN B2006100413160 A CNB2006100413160 A CN B2006100413160A CN 200610041316 A CN200610041316 A CN 200610041316A CN 100509329 C CN100509329 C CN 100509329C
- Authority
- CN
- China
- Prior art keywords
- pebble
- concrete precast
- preparation
- ecological concrete
- precast member
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种仿卵石生态混凝土预制件及其制备方法。由下列原料配制：水泥8～20份；颗粒状炉渣65～75份；十二烷基苯磺酸钠1～2份；硅粉2-4份；沸石粉5～10份；减水剂0.5～2.5份；无机颜料1～2份；水适量。制备方法包括：将上述原料按比例配制，搅拌均匀形成混合料；在卵石预制模具的内壁涂抹脱模剂；将混合料由预制模具压制成形，或将混合料置于预制模具中振动成形，静置0.5小时后脱模，养护24小时。本发明的优点在于：它提供的仿卵石生态混凝土预制件即可以作为水生植物及动物栖息生长的场所，又有助于水环境生态系统的恢复，它同时具有水质净化及美化景观的功能。
Description
技术领域
本发明涉及一种生态混凝土预制件及其制备方法，尤其是一种仿卵石生态混凝土预制件及其制备方法。
背景技术
生态混凝土是上个世纪90年代提出的新概念，在生态混凝土方面的研究，国外比国内起步早，目前日本、荷兰，尤其是日本处于世界领先的地位。近几年来，生态混凝土在公路护坡，水环境治理等方面得到应用。
CN1237866C号专利文献公开了一种植物生长型多孔混凝土球状砌块，在铺设护岸和道路护坡时，预留了植物能够生长的孔。CN1584218A号专利文献公开了一种多孔混凝土预制球，集水土保持、生态修复于一体，植物能够从球体缝隙生长。CN1768569A号专利文献公开了一种植被生态混凝土预制块，采用多层植生基材，植物能够在混凝土预制块上生长。上述各种方式的生态混凝土，在混凝土实现固土的同时，只能通过植物的根系很有限的降解水中COD等污染物，达到水体净化的效果，但是，对水中的氨氮等污染物的去除效果并不理想。且上述各种方式的生态混凝土造型呆板，人工痕迹强，难以遵从生态的理念。
发明内容
本发明的目的在于：针对上述生态混凝土在实际应用中存在的对于水中的氨氮污染效果并不理想的问题，提供一种仿卵石生态混凝土预制件及其制备方法。
本发明的目的是这样实现的：一种仿卵石生态混凝土预制件，其特征在于：预制件由下列原料按质量份配制：
水泥 8～20份；
颗粒状炉渣 65～75份；
十二烷基苯磺酸钠 1～2份；
硅粉 2～4份；
沸石粉 5～10份；
减水剂 0.5～2.5份；
无机颜料 1～2份；
水 适量。
在本发明中：所述的水泥为42.5级及其以上的硅酸盐水泥；颗粒状炉渣的单粒直径为10～20mm；沸石粉的单粒直径≤2mm；无机颜料为氧化铁或氧化铬或氧化钴或它们的混合物。
一种上述仿卵石生态混凝土预制件的制备方法，其特征在于：
a)将上述原料按比例配制，搅拌均匀形成混合料；
b)在卵石预制模具的内壁涂抹脱模剂；
c)将混合料由预制模具压制成形，或将混合料置于预制模具中振动成形，静置0.5小时后脱模，养护24小时。
在本发明所述的制备方法中：混合料是由一对模腔为半球形的预制模具压制形成卵石形。
在本发明所述的制备方法中：混合料是置于一对模腔为半球形的预制模具中通过振动成卵石形。
在本发明所述的制备方法中：预制模具的半球形模腔的端口直径为20～50cm。
本发明的优点在于：在本发明中采用颗粒状炉渣，提高了废物利用率，同时高孔隙率的炉渣保证了砌块良好的透水性，为水生微生物提供栖息场所，有利于水环境生态系统的恢复。沸石有利于去处水中氨氮污染，沸石吸附饱和后可以利用水体中的微生物实现原位再生。通过无机颜料的添加，多彩的卵石状生态混凝土能起到很好的景观功能。总之，本发明提供的仿卵石生态混凝土预制件即可以作为水生植物及动物栖息生长的场所，又有助于水环境生态系统的恢复，它同时具有水质净化及美化景观的功能。
附图说明：
图1是分别采用普通卵石和本发明的湖在同时注入富营养化水后氨氮浓度变化的对比实验曲线。
具体实施方式
实施例1
备料(在本实施例中，所述各原料以10KG为一基准份配制)：42.5级的硅酸盐水泥100KG，单粒直径为10～20mm的颗粒状炉渣700KG，十二烷基苯磺酸钠20KG，硅粉30KG，单粒直径≤2mm的沸石粉(由浙江宁海县金鑫沸石粉厂生产)100KG，减水剂(减水率>20％)10KG，氧化铁15KG，水适量。
制备过程：将上述原料按比例配制，搅拌均匀形成混合料；在卵石预制模具的内壁涂抹脱模剂；将混合料由预制模具压制成形，或将混合料置于预制模具中振动成形；静置0.5小时后脱模，养护24小时。本实施例中，预制模具的半球形模腔的端口直径为35cm，预制模具的内壁涂抹脱模剂为柴油。
实施例2
选取小区内A、B两座几乎同等大小的100m2左右的人工湖，湖体平均深1.5m。A湖选用传统浆砌片石建造，内抛5m3普通卵石；B湖用传统浆砌片石砌底，内抛5m3仿卵石生态混凝土预制件(由实施例1获得)。两湖同时于2005年4月1日注入富营养化水，原水初始氨氮浓度约80mg/l。并于2005年5月1日至2006年3月1日进行水质检测，检测结果如图1。由图可见，B湖中湖水的氨氮浓度明显低于A湖，7个月后，使氨氮浓度下降并保持20～30mg/l之间；同时，由于在制备仿卵石生态混凝土预制件的过程中添加了氧化铁，使B湖中的生态混凝土表面具有淡淡的铁锈红，具有美感。
以上实施例不是对本发明的限制，具体实施时，所述的无机颜料可以选择使用氧化铁或氧化铬或氧化钴或它们的混合物。各材料应该在本发明提供的范围内选择搭配，预制模具的半球形模腔的端口直径在20～50cm范围内，按照实施例1的制备方法来实现。
Claims (6)
1、一种仿卵石生态混凝土预制件，其特征在于：预制件由下列原料按质量法配制：
水泥 8～20份；
颗粒状炉渣 65～75份；
十二烷基苯磺酸钠 1～2份；
硅粉 2～4份；
沸石粉 5～10份；
减水剂 0.5～2.5份；
无机颜料 1～2份；
水 适量。
2、根据权利要求1所述的仿卵石生态混凝土预制件，其特征在于：所述的水泥为42.5级及其以上的硅酸盐水泥；颗粒状炉渣的单粒直径为10～20mm；沸石粉的单粒直径≤2mm；无机颜料为氧化铁或氧化铬或氧化钴或它们的混合物。
3、根据权利要求1或2所述的仿卵石生态混凝土预制件的制备方法，其特征在于：
a)将上述原料按比例配制，搅拌均匀形成混合料；
b)在卵石预制模具的内壁涂抹脱模剂；
c)将混合料由预制模具压制成形，或将混合料置于预制模具中振动成形，静置0.5小时后脱模，养护24小时。
4、根据权利要求3所述的仿卵石生态混凝土预制件的制备方法，其特征在于：混合料是由一对模腔为半球形的预制模具压制形成卵石形。
5、根据权利要求3所述的仿卵石生态混凝土预制件的制备方法，其特征在于：混合料是置于一对模腔为半球形的预制模具中通过振动成卵石形。
6、根据权利要求4或5所述的仿卵石生态混凝土预制件的制备方法，其特征在于：预制模具的半球形模腔的端口直径为20～50cm。