CN100494227C - Method for synthesizing nano dispersible CMC-acrylic acid macromolecule water-absorbing resin - Google Patents
Method for synthesizing nano dispersible CMC-acrylic acid macromolecule water-absorbing resin Download PDFInfo
- Publication number
- CN100494227C CN100494227C CNB2007100523790A CN200710052379A CN100494227C CN 100494227 C CN100494227 C CN 100494227C CN B2007100523790 A CNB2007100523790 A CN B2007100523790A CN 200710052379 A CN200710052379 A CN 200710052379A CN 100494227 C CN100494227 C CN 100494227C
- Authority
- CN
- China
- Prior art keywords
- carboxymethyl cellulose
- water
- active agent
- ester type
- sulfuric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to process of synthesizing water absorbing polymer resin, and is especially process of synthesizing water absorbing nanometer dispersive CMC-acrylate polymer resin. The process includes the following steps: 1. preparing materials including acrylic acid 10-50 weight portions, sodium hydroxide 3-10 weight portions, water 8-20 weight portions, CMC 1-10 weight portions, N, N'-methylene biacrylamide 0.01-0.5 weight portion, ammonium persulfate 0.01-1 weight portion, normal hexane 20-200 weight portions and sulfuric ester type surfactant 10-100 weight portions; 2. reacting the materials in a reaction kettle with introduced nitrogen while stirring and heating to 60-70 deg.c for 4-6 hr; 3. cooling through leading water to the jacket of the reaction kettle, and discharging the resultant; and 4. drying to obtain the product. The water absorbing polymer resin may be dispersed homogeneously in water solution.
Description
Technical field
The present invention relates to a kind of synthetic method of hydroscopic high-molecular resin.
Background technology
The synthetic method of carboxymethyl cellulose in prior art---acrylic acid series hydroscopic high-molecular resin mainly adopts methods such as solution polymerization, inverse suspension polymerization.
Inverse suspension polymerization method is meant and adds organic solvent and suspension agent (tensio-active agent) in reaction vessel; under certain mixing speed; add again and be dissolved with water soluble starter and the linking agent and the reaction monomers aqueous solution; under the shielding gas effect and under the certain temperature condition, carry out the method for chemical polymerization.
Solution polymerization is simple to operate, and non-environmental-pollution but the reaction heat that produces are difficult to distribute, and polymerization system viscosity is too high, often is difficult to carry out in common reactor, and aftertreatment is very difficult.
Usually inverse suspension polymerization method synthetic carboxymethyl cellulose---acrylic acid series hydroscopic high-molecular resin suction back molecular chain can not disperse, be bulk congeries (as shown in Figure 1), the molecular chain that does not reach hydroscopic high-molecular resin is the specific order of nanometer degree dispersive ground.
Summary of the invention
The object of the present invention is to provide a kind of nanometer can disperse carboxymethyl cellulose---the synthetic method of acroleic acid macromolecular absorbent resin, the hydroscopic high-molecular resin that this method obtains homodisperse in the aqueous solution.
To achieve these goals, technical scheme of the present invention is: nanometer can be disperseed carboxymethyl cellulose---the synthetic method of acroleic acid macromolecular absorbent resin, adopt inverse suspension polymerization method, and it is characterized in that it comprises the steps:
1) parts by weight by each constitutive material are:
Vinylformic acid (AA) 10-50,
Sodium hydroxide 3-10,
Water 8-20,
CMC (carboxymethyl cellulose) 1-10,
N, N '-methylene-bisacrylamide 0.01-0.5,
Ammonium persulphate 0.01-1,
Normal hexane 20-200,
Sulfuric acid ester type tensio-active agent 10-100;
Choose vinylformic acid, sodium hydroxide, water, carboxymethyl cellulose, N, N '-methylene-bisacrylamide, ammonium persulphate, normal hexane and sulfuric acid ester type tensio-active agent, standby;
2) with vinylformic acid, sodium hydroxide, water, carboxymethyl cellulose, N, N '-methylene-bisacrylamide, ammonium persulphate, normal hexane and sulfuric acid ester type tensio-active agent add in the reactor of strap clamp cover, condenser, stirring velocity is more than 400 rev/mins, in reactor, fed the nitrogen aeration time 15-30 minute, progressively be warmed up to 60-70 ℃ then in normal-pressure reaction kettle, the reaction times is 4-6 hour;
3), logical cooling water temperature is emitted reaction mass to room temperature in the chuck of reactor, reaction mass;
4), (purpose is that unreacted reactants such as normal hexane are isolated to the reaction mass that obtains of step 3) with drier, its unreacted reactant isolate is reusable) dry, will be finished product (being that nanometer can be disperseed carboxymethyl cellulose---acroleic acid macromolecular absorbent resin) o after the reaction mass drying that dry
Described sulfuric acid ester type tensio-active agent is a polyoxyethylene alkyl ether sulfate salt.
The finished product that obtains is milky white particulate material, and its water-intake rate can reach more than 200-800 times of absorption own wt.The length of the molecular chain of dispersive hydroscopic high-molecular resin is number nanometer (see figure 2) in the aqueous solution.
The tensio-active agent that traditional synthetic method is used seldom generally is used as suspension agent; Make synthetic hydroscopic high-molecular resin dispersed relatively poor in water, be bulk congeries (see figure 1).The present invention adopts the method that increases the tensio-active agent that uses, make and contain a large amount of tensio-active agents in the synthetic hydroscopic high-molecular resin, tensio-active agent becomes inierpeneirating network structure with the molecular chain of hydroscopic high-molecular resin, the molecular chain of macromolecular chain and tensio-active agent interacts after the hydroscopic high-molecular resin suction, the hydroscopic high-molecular resin molecular chain is disperseed in the aqueous solution rapidly, the length of hydroscopic high-molecular resin molecular chain is the number nanometer, under the effect of stirring tool, can be in the aqueous solution homodisperse, and do not cause environmental pollution.
Synthetic method of the present invention can effectively be controlled synthesis temperature, and its technical process is simple, production safety coefficient height, and production cost is low.Can be used as at aspects such as industry, agricultural, daily necessities, health cares and have extensive use.Be particularly suitable for doing water-retaining agent, tensio-active agent, the deicing fluid subsidiary material, height solidifies---dissolve the energy storage solution material of latent heat, uses such as pigment is wetting with high molecule multifunction, dispersing auxiliary material.
Description of drawings
Fig. 1 is the carboxymethyl cellulose that traditional synthetic method obtains---acroleic acid macromolecular absorbent resin is at scatter diagram in the aqueous solution.
Fig. 2 is the carboxymethyl cellulose that synthetic method of the present invention obtains---acroleic acid macromolecular absorbent resin is at scatter diagram in the aqueous solution.
Embodiment
In order to understand the present invention better, further illustrate content of the present invention below in conjunction with embodiment, but content of the present invention not only is confined to the following examples.
Embodiment 1:
In small-sized glass-lined kettle, add 2.6 liter normal hexanes, CMC (carboxymethyl cellulose) 1kg, sulfuric acid ester type tensio-active agent 0.62 liter [described sulfuric acid ester type tensio-active agent, as: (be called for short: AES), molecular formula is R-O (CH to polyoxyethylene alkyl ether sulfate salt
2CH
2O) nSO
3Na], N, N methylene-bisacrylamide 28g, ammonium persulphate 37g, in reactor, fed the nitrogen aeration time 15-30 minute, start stirrer and remain on 450 rev/mins, stirred 10-30 minute, add the sodium acrylate aqueous solution (vinylformic acid 7kg, sodium hydroxide 2.7kg, water 7.6kg) remain on 400 rev/mins then, be warmed up to 60 ℃ and kept 1 hour, be warmed up to 70 ℃ and kept 4 hours, after reaction finishes.Logical cooling water temperature is emitted reaction mass to room temperature in the reacting kettle jacketing.Use drier that unreacted reactants such as normal hexane are isolated, its isolate is reusable.To be finished product (nanometer can be disperseed carboxymethyl cellulose---acroleic acid macromolecular absorbent resin) after the reaction mass drying that dry, the finished product that obtains is milky white particulate material, and its water-intake rate can reach and absorb more than 200 times of own wt.The finished product that obtains homodisperse in the aqueous solution, the length of the molecular chain of dispersive hydroscopic high-molecular resin is number nanometer (see figure 2) in the aqueous solution.
Embodiment 2:
In small-sized glass-lined kettle, add 3.2 liter normal hexanes, CMC (carboxymethyl cellulose) 1kg, sulfuric acid ester type tensio-active agent 1.25 liters [described sulfuric acid ester type tensio-active agent, as: (be called for short: AES), molecular formula is R-O (CH to polyoxyethylene alkyl ether sulfate salt
2CH
2O) nSO
3Na], N, N methylene-bisacrylamide 14g, ammonium persulphate 26g, in reactor, fed the nitrogen aeration time 15-30 minute, start stirrer and remain on 450 rev/mins, stirred 10-30 minute, add the sodium acrylate aqueous solution (vinylformic acid 7kg, sodium hydroxide 2.7kg, water 7.6kg) remain on 400 rev/mins then, be warmed up to 60 ℃ and kept 1 hour, be warmed up to 70 ℃ and kept 4 hours, after reaction finishes.Logical cooling water temperature is emitted reaction mass to room temperature in the reacting kettle jacketing.Use drier that unreacted reactants such as normal hexane are isolated, its isolate is reusable.To be finished product (nanometer can be disperseed carboxymethyl cellulose---acroleic acid macromolecular absorbent resin) after the reaction mass drying that dry, the finished product that obtains is milky white particulate material, and its water-intake rate can reach and absorb more than 300 times of own wt.The finished product that obtains homodisperse in the aqueous solution.
Embodiment 3:
In small-sized glass-lined kettle, add 3.8 liter normal hexanes, CMC (carboxymethyl cellulose) 1kg, sulfuric acid ester type tensio-active agent 1.85 liters [the sulfuric acid ester type tensio-active agent, as: (be called for short: AES), molecular formula is R-O (CH to polyoxyethylene alkyl ether sulfate salt
2CH
2O) nSO
3Na], N, N methylene-bisacrylamide 7g, ammonium persulphate 26g, in reactor, fed the nitrogen aeration time 15-30 minute, start stirrer and remain on 450 rev/mins of 10-30 branches, add the sodium acrylate aqueous solution (vinylformic acid 7kg, sodium hydroxide 2.7kg, water 7.6kg) remains on 400 rev/mins then, be warmed up to 60 ℃ and kept 1 hour, be warmed up to 70 ℃ and kept 4 hours, after reaction finishes.Logical cooling water temperature is emitted reaction mass to room temperature in the reacting kettle jacketing.Use drier that unreacted reactants such as normal hexane are isolated, its isolate is reusable.To be finished product (nanometer can be disperseed carboxymethyl cellulose---acroleic acid macromolecular absorbent resin) after the reaction mass drying that dry, the finished product that obtains is milky white particulate material, and its water-intake rate can reach and absorb more than 800 times of own wt.The finished product that obtains homodisperse in the aqueous solution.
Embodiment 4:
Nanometer can be disperseed carboxymethyl cellulose---the synthetic method of acroleic acid macromolecular absorbent resin, adopt inverse suspension polymerization method, and it comprises the steps:
1) parts by weight by each constitutive material are: vinylformic acid (AA) 10, sodium hydroxide 3, water 8, CMC (carboxymethyl cellulose) 1, N, N '-methylene-bisacrylamide 0.01, ammonium persulphate 0.01, normal hexane 20, sulfuric acid ester type tensio-active agent 10; Choose vinylformic acid, sodium hydroxide, water, carboxymethyl cellulose, N, N '-methylene-bisacrylamide, ammonium persulphate, normal hexane and sulfuric acid ester type tensio-active agent, standby; Sulfuric acid ester type tensio-active agent wherein, as: (be called for short: AES), molecular formula is R-O (CH to polyoxyethylene alkyl ether sulfate salt
2CH
2O) nSO
3Na;
2) with vinylformic acid, sodium hydroxide, water, carboxymethyl cellulose, N, N '-methylene-bisacrylamide, ammonium persulphate, normal hexane and sulfuric acid ester type tensio-active agent add in the reactor of strap clamp cover, condenser, stirring velocity is more than 400 rev/mins, in reactor, fed the nitrogen aeration time 15 minutes, progressively be warmed up to 60 ℃ then in normal-pressure reaction kettle, the reaction times is 4 hours;
3), logical cooling water temperature is emitted reaction mass to room temperature in the chuck of reactor, reaction mass;
4), (purpose is that unreacted reactants such as normal hexane are isolated to the reaction mass that obtains of step 3) with drier, its unreacted reactant isolate is reusable) dry, will be finished product (being that nanometer can be disperseed carboxymethyl cellulose---acroleic acid macromolecular absorbent resin) after the reaction mass drying that dry.
Embodiment 5:
Nanometer can be disperseed carboxymethyl cellulose---the synthetic method of acroleic acid macromolecular absorbent resin, adopt inverse suspension polymerization method, and it comprises the steps:
1) parts by weight by each constitutive material are: vinylformic acid (AA) 50, sodium hydroxide 10, water 20, CMC (carboxymethyl cellulose) 10, N, N '-methylene-bisacrylamide 0.5, ammonium persulphate 1, normal hexane 200, sulfuric acid ester type tensio-active agent 100; Choose vinylformic acid, sodium hydroxide, water, carboxymethyl cellulose, N, N '-methylene-bisacrylamide, ammonium persulphate, normal hexane and sulfuric acid ester type tensio-active agent, standby; Sulfuric acid ester type tensio-active agent wherein, as: (be called for short: AES), molecular formula is R-O (CH to polyoxyethylene alkyl ether sulfate salt
2CH
2O) nSO
3Na;
2) with vinylformic acid, sodium hydroxide, water, carboxymethyl cellulose, N, N '-methylene-bisacrylamide, ammonium persulphate, normal hexane and sulfuric acid ester type tensio-active agent add in the reactor of strap clamp cover, condenser, stirring velocity is more than 400 rev/mins, in reactor, fed the nitrogen aeration time 30 minutes, progressively be warmed up to 70 ℃ then in normal-pressure reaction kettle, the reaction times is 6 hours;
3), logical cooling water temperature is emitted reaction mass to room temperature in the chuck of reactor, reaction mass;
4), (purpose is that unreacted reactants such as normal hexane are isolated to the reaction mass that obtains of step 3) with drier, its unreacted reactant isolate is reusable) dry, will be finished product (being that nanometer can be disperseed carboxymethyl cellulose---acroleic acid macromolecular absorbent resin) after the reaction mass drying that dry.
Claims (1)
1. nanometer can be disperseed carboxymethyl cellulose---the synthetic method of acroleic acid macromolecular absorbent resin, adopt inverse suspension polymerization method, and it is characterized in that it comprises the steps:
1) parts by weight by each constitutive material are:
Vinylformic acid 10-50,
Sodium hydroxide 3-10,
Water 8-20,
Carboxymethyl cellulose 1-10,
N, N '-methylene-bisacrylamide 0.01-0.5,
Ammonium persulphate 0.01-1,
Normal hexane 20-200,
Sulfuric acid ester type tensio-active agent 10-100;
Choose vinylformic acid, sodium hydroxide, water, carboxymethyl cellulose, N, N '-methylene-bisacrylamide, ammonium persulphate, normal hexane and sulfuric acid ester type tensio-active agent, standby; Described sulfuric acid ester type tensio-active agent is a polyoxyethylene alkyl ether sulfate salt;
2) with vinylformic acid, sodium hydroxide, water, carboxymethyl cellulose, N, N '-methylene-bisacrylamide, ammonium persulphate, normal hexane and sulfuric acid ester type tensio-active agent add in the reactor of strap clamp cover, condenser, stirring velocity is more than 400 rev/mins, in reactor, fed the nitrogen aeration time 15-30 minute, progressively be warmed up to 60-70 ℃ then in normal-pressure reaction kettle, the reaction times is 4-6 hour;
3), logical cooling water temperature is emitted reaction mass to room temperature in the chuck of reactor, reaction mass;
4), the reaction mass that obtains of step 3) with drier get rid of in, after the reaction mass drying that dries, nanometer can be disperseed carboxymethyl cellulose---acroleic acid macromolecular absorbent resin.