CN100471595C - Hot pressing method for high strength member using hot pressed parts of steel sheet - Google Patents
Hot pressing method for high strength member using hot pressed parts of steel sheet Download PDFInfo
- Publication number
- CN100471595C CN100471595C CNB200580023694XA CN200580023694A CN100471595C CN 100471595 C CN100471595 C CN 100471595C CN B200580023694X A CNB200580023694X A CN B200580023694XA CN 200580023694 A CN200580023694 A CN 200580023694A CN 100471595 C CN100471595 C CN 100471595C
- Authority
- CN
- China
- Prior art keywords
- hot
- heating
- steel sheet
- steel plate
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a method of hot pressing using hot rolled and cold rolled steel sheet or Al-based plated steel sheet or Zn-based plated steel sheet enabling a strength of at least 1200 MPa to be obtained after high temperature forming and with extremely little possibility of hydrogen embrittlement and such hot pressed parts, that is, a method of hot pressing a high strength automobile parts comprising using steel sheet containing as steel compositions by wt% C:0.05 to 0.5% or steel sheet plated mainly with Al or Zn to produce automobile members by hot pressing during which making the heating temperature before pressing Ac 3 or more to 1100 DEG C or less, making the hydrogen concentration in the heating atmosphere 6 vol% or less, and making the dew point 10 DEG C or less and such hot pressed parts.
Description
Technical field
Hot-press method and hot press parts when the present invention relates to use the steel plate of cold rolling, hot rolled steel plate or plating Al system or plating Zn system to make collision prevention girders, center beam of bumper equal strength parts in the column of automobile, the car door.
Background technology
Because the lightweight of the automobile that causes because of the earth environment problem need make the employed steel plate high strength of automobile as far as possible, but when generally steel plate being carried out high strength, percentage elongation and the reduction of r value, formability deterioration.In order to solve such problem, the spy opens to disclose in the 2000-234153 communique and a kind ofly forms, utilizes the heat of this moment to seek the technology that intensity improves in middle temperature.In this technology, suitably control composition in the steel, heat in the ferrite humidity province, utilize the precipitation strength in this humidity province that intensity is improved.
In addition, the spy opens the 2000-87183 communique for the purpose that improves the drawing precision, has proposed the high-strength steel sheet that a kind of yield strength ratio under forming temperature yield strength at normal temperatures reduces greatly., in these technology, has the limited possibility of resulting intensity.On the other hand, for the purpose that obtains higher intensity, the spy opens the austenite one phase district that the 2000-38640 communique has proposed to be heated to after a kind of be shaped high temperature, and phase transformation becomes the technology of hard phase in cooling procedure thereafter.
, when the laggard row heating that is shaped is cooled off rapidly, exist in the possibility that has problems on the form accuracy.As the technology that overcomes this shortcoming, document (SAE, 2001-01-0078) and spy open the 2001-181833 communique and disclose such technology: steel plate is heated to the austenite one phase district, in stamping process, adopt by the cooling velocity critical cooling rate of composition of steel definite martensite phase transformation more than implement cooling thereafter.Disclose following content in the former document: the oxide skin on surface takes place and uses Al-plated steel sheet in order to suppress to heat.In the present invention such stamping procedure is called hot pressing.
As with the relevant prior art of hot pressing of using such coated steel sheet, can enumerate following technology.Open in the 2003-147499 communique the spy, the example that the steel plate that will adopt the coating lining that is made of the Fe-Zn alloy is used for hot pressing is disclosed, in addition, the spy opens the 2003-41343 communique and discloses that will to adopt the plating Al of the coating lining that is made of the Fe-Al alloy be the example that steel plate is used for hot pressing.
In addition, the spy opens the 2002-282951 communique and discloses such example: as the method for using punch die (dies) and drift to come punching press heated metal board material, the gap of having stipulated mould from the viewpoint of formability and hardenability.
Summary of the invention
Like this, the high-strength steel sheet that automobile etc. are used, just there is above-mentioned formability problem in high strength more, particularly in surpassing the such high-strength material of 1000MPa, has this essential problem of hydrogen embrittlement (also being sometimes referred to as strain-aging cracking, delayed fracture) known to resembling in the past.Therefore, be used as the occasion of hot pressing with steel plate, the hydrogen quantitative change that reduces the base material gets important.
The present invention is for solving the invention that above-mentioned problem is made, provide a kind of and used, and minimum hot rolling cold-rolled steel sheet, the plating Al of the possibility of hydrogen embrittlement is that steel plate or plating Zn are the hot-press method and the hot press parts of steel plate in the intensity that can obtain behind the hot forming more than the 1200MPa.
Present inventors have implemented various investigations in order to solve above-mentioned problem.It found that, before the control punching press be heated to the austenite one phase district time atmosphere and temperature be very important to the hot press parts of making the resistance to hydrogen embrittlement excellence.That is to say that when containing hydrogen in the atmosphere when this heating, this hydrogen is invaded in the steel plate, in addition, even contain moisture, have the possibility in the hydrogen intrusion steel plate too, it is important therefore reducing these compositions.In addition, in order to prevent hydrogen embrittlement, the gap of suitably selecting mould is important.Main idea of the present invention based on described knowledge opinion is as follows.
(1) a kind of hot-press method of high-strength vehicle parts, it is characterized in that, use the steel plate of the C that contains 0.05～0.5 quality % in the composition of steel or implemented with Al or Zn as the steel plate of the plating of main body, when adopting pressure sintering to make automobile component, the heating-up temperature before the punching press is defined as Ac
3More than, below 1100 ℃, the hydrogen concentration in the heating atmosphere is defined as below the 6 volume %, dew point is defined as below 10 ℃.
As the hot-press method of (1) described high-strength vehicle parts, it is characterized in that (2) hydrogen concentration in the heating atmosphere is below the 1 volume %, dew point is below 10 ℃.
(3) as (1) or (2) described hot-press method, it is characterized in that, with the steel plate after the heating import forcing press when forming punch die and 1.0～1.8 times of the gap between drift (clearance) plate thickness of being used steel.
(4) a kind of hot press parts is characterized in that, uses wantonly 1 described hot-press method of (1)～(3) to make.
Description of drawings
Fig. 1 is the outline drawing of mould of the employed cap shaped of processing experiment of embodiment.
The specific embodiment
The following describes qualification reason of the present invention.
As described above, the steel plate that the present invention with hot rolling, cold-rolled steel sheet or plating Al system, plating Zn is carries out hot forming after being heated to more than 700 ℃, cooling in mould, quenching immediately, obtain desirable intensity, in the present invention, the steel plate before heating, the drawing has been made regulation.As the steel plate composition, need the hardenability excellence, need the C amount is more than 0.05%, to be preferably more than 0.1% for this reason.About element in other the steel, add elements such as Si, Mn, Ti, B, Cr, Mo, Al, P, S, N sometimes.Si produces effect to fatigue properties, and the occasion that contains Si is preferably 0.05～1%.Mn, B, Cr, Mo help to improve hardenability, are containing the occasion of these elements, are preferably that Mn:0.5～3%, B:0.05% are following, Cr:2% is following, below the Mo:0.5%.It is the non-oxidizability of steel plate that Ti, Al improve plating Al, is preferably below the Ti:0.5% in the occasion that contains these elements, below the Al:0.1%.
Can expect having applied Al system or Zn is the steel plate of coating as the coating kind, when these steel plates were used for hot pressing, the iron oxide that can suppress the surface generated, and gives corrosion resistance.
Be that the formation of coating is narrated at first to Al.Having made plating Al towards various uses now is steel plate, and the present invention can use these steel plates.Such steel plate is arranged: as Al is the formation of coating, is principal component with Al, and the alloy-layer when suppressing hot-dip Al generates, and preferably contains 3～15% Si.In addition,, Cr, Mg, Ti, Sn etc. are arranged, also can add these elements as the element that the corrosion resistance that makes coating improves more.At this moment, preferably contain Cr:0.1～1%, Mg:0.5～10%, Ti:0.1～1%, Sn:1～5%.Moreover Al contains Fe with the impurity form in the coating, and the amount of this Fe is generally 0.05～0.5%.
Moreover the heating rear surface can generate FeAl
3, Fe
2Al
5, Fe
3Al, Fe
2Al
8Intermetallic compounds such as Si.These have the tendency that forms sandwich construction mutually, typically become 5 layers of structure, but the structure of these phases is not damaged the main idea of the present application for what kind of phase structure.In addition, as its composition, be principal component with Al, Fe, when in the Al plating bath, being added with Si, also contain the Si about 5～10%.The composition total of these elements accounts for more than 90%.If the situation of AI that the not alloying of remaining trace also can be arranged in addition is but on a small quantity then to the not special influence of performance.Oxide, the nitride covering surfaces of heating back Al system, but do not do special provision about their amount.
Be that the formation of coating is narrated then to Zn.Plating Zn is the steel plate that steel plate has been made various compositions now, and the present invention can use these steel plates.As representational Zn is the formation of coating, can enumerate following formation: Zn-0.2%Al, Zn-5%Al-0.1%Mg, Zn-5%Al-0.1%Mg-mixed rare earth alloy, Zn-7%Al-3%Mg, Zn-11%Al-3%Mg-0.1%Si, Zn-55%Al-1.6%Si or the like.In addition, thus also useful Zn-0.1%Al bathes to heat after the plating and becomes such formation for Zn-10%Fe.In addition,, Cr, Mg, Ti, Sn etc. are arranged, also can add these elements as the element that the corrosion resistance that makes coating improves more.At this moment, preferably contain Cr:0.1～1%, Mg:0.5～10%, Ti:0.1～1%, Sn:1～5%.
Moreover heating can generate ζ, δ on the rear surface
1, Γ, Γ
1The ferritic phase of Zn that equated intermetallic compound, solid solution.These can layeredly distribute mutually or granular the distribution, but their phase structure is not damaged the main idea of the present application for what kind of phase structure.In addition, form,, then also have the situation that generates above-mentioned Fe-Al based compound if contain the coating of Al as it.Zn is the occasion of coating, and heating back generates the oxide-film of Zn system or Al system, even but generate these materials and also do not damage main idea of the present invention.
About Al system, Zn is adhesion amount, plating pre-treatment, the plating post processing of coating, be not particularly limited, but the coating adhesion amount is preferably single face 50g/m
2More than.Reason is that the coating adhesion amount is many more, and the corrosion resistance when making parts after the effect of the inhibition oxidation during heating, heating, the shaping improves more.As the plating post processing, be purpose with antirust, lubricity once, chromate processings, resin-coated processing etc. can be arranged, but since organic resin once heating disappearance, so not preferred.Chromate is handled if consider in recent years 6 valency chromium restriction, also the processing epithelium of 3 valencys of preferred electrolytic chromate etc.At the plating Al of corrosion resistance excellent is the occasion of steel plate, does not give the chromate epithelium, and it is also passable only to carry out oiling.
Temperature and atmosphere during in the present invention to heating stipulate that this temperature is defined as Ac
3More than, below 1100 ℃.This be because, be phase-changed into the austenite one phase district fully in order to make steel plate, need be Ac
3More than the temperature, on the other hand, if oxidation will take place on heating-up temperature too high then surface or the intrusion of hydrogen in steel comes to life.Using Zn is the occasion of coating, and in addition, because the boiling point of Zn is about 910 ℃, therefore when for too high temperature, Zn evaporates fully, and it is fierce that the oxidation of steel plate becomes, so preferred 1000 ℃ is the upper limit.More preferably ceiling temperature is 920 ℃.Lower limit temperature is preferably 800 ℃.Even reason is to be heated to Ac
3More than the temperature, temperature also can reduce during the taking-up steel plate transferred to forcing press from stove after the heating, thereby can generate ferrite.
In the heating atmosphere, hydrogen concentration is defined as below the 6 volume %.This is because as described above, hydrogen is invaded in steel, thereby improves the cause of the possibility of hydrogen embrittlement.The lower limit of hydrogen concentration is not set especially, and hydrogen concentration is low for well.More preferably the hydrogen amount is below 1%.The present invention finds that the moisture in the atmosphere can easily invade in the steel with the form of hydrogen too.Therefore, the moisture in the preferred atmosphere is also low, from practicality, measures amount of moisture by measuring dew point, and the upper limit of dew point is defined as 10 ℃.Moreover, about the conversion of dew point and amount of moisture is known following formula arranged, be 1.2 volume % as the amount of moisture of this moment.When particularly using plating Zn to be steel plate, exist in the oxide that surface of steel plate forms Zn when containing aerobic in the atmosphere, suppress the tendency of the evaporation of Zn.Therefore, when using plating Zn to be steel plate, preferably in atmosphere, contain 1～21% oxygen.In addition, not only coated steel sheet for the steel plate of not implementing plating (naked material), adding the intrusion of pining for also having hydrogen, so the management of hydrogen concentration in the heating atmosphere and amount of moisture is necessary.
Mathematical expression 1
PH
2O: hydrogen concentration (volume fraction); Tdp: dew point (absolute temperature)
Do not establish special regulation about heating means, can adopt radiant tube etc. to carry out radiation heating, can adopt eddy-current heating, energising heating etc. yet.The firing rate of this moment does not limit yet.This depends on plate thickness, shape certainly greatly.
Hot pressing has following characteristics: cool off mutually from austenite, obtain quenching structure, the influence of the cooling velocity after the heating is also big certainly.Among the present invention, need by composition of steel decision be used to obtain cooling off more than the critical cooling rate of martensitic structure, as desired value, be preferably more than 15 ℃/second from 700 ℃ to 350 ℃ average cooling rates.Can think that this cooling velocity depends on composition of steel, for the good steel of hardenability, even adopt the cooling velocity about 20 ℃/second, also can obtain desirable tissue,, need the cooling velocity about 30 ℃/second sometimes according to the steel grade difference based on martensite.
During punching press, the gap of punch die and drift (clearance) is one of important factor, and in the present invention, this gap is 1.0～1.8 times of plate thickness preferably.Can think, if narrow gaps then plate be difficult to enter, become attenuate pull and stretch processing, so surface of steel plate can adhere, have the possibility of the starting point that becomes hydrogen embrittlement.Can think that in addition if relief width then exists to be difficult to by the tendency of through hardening, it is irregular to produce intensity in parts, residual residual stress in the parts, the possibility of hydrogen embrittlement improves.
Embodiment
Utilize embodiment to illustrate in greater detail the present invention below.
Embodiment 1
The cold-rolled steel sheet that will have the plate thickness 1.4mm of such composition of steel as shown in table 1 heats under various conditions, and the mould with cap shaped shown in Figure 1 forms then.Clearance gauge is decided to be 1.1 times of plate thickness.Carry out the Φ 5mm of 10 points, the punching of gap 0.5mm (both sides) at the edge part of cap then, after 7 days, observe punching portion, judge to have or not fine crack with 20 times magnifying glass.Heating is sample to be inserted in the electric furnace of controlled atmospher carry out.Heating-up time till 900 ℃ is roughly 4 minutes, and the time from the stove to the forcing press is about 10 seconds, and it is about 750 ℃ that punching press begins temperature.Cooling is carried out in mould, is 40 ℃/second from 700 ℃ to 350 ℃ average cooling rates.Table 2 illustrates heating condition and has or not fine crack.Moreover, to carry out cutting after the cap shape is shaped a part and under load 10kgf, measure Vickers hardness, the overall level of result is in the scope of Hv:410～510, and tissue demonstrates martensitic structure.In addition, the surface at these steel plates has produced iron oxide after the hot pressing.
The No.7 of embodiment 1 is because therefore the fine crack more than 5 has taken place in the dew point height.Therefore a spot of crackle has taken place because the hydrogen amount is more than 1% in No.1 and No.3.
Table 1
| Symbol | C | Si | Mn | P | S | Al | N | Ti | Cr | Mo | B |
| A | 0.15 | 0.1 | 2.1 | 0.01 | 0.004 | 0.03 | 0.004 | 0.02 | 0.4 | 0.01 | 0.003 |
| B | 0.21 | 0.2 | 0.9 | 0.02 | 0.005 | 0.015 | 0.005 | 0.01 | 0.9 | 0.4 | 0.004 |
| C | 0.27 | 0.15 | 0.88 | 0.01 | 0.002 | 0.02 | 0.004 | 0.02 | 0.23 | 0.5 | 0.003 |
Table 2
The fine crack scoring that a situation arises
The number total amount of the fine crack in 10 points: o:0; Zero: 1; △: less than 5; *: more than 5.
Embodiment 2
To carry out hot-dip Al as material through the cold-rolled steel sheet (plate thickness 1.4mm) of such composition of steel common hot rolling, cold rolling process, as shown in table 3.Hot-dip Al uses the production line of non-oxidation furnace-reduction furnace type, and the plating back adopts the gas friction method that the coating adhesion amount is adjusted to single face 80g/m
2, cooling then.The plating bath of this moment consists of Al-10%Si-2%Fe, and bathing temperature is 660 ℃.Fe in the bath is the inevitable element of being supplied with by plating equipment or lath.The coating outward appearance is plating etc. not, for well.The hot dipping Al-plated steel sheet of making is like this heated under various conditions, and the mould with cap shaped shown in Figure 1 forms then.Clearance gauge is decided to be 1.1 times of plate thickness.Carry out the Φ 5mm of 10 points, the punching of gap 0.5mm (both sides) at the edge part of cap then, after 7 days, observe punching portion, judge to have or not fine crack with 20 times magnifying glass.Heating is sample to be inserted in the electric furnace of controlled atmospher carry out.Heating-up time till 900 ℃ is roughly 4 minutes, and the time from the stove to the forcing press is about 10 seconds, and it is about 750 ℃ that punching press begins temperature.Cooling is carried out in mould, is 40 ℃/second from 700 ℃ to 350 ℃ average cooling rates.Table 4 illustrates heating condition and has or not fine crack.Moreover, to carry out cutting after the cap shape is shaped a part and under load 10kgf, measure Vickers hardness, the overall level of result is in the scope of Hv:410～510, and tissue demonstrates martensitic structure.In addition, iron oxide does not take place in the surface at these steel plates after the hot pressing.
Table 3
| C | Si | Mn | P | S | Al | N | Ti | Cr | Mo | B |
| 0.22 | 0.21 | 1.20 | 0.02 | 0.003 | 0.027 | 0.003 | 0.002 | 0.18 | 0.02 | 0.0018 |
Table 4
The fine crack scoring that a situation arises
The number total amount of the fine crack in 10 points: zero: 0; Zero: 1; △: less than 5; *: more than 5.
As shown in table 4, different with temperature according to heating atmosphere, the hydrogen amount that invades in the steel also changes, and the sensitiveness of fine crack is also changed.Hydrogen concentration is that the No.5 of 10vol%, No.7 that dew point is 15 ℃ can see the crackle more than 5 has taken place.Along with hydrogen concentration, dew point reduce, the generation of crackle is suppressed all the more, but in No.6,10,15 such occasions, the crackle of a little has taken place.
Embodiment 3
Use has the cold-rolled steel sheet of the plate thickness 1.4mm of such composition of steel as shown in table 5, and having implemented various Zn is plating.The coating kind of this moment and bath composition, bath temperature are shown in table 6.Using these platings Zn is steel plate, carries out the cap shape similarly to Example 1 and is shaped, and has observed the mode of entrance of fine crack after the punching processing.The heating condition of this moment and the relation of crackle situation occurred are shown in table 7.Cooling is carried out in mould, is 20 ℃/second from 700 ℃ to 350 ℃ average cooling rates.Measured the cross section hardness after being shaped similarly to Example 1, all between Hv:410～510, organized also to demonstrate martensitic structure.In addition, iron oxide does not take place in the surface at these steel plates after the hot pressing.
Table 5
| Symbol | C | Si | Mn | P | S | Al | N | Ti | Cr | Mo | B |
| A | 0.15 | 0.1 | 2.1 | 0.01 | 0.004 | 0.03 | 0.004 | 0.02 | 0.4 | 0.01 | 0.003 |
| B | 0.21 | 0.2 | 0.9 | 0.02 | 0.005 | 0.015 | 0.005 | 0.01 | 0.9 | 0.4 | 0.004 |
| C | 0.27 | 0.15 | 0.88 | 0.01 | 0.002 | 0.02 | 0.004 | 0.02 | 0.23 | 0.5 | 0.003 |
Table 6
| Symbol | Coating is formed | Single face adhesion amount (g/m 2) | The bath temperature (℃) |
| GI | Zn-0.2％Al | 85 | 460 |
| GA | Zn-10.5％Fe | 70 | 460 |
| GL | Zn-55％Al-1.6％Si | 75 | 610 |
| GAM | Zn-6％Al-3％Mg | 65 | 420 |
| GAMS | Zn-11％Al-3％Mg-0.1％Si | 80 | 430 |
Table 7
The fine crack scoring that a situation arises
The number total amount of the fine crack in 10 points: zero: 0; Zero: 1; △: less than 5; *: more than 5.
Same with embodiment 1,2, the No.7 of table 7 is because therefore small crackle has taken place in the dew point height.No.1, No.3 are because the fine crack of a little greater than 1%, has therefore taken place in the hydrogen amount.In addition, No.1～3 are because oxygen concentration is low, therefore can see with stove in the stove that accompanies of the evaporation of Zn in pollution, the deterioration of surface of steel plate.
Embodiment 4
Use cold-rolled steel sheet (plate thickness 1.4mm) through such composition of steel common hot rolling, cold rolling process, as shown in table 8 as material.Its part has been implemented hot-dip Al or hot-dip Zn system.The production line of non-oxidation furnace-reduction furnace type is used in hot-dip, and the plating back adopts the gas friction method to regulate the coating adhesion amount, cooling then, and the outward appearance of resulting coating is plating etc. not, for well.Coating kind and bath composition, bath temperature are shown in table 9.
Table 8
| C | Si | Mn | P | S | Al | N | Ti | Cr | Mo | B |
| 0.22 | 0.21 | 1.20 | 0.02 | 0.003 | 0.027 | 0.003 | 0.002 | 0.18 | 0.02 | 0.0018 |
Table 9
| Symbol | Coating is formed | Single face adhesion amount (g/m 2) | The bath temperature (℃) |
| AL | Al-10％Si-2％Fe | 80 | 660 |
| GI | Zn-0.2％Al | 85 | 460 |
| GA | Zn-10.5％Fe | 70 | 460 |
The steel plate of making is like this heated under various conditions, and the mould with cap shaped shown in Figure 1 forms then.Gap during hot pressing is shown in table 10.Carry out the Φ 5mm of 10 points, the punching of gap 0.5mm (both sides) at the edge part of cap then, after 7 days, observe punching portion, judge to have or not fine crack with 20 times magnifying glass.Heating is sample to be inserted in the electric furnace of controlled atmospher carry out.Heating-up time till 900 ℃ is roughly 4 minutes, and the time from the stove to the forcing press is about 10 seconds, and it is about 750 ℃ that punching press begins temperature.Cooling is carried out in mould, is 40 ℃/second from 700 ℃ to 350 ℃ average cooling rates.Table 10 illustrates heating condition and has or not fine crack.Moreover, to carry out cutting after the cap shape is shaped a part and under load 10kgf, measure Vickers hardness, the overall level of result is in the scope of Hv:410～510, and tissue demonstrates martensitic structure.
Table 10
The fine crack scoring that a situation arises
The number total amount of the fine crack in 10 points: zero: 0; Zero: 1; △: less than 5; *: more than 5.
The No.1 of table 10,7,13, the fine crack more than 5 can be seen in the gap of the mould during owing to hot pressing therefore below the lower limit of regulation.The No.6 of table 10,12,18, the gap of the mould during owing to hot pressing is more than set upper limit, and it is irregular therefore intensity to take place, and residual residual stress in the parts can be seen the fine crack more than 5.No.5,11,17 because the gap of the mould during hot pressing is big, therefore demonstrate take place that intensity is irregular, the tendency of residual residual stress in the parts, therefore a little fine crack has taken place.
Utilizability on the industry
According to the present invention, can use hot rolling, cold-rolled steel sheet, plating Al is that steel plate or plating Zn are steel plate, adopts the heat pressing process legal system to make high-strength parts, and the use of hydrogen embrittlement ground can not occur.
Claims (4)
1. the hot-press method of high-strength vehicle parts, it is characterized in that, use following hot rolling Cr, that do not implement plating or the cold-rolled steel sheet of C, 2 quality % that contains 0.05～0.5 quality % in the composition of steel, when adopting pressure sintering to make automobile component, the heating-up temperature before the punching press is defined as Ac
3More than, below 1100 ℃, the hydrogen concentration of heating atmosphere is defined as below the 2 volume %, dew point is defined as more than-10 ℃, below 6 ℃, and oxygen concentration is defined as 0.3～21 volume %.
2. the hot-press method of high-strength vehicle parts, it is characterized in that, use on the steel plate of the C, the Cr below the 2 quality % that in composition of steel, contain 0.05～0.5 quality % and implemented the steel plate as the plating of main body with Al, when adopting pressure sintering to make automobile component, the heating-up temperature before the punching press is defined as Ac
3More than, below 1100 ℃, the hydrogen concentration of heating atmosphere is defined as below the 2 volume %, dew point is defined as more than-20 ℃, below 7 ℃, and oxygen concentration is defined as 0.3～21 volume %.
3. the hot-press method of high-strength vehicle parts, it is characterized in that, use on the steel plate of the C, the Cr below the 2 quality % that in composition of steel, contain 0.05～0.5 quality % and implemented the steel plate as the plating of main body with Zn, when adopting pressure sintering to make automobile component, with the heating-up temperature before the punching press be defined as more than 800 ℃, below 1000 ℃, the hydrogen concentration of heating atmosphere is defined as below the 2 volume %, and dew point is defined as more than-10 ℃, below 6 ℃, and oxygen concentration is defined as 1～21 volume %.
4. a hot press parts is characterized in that, uses wantonly 1 described hot-press method of claim 1～3 to make.