A kind of manufacture method of operative clip of titanium
Technical field:
The present invention relates to a kind of operative clip of titanium and preparation method thereof, be mainly used in the medical instruments field surgery Minimally Invasive Surgery and prick inner tubular structure for envelope in the implant into body.
Background technology:
Operative clip of titanium of the prior art inboard does not have groove and band, and the goodness of fit of operative clip of titanium and inner tubular structure is bad, is easy to generate to leak and offset phenomena, and gripping performance compares relatively poor.In addition, the manufacture method of former operative clip of titanium adopts one heat treatment step usually, causes the poor toughness of product, phenomenon of rupture takes place when pulling open easily, and the glossing in the traditional handicraft is unfavorable for the concordance of product processing dimension.
Summary of the invention:
Technical problem to be solved by this invention is to overcome above shortcomings in the prior art, and a kind of have good clamping and flexible operative clip of titanium and preparation method thereof are provided.
The present invention solves the problems of the technologies described above the technical scheme that is adopted: this operative clip of titanium, and the external form that it is characterized in that operative clip of titanium is a V-type, the inboard of operative clip of titanium is provided with the groove and the band of certain width.
Groove width of the present invention is 0.3 millimeter.
Band width of the present invention is 0.2 millimeter.
The present invention also comprises a kind of manufacture method of operative clip of titanium as mentioned above, comprises and getting the raw materials ready, the cleaning-sterilizing oven dry, test package, it is characterized in that after getting the raw materials ready further comprising the steps of: wire-drawing shape, blanking, heat treatment A, the profile molding, heat treatment B, the deoxidation layer cleans, pickling, ultrasonic waves for cleaning.
The present invention compared with prior art has the following advantages and effect: reasonable in design, the operative clip of titanium of producing has good clamping and toughness.
Description of drawings:
Fig. 1 is the structural representation of the embodiment of the invention.
Fig. 2 is that the B of Fig. 1 is to view.
Fig. 3 is the A-A amplification view of Fig. 1.
Fig. 4 is the sketch map of embodiment of the invention manufacture method.
The specific embodiment:
Referring to Fig. 1~Fig. 3, the external form of embodiment of the invention operative clip of titanium 1 is a V-type, and the inboard of operative clip of titanium 1 is provided with the groove 2 and the band 3 of certain width.
The width of embodiment of the invention groove 2 can be 0.3 millimeter, can play the effect of reinforcement, and band 3 every sides can be the 3-8 groups, can play the effect that improves clamping, and its width can be 0.2 millimeter.
Referring to Fig. 4, the embodiment of the invention also comprises a kind of manufacture method of operative clip of titanium as mentioned above 1, and its key step comprises gets the raw materials ready, wire-drawing shape, blanking, heat treatment A, the profile molding, heat treatment B, the deoxidation layer cleans, pickling, ultrasonic waves for cleaning, cleaning-sterilizing oven dry, test package.Wherein get the raw materials ready and comprise preparation Φ 0.75mm circle titanium silk, Φ 0.95mm circle titanium silk or 1 * 0.7 flat titanium silk; Wire-drawing shape is mainly finished titanium silk wire drawing in corresponding wire-drawing die of different size, thereby guarantees cross section and groove 2 molding and conformance with standard; Blanking comprises that the good titanium silk of wire drawing carries out blanking with corresponding blanking mould, finishes the molding of band 3; Heat treatment A comprises that the titanium silk after the blanking puts into special implement, carries out annealing in process, and certain that this moment, ambient temperature can be between 480~680 ℃ was a bit stablized 3~10 minutes, took out the titanium silk then and was cooled to room temperature; The profile molding comprises that the titanium silk through Overheating Treatment A is carried out to type with corresponding profile mould, thereby obtains the titanium folder; Heat treatment B comprises that the titanium through the profile molding folds up in the special implement, carry out annealing in process, certain that this moment, ambient temperature can (exceed 20 ℃ of heat treatment A temperature) usually between 500~700 ℃ was a bit stablized 3~10 minutes, took out the titanium folder then and was cooled to room temperature; The deoxidation layer comprises that the titanium through Overheating Treatment B is added with in the cylinder of 30~60 order sands in the middle of inserting and putting, and this cylinder rolled 5~8 hours with about 90 rev/mins speed, pours sand and titanium folder into sieve then and separates; Cleaning is included in the container of cleaning and pours 90~100 ℃ boiled water into, adds an amount of liquid detergent again, pours the titanium folder of handling through the deoxidation layer then into, treats to wash by rubbing with the hands repeatedly after water temperature reduces, and takes out the titanium folder then; Pickling is included in the container of cleaning and pours warm water into, the nitric acid of concentration 65%~68%, concentration is not less than 40% Fluohydric acid., their weight ratio is 5: 0.3: 0.2, in little plastic containers, add about 1000 titanium folders again through cleaning, these titaniums are folded up in the solution that configures, soak about 1 minute for the first time, take out titanium and fold up cleaning back airing in the clear water, putting into for the second time the solution that configures again soaked about 2 minutes, take out titanium and fold up cleaning back airing in the clear water, putting into the solution that configures for the third time again soaked about 4 minutes, airing was finished pickling after the taking-up titanium folded up and cleans in the clear water, then solution is outwelled, reconfigure solution by above-mentioned prescription, pressing from both sides other unpickled titanium as stated above, pickling finishes; Ultrasonic waves for cleaning comprises that the titanium after the pickling folds up in the ultrasound wave washer, water temperature is heated to about 60 ℃ and cleaned 20 minutes, send into 100,000 grades of clean areas after taking out titanium folder airing water, then the titanium holder is put into ultrasonic cleaner, water temperature is heated to about 30 ℃ and cleaned 10 minutes, sends into 100,000 grades of clean areas behind the taking-up titanium holder airing water; Cleaning-sterilizing oven dry comprises that the titanium through ultrasonic waves for cleaning folds up into the constant temperature air dry oven dries, bake out temperature is arranged on about 50 ℃, drying time is 10 minutes, titanium after the oven dry clamps the titanium holder after ultrasound wave cleans, and takes out airing after the titanium holder that the titanium folder will be housed is then put into the container rinsing that fills purified water; Test package comprises the test package work of finishing product according to standard.