CN100445723C - 一种高温应变疲劳试验中固定引伸计的方法 - Google Patents
一种高温应变疲劳试验中固定引伸计的方法 Download PDFInfo
- Publication number
- CN100445723C CN100445723C CNB2005100479604A CN200510047960A CN100445723C CN 100445723 C CN100445723 C CN 100445723C CN B2005100479604 A CNB2005100479604 A CN B2005100479604A CN 200510047960 A CN200510047960 A CN 200510047960A CN 100445723 C CN100445723 C CN 100445723C
- Authority
- CN
- China
- Prior art keywords
- test
- sample
- extensometer
- fatigue test
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种热机械疲劳试验时测量试样应变用的引伸计的固定方法，具体为能够使引伸计在热机械疲劳试验时，使之与试样相对固定的方法。采用中性粉剂Al2O3粉与粘结剂水玻璃按重量比为(1∶1)-(1∶5)配制而成浆体，涂刷在试样表面，涂刷厚度为10-100微米。由于疲劳试验的试样表面非常光滑，又不能破坏，因此本发明采用一种耐高温、无腐蚀的中性粉剂与耐高温低强度的粘合剂配制而成的浆体，刷在试样表面，达到不破坏试样表面及性能的情况下，增大表面的粗糙度，增大引伸杆与表面摩擦力，避免了疲劳试验中，引伸计的引伸杆在试样上打滑的现象，确保试验顺利进行。
Description
技术领域
本发明涉及一种热机械疲劳试验时测量试样应变用的引伸计的固定方法，具体为能够使引伸计在热机械疲劳试验时，使之与试样相对固定的方法。
背景技术
由于航空、航天技术的发展，许多材料被应用在航空、航天器材上，但航空航天材料不同于一般材料，对它的各种性能指标的要求既高又精，因此实验室对这些材料的各种性能测试的数据也要求既准确又精确。其中测量材料在高温环境下的热机械疲劳寿命时，采用应变控制，如图1所示，高温应变疲劳试验机包括：试样1、试验机上夹头2、试验机下夹头3(可上下移动)、加热管4、引伸杆5、悬壁梁6、引伸计等，材料应变的测量由引伸计测出，引伸计两个引伸杆顶在试样的两点上，要随试验中的试样整体上下移动，同时要保持引伸计两杆与试样上的两个点保持相对静止，测出两点的应变。从常温环境中的引伸计的主体到高温环境下的试样上，引伸计的引伸杆需要足够长。如此，引伸计就具有一定重量，由悬臂梁固定的引伸计存在杠杆效应。另外，做疲劳试验的试样，由于表面缺陷会影响疲劳寿命，因此表面要求很高，试样的表面非常光滑，引伸杆的尖端为了与试样接触时不破坏试样表面，也做得非常光滑，这样引伸计的引伸杆顶在试样上的两点时，很容易打滑，不能确保试样上两点与引伸杆两端保持相对静止。
热机械疲劳的试验周期为2-3分钟，每个试样需要105-107周次，非常耗时；而且引伸杆价格昂贵，坏掉一个引伸杆会损失几万元人民币，因此，如果试验中出现打滑现象，就会因为数据不准或打滑过程引伸杆断掉而试验失败，如果一个试验失败，会造成人力、物力大量损失。
发明内容
本发明的目的在于提供一种高温应变疲劳试验中固定引伸计的方法，使试验过程中引伸计的引伸杆在试样上不打滑，确保试验正常进行。
本发明的技术方案是：
一种高温应变疲劳试验中固定引伸计的方法，采用中性粉剂Al2O3粉与粘结剂水玻璃按重量比为(1∶1)-(1∶5)配制而成浆体，涂刷在试样表面，涂刷厚度为10-100微米。
所述中性粉剂采用高纯度Al2O3粉(重量纯度为99％以上)，其粒度为0.1-10微米；
所述水玻璃模数为2.2-3.5，浓度为45-55波美度。
本发明的有益效果是：
由于疲劳试验的试样表面非常光滑，又不能破坏，因此本发明采用一种耐高温、无腐蚀的中性粉剂与耐高温低强度的粘合剂配制而成的浆体，刷在试样表面，达到不破坏试样表面及性能的情况下，增大表面的粗糙度，增大引伸杆与表面摩擦力，避免了疲劳试验中，引伸计的引伸杆在试样上打滑的现象，确保试验顺利进行，此项技术试验过程中，成功率可达100％。
附图说明
图1为高温应变疲劳试验示意图。
图2为涂刷浆料后的试样示意图。
图中，1试样；2试验机上夹头；3试验机下夹头(可上下移动)；4加热管；5引伸杆；6悬臂梁；7浆体。
具体实施方式
本发明把耐高温无腐蚀的中性粉剂与耐高温低强度的粘合剂按所需比例配成浆体，用软刷将浆体7刷在试样1表面上，如图2所示。待浆体干透，按正常程序组装试样，进行试验即可，高温应变疲劳试验采用如图1所示装置。所述中性粉剂采用高纯度Al2O3粉(重量纯度为99％以上)，其粒度为0.1-10微米；所述粘结剂采用水玻璃，其模数为2.2-3.5，浓度为45-55波美度。
实施例1
采用中性粉剂Al2O3粉(重量纯度为99％以上，粒度2-5微米)与粘结剂水玻璃按重量比为1∶3配制而成浆体，涂刷在试样表面，涂刷厚度为60-80微米。经试验，成功率可达100％。
实施例2
采用中性粉剂Al2O3粉(重量纯度为99％以上，粒度8-10微米)与粘结剂水玻璃按重量比为1∶2配制而成浆体，涂刷在试样表面，涂刷厚度为90-100微米。经试验，成功率可达100％。
实施例3
采用中性粉剂Al2O3粉(重量纯度为99％以上，粒度0.1-0.5微米)与粘结剂水玻璃按重量比为1∶1配制而成浆体，涂刷在试样表面，涂刷厚度为10-20微米。经试验，成功率可达100％。
实施例4
采用中性粉剂Al2O3粉(重量纯度为99％以上，粒度0.5-1微米)与粘结剂水玻璃按重量比为1∶5配制而成浆体，涂刷在试样表面，涂刷厚度为30-50微米。经试验，成功率可达100％。
Claims (1)
1、一种高温应变疲劳试验中固定引伸计的方法，其特征在于：采用中性粉剂Al2O3粉与粘结剂水玻璃按重量比为(1∶1)-(1∶5)配制而成浆体，涂刷在试样表面，涂刷厚度为10-100微米；所述Al2O3粉的重量纯度为99％以上，其粒度为0.1-10微米；所述水玻璃的模数为2.2-3.5，其浓度为45-55波美度。