CN100442982C - Method for preparing nano Ag (I)/Ag (III)/TiO2 composite material - Google Patents
Method for preparing nano Ag (I)/Ag (III)/TiO2 composite material Download PDFInfo
- Publication number
- CN100442982C CN100442982C CNB2006101047104A CN200610104710A CN100442982C CN 100442982 C CN100442982 C CN 100442982C CN B2006101047104 A CNB2006101047104 A CN B2006101047104A CN 200610104710 A CN200610104710 A CN 200610104710A CN 100442982 C CN100442982 C CN 100442982C
- Authority
- CN
- China
- Prior art keywords
- solution
- agno
- concentration
- ammonia
- iii
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a preparation method of nano Ag(I)/Ag(III)/TiO2 composite material. Said method includes the following steps: dissolving AgNO3 in ammonia water to obtain AgNO3 ammonia solution; dissolving Ti(SO4)2 in deionized water to obtain Ti(SO4)2 solution: mixing the above-mentioned both them to obtain white colloidal solution; adding KOH or NaOH and K2SiO8 crystal or H2O2 solution into said colloidal solution, stirring them at 50-90 deg.C, standing still at 40-80 deg.C, vacuum filtering and using deionized water to wash the above-mentioned material and remove SO42- ions, drying and grinding to obtain powder body, treating said powder body at 500-600 deg.C for 2h, and cooling so as to obtain the invenled product.
Description
Technical field
The invention belongs to nano-TiO
2The preparation method of composite, particularly a kind of nanometer Ag (I)/Ag (III)/TiO
2The preparation method of composite.
Background technology
The TiO of anatase phase
2It is material with photocatalysis characteristic, it utilizes the ultraviolet light in sunshine, the fluorescent lamp to make excitaton source and have antimicrobial effect, action effect is lasting, and have purify air, dispose of sewage, from photocatalytic effects such as cleanings, the prerequisite of its realization is exciting of ultraviolet light, so, in the occasion that does not have ultraviolet light to exist, even the TiO of anatase phase
2There is not antibiotic effect, with the TiO of anatase phase yet
2Nano silver-carrying composite titania material (Ag/TiO for carrier
2) be desirable anti-biotic material, do not having have strong anti-, biocidal property when ultraviolet ray excited yet, silver wherein is monovalence silver Ag (I).Studies show that: the antibiotic property of Ag (II), Ag (III) is 50~200 times of Ag (I), and the sterilization speed of Ag (III) is 240 times of Ag (I), if therefore can prepare Ag (II)/TiO
2Or Ag (III)/TiO
2Antimicrobial composite material will be carried the anti-microbial property of high silver supported composite titania material greatly, because the oxidisability of Ag (III) is high more a lot of than Ag (I), E ° of Ag (I)/Ag=0.799 lies prostrate, and E ° of Ag (III)/Ag>2 volt, therefore, Ag (II)/TiO
2Or Ag (III)/TiO
2Antimicrobial composite material also can have stronger catalytic oxidation activity.
At present, Ag/TiO
2With contain argentic active carbon, phosphate and silver-colored zinc antimicrobial composite material and prepared success, and good application (Liu Qingju, Zhang Jin, Zhu Zhongqi etc. are arranged.Carry silver-colored TiO
2The preparation and property research of inorganic antiseptic.Functional material.2005.3 (36): 474~476; Ma Dengfeng, Peng Bing, Chai Liyuan etc.The Study on Preparation of Ag-carried nanometer titanium dioxide antimicrobial powder.Fine-chemical intermediate.2006.2,36 (1): 63~66; Huang Yueyuan, Mi Yu, Guo Renmin etc.TiO
2The research of base composite nano germicide.Chemical Engineering.2004.8,32 (4): 46~48; Huang Yueyuan, Mi Yu, Guo Renmin etc.TiO
2/ Ag nano anti-biotic material.Northwest University's journal (natural science edition) 2003.10,33 (5): 566~571; Liu Xuefeng is coated with an inscription ancient type of banner hoisted on a featherdecked mast.The development of rare earth loaded type nano titanium dioxide anti-bacterial agent.Modern chemical industry.2005.7,145~147; Liu Xuefeng, Zhang Li is coated with an inscription ancient type of banner hoisted on a featherdecked mast.Nano Ce/TiO
2The preparation of inorganic antiseptic and performance evaluation thereof.The process engineering journal.2004.6,4 (3): 256~260; Han Qing profit 1, gold is revitalized, Huang Hongyan.Microwave drying prepares Ag/TiO
2The photocatalytic activity experimental study.Environmental protection science.2005.10,31 (131): 6~12; Zhang Fuxiang, Zhang Xiu, Chen Jixin etc.Ag/TiO
2The preparation of composite nano-catalyst and sign and photocatalytic activity thereof.The catalysis journal.2003.11,24 (11): 887~880; Zhao Gaoling, Han Gaorong.The Prepared by Sol Gel Method of Nano silver grain P titania coextruded film and the research of optical property thereof.Materials Science and Engineering.2001,19 (1): 21~25; What advances, Chen Xingbi, Yang Chuanren.TiO
2(Ag) preparation of Nano semiconductor film and photocatalysis performance thereof.Electronic component and material.1999,2:13~17; Wang Zhiqun.Compound silver series inorganic germifuge.The number of applying for a patent: 98111623.X; Be coated with an inscription ancient type of banner hoisted on a featherdecked mast; Yan Qingwei; Hair is strong; Zhang Xiaoli.A kind of dichloride in anatase type TiO
2Composite inorganic antimicrobial agent and preparation method thereof.The number of applying for a patent: 200410081239.2; Open civilian bell-shaped percussion instrument, used in ancient time by troops on march; Wang Guangwen; For grand celebration.A kind of silver-colored phosphate inorganic antiseptic of high price and preparation method thereof that contains.The number of applying for a patent: 200310105878.3; Zheng Rongyu; Luo Xiaoming; Blue equality.A kind of silver carried bactericidal active carbon and preparation method thereof and application.Patent announcement number: CN1720801; Zheng Rongyu; Jiang Huade; Luo Xiaoming.A kind of argentiferous, zinc composite sterilizing agent and preparation method thereof and application.Patent announcement number: CN1751577).
Summary of the invention
The object of the present invention is to provide nanometer Ag (I)/Ag (III)/TiO that a kind of preparation technology is simple, easy to operate, pollution is few
2The preparation method of composite.
The technical solution used in the present invention is in order to achieve the above object: at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.001~0.01mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.02~0.2mol/L
4)
2Solution; Under 40~80 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1~1: 1.5 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 90~100 ℃, constant temperature 2 hours adds KOH or NaOH then in colloidal solution, and the concentration of control KOH or NaOH is 0.05mol/L, adds K again
2S
2O
8Crystal or mass concentration are 30% H
2O
2Solution, control K
2S
2O
8Or H
2O
2Concentration be 0.05~0.1mol/L, at 50~90 ℃, rapid stirring constant temperature is processed 5~10h, leaves standstill 12~24h then under 40~80 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of drying 20~24h, be ground to powder; Above-mentioned gained powder in 500~600 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (I) or Ag (III).
The present invention is with AgNO
3Ammonia solution provides the precipitating reagent of precipitated titanium ion simultaneously for composite provides silver, is the key substance that realizes one-step synthesis; Under stirring condition the mixing of two kinds of solution guaranteed uniformity, the degree of supersaturation when having controlled precipitation and the growth of crystal; Be warmed up to 90~100 ℃ and to stir main purpose be volatilization except ammonia, reduce the pH value to 5 of solution~6 after the mixing, make Ag
+Enter into TiO by ion-exchange or absorption
2In the crystal; " add KOH or NaOH and K
2S
2O
8Crystal or H
2O
2Solution changes into Ag with Ag (I)
2O
2, K
2S
2O
8Strong oxidizer, Ag
2O
2In one of them silver be Ag (I), another is Ag (III), therefore resulting composite is nanometer Ag (I)/Ag (III)/TiO
2Adding to leave standstill to make crystal more complete; Powder is to obtain the TiO of Detitanium-ore-type in 500~600 ℃ of processing intents
2Crystal is fixed on Ag (I), Ag (III) in the crystal simultaneously, increases its stability.The present invention adopts Ti (SO
4)
2As raw material, with the employing nano-TiO
2Or metatitanic acid is that raw material prepares nanometer titanium dioxide composite material and compares, and low price can make production cost greatly reduce, owing to there is not the acid hydrolysis process not only can reduce cost but also can reduce acid pollution.
Embodiment
Embodiment 1, and at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.001mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.2mol/L
4)
2Solution; Under 60 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 90 ℃, constant temperature 2 hours; In colloidal solution, add then KOH, and control KOH concentration be 0.05mol/L, add again K
2S
2O
8Crystal, control K
2S
2O
8Concentration is 0.07mol/L, and at 80 ℃, rapid stirring constant temperature is processed 6h, leaves standstill 24h then under 40 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 24h, be ground to powder; Above-mentioned gained powder in 500 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (II) or Ag (III).
Embodiment 2, and at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.01mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.06mol/L
4)
2Solution; Under 40 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1.3 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 94 ℃, constant temperature 2 hours; In colloidal solution, add then NaOH, and the concentration of control NaOH is 0.05mol/L, adds again mass concentration and be 30% H
2O
2Solution, control H
2O
2Concentration be 0.05mol/L, at 60 ℃, rapid stirring constant temperature is processed 9h, leaves standstill 18h then under 60 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 20h, be ground to powder; Above-mentioned gained powder in 600 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (II) or Ag (III).
Embodiment 3, and at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.005mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.1mol/L
4)
2Solution; Under 70 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1.5 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 98 ℃, constant temperature 2 hours; In colloidal solution, add then KOH, and control KOH concentration be 0.05mol/L, add again K
2S
2O
8Crystal, control K
2S
2O
8Concentration be 0.09mol/L, at 50 ℃, rapid stirring constant temperature is processed 10h, leaves standstill 12h then under 80 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 23h, be ground to powder; Above-mentioned gained powder in 530 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (II) or Ag (III).
Embodiment 4, and at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.003mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.15mol/L
4)
2Solution; Under 50 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1.2 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 92 ℃, constant temperature 2 hours; In colloidal solution, add then NaOH, and the concentration of control NaOH is 0.05mol/L, adds again mass concentration and be 30% H
2O
2Solution, control H
2O
2Concentration be 0.06mol/L, at 90 ℃, rapid stirring constant temperature is processed 5h, leaves standstill 20h then under 50 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 21h, be ground to powder; Above-mentioned gained powder in 560 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (II) or Ag (III).
Embodiment 5, and at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.007mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.02mol/L
4)
2Solution; Under 80 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1.4 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 100 ℃, constant temperature 2 hours; In colloidal solution, add then KOH, and the concentration of control KOH is 0.05mol/L, adds again mass concentration and be 30% H
2O
2Solution, control H
2O
2Concentration be 0.1mol/L, at 70 ℃, rapid stirring constant temperature is processed 7h, leaves standstill 16h then under 70 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 22h, be ground to powder; Above-mentioned gained powder in 510 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (II) or Ag (III).
The present invention is simple to operate, and one-step synthesis does not need the acid hydrolysis process, and consumption acids not pollutes littlely, becomes This is cheap, is easy to suitability for industrialized production; Resulting materials is nanometer Ag (I)/Ag (III)/TiO2Composite, granular size are 30~40nm, and main crystal composition is Detitanium-ore-type TiO2, with present Ag/TiO2(wherein silver for Ag (I)) composite is compared has more high light catalytic action and antibiotic property. It is significantly special Point is: one-step synthesis, technology are simple; Carrying silver is at nano level TiO2Carry out in the colloidal solution, the mixing ratio conventional method is more even, much larger in silver and the existing method of titanium dioxide contact area rate, carrying silver not only carries out on the surface, but in all titanium dioxide nanoparticles, carry out, reduced silver-colored oxidation stain degree, thus very be conducive to obtain that silver disperses very evenly, the variable color degree is littler, nanometer Ag (I) that catalytic activity and bactericidal property are very strong/Ag (III)/TiO2。
Claims (6)
1, a kind of nanometer Ag (I)/Ag (III)/TiO
2The preparation method of composite is characterized in that:
1) at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.001~0.01mol/L in the ammonia spirit
3Ammonia solution;
2) secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.02~0.2mol/L
4)
2Solution;
3) under 40~80 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1~1: 1.5 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution;
4) continue to stir and gained colloidal solution is warming up to 90~100 ℃, constant temperature 2 hours,
5) in colloidal solution, add then KOH or NaOH, and the concentration of control KOH or NaOH is 0.05mol/L, adds again K
2S
2O
8Crystal or mass concentration are 30% H
2O
2Solution, control K
2S
2O
8Or H
2O
2Concentration be 0.05~0.1mol/L, at 50~90 ℃, rapid stirring constant temperature is processed 5~10h, leaves standstill 12~24h then under 40~80 ℃;
6) vacuum filtration and remove SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of drying 20~24h, it is ground is powder;
7) above-mentioned gained powder is handled 2h in 500~600 ℃,, obtain nanometer Ag (I)/Ag (III)/TiO with the stove cooling
2, wherein main crystal consists of Detitanium-ore-type TiO
2, wherein be loaded with Ag (I) or Ag (III).
2, nanometer Ag according to claim 1 (I)/Ag (III)/TiO
2The composite manufacture method is characterized in that: at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.001mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.2mol/L
4)
2Solution; Under 60 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 90 ℃, constant temperature 2 hours; In colloidal solution, add then KOH, and control KOH concentration be 0.05mol/L, add again K
2S
2O
8Crystal, control K
2S
2O
8Concentration is 0.07mol/L, and at 80 ℃, rapid stirring constant temperature is processed 6h, leaves standstill 24h then under 40 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 24h, be ground to powder; Above-mentioned gained powder in 500 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (I) or Ag (III).
3, nanometer Ag according to claim 1 (I)/Ag (III)/TiO
2The composite manufacture method is characterized in that: at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.01mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.06mol/L
4)
2Solution; Under 40 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1.3 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 94 ℃, constant temperature 2 hours; In colloidal solution, add then NaOH, and the concentration of control NaOH is 0.05mol/L, adds again mass concentration and be 30% H
2O
2Solution, control H
2O
2Concentration be 0.05mol/L, at 60 ℃, rapid stirring constant temperature is processed 9h, leaves standstill 18h then under 60 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 20h, be ground to powder; Above-mentioned gained powder in 600 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (I) or Ag (III).
4, nanometer Ag according to claim 1 (I)/Ag (III)/TiO
2The composite manufacture method is characterized in that: at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.005mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.1mol/L
4)
2Solution; Under 70 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1.5 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 98 ℃, constant temperature 2 hours; In colloidal solution, add then KOH, and control KOH concentration be 0.05mol/L, add again K
2S
2O
8Crystal, control K
2S
2O
8Concentration be 0.09mol/L, at 50 ℃, rapid stirring constant temperature is processed 10h, leaves standstill 12h then under 80 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 23h, be ground to powder; Above-mentioned gained powder in 530 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (I) or Ag (III).
5, nanometer Ag according to claim 1 (I)/Ag (III)/TiO
2The composite manufacture method is characterized in that: at first being 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.003mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.15mol/L
4)
2Solution; Under 50 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1.2 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 92 ℃, constant temperature 2 hours; In colloidal solution, add then NaOH, and the concentration of control NaOH is 0.05mol/L, adds again mass concentration and be 30% H
2O
2Solution, control H
2O
2Concentration be 0.06mol/L, at 90 ℃, rapid stirring constant temperature is processed 5h, leaves standstill 20h then under 50 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 21h, be ground to powder; Above-mentioned gained powder in 560 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (I) or Ag (III).
6, nanometer Ag according to claim 1 (I)/Ag (III)/TiO
2The composite manufacture method is characterized in that: being earlier 25% ammoniacal liquor and deionized water with mass concentration is mixed and made into ammonia spirit by 1: 1 volume ratio, then with AgNO
3Be dissolved in and make the AgNO that concentration is 0.007mol/L in the ammonia spirit
3Ammonia solution; Secondly with Ti (SO
4)
2Be dissolved in the deionized water, being mixed with concentration is the Ti (SO of 0.02mol/L
4)
2Solution; Under 80 ℃ of stirrings, press AgNO
3Ammonia solution and Ti (SO
4)
2Solution is that 1: 1.4 volume ratio is with AgNO
3Ammonia solution stream is added to Ti (SO
4)
2In the solution or with Ti (SO
4)
2Flow of solution is added to AgNO
3In the ammonia solution, obtain the white size liquid solution; Continue to stir and gained colloidal solution is warming up to 100 ℃, constant temperature 2 hours; In colloidal solution, add then KOH, and the concentration of control KOH is 0.05mol/L, adds again mass concentration and be 30% H
2O
2Solution, control H
2O
2Concentration be 0.1mol/L, at 70 ℃, rapid stirring constant temperature is processed 7h, leaves standstill 16h then under 70 ℃; Vacuum filtration is also removed SO through deionized water washing
4 2-Behind the ion, behind 90 ℃ of dry 22h, be ground to powder; Above-mentioned gained powder in 510 ℃ of processing 2h, with the stove cooling, is obtained nanometer Ag (I)/Ag (III)/TiO
2, wherein main crystal composition is Detitanium-ore-type TiO
2, wherein be loaded with Ag (I) or Ag (III).