CN100420768C - 一种低合金铸钢及其制备方法 - Google Patents
一种低合金铸钢及其制备方法 Download PDFInfo
- Publication number
- CN100420768C CN100420768C CNB2007100133037A CN200710013303A CN100420768C CN 100420768 C CN100420768 C CN 100420768C CN B2007100133037 A CNB2007100133037 A CN B2007100133037A CN 200710013303 A CN200710013303 A CN 200710013303A CN 100420768 C CN100420768 C CN 100420768C
- Authority
- CN
- China
- Prior art keywords
- low
- alloy cast
- cast steel
- chemical ingredients
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种低合金铸钢及其制备方法,本发明低合金铸钢包含下列重量百分比的化学成分:C:0.48-0.55%,Si:0.20-0.40%,Mn:0.70-1.00%,Ni:0.50-0.70%,Cr:0.45-0.70%,Mo:0.15-0.25%,P≤0.040%,S:≤0.040%,余量为铁。本发明的低合金铸钢的制备方法包括如下步骤:1.配料;2.熔炼;3.浇注;4.调质处理。本发明有益效果:本发明低合金铸钢在经调质处理后,其机械性能为σb≥1035MPa,σs≥930MPa,δ≥9%,布氏硬度HB=321-388;能满足汽车行业中轮体铸件的各项性能要求。
Description
(一)技术领域
本发明涉及一种铸钢及其制备方法,特别是一种低合金铸钢及其制备方法。
(二)背景技术
近年来随着铸钢行业的发展,部分铸钢件对机械性能及硬度要求越来越高,特别是汽车行业中轮体铸件要求具有高强度高硬度的性能。但目前,能达到上述性能要求的材为较少,且价格较贵。
(三)发明内容
本发明要解决的技术问题是:提供一种具有高强度高硬度的低合金铸钢材料及其制备方法。
为了解决上技术问题:
本发明低合金铸钢包含下列重量百分比的化学成分:
C:0.48-0.55%,Si:0.20-0.40%,Mn:0.70-1.00%,Ni:0.50-0.70%,Cr:0.45-0.70%,Mo:0.15-0.25%,P≤0.040%,S:≤0.040%,余量为铁。
为了获得较好的机械性能,所述C:0.49%,Si:0.27%,Mn:0.79%,Ni:0.53%,Cr:0.50%,Mo:0.18%,P:0.022%,S:0.024%。
为了获得较好的机械性能,所述C:0.53%,Si:0.30%,Mn:0.88%,Ni:0.54%,Cr:0.56%,Mo:0.21%,P:0.025%,S:0.023%。
本发明的低合金铸钢的制备方法包括如下步骤:1、按照所给出的化学成分范围,用废钢和生铁配料;2、把配好的料装入电弧炉中进行熔炼,熔炼过程中加入硅铁、锰铁、电解镍、铬铁和钼铁合金调整化学成分;3、把熔炼得到的钢水浇注成铸件;4、调质处理。
本发明有益效果:本发明低合金铸钢在经调质处理后,其机械性能为σb≥1035Mpa,σs≥930Mpa,δ≥9%,布氏硬度HB=321-388;能满足汽车行业中轮体铸件的各项性能要求。
(四)具体实施方式
实施例1
本实施例为一种低合金铸钢,其化学成分为(重量百分比):C:0.49%,Si:0.27%,Mn:0.79%,Ni:0.53%,Cr:0.50%,Mo:0.18%,P:0.022%,S:0.024%,余量为铁。
本具体实施例低合金铸钢的制备方法为:包括如下步骤:1、按照所给出的化学成分范围,用废钢和生铁配料;2、把配好的料装入电弧炉中进行熔炼,熔炼过程中加入硅铁、锰铁、电解镍、铬铁和钼铁合金调整化学成分;3、把熔炼得到的钢水浇注成铸件;4、调质处理,进行测量后,其机械性能如下:σb=1086Mpa,σs=947Mpa,δ=9.8%,布氏硬度HB=335。
实施例2
本实施例为一种低合金铸钢,其化学成分为(重量百分比):C:0.53%,Si:0.30%,Mn:0.88%,Ni:0.54%,Cr:0.56%,Mo:0.21%,P:0.025%,S:0.023%,余量为铁。
本具体实施例低合金铸钢的制备方法为:包括如下步骤:1、按照所给出的化学成分范围,用废钢和生铁配料;2、把配好的料装入电弧炉中进行熔炼,熔炼过程中加入硅铁、锰铁、电解镍、铬铁和钼铁合金调整化学成分;3、把熔炼得到的钢水浇注成铸件;4、正火处理,进行测量后,其机械性能如下:σb=1108Mpa,σs=959Mpa,δ=9.4%,布氏硬度HB=357。
Claims (4)
1. 一种低合金铸钢,其特征在于:包含下列重量百分比的化学成分:
C:0.48-0.55%,Si:0.20-0.40%,Mn:0.70-1.00%,Ni:0.50-0.70%,Cr:0.45-0.70%,Mo:0.15-0.25%,P≤0.040%,S:≤0.040%,余量为铁。
2. 根据权利要求1所述的低合金铸钢,其特征在于:所述C:0.49%,
Si:0.27%,Mn:0.79%,Ni:0.53%,Cr:0.50%,Mo:0.18%,P:0.022%,S:0.024%。
3. 根据权利要求1所述的低合金铸钢,其特征在于:所述C:0.53%,
Si:0.30%,Mn:0.88%,Ni:0.54%,Cr:0.56%,Mo:0.21%,P:0.025%,S:0.023%。
4. 一种权利要求1、2或3所述的低合金铸钢的制备方法,其特征在于:包括如下步骤:1、按照所给出的化学成分范围,用废钢和生铁配料;2、把配好的料装入电弧炉中进行熔炼,熔炼过程中加入硅铁、锰铁、电解镍、铬铁和钼铁合金调整化学成分;3、把熔炼得到的钢水浇注成铸件;4、调质处理。