CN100413923C - Nano composite material of epoxy resin and its preparing method - Google Patents
Nano composite material of epoxy resin and its preparing method Download PDFInfo
- Publication number
- CN100413923C CN100413923C CNB031281362A CN03128136A CN100413923C CN 100413923 C CN100413923 C CN 100413923C CN B031281362 A CNB031281362 A CN B031281362A CN 03128136 A CN03128136 A CN 03128136A CN 100413923 C CN100413923 C CN 100413923C
- Authority
- CN
- China
- Prior art keywords
- epoxy resin
- epoxy
- rectorite leng
- organises
- organic amine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to an epoxy resin nanometer composite material which comprises 40 to 95% of epoxy resin, 0.1 to 10% of organized rectorite and 1 to 59% of curing agent used for epoxy resin. The present invention also provides a preparation method of the epoxy resin nanometer composite materials, which comprises the following steps: adding the organized rectorite to the epoxy resin; heating the epoxy resin to be melting; adding and uniformly stirring the epoxy resin curing agent to the mixture of epoxy resin and the rectorite which are stirred in a vacuum pumping mode; pouring the mixture in a mould and molding the mixture at 60 to 160 DEG C by solidifying. The preparation method of the present invention is simple, and the obtained epoxy resin nanometer composite material has the advantages of preferable toughness, high shock resistance, excellent heat resistance and low cost.
Description
Technical field
The present invention relates to a kind of epoxy resin nano composites and preparation method thereof.
Background technology
The casting material of existing model, instrument, electrical equipment, sheet metal mould adopts Resins, epoxy usually.Resins, epoxy is fragility, and impact resistance is bad, and resistance toheat also has much room for improvement.The needs of higher model, instrument, electrical equipment, sheet metal mould etc. are difficult to meet the demands.
Summary of the invention
The present invention provides a kind of epoxy resin nano composites and preparation method thereof at the problems referred to above exactly, and the gained epoxy resin nano composites has toughness and resistance toheat preferably, and with low cost.
Technical scheme provided by the invention is: a kind of epoxy resin nano composites comprises 40~95% Resins, epoxy, 0.1~10% the rectorite leng that organises, 1~59% hardener for epoxy resin; The rectorite leng that wherein organises is nano-sheet and is dispersed in the epoxy matrix; Above per-cent is mass percent.
The above-mentioned rectorite leng that organises obtains by the following method: be that 2~8: 1 ratio is with water and rectorite leng mixing and stirring in mass ratio; In the mass ratio of organic amine and rectorite leng is that 1: 2~10 ratio is got organic amine, adds entry in organic amine, and the mass ratio of organic amine and water is 1: 10~20, drips acid again and makes pH value less than 7, makes organic amine change into ammonium salt; Subsequently with joining ammonium salt slowly be added in the mixture of above-mentioned water and rectorite leng, stir, filter, oven dry promptly gets the required rectorite leng that organises.
Also contain mass percent in the above-mentioned epoxy resin nano composites and be 0.1~0.5% reactive thinner.
The present invention also provides the preparation method of above-mentioned epoxy resin nano composites: the rectorite leng that organises is joined in the Resins, epoxy, add reactive thinner in case of necessity, be heated to the resin fusing then, vacuumizing stirring back adding epoxy curing agent stirs, pour mould again into, at 60 ℃--160 ℃ of curing moldings.
Preparation method of the present invention is simple, and the gained epoxy resin nano composites has toughness preferably, and not only impact resistance is good, and resistance toheat is superior, and is with low cost.Rectorite leng becomes the nano-dispersed shape in Resins, epoxy, can see with electron microscopy observation, can't see diffraction peak with the X diffractometer, rectorite leng is peeled away into nano-sheet by Resins, epoxy and is dispersed in the epoxy matrix, model, instrument, electrical equipment, sheet metal mould that the present invention makes as casting material.
Embodiment
Embodiment 1: restrain the rectorite leng that organises with 0.5 and join in 100 gram E-44 (#6101) Resins, epoxy, add 050 reactive thinner (commercially available prod), 0.3 gram again, be heated to 80 ℃, vacuumize and stir 1 hour simultaneously. add 650 polymeric amide, 100 grams at last and stir, pour in the mould, promptly got epoxy resin nano composites required for the present invention in one hour 65 ℃ of curing.
Embodiment 2: restrain the rectorite leng that organises with 10 and join in 100 gram E-54 (#616) Resins, epoxy, being heated to 90 ℃ vacuumizes and stirs 1 hour simultaneously, add the poly-nonane diacid acid anhydride of 8 grams at last, pour in the mould and promptly got epoxy resin nano composites required for the present invention in 1.5 hours 130 ℃ of curing.
Embodiment 3: restrain the rectorite leng that organises with 1 and join in 100 gram E-44 (#6101) Resins, epoxy, add 0.5 gram reactive thinner n-butyl glycidyl ether again, be heated to 80 ℃, vacuumize and stir 1.5 hours simultaneously, add 14 gram Triethylenetetramine (TETA)s at last, pour in the mould and promptly get epoxy resin nano composites required for the present invention 100 ℃ of curing.
The above-mentioned rectorite leng that organises can be the method preparation that 02115758.8 patent application that is called organic composite rectorite and preparation method thereof provides by number of patent application; The method of also can pressing makes: add rectorite leng in container 1, add entry again, the mass ratio of water and rectorite leng is in 2: 1 to 8: 1 scopes, mixing and stirring; Add organic amine as (hexadecylamine) (organic amine and rectorite leng mass ratio are 1: 10 to 1: 2 scope in) in container 2, add entry again, the mass ratio of organic amine and water is 1: 10 to 1: 20, drips acid again and makes pH value less than 7, allows organic amine change into ammonium salt; Subsequently with joining ammonium salt slowly add in the container 1, drip off back restir more than 1 hour, refilter, be dried into the required rectorite leng that organises.
Claims (4)
1. an epoxy resin nano composites comprises 40~95% Resins, epoxy, 0.1~10% the rectorite leng that organises, 1~59% hardener for epoxy resin; The rectorite leng that wherein organises is nano-sheet and is dispersed in the epoxy matrix; Join in the Resins, epoxy by the rectorite leng that will organise, be heated to the resin fusing, vacuumize stirring back adding epoxy curing agent and stir, pour mould again into, obtain epoxy resin nano composites at 60 ℃~160 ℃ curing moldings; Above per-cent is mass percent; The rectorite leng that organises obtains by the following method, is that 2~8: 1 ratio is with water and rectorite leng mixing and stirring in mass ratio; In the mass ratio of organic amine and rectorite leng is that 1: 2~10 ratio is got organic amine, adds entry in organic amine, and the mass ratio of organic amine and water is 1: 10~20, drips acid again and makes pH value less than 7, makes organic amine change into ammonium salt; Subsequently with joining ammonium salt slowly be added in the mixture of above-mentioned water and rectorite leng, stir, filter, oven dry promptly gets the required rectorite leng that organises.
2. matrix material according to claim 1 is characterized in that: contain mass percent and be 0.1~0.5% reactive thinner.
3. the preparation method of the described epoxy resin nano composites of claim 1, it is characterized in that: the rectorite leng that organises is joined in the Resins, epoxy, be heated to the resin fusing, vacuumizing stirring back adding epoxy curing agent stirs, pour mould again into, at 60 ℃~160 ℃ curing moldings.
4. preparation method according to claim 3, it is characterized in that: the rectorite leng that organises is joined in the Resins, epoxy, add reactive thinner again, be heated to the resin fusing then, vacuumizing stirring back adding epoxy curing agent stirs, pour mould again into, at 60 ℃~160 ℃ curing moldings.