CN100396746C - Cleaning glue - Google Patents
Cleaning glue Download PDFInfo
- Publication number
- CN100396746C CN100396746C CNB2006100504297A CN200610050429A CN100396746C CN 100396746 C CN100396746 C CN 100396746C CN B2006100504297 A CNB2006100504297 A CN B2006100504297A CN 200610050429 A CN200610050429 A CN 200610050429A CN 100396746 C CN100396746 C CN 100396746C
- Authority
- CN
- China
- Prior art keywords
- rubber
- acetone
- alcohol
- carbon black
- white carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides cleaning glue which comprises 65 to 85 wt% of acetone, 0 to 10 wt% of alcohol, 2 to 10 wt% of gas phase silica white and 5 to 25 wt% of synthetic rubber. The present invention has the advantage that alpha-cyanoacrylate can be cleared thoroughly.
Description
Technical field
The present invention relates to a kind of cleaning rubber, especially a kind of cleaning rubber that is used to remove the a-cyanoacrylate.
Background technology
A-cyanacrylate (being commonly called as 502) is easy to use, the adhesive strength height, thereby be widely used in a lot of industries, and accepted by people day by day as family expenses glue.But people in use can do the a-cyanacrylate on the skin or on other object unavoidably because of carelessness, and its curing speed is fast, must adopt specific solvent after the curing otherwise be difficult to and remove.People generally adopt acetone that its dissolving is softening at present, use the wiper wiping again.But because acetone is liquid, can flow away toward the next door when dripping to it on the a-cyanacrylate, not only can not dissolve the a-cyanacrylate fully, but also can pollute; Moreover, acetone is volatile substances, when it vapors away, the a-cyanacrylate that is softened still remains on the skin or on other object, if untimelyly use the wiper wiping, the a-cyanacrylate can't be removed, the a-cyanacrylate that contacts post softening with air is cured again.Through applicant retrieval, patent database still is not used to remove the record of the material of a-cyanacrylate better at present.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of cleaning rubber is provided, can remove the a-cyanacrylate up hill and dale.
For achieving the above object, the invention provides a kind of cleaning rubber, by weight percentage, contain following composition:
The white carbon black 2～10 of acetone 65～85 alcohol 0～10 gas phase
Synthetic rubber 5～25.
The blending ratio of above-mentioned composition:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Synthetic rubber 8～20.
Above-mentioned synthetic rubber is at least a in paracril, isoprene-isobutylene rubber, the styrene-butadiene rubber(SBR).
The blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Paracril 8～20.
The blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Styrene-butadiene rubber(SBR) 8～20.
The blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Isoprene-isobutylene rubber 8～20.
The blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Paracril and isoprene-isobutylene rubber 8～20.
The blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Paracril and styrene-butadiene rubber(SBR) 8～20.
The blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Paracril and isoprene-isobutylene rubber and styrene-butadiene rubber(SBR) 8～20.
The present invention as carrier, is fused into glue with acetone, in the time of use with synthetic rubber, cleaning rubber is dropped on the a-cyanacrylate, cleaning rubber can surround the a-cyanacrylate, can not run off, like this acetone just can be fully and the a-cyanacrylate separate; Melt the back and rub with the hands lightly back and forth with finger, cleaning adhesive tape remollescent a-cyanacrylate and is come off.The present invention utilizes conventional gimmick promptly to can be made into.
Embodiment
Be described in further detail below in conjunction with embodiment:
Embodiment one
Get acetone 75g, paracril 20g stirs both and makes it thorough mixing; Add the white carbon black 5g of gas phase, can be divided in the flexible pipe after stirring.
Embodiment two
Get acetone 85g, styrene-butadiene rubber(SBR) 10g stirs both and makes it thorough mixing; Add the white carbon black 3g of gas phase, fully stir; Pour alcohol 2g at last into, can be divided in the flexible pipe after stirring.
Embodiment three
Get acetone 75g, isoprene-isobutylene rubber 15g stirs both and makes it thorough mixing; Add the white carbon black 5g of gas phase, fully stir; Pour alcohol 5g at last into, can be divided in the flexible pipe after stirring.
Embodiment four
Get acetone 65g, paracril 13g, isoprene-isobutylene rubber 12g stir both and make it thorough mixing; Add the white carbon black 3g of gas phase, fully stir; Pour alcohol 7g at last into, can be divided in the flexible pipe after stirring.
Embodiment five
Get acetone 72g, butyronitrile 12g, styrene-butadiene rubber(SBR) 6g stir and make it thorough mixing; Add the white carbon black 7g of gas phase, fully stir; Pour alcohol 3g at last into, can be divided in the flexible pipe after stirring.
Embodiment six
Get acetone 72g, paracril 10g, styrene-butadiene rubber(SBR) 5g, isoprene-isobutylene rubber 5g stir and make it thorough mixing; Add the white carbon black 5g of gas phase, fully stir; Pour alcohol 3g at last into, can be divided in the flexible pipe after stirring.
The present invention compared with prior art has the following advantages:
1, this product is colloid, can not run off when dripping on the a-cyanacrylate, can Dissolve fully the a-cyanacrylate;
2, cleaning rubber can surround softening a-cyanacrylate, as long as back and forth light with finger Gently rub with the hands, cleaning rubber just can come off with the a-cyanacrylate.
Claims (9)
1. cleaning rubber is characterized in that: by weight percentage, contain following composition:
The white carbon black 2～10 of acetone 65～85 alcohol 0～10 gas phase
Synthetic rubber 5～25.
2. a kind of cleaning rubber as claimed in claim 1 is characterized in that: the blending ratio of above-mentioned composition:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Synthetic rubber 8～20.
3. a kind of cleaning rubber as claimed in claim 1 or 2 is characterized in that: above-mentioned synthetic rubber is at least a in paracril, isoprene-isobutylene rubber, the styrene-butadiene rubber(SBR).
4. a kind of cleaning rubber as claimed in claim 1 or 2 is characterized in that: the blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Paracril 8～20.
5. a kind of cleaning rubber as claimed in claim 1 or 2 is characterized in that: the blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Styrene-butadiene rubber(SBR) 8～20.
6. a kind of cleaning rubber as claimed in claim 1 or 2 is characterized in that: the blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Isoprene-isobutylene rubber 8～20.
7. a kind of cleaning rubber as claimed in claim 1 or 2 is characterized in that: the blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Paracril and isoprene-isobutylene rubber 8～20.
8. a kind of cleaning rubber as claimed in claim 1 or 2 is characterized in that: the blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Paracril and styrene-butadiene rubber(SBR) 8～20.
9. a kind of cleaning rubber as claimed in claim 1 or 2 is characterized in that: the blending ratio of above-mentioned composition is:
The white carbon black 3～5 of acetone 70～80 alcohol 5～8 gas phases
Paracril and isoprene-isobutylene rubber and styrene-butadiene rubber(SBR) 8～20.