CN100389274C - Preparation process for disk type brake lining and dedicated apparatus therefor - Google Patents
Preparation process for disk type brake lining and dedicated apparatus therefor Download PDFInfo
- Publication number
- CN100389274C CN100389274C CNB2006100125642A CN200610012564A CN100389274C CN 100389274 C CN100389274 C CN 100389274C CN B2006100125642 A CNB2006100125642 A CN B2006100125642A CN 200610012564 A CN200610012564 A CN 200610012564A CN 100389274 C CN100389274 C CN 100389274C
- Authority
- CN
- China
- Prior art keywords
- brake block
- die cavity
- hot
- sulfuration
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention belongs to the technical field of preparing techniques of brake blocks, which particularly to discloses a preparation process and a special device of a disk-type brake block. The process for preparing the disk-type brake block has the processing steps of steel back preparation, liner material preparation, cold briquetting, hot pressing, solidification and heat treatment. Because the cold briquetting of the brake block is added in the process, the present invention has the advantages that thermal stress distribution of the inner structure of the prepared brake block is uniform, the defects of expansion, crazing, etc., in the process of using are overcome, and the brake block prepared by the process also has the characteristics of low cost and high productive efficiency.
Description
Technical field
The invention belongs to the preparing technical field of brake block, disclose a kind of preparation process of disc brake pad specifically.
Background technique
At present, the preparation of disc brake pad has two kinds of technologies.A kind of technology---as the disclosed technology of patent of invention that the patent No. is 96115295.8, notification number is CN1165255, name is called a kind of brake block.The preparation section of its brake block is: the tailoring of steel backing, the kneading of brake block liner, raw material comprise the pretreatment of drying, pulverizing, in the mould of preheating coating release agent, dose behind the steel backing that scribbles tackiness agent and the pretreated liner material operations such as the heating pressurization is once hot-forming.Utilize this technology to prepare disc brake pad and then have following shortcoming: the mold filling operation in this technology is the batch mixing of the liner of powdery directly to be inserted to heat with steel backing in the mould be bonded together, because the heat transfer inequality of the liner batch mixing of powdery, temperature gradient is big, can make the powdery batch mixing can not get the even variation of uniform chemical reaction and physical form, cause the brake block internal structure thermal stress distribution inequality prepared, the brake block of preparing in use easily produces and expands and unconquerable defectives such as be full of cracks; Although this technology makes the brake block once-through since the mould of preparation brake block too thick and heavy, make that hot pressing time is long, power consumption is high, therefore also exist the low defective of manufacturing efficiency (manufacturing mechanism can only produce about 20/hour).The preparation process's of another kind of brake block manufacturing process is: tailor the batching of steel backing, brake block liner and batch mixing, the brake block liner is hot-forming, with tackiness agent the two is bonded together then.Utilize this technology to prepare disc brake pad, in use then exist steel backing and the caducous defective of brake block liner.
Summary of the invention
Purpose of the present invention just provides that a kind of brake block internal structure thermal stress distribution is even, the preparation process of the simple disc brake pad of technology.
Another object of the present invention just provides the special device of the high preparation disc brake pad of a kind of manufacturing efficiency.
The preparation process who realizes a kind of disc brake pad proposed by the invention includes following operation:
The preparation of first step steel backing
Tailor steel backing, the surface is handled and coating adhesive;
The preparation of the second step liner material
To the material that liner is required pulverize, pretreatment such as drying, mixing;
The 3rd step cold moudling
In the die cavity that the liner material for preparing and steel backing are inserted mould, compression moulding;
The 4th step hot-press solidifying
The brake block of cold moudling is inserted hot-press solidifying in the vulcanization die;
The 5th step heat treatment
The brake block of sulfidization molding is heat-treated.
The special device that uses in the technology of above-mentioned preparation disc brake pad comprises: the sulfuration mechanism of cold moudling mechanism and hot-press solidifying.
Wherein, described cold moudling mechanism comprises pressure mechanism and platform, and described pressure mechanism is provided with at least one patrix, is fixed with the displaceable counterdie corresponding with patrix on the described platform, and described platform is provided with positioning means and type hole; The structure of the sulfuration mechanism of described hot-press solidifying comprises pressure flat and working platform, the two is provided with several layers and is connected with the heating plate that thermal source has heating function, and the Die and mould plate that has some die cavitys can insert and finish the sulfidization molding that places the die cavity brake block between described heating plate; Be connected with drawing mechanism between the heating plate in the sulfuration mechanism of described hot-press solidifying.
The preparation process of disc brake pad provided by the present invention and special device, compared with prior art have the following advantages: one, because before brake block is hot-forming, carry out cold moudling after having increased dusty material mold filling with the brake block liner, and make the brake block liner under physical condition, be compressed the operation that is bonded on the steel backing, therefore internal heat transfer is even when making the brake block of moulding be heating and curing sulfuration, temperature gradient is less, the brake block internal structure thermal stress distribution of preparing is even, has avoided in use easily producing the defective of phenomenons such as expansion and be full of cracks; They are two years old, when being heating and curing vulcanizing treatment again after brake block colded pressing earlier, the thickness of hot pressing die is 1/3rd of one-shot forming technique mold thickness, therefore transmission of heat is accelerated when the brake block liner of moulding being heating and curing, the time of whole hot-press solidifying is 1/2nd of one-shot forming technique only, and power consumption reduces greatly; Its three, the equipment that this technology provides can be so that be heating and curing the operation continization, the hydraulic press suitable with one-shot forming technique once can be heating and curing to the brake block liner of 60 (about 120/hour) at least, improved manufacturing efficiency greatly.
Description of drawings
Fig. 1: be the structural representation of cold moudling mechanism;
Fig. 2: be the structural representation of the mould that is used for cold moudling mechanism;
Fig. 3: be the structural representation of hot-press solidifying sulfuration mechanism;
Fig. 4: for being used for the structural representation of hot-press solidifying sulfuration mechanism mould;
Fig. 5: be the structural representation of the brake block base of cold moudling.
Embodiment
Be described in further detail below in conjunction with the preparation process and the special device of accompanying drawing disc brake pad provided by the invention:
Be the structural representation of the former block that uses in the cold moudling operation among the preparation process of disc brake pad and the structural representation of mould as depicted in figs. 1 and 2.Be that cold moudling mechanism comprises the pressure mechanism 1 that is provided with two (can be one or more) patrixes 2 and is provided with positioning means and is used for fixing the platform 4 of the displaceable counterdie 3 corresponding with patrix 2, this platform 4 is provided with the type hole 5 corresponding with the die cavity 6 of counterdie.
Be the structural representation of the sulfuration mechanism that uses in the hot-press solidifying operation among the preparation process of disc brake pad and the structural representation of sulfuration mechanism mould as shown in Figure 3 and Figure 4.The structure of the sulfuration mechanism of pressing solidly of instant heating comprises pressure flat 7 and working platform 8, the two is provided with the heating plate 10 that 6 layers (its number of plies is set as required) have thermal source 9, the Die and mould plate 12 that has ten (can be provided with a plurality of as required) second die cavitys 11 can insert 10 of heating plates, finishes the sulfidization molding that places die cavity brake block base 13.
The operation of utilizing above-mentioned special device to prepare disc brake pad is:
The preparation of first step steel backing
Be tailoring of steel backing: utilize the brake block steel back of punch press punching out moulding, by cleaning, polishing its surface is handled, and coat layer of adhesive;
The preparation of the second step liner material
Select the material of required preparation brake block liner as requested, carry out pretreatment process such as drying, pulverizing, mixing and be prepared into required Powdered;
The 3rd step cold moudling
With steel backing 14 and the good pulverous liner material 17 of weighing successively (steel backing 14 down) be filled in the die cavity 6 of counterdie 3 as depicted in figs. 1 and 2, breakout pressure mechanism 1 is pressed in this die cavity 6 patrix 2, compression moulding is brake block base as shown in Figure 5, make steel backing 14 and liner base 15 be combined as a whole, meanwhile finish the filler of opposite side die cavity; Start patrix then, make it to lift, pulling counterdie 3 makes the die cavity 6 of moulding aim at the brake block base that is arranged on the platform 4 to portal and 5 make it depanning that breakout pressure mechanism 1 is pressed in this die cavity patrix 2 simultaneously.So circulation has improved the manufacturing efficiency of cold moudling.
The 4th step hot-press solidifying
The brake block base arrangement of cold moudling is inserted in second die cavity 11 of sulfuration plate 12 as shown in Figure 4, on it propelling heating plate 10 as shown in Figure 3, will vulcanize plate 12 and push away full heating plate 10 back breakout pressure flat boards 7 and compress and heat and make 13 moulding of brake block base and solidify.Restart pressure flat board 7 makes on the drawing mechanism 16 of 10 connections of heating plate and lifts, and extracts sulfuration plate 12 out, and the brake block of moulding is taken out.
The 5th step heat treatment
The brake block of sulfidization molding is heat-treated.
Claims (1)
1. technology for preparing disc brake pad is characterized in that: include following operation:
The preparation of first step steel backing
Tailor steel backing, the surface is handled and coating adhesive;
The preparation of the second step liner material
To the material that liner is required pulverize, pretreatment such as drying, mixing;
The 3rd step cold moudling
Adopt cold moudling mechanism, wherein cold moudling mechanism comprises pressure mechanism and platform, described pressure mechanism is provided with at least one patrix, be fixed with the displaceable counterdie corresponding on the described platform with patrix, described counterdie has die cavity, and described platform is provided with positioning means and type hole, and steel backing and the liner material for preparing are filled in the die cavity of described counterdie successively, breakout pressure mechanism is pressed in the die cavity patrix, and compression moulding is the brake block base;
The 4th step hot-press solidifying
Adopt the sulfuration mechanism of hot-press solidifying, wherein the sulfuration mechanism of hot-press solidifying comprises pressure flat and working platform, the two is provided with several layers and is connected with the heating plate that thermal source has heating function, be connected with drawing mechanism between heating plate, the sulfuration plate that has some die cavitys can insert and finish the sulfidization molding that places the die cavity brake block between described heating plate, the brake block base arrangement of cold moudling is inserted in the die cavity of described sulfuration plate, and hot-press solidifying is the brake block of moulding;
The 5th step heat treatment
The brake block of sulfidization molding is heat-treated.