CN100387646C - Fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked and its preparation - Google Patents
Fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked and its preparation Download PDFInfo
- Publication number
- CN100387646C CN100387646C CNB2006100356990A CN200610035699A CN100387646C CN 100387646 C CN100387646 C CN 100387646C CN B2006100356990 A CNB2006100356990 A CN B2006100356990A CN 200610035699 A CN200610035699 A CN 200610035699A CN 100387646 C CN100387646 C CN 100387646C
- Authority
- CN
- China
- Prior art keywords
- parts
- ethylene
- fire
- shrinked
- double pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A radiant cross-linking fire-retardant and heat-shrinkage indicating double pipe and its production are disclosed. The process is carried out by taking ethane-vinyl acetate multi-polymer, ethane-ethyl acrylate multi-polymer, ethylene-propylene rubber, fire-retardant decabromodiphenyl ethane, antimonous oxide, surface-activated superfine-magnesium hydrate and auxiliary as raw material, mill granulating, extrude forming, radiant cross-linking, expand sizing, and finish treating. It has better weather-resisting, high and low-temperature-resisting, anti-corrosive and antibacterial performances and long-period storage. It can be used for military industry, aviation and aerospace, civil high-terminal electronic equipment and cable.
Description
Technical field
The invention belongs to a kind of material, relate to a kind of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked and material thereof and preparation method.
Background technology
In the electrical equipment assembling process, in order accurately to discern and to distinguish various cables and components and parts, be convenient to production, debugging, keep in repair and detect, often to mark to the electric wire and the components and parts of assembling.Early stage material as the electric wire Sign Board is a thin aluminum sheet, and it is bad that aluminium sheet is cut into T shape hair, by manual carving machine and the ready-made in advance type matrix symbol of carving characters on blank.This method efficient is low, be not suitable for producing in batches, and the tack of label is poor, easily gets loose, and can't use on airborne and Shipborne Electronic Equipment.Not collapsible plastic casing Sign Board had appearred afterwards, written character by hand on plastic casing.The character of this Sign Board is not attractive in appearance also unintelligible, and label can only use at normal temperatures, and easily aging, and work-ing life is short.Along with science and technology and rapid economy development, in order to satisfy the needs that use under special occasions and the severe environment, especially military industry requires writing clear attractive in appearance to the Sign Board of electrical equipment assembling usefulness, the permanent maintenance, and heat-resisting, ageing-resistant, corrosion-resistant, anti-mould, strong adhesion, easy to use, have good flame retardant property, insulating property and mechanical property excellent performance simultaneously.Various flame-retardant heat shrinkable sleeves have been developed both at home and abroad in succession from the seventies in last century.Thermal contraction casing tube is a kind of radially permanent plastic casing-pipe that shrinks that can produce after being heated to certain temperature; belong to novel shapememory polymer functional materials; its production process generally comprises mixing granulator, extrusion moulding, cross-linking radiation and vacuum expansion etc.; have good mechanical property, insulating property, flame retardant properties and heat-resisting, corrosion-resistant, salt spray resistance and characteristics such as easy to use; be widely used in the connection protection of cable; the de-stressing of terminal processing or junction, and the fields such as coating of solder joint protection and electronic devices and components.At present, these thermal contraction casing tubes all adopt the printing ink lettering, exist the not anti-wiping of writing, deficiency such as can not forever keep.
Summary of the invention
The objective of the invention is to: propose a kind of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
The objective of the invention is to: propose a kind of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked preparation methods.
Another object of the present invention is to: the preparation method who proposes a kind of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked.
In the present invention, adopt the printing ink lettering, exist the not anti-wiping of writing, the deficiency that can not forever keep etc. for the thermal contraction casing tube that overcomes prior art can only adapt to; Propose a kind of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked product and material prescription and manufacture method that thermal transfer printer is printed that be adapted to, its technical scheme is as follows:
The material of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked of the present invention (or claiming masterbatch) is made up of following material: (by weight)
25～45 parts of ethylene-vinyl acetate copolymers (EVA),
1～15 part of ethylene-acrylate copolymer,
5～15 parts in ethylene-propylene rubber(EPR) (EPDM),
0～10 part of chlorosulfonated polyethylene rubber
10～20 parts of TDE,
5～12 parts of antimonous oxides,
10～20 parts of the super fine magnesium hydroxides of surface activation process,
Composite antioxidant 0.5～1.5,
0.5～1.5 part of lubricant,
Sensitizing agent 1～3,
2～8 parts of colour batches.
The optimization of material of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked of the present invention consists of: (by weight)
25～45 parts of ethylene-vinyl acetate copolymers (EVA),
5～15 parts of ethylene-acrylate copolymers,
5～9 parts in ethylene-propylene rubber(EPR) (EPDM),
3～8 parts of chlorosulfonated polyethylene rubbers
10～20 parts of TDE,
5～12 parts of antimonous oxides,
10～20 parts of the super fine magnesium hydroxides of surface activation process,
Composite antioxidant 0.5～1.5,
0.5～1.5 part of lubricant,
Sensitizing agent 1～3,
2～8 parts of colour batches.
Described ethylene-vinyl acetate copolymer (EVA), wherein the content of vinyl-acetic ester (VA content) is 14～20% (weight), melting index is in 0.5～6.0g/10min scope.
Described ethylene-acrylate copolymer, comprise ethylene-ethyl acrylate copolymer (EEA), ethylene-methyl acrylate copolymer (EMA) or ethylene-butyl acrylate copolymer (EBA), wherein the content of acrylate (EA or MA or BA content) is 5～25% (weight), and melting index is in 1.0～8.0g/10min scope.
Described ethylene-acrylate copolymer, but ethylene-ethyl acrylate copolymer (EEA), ethylene-methyl acrylate copolymer (EMA) or ethylene-butyl acrylate copolymer (EBA) one of them, also can adopt two or more mixing to use.
Described ethylene-propylene rubber(EPR) (EPDM), therein ethylene content are 50～65% (weight), and mooney viscosity (ML (1+4), 125 ℃) is in 38～52MU scope.
Described chlorosulfonated polyethylene rubber, wherein cl content is 30～40% (weight), mooney viscosity (ML (1+4), 100 ℃) is in 40～56MU scope.
Described TDE is white powder, does not have mechanical impurity, and whiteness is not less than 85, and total bromine content is not less than 82%, and median size is less than 3um.
Described antimonous oxide is white powder, Sb
2O
3Content is not less than 99.5%, and whiteness is not less than 93, and median size is less than 1.8um.
The super fine magnesium hydroxide of described surface activation process is white powder, and median size is 0.5～2.0um, and whiteness is not less than 90, and the surface is that silane treatment or polymer modification are handled.
Described composite antioxidant is the composite antioxidant that the efficient auxiliary antioxidant allotment of hindered phenol primary antioxidant and thioether forms, and both weight ratios are 1: 1～4.The hindered phenol primary antioxidant comprises: four [β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester (antioxidant 1010) and β-(4-hydroxyl-3,5-di-tert-butyl-phenyl) positive octadecyl esters of propionic acid (antioxidant 1076).The efficient auxiliary antioxidant of thioether comprises: Tyox B (DLTP) and thio-2 acid two (18) ester (DSTP).
Described lubricant is a Zinic stearas etc.
Described sensitizing agent comprises Viscoat 295 (TMPTA), tetramethylol methane tetraacrylate (PETEA), triallyl isocyanate (TAIC) etc.
Fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked preparation methods of the present invention: (by weight) is with 25～45 parts of ethylene-vinyl acetate copolymers (EVA), 1～15 part of ethylene-acrylate copolymer, 5～15 parts in ethylene-propylene rubber(EPR) (EPDM), 0～10 part of chlorosulfonated polyethylene rubber, 10～20 parts of TDE, 5～12 parts of antimonous oxides, 10～20 parts of the super fine magnesium hydroxides of surface activation process, 0.5～1.5 part of composite antioxidant, 0.5～1.5 part of lubricant, 1～3 part of sensitizing agent, the part by weight that colour batch is 2～8 parts adds in the homogenizer successively, high-speed stirring 3～7 minutes is no more than 80 ℃ with temperature of charge and is advisable.With mixed material with reciprocating type single screw mixing forcing machine extrude in 100～160 ℃ of intervals, wire drawing, water-cooled, air-cooled, pelletizing, promptly obtain the granulated product (being the granular masterbatch that tubulation is used) of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
The preparation method of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked of the present invention may further comprise the steps:
A, (by weight) are with 25～45 parts of ethylene-vinyl acetate copolymers (EVA), 1～15 part of ethylene-acrylate copolymer, 5～15 parts in ethylene-propylene rubber(EPR) (EPDM), 0～10 part of chlorosulfonated polyethylene rubber, 10～20 parts of TDE, 5～12 parts of antimonous oxides, 10～20 parts of the super fine magnesium hydroxides of surface activation process, 0.5～1.5 part of composite antioxidant, 0.5～1.5 part of lubricant, 1～3 part of sensitizing agent, the part by weight that colour batch is 2～8 parts adds in the homogenizer successively, high-speed stirring 3～7 minutes is no more than 80 ℃ with temperature of charge and is advisable.With mixed material with reciprocating type single screw mixing forcing machine extrude in 100～160 ℃ of intervals, wire drawing, water-cooled, air-cooled, pelletizing, promptly obtain the bulk goods of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
B, with the bulk goods of above-mentioned fire-retardant thermal contraction sign shell material, under 100～160 ℃ of temperature, be extruded into pipe with the single screw extrusion machine that mouthful mould and core are installed;
C, with above-mentioned tubular material rumbatron cross-linking radiation, irradiation dose is 4～8Mrad.Tubing behind the cross-linking radiation obtains the cross-linking radiation thermal contraction casing tube through 2～3 times of postcooling of vacuum expansion device expansion, typing in 100～180 ℃ of intervals;
D, at last above-mentioned thermal contraction casing tube is handled through plastic cement planer leveling, promptly obtained to be adapted to the fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked product that thermal transfer printer is printed.
The user can print required mark with thermal transfer printer as required, obtains the fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked of tape label.
The present invention compared with prior art has following advantage and effect:
1. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked of the present invention has overcome the prior art thermal contraction casing tube and can only adopt the printing ink lettering, the not anti-wiping of its writing, and weathering resistance is poor, the deficiency that can not forever keep.Realized to utilize the thermal transfer printer that connects computer at its printout surface character; Be printed on the character mark on the sleeve pipe, have good anti-wiping and high-and low-temperature resistance, corrosion-resistant, salt spray resistance, the weathering resistance of antifungal etc. can forever keep.
2. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked of the present invention, weather-proof integrated performance index such as its thermal contraction, physical strength and physicals, fire-retardant, salt spray resistance, corrosion-resistant, antifungal reaches my national military standard GJB150.11-86 requirement; Print performance reaches U.S. army mark MIL-STD-202 requirement; Environmentally hazardous substance meets the RoHS of European Union environmental protection command request through test.Can satisfy the high standard requirement of cable and components and parts in industries such as military project, Aeronautics and Astronautics and civilian high-end electronics, the electrical equipment.
3. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked of the present invention, the preparation method is simple and easy, and raw material is easy to get, and is cheap, is suitable for suitability for industrialized production.
Concrete embodiment:
Below in conjunction with embodiment technical scheme of the present invention is described in further detail, but embodiments of the present invention are not limited thereto.
Embodiment one
Get 30 parts of ethylene-vinyl acetate copolymers (EVA), (VA content is 14% (weight), and melting index is 3.6g/10min); 10 parts of ethylene-ethyl acrylate copolymers (EEA) (EA content is 19 (weight) %, and melting index is 3.2g/10min); 12 parts in ethylene-propylene rubber(EPR) (EPDM), (ethylene content is 53% (weight), and mooney viscosity (ML (1+4), 125 ℃) is 42MU); 18 parts of TDE; 9 parts of antimonous oxides; 16 parts of the super fine magnesium hydroxides of surface activation process; 1 part of composite antioxidant (wherein: 0.5 part of pentaerythritol ester (antioxidant 1010), 0.5 part of Tyox B (DLTP)); 1 part on lubricant stearic acid zinc; 1.5 parts of sensitizing agent Viscoat 295s (TMPTA); Female 6 parts of white; Add successively in the homogenizer, high-speed stirring 8 minutes, temperature of charge is no more than 80 ℃ and is advisable.With mixed material with reciprocating type single screw mixing forcing machine under 100～160 ℃, extrude, wire drawing, water-cooled, air-cooled, pelletizing.Promptly obtain the granulated product of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
Embodiment two
Get 40 parts of ethylene-vinyl acetate copolymers (EVA), (VA content is 14% (weight), and melting index is 3.6g/10min); 5 parts of ethylene-ethyl acrylate copolymers (EEA), (EA content is 19% (weight), and melting index is 3.2g/10min); 9 parts in ethylene-propylene rubber(EPR) (EPDM), (ethylene content is 53% (weight), and mooney viscosity (ML (1+4), 125 ℃) is 42MU); 8 parts of chlorosulfonated polyethylene rubbers, wherein cl content is 30～40% (weight), mooney viscosity (ML (1+4), 100 ℃) is in 40～56MU scope; 16 parts of TDE; 8 parts of antimonous oxides; 20 parts of the super fine magnesium hydroxides of surface activation process; Composite antioxidant (wherein: 0.5 part of pentaerythritol ester (antioxidant 1010); 1 part of Tyox B (DLTP)) 1.5 part; 1 part on lubricant stearic acid zinc; 1.5 parts of sensitizing agent Viscoat 295s (TMPTA); Yellow female 6 parts; Add successively in the homogenizer, high-speed stirring 8 minutes is no more than 80 ℃ with temperature of charge and is advisable.With mixed material with reciprocating type single screw mixing forcing machine under 100～160 ℃, extrude, wire drawing, water-cooled, air-cooled, pelletizing.Promptly obtain the granulated product of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
Embodiment three
Get 30 parts of ethylene-vinyl acetate copolymers (EVA), wherein VA content is 15% (weight), and melting index is 1.5g/10min); 10 parts of ethylene-acrylate copolymers, wherein: 5 parts of EEA, its acrylate EA content is 16% (weight), melting index is 6.0g/10min; 5 parts of EMA, its acrylate MA content is 20% (weight), melting index is in the 5.0g/10min scope; 12 parts in ethylene-propylene rubber(EPR) (EPDM), therein ethylene content are 53% (weight), and mooney viscosity (ML (1+4), 125 ℃) is 42MU); 3 parts of chlorosulfonated polyethylene rubbers, wherein cl content is 30～40% (weight), mooney viscosity (ML (1+4), 100 ℃) is in 40～56MU scope; 18 parts of TDE; 9 parts of antimonous oxides; 16 parts of the super fine magnesium hydroxides of surface activation process; 1.5 parts of composite antioxidants (wherein: 0.5 part of pentaerythritol ester (antioxidant 1010), 1 part of Tyox B (DLTP)); 1.5 parts of magnesium stearate lubricants; 2 parts of sensitizing agent tetramethylol methane tetraacrylates (PETEA); Female 6 parts of white; Add successively in the homogenizer, high-speed stirring 8 minutes is no more than 80 ℃ with temperature of charge and is advisable.With mixed material with reciprocating type single screw mixing forcing machine under 100～160 ℃, extrude, wire drawing, water-cooled, air-cooled, pelletizing.Promptly obtain the granulated product of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
Embodiment four
Get 30 parts of ethylene-vinyl acetate copolymers (EVA); (VA content is 14% (weight), and melting index is 3.6g/10min); 8 parts of ethylene-butyl acrylate copolymers (EBA), wherein acrylate BA content is 5～25% (weight), melting index is in 1.0～8.0g/10min scope; 12 parts in ethylene-propylene rubber(EPR) (EPDM), (ethylene content is 53% (weight), and mooney viscosity (ML (1+4), 125 ℃) is 42MU); 18 parts of TDE; 9 parts of antimonous oxides; 16 parts of the super fine magnesium hydroxides of surface activation process; 1 part of composite antioxidant (wherein: 0.5 part of pentaerythritol ester (antioxidant 1010), 0.5 part of Tyox B (DLTP)); 1 part on lubricant stearic acid zinc; 1.5 parts of sensitizing agent Viscoat 295s (TMPTA); Female 6 parts of white; Add successively in the homogenizer, high-speed stirring 8 minutes is no more than 80 ℃ with temperature of charge and is advisable.With mixed material with reciprocating type single screw mixing forcing machine under 100～160 ℃, extrude, wire drawing, water-cooled, air-cooled, pelletizing.Promptly obtain the granulated product of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
Embodiment five
Get 25 parts of ethylene-vinyl acetate copolymers (EVA) (VA content is 14% (weight), and melting index is 3.6g/10min); 1 part of ethylene-ethyl acrylate copolymer (EEA) (EA content is 19% (weight), and melting index is 3.2g/10min); 5 parts in ethylene-propylene rubber(EPR) (EPDM), (ethylene content is 53% (weight), and mooney viscosity (ML (1+4), 125 ℃) is 42MU); 10 parts of TDE; 5 parts of antimonous oxides; 10 parts of the super fine magnesium hydroxides of surface activation process; 0.5 part of composite antioxidant (wherein: 0.25 part of pentaerythritol ester (antioxidant 1010), 0.25 part of Tyox B (DLTP)); 0.5 part on lubricant stearic acid zinc; 1 part of sensitizing agent Viscoat 295 (TMPTA); Female 2 parts of white; Add successively in the homogenizer, high-speed stirring 8 minutes is no more than 80 ℃ with temperature of charge and is advisable.With mixed material with reciprocating type single screw mixing forcing machine extrude down at 100～160 ℃, wire drawing, water-cooled, air-cooled, pelletizing.Promptly obtain the granulated product of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
Embodiment six
Get 45 parts of ethylene-vinyl acetate copolymers (EVA) (VA content is 14% (weight), and melting index is 3.6g/10min); 15 parts of ethylene-ethyl acrylate copolymers (EEA); (EA content is 19% (weight), and melting index is 3.2g/10min); 15 parts in ethylene-propylene rubber(EPR) (EPDM) (ethylene content is 53% (weight), and mooney viscosity (ML (1+4), 125 ℃) is 42MU), 10 parts of chlorosulfonated polyethylene rubbers, wherein cl content is 30～40% (weight), and mooney viscosity (ML (1+4), 100 ℃) is in 40～56MU scope; 20 parts of TDE; 12 parts of antimonous oxides; 20 parts of the super fine magnesium hydroxides of surface activation process; Composite antioxidant (wherein: 1 part of pentaerythritol ester (antioxidant 1010); 0.5 part of Tyox B (DLTP)) 1.5 part; 1.5 parts on lubricant stearic acid zinc; 3 parts of sensitizing agent Viscoat 295s (TMPTA); Female 8 parts of white; Add successively in the homogenizer, high-speed stirring 8 minutes, temperature of charge is no more than 80 ℃ and is advisable.With mixed material with reciprocating type single screw mixing forcing machine under 100～160 ℃, extrude, wire drawing, water-cooled, air-cooled, pelletizing.Promptly obtain the granulated product of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
Embodiment seven
The preparation of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked: get above-mentioned 6 bulk goodses that embodiment makes respectively, under 100～160 ℃ of temperature, be extruded into pipe with the single screw extrusion machine that mouthful mould and core are installed respectively, then that this tubular material is crosslinked through electron accelerator irradiation, irradiation dose is 4～8Mrad; Tubing behind the cross-linking radiation is under 100～180 ℃, and after 2 or 3 times of vacuum expansion device expansions, cooling and shaping promptly obtains thermal contraction casing tube.Then with the thermal contraction casing tube of gained, after leveling handles under with certain temperature and speed, promptly obtain to be adapted to the fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked product that thermal transfer printer is printed through the plastic cement planer.
Product performance detect:
Get above-mentioned 6 bulk goodses that embodiment makes respectively, fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked sample with embodiment seven method productions (expanding 2 and 3 times of two kinds of specifications), respectively connect print color character such as red, yellow, white, blue, green, black on the thermal transfer printer of computer after, its each performance index are detected, and the result is as follows: contraction ratio was respectively 2: 1 and 3: 1; Use temperature scope-55～135 ℃; Tensile strength 〉=10.4Mpa, elongation at break 〉=300%; Aging (175 ℃, 168 hours) back elongation at break 〉=200%; Thermal shocking (225 ℃, 4 hours) flawless; Cold bend(ing) (55 ℃, 4 hours) flawless; High/low-temperature impact (55～135 ℃, circulation in 1 hour 10 times) passes through; Dielectric voltage withstand (2500V, 60 seconds) does not puncture; Volume specific resistance 〉=10
14Ω cm; Copper corrosion (175 ℃, 16 hours) does not have corrosion; Salt spray resistance meets my national military standard GJB150.11-86 requirement; Flame retardant resistance is put out in 1 minute certainly; Print performance reaches U.S. army mark MIL-STD-202 requirement; Environmentally hazardous substance meets the RoHS of European Union environmental protection command request through test.
Claims (10)
1. a fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material is characterized in that, form by following substances, by weight:
25～45 parts of ethylene-vinyl acetate copolymers,
1～15 part of ethylene-acrylate copolymer,
5～15 parts in ethylene-propylene rubber(EPR),
0～10 part of chlorosulfonated polyethylene rubber,
10～20 parts of TDE,
5～12 parts of antimonous oxides,
10～20 parts of the super fine magnesium hydroxides of surface activation process,
0.5～1.5 part of hindered phenol and thioether composite antioxidant,
0.5～1.5 part of lubricant,
1～3 part of sensitizing agent,
2～8 parts of colour batches.
2. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material according to claim 1, it is characterized in that: by weight, the optimization deal of component ethylene-acrylate copolymer is 5-15 part, the optimization deal of component ethylene-propylene rubber(EPR) is 5-9 part, and it is 3～8 parts that the component chlorosulfonated polyethylene rubber is optimized deal.
3. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material according to claim 1, it is characterized in that: described ethylene-acrylate copolymer, comprise ethylene-ethyl acrylate copolymer, ethylene-methyl acrylate copolymer, ethylene-butyl acrylate copolymer, wherein the acrylate weight percent content is 5～25%, and melting index is in 1.0～8.0g/10min scope.
4. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material according to claim 1, it is characterized in that: described ethylene-acrylate copolymer is ethylene-ethyl acrylate copolymer, ethylene-methyl acrylate copolymer, ethylene-butyl acrylate copolymer is one kind of or be no less than two kinds mixture.
5. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material according to claim 1 is characterized in that: described ethylene-propylene rubber(EPR), therein ethylene weight percent content are 50～65%, mooney viscosity, and 125 ℃, ML1+4 is in 38～52MU scope.
6. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material according to claim 1 is characterized in that: described chlorosulfonated polyethylene rubber, and wherein the chlorine weight percent content is 30～40%, mooney viscosity, 100 ℃, ML1+4 is in 40～56MU scope.
7. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material according to claim 1, it is characterized in that: described composite antioxidant is that hindered phenol and thioether allotment form, both weight ratios are 1: 1～4, hindered phenol comprises: four [β-(3, the 5-di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester and β-(4-hydroxyl-3,5-di-tert-butyl-phenyl) positive octadecyl ester of propionic acid; Thioether comprises: Tyox B, thio-2 acid two (18) ester.
8. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material according to claim 1 is characterized in that: described sensitizing agent is Viscoat 295 or tetramethylol methane tetraacrylate or triallyl isocyanate.
9. fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked preparation methods according to claim 1, it is characterized in that: by weight, with 25～45 parts of ethylene-vinyl acetate copolymers, 1～15 part of ethylene-acrylate copolymer, 5～15 parts in ethylene-propylene rubber(EPR), 0～10 part of chlorosulfonated polyethylene rubber, 10～20 parts of TDE, 5～12 parts of antimonous oxides, 10～20 parts of the super fine magnesium hydroxides of surface activation process, 0.5～1.5 part of hindered phenol and thioether composite antioxidant, 0.5～1.5 part of lubricant, 1～3 part of sensitizing agent, 2～8 parts of colour batches, add successively in the homogenizer, temperature of charge is no more than under 80 ℃ of conditions high-speed stirring to be mixed 3～7 minutes; Then with mixture with the screw mixing forcing machine under 100～160 ℃, extrude, wire drawing, water-cooled, air-cooled, pelletizing, promptly obtain the granulated product of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material.
10. the preparation method of a fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked is characterized in that, comprises the steps:
A, by weight, with 25～45 parts of ethylene-vinyl acetate copolymers, 1～15 part of ethylene-acrylate copolymer, 5～15 parts in ethylene-propylene rubber(EPR), 0～10 part of chlorosulfonated polyethylene rubber, 10～20 parts of TDE, 5～12 parts of antimonous oxides, 10～20 parts of the super fine magnesium hydroxides of surface activation process, 0.5～1.5 part of hindered phenol and thioether composite antioxidant, 0.5～1.5 part of lubricant, 1～3 part of sensitizing agent, 2～8 parts of colour batches add in the homogenizer successively, and temperature of charge is no more than 80 ℃ of following high-speed stirring to be mixed 3～7 minutes; Then with mixture with the screw mixing forcing machine under 100～160 ℃, extrude, wire drawing, water-cooled, air-cooled, pelletizing, promptly obtain the bulk goods of fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked material;
B, with the bulk goods of above-mentioned fire-retardant thermal contraction sign shell material, under 100～160 ℃ of temperature, be extruded into pipe with the screw extrusion press that mouthful mould and core are installed;
C, with tubular material rumbatron cross-linking radiation, irradiation dose is 4～8Mrad, the tubing behind the cross-linking radiation carries out 2～3 times of postcooling of vacuum expansion device expansion, typing obtains the irradiation cross-linking flame-retardant thermal contraction casing tube under 100～180 ℃;
D, at last with above-mentioned thermal contraction casing tube, flatten processing with planer after, promptly obtain the fire-retarding thermal-shrinked indicated double pipe of radiant cross-linked product.