CN100365138C - Method for mfg. composite carbon containing pellets and device thereof - Google Patents
Method for mfg. composite carbon containing pellets and device thereof Download PDFInfo
- Publication number
- CN100365138C CN100365138C CNB2005101176454A CN200510117645A CN100365138C CN 100365138 C CN100365138 C CN 100365138C CN B2005101176454 A CNB2005101176454 A CN B2005101176454A CN 200510117645 A CN200510117645 A CN 200510117645A CN 100365138 C CN100365138 C CN 100365138C
- Authority
- CN
- China
- Prior art keywords
- planet
- links
- travelling belt
- roller
- feed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention belongs to the technical field of metallurgy of iron and steel, in particular to a method for manufacturing carbon containing pellets for steel smelting. The method for manufacturing carbon containing pellets for steel smelting, which is provided by the present invention, comprises a material preparing process, a material mixing process, a pellet pressing process, a pellet billet film coating process and a cooling process; a manufacturing device of the present invention is composed of a storage hopper, a weighing material preparing device, a three-roller planet material mixer, a high-pressure pellet pressing machine, a laminating machine, a cooling device and a metering and packing machine set. When a composite carbon containing pellet which is manufactured by the present invention is adopted, not only appropriate carbon contents can be selected, but also a layer of passivation protecting film is coated on the surface of the pellet; thus, water can not be absorbed by the pellet, the moisture resistance is good, and good use performance can be kept within a long time; in addition, the density of the carbon containing pellet is high, which can reach more than 3.0 g/cm<3>, and thus, the bearing strength is large; one pellet body can bear the pressure of more than 5MPa. The carbon containing pellet is especially suitable for being used as a metallurgical auxiliary material for a carburetant in the process of smelting steel or casting steel in an electric furnace.
Description
Technical field
The present invention is in the ferrous metallurgy field, relates generally to the manufacture method and the device thereof of the carbonaceous pelletizing that smelting iron and steel uses.
Background technology
The raw material types of ferrous metallurgy industry is various; wherein main raw material has ore, coke, powdered iron ore pelletizing, steel scrap etc.; auxiliary raw material has refractory materials, lime, various flux and covering slag etc.; wherein the powdered iron ore pelletizing also is a kind of raw material of using always, as blast furnace with agglomerates of sintered pellets, external refining with synthetic pelletizing, electric furnace with carbonaceous pelletizing etc.These pelletizings use two or more Powdered or granular metallurgy starting material, directly or again add binding agent, via different mechanism synthetic.These pelletizings require to have certain shape and size, and certain intensity and density are arranged, and are suitable for transportation, loading and unloading etc.Because these pelletizing consumptions are big, its manufacturing installation will have certain scale and productivity.At present, the manufacture method of this class pelletizing mainly contains two kinds: first kind is that ball or granulation are made in disk (inclination) rotation, this machinery is made ball normally powder-material water or other liquid, aqueous binding agent of doing, as the blast furnace ironmaking pelletizing, gypsum for cement is made additive etc., must carry out drying after the pelletizing moulding, and then uses, the main weak point of this manufacture method and device thereof is that the compressive strength of pelletizing is low, is unfavorable for preserving, transports and loading and unloading; Second kind is to utilize steel die, model carries out punching press or extruding or the extruding of rotation pair roller and makes ball or granulation, refractory materials fragment of brick or agglomerate that the monomer punching press of discontinuity or extruding are applicable to large-size, its shortcoming is that productivity is low, the production cost height, and but the rotation pair roller pushes continuous production, be applicable to various special pelletizings, its shortcoming is that institute's pelletizing water-absorbent of making is strong, pelletizing is not fine and close, compressive strength is low, and above-mentioned manufacture method has manufacturing installation miscellaneous, as monomeric continuous extrusion apparatus, by then production line for forming by different system, as comprise feeding system, mixing system, roll-in and weighing, packing etc.In sum, the manufacture method of above-mentioned pelletizing and the common drawback of device thereof are that the pelletizing surface is unprocessed, and water-absorbent is strong, and deliquescence is not fine and close easily, so compressive strength is low, are not suitable for the carbonaceous pelletizing of making steel-making usefulness especially.
Summary of the invention
The object of the present invention is to provide a kind of dense materials, compressive strength height, be applicable to the manufacture method and the device thereof of the composite carbon containing pellet that Electric furnace steel making or cast steel carburetting are used.
The manufacture method of composite carbon containing pellet of the present invention, its processing step comprise batching, batch mixing, pressure ball, ball base overlay film and cooling.Existing division is as follows:
(1) batching
Chemical Composition according to composite carbon containing pellet is prepared burden.The Chemical Composition of composite carbon containing pellet comprises carbonaceous material, metal oxide, rare earth oxide, binding agent, toughener, swelling agent and steel processing smear metal.Adopt the negative pressure suction type material loading during batching.
(2) batch mixing
Batch mixing rolls in the mixer at three-roller planetary and carries out.Roll in the mixer by travelling belt input three-roller planetary being equipped with good mixture, and start and roll stirring system, mixture is rolled mixing, wherein binding agent and toughener add in mixing process, roll to be stirred to mix.Rolled mixing time 0.3～1.0 hour.Adopt pressure delivering liquid binding agent.
(3) pressure ball
Pressure ball carries out on the high pressure ball press.Through chute, the opening for feed by the high pressure ball press enters in the forced feed case, and by the revolver gress in the case, the material that enters in the forced feed case has been carried out precompressed with the material that mixes, and the pressure of precompressed is 2 * 10
4MPa, more closely knit material after precompressed, suppress the chamber by revolver gress force feed to the pair roller matched moulds under being arranged in, in the pair roller matched moulds rotation process of this compacting chamber, by motor drive roll is exerted pressure, material is suppressed the balling-up base, after the mould system of closing along with the rotation of pressure roller, mould ball chamber in two pressure rollers begins to separate gradually, removes the snap-in force to the ball base, because the deadweight and the equilibrium of forces effect of ball base, and the retarded elasticity effect of ball base, the ball base is fallen into automatic demoulding in the discharge port of pair roller matched moulds compacting chamber, finishes the pressing process of ball base.The total pressure that drive roll is applied is 1～2 * 10
5MPa, linear pressure are 4～8 * 10
3Mpa/cm, the mean density of ball base is 3.0g/cm
3
(4) ball base overlay film
Ball base overlay film carries out in laminating machine.Suppress the discharge port of chamber from the pair roller matched moulds by the ball base that the high pressure ball press is pressed into, enter in the coating bath of coating equipment through travelling belt and laminating machine opening for feed, placed liquid passivator in the coating bath in advance, and by being arranged on the electric heater unit under the coating bath, liquid passivator is heated in advance in 100～200 ℃ the temperature range, ball base in coating bath parked 1～2 minute, then each even plating last layer thickness in ball base surface is the passive film of 0.1～1.0mm, make ball base and air isolated, the ball base behind the overlay film then becomes composite carbon containing pellet.Pelletizing behind the overlay film is by stretching into the discharge port that travelling belt in the coating bath is input to laminating machine.
Aforesaid liquid passivator is any or any two above sum in tar, paraffin wax, vegetables oil or the mineral oil.
(5) cooling
Cooling is carried out on refrigerating unit.Pelletizing behind the overlay film is input on the refrigerating unit by the discharge port of travelling belt from laminating machine, carries out air-cooled or naturally cooling.Through cooled pelletizing, promptly become composite carbon containing pellet of the present invention, send into packing in the metering packaging machine, seal up for safekeeping by travelling belt at last.
The manufacturing installation of composite carbon containing pellet of the present invention rolls mixer, high pressure ball press, laminating machine, refrigerating unit, metering packaging machine, one-level sack cleaner and secondary sack cleaner by feed bin, weighing and burden device, three-roller planetary and forms; The weighing and burden device is right after under the feed bin, the weighing and burden device rolls the mixer opening for feed by travelling belt and three-roller planetary and links to each other, the discharge port that three-roller planetary rolls mixer links to each other with high pressure ball press opening for feed by travelling belt, pair roller matched moulds compacting chamber discharge port in the high pressure ball press links to each other with the laminating machine opening for feed by travelling belt, the discharge port of laminating machine links to each other with refrigerating unit by travelling belt, refrigerating unit links to each other with metering packaging machine by travelling belt, and metering packaging machine links to each other with stockyard by travelling belt; Flow through process and feed bin, weighing and burden device, three-roller planetary of whole logistics rolls on mixer, high pressure ball press, laminating machine and the refrigerating unit and is equipped with shield cap, and link to each other with the secondary sack cleaner with the one-level sack cleaner by pipeline.
Three-roller planetary rolls mixer and is made up of batch mixing chamber, planet shovel, planet roller, planet scraper, motor, reduction box, rolling disc, shack, union lever and top cover; Top cover is installed on the batch mixing chamber, motor is fixed on the top cover, reduction box links to each other with motor, rolling disc links to each other with reduction box, shack links to each other with rolling disc, union lever links to each other with shack, and planet shovel, planet roller link to each other with union lever respectively with the planet scraper, and motor drives the union lever rotation respectively by reduction box, rolling disc and shack; The batch mixing chamber is fixed on the support by the chassis.
Planet shovel, planet roller and planet scraper are vertically regulated height, and the gap between planet shovel and the chassis is 1～7mm, and the gap between planet roller and the chassis is 3～6mm, and the gap between planet scraper and the chassis is 1～7mm.
Planet shovel, planet roller and planet scraper all have 3 to 5.
The high pressure ball press is made up of motor, reduction box, spinning bar, spinning apparatus, forced feed case, pair roller matched moulds compacting chamber, pair roller, worm screw, motor and reduction box.
Forced feed case and pair roller matched moulds compacting chamber counterpart are joined, spinning apparatus is in the forced feed case, link to each other with reduction box and motor by the spinning bar on it, two pair rollers are in the pair roller matched moulds compacting chamber, its drive roll links to each other with motor with reduction box by worm screw, and the discharge port of high pressure ball press links to each other with the opening for feed of laminating machine by travelling belt.
Laminating machine is made up of coating bath, base, power wheel, travelling belt, electric heater unit, worm screw, motor and reduction box; Coating bath is installed on the base, motor links to each other with reduction box, reduction box links to each other with power wheel by worm screw, travelling belt is around in power wheel, fill liquid passivator in the coating bath, on the base under the passivator electric heater unit is installed, is used for heating liquid passivator, the discharge port of laminating machine links to each other with refrigerating unit by travelling belt.
Now elaborate by the manufacturing installation of accompanying drawing to composite carbon containing pellet of the present invention.
Description of drawings
Accompanying drawing 1 is the structural representation of composite carbon containing pellet manufacturing installation of the present invention.
Accompanying drawing 2 rolls the structural representation of mixer for three-roller planetary.
Accompanying drawing 3 is the structural representation of high pressure ball press.
Accompanying drawing 4 is the structural representation of laminating machine.
Embodiment
From accompanying drawing 1～4 as can be seen, the manufacturing installation of composite carbon containing pellet of the present invention rolls mixer 3, high pressure ball press 4, laminating machine 5, refrigerating unit 6, metering packaging machine 7, one-level sack cleaner 62 and secondary sack cleaner 63 by feed bin 1, weighing and burden device 2, three-roller planetary and forms.Weighing and burden device 2 is right after under the feed bin 1, weighing and burden device 2 links to each other by the opening for feed 16 that travelling belt 9 and three-roller planetary roll mixer 3, the discharge port 21 that three-roller planetary rolls mixer 3 links to each other with the opening for feed 42 of high pressure ball press 4 by travelling belt 10, the discharge port 38 of the pair roller matched moulds compacting chamber 36 in the high pressure ball press 4, link to each other with the opening for feed 51 of laminating machine 5 by travelling belt 11, the discharge port 54 of laminating machine 5 links to each other with refrigerating unit 6 by travelling belt 12, refrigerating unit 6 links to each other with metering packaging machine 7 by travelling belt 13, and metering packaging machine 7 links to each other with stockyard 8 by travelling belt 14; Flow through process and feed bin 1, weighing and burden device 2, three-roller planetary of whole logistics rolls on mixer 3, high pressure ball press 4, laminating machine 5 and the refrigerating unit 6 and is equipped with shield cap, and link to each other with secondary sack cleaner 63 with one-level sack cleaner 62 by pipeline 64.
Find out that from accompanying drawing 2 three-roller planetary rolls mixer 3 and is made up of batch mixing chamber 25, planet shovel 29, planet roller 17, planet scraper 18, motor 30, reduction box 20, rolling disc 27, shack 15, shack 19, shack 23, union lever 22, union lever 24 and union lever 28 and top cover 26.Top cover 26 is installed on the batch mixing chamber 25, motor 30 is fixed on the top cover 26, reduction box 20 links to each other with motor 30, rolling disc 27 links to each other with reduction box 20, shack 23, shack 19 links to each other with rolling disc 27 with shack 15, union lever 22, union lever 24 and union lever 28 respectively with shack 23, shack 19 links to each other with shack 15, planet shovel 29, planet roller 17 and planet scraper 18 respectively with union lever 28, union lever 24 links to each other with union lever 22, motor 30 is by reduction box 20, rolling disc 27 and shack 23, shack 19 and shack 15 drive union lever 22, union lever 24 and union lever 28 rotations, union lever 22, union lever 24 and union lever 28 constitute by two joint concentric tubes, it is planet shovel 29, planet roller 17 and planet scraper 18 all can vertically be regulated height, planet shovel 29, planet roller 17 and planet scraper 18 all have 3 to 5; Rolling disc 27 has certain width, and the position of shack 23, shack 19 and shack 15 all can radially with on the circumferential direction adjusting at rolling disc 27.Among the figure, 16 roll the opening for feed of mixer 3 for three-roller planetary, 21 roll the discharge port of mixer 3 for three-roller planetary, both link to each other with high pressure ball press 4 with weighing and burden device 2 respectively by travelling belt, 31 is the housing of batch mixing chamber 25,32 is the chassis of batch mixing chamber 25, and batch mixing chamber 25 is fixed on the support by chassis 32.
Planet shovel 29, planet roller 17 and planet scraper 18 all can vertically be regulated height.Gap between planet shovel 29 and the chassis 32 is 1～7mm, and the gap between planet roller 17 and the chassis 32 is 3～6mm, and the gap between planet scraper 18 and the chassis 32 is 1～7mm.
Find out that by Fig. 3 high pressure ball press 4 is made up of motor 39, reduction box 45, spinning bar 43, spinning apparatus 33, forced feed case 46, pair roller matched moulds compacting chamber 36, pair roller 34 and pair roller 35, worm screw 40, motor 37 and reduction box 44.
Forced feed case 46 joins with pair roller matched moulds compacting chamber 36 counterparts, spinning apparatus 33 is in the forced feed case 46, link to each other with reduction box 45 and motor 39 by spinning bar 43 on it, pair roller 34 and pair roller 35 are in the pair roller matched moulds compacting chamber 36, its active pair roller 35 links to each other with motor 37 with reduction box 44 by worm screw 40, and 42 and 38 are respectively the opening for feed and the discharge port of high pressure ball press 4.Discharge port 38 links to each other with the opening for feed 51 of laminating machine 5 by travelling belt.
Find out that by Fig. 4 laminating machine 5 is made up of coating bath 52, base 61, power wheel 55, travelling belt 53, electric heater unit 60, worm screw 56, motor 58 and reduction box 57.Coating bath 52 is installed on the base 61, motor 58 links to each other with reduction box 57, reduction box 57 links to each other with power wheel 55 by worm screw 56, travelling belt 53 is around on the power wheel 55, fill liquid passivator 59 in the coating bath 52, electric heater unit 60 is installed on the base under the passivator 59, is used for heating liquid passivator 59.51 and 54 are respectively the opening for feed and the discharge port of laminating machine 5.The discharge port 54 of laminating machine 5 links to each other with refrigerating unit 6 by travelling belt.Passivator be in the mineral oil paraffin wax vegetables oil any.
Adopt the manufacture method of composite carbon containing pellet of the present invention and the composite carbon containing pellet compressive strength height that device is produced thereof, single pelletizing can bear the above pressure of 5Mpa, composite carbon containing pellet is placed in the atmosphere or is indoor, three months indeformable, do not break, can satisfy long-distance transportation, loading and unloading and storage.And carbon content is suitable, is specially adapted to the metallurgical auxiliary material of using as carburelant in Electric furnace steel making or the cast steel.
Compared with prior art, the present invention has following advantage
1. the carbonaceous pelletizing density height of being produced reaches 3.0g/cm
3More than, so bearing resistance is big, single spheroid can bear the above pressure of 5Mpa, is convenient to storage, loading and unloading and long-distance transportation.
2. there is one deck passivation protection film on the pelletizing surface, does not absorb water, and moistureproofness is good, still can keep good use properties in the long time, and is favourable to storing, transporting.
But 3. continuous production, the production efficiency height, cost is low.
4. and carbon content suitable, be easy to be absorbed by molten steel, be specially adapted to the metallurgical auxiliary material of using as carburelant in Electric furnace steel making or the cast steel.
Embodiment
Adopt manufacture method of the present invention and device thereof, produced three replies and closed carbonaceous pelletizing.After raw material according to chemical composition is equipped with, except that passivator and toughener, remaining compound adds three-roller planetary and rolls in the mixer 3 and roll mixing, roll mix for some time after, to be equipped with good binding agent and toughener again and add wherein, until pulverizing and mixing.The relevant blended parameter that rolls is listed in the table 1.After mixing of materials is even, enter in the high pressure ball press 4 by travelling belt and to make ball, material at first enters pair roller matched moulds compacting chamber after the revolver gress precompressed, motor 37 applies total pressure by 40 pairs of actives of worm screw pair roller 35, carry out the pair roller matched moulds and make ball, it is as shown in table 1 to make the precompression, total pressure and the ball base size that are applied in the ball process.The pelletizing of making enters by travelling belt in the coating bath 52 of laminating machine 5 and carries out overlay film, in the coating bath 52 kind of liquid passivator, Heating temperature and the pelletizing residence time in liquid passivator as shown in table 2, final overlay film thickness is also listed in the table 2.Enter refrigerating unit by travelling belt behind the pelletizing overlay film and cool off, its type of cooling is as shown in table 2.Cooled pelletizing is composite carbon containing pellet of the present invention, and composite carbon containing pellet is placed in the atmosphere or is indoor, three months indeformable, do not break.In addition, pelletizing is carried out pressure test, gained is the result list in the table 2.
Table 1 embodiment raw material rolls mixing and makes the ball parameter
| Lot number | Roll hybrid parameter | Make the ball parameter | Ball base size | |||||||
| Stone roller is done time hour | Muller, scraper, planet shovel and chassis are apart from mm | Precompression * 10 4MPa | Total pressure * 10 5MPa | Linear pressure * 10 3Mpa/cm | Long mm | Wide mm | Thick mm | |||
| Muller | Scraper | The |
||||||||
| 1 | 1.5 | 3～ 5.8 | 1～6 | 1～6 | 2 | 2.0 | 5.2 | 48 | 38 | 24 |
| 2 | 1.2 | 3.3 ～5 | 1～ 5.2 | 1～ 5.2 | 2 | 1.7 | 6.7 | 40 | 30 | 20 |
| 3 | 1.9 | 3～5 | 1～5 | 1～5 | 2 | 1.8 | 7.5 | 45 | 35 | 25 |
Table 2 embodiment overlay film parameter and pelletizing performance index
| Lot number | Liquid passivator | Pelletizing residence time minute in passivator | The thickness mm of pelletizing overlay film | The pelletizing type of cooling behind the overlay film | The density g/cm of overlay film pelletizing 3 | The compressive strength MPa of single pelletizing | |
| Kind | Passivation temperature ℃ | ||||||
| Mineral oil | 100 | 1 | 0.5 | Air-cooled | 3.8 | 7.1 | |
| Paraffin wax | 150 | 1.2 | 0.9 | Naturally cooling | 3.5 | 5.9 | |
| Vegetables oil | 120 | 1.1 | 0.4 | Air-cooled | 3.6 | 6.8 | |
Claims (4)
1. the manufacture method of a composite carbon containing pellet is characterized in that its processing step comprises batching, batch mixing, pressure ball, ball base overlay film and cooling:
(1) batching
Chemical Composition according to composite carbon containing pellet is prepared burden, and adopts the negative pressure suction type material loading during batching;
(2) batch mixing
Batch mixing rolls in the mixer at three-roller planetary and carries out, roll in the mixer by travelling belt input three-roller planetary being equipped with good mixture, and startup rolls stirring system, mixture is rolled mixing, wherein binding agent and toughener add in mixing process, roll to be stirred to and mix, rolled mixing time 0.3～1.0 hour;
(3) pressure ball
Pressure ball carries out on the high pressure ball press, and through chute, the opening for feed by the high pressure ball press enters in the forced feed case, and by the revolver gress in the case, the material that enters in the forced feed case has been carried out precompressed with the material that mixes, and the pressure of precompressed is 2 * 10
4MPa, more closely knit material after precompressed, by the revolver gress force feed to pair roller matched moulds compacting chamber, in the pair roller matched moulds rotation process of this compacting chamber, drive roll is exerted pressure, material is suppressed the balling-up base, fall in the discharge port of pair roller matched moulds compacting chamber, finish the pressing process of ball base;
The total pressure that drive roll is applied is 1～2 * 10
5MPa, linear pressure are 4～8 * 10
3Mpa/cm, the mean density of ball base is 3.0g/cm
3
(4) ball base overlay film
Ball base overlay film carries out in laminating machine, suppress the discharge port of chamber from the pair roller matched moulds by the ball base that the high pressure ball press is pressed into, enter in the coating bath of laminating machine through travelling belt and laminating machine opening for feed, placed liquid passivator in the coating bath in advance, and by being arranged on the electric heater unit under the coating bath, liquid passivator is heated in advance in 100～200 ℃ the temperature range, ball base in coating bath parked 1～2 minute, then whole ball base surface evenly plating last layer thickness is the passive film of 0.1～1.0mm, and the ball base behind the overlay film then becomes composite carbon containing pellet;
(5) cooling
Cooling is carried out on refrigerating unit, pelletizing behind the overlay film is input on the refrigerating unit from the laminating machine discharge port by travelling belt, cool off by air-cooled or naturally cooling, through cooled pelletizing, promptly become final required composite carbon containing pellet, send into packing in the electronics metering automatic packing machine, seal up for safekeeping by travelling belt at last.
2. the manufacturing installation of a composite carbon containing pellet is characterized in that:
1. this device rolls mixer (3), high pressure ball press (4), laminating machine (5), refrigerating unit (6), metering packaging machine (7), primary dust removing device (62) and secondary ash collector (63) by feed bin (1), weighing and burden device (2), three-roller planetary and forms; Weighing and burden device (2) is right after under the feed bin (1), weighing and burden device (2) links to each other by the opening for feed (16) that travelling belt (9) and three-roller planetary roll mixer (3), the discharge port (21) that three-roller planetary rolls mixer (3) links to each other with the opening for feed (42) of high pressure ball press (4) by travelling belt (10), pair roller matched moulds compacting chamber (36) discharge port (38) in the high pressure ball press (4) links to each other with the opening for feed (51) of laminating machine (5) by travelling belt (11), the discharge port (54) of laminating machine (5) links to each other with refrigerating unit (6) by travelling belt (12), refrigerating unit (6) links to each other with metering packaging machine (7) by travelling belt (13), and metering packaging machine (7) links to each other with stockyard (8) by travelling belt (14); Flow through process and feed bin (1), weighing and burden device (2), three-roller planetary of whole logistics rolls on mixer (3), high pressure ball press (4), laminating machine (5) and the refrigerating unit (6) and is equipped with shield cap, and link to each other with secondary ash collector (63) with primary dust removing device (62) by pipeline (64);
2. three-roller planetary rolls mixer (3) by batch mixing chamber (25), planet shovel (29), planet roller (17), planet scraper (18), motor (30), reduction box (20), rolling disc (27), shack (23,19 and 15), and union lever (22,24 and 28) and top cover (26) are formed; Top cover (26) is installed on the batch mixing chamber (25), motor (30) is fixed on the top cover (26), reduction box (20) links to each other with motor (30), rolling disc (27) links to each other with reduction box (20), shack (23,19 and 15) link to each other with rolling disc (27), union lever (22,24,28) respectively with shack (23,19 and 15) link to each other, planet shovel (29), planet roller (17) and planet scraper (18) respectively with union lever (28,24 and 22) link to each other, motor (30) is by reduction box (20), rolling disc (27) and shack (23,19 and 15) drive union lever (22 respectively, 24 and 28) rotation; Batch mixing chamber (25) is fixed on the support by chassis (32);
3. high pressure ball press (4) is by motor (39), reduction box (45), spinning bar (43), spinning apparatus (33), forced feed case (46), pair roller matched moulds compacting chamber (36), pair roller (34 and 35), worm screw (40)), motor (37) and reduction box (44) form;
Forced feed case (46) joins with pair roller matched moulds compacting chamber (36) counterpart, spinning apparatus (33) is in the forced feed case (46), link to each other with reduction box (45) and motor (39) by spinning bar (43) on it, pair roller (34 and 35) is in the pair roller matched moulds compacting chamber (36), its active pair roller (35) links to each other with motor (37) with reduction box (44) by worm screw (40), (42 and 38) are respectively the opening for feed and the discharge port of high pressure ball press (4), and discharge port (38) links to each other with the opening for feed (51) of laminating machine (5) by travelling belt;
4. laminating machine (5) is made up of coating bath (52), base (61), power wheel (55), travelling belt (53), electric heater unit (60), worm screw (56), motor (58) and reduction box (57); Coating bath (52) is installed on the base (61), motor (58) links to each other with reduction box (57), reduction box (57) links to each other with power wheel (55) by worm screw (56), travelling belt (53) is around on the power wheel (55), fill liquid passivator (59) in the coating bath (52), electric heater unit (60) is installed on the base under the passivator (59), be used for heating liquid passivator (59), (51 and 54) are respectively the opening for feed and the discharge port of laminating machine (5), and the discharge port (54) of laminating machine (5) links to each other with refrigerating unit (6) by travelling belt.
3. device according to claim 2, it is characterized in that planet shovels (29), planet roller (17) and planet scraper (18) and vertically regulates height, gap between the planet shovel (29) and chassis (32) is 1～7mm, gap between planet roller (17) and chassis (32) is 3～6mm, and the gap between planet scraper (18) and chassis (32) is 1～7mm.
4. according to claim 2 or 3 described devices, it is characterized in that planet shovel (29), planet roller (17) and planet scraper (18) all have 3 to 5.