CN100358986C - 复合高温脲基脂 - Google Patents

复合高温脲基脂 Download PDF

Info

Publication number
CN100358986C
CN100358986C CNB2005100470012A CN200510047001A CN100358986C CN 100358986 C CN100358986 C CN 100358986C CN B2005100470012 A CNB2005100470012 A CN B2005100470012A CN 200510047001 A CN200510047001 A CN 200510047001A CN 100358986 C CN100358986 C CN 100358986C
Authority
CN
China
Prior art keywords
high temperature
composite
temperature
agent
extreme pressure
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB2005100470012A
Other languages
English (en)
Other versions
CN1718701A (zh
Inventor
李辉
刘鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Liaoning Haihua Polytron Technologies Inc
Original Assignee
HAIHUA GREASE CHEMISTRY CO Ltd ANSHAN
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIHUA GREASE CHEMISTRY CO Ltd ANSHAN filed Critical HAIHUA GREASE CHEMISTRY CO Ltd ANSHAN
Priority to CNB2005100470012A priority Critical patent/CN100358986C/zh
Publication of CN1718701A publication Critical patent/CN1718701A/zh
Application granted granted Critical
Publication of CN100358986C publication Critical patent/CN100358986C/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种以高粘度矿物油为基础油，以复合聚脲为稠化剂，加入多种高效添加剂的复合高温脲基脂，主要成分为高粘度矿油、复合聚脲、抗氧剂、极压剂、防锈剂。按规定的重量份配比加入基础油，加入异氰酸酯类，脂肪胺类和芳香胺类进行反应得聚脲产物，升温到100℃加入低分子酸盐，最高升温到160℃进行高温炼制，降温到110℃加入抗氧剂、极压剂、防锈剂，然后用均质机进行后处理，过滤，包装。优点是高温性能突出，滴点高达260℃以上，高温时不流淌，不结焦；抗水性能优异，38℃水淋流失量只有2%，能保证大量水冲刷时流失少；极压性能高，不结焦，不卡轴承，使用寿命长。

Description

复合高温脲基脂
技术领域
本发明涉及一种润滑脂，是以高粘度矿物油为基础油，以复合聚脲为稠化剂，加入多种高效添加剂的复合高温脲基脂。
背景技术
冶金工业中炼钢厂的设备多处于高温、多水、冲击负荷的条件下运行，如结晶器、扇形段、拉矫机轴承等部位。对炼钢设备轴承所用的润滑脂性能提出了较高的要求。
用于炼钢设备轴承的润滑脂多以极压复合锂或复合铝为主，但这类脂的高温性能和轴承寿命不是很好，经常在高温下变稀流淌，导致润滑脂在轴承中的存量变少，严重时脂在轴承内结焦卡死轴承，从而影响润滑效果，也给生产和维护带来了诸多不便，影响了钢厂的效益。
发明内容
本发明的目的是提供一种以复合聚脲为稠化剂，以高粘度矿油为基础油，加入多种功能性添加剂的润滑脂复合高温脲基脂，经多家炼钢厂试验证明，该脂高温不流失，不结焦，抗水性良好，延长了使用时间，减少了维护次数，对轴承提供了良好的润滑保护，使炼钢厂收到了可观的综合经济效益。
复合高温脲基脂，其特征在于以高粘度矿油为基础油，以复合聚脲为稠化剂，加入抗氧剂、极压剂、防锈剂制成，其中各成分的重量份配比如下：
高粘度矿油：70-75
复合聚脲：15-20
抗氧剂：0.5-2
极压剂：3-6
防锈剂：0.5-2
所述的高粘度矿油是指150BS和400SN的混合油，其100℃的运动粘度为20-25mm2/s；
所述的极压剂是指硼酸盐类化合物或磷酸酯或亚磷酸酯类化合物；
所述的防锈剂是指石油磺酸钡类化合物。
所述的复合聚脲是指异氰酸酯类与脂肪胺类和芳香胺类反应的聚脲产物，和低分子酸盐组成的复合稠化剂。所述的低分子酸盐是指醋酸钙。
所述的抗氧剂是指苯基-α-萘胺。
复合高温脲基脂的生产工艺为：按规定的重量份配比加入基础油，加入异氰酸酯类，脂肪胺类和芳香胺类进行反应得聚脲产物，升温到100℃加入低分子酸盐，最高升温到160℃进行高温炼制，降温到110℃加入抗氧剂、极压剂、防锈剂，然后用均质机进行后处理，过滤，包装。
本发明具有如下优点；
1)高温性能突出，滴点高达260℃以上，高温时不流淌，不结焦；
2)抗水性能优异，38℃水淋流失量只有2％，能保证大量水冲刷时流失少；
3)极压性能高，四球机PB值可达980N以上，PD值可达4900以上，适合重负荷工况。
4)适合炼钢厂的高温轴承使用，不结焦，不卡轴承，使用寿命长。
具体实施方式
实施例1：
复合高温脲基脂，以高粘度矿油为基础油，以复合聚脲为稠化剂，加入抗氧剂、极压剂、防锈剂制成，其中各成分的重量份配比如下：
150BS：35
400SN：35
异氰酸酯与脂肪胺和芳香胺类：15
醋酸钙：5
苯基-α-萘胺：2
硼酸盐类化合物：4
石油磺酸钡：1
复合高温脲基脂的生产工艺为：按规定的重量份配比加入基础油，加入异氰酸酯类，脂肪胺类和芳香胺类进行反应得聚脲产物，升温到100℃加入低分子酸盐，最高升温到160℃进行高温炼制，降温到110℃加入抗氧剂、极压剂、防锈剂，然后用均质机进行后处理，过滤，包装。
实施例2：
复合高温脲基脂，以高粘度矿油为基础油，以复合聚脲为稠化剂，加入抗氧剂、极压剂、防锈剂制成，其中各成分的重量份配比如下：
150BS：40
400SN：35
异氰酸酯与脂肪胺和芳香胺类：10
醋酸钙：5
苯基-α-萘胺：0.5
硼酸盐类化合物：6
石油磺酸钡：0.5
复合高温脲基脂的生产工艺同实施例1。
实施例3：
复合高温脲基脂，以高粘度矿油为基础油，以复合聚脲为稠化剂，加入抗氧剂、极压剂、防锈剂制成，其中各成分的重量份配比如下：
150BS：38
400SN：35
异氰酸酯与脂肪胺和芳香胺类：12
醋酸钙：5
苯基-α-萘胺：1.5
硼酸盐类化合物：3
石油磺酸钡：2
复合高温脲基脂的生产工艺同实施例1。

Claims (5)

1、复合高温脲基脂，其特征在于以高粘度矿油为基础油，以复合聚脲为稠化剂，加入抗氧剂、极压剂、防锈剂制成，其中各成分的重量份配比如下：
高粘度矿油：70-75
复合聚脲：15-20
抗氧剂：0.5-2
极压剂：3-6
防锈剂：0.5-2
所述的高粘度矿油是指150BS和400SN的混合油，其100℃的运动粘度为20-25mm2/s；
所述的极压剂是指硼酸盐类化合物或磷酸酯或亚磷酸酯类化合物；
所述的防锈剂是指石油磺酸钡类化合物。
2、根据权利要求1所述的复合高温脲基脂，其特征在于所述的复合聚脲是指异氰酸酯类与脂肪胺类和芳香胺类反应的聚脲产物，和低分子酸盐组成的复合稠化剂。
3、根据权利要求2所述的复合高温脲基脂，其特征在于所述的低分子酸盐是指醋酸钙。
4、根据权利要求1所述的复合高温脲基脂，其特征在于所述的抗氧剂是指苯基-α-萘胺。
5、根据权利要求1所述的复合高温脲基脂的生产工艺，其特征在于其工艺步骤为：按规定的重量份配比加入基础油，加入异氰酸酯类，脂肪胺类和芳香胺类进行反应得聚脲产物，升温到100℃加入低分子酸盐，最高升温到160℃进行高温炼制，降温到110℃加入抗氧剂、极压剂、防锈剂，然后用均质机进行后处理，过滤，包装。
CNB2005100470012A 2005-08-05 2005-08-05 复合高温脲基脂 Active CN100358986C (zh)