CN100351472C - 建筑墙体喷涂保温材料 - Google Patents
建筑墙体喷涂保温材料 Download PDFInfo
- Publication number
- CN100351472C CN100351472C CNB031215882A CN03121588A CN100351472C CN 100351472 C CN100351472 C CN 100351472C CN B031215882 A CNB031215882 A CN B031215882A CN 03121588 A CN03121588 A CN 03121588A CN 100351472 C CN100351472 C CN 100351472C
- Authority
- CN
- China
- Prior art keywords
- present
- brick
- charging stock
- clay brick
- spray coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种建筑墙体喷涂保温材料,包括固体原料及液体原料,固体原料置于喷涂设备的主机,液体原料置于喷涂设备的附机,上述固体原料与液体原料经喷涂设备喷到作业面上,其中固体原料为无机纤维,纤维长度0~30mm,纤维直径3~5μm,渣球含量为0;液体原料由丙烯酸苯丙乳液、液体阻燃剂、羟甲基纤维素组成,液体原料的配比如下:①丙烯酸苯丙乳液 50~100kg;②液体阻燃剂 25~50kg;③羟甲基纤维素 3~5kg。
Description
(一)、技术领域:本发明涉及一种建筑墙体喷涂保温材料。
本发明是解决建筑墙体沿用粘土砖的陈旧历史,所述建筑墙体喷涂保温材料是一种崭新及建筑墙体材料,主要是在建筑行业上,代替砖混结构的墙体,它质轻(喷层容重0.15吨/M3)是普通粘土砖容重的1/10。导热系数也比粘土砖小,是粘土砖的1/15。可以说它是十分优良的保温材料。
此外它还用于石油化工大型贮罐的保温,用于钢结构防火层,实验证明,喷层厚度3cm,防火极限可达2小时。
用于军工,可作舰船、潜水艇的舱壁保温。它还可以用于石化、电力、冶金等大型工业炉窑,代替耐火砖作炉衬,不但大大减轻炉体的重量,而且它导热系数小,热容量小,因而整炉热损失大大减小,是节约能源的绝佳材料。
(二)、背景内容:秦砖汉瓦在中国建筑上已有几千所的历史了,随着时代的进步,新材料的不断涌现,原来的砖瓦将退出历史舞台,因为新型的、大型的高层建筑的出现,陈旧的建筑材料已不适用了。而且,粘土砖要毁坏大量的土地,烧制砖瓦要消耗大量的能源和产生大量的废气,污染环境。
国家建设部,2000年即有文件规定,像北京、上海、天津、重庆、南京等大中型城市,不准再使用粘土砖盖房子。于是像空心砖、聚苯板、聚氨酯板等材料开始广泛应用,虽然它们比粘土砖质轻,隔热效果好,但空心砖仍然是粘土砖一类,而聚苯板、聚氨酯板在强度上施工工序繁杂,最大缺点(也是致命缺点)是它不阻燃。
本发明彻底解决建筑材料存在的上述弊病。本发明是利用机械化施工,工序简,施工速度快。一台机器,一个台班(8小时作业)可施工500-700M2,而且材料是无机纤维(玻璃棉)是不燃的材料。材料成本也与上述材料相当。要说粘土质砖瓦是第一代建材,空心砖等属第二代建材,本发明即是最新型、最理想的第三代建筑材料。
(三)、发明内容:喷涂所用的设备,目前国内已有多家生产厂,本发明的建筑墙体喷涂保温材料包括固体原料及液体原料,固体原料置于喷涂设备的主机,液体原料置于喷涂设备的附机,上述固体原料与液体原料经喷涂设备喷到作业面上,其中固体原料为无机纤维,纤维长度0~30mm,纤维直径3~5μm,渣球含量为0;液体原料由丙烯酸苯丙乳液、液体阻燃剂、羟甲基纤维素组成,液体原料的配比如下:
①丙烯酸苯丙乳液 50~100kg
②液体阻燃剂 25~50kg
③羟甲基纤维素 3~5kg.
以上三种均匀混合,过滤后置于附机的罐内。
工艺过程:主机接通电源,输料管及组合喷头联接。附机接通电源,联接高压泵,输送管至组合喷头。
开机:将纤维徐徐投入主机进料口,同时打开喷头,结合剂阀门,视液体结合剂,呈雾状并聚焦在喷头前,打开组合喷头,固体阀,纤维喷出与结合剂混合液喷到作业面上。喷层厚度与表面平整度由工人操作时掌握的熟练程度而定。
若喷涂防火层,配比如下:
①固体料,硅酸铝纤维,渣球含量<5%,纤维长度L=0-30mm,纤维
直径Φ5-6μm。
②液体料:中性硅容胶,100kg+1kg,羟甲基纤维素。
工艺过程同上。
①在建筑上:它是取代粘土砖作轻质墙体的优良材料,它比聚苯板,聚氢酯板作墙体保温优越很多:a、阻燃b、强度好c、耐老化d、施工费用低e、施工速度加快f、防水g、环保(无毒、无嗅)。
②用于钢结构防火层:它比传统的厚浆型防火涂料有如下优点:a、质轻b、施工速度快c、同样厚度耐火极限提高1倍d、表面平整装饰效果好。
③作炉衬:它比传统的耐火砖有如下优点:a、质轻b、施工便利c、投产时不用烘炉d、导热系数小,热容量小,故节约能源。
(四)、具体实施方式:本发明的建筑墙体喷涂保温材料,包括固体原料及液体原料,固体原料置于喷涂设备的主机,液体原料置于喷涂设备的附机,上述固体原料与液体原料经喷涂设备喷到作业面上,其中固体原料为无机纤维,纤维长度0~30mm,纤维直径3~5μm,渣球含量为0;液体原料由丙烯酸苯丙乳液、液体阻燃剂、羟甲基纤维素组成,液体原料的配比如下:
①丙烯酸苯丙乳液 50~100kg
②液体阻燃剂 25~50kg
③羟甲基纤维素 3~5kg.
2000年,在北京立水桥高尔夫球场的游泳馆第一次试用,喷外墙的内保温层(屋顶、四面墙体,其中对墙面±0.00-1.7米。围墙在喷层表面,粘贴马骞克至今无任何脱落现象。2001年在北京田村吉彩健康娱乐中心,楼顶大跨度拱形彩钢板内侧喷保温层,取得良好效果,受到用户好评。2001-2002年,在北京六里桥兰景丽家家具城,30000M2平面钢板屋顶作保温喷层。
在河北坝州温泉如乐城,大跨度拱形屋顶均取得良好效果。前不久在南方某一大型钢厂,新建大转炉车间,作钢结构防火涂层。
Claims (1)
1.一种建筑墙体喷涂保温材料,包括固体原料及液体原料,固体原料置于喷涂设备的主机,液体原料置于喷涂设备的附机,上述固体原料与液体原料经喷涂设备喷到作业面上,其中固体原料为无机纤维,纤维长度0~30mm,纤维直径3~5μm,渣球含量为0;液体原料由丙烯酸苯丙乳液、液体阻燃剂、羟甲基纤维素组成,液体原料的配比如下:
①丙烯酸苯丙乳液50~100kg
②液体阻燃剂25~50kg
③羟甲基纤维素3~5kg。