CN100341479C - Lead of cosmetic pencil - Google Patents
Lead of cosmetic pencil Download PDFInfo
- Publication number
- CN100341479C CN100341479C CNB2005100625808A CN200510062580A CN100341479C CN 100341479 C CN100341479 C CN 100341479C CN B2005100625808 A CNB2005100625808 A CN B2005100625808A CN 200510062580 A CN200510062580 A CN 200510062580A CN 100341479 C CN100341479 C CN 100341479C
- Authority
- CN
- China
- Prior art keywords
- lead
- cosmetic pencil
- soap
- contain
- pen core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention provides a cosmetic stick for the purpose of decoration and skin care. The stick base material comprises at least one fatty acid salt, at least one lipophilic material having melting temperature range no more than 50 DEG C, and the ratio of the solid particles is no more than 50 percents.
Description
Technical field
Being used to of using in liner, lip liner, eye shadow product, eyeliner, Kajal pen, Lipstick holder etc. decorates and the lead of cosmetic pencil of skin nursing purpose.When saying at this and during pen core, will be understood that chalk also belongs to this type of.This lead of cosmetic pencil contains pen core base material and oil, filler and the pigment of being made up of waxy substance such as wax, fat and emulsifying agent usually.
Disadvantageously, it has relatively low heat stability and particularly low maximum applied temperature in such pen core.At this, the maximum applied temperature is meant such temperature, promptly just still pen core material or chalk material can be coated on lip, eyelid or other parts of skin under this temperature, and pen core do not appear and smear confusion, distortion, perhaps pen core or chalk fractures.Though common pen core has 60 ℃-90 ℃ fusing point or fusion range, their maximum applied temperature is much lower naturally.Be used to form pen core method affect the micro structure of pen core base material, therefore influenced the machinery of the pen core that formed afterwards and used characteristic.The influence of dump method is minimum, and can produce application temperature with the method is about 40 ℃-45 ℃ pen core.In pressing method, the pen core starting material is compressed in cylinder and it is extruded with the rope form form through delivery outlet, if the pen core base material is subjected to the load of machinery and heat by this way, the pen core for preparing only has about 30 ℃-35 ℃ application temperature.
Summary of the invention
From this point, task of the present invention is, a kind of pen core that is used for cosmetic applications is provided, and this pen core is being improved aspect its heat stability, particularly can use under higher temperature.
This task is resolved by the pen core according to claim 1.The pen core base material of predesignating pen core like this is that oil or waxy substance form by the lipophilic substance of at least a soap and at least a fusion range<50 ℃.At this, such material can be thought the pen core base material, and promptly this material is as the binding agent of solid particle, and uses characteristic and heat stability decisive role for pen core.
Show astoundingly, can prepare the pen core that fusing point surpasses 90 ℃ with such base material, therefore this pen core can withstand the storage temperature more much higher than common pen core harmlessly, and can promptly be higher than in the temperature higher than common pen core under 50 ℃ the temperature and use.In addition surprisingly, the pen core with the pen core base material that is provided can hold the solid particle until 90%, can prepare the very high pen core ingredients of color intensity thus.Can not prepare such pen core with common pen core base material.Because the high-load of solid particle, the pen core material that therefore becomes molten condition has too high viscosity, so that it can't pour into.But, in pressing method, be shaped or by for example extrusion molding also is impossible by means of extruser, because the liquefaction too consumingly under required temperature of common pen core base material.In contrast, pen core material of the present invention can be extruded on no problem ground under about 80 ℃-about 140 ℃ temperature, except other this be because pen core material or pen core base material this under this temperature, still have sufficiently high processing viscosity.With containing 1%-20%, the pen core of the soap of preferred 3%-10% can obtain good especially result.Adopt the fatty acid salt content of 4%-8% can obtain best result.The content of lipophilic substance is 5%-40%, preferred 10%-35%.The lipophilic substance content of 16%-32% is verified to be specially suitable.
At least 50%, the solid content of better 60%-90% has advantageously influenced the heat stability of pen core, has particularly influenced the application temperature of pen core.At this, think filler such as Talcum and Muscovitum and for example pigment all belong to solid particle.At first preferred lead of cosmetic pencil form is made up of 1-20% soap, 5-40% lipophilic substance, 30-90% solid particle, 0-10% additive, and further preferred pen core form is made up of 4-8% soap, 16-32% lipophilic substance, 60-80% solid particle, 0-10% additive.
Soap deemed appropriate soap, particularly calcium laurate, magnesium stearate, zinc stearate with chain length of 10-20 carbon atom, and palmitate, myristate, oleate and linoleate.Specially suitable is the mixture of lithium stearate, aluminium stearate, Aluminium Tristearate Micronized sterile and described soap.Can obtain optimal results with aluminium distearate.
Following material can be used as lipophile liquid or have<50 ℃ low-melting oil or waxy substance: and Oleum Ricini, mineral oil, stearyl dimethicone, hydrogenation (sclerosis) Oleum Cocois, isopropyl palmitate, isopropyl myristate, triglyceride such as tricaprylin and decanoin, hydrogenated palm kernel oil-glyceride and hydrogenated palm oil-glyceride also have olive oil, Oleum Brassicae campestris and other to be usually used in the oil of cosmetics.
Can add be usually used in cosmetics the organic or inorganic pigment as coloring agent.It is also conceivable that the use dyestuff in addition, for example the lipophilic dyestuff.In needs, can consider absorb fillers, for example Talcum, Kaolin, Muscovitum or be coated with the Muscovitum of silicon dioxide.In needs, can add the one-tenth structural agent or the one-tenth of antiseptic, sunscreen, aromatic substance, vitamin, spice, care substance and low content and organize agent such as C 30-45 alkyl methyl siloxanes (CAS Nr.131459-42-2) as additive or auxiliary agent.At this, be 10% to the maximum in the total amount of additives in raw materials.
Material of the present invention is homogenized in mixer, kneading compactor, roller base etc., and be extruded into pen core or chalk in 80-140 ℃.
As basic recipe, can provide following composition:
Soap: 1-20%
The lipophilic substance of fusing point<50 ℃: 5-40%
Pigment, filler: 30-90%
Additive: 0-10%
A preferred basic recipe has following composition:
Soap: 4-8%
Lipophilic substance: 16-32%
Solid particle: 60-80%
Additive: 0-10%
The specific embodiment
To specifically describe the present invention by embodiment:
Embodiment 1:
The pen core diameter is the blue eyeliner pen core of 4mm:
Lithium stearate (CAS 4485-12-5): 8.0%
Isopropyl myristate (CAS 110-27-0): 20.0%
Hydrogenated palm kernel glyceride
(trade name: Lipocire CM; Buy in Gattefoss é): 11.0%
Pigment indigo plant 27; CI 77510:60.0%
Pantothenylol (CAS 16485-10-2): 0.5%
Propyl parabene: 0.5%
Embodiment 2:
Be used to be applied in the prescription of the atrous lead of cosmetic pencil on the eye.Diameter is 3MM, be used to be applied in the pen core of exsiccant and moistening skin (eyeliner is used and the Kajal application).This pen core can also used under 60 ℃, and has and be higher than 95 ℃ heat stability.
Aluminium distearate (CAS 300-92-5): 4.0%
Tricaprylin/decanoin: 16.0%
(trade name: Myritol 318;
Supplier/manufacturer: Henkel)
Pigment basket 29; CI 77007:5.0%
Be coated with the Muscovitum of silicon dioxide
(trade name: Micronasphere M (Merck)): 15.0%
Black pigment 11; CI 77499:60.0%
Embodiment 3:
Diameter is 10mm, is used for the chalk of the skin marker of a metallic luster that it has 55 ℃ maximum applied temperature:
Aluminium stearate (CAS 7047-84-9): 4.0%
Zinc stearate (CAS 557-05-1): 2.0%
Hydrogenated palm/core oil 10.0%
PEG-6 ester: 10.0%
(trade name: Lipocire BP Pastilles;
Manufacturer/supplier: Gattefoss é)
Hydrogenated coconut oil (CAS 84836-98-6): 12.0%
Talcum: 20.0%
Aluminium powder: pigment metal 1; CI 77000:42.0%
Embodiment 4:
The prescription that is used for peony liner pen core, the diameter of this pen core are 8.0mm, and it has painted and>90 ℃ the fusing point of the non-flash of light of peony:
Aluminium distearate: 4.0%
Stearyl dimethicone: 16.0%
(trade name: Dowcorning 2503)
(manufacturer: Dowcorning)
Propyl parabene: 1.0%
Talcum: 28.0%
Neutral red 4; CI 75470:51.0%
Embodiment 5:
Weak painted pen core prescription, it has the treatment soil (loess) that is used to be applied on the skin.Diameter is 5mm, be used to be applied in the pen core on the exsiccant and moistening skin.This pen core can also used under 60 ℃, and has and be higher than 95 ℃ heat stability.
Aluminium distearate (CAS 300-92-5): 4.0%
Tricaprylin/decanoin: 16.0%
(trade name: Myritol 318;
Supplier/manufacturer: Henkel)
Treatment soil (loess), (D90≤20 μ m) of grinding: 50%
Hydrogenated palm kernel glyceride
(trade name: Lipocire CM; Buy in Gattefoss é): 5%
Be coated with the Muscovitum of silicon dioxide
(trade name: Micronasphere M (Merck)): 24.0%
Propyl parabene: 1.0%
All percentage data are percetage by weight.
Claims (15)
1. have the pen core base material and be distributed in the lead of cosmetic pencil of the solid particle among the base material, it is characterized in that, this pen core base material is formed by the lipophilic substance of at least a soap and at least a fusion range<50 ℃, and has following composition:
Soap: 1-20%
Lipophilic substance: 5-40%
Solid particle: 50-90%
Additive: 0-10%.
2. according to the lead of cosmetic pencil of claim 1, it is characterized in that, contain the soap that content is 3%-10%.
3. according to the lead of cosmetic pencil of claim 1, it is characterized in that, contain the soap that content is 4%-8%.
4. according to the lead of cosmetic pencil of claim 1, it is characterized in that, contain the lipophilic substance that content is 10%-35%.
5. according to the lead of cosmetic pencil of claim 4, it is characterized in that, contain the lipophilic substance that content is 16%-32%.
6. according to the lead of cosmetic pencil of claim 1, it is characterized in that, contain the solid particle of 60%-80%.
7. according to each lead of cosmetic pencil of claim 1-6, it is characterized in that containing soap with 12-18 carbon atom.
8. according to the lead of cosmetic pencil of claim 7, it is characterized in that containing and at least aly be selected from calcium laurate, magnesium stearate, zinc stearate, and the soap of palmitate, linoleate, oleate and myristate.
9. according to the lead of cosmetic pencil of claim 7, it is characterized in that containing at least a soap that is selected from lithium stearate, aluminium stearate and Aluminium Tristearate Micronized sterile.
10. according to the lead of cosmetic pencil of claim 7, it is characterized in that, contain aluminium distearate as soap.
11., it is characterized in that containing at least a lipophilic substance that is selected from mineral oil, Oleum Ricini, isopropyl myristate, isopropyl palmitate, hydrogenated coconut oil, stearyl dimethicone, tricaprylin, decanoin, hydrogenated palm kernel oil-glyceride and hydrogenated palm oil-glyceride according to each lead of cosmetic pencil of claim 1-6.
12. according to each lead of cosmetic pencil of claim 1-6, it is characterized in that, contain inorganic and/or organic pigment as solid particle.
13. according to each lead of cosmetic pencil of claim 1-6, it is characterized in that, contain the micaceous solid particle that is selected from Talcum, Kaolin, Muscovitum, is coated with silicon dioxide.
14., it is characterized in that containing at least a additive that is selected from aromatic substance, care substance, film former, antiseptic, sunscreen, spice, vitamin and care substance according to each lead of cosmetic pencil of claim 1-6.
15. preparation is according to each the method for lead of cosmetic pencil of claim 1-14, it mixes the starting material that forms by cosmetic pencil core inclusions and obtains by extruding in 80-140 ℃.