CA2918670C - Positive electrode material for lithium secondary battery - Google Patents
Positive electrode material for lithium secondary battery Download PDFInfo
- Publication number
- CA2918670C CA2918670C CA2918670A CA2918670A CA2918670C CA 2918670 C CA2918670 C CA 2918670C CA 2918670 A CA2918670 A CA 2918670A CA 2918670 A CA2918670 A CA 2918670A CA 2918670 C CA2918670 C CA 2918670C
- Authority
- CA
- Canada
- Prior art keywords
- lithium
- positive electrode
- compound
- secondary battery
- electrode material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A positive electrode material which can achieve high output, high energy density, and/or a long cycle life required for on-vehicle applications is discussed. The positive electrode material is used to produce a positive electrode of a lithium secondary battery, the positive electrode material being a composite lithium material that includes a first lithium compound and a second lithium compound. For instance, the first lithium compound is in the form of particles and comprises at least one compound selected from a layered lithium compound and a spinel-type lithium compound. Preferably, the second lithium compound comprises at least one compound selected from a lithium-containing phosphate compound and a lithium-containing silicate compound. An amorphous carbon material layer and/or graphene-structured carbon material layer is present on the entire surface of the first lithium compound and the second lithium compound. The second lithium compound forms a thin-film layer on part or the entirety of the carbon material layer present on the surface of the first lithium compound particles.
Description
POSITIVE ELECTRODE MATERIAL FOR LITHIUM SECONDARY BATTERY
FIELD OF THE INVENTION
The invention relates to a positive electrode material for a lithium secondary battery. For instance, the invention relates to a positive electrode material for a lithium secondary battery that is to be used as a vehicle battery.
BACKGROUND OF THE INVENTION
In recent years, lithium secondary batteries including positive and negative electrodes formed using a material that allows insertion and extraction of lithium ions, which were developed, aimed at on-vehicle applications. It has been a great challenge to implement a lithium secondary battery that achieves high energy density, high output (large-current charge/discharge), long lifetime, and high safety.
Various solutions such as (1) improvements in positive/negative electrode material (Japanese Patent No. 3867030, Sei KK); (2) improvements in the .. collector foil (W02011/049153, SEI Corporation); and (3) improvements in the separator (PCT/JP2012/056998) have been proposed to implement such a lithium secondary battery.
Energy density and output of a lithium secondary battery were improved, for example, by reducing the particle size of positive/negative electrode active material particles, increasing the specific surface area of positive/negative electrode active material particles via surface modification or the like, or increasing the electrode area by improving the electrode design. Although these measures have opened the door to a possibility to implement a lithium secondary battery aimed at on-vehicle applications, the improvement in energy density, safety, and lifetime is currently insufficient.
Date Recue/Date Received 2021-03-31
FIELD OF THE INVENTION
The invention relates to a positive electrode material for a lithium secondary battery. For instance, the invention relates to a positive electrode material for a lithium secondary battery that is to be used as a vehicle battery.
BACKGROUND OF THE INVENTION
In recent years, lithium secondary batteries including positive and negative electrodes formed using a material that allows insertion and extraction of lithium ions, which were developed, aimed at on-vehicle applications. It has been a great challenge to implement a lithium secondary battery that achieves high energy density, high output (large-current charge/discharge), long lifetime, and high safety.
Various solutions such as (1) improvements in positive/negative electrode material (Japanese Patent No. 3867030, Sei KK); (2) improvements in the .. collector foil (W02011/049153, SEI Corporation); and (3) improvements in the separator (PCT/JP2012/056998) have been proposed to implement such a lithium secondary battery.
Energy density and output of a lithium secondary battery were improved, for example, by reducing the particle size of positive/negative electrode active material particles, increasing the specific surface area of positive/negative electrode active material particles via surface modification or the like, or increasing the electrode area by improving the electrode design. Although these measures have opened the door to a possibility to implement a lithium secondary battery aimed at on-vehicle applications, the improvement in energy density, safety, and lifetime is currently insufficient.
Date Recue/Date Received 2021-03-31
2 Extensive research and development have been conducted in order to achieve higher energy density. For example, an increase in charge voltage of an Ni-rich LNMC (Li(Ni/Mn/Co)02) positive electrode material, use of a sulfur compound having high theoretical energy density as a positive electrode material, and use of an alloy-based negative electrode material (or an oxide thereof) having semiconductor properties have been proposed. Lithium-air batteries have also been proposed as novel lithium batteries.
A Li(Ni/Mn/Co)02/LiFePO4 mixed battery has also been proposed in the Abstracts of 53rd Battery Symposium in Japan (p. 40, Nov. 2012), Committee of Battery Technology, Electrochemical Society of Japan.
The initial energy density of a lithium battery can temporarily be increased by the above means. However, it is difficult to implement the cycle life of 5,000 to 10,000 cycles (10 years) required for vehicle applications which necessitate maintaining a high energy density.
A Ni-rich LNMC positive electrode material achieves long constant-current discharge, but does not exhibit flat voltage characteristics (i.e., generally exhibits voltage characteristics that decrease from the high-voltage region). An on-vehicle battery should exhibit flat voltage characteristics from the viewpoint of quality, high output and high energy density, which characteristics cannot be practically achieved when using a Ni-rich LNMC positive electrode material.
More specifically, since an on-vehicle battery is used at a constant power, it is impossible to use an on-vehicle battery up to a considerable discharge depth.
A mixed battery can initially prevent a decrease in output due to the mixed potential, but shows a decrease in output as the number of charge-discharge cycles increases since the reaction site is concentrated on an active material having low resistance.
Date Recue/Date Received 2021-03-31
A Li(Ni/Mn/Co)02/LiFePO4 mixed battery has also been proposed in the Abstracts of 53rd Battery Symposium in Japan (p. 40, Nov. 2012), Committee of Battery Technology, Electrochemical Society of Japan.
The initial energy density of a lithium battery can temporarily be increased by the above means. However, it is difficult to implement the cycle life of 5,000 to 10,000 cycles (10 years) required for vehicle applications which necessitate maintaining a high energy density.
A Ni-rich LNMC positive electrode material achieves long constant-current discharge, but does not exhibit flat voltage characteristics (i.e., generally exhibits voltage characteristics that decrease from the high-voltage region). An on-vehicle battery should exhibit flat voltage characteristics from the viewpoint of quality, high output and high energy density, which characteristics cannot be practically achieved when using a Ni-rich LNMC positive electrode material.
More specifically, since an on-vehicle battery is used at a constant power, it is impossible to use an on-vehicle battery up to a considerable discharge depth.
A mixed battery can initially prevent a decrease in output due to the mixed potential, but shows a decrease in output as the number of charge-discharge cycles increases since the reaction site is concentrated on an active material having low resistance.
Date Recue/Date Received 2021-03-31
3 A lithium battery with improved properties, while avoiding the drawbacks of the preceding examples, for an on-vehicle battery is thus desirable.
SUMMARY OF THE INVENTION
An object of the invention is to provide a lithium secondary battery positive electrode material that can achieve the high energy density and high output required for on-vehicle applications, and can be applicable to mass production.
In one aspect, the positive electrode material is a composite lithium material which includes a first lithium compound in the form of particles, a thin layer of a second lithium compound and a carbon material layer in between. More specifically, the positive electrode material is a composite lithium material comprising a first lithium compound in the form of particles; a first carbon material layer present on an entire surface of the first lithium compound particles; a second lithium compound forming a thin-film layer on part or the entirety of a surface of the first carbon material layer; and a second carbon material layer present on an entire surface of the thin-film layer of the second lithium compound; wherein the carbon material of the first and second carbon material layers is independently selected from amorphous carbon material, graphene-structured carbon material, or a combination thereof; wherein the first lithium compound comprises a layered lithium compound, a spinel-type lithium compound, or a combination thereof; wherein the second lithium compound comprises a lithium-containing phosphate compound, a lithium-containing silicate compound, or a combination thereof; and wherein the first and second lithium compounds are not in direct physical contact.
The first lithium compound comprises at least one compound selected from a layered lithium compound, a spinel-type lithium compound or a combination thereof. The layered lithium compound may be a-layered Li(Nia/Mnp/Coy)02 (wherein a+p+y=1). The spinel-type lithium compound may be spinel-type LiNisMnE04 (wherein O+E=2). A compound that includes an element among the Date Recue/Date Received 2021-03-31 3a elements of groups 3 to 6 of the periodic table, or an oxide thereof, or an aluminum halide compound may be present on the surface of the particles of the layered lithium compound and/or spinel-type lithium compound. For example, an element within groups 3 to 6 of the periodic table may be selected from aluminum, molybdenum, titanium, zirconium, and sulfur.
Note that the expression "a+p-Fy=1" means that the total number of moles of Ni, Mn, and Co atoms is 1, and the expression "O-FE=2" means that the total number of moles of Ni and Mn atoms is 2. The above definition is similarly applied to the expressions "-Fn-Fe=1" and "i+K+A=1" below. It the foregoing definitions, each of Date Recue/Date Received 2021-03-31
SUMMARY OF THE INVENTION
An object of the invention is to provide a lithium secondary battery positive electrode material that can achieve the high energy density and high output required for on-vehicle applications, and can be applicable to mass production.
In one aspect, the positive electrode material is a composite lithium material which includes a first lithium compound in the form of particles, a thin layer of a second lithium compound and a carbon material layer in between. More specifically, the positive electrode material is a composite lithium material comprising a first lithium compound in the form of particles; a first carbon material layer present on an entire surface of the first lithium compound particles; a second lithium compound forming a thin-film layer on part or the entirety of a surface of the first carbon material layer; and a second carbon material layer present on an entire surface of the thin-film layer of the second lithium compound; wherein the carbon material of the first and second carbon material layers is independently selected from amorphous carbon material, graphene-structured carbon material, or a combination thereof; wherein the first lithium compound comprises a layered lithium compound, a spinel-type lithium compound, or a combination thereof; wherein the second lithium compound comprises a lithium-containing phosphate compound, a lithium-containing silicate compound, or a combination thereof; and wherein the first and second lithium compounds are not in direct physical contact.
The first lithium compound comprises at least one compound selected from a layered lithium compound, a spinel-type lithium compound or a combination thereof. The layered lithium compound may be a-layered Li(Nia/Mnp/Coy)02 (wherein a+p+y=1). The spinel-type lithium compound may be spinel-type LiNisMnE04 (wherein O+E=2). A compound that includes an element among the Date Recue/Date Received 2021-03-31 3a elements of groups 3 to 6 of the periodic table, or an oxide thereof, or an aluminum halide compound may be present on the surface of the particles of the layered lithium compound and/or spinel-type lithium compound. For example, an element within groups 3 to 6 of the periodic table may be selected from aluminum, molybdenum, titanium, zirconium, and sulfur.
Note that the expression "a+p-Fy=1" means that the total number of moles of Ni, Mn, and Co atoms is 1, and the expression "O-FE=2" means that the total number of moles of Ni and Mn atoms is 2. The above definition is similarly applied to the expressions "-Fn-Fe=1" and "i+K+A=1" below. It the foregoing definitions, each of Date Recue/Date Received 2021-03-31
4 a, 13, y, 5, C, 8, I, K, and A may be a positive integer (i.e. a whole number), a positive fraction, or may be zero (0), given that the given formula in which it appears is satisfied.
The second lithium compound comprises at least one compound selected from a lithium-containing phosphate compound, a lithium-containing silicate compound and combinations thereof. The lithium-containing phosphate compound may be of olivine-type Li(Fe4/Con/Mne)PO4 (wherein -Fri+e=1). The lithium-containing silicate compound may be Li(FejCoK/Mn)SiO4. (wherein i+K+A=1).
A carbon material layer selected from an amorphous carbon material layer, a graphene-structured carbon material layer or a combination thereof is present on the entire surface of the first lithium compound and the second lithium compound.
The first lithium compound is in the form of particles, and the second lithium compound forms a thin-film layer on part or the entirety of the carbon material layer surface of the covered first lithium compound particles. According to one aspect, a second carbon material layer is present on the entire surface of the second lithium compound opposite to the surface in contact with the carbon material layer covering the first lithium compound particles.
The lithium secondary battery positive electrode material may further include a conductive carbon material, together with the first lithium compound and the second lithium compound that are entirely covered with the carbon material layer, and the second carbon material layer and the surface layer of the conductive carbon material may be fusion-bonded.
According to another aspect, the invention provides a lithium secondary battery comprising at least one lithium secondary battery positive electrode as defined in any of the foregoing embodiments, at least one lithium secondary battery negative electrode, at least one separator between positive and negative electrodes, and an electrolyte.
For instance, the invention provides a lithium secondary battery positive electrode material adapted for use in the production of a positive electrode of a lithium secondary battery. The battery is configured in such a manner that at least one positive electrode and at least one negative electrode are wound or
The second lithium compound comprises at least one compound selected from a lithium-containing phosphate compound, a lithium-containing silicate compound and combinations thereof. The lithium-containing phosphate compound may be of olivine-type Li(Fe4/Con/Mne)PO4 (wherein -Fri+e=1). The lithium-containing silicate compound may be Li(FejCoK/Mn)SiO4. (wherein i+K+A=1).
A carbon material layer selected from an amorphous carbon material layer, a graphene-structured carbon material layer or a combination thereof is present on the entire surface of the first lithium compound and the second lithium compound.
The first lithium compound is in the form of particles, and the second lithium compound forms a thin-film layer on part or the entirety of the carbon material layer surface of the covered first lithium compound particles. According to one aspect, a second carbon material layer is present on the entire surface of the second lithium compound opposite to the surface in contact with the carbon material layer covering the first lithium compound particles.
The lithium secondary battery positive electrode material may further include a conductive carbon material, together with the first lithium compound and the second lithium compound that are entirely covered with the carbon material layer, and the second carbon material layer and the surface layer of the conductive carbon material may be fusion-bonded.
According to another aspect, the invention provides a lithium secondary battery comprising at least one lithium secondary battery positive electrode as defined in any of the foregoing embodiments, at least one lithium secondary battery negative electrode, at least one separator between positive and negative electrodes, and an electrolyte.
For instance, the invention provides a lithium secondary battery positive electrode material adapted for use in the production of a positive electrode of a lithium secondary battery. The battery is configured in such a manner that at least one positive electrode and at least one negative electrode are wound or
5 stacked through separators, and are infiltrated with or immersed in an organic electrolyte solution so that insertion and extraction of lithium ions occur repeatedly.
According to a further aspect, the invention provides a method for the manufacture of a lithium secondary battery positive electrode material comprising the steps of a) providing particles of a first lithium compound, e.g. selected from a layered lithium compound, a spinel-type lithium compound, and combinations thereof; b) forming a first carbon material layer on the particles provided in (a), the carbon material being preferably selected from an amorphous carbon material layer, a graphene-structured carbon material layer, or a combination thereof, to provide carbon-coated particles; c) forming a thin film layer of a second lithium compound on part or the entirety of the carbon-coated particles provided in step (b), the second lithium compound being selected from, e.g. a lithium-containing phosphate compound, a lithium-containing silicate compound, and combinations thereof; and d) coating the thin film layer of the second lithium compound with a second carbon material layer present on an entire surface, wherein the carbon material is preferably selected from an amorphous carbon material layer, a graphene-structured carbon material layer, or a combination thereof.
According to yet another aspect, the invention provides a method for the manufacture of a lithium secondary battery. According to yet another aspect, the invention also contemplates the use of a lithium secondary battery of the invention in replacement of lithium-ion batteries and in systems demanding high energy rechargeable batteries, and for example, as industrial batteries, as on-vehicle batteries (e.g. electric or hybrid vehicles), and in ubiquitous IT
devices.
According to a further aspect, the invention provides a method for the manufacture of a lithium secondary battery positive electrode material comprising the steps of a) providing particles of a first lithium compound, e.g. selected from a layered lithium compound, a spinel-type lithium compound, and combinations thereof; b) forming a first carbon material layer on the particles provided in (a), the carbon material being preferably selected from an amorphous carbon material layer, a graphene-structured carbon material layer, or a combination thereof, to provide carbon-coated particles; c) forming a thin film layer of a second lithium compound on part or the entirety of the carbon-coated particles provided in step (b), the second lithium compound being selected from, e.g. a lithium-containing phosphate compound, a lithium-containing silicate compound, and combinations thereof; and d) coating the thin film layer of the second lithium compound with a second carbon material layer present on an entire surface, wherein the carbon material is preferably selected from an amorphous carbon material layer, a graphene-structured carbon material layer, or a combination thereof.
According to yet another aspect, the invention provides a method for the manufacture of a lithium secondary battery. According to yet another aspect, the invention also contemplates the use of a lithium secondary battery of the invention in replacement of lithium-ion batteries and in systems demanding high energy rechargeable batteries, and for example, as industrial batteries, as on-vehicle batteries (e.g. electric or hybrid vehicles), and in ubiquitous IT
devices.
6 BRIEF DESCRIPTION OF DRAWINGS
Figure 1 is a schematic view illustrating an example of a positive electrode material according to the invention.
Figure 2 is an enlarged view of area A from Figure 1.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
It is considered that previous Li(Ni/Mn/Co)02/LiFePO4 mixed batteries show a decrease in output since the crystal structure of Li(Ni/Mn/Co)02 deteriorates, and the network of the conductive material is destroyed (i.e., reaction sites become non-uniform) as the number of charge-discharge cycles increases.
Specifically, an oxide having a layered structure (e.g., Li(Ni/Mn/Co)02) or a spinel-type compound allow repeated insertion and extraction of lithium ions to achieve charge and discharge. In contrast, a phosphate compound (e.g., LiFePO4) or a silicate compound is essentially an ion-binding compound. In this case, the insertion and extraction of lithium ions is believed to occur via a mechanism that differs from that of an oxide having a layered structure or a spinel-type compound. For example, it has recently been found that LiFePO4 (powder) allows insertion and extraction of lithium ions through the crystal structure of the surface area of the powder, and the lithium ion diffusion rate inside the powder is considered relatively low.
When positive electrode materials that differ in lithium ion insertion/extraction mechanism are merely mixed, the characteristics of each positive electrode material are observed. Therefore, when implementing an on-vehicle battery for which high output is required, reaction control occurs due to LiFePO4, resulting in a decrease in output.
Date Recue/Date Received 2021-03-31
Figure 1 is a schematic view illustrating an example of a positive electrode material according to the invention.
Figure 2 is an enlarged view of area A from Figure 1.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
It is considered that previous Li(Ni/Mn/Co)02/LiFePO4 mixed batteries show a decrease in output since the crystal structure of Li(Ni/Mn/Co)02 deteriorates, and the network of the conductive material is destroyed (i.e., reaction sites become non-uniform) as the number of charge-discharge cycles increases.
Specifically, an oxide having a layered structure (e.g., Li(Ni/Mn/Co)02) or a spinel-type compound allow repeated insertion and extraction of lithium ions to achieve charge and discharge. In contrast, a phosphate compound (e.g., LiFePO4) or a silicate compound is essentially an ion-binding compound. In this case, the insertion and extraction of lithium ions is believed to occur via a mechanism that differs from that of an oxide having a layered structure or a spinel-type compound. For example, it has recently been found that LiFePO4 (powder) allows insertion and extraction of lithium ions through the crystal structure of the surface area of the powder, and the lithium ion diffusion rate inside the powder is considered relatively low.
When positive electrode materials that differ in lithium ion insertion/extraction mechanism are merely mixed, the characteristics of each positive electrode material are observed. Therefore, when implementing an on-vehicle battery for which high output is required, reaction control occurs due to LiFePO4, resulting in a decrease in output.
Date Recue/Date Received 2021-03-31
7 It was found that a battery that can, for instance, maintain high output over a wide voltage range and/or exhibit high energy density can be obtained by using an oxide having a layered structure or a spinel-type compound as a particulate first lithium compound, forming a first carbon material layer on the surface of the particulate first lithium compound, and forming a thin-film layer of a lithium-containing phosphate compound or silicate compound (second lithium compound) on the first carbon material layer. One hypothesis would include the particles of the first lithium compound serving as a reaction site in a high-voltage region, and the thin-film layer of the second lithium compound having a relatively .. low oxidation-reduction potential serving as a reaction site in a low-voltage region during charge and discharge. It was found that an on-vehicle battery can maintain high output by forming a thin-film layer of the second lithium compound so that a decrease in output does not occur, and insertion and extraction of lithium ions in the reaction site are not limited.
Figure 1 is a schematic view illustrating an example of a positive electrode material according to one embodiment of the invention. Figure 2 is an enlarged view of the area A in Figure 1.
A positive electrode material 1 is configured such that a layer of a first carbon material (amorphous and/or graphene-structured) 3a is formed on the surface of a particulate first lithium compound 2 that serves as a nucleus or core, a thin-film layer of a second lithium compound 4 is formed on the surface of the layer of carbon material 3a, and the thin-film layer of the second lithium compound 4 is further covered with a layer of carbon material 3b.
In the embodiment shown in Figure 1, the positive electrode material 1 further .. includes a conductive carbon material 5 together with the first lithium compound 2 in the form of a particle and the second lithium compound 4 in the form of a thin film that are each entirely covered with the layers of carbon material 3. The layer of carbon material 3b and the surface layer of the conductive carbon material Date Recue/Date Received 2021-03-31
Figure 1 is a schematic view illustrating an example of a positive electrode material according to one embodiment of the invention. Figure 2 is an enlarged view of the area A in Figure 1.
A positive electrode material 1 is configured such that a layer of a first carbon material (amorphous and/or graphene-structured) 3a is formed on the surface of a particulate first lithium compound 2 that serves as a nucleus or core, a thin-film layer of a second lithium compound 4 is formed on the surface of the layer of carbon material 3a, and the thin-film layer of the second lithium compound 4 is further covered with a layer of carbon material 3b.
In the embodiment shown in Figure 1, the positive electrode material 1 further .. includes a conductive carbon material 5 together with the first lithium compound 2 in the form of a particle and the second lithium compound 4 in the form of a thin film that are each entirely covered with the layers of carbon material 3. The layer of carbon material 3b and the surface layer of the conductive carbon material Date Recue/Date Received 2021-03-31
8 are fusion-bonded. The conductive carbon material 5 is at least one material selected from a conductive carbon powder 5a and a conductive carbon fiber 5b.
The conductive carbon powder 5a is preferably at least one powder selected from acetylene black, ketjen black, and a powder that partially includes a graphite crystal. The conductive carbon fiber 5b is preferably at least one fiber selected from a carbon fiber, a graphite fiber, a vapor-grown carbon fiber, a carbon nanofiber, and a carbon nanotube. The diameter of the carbon fiber is preferably 5 to 200 nm, and more preferably 10 to 100 nm. The length of the carbon fiber is preferably 100 nm to 50 pm, and more preferably Ito 30 pm.
The expression "the layers of carbon material 3b and the surface layer of the conductive carbon material 5 are fusion-bonded" means, for instance, that graphene-structured layers 6 (see Figure 2) present on the surface of the carbon material layer 3b and the surface of the conductive carbon material 5 overlap each other. This makes electrical conductivity improvements possible. The layer of the carbon material 3b and the surface layer of the conductive carbon material 5 may be fusion-bonded by mixing the carbon material 3b and the conductive carbon material 5, and calcining the mixture.
When mixing a carbon source (e.g., lactose) to effect partial graphitization, and then implementing reliable fusion bonding, it is preferable to apply a dry mechanochemical method after calcining the mixture. When a carbon source is not used, fusion bonding can be implemented by a calcination method since the calcination temperature is close to the carbon-carbon bond cleavage temperature. In contrast, it is preferable to apply a mechanochemical method when mixing a carbon source.
The average particle size of the first lithium compound particles 2 ranges from about 3 to about 15 pm. The thickness of the carbon material layer 3a formed on the surface of the particles of the first lithium compound 2 ranges from about nm to about 10 nm, and preferably from about 2 nm to about 5 nm. If the
The conductive carbon powder 5a is preferably at least one powder selected from acetylene black, ketjen black, and a powder that partially includes a graphite crystal. The conductive carbon fiber 5b is preferably at least one fiber selected from a carbon fiber, a graphite fiber, a vapor-grown carbon fiber, a carbon nanofiber, and a carbon nanotube. The diameter of the carbon fiber is preferably 5 to 200 nm, and more preferably 10 to 100 nm. The length of the carbon fiber is preferably 100 nm to 50 pm, and more preferably Ito 30 pm.
The expression "the layers of carbon material 3b and the surface layer of the conductive carbon material 5 are fusion-bonded" means, for instance, that graphene-structured layers 6 (see Figure 2) present on the surface of the carbon material layer 3b and the surface of the conductive carbon material 5 overlap each other. This makes electrical conductivity improvements possible. The layer of the carbon material 3b and the surface layer of the conductive carbon material 5 may be fusion-bonded by mixing the carbon material 3b and the conductive carbon material 5, and calcining the mixture.
When mixing a carbon source (e.g., lactose) to effect partial graphitization, and then implementing reliable fusion bonding, it is preferable to apply a dry mechanochemical method after calcining the mixture. When a carbon source is not used, fusion bonding can be implemented by a calcination method since the calcination temperature is close to the carbon-carbon bond cleavage temperature. In contrast, it is preferable to apply a mechanochemical method when mixing a carbon source.
The average particle size of the first lithium compound particles 2 ranges from about 3 to about 15 pm. The thickness of the carbon material layer 3a formed on the surface of the particles of the first lithium compound 2 ranges from about nm to about 10 nm, and preferably from about 2 nm to about 5 nm. If the
9 thickness of the carbon material layer 3a exceeds 10 nm, lithium ions may not be sufficiently diffused into the surface of the active material, i.e. at the reaction site.
As a result, the output characteristics of the lithium battery may deteriorate. The thickness of the second lithium compound layer 4 is, for example, within the .. range of about 50 nm to about 300 nm.
The first lithium compound 2 is a particulate compound that serves as a nucleus, or core, for the electrode material. The first lithium compound is preferably a layered lithium compound, a spinel-type lithium compound, or a mixture of a layered lithium compound and a spinel-type lithium compound.
For example, the layered lithium compound is an intercalation compound in which lithium is incorporated in a molecular host in which Co02 sheets formed by ridge sharing of Co06 octahedrons are stacked. The layered lithium compound that may be used in connection with the embodiments of the invention is represented by a-layered Li(Ni/Mn/Co)02, wherein a-F13+y=1.
The spinel-type lithium compound may be a lithium-containing metal oxide having a spinel structure, for example, represented by LiNi6Mn104, wherein O-FE=2.
Specific examples of the layered lithium compound and the spinel-type lithium compound include LiCo02, Li(Ni/Mn/Co)02, Li(Ni0.6/Mn1 6)04, LiMn204, Li2M03-LiM02 (wherein M=Ni, Co, or Mn) (solid solution), and the like. For instance, the use of Li(Ni/Mn/Co)02 or Li(Ni0.6/Mn1.6)04 may be preferred from a viewpoint of electrochemical characteristics, safety, and cost.
In one embodiment, a compound including an element selected from the elements of groups 3 to 6 of the periodic table of elements, or an oxide thereof, or an aluminum halide compound is present on the surface of the particles of the .. first lithium compound, e.g. layered or spinel-type lithium compound. When the above compound is present in the crystal lattice site of the surface of the layered lithium or spinel-type lithium compound, the resistance of Mn-based material can be reduced. Compounds containing an element selected from groups 3 to 6 of the periodic table of elements are, for example, compounds that include an element selected from Al, Mo, Ti, Zr, and S. Examples of aluminum halide compounds include aluminum fluoride. Preferably, the surface of the particles of 5 the layered lithium or spinel-type lithium compound is doped with aluminum fluoride or the like in a ratio of about 1% to about 3 % (by weight).
The second lithium compound 4 forms a thin film on the surface of the particles of the first lithium compound 2 through the layer of carbon material 3a. The second lithium compound is, for example, a lithium-containing phosphate compound, a
As a result, the output characteristics of the lithium battery may deteriorate. The thickness of the second lithium compound layer 4 is, for example, within the .. range of about 50 nm to about 300 nm.
The first lithium compound 2 is a particulate compound that serves as a nucleus, or core, for the electrode material. The first lithium compound is preferably a layered lithium compound, a spinel-type lithium compound, or a mixture of a layered lithium compound and a spinel-type lithium compound.
For example, the layered lithium compound is an intercalation compound in which lithium is incorporated in a molecular host in which Co02 sheets formed by ridge sharing of Co06 octahedrons are stacked. The layered lithium compound that may be used in connection with the embodiments of the invention is represented by a-layered Li(Ni/Mn/Co)02, wherein a-F13+y=1.
The spinel-type lithium compound may be a lithium-containing metal oxide having a spinel structure, for example, represented by LiNi6Mn104, wherein O-FE=2.
Specific examples of the layered lithium compound and the spinel-type lithium compound include LiCo02, Li(Ni/Mn/Co)02, Li(Ni0.6/Mn1 6)04, LiMn204, Li2M03-LiM02 (wherein M=Ni, Co, or Mn) (solid solution), and the like. For instance, the use of Li(Ni/Mn/Co)02 or Li(Ni0.6/Mn1.6)04 may be preferred from a viewpoint of electrochemical characteristics, safety, and cost.
In one embodiment, a compound including an element selected from the elements of groups 3 to 6 of the periodic table of elements, or an oxide thereof, or an aluminum halide compound is present on the surface of the particles of the .. first lithium compound, e.g. layered or spinel-type lithium compound. When the above compound is present in the crystal lattice site of the surface of the layered lithium or spinel-type lithium compound, the resistance of Mn-based material can be reduced. Compounds containing an element selected from groups 3 to 6 of the periodic table of elements are, for example, compounds that include an element selected from Al, Mo, Ti, Zr, and S. Examples of aluminum halide compounds include aluminum fluoride. Preferably, the surface of the particles of 5 the layered lithium or spinel-type lithium compound is doped with aluminum fluoride or the like in a ratio of about 1% to about 3 % (by weight).
The second lithium compound 4 forms a thin film on the surface of the particles of the first lithium compound 2 through the layer of carbon material 3a. The second lithium compound is, for example, a lithium-containing phosphate compound, a
10 lithium-containing silicate compound, or a mixture of a lithium-containing phosphate compound and a lithium-containing silicate compound. For example, a lithium-containing phosphate compound may be represented by olivine-type Li(Fe/Con/Mne)PO4 (wherein +r-I-F6=1). A lithium-containing silicate compound may be represented by, for instance, Li(Fel/CoK/MnA)SiO4 (wherein i+k+A=1).
Specific examples of such compounds include LiFePO4, LiCoPO4, LiMnPO4, LiFedVinePO4 (wherein +=i), and the like. Among these, LiFePO4 is preferable from the viewpoint of the effects achieved when used in combination with the first lithium compound.
Examples of a combination of the first lithium compound and the second lithium compound include a combination of Li(Nia/Mnp/Coy)02 (wherein a+13+y=1) and LiFePO4, a combination of Li(Ni0.5/Mn1.5)04 and LiFePO4, a combination of Li(Nia/Mnp/Coy)02 (wherein a+6+y=1) and Li(Fe4/Mne)PO4 (wherein -F0=1), a combination of Li(Nio 5/Mni.5)04 and Li(Fe4Mne)PO4 (wherein -F6=1), and the like.
The entire surface of the first lithium compound and the second lithium compound is covered with the carbon material layer (amorphous and/or graphene-structured carbon). Specifically, the first lithium compound and the second lithium compound do not come in direct physical contact with each other
Specific examples of such compounds include LiFePO4, LiCoPO4, LiMnPO4, LiFedVinePO4 (wherein +=i), and the like. Among these, LiFePO4 is preferable from the viewpoint of the effects achieved when used in combination with the first lithium compound.
Examples of a combination of the first lithium compound and the second lithium compound include a combination of Li(Nia/Mnp/Coy)02 (wherein a+13+y=1) and LiFePO4, a combination of Li(Ni0.5/Mn1.5)04 and LiFePO4, a combination of Li(Nia/Mnp/Coy)02 (wherein a+6+y=1) and Li(Fe4/Mne)PO4 (wherein -F0=1), a combination of Li(Nio 5/Mni.5)04 and Li(Fe4Mne)PO4 (wherein -F6=1), and the like.
The entire surface of the first lithium compound and the second lithium compound is covered with the carbon material layer (amorphous and/or graphene-structured carbon). Specifically, the first lithium compound and the second lithium compound do not come in direct physical contact with each other
11 (i.e. physically isolated), but are in indirect contact with each other through the first carbon material layer.
Examples of methods for forming the second lithium compound layer on the surface of the first lithium compound that is covered with the carbon material layer include a vacuum CVD method, a wet sal-gel method, a dry mechanochemical method, a mechanofusion method, and the like.
Examples of negative electrode materials for the lithium battery include artificial graphite, composite negative electrode materials which include metallic silicon, and the like. A high capacity, high regeneration, and a long lifetime may be implemented by utilizing a negative electrode material prepared by coating the surface of a silicon oxide powder that includes metallic silicon with conductive carbon, forming a composite of the resulting powder and a graphitic powder (artificial graphite or graphitizable powder) of which the surface is coated with conductive carbon, and bonding the composite and conductive carbon (e.g., acetylene black or carbon nanotubes).
A separator is provided between the positive electrode and the negative electrode to electrically insulate the two electrodes from each other, and to retain the electrolyte solution. The separator includes, for example, a synthetic resin film, a separator formed of fibers or inorganic fibers, and the like. Specific examples of separators include a polyethylene film, a polypropylene film, a polyethylene woven fabric, a polyethylene nonwoven fabric, a polypropylene woven fabric, a polypropylene nonwoven fabric, a separator formed of glass fibers, a separator formed of cellulose fibers, a separator formed of polyethylene terephthalate fibers, and the like.
A non-aqueous electrolyte solution which includes a lithium salt, an ion-conductive polymer, or the like is preferably used as the electrolyte solution of the lithium secondary battery in which the positive electrode and the negative
Examples of methods for forming the second lithium compound layer on the surface of the first lithium compound that is covered with the carbon material layer include a vacuum CVD method, a wet sal-gel method, a dry mechanochemical method, a mechanofusion method, and the like.
Examples of negative electrode materials for the lithium battery include artificial graphite, composite negative electrode materials which include metallic silicon, and the like. A high capacity, high regeneration, and a long lifetime may be implemented by utilizing a negative electrode material prepared by coating the surface of a silicon oxide powder that includes metallic silicon with conductive carbon, forming a composite of the resulting powder and a graphitic powder (artificial graphite or graphitizable powder) of which the surface is coated with conductive carbon, and bonding the composite and conductive carbon (e.g., acetylene black or carbon nanotubes).
A separator is provided between the positive electrode and the negative electrode to electrically insulate the two electrodes from each other, and to retain the electrolyte solution. The separator includes, for example, a synthetic resin film, a separator formed of fibers or inorganic fibers, and the like. Specific examples of separators include a polyethylene film, a polypropylene film, a polyethylene woven fabric, a polyethylene nonwoven fabric, a polypropylene woven fabric, a polypropylene nonwoven fabric, a separator formed of glass fibers, a separator formed of cellulose fibers, a separator formed of polyethylene terephthalate fibers, and the like.
A non-aqueous electrolyte solution which includes a lithium salt, an ion-conductive polymer, or the like is preferably used as the electrolyte solution of the lithium secondary battery in which the positive electrode and the negative
12 electrode are immersed. An ion-conductive solid polymer layer may also replace the separator and electrolyte solution in a solid state battery.
Examples of the non-aqueous solvent included in the non-aqueous electrolyte solution that includes a lithium salt include ethylene carbonate (EC), propylene carbonate (PC), diethyl carbonate (DEC), dimethyl carbonate (DMC), methylethyl carbonate (MEC), and the like, or a combination of two or more of any of the foregoing non-aqueous solvents.
Examples of lithium salts which can be dissolved in the non-aqueous solvent include lithium hexafluorophosphate (LiPF6), lithium tetrafluoroborate (LiBF4), lithium trifluoromethanesulfonate (LiSO3CF3), and the like, or combinations thereof.
The lithium secondary battery electrode material according to one embodiment of the invention may include a binder which is physically and chemically stable in the battery's internal conditions. Examples of binders include fluorine-containing resins such as polytetrafluoroethylene, polyvinylidene fluoride, and fluororubber, and thermoplastic resins such as polypropylene and polyethylene. Further examples of binders include acrylic resin materials, styrene-butadiene-based materials, and the like.
The lithium secondary battery electrode includes the above electrode material and an optional additional member. Examples of such additional member include a collector to collect current from the electrode material. Examples of collectors include a thin metal film. A positive electrode collector is, for example, an aluminum foil. A negative electrode collector is, for example, a copper foil.
Since the first lithium compound on which the first carbon material layer (amorphous and/or graphene-structured) is present is in the form of particles, and the second lithium compound forms a thin-film layer on part or the entirety of the surface of the particles of the first lithium compound, the particles of the first
Examples of the non-aqueous solvent included in the non-aqueous electrolyte solution that includes a lithium salt include ethylene carbonate (EC), propylene carbonate (PC), diethyl carbonate (DEC), dimethyl carbonate (DMC), methylethyl carbonate (MEC), and the like, or a combination of two or more of any of the foregoing non-aqueous solvents.
Examples of lithium salts which can be dissolved in the non-aqueous solvent include lithium hexafluorophosphate (LiPF6), lithium tetrafluoroborate (LiBF4), lithium trifluoromethanesulfonate (LiSO3CF3), and the like, or combinations thereof.
The lithium secondary battery electrode material according to one embodiment of the invention may include a binder which is physically and chemically stable in the battery's internal conditions. Examples of binders include fluorine-containing resins such as polytetrafluoroethylene, polyvinylidene fluoride, and fluororubber, and thermoplastic resins such as polypropylene and polyethylene. Further examples of binders include acrylic resin materials, styrene-butadiene-based materials, and the like.
The lithium secondary battery electrode includes the above electrode material and an optional additional member. Examples of such additional member include a collector to collect current from the electrode material. Examples of collectors include a thin metal film. A positive electrode collector is, for example, an aluminum foil. A negative electrode collector is, for example, a copper foil.
Since the first lithium compound on which the first carbon material layer (amorphous and/or graphene-structured) is present is in the form of particles, and the second lithium compound forms a thin-film layer on part or the entirety of the surface of the particles of the first lithium compound, the particles of the first
13 lithium compound serve as a reaction site in a high-voltage region, and the thin-film layer of the second lithium compound having a relatively low oxidation-reduction potential serves as a reaction site in a low-voltage region during charge and discharge. Therefore, it is possible to implement a battery including a lithium secondary battery positive electrode material according to one aspect of the invention which can maintain high output over a wide voltage range, and exhibits high energy density.
When a compound which includes an element among the elements of groups 3 to 6 in the periodic table, or an oxide thereof, or an aluminum halide compound is present on the surface of the particles of the first lithium compound, it is possible to reduce the resistance of a Mn-based material, and potentially prevent a situation in which the first lithium compound would crystallize or break during charge and discharge due to an increase in voltage.
When the lithium secondary battery positive electrode material further includes a conductive carbon material together with the first lithium compound and the second lithium compound that are entirely covered with the first and second carbon material layers (amorphous and/or graphene-structured carbon), and the second carbon material layer and the surface layer of the conductive carbon material are fusion-bonded, it is possible to prevent the destruction of the electronic conduction network due to expansion and contraction of the electrode during charge and discharge, thereby achieving a long lifetime. The olivine-type material does not easily undergo deoxidation, and may significantly contribute to preventing thermal runaway of a battery, thereby improving the safety of the lithium secondary battery.
The following examples are for illustrative purposes and should not be construed as further limiting the scope of the invention.
Date Recue/Date Received 2021-03-31
When a compound which includes an element among the elements of groups 3 to 6 in the periodic table, or an oxide thereof, or an aluminum halide compound is present on the surface of the particles of the first lithium compound, it is possible to reduce the resistance of a Mn-based material, and potentially prevent a situation in which the first lithium compound would crystallize or break during charge and discharge due to an increase in voltage.
When the lithium secondary battery positive electrode material further includes a conductive carbon material together with the first lithium compound and the second lithium compound that are entirely covered with the first and second carbon material layers (amorphous and/or graphene-structured carbon), and the second carbon material layer and the surface layer of the conductive carbon material are fusion-bonded, it is possible to prevent the destruction of the electronic conduction network due to expansion and contraction of the electrode during charge and discharge, thereby achieving a long lifetime. The olivine-type material does not easily undergo deoxidation, and may significantly contribute to preventing thermal runaway of a battery, thereby improving the safety of the lithium secondary battery.
The following examples are for illustrative purposes and should not be construed as further limiting the scope of the invention.
Date Recue/Date Received 2021-03-31
14 EXAMPLES
Example 1 Li(Ni1/3/C01/3/Mn1/3)02 was provided as the lithium secondary battery positive electrode material. Li(Ni1/3/C01/3/Mn1/3)02 was in the form of particles having an average particle size of 5 to 8 pm, and ceramic particles (e.g., AlF3) were provided on the surface of the Li(Nii/3/Coi/3/Mni/3)02 particles in order to prevent generation of gas and the like.
The surface of the Li(Ni1i3/C01/3/Mn1/3)02 particles was coated with a graphitizable resin, and calcined at 400 to 500 C (at which the compound did not decompose) to cover the surface of the Li(Nii/3/Cov3/Mni/3)02 particles with an amorphous carbon layer having a thickness of 2 to 5 nm.
A LiFePO4 thin film was formed on the surface of the amorphous carbon layer by a solid-phase method by heating iron oxalate and lithium phosphate at 600 to 650 C in an argon gas atmosphere under normal pressure to produce a composite lithium material. The thickness of the thin film was 200 nm, and the ratio of the thin film was 20 % (by weight).
An amount of 84 parts by weight of the composite lithium material, and a mixture of 8 parts by weight of conductive carbon and 2 parts by weight of conductive carbon fibers (conductive material), were mixed in a lactose aqueous solution, dried, and calcined at 400 to 500 C. The surface layer of the composite lithium material and the surface layer of the conductive material were then fusion-bonded by mechanofusion, using the heat generated by shear forces between powders at the carbon material interface.
An amount of 6 parts by weight of polyvinylidene fluoride (binder) was added to the resulting positive electrode material. After the addition of N-methylpyrrolidone (dispersion solvent), the mixture was kneaded to prepare a positive electrode slurry. The slurry was applied to an aluminum foil having a thickness of 20 pm to obtain a positive electrode having a thickness of 160 pm (including the aluminum foil).
A negative electrode provided opposite to the positive electrode was obtained as described below. A negative electrode material (artificial graphite), a conductive 5 material, a carboxymethyl cellulose (CMC) aqueous solution, and a styrene-butadiene-based material (SBR) solution (binder) were mixed to prepare a slurry.
The slurry was applied to a 10 pm copper foil to obtain a negative electrode having a thickness of 100 pm (including the copper foil).
The positive electrode and the negative electrode were cut to predetermined dimensions. Five positive electrodes and six negative electrodes were stacked, nonwoven fabric separators separating each of the positive and negative electrodes. After welding a terminal, the electrodes were wrapped with a laminate film to obtain a laminated battery. A solution prepared by dissolving lithium hexafluorophosphate (LiPF6) in a solvent mixture containing ethylene
Example 1 Li(Ni1/3/C01/3/Mn1/3)02 was provided as the lithium secondary battery positive electrode material. Li(Ni1/3/C01/3/Mn1/3)02 was in the form of particles having an average particle size of 5 to 8 pm, and ceramic particles (e.g., AlF3) were provided on the surface of the Li(Nii/3/Coi/3/Mni/3)02 particles in order to prevent generation of gas and the like.
The surface of the Li(Ni1i3/C01/3/Mn1/3)02 particles was coated with a graphitizable resin, and calcined at 400 to 500 C (at which the compound did not decompose) to cover the surface of the Li(Nii/3/Cov3/Mni/3)02 particles with an amorphous carbon layer having a thickness of 2 to 5 nm.
A LiFePO4 thin film was formed on the surface of the amorphous carbon layer by a solid-phase method by heating iron oxalate and lithium phosphate at 600 to 650 C in an argon gas atmosphere under normal pressure to produce a composite lithium material. The thickness of the thin film was 200 nm, and the ratio of the thin film was 20 % (by weight).
An amount of 84 parts by weight of the composite lithium material, and a mixture of 8 parts by weight of conductive carbon and 2 parts by weight of conductive carbon fibers (conductive material), were mixed in a lactose aqueous solution, dried, and calcined at 400 to 500 C. The surface layer of the composite lithium material and the surface layer of the conductive material were then fusion-bonded by mechanofusion, using the heat generated by shear forces between powders at the carbon material interface.
An amount of 6 parts by weight of polyvinylidene fluoride (binder) was added to the resulting positive electrode material. After the addition of N-methylpyrrolidone (dispersion solvent), the mixture was kneaded to prepare a positive electrode slurry. The slurry was applied to an aluminum foil having a thickness of 20 pm to obtain a positive electrode having a thickness of 160 pm (including the aluminum foil).
A negative electrode provided opposite to the positive electrode was obtained as described below. A negative electrode material (artificial graphite), a conductive 5 material, a carboxymethyl cellulose (CMC) aqueous solution, and a styrene-butadiene-based material (SBR) solution (binder) were mixed to prepare a slurry.
The slurry was applied to a 10 pm copper foil to obtain a negative electrode having a thickness of 100 pm (including the copper foil).
The positive electrode and the negative electrode were cut to predetermined dimensions. Five positive electrodes and six negative electrodes were stacked, nonwoven fabric separators separating each of the positive and negative electrodes. After welding a terminal, the electrodes were wrapped with a laminate film to obtain a laminated battery. A solution prepared by dissolving lithium hexafluorophosphate (LiPF6) in a solvent mixture containing ethylene
15 carbonate (EC), dimethyl carbonate (DMC), and diethyl carbonate (DEC) at a concentration of 1 mol/L was used as electrolyte solution. A polyethylene (PE) resin film having a thickness of 40 pm was used as separator. After injecting the electrolyte solution, the laminate film was sealed by welding, and the battery was charged to obtain a 3.6 V-700 mAh lithium battery.
A cycle test was performed using the resulting battery (1 cycle: 1.5 W
constant-power discharge, 2.5 V cut-off, and 4.1 V (700 mA) CC/CV charge). Table 1 shows the measurement results for the ratio (Wh retention ratio) of the 1000th cycle Wh capacity to the initial Wh capacity.
Example 2 A positive electrode was produced in the same manner as in Example 1, except that Li(Ni0.6/Mn1.6)04 was used instead of Li(Nii/3/Coi/3/Mni/3)02. A
laminated lithium battery was produced as in Example 1 using the resulting positive
A cycle test was performed using the resulting battery (1 cycle: 1.5 W
constant-power discharge, 2.5 V cut-off, and 4.1 V (700 mA) CC/CV charge). Table 1 shows the measurement results for the ratio (Wh retention ratio) of the 1000th cycle Wh capacity to the initial Wh capacity.
Example 2 A positive electrode was produced in the same manner as in Example 1, except that Li(Ni0.6/Mn1.6)04 was used instead of Li(Nii/3/Coi/3/Mni/3)02. A
laminated lithium battery was produced as in Example 1 using the resulting positive
16 electrode and a negative electrode also produced as in Example 1. The resulting lithium battery was a 4.5 V-600 mAh lithium battery.
A cycle test was performed using the resulting battery (1 cycle: 3.0 W
constant-power discharge, 2.7 V cut-off, and 4.8 V (600 mA) CC/CV charge). Table 1 shows the measurement results for the ratio (Wh retention ratio) of the 1000th cycle Wh capacity to the initial Wh capacity.
Comparative Example 1 The surface of Li(Ni/Co/Mn)02 particles was covered with the amorphous carbon layer in the same manner as in Example 1. A LiFePO4 powder was provided, and was merely mixed with the Li(Ni/Co/Mn)02 particles and the conductive material to obtain a positive electrode. The mixing ratio (weight ratio) of each component was the same as that employed in Example 1. A laminated lithium battery was produced in the same manner as in Example 1 using the resulting positive electrode and a negative electrode that was produced in the same manner as for Example 1. The resulting lithium battery was a 3.8 V-700 mAh lithium battery.
A cycle test was performed in the same manner as Example 1 using the resulting battery. Table 1 shows the measurement results for the ratio (Wh retention ratio) of the 1000th cycle Wh capacity to the initial Wh capacity.
Comparative Example 2 The surface of Li(Ni05/Mn1.5)04 particles was covered with an amorphous carbon layer in the manner accomplished in Example 1. A LiFePO4 powder was provided, and was merely mixed with the LiNi0.5/Mn1.504 particles and the conductive material to obtain a positive electrode material. The mixing ratio (weight ratio) of each component was the same as that employed in Example 2.
A laminated lithium battery was produced in the same manner as in Example 1 using the resulting positive electrode and a negative electrode that was also
A cycle test was performed using the resulting battery (1 cycle: 3.0 W
constant-power discharge, 2.7 V cut-off, and 4.8 V (600 mA) CC/CV charge). Table 1 shows the measurement results for the ratio (Wh retention ratio) of the 1000th cycle Wh capacity to the initial Wh capacity.
Comparative Example 1 The surface of Li(Ni/Co/Mn)02 particles was covered with the amorphous carbon layer in the same manner as in Example 1. A LiFePO4 powder was provided, and was merely mixed with the Li(Ni/Co/Mn)02 particles and the conductive material to obtain a positive electrode. The mixing ratio (weight ratio) of each component was the same as that employed in Example 1. A laminated lithium battery was produced in the same manner as in Example 1 using the resulting positive electrode and a negative electrode that was produced in the same manner as for Example 1. The resulting lithium battery was a 3.8 V-700 mAh lithium battery.
A cycle test was performed in the same manner as Example 1 using the resulting battery. Table 1 shows the measurement results for the ratio (Wh retention ratio) of the 1000th cycle Wh capacity to the initial Wh capacity.
Comparative Example 2 The surface of Li(Ni05/Mn1.5)04 particles was covered with an amorphous carbon layer in the manner accomplished in Example 1. A LiFePO4 powder was provided, and was merely mixed with the LiNi0.5/Mn1.504 particles and the conductive material to obtain a positive electrode material. The mixing ratio (weight ratio) of each component was the same as that employed in Example 2.
A laminated lithium battery was produced in the same manner as in Example 1 using the resulting positive electrode and a negative electrode that was also
17 produced in the same manner as for Example 1. The resulting lithium battery was a 4.1 V-500 mAh lithium battery.
A cycle test was performed in the same manner as in Example 1 using the resulting battery. Table 1 shows the measurement results for the ratio (Wh retention ratio) of the 1000th cycle Wh capacity to the initial Wh capacity.
TABLE 1. Ratio (%) of Wh capacity at 1000th cylcle to initial Wh capacity Example Comparative Example Wh retention ratio (%) 96 92 73 66 The results shown in Table 1 confirmed that the lithium batteries of Examples and 2 in which the LiFePO4 thin film was formed on the surface of the core material, could maintain a mixed potential continuity without showing reaction control due to LiFePO4, as compared with the lithium batteries of Comparative Examples 1 and 2 in which the electrode materials were merely mixed in the same mixing ratio. The lithium batteries of Comparative Examples 1 and 2 could initially prevent a decrease in output (SOC) due to the mixed potential, but showed a decrease in output as the crystal structure of Li(Ni/Mn/Co)02 deteriorated, and the network of the conductive material was destroyed (i.e., reaction sites became non-uniform) as the number of charge-discharge cycles increased. As a result, the mixed potential continuity was lost, and a decrease in output occurred.
Similar effects were obtained when using a layered compound having a different element mixing ratio, or using an olivine-type compound including Co and/or Mn instead of Fe, or using a silicic acid compound instead of a phosphate compound.
The lithium secondary battery electrode material according to the embodiments of the invention renders possible the implementation of a lithium secondary battery that, for instance, exhibits high output and high energy density, has a
A cycle test was performed in the same manner as in Example 1 using the resulting battery. Table 1 shows the measurement results for the ratio (Wh retention ratio) of the 1000th cycle Wh capacity to the initial Wh capacity.
TABLE 1. Ratio (%) of Wh capacity at 1000th cylcle to initial Wh capacity Example Comparative Example Wh retention ratio (%) 96 92 73 66 The results shown in Table 1 confirmed that the lithium batteries of Examples and 2 in which the LiFePO4 thin film was formed on the surface of the core material, could maintain a mixed potential continuity without showing reaction control due to LiFePO4, as compared with the lithium batteries of Comparative Examples 1 and 2 in which the electrode materials were merely mixed in the same mixing ratio. The lithium batteries of Comparative Examples 1 and 2 could initially prevent a decrease in output (SOC) due to the mixed potential, but showed a decrease in output as the crystal structure of Li(Ni/Mn/Co)02 deteriorated, and the network of the conductive material was destroyed (i.e., reaction sites became non-uniform) as the number of charge-discharge cycles increased. As a result, the mixed potential continuity was lost, and a decrease in output occurred.
Similar effects were obtained when using a layered compound having a different element mixing ratio, or using an olivine-type compound including Co and/or Mn instead of Fe, or using a silicic acid compound instead of a phosphate compound.
The lithium secondary battery electrode material according to the embodiments of the invention renders possible the implementation of a lithium secondary battery that, for instance, exhibits high output and high energy density, has a
18 cycle life of 5000 to 10,000 cycles (10 years), and may be used as an industrial battery (e.g., on-vehicle battery).
REFERENCE NUMBERS LIST
1 Positive electrode material 2 First lithium compound 3 Carbon material layers (amorphous and/or graphene-structured carbon) 3a First carbon material layer 3b Second carbon material layer 4 Second lithium compound 5 Conductive carbon material 5a Conductive carbon powder material 5b Conductive carbon fiber material 6 Graphene-structured layer.
REFERENCE NUMBERS LIST
1 Positive electrode material 2 First lithium compound 3 Carbon material layers (amorphous and/or graphene-structured carbon) 3a First carbon material layer 3b Second carbon material layer 4 Second lithium compound 5 Conductive carbon material 5a Conductive carbon powder material 5b Conductive carbon fiber material 6 Graphene-structured layer.
Claims (36)
1. A positive electrode material being a composite lithium material comprising:
a first lithium compound in the form of particles;
a first carbon material layer present on an entire surface of the first lithium compound particles;
a second lithium compound forming a thin-film layer on part or the entirety of a surface of the first carbon material layer; and a second carbon material layer present on an entire surface of the thin-film layer of the second lithium compound, wherein the carbon material of the first and second carbon material layers is independently selected from amorphous carbon material, graphene-structured carbon material, or a combination thereof;
wherein the first lithium compound comprises a layered lithium compound, a spinel-type lithium compound, or a combination thereof;
wherein the second lithium compound comprises a lithium-containing phosphate compound, a lithium-containing silicate compound, or a combination thereof;
and wherein the first and second lithium compounds are not in direct physical contact.
a first lithium compound in the form of particles;
a first carbon material layer present on an entire surface of the first lithium compound particles;
a second lithium compound forming a thin-film layer on part or the entirety of a surface of the first carbon material layer; and a second carbon material layer present on an entire surface of the thin-film layer of the second lithium compound, wherein the carbon material of the first and second carbon material layers is independently selected from amorphous carbon material, graphene-structured carbon material, or a combination thereof;
wherein the first lithium compound comprises a layered lithium compound, a spinel-type lithium compound, or a combination thereof;
wherein the second lithium compound comprises a lithium-containing phosphate compound, a lithium-containing silicate compound, or a combination thereof;
and wherein the first and second lithium compounds are not in direct physical contact.
2. The positive electrode material according to claim 1, wherein the layered lithium compound is a-layered Li(Nia/Mnp/Coy)02, wherein a+13+y=1.
3. The positive electrode material according to claim 1, wherein the spinel-type lithium compound is spinel-type Li(Nis/MnE)04, wherein 6+E=2.
4. The positive electrode material according to any one of claims 1 to 3, further comprising a compound that includes an element selected from the elements of groups 3 to 6 of the periodic table, or an oxide thereof, or an aluminum halide compound, said compound being present on the surface of the particles of the first lithium compound.
5. The positive electrode material according to claim 4, wherein the element selected from the elements of groups 3 to 6 of the periodic table is aluminum, molybdenum, titanium, zirconium, or sulfur.
6. The positive electrode material according to claim 4, wherein the aluminum halide compound is aluminum fluoride.
7. The positive electrode material according to any one of claims 1 to 6, wherein the lithium-containing phosphate compound is olivine-type Li(FeaCon/Mne)PO4, wherein -Fri-F8=1.
8. The positive electrode material according to any one of claims 1 to 6, wherein the lithium-containing silicate compound is Li(Fel/CoK/MnA)SiO4, wherein l+k-FA=1.
9. The positive electrode material according to any one of claims 1 to 8, further comprising a conductive carbon material, wherein the second carbon material layer and a surface layer of the conductive carbon material are fusion-bonded.
10. The positive electrode material according to claim 9, wherein the fusion-bonding is implemented by at least one method selected from calcination and mechanochemical methods.
11. The positive electrode material according to claim 9 or 10, wherein the conductive carbon material comprises at least one conductive carbon material selected from conductive carbon powders and conductive carbon fibers.
12. The positive electrode material according to claim 11, wherein the conductive carbon powder comprises at least one powder selected from acetylene black, ketjen black, and a powder that partially includes a graphite crystal.
13. The positive electrode material according to claim 11, wherein the conductive carbon fiber comprises at least one fiber selected from carbon fibers, graphite fibers, vapor-grown carbon fibers, carbon nanofibers, and carbon nanotubes.
14. The positive electrode material according to any one of claims 1 to 13, for use in producing a positive electrode of a lithium secondary battery.
15. A positive electrode comprising a positive electrode material as defined in any one of claims 1 to 13.
16. The positive electrode of claim 15, further comprising a binder.
17. The positive electrode of claim 16, wherein the binder is selected from fluorine-containing resins, thermoplastic resins, acrylic resin materials, styrene-butadiene-based materials, and combinations thereof.
18. The positive electrode of claim 17, wherein the fluorine-containing resins are selected from polytetrafluoroethylene, polyvinylidene fluoride, and fluororubber.
19. The positive electrode of claim 17, wherein the thermoplastic resins are selected from polypropylene and polyethylene.
20. The positive electrode of any one of claims 15 to 19, further comprising a current collector.
21. A lithium secondary battery comprising at least one positive electrode as defined in any one of claims 15 to 20, at least one negative electrode and at least one electrolyte.
22. The lithium secondary battery according to claim 21, wherein the negative electrode comprises a material selected from artificial graphite, a composite negative electrode material that includes metallic silicon, a composite of a silicon oxide/metallic silicon powder coated with conductive carbon and a graphitic powder coated with conductive carbon.
23. The lithium secondary battery according to claim 21 or 22, further comprising at least one separator in between stacked positive and negative electrodes, and an electrolyte solution in which the positive and negative electrodes are immersed.
24. The lithium secondary battery according to claim 23, wherein the separator is selected from a synthetic resin film, and a separator formed of fibers or inorganic fibers.
25. The lithium secondary battery according to claim 23, wherein the separator is selected from a polyethylene film, a polypropylene film, a polyethylene woven fabric, a polyethylene nonwoven fabric, a polypropylene woven fabric, a polypropylene nonwoven fabric, a separator formed of glass fibers, a separator formed of cellulose fibers, and a separator formed of polyethylene terephthalate fibers.
26. The lithium secondary battery according to any one of claims 21 to 25, wherein the electrolyte is a non-aqueous electrolyte solution which includes a non-aqueous solvent and at least one lithium salt, or an ion-conductive polymer.
27. The lithium secondary battery according to claim 26, wherein the non-aqueous solvent is an alkyl carbonate or a mixture of alkyl carbonates.
28. The lithium secondary battery according to claim 27, wherein the non-aqueous solvent is selected from ethylene carbonate (EC), propylene carbonate (PC), diethyl carbonate (DEC), dimethyl carbonate (DMC), methylethyl carbonate (MEC), and combinations thereof.
29. The lithium secondary battery according to any one of claims 26 to 28, wherein the lithium salt is selected from lithium hexafluorophosphate (LiPF6), lithium tetrafluoroborate (LiBF4), and lithium trifluoromethanesulfonate (LiSO3CF4).
30. A method for the manufacture of a positive electrode material as defined in any one of claims 1 to 13, comprising the steps of:
a) providing particles of the first lithium compound;
b) forming the first carbon material layer on the entire surface of the particles provided in (a), to provide carbon-coated particles;
c) forming the thin-film layer of the second lithium compound on part or the entirety of the carbon-coated particles provided in step (b); and d) coating the entire surface of the thin-film layer of the second lithium compound with the second carbon material layer, to provide the positive electrode material.
a) providing particles of the first lithium compound;
b) forming the first carbon material layer on the entire surface of the particles provided in (a), to provide carbon-coated particles;
c) forming the thin-film layer of the second lithium compound on part or the entirety of the carbon-coated particles provided in step (b); and d) coating the entire surface of the thin-film layer of the second lithium compound with the second carbon material layer, to provide the positive electrode material.
31. The method of claim 30, further comprising mixing the material of step (d) with a conductive carbon material, and fusion bonding the conductive carbon material and the second carbon material layer.
32. The method of claim 30 or 31, further comprising mixing the particle provided in step (a) with a compound comprising an element selected from the elements of groups 3 to 6 in the periodic table, or an oxide thereof, or an aluminum halide compound.
33. A system comprising a positive electrode material as defined in any one of claims 1 to 14, a positive electrode as defined in any one of claims 15 to 20, or a lithium secondary battery as defined in any one of claims 21 to 29.
34. Use of a lithium secondary battery as defined in any one of claims 21 to 29, as an industrial battery.
35. Use of a lithium secondary battery as defined in any one of claims 21 to 29, as an on-vehicle battery.
36. Use of a lithium secondary battery as defined in any one of claims 21 to 29, in electric or hybrid vehicles or in information technology devices.