Abstract

A fuel-cell gas dispersion layer configured from a porous carbon fiber substrate obtained by binding discontinuous carbon fibers using a carbide, and a porous layer containing at least carbonaceous particles, wherein: a porous layer (A) is disposed on one surface (A) of the porous carbon fiber substrate so as to have an average thickness (t1) of 10-55µm; a porous layer (J) is inserted into the interior of the porous carbon fiber substrate in a manner such that at least a portion thereof is present on the opposite surface (B); the proportion of the cross-sectional area in the thickness direction of openings in the interior of the porous carbon fiber substrate is 5-40%; the proportion of openings in the porous layer (A) and/or the porous layer (J) is 50-85%; the thickness of the porous carbon fiber substrate is 60-300µm; and the bulk density of the porous carbon fiber substrate is 0.20-0.45g/cm3.

Description

DESCRIPTION
TITLE OF THE INVENTION:
FUEL-CELL GAS DIFFUSION LAYER, AND METHOD FOR PRODUCING SAME
TECHNICAL FIELD
[0001]
The present invention relates to a gas diffusion layer that is suitably used in fuel cells, particularly in polymer electrolyte fuel cells. More specifically, it relates to a gas diffusion layer that has a high gas diffusivity and a high water removal performance in the through-plane direction to ensure high fuel cell performance, has a decreased gas permeability in the in-plane direction so that short cuts of gas are prevented from being formed between the channels in the bipolar plates to allow the gas (hydrogen and oxygen) coming from the bipolar plates to be supplied uniformly into the catalyst layers, and also has good mechanical properties, high electrical conductivity, and high thermal conductivity.
BACKGROUND ART

[0002]
A polymer electrolyte fuel cell in which fuel gas containing hydrogen is supplied to an anode while oxidizing gas containing oxygen is supplied to a cathode to cause electromotive force to be produced from electrochemical reaction taking place at the two poles commonly consists mainly of a bipolar plate, gas diffusion layer, catalyst layer, electrolyte membrane, catalyst layer, gas diffusion layer, and bipolar plate stacked in this order. The gas diffusion layers are required to have a high gas diffusivity so that gas supplied from the bipolar plates are allowed to diffuse into the catalyst, high water removal performance so that the water resulting from the electrochemical reaction is discharged into the bipolar plates, and high electrical conductivity so that the generated electric currents are taken out efficiently. Gas diffusion layers formed of carbon fiber etc.
(hereinafter referred to simply as gas diffusion layer) have been used widely.

[0003]
In a fuel cell, the gas diffusivity and water removal performance should be high in the through-plane direction of the gas diffusion layers to ensure high fuel cell performance in a wide range of environment conditions. To meet this requirement, Patent document 1 proposes a method of reducing the bulk density of the porous carbon fiber base substrate and Patent document 2 proposes a method of reducing the thickness of the porous carbon fiber base substrate. To allow the gas (hydrogen and oxygen) coming from the bipolar plates to be supplied uniformly into the catalyst layers, on the other hand, the gas permeability in the in-plane direction (in-plane gas pen-neability) of the gas diffusion layers should be reduced to depress short cuts of gas between the channels in the bipolar plates. To meet this requirement, Patent document 3 proposes a method of increasing the bulk density of the porous carbon fiber base substrate and Patent document 4 proposes a method of impregnating the porous carbon fiber base substrate with a porous layer. However, a trade-off relationship exists between increasing the gas diffusivity and water removal performance in the through-plane direction and decreasing the gas permeability in the in-plane direction and it has been difficult to realize both of them in a higher level balance. Patent document 5, furthermore, proposes a method of intentionally forming concave-shape portions in the porous layer surface to increase the gas diffusivity in the through-plane direction, although leading to problems with the durability of the porous layer taking place when used repeatedly for power generation.
PRIOR ART DOCUMENTS

PATENT DOCUMENTS

[0004]
Patent document 1: Japanese Unexamined Patent Publication (Kokai) No.

Patent document 2: Japanese Unexamined Patent Publication (Kokai) No.

Patent document 3: Japanese Unexamined Patent Publication (Kokai) No.

Patent document 4: Japanese Unexamined Patent Publication (Kokai) No.

Patent document 5: Japanese Unexamined Patent Publication (Kokai) No.

SUMMARY OF THE INVENTION
PROBLEMS TO BE SOLVED BY THE INVENTION

[0005]
In view of these problems with the conventional methods, the present invention aims to provide a gas diffusion layer that serves to develop high fuel cell performance by increasing the gas diffusivity and water removal performance in the through-plane direction and also serves to depress short cuts of gas between the channels in the bipolar plates by decreasing the gas permeability in the in-plane direction and further aims to provide a gas diffusion layer that contains a porous layer with a highly smooth surface.
MEANS OF SOLVING THE PROBLEMS

[0006]
As a result of intensive studies aiming to solve these problems, the present inventors have found that the problems can be solved by using the fuel cell gas diffusion = 4 layer and the production method therefore according to the present invention.

[0007]
To solve the problems, the fuel cell gas diffusion layer according to the present invention has the following constitution. Specifically, the invention provides a fuel cell gas diffusion layer comprising a porous carbon fiber base substrate containing discontinuous carbon fibers bonded to each other with carbide and a porous layer containing at least carbonaceous particles, the porous carbon fiber base substrate having a porous layer (A) with a thickness ti of 10 to 55 gm deposited on one surface, namely surface A, thereof, the porous carbon fiber base substrate being impregnated with a porous layer (J) at least part of which is exposed at the opposite surface, namely surface B, the porous carbon fiber base substrate holding internal pores having a cross-section area accounting for 5% to 40% of the total cross section in the through-plane direction, at least porous layer (A) and porous layer (J) both having a percentage of void of 50%
to 85%, the porous carbon fiber base substrate having a thickness of 60 to 300 gm, and the porous carbon fiber base substrate having a bulk density of 0.20 to 0.45 g/cm3.

[0008]
According to a preferred embodiment of the present invention, porous layer (A) mentioned above and porous layer (J) mentioned above have different constitutions.

[0009]
According to another preferred embodiment of the present invention, porous layer (A) mentioned above and porous layer (J) mentioned above have the same constitution.

[0010]
To solve the problems, furthermore, the production method for the fuel cell gas diffusion layer according to the present invention has the following constitution.

Specifically, the invention provides a production method for the fuel cell gas diffusion layer mentioned above comprising an impregnation process (I) for impregnating a porous carbon fiber base substrate containing discontinuous carbon fibers bonded to each other with carbide with dispersion liquid (1) containing at least carbonaceous particles and a dispersion medium, a deposit process (II) for depositing dispersion liquid (2) containing at least carbonaceous particles and a dispersion medium on one surface, namely surface A, of the porous carbon fiber base substrate resulting from the impregnation process (I), and a process for heating and sintering the porous carbon fiber base substrate resulting from the deposit process (II).

[0011]
To produce a fuel cell gas diffusion layer according to the second preferred embodiment the present invention where porous layer (A) and porous layer (J) have the same constitution, an adoptable production method for the fuel cell gas diffusion layer comprises a deposit-impregnation process (II-3) for depositing dispersion liquid (2) containing at least carbonaceous particles and a dispersion medium on one surface, namely surface A, of a porous carbon fiber base substrate containing discontinuous carbon fibers bonded to each other with carbide, and infiltrating dispersion liquid (2) into the porous carbon fiber base substrate and a process for heating and sintering the porous carbon fiber base substrate resulting from the deposit-impregnation process (II-3).
[0011a]
In one aspect, the present invention provides a fuel cell gas diffusion layer comprising a porous carbon fiber base substrate comprising discontinuous carbon fibers bonded to each other with carbide, wherein the porous fiber substrate (i) has a thickness of 60 to 300 gm and a bulk density of 0.20 to 0.45 g/cm3, (ii) is impregnated with a porous material (J) containing carbonaceous particles at least part of which is exposed at opposite surface B
thereof, and (iii) has internal pores with a cross-sectional area accounting for 5% to 40% of the total cross section Date Recue/Date Received 2022-06-17 5a in a through-plane direction in the porous carbon fiber base substrate, and a porous layer (A) with a mean thickness ti of 10 to 55 gm and containing carbonaceous particles deposited on a surface A of the porous carbon fiber base substrate, wherein at least the porous layer (A) and the porous material (J) both have a percentage of void of 50% to 85%.
[0011b]
In another aspect, the present invention provides a production method for the fuel cell gas diffusion layer as described herein comprising providing a precursor porous material (J) in the form of a dispersion liquid (1) that contains at least the carbonaceous particles and a dispersion medium (1), a precursor porous layer (A) in the form of a dispersion liquid (2) that contains at least the carbonaceous particles and a dispersion medium (2), and the porous carbon fiber base substrate, performing an impregnation process (I) to impregnate the porous carbon fiber base substrate with the dispersion liquid (1), performing a deposit process (II) to deposit the dispersion liquid (2) on the surface A of the porous carbon fiber base substrate, thereby forming the precursor porous layer (A) on the surface A of the porous carbon fiber base substrate, and subsequently heating and sintering the porous carbon fiber base substrate with the precursor porous layer (A) thereon, thereby forming the porous carbon fiber base substrate impregnated with the porous material (J) and having the porous layer (A) deposited on the surface A.
[0011c]
In another aspect, the present invention provides a production method for the fuel cell gas diffusion layer as described herein comprising providing a precursor porous layer (A) in the form of a dispersion liquid (2) that contains at least the carbonaceous particles and a dispersion medium (2), and the porous carbon fiber base substrate, performing a deposit process (II-3) to deposit the dispersion liquid (2) on the surface A of the porous carbon fiber base substrate, and infiltrating the dispersion liquid (2) into the porous carbon fiber base substrate, Date Recue/Date Received 2022-06-17 5b thereby forming a precursor porous material (J) and the precursor porous layer (A) on the surface A of the porous carbon fiber base substrate, and subsequently heating and sintering the porous carbon fiber base substrate with the precursor porous layer (A) thereon, thereby forming the porous carbon fiber base substrate impregnated with the porous material (J) and having the porous layer (A) deposited on the surface A.
[0011d]
In another aspect, the present invention provides a production method for the fuel cell gas diffusion layer as described herein comprising: performing the method of as described herein, wherein the providing further comprises providing: a precursor porous layer (B) in the form of a dispersion liquid (3) that contains at least the carbonaceous particles and a dispersion medium (3), the method further comprising, prior to the heating and sintering, performing an opposite surface deposit process (II-2) to deposit the dispersion liquid (3) on the opposite surface B of the porous carbon fiber base substrate, wherein the heating and sintering thereby forms the porous carbon fiber base substrate further having the porous layer (B) deposited on the opposite surface B.
Date Recue/Date Received 2022-06-17 =

channels in the bipolar plates by decreasing the gas permeability in the in-plane direction and that contains a porous layer with a highly smooth surface.
BRIEF DESCRIPTION OF THE DRAWINGS
[0013]
[Fig. 1] Fig. 1 gives schematic cross-section diagrams of a fuel cell gas diffusion layer according to the present invention, diagram (a) illustrating an embodiment where the porous carbon fiber base substrate being impregnated with a porous layer (B) at least part of which is exposed at the other surface, or surface B, and diagram (b) illustrating porous layer (B) exposed over the entirety of the other surface, or surface B, of the porous carbon fiber base substrate.
[Fig. 2] Fig. 2 is a schematic diagram of a cross section of a porous layer used for the present invention, image-processed for binarization to identify voids.
[Fig. 3] Fig. 3 is a schematic cross-section diagram of a membrane electrode assembly (MEA) containing a gas diffusion layer according to the present invention.
DESCRIPTION OF PREFERRED EMBODIMENTS
[0014]
The fuel cell gas diffusion layer according to the present invention is described below with reference to diagrams. It should be understood, however, that the invention is not construed as being limited by the constitutions given in the diagrams.
[0015]
Fig. 1 is a schematic cross-section diagram of a fuel cell gas diffusion layer according to the present invention. It is a fuel cell gas diffusion layer (hereinafter occasionally abbreviated as GDL) including a porous carbon fiber base substrate (hereinafter occasionally abbreviated as CP) containing discontinuous carbon fibers bonded to each other with carbide and a porous layer (hereinafter occasionally abbreviated as MPL) containing at least carbonaceous particles, the porous carbon fiber base substrate containing porous layer (A) deposited to an average thickness oft 1 ( m) on one surface A thereof, the porous carbon fiber base substrate being impregnated with porous layer (J), and the porous carbon fiber base substrate holding pores inside. Each of the components is described below.
[0016]
The porous carbon fiber base substrate, which is an integral component of the present invention, is described first in detail below.
[0017]
For the present invention, the porous carbon fiber base substrate is required to have a high gas diffusivity so that gas supplied from the bipolar plates are allowed to diffuse into the catalyst, high water removal performance so that the water resulting from the electrochemical reaction is discharged into the bipolar plates, and high electrical conductivity so that the generated electric currents are taken out efficiently. To this end, it is preferable to use a porous carbon fiber base substrate that has electrical conductivity and a mean pore size of 10 to 100 urn. More specifically, it is preferable, for example, to use carbon fiber woven fabric or carbon fiber non-woven fabric such as carbon fiber papermaking substrate. In particular, it is preferable to use a substrate formed of a carbon fiber papermaking substrate bonded with carbide, that is, so-called carbon paper, because of its property of absorbing dimensional changes of electrolyte membrane in the through-plane direction, that is, so-called spring property.
For the present invention, a substrate formed of a carbon fiber papermaking substrate bonded with carbide is commonly produced by impregnating a carbon fiber papermaking substrate with resin, followed by carbonization, as described later.
[0018]

Useful carbon fiber materials include polyacrylonitrile (hereinafter abbreviated as PAN) based, pitch-based, rayon-based, and vapor-grown carbon fiber materials.
Among others, PAN-based or pitch-based carbon fiber materials are preferred for the present invention because they have high mechanical strength.
[0019]
Carbon fiber used for the present invention preferably has a single-yam mean diameter in the range of 3 to 20 pm, more preferably in the range of 5 to 10 p.m. If the mean diameter is 3 um or more, the pore size will be increased and the water removal performance will be improved, serving to depress flooding. If the mean diameter is 20 p.m or less, on the other hand, the water vapor diffusivity will be low and dry-out can be depressed. The use of two or more carbon fiber materials with different mean diameters is preferable because the porous carbon fiber base substrate will have an improved surface smoothness Here, in order to determine the mean diameter of single carbon fibers, the carbon fiber was photographed under a microscope such as scanning electron microscope at a magnification of 1,000 times or more and 30 single fibers were selected at random and subjected to diameter measurement, followed by calculating the average.
Useful scanning electron microscopes include S-4800 manufactured by Hitachi, Ltd., and its equivalents.
[0020]
Carbon fiber used for the present invention is composed of discontinuous single yarns and specifically, its mean length is preferably in the range of 3 to 20 mm, more preferably in the range of 5 to 15 mm. A mean length of 3 mm or more is preferable because the porous carbon fiber base substrate will be high in mechanical strength, electrical conductivity, and thermal conductivity. On the other hand, a mean length of 20 mm or less is preferable because the carbon fiber will have high dispersibility during a paper-making process, leading to a homogeneous porous carbon fiber base substrate. Carbon fiber having such a mean length can be produced by, for example, cutting continuous carbon fiber to a required length.
[0021]
Here, in order to determine the mean length of carbon fiber, the carbon fiber was photographed under a microscope such as scanning electron microscope at a magnification of 50 times or more and 30 single fibers were selected at random and subjected to length measurement, followed by calculating the average. Useful scanning electron microscopes include S-4800 manufactured by Hitachi, Ltd., and its equivalents.
Here, the mean diameter and mean length of single carbon fibers are commonly determined from direct observations of the carbon fiber that is used as raw material, but they may be determined from observations of the porous carbon fiber base substrate.
[0022]
For the present invention, the porous carbon fiber base substrate preferably has a pore size in the range of 20 to 80 pin, more preferably in the range of 25 to 75 inn, and still more preferably in the range of 30 to 70 1.1m. If the pore size is 20 gm or more, the water removal performance will be improved and flooding will be depressed. If the pore size is 80 pm or less, the electrical conductivity will be high, leading to improved fuel cell performance at both high and low temperatures.
[0023]
Here, the pore size of the porous carbon fiber base substrate is determined by measuring the pore size distribution by the mercury intrusion technique performed at a measuring pressure of 6 kPa to 414 MPa (pore size 30 nm to 400 pm) and then identifying the peak diameter. Here, if a plurality of peaks appear, the peak diameter for the highest peak is adopted. Useful measuring apparatuses include Autopore manufactured by SHIMADZU CORPORATION and its equivalents.
[0024]
For the present invention, the porous carbon fiber base substrate preferably contains carbonaceous particles. The existence of carbonaceous particles improves the electrical conductivity of the porous carbon fiber base substrate itself. The carbonaceous particles preferably have a mean particle size of 0.01 to 10 gm, more preferably 1 to 8 gm, and still more preferably 3 to 6 gm. The carbonaceous particles are preferably powder of graphite or carbon black, more preferably graphite powder. The mean particle size of carbonaceous particles can be determined by measuring the particle diameter distribution with the dynamic light scattering technique, followed by calculating the number average.
[0025]
For the present invention, the porous carbon fiber base substrate has a thickness of 60 to 300 gm, preferably 70 to 250 m, and more preferably 80 to 200 gm, and has a bulk density of 0.20 to 0.45 g/cm3, preferably 0.22 to 0.43 g/cm3, and more preferably 0.24 to 0.40 g/ein3. If the porous carbon fiber base substrate has a thickness of 60 gm or more, it ensures a high mechanical strength and an easy handling. If the thickness is 300 pm or less, the porous carbon fiber base substrate will have a decreased cross-section area and accordingly prevents interception of gas and shifts from a flow channel to an adjacent flow channel, leading to an increased quantity of gas for sweeping away liquid water through the flow channels. Accordingly, this serves not only for prevention of plugging but also for shortening of the paths for water removal, leading to improved flooding and increased fuel cell performance at low temperatures. If the porous carbon fiber base substrate has a bulk density of 0.20 g/cm3 or more, it ensures a high mechanical strength and an easy handling. A bulk density of 0.45 g/cm3 or less is preferable because it will lead to high water removal performance and high gas [0026]
Here, the thickness of the porous carbon fiber base substrate is determined by measuring the thickness while pressing the porous carbon fiber base substrate under a pressure of 0.15 MPa. Specifically, 20 or more different points are selected at random and, while applying a pressure of 0.15 MPa in the through-plane direction of the sheet, thickness measurements are taken at each point using a micrometer with a micrometer head having a circular cross section with a diameter of 5 mm, followed by averaging the thickness measurements taken separately.
[0027]
The bulk density of the porous carbon fiber base substrate can be determined by cutting out ten 10 cm x 10 cm rectangular pieces from the sheet, weighing them on an electronic balance, averaging the measurements to calculate the areal weight (mass per unit area) of the porous carbon fiber base substrate, and dividing it by the thickness of the porous carbon fiber base substrate.
[0028]
Described in more detail below is a case where carbon paper is used as the porous carbon fiber base substrate.
[0029]
For the present invention, a papermaking substrate containing carbon fiber and impregnated with a resin composition is referred to as prepreg. To obtain a porous carbon fiber base substrate suitable for the present invention, it is particularly effective to control the areal weight of the carbon fiber in the prepreg and the weight proportion of the resin components to the carbon fiber. Here, a substrate with a low bulk density

12 can be obtained when using prepreg with a small areal weight of carbon fiber while a substrate with a high bulk density can be obtained when using prepreg with a large areal weight of carbon fiber is used. Furthermore, a substrate with a low bulk density can be obtained by decreasing the weight proportion of the resin components to the carbon fiber while a substrate with a high bulk density can be obtained by increasing the weight proportion of the resin components. If there is not a significant difference in areal weight of carbon fiber, a substrate with a low bulk density can be obtained by increasing the thickness of the porous carbon fiber base substrate while a substrate with a high bulk density can be obtained by decreasing its thickness. A porous carbon fiber base substrate having a desired bulk density can be produced by controlling the areal weight of carbon fiber in the prepreg, the weight proportion of the resin components to the carbon fiber, and the thickness of the porous carbon fiber base substrate in carrying out the production method described later.
[0030]
Described next is the porous layers used as constituents of the present invention. For the present invention, three types of porous layers, categorized as porous layer (A), porous layer (J), and porous layer (B), are used. In a porous layer, carbonaceous particles commonly account for 50A to 95% in mass percentage of the total quantity.
[0031]
Porous layer (A) is a porous layer with a finite mean thickness ti deposited on one surface, or surface A, of the porous carbon fiber base substrate and it is required to have a high gas diffusivity so that gas supplied from the bipolar plates are allowed to diffuse into the catalyst, high water removal performance so that the water resulting from electrochemical reaction is discharged into the bipolar plates, and high electrical

13 conductivity so that the generated electric currents are taken out efficiently. In addition, it is also required to have a function of promoting the back-diffusion of water into the electrolyte membrane. Accordingly, porous layer (A) is preferably formed of a porous material having electrical conductivity and a mean pore size of 1 to 10 nm and more specifically, it is preferably formed of a mixture of, for example, carbonaceous particles and a hydrophobic polymer. Useful carbonaceous particle materials to be used for the present invention include graphite, carbon black, graphene, carbon nanofiber (such as single-walled carbon nanotube, multi-walled carbon nanotube, and vapor grown carbon fiber), and milled carbon fiber, of which carbon black is preferred. It is preferable for these carbonaceous particles to have a particle size of 10 to 200 nm. Here, the particle size of carbonaceous particles should be determined by transmission electron microscopy. Observation by transmission electron microscopy is performed at a magnification nf 500,0n0 and 1n0 particles are selected in the screen Their outside diameter is measured and the average of the measurements is adopted as the particle size of the carbon particles. Here, the term "outside diameter" refers to the maximum diameter of a particle (specifically, major axis of the particle, or the largest size across the particle). Useful transmission electron microscopes include JEM-4000EX
manufactured by JEOL Ltd. and its equivalents.
[0032]
For the present invention, the term "carbon black" refers to fine carbon particles in which carbon atoms account for 80% or more and that have a primary particle size of about 3 to 500 nm. The use of carbon black in which carbon atoms account for 80% or more serves to produce a porous layer with a higher electrical conductivity and corrosion resistance. The use of carbon black having a primary particle size of 500 nm or less increases the particle density per unit mass and promotes

14 structural development, leading to porous layer (A) with improved electrical conductivity and mechanical properties.
[0033]
For the present invention, useful carbon black materials include furnace black, channel black, acetylene black, and thermal black. Among others, the use of acetylene black is preferred because of having high electrical conductivity and low impurity content.
[0034]
To improve the electrical conductivity, it is also preferred for porous layer (A) to contain carbon nanofiber. If containing carbon nanofiber, porous layer (A) will have a higher percentage of void and a higher electrical conductivity. The fiber diameter of the carbon nanofiber is preferably 1 to 1,000 nm, more preferably 10 to 500 nm. If carbon nanofiber with s fiber diameter of less than 1 nm is used, porous layer (A) will have a poor percentage of void, possibly failing to have improved water removal performance as expected. If carbon nanofiber with a fiber diameter of more than 1,000 run is used, porous layer (A) will suffer a decrease in smoothness and possibly fail to have improved plugging properties as expected. It may also lead to an increased contact resistance.
[0035]
In carbon nanofiber used for the present invention, carbon atoms account for 90% or more and the aspect ratio is 10 or more. Since carbon atoms account for 90% or more and the aspect ratio is 10 or more in the carbon nanofiber, the use thereof serves to provide a porous layer with improved electrical conductivity and mechanical properties.
[0036]
Here, the aspect ratio of carbon nanofiber is defined as the ratio between the fiber diameter and fiber length determined by transmission electron microscopy.

Observation by transmission electron microscopy is performed at a magnification of 500,000 and 100 single fibers are selected in the screen. Their diameter and length are measured and the measurements are averaged, followed by dividing the mean fiber length by the mean fiber diameter to calculate the aspect ratio. Useful transmission electron microscopes include JEM-4000EX manufactured by JEOL Ltd. and its equivalents.
[0037]
Useful carbon nanofiber materials for the present invention include single-walled carbon nanotube, double-walled carbon nanotube, multi-walled carbon nanotube, carbon nanohom, carbon nanocoil, cup stacked carbon nanotube, bamboo structured carbon nanotube, vapor grown carbon fiber, and graphite nanofiber.
In particular, the use of single-walled carbon nanotube, double-walled carbon nanotube, multi-walled carbon nanotube, or vapor grown carbon is preferred because it ensures a large aspect ratio, high fiber electrical conductivity and good mechanical properties.
Vapor grown carbon fiber is produced by growing carbon in a gas phase using a catalyst, and products with a mean diameter of 5 to 200 nm and a mean fiber length of 1 to 20 tim are preferred.
[002g]
To add a hydrophobic polymer with the aim of improving the water removal performance, porous layer (A) may also contain a hydrophobic polymer additionally in combination with carbonaceous particles such as carbon black and carbon nanofiber described above. Here, such hydrophobic polymers include fluorine resins such as polychlorotrifluorocthylene resin (PCTFE), polytetrafluoroethylene resin (PTFE), polyvinylidene fluoride resin (PVDF), tetrafluoroethylene-hexa fluor propylene copolymer (FEP), tetrafluoroethylene-perfluoroalkylvinyl ether copolymer (PFA), and tetrafluoroethylene-ethylene copolymer (ETFE). Here, fluorine resin refers to a hydrophobic resin containing a fluorine atom in its structure.
[0039]
If a hydrophobic polymer is added to porous layer (A), its blending quantity is preferably 1 to 70 parts by mass, more preferably 5 to 60 parts by mass, relative to 100 parts by mass of the carbonaceous particles in porous layer (A). If the hydrophobic polymer accounts for 1 part by mass or more, porous layer (A) will improve in water removal performance and mechanical strength while if the hydrophobic polymer accounts for 70 parts by mass or less, porous layer (A) will improve in electrical conductivity. The carbonaceous particles to be used to form porous layer (A) may be a mixture of, for example, carbon black, such as acetylene black, and carbon nanofiber.
[0040]
It is important for porous layer (A) to have a mean thickness tl in the range of to 55 pm, preferably in the range of 15 to 50 pm, more preferably in the range of 20 to 45 pm. If ti is 10 pm or more, the single carbon fibers of the porous carbon fiber base substrate can be prevented from sticking into the electrolyte membrane while if ti is 55 pm or less, porous layer (A) can decrease in electrical resistance and the number of cracks in the surface of porous layer (A) can be maintained at a rate of one or less in a 1 mm X1 mm square.
[0041]
Here, the mean thickness tl of porous layer (A) can be determined by first measuring the mean thickness of the porous carbon fiber base substrate that contains porous layer (J) and porous layer (B) deposited thereon and then subtracting it from the mean thickness of the entire gas diffusion layer. The thickness of the entire gas diffusion layer and the thickness of the porous carbon fiber base substrate that contains porous layer (J) and porous layer (B) deposited thereon can be measured by the same method as used above for the porous carbon fiber base substrate.
[0042]
Here, to determine the number of cracks in the surface of porous layer (A), observation is performed by microscopy, such as optical microscopy, to select different portions at random on the surface of porous layer (A) and photograph them at a magnification of 50 to 100, and the number of isolated cracks existing in an arbitrarily selected 1 mm x 1 mm area is counted, followed by averaging the number of cracks found in the photographs. Useful optical microscopes include digital microscopes manufactured by ICEYENCE CORPORATION or their equivalents.
[0043]
Porous layer (J) is a porous layer infiltrated inside the porous carbon fiber base substrate and it is required to have a high gas diffusivity so that gas supplied from the bipolar plates are allowed to diffuse into the catalyst, high water removal performance so that the water resulting from electrochemical reaction is discharged into the bipolar plates, and high electrical conductivity so that the generated electric currents are taken out efficiently. In addition, it should be infiltrated inside the porous carbon fiber base substrate to decrease the in-plane gas permeability, thereby preventing plugging.
Accordingly, porous layer (J) is preferably electrically conductive and formed of a porous material having a mean pore size of 1 to 10 nm and more specifically, it may be formed of the same material as in porous layer (A) preferably such as a mixture of, for example, carbonaceous particles and a hydrophobic polymer. Useful carbonaceous particle materials are as given previously.
[0044]
The constitution of porous layer (J) may be either identical to or different from that of porous layer (A), but it is preferable for them to be different in the case where porous layer (J) and porous layer (A) are expected to have different functions.
Specifically, porous layer (A) may be required to have a loose structure particularly for realizing a high gas diffusivity while porous layer (J) may be required to have a dense structure particularly for realizing a high electrical conductivity and moisture retention capability. Accordingly, it is better for them to have different constitutions that are suitable to meet the different purposes.
[0045]
Compared to this, when the water removal performance for operation in a high humidify environment is to be further improved, it will be preferable for porous layer (J) to have the same constitution as that of porous layer (A). This is also advantageous in that porous layer (A) and porous layer (J) can be prepared from only one dispersion liquid, allowing gag diffusion layers to he produced efficiently.
[0046]
To improve the electrical conductivity, it is preferred for porous layer (J), as in the case of porous layer (A), to contain carbon nanofiber. If containing carbon nanofiber, porous layer (J) will have a higher percentage of void and a higher electrical conductivity. The fiber diameter of the carbon nanofiber is preferably 1 to 1,000 nm, more preferably 10 to 500 nm. If carbon nanofiber with a fiber diameter of less than 1 nm is used, porous layer (J) will have a poor percentage of void and fail to have improved water removal performance as expected. If using carbon nanofiber with a fiber diameter of more than 1,000 nm, porous layer (J) may fail to infiltrate in sufficient amounts into the porous carbon fiber base substrate and possibly fail to decrease the in-plane gas permeability as expected.
[0047]

To add a hydrophobic polymer with the aim of improving the water removal performance, porous layer (J), as in the case of porous layer (A), may also contain a hydrophobic polymer in combination with the carbon black and carbon nanofiber described above. Here, examples of the hydrophobic polymer include the fluorine resins listed previously.
[0048]
The blending quantity of a hydrophobic polymer added to porous layer (J) is, as in the case of porous layer (A), preferably 1 to 70 parts by mass, more preferably 5 to 60 parts by mass, relative to 100 parts by mass of the carbonaceous particles in porous layer (J). Addition of a hydrophobic polymer in this range of blending quantity leads to the same advantage as described for porous layer (A). Useful materials for the carbonaceous particles to be used to form porous layer (J) include those listed for porous layer (A) including a mixture of, for example, carbon black, such as acetylene black, and carbon nanofiber.
[0049]
The percentage of void of porous layer (J) is preferably 50 to 85%, more preferably 60 to 80%. The gas diffusion layer will have high water removal performance and high gas diffusivity if the percentage of void of porous layer (J) is 50%
or more while porous layer (J) will have high mechanical strength if the percentage of void of porous layer (J) is 85% or less. The percentage of void can be controlled by changing the compounding ratio of the carbonaceous particles or the compounding ratio of the hydrophobic polymer.
[0050]
Porous layer (J) infiltrates into the porous carbon fiber base substrate and at least partially exposed at the other surface, i.e. surface B. As porous layer (J) infiltrates into the porous carbon fiber base substrate, pores should be left inside the porous carbon fiber base substrate and their cross-section area in the through-plane direction should account for 5 to 40% of the entire cross-section area. Here, the proportion of the through-thickness cross-section area of the pores left inside the porous carbon fiber base substrate to the entire cross-section area is hereinafter referred to as porosity. If the porosity is 5% or more, the gas diffusion layer will have high water removal performance and high gas diffusivity. If the porosity is 40% or less, on the other hand, the in-plane gas permeability will decrease to allow plugging to be prevented.
The porosity can be controlled by adjusting the concentration of carbonaceous particles in dispersion liquid (1) that consists mainly of carbonaceous particles and dispersion medium and the concentration of the hydrophobic polymer. Porous layer (J) is at least partially exposed at the other surface, i.e. surface B, thereby allowing a reduction in the contact resistance between the gas diffusion layer and the bipolar plate and an increase in the power generation efficiency.
[0051]
Whether porous layer (I) is existent inside the porous carbon fiber base substrate and at least partially exposed at the other surface, i.e. surface B, may be determined from observation of a cross section of the gas diffusion layer at a magnification of about 400 by microscopy, such as scanning electron microscopy. Here, the expression "porous layer (J) is existent inside the porous carbon fiber base substrate and at least partially exposed at the other surface, i.e. surface B," means that porous layer (J) is visible in at least part of a cross section and the other surface, i.e. surface B, of the porous carbon fiber base substrate. The porosity can be determined by selecting 5 different portions at random in a cross section that is perpendicular to the sheet plane of the gas diffusion layer, photographing them by, for example, scanning electron microscopy, at a magnification of about 400, binarizing the images by image processing, measuring the porosity in each portion of the porous carbon fiber base substrate, and averaging the porosity measurements taken separately from the photographs.
Image processing can be carried out by, for example, the procedure described below.
= The size of the total processing area (number of vertical pixels x number of horizontal pixels) is calculated to determine the total area.
= The image is averaged over each 9 pixel area (3 vertical pixels x 3 horizontal pixels) and the noise per pixel is removed to provide image 1.
= From image 1, those regions (porous layer and carbon fiber cross section) that contain non-pore portions and have a luminance that is equal to or greater than an arbitrary mean luminance value or equal to or smaller than an arbitrary mean luminance value are extracted to provide image 2.
= From image 2, only those islands that have a size of 100 pixels or more are extracted to provide image 3.
= Image 3 is subjected to circular closing processing for a radius of 2.5 pixels (to fill small holes) to provide image 4.
= The area of image 4 (i.e., non-pore portion) is determined.
- The area of images 4 is subtracted from the total area to calculate the area of pores, which is then divided by the total area to determine the porosity in one portion.
[0052]
The percentage of void is calculated in this way for the 5 portions and averaged to provide the mean percentage of void. Here, S-4800 manufactured by Hitachi, Ltd., or its equivalent can be used for scanning electron microscopy and HALCON
(registered trademark) 9.0 manufactured by MVTec or its equivalent can be used as software for image processing.

[0053]
For the present invention, furthermore, it is preferable for the crack frequency in the porous layer (A) to be lower than the crack frequency in porous layer (J). Existing inside the porous carbon fiber base substrate, porous layer (J) will suffer little direct load due to expansion or shrinkage of the electrolyte membrane when working in a fuel cell. Porous layer (A), on the other hand, is liable to such a direct load and accordingly, it is particularly preferable for porous layer (A) to be low in crack frequency from the viewpoint of durability. From the viewpoint of gas diffusivity, however, a higher crack frequency is preferable. For these two reasons, furthermore, it is preferable for the crack frequency in the porous layer (A) to be lower than the crack frequency in porous layer (J). The crack frequency in the porous layer can be determined by selecting 5 different portions at random in a cross section that is perpendicular to the sheet plane of the gas diffusion layer, photographing them by, for example, scanning electron microscopy, at a magnification of about 400, and counting the number of isolated, continuous cracks with a length of 10 um or more.
[0054]
In the porous carbon fiber base substrate, porous layer (B) is one deposited as required on the opposite surface, i.e. surface 13, to surface A where porous layer (A) is deposited. Porous layer (B), if existing, works to prevent plugging more effectively and in particular, further reduce the contact resistance with the bipolar plate.
Porous layer (B), if existing, is required to have a high gas diffusivity so that gas supplied from the bipolar plates are allowed to diffuse into the catalyst, high water removal performance so that the water resulting from the electrochemical reaction is discharged into the bipolar plates, and high electrical conductivity so that the generated electric currents are taken out efficiently. To this end, it is preferable for porous layer (B) to be of a porous material that has electrical conductivity and has a mean pore size of 1 to 10 tun. More specifically, such materials include those listed for porous layer (A).
[0055]
To improve the electrical conductivity, it is preferred for porous layer (B), as in the case of porous layer (A), to contain carbon nanofiber. If containing carbon nanofiber, porous layer (B) will have a higher percentage of void and a higher electrical conductivity. The fiber diameter of the carbon nanofiber is preferably 1 to 1,000 nm, more preferably 10 to 500 nm. If carbon nanofiber with a fiber diameter of less than 1 nm is used, porous layer (B) will have a poor percentage of void and fail to have improved water removal performance as expected. If carbon nanofiber with a fiber diameter of more than 1,000 nm is used, porous layer (B) will suffer a decrease in smoothness and possibly fail to have improved plugging properties as expected.
It may also lead to an increased contact resistance.
[0056]
To add a hydrophobic polymer with the aim of improving the water removal performance, porous layer (B), as in the case of porous layer (A), may also contain a hydrophobic polymer in combination with the carbon black and carbon nanofiber described above. Here, examples of the hydrophobic polymer include the fluorine resins listed previously.
[0057]
The blending quantity of a hydrophobic polymer added to porous layer (B) is, as in the case of porous layer (A), preferably 1 to 70 parts by mass, more preferably 5 to 60 parts by mass, relative to 100 parts by mass of the carbonaceous particles in porous layer (B). Addition of a hydrophobic polymer in this range of blending quantity leads to the same advantage as described for porous layer (A). Useful materials for the carbonaceous particles to be used to form porous layer (B) include, for example, those listed for porous layer (A) including a mixture of, for example, carbon black, such as acetylene black, and carbon nanofiber.
[0058]
The mean thickness t2 of porous layer (B) is preferably in the range of 0 to Jim, more preferably 3 to 10 p.m. If porous layer (J) is existent inside the porous carbon fiber base substrate and at least partially exposed at the opposite surface, i.e. surface B, as shown in Fig. 1(a), the mean thickness of porous layer (B) may be substantially 0 gm, which means that deposition of porous layer (B) may not be required. If porous layer (B) has a thickness of 3 um or more over the entirety of the opposite surface, i.e. surface B, as shown in Fig. 1(b), and if it faces a bipolar plate, the interface gap between the bipolar plate and the gas diffusion layer will be small, which serves not only to reduce the in-plane gas permeability and accordingly enhance the plugging prevention effect, but also to further decrease the contact resistance with the bipolar plate as described above, thereby leading to a further increase in power generation efficiency.
Compared to this, it is not preferable for porous layer (B) to have a thickness t2 of more than 20 p.m because high water removal performance as expected will not be realized whereas a thickness of 10 inn or less is preferable from the viewpoint of water removal performance. Here, the mean thickness t2 of porous layer (B) can be determined by subtracting the thickness of the porous carbon fiber base substrate and the mean thickness tl of porous layer (A) from the mean thickness of the entire gas diffusion layer.
[0059]
It is more preferable for porous layer (B) to have the same constitution as the porous layer (J). If porous layer (B) has the same constitution as the porous layer (J), the coating process for forming porous layer (B) can be eliminated.
[0060]
Both porous layer (A) and porous layer (J) should have a percentage of void of 50 to 85%, preferably 60 to 80%. The gas diffusion layer will have high water removal performance and high gas diffusivity if the percentage of void is 50% or more while the porous layer will have high mechanical strength if the percentage of void is 85% or less.
In addition, it is more preferable also for porous layer (B) to have a percentage of void in the above-mentioned range. In particular, it is preferable for the percentage of void of porous layer (A) to be higher than either the percentage of void of porous layer (B) or that of porous layer (J). If porous layer (B) is not existent, it is preferable for the percentage of void of porous layer (A) to be higher than the percentage of void of porous layer (J). It is preferable for the percentage of void of porous layer (A) to be higher than either the percentage of void of porous layer (B) or that of porous layer (1) because it serves to maintain the gas diffusivity at a sufficiently high level. The percentage of void can be controlled by changing the compounding ratio of the carbonaceous particles or the compounding ratio of the hydrophobic polymer.
[0061]
Here, for porous layer (A), porous layer (B), and porous layer (J), the percentage of void can be determined by observing each layer by, for example, scanning electron microscopy, selecting 5 different portions at random in a cross section that is perpendicular to the sheet plane of the gas diffusion layer, photographing them at a magnification of about 20,000, binarizing the images by image processing, measuring the percentage of void using the binarized images, and averaging the percentage of void measurements taken separately from the photographs. Image processing can be carried out by, for example, the procedure described below.

= The size of the total processing area (number of vertical pixels x number of horizontal pixels) is calculated to determine the total area.
= The image is averaged over each 9 pixel area (3 vertical pixels x 3 horizontal pixels) and the noise per pixel is removed to provide image 1.
= From image 1, those regions (porous layer cross section) that contain non-void portions and have a luminance that is equal to or greater than an arbitrary mean luminance value are extracted to provide image 2.
= From image 2, only those islands that have a size of 100 pixels or more are extracted to provide image 3.
= Image 3 is subjected to circular closing processing for a radius of 2.5 pixels (to fill small holes) to provide image 4. An example of image 4 is shown in Fig. 2.
= The area of image 4 (i.e., non-void portion) is determined.
= The area of image 4 is subtracted from the total area to calculate the area of voids, which is then divided by the total area to determine the percentage of void in one portion.
[0062]
The percentage of void is calculated in this way for the 5 portions and averaged to provide the mean percentage of void. Here, S-4800 manufactured by Hitachi, Ltd., or its equivalent can be used for scanning electron microscopy and HALCON
(registered trademark) 9.0 manufactured by MVTec or its equivalent can be used as software for image processing.
[0063]
A method suitable for producing the gas diffusion layer according to the present invention is described in detail below.
[0064]

<Carbon fiber non-woven fabric>
Methods to produce nonwoven fabric containing carbon fiber include a wet method in which carbon fiber is dispersed in a liquid and a dry method in which it is dispersed in air. In particular, it has been preferred to use the wet papermaking method, which can produce thin carbon fiber non-woven fabric. Carbon fiber non-woven fabric produced by the wet papermaking method is referred to as carbon fiber papermaking substrate.
[0065]
It is preferable to add pulp to carbon fiber used for the papermaking method with the aim of lowering the in-plane gas permeability. Useful pulp materials include natural pulp materials such as wood pulp, bagasse pulp, and straw pulp and synthetic pulp materials such as fibrillated polyethylene fiber, vinylon fiber, polyacetal fiber, polyester fiber, polyamide fiber, rayon fiber, acrylic fiber, and aramid fiber.
[0066]
Carbon fiber non-woven fabrics to be used are preferably in the form of a sheet in which carbon fiber is disPersed randomly in a two-dimensional plane so that isotropic electrical conductivity and thermal conductivity are maintained in the plane.
[0067]
The pore size distribution in nonwoven fabric tends to be influenced by the content and dispersion state of carbon fibers, but pores with a size of about 20 to 100 j_un may be formed.
[0068]
The carbon fibers in the nonwoven fabric preferably have an area weight in the range of 10 to 60 g/m2, more preferably in the range of 20 to 50 g/m2. The porous carbon fiber base substrate will have high mechanical strength if the carbon fibers have an areal weight of 10 g/m2 or more while the porous carbon fiber base substrate will have high gas diffusivity and high water removal performance if it is 60 g/m2 or less. If a plurality of nonwoven fabric sheets are stuck, it is preferable for the carbon fiber to have an areal weight in the above range after the pasting.
[0069]
Here, the areal weight of carbon fiber in a porous carbon fiber base substrate can be determined by cutting out a 10 cm x 10 cm piece from a nonwoven fabric sheet, leaving it in an nitrogen atmosphere at a temperature of 450 C for 15 minutes in an electric furnace, and dividing the mass of the residue by the area (0.01 m2) of the piece of nonwoven fabric.
[0070]
<Production method for prepreg>
Nonwoven fabric containing carbon fiber is impregnated with a resin composition to prepare prepreg. Useful methods for impregnating nonwoven fabric containing carbon fiber with a resin composition include a method of dipping nonwoven fabric in a solution containing resin composition, a method of coating nonwoven fabric with a solution containing resin composition, a method of putting a film formed of a resin composition on nonwoven fabric and transferring it. Of these, the method of dipping nonwoven fabric in a solution containing resin composition is preferred because a high productivity is ensured.
[0071]
Here, the resin composition should be one that can be carbonized when baked, to form an electrically conductive carbide. Thus, the baked material has a structure in which discontinuous carbon fibers are bonded to each other with the carbide.
The resin composition is a mixture of resin components mixed as required with a solvent etc. The resin components include resin, such as thermosetting resin, and other required additives, such as carbon based filler and surfactant. The carbonization yield of the resin components contained in the resin composition is preferably 40 mass % or more.
A
carbonization yield of 40 mass % or more is preferable because the porous carbon fiber base substrate will have good mechanical properties, high electrical conductivity, and high thermal conductivity. A higher carbonization yield is more favorable, but at the current technical level, it is generally 70 mass % or less.
[0072]
Useful resins to constitute the resin components include thermosetting resins such as phenol resin, epoxy resin, melamine resin, and furan resin. Of these, phenol resin is preferred because of a high carbonization yield. Furthermore, additives that can be added to the resin components as required include carbon based fillers such as the carbonaceous particles listed previously, which may he used with the aim of improving the mechanical properties, electrical conductivity, and thermal conductivity of porous carbon fiber base substrates. Here, useful carbon based fillers include carbon black, carbon nanotube, carbon nanofiber, milled carbon fiber, and graphite.
[0073]
As the resin compositions, those resin components described above may be used as they are, but may also contain various solvents as required in order to enhance the impregnating ability for papermaking substrates. Here, useful solvents include water, methanol, ethanol, isopropyl alcohol, and acetone.
[0074]
The resin components used for impregnation is preferably account for 30 to 400 parts by mass, more preferably 50 to 300 parts by mass, relative to 100 parts by mass of the carbon fiber. If the impregnation quantity of the resin component is 30 parts by mass or more, it is preferable because the porous carbon fiber base substrate will have good mechanical properties, high electrical conductivity, and high thermal conductivity. If the impregnation quantity of the resin component is 400 parts by mass or less, it is preferable because the porous carbon fiber base substrate will have high gas diffusivity.
[0075]
<Pasting and annealing>
After the prepreg formation, lamination and annealing of prepreg sheets may be performed before carbonization. A plurality of prepreg sheets may be laminated together with the aim of providing a porous carbon fiber base substrate with a predetermined thickness. In this case, a plurality of prepreg sheets with identical properties may be laminated together or a plurality of prepreg sheets with different properties may be laminated together. Specifically, a plurality of prepreg sheets that differ in mean diameter and mean length of single carbon fibers, areal weight of carbon fiber in the papermaking substrate, and impregnation quantity of the resin components may be laminated together.
[0076]
The prepreg may be annealed with the aim of increasing the viscosity of the resin composition or partially cross-linking it. Useful annealing methods include a method of blowing hot air, a method of heating between hot plates in a press apparatus etc., and a method of heating between continuous belts.
[0077]
<Carbonization>
After impregnating carbon fiber non-woven fabric with a resin composition, it is baked in an inert atmosphere for carbonization. Such baking may be performed by CA 028929,18 2015-05-27 using either a batch type heating furnace or a continuous heating furnace.
Such an inert atmosphere can be created by causing an inert gas, such as nitrogen gas and argon gas, to flow through the furnace.
[0078]
The maximum baking temperature is preferably in the range of 1,300 C to 3,000 C, more preferably in the range of 1,700 C to 2,850 C, and still more preferably in the range of 1,900 C to 2,700 C. A maximum temperature of 1,300 C or more is preferable because the resin components will be carbonized to a high degree and the porous carbon fiber base substrate will have high electrical conductivity and high thermal conductivity. On the other hand, a maximum temperature of 3,000 C or less is preferable because the required heating furnace operation cost will decrease.
For the present invention, nonwoven fabric containing carbon fiber that is impregnated with a resin composition and then carbonized is referred to as a porous carbon fiber base substrate.
[0079]
<Hydrophobic treatment>
For the present invention, the porous carbon fiber base substrate may be subjected to hydrophobic treatment with the aim of improving its water removal performance. Hydrophobic treatment may be carried out by adding a hydrophobic polymer to the porous carbon fiber base substrate. There are no specific limitations on the hydrophobic polymer, but, for example, the fluorine resins listed previously may be used. In regard to the quantity of the hydrophobic polymer to be added, it preferably accounts for 1 to 50 parts by mass, more preferably 3 to 40 parts by mass, relative to 100 parts by mass of the porous carbon fiber base substrate. The porous carbon fiber base substrate will have high water removal performance if the hydrophobic polymer accounts for 1 part by mass or more while the porous carbon fiber base substrate will be high in electrical conductivity if it accounts for 50 parts by mass or less.
[0080]
Here, if the hydrophobic polymer is unevenly distributed with a higher concentration near porous layer (A), which is described later, in the porous carbon fiber base substrate, it is preferable because the required quantity of the expensive hydrophobic polymer can be minimized without suffering a performance deterioration for water removal from the catalyst layer to the bipolar plate. A useful method to check for such an uneven distribution of the hydrophobic polymer in the porous carbon fiber base substrate is to observe a cross section of the gas diffusion layer at a magnification of 400 by microscopy, such as scanning electron microscopy, and analyze the fluorine concentration distribution in a cross-sectional direction by using an energy dispersive X-ray spectrometry, electron probe microanalyzer, etc.
[0081]
Described next is the first preferred method for forming a porous layer in a porous carbon fiber base substrate according to the present invention.
[0082]
.Impregnation process (I): formation of porous laycr (J) Porous layer (J) is formed by dispersing carbonaceous particles in a dispersion medium such as water and organic solvent to prepare dispersion liquid (1) and infiltrating it into a porous carbon fiber base substrate. Commonly, a hydrophobic polymer, such as the one used for the hydrophobic treatment described above, is added to dispersion liquid (1). Useful infiltration methods include dipping, die coating, kiss coating, screen printing, rotary screen printing, spraying, intaglio printing, gravure printing, bar coating, and blade coating, of which dipping is preferred because it can CA 028929.18 2015-05-27 realize uniform infiltration. The constitution and solid content of the dispersion liquid may be adjusted appropriately to ensure a porosity of 5% to 40% after the impregnation.
[0083]
Dispersion liquid (1), as well as dispersion liquid (2) and dispersion liquid (3), which are described later, may contain a dispersant such as surfactant. For dispersion liquid (1), as well as dispersion liquid (2) and dispersion liquid (3), which are described later, water is preferably used as the dispersion medium and a nonionic surfactant is preferably used as the dispersant.
[0084]
<Squeezing process (I-2)>
After process (I), a porosity of 5% to 40% may be realized by removing an excess of dispersion liquid (1) from the surface of the porous carbon fiber base substrate using a blade or squeeze roller. The blade may be of an appropriately selected material such as rubber, plastic, and metal. The squeeze roller may also be of an appropriately selected material such as rubber, plastic, and metal, and an appropriately selected method such as nipping and clearance may be used.
[0085]
----Drying process (I'): drying of porous layer (J)>
After undergoing impregnation process (I), and squeeze process (I-2) as required, the porous carbon fiber base substrate is preferably deprived (dried) of the dispersion medium in dispersion liquid (1) by heating at a temperature of 80 C
to 200 C
before feeding it to the subsequent processes.
[0086]
<Deposit process (II): formation of porous layer (A)>
Porous layer (A) is formed by coating one surface, i.e. surface A, of a porous carbon fiber base substrate with dispersion liquid (2) prepared by dispersing carbonaceous particles in a dispersion medium such as water and organic solvent.
Commonly, a hydrophobic polymer, such as the one used for the hydrophobic treatment described above, is added to dispersion liquid (2). Useful coating methods include die coating, kiss coating, screen printing, rotary screen printing, spraying, intaglio printing, gravure printing, bar coating, and blade coating, of which die coating is preferred because it allows quantification of the coating weight regardless of the surface roughness of the porous carbon fiber base substrate.
[0087]
<Drying process (II'): drying of porous layer (A)>
After undergoing deposit process (II), the porous carbon fiber base substrate is preferably deprived (dried) of the dispersion medium in dispersion liquid (2) by heating at a temperature of 80 C to 200 C before feeding it to the subsequent processes.
[0088]
Furthermore, if a fuel cell gas diffusion layer is produced according to the preferred embodiment of this invention in which porous layer (A) and porous layer (J) have the same constitution in forming porous layers on the porous carbon fiber base substrate, the second method that contains deposit-impregnation process (11-3) described below instead of the process described above may be adopted.
[0089]
<Deposit-impregnation process (II-3)>
Porous layer (A) is formed by coating one surface, i.e. surface A, of a porous carbon fiber base substrate with dispersion liquid (2) prepared by dispersing carbonaceous particles in a dispersion medium such as water and organic solvent and, while leaving part of dispersion liquid (2) at the surface, allowing the remaining part of dispersion liquid (2) to infiltrate into the porous carbon fiber base substrate. Commonly, a hydrophobic polymer, such as the one used for the hydrophobic treatment described above, is added to dispersion liquid (2). Useful coating methods include die coating, kiss coating, screen printing, rotary screen printing, spraying, intaglio printing, gravure printing, bar coating, and blade coating, of which die coating is preferred because it allows precise control of the coating weight regardless of the surface roughness of the porous carbon fiber base substrate and ensures easy control of the degree of infiltration into the porous carbon fiber base substrate. If using the die coating technique, the degree of infiltration of dispersion liquid (2) into the porous carbon fiber base substrate can be controlled by adjusting the coating rate, discharge rate, clearance between the discharge rip and the porous carbon fiber base substrate, viscosity of the dispersion liquid, etc.
[0090]
<Drying process (II 3'): drying of porous layer (A), After undergoing deposit-impregnation process (II-3), the porous carbon fiber base substrate is preferably deprived (dried) of the dispersion medium in dispersion liquid (2) by heating at a temperature of 80 C to 200 C before feeding it to the subsequent processes.
[0091]
<Opposite surface deposit process (11-2): formation of porous layer (B)>
After undergoing deposit process (II) or deposit-impregnation process (II-3), the porous carbon fiber base substrate is subjected to a porous layer (B) formation process as required. Porous layer (B) is formed by coating the opposite surface, i.e.
surface B, which is located opposite to the surface coated with porous layer (A), i.e.
surface A of the porous carbon fiber base substrate, with dispersion liquid (3) prepared by dispersing carbonaceous particles in a dispersion medium such as water and organic solvent. Commonly, a hydrophobic polymer, such as the one used for the hydrophobic treatment described above, is added to dispersion liquid (3). Useful coating methods include die coating, kiss coating, screen printing, rotary screen printing, spraying, intaglio printing, gravure printing, bar coating, and blade coating, of which kiss coating and screen printing are preferred for the present invention because they serve for easy control of the coating weight in coating the opposite surface compared to the other techniques.
[0092]
If impregnation process (I) is to be adopted, it is also preferable that porous layer (B), which has the same composition as porous layer (J), be formed at least on one surface of the porous carbon fiber base substrate when porous layer (J) is formed. In this case, opposite surface deposit process (11-2) and drying process (11-2') can be omitted.
[0093]
<Drying process (II-2'): drying of porous layer (B)>
After undergoing opposite surface deposit process (II-2), the porous carbon fiber base substrate is preferably deprived (dried) of the dispersion medium in dispersion liquid (3) by heating at a temperature of 80 C to 200 C before feeding it to the subsequent processes.
[0094]
<Sintering process (III):>
After undergoing deposit process (II) or deposit-impregnation process (II-3), the porous carbon fiber base substrate is subjected to drying process (II'), opposite surface deposit process (II-2), drying process (I1-2'), and drying process (II-3') as required, and then fed to or sent through a muffle furnace, baking furnace, or high-temperature type drying furnace where it is sintered by heating at 300 C
to 3 80 C

CA 028929,18 2015-05-27 for 1 to 30 minutes. If a hydrophobic polymer exists, it is melted during the sintering process and acts to bind the carbonaceous particles to form a porous layer.
[0095]
The coating techniques described above are only given as samples, and the invention is not limited thereto.
[0096]
A membrane electrode assembly (MEA) and fuel cell that use the gas diffusion layer according to the present invention are described next with reference to Fig. 3.
[0097]
For the present invention, a membrane electrode assembly can be produced by forming catalyst layers 9 on both surfaces of a solid polymer electrolyte membrane 8 and then attaching an gas diffusion layer as described above to at least one side thereof.
In doing this, it is preferable to deposit porous layer (A) 1 on the catalyst layer 9, that is, structure the membrane electrode assembly in such a manner that porous layer (A) 1 comes in contact with the catalyst layer 9.
[0098]
Bipolar plates (not shown in Figure) are then formed on both sides of the membrane electrode assembly to form a fuel cell. Commonly, a gasket is provided between each bipolar plate and the relevant surface of the membrane electrode assembly and a plurality of such laminates are stacked to produce a polymer electrolyte fuel cell.
The catalyst layer 9 includes a layer containing a solid polymer electrolyte and carbon material of carbon-supported catalyst. Platinum is commonly used as the catalyst. For a fuel cell in which reformed gas containing carbon monoxide is supplied to the anode, it is preferable to adopt platinum or ruthenium as the catalyst in the anode. The solid polymer electrolyte is preferably of perfluorosulfonic acid based polymer material which is high in protonic conductivity, oxidation resistance, and heat resistance. For fuel cell units and fuel cells, such structural features themselves have been well known.
EXAMPLES
[0099]
The invention is described more specifically below with reference to Examples.

The measuring methods used to determine various characteristics in Examples are described below.
[0100]
<Measurement of thickness etc. of entire gas diffusion layer>
The thickness of the porous carbon fiber base substrate, thickness of the entire gas diffusion layer, and thickness of the porous carbon fiber base substrate having porous layer (J) and porous layer (B) deposited thereon were measured as follows.
Specifically, 20 different points were selected at random on a sheet-like specimen to be examined and the thickness was measured at each point under a pressure of 0.15 MPa using a MF-50 1 micrometer, which is equipped with a micrometer head having a circular cross section with a diameter of 5 mm, manufactured by Nikon Corporation, followed by averaging the individual thickness measurements.
{O 101]
<Measurement of thickness ti of porous layer (A)>
The mean thickness t 1 of porous layer (A) was determined by first measuring the mean thickness of the porous carbon fiber base substrate that has porous layer (J) and porous layer (B) deposited thereon and then subtracting it from the mean thickness of the entire gas diffusion layer.
[0102]
<Measurement of thickness t2 of porous layer (B)>

The mean thickness t2 of porous layer (B) was determined by subtracting the thickness of the porous carbon fiber base substrate and the mean thickness ti of porous layer (A) from the mean thickness of the entire gas diffusion layer.
[0103]
<Measurement of bulk density of porous carbon fiber base substrate>
The bulk density of a porous carbon fiber base substrate is determined by measuring the areal weight (mass per unit area) of the porous carbon fiber base substrate using an electronic balance and dividing it by the thickness of the porous carbon fiber base substrate.
[0104]
<Porosity>
The gas diffusion layer was cut in a direction perpendicular to the sheet plane and subjected to preliminary treatment, and a section for cross-sectional observation was prepared by using a SM-9010 cross section polisher manufactured by JEOL
Ltd.
[0105]
Then, a photograph containing the entire thickness of the gas diffusion layer was taken at a magnification of 400 using an S-4800 field emission-type scanning electron microscope (FE-SEM) manufactured by Hitachi High-Technologies Corporation and it was found that porous layer (A) had been deposited on one surface of the porous carbon fiber base substrate, that porous layer (J) had infiltrated into the porous carbon fiber base substrate and at least partially reached the other surface, i.e.
surface B, and that pores were maintained in the porous carbon fiber base substrate.
Five different points were selected at random in a cross section and the measurements taken at these points were image-processed as described below by HALCON 9.0 image processing software manufactured by MVTec to provide binarized data, from which porosity was determined for each point.
(Image processing) = The size of the total processing area (number of vertical pixels x number of horizontal pixels) was calculated to determine the total area.
= The image was averaged over each 9 pixel area (3 vertical pixels x 3 horizontal pixels) and the noise per pixel is removed to provide image 1.
= From image 1, those regions (porous layer and carbon fiber cross section) that contained non-pore portions and had a luminance that was equal to or greater than an arbitrary mean luminance value or equal to or smaller than an arbitrary mean luminance value were extracted to provide image 2.
= From image 2, only those islands that had a size of 100 pixels or more were extracted to provide image 3.
- Image 3 was subjected to circular closing processing for a radius of 2.5 pixels (to fill small holes) to provide image 4.
= The area of image 4 (i.e., non-pore portion) was determined.
= The area of images 4 was subtracted from the total area to calculate the area of pores, which was then divided by the total area to determine the porosity in one portion.
[0106]
The porosity was calculated in this way for the 5 portions and averaged to provide the mean porosity.
[0107]
<Percentage of void of porous layer>
Specimens similar to those used for porosity determination were prepared.
[0108]
Five different points were selected at random in a cross section of a specimen CA 028929.18 2015-05-27 41.
of the porous layer and observed at a magnification of 20,000 using an S-4800 field emission-type scanning electron microscope (FE-SEM) manufactured by Hitachi High-Technologies Corporation and the measurements taken at these points were image-processed as described below by using HALCON 9.0 image processing software manufactured by MVTec to provide binarized data, from which percentage of void was determined for each point.
(Image processing) = The size of the total processing area (number of vertical pixels x number of horizontal pixels) was calculated to determine the total area.
= The image was averaged over each 9 pixel area (3 vertical pixels x 3 horizontal pixels) and the noise per pixel is removed to provide image 1.
= From image 1, those regions (porous layer cross section) that contain non-void portions and have a luminance that is equal to ut peat= than an atbittaty mean luminance value are extracted to provide image 2.
= From image 2, only those islands that had a size of 100 pixels or more were extracted to provide image 3.
= Image 3 was subjected to circular closing processing for a radius of 2.5 pixels (to fill small holes) to provide image 4.
= The area of image 4 (i.e., non-void portion) was determined.
= The area of image 4 was subtracted from the total area to calculate the area of voids, which was then divided by the total area to determine the percentage of void in one portion.
[0109]
The percentage of void was calculated in this way for the 5 portions and averaged to provide the mean percentage of void.

[0110]
<Number of cracks in the surface of porous layer (A) and porous layer (B)>
Observation was performed at a magnification of 50 using a digital microscope manufactured by KEYENCE CORPORATION to determine the number of isolated cracks in an arbitrarily selected 1 mm x 1 mm area.
[0111]
<Evaluation of fuel cell performance of polymer electrolyte fuel cell>
First, 1.00 g of carbon material of carbon-supported platinum catalyst (manufactured by Tanaka Kikinzoku Kogyo K.K., platinum supporting amount 50 mass %), 1.00 g of purified water, 8.00 g of a Nafion (registered trademark) solution (manufactured by Aldrich, Nafion (registered trademark) 5.0 mass %), and 18.00 g of isopropyl alcohol (manufactured by Nacalai Tesque, Inc.) were added in this order to prepare a catalyst paste.
[0112]
The catalyst paste was sprayed over a 7 cm x 7 cm piece of NAFLON
(registered trademark) PTFE tape TOMBO (registered trademark) No. 9001 (manufactured by NICHIAS Corporation) and dried at room temperature to prepare a PTFE sheet carrying a catalyst layer with a platinum quantity of 0.3 mg/cm2.
Then, a 10 cm x 10 cm piece of a Nation (registered trademark) NRE-211cs solid polymer electrolyte membrane (manufactured by DuPont) was sandwiched between two catalyst layer-covered PTFE sheets and hot-pressed at 130 C under a pressure of 5 MPa in a pressing machine with flat plate to transfer the catalyst layer to the solid polymer electrolyte membrane. After the pressing, the PTFE sheets were removed to provide a solid polymer electrolyte membrane carrying a catalyst layer.
[0113]

Then, the solid polymer electrolyte membrane carrying a catalyst layer was sandwiched between two 7 cm x 7 cm gas diffusion layers and hot-pressed at 130 C
under a pressure of 3 MPa in a pressing machine with flat plate to prepare a membrane electrode assembly. Here, the gas diffusion layer was disposed in such a manner that porous layer (A) was in contact with the catalyst layer.
[0114]
The resulting membrane electrode assembly was incorporated in a fuel cell evaluation unit cell and the current density was measured at different voltages. Here, the bipolar plates used were serpentine, single-flow-channel type ones with a channel width of 1.5 mm, channel depth of 1.0 mm, and rib width of 1.1 mm. For evaluation, hydrogen compressed at 210 kPa was supplied to the anode while air compressed at 140 kPa was supplied to the cathode. It should be noted that both hydrogen and air were humidified by a humidification pot set at 70 C. The utilization ratio of hydrogen and that of oxygen in air were 80% and 67%, respectively.
[0115]
First, the output voltage was measured at an operation temperature maintained at 65 C and a current density set to 2.2 A/cm2 and used as indicator of the anti-flooding characteristic (low temperature performance). The anti-plugging characteristic was evaluated based on observations of the frequency of instantaneous drop in fuel cell performance during a 30 minute period in which the current density was maintained at 2.2 A/cm2. Specifically, the number of times the output voltage dropped below 0.2 V
during the 30 minute period was counted, and the specimen was ranked as C if such a drop occurred 7 times or more, B if it occurred 5 or 6 times, A if it occurred 3 or 4 times, and S if it occurred twice or less. Then, the current density was set to 1.2 A/cm2 and the operation temperature, starting at 80 C, was maintained for 5 minutes and raised by 2 C

CA 028929,18 2015-05-27 in 5 minutes. This procedure was repeated while measuring the output voltage to determine the upper limit temperature where power generation can be performed, which was adopted as indicator of the anti-dry-out characteristic (high temperature performance).
[0116]
(Example I) Polyacrylonitrile based carbon fiber, TORAYCA (registered trademark) T300 manufactured by Toray Industries, Inc. (mean single fiber diameter 7 [irn), was cut to 12 mm length and subjected to a papermaking process in which the fiber undergo sheet-making processing using water as sheet-making medium, dipping in a 10 mass %
aqueous solution of polyvinyl alcohol, and drying, thereby providing a long piece of carbon fiber paper with an areal weight of carbon fiber of 16 g/m2. The polyvinyl alcohol attached to the fiber accounted for 20 parts by mass relative to 100 parts by mass of carbon fiber.
[0117]
A dispersion liquid consisting of flake graphite (mean particle diameter 5 p.m), phenol resin, and methanol mixed at a ratio by mass of 1:9:50 was prepared.
The carbon fiber paper was continuously impregnated with the above dispersion liquid in such a manner that the phenol resin accounted for 104 parts by mass relative to 100 parts by mass of the carbon fiber and the resin impregnation process was finished at a temperature of 90 C to provide resin-impregnated carbon fiber paper (prepreg).
The phenol resin used was a mixture of resol type phenolic resin and novolak type phenolic resin mixed at a ratio by mass of 1:1.
[0118]
A pressing machine was set so that the upper and lower hot plates were parallel CA 028929.18 2015-05-27 to each other and the resin-impregnated carbon fiber paper was subjected to compression treatment to allow it to be heated and compressed at a hot plate temperature of 170 C and a pressure of 0.8 MPa.
[0119]
The compression-treated carbon fiber paper, used as precursory fiber sheet, was fed to a heating furnace that maintains a nitrogen gas atmosphere with a maximum temperature of 2,400 C, and then carbonized to provide a porous carbon fiber base substrate with a thickness of 100 [tm, areal weight of 24 g/m2, and bulk density of 0.24 g/cm3.
[0120]
PTFE resin was added at a ratio of 5 parts by mass relative to 95 parts by mass of the porous carbon fiber base substrate and heat-drying was performed at 100 C to provide a hydrophobic-treated substrate.
[0121]
<Formation of porous layer (A), porous layer (J), and porous layer (B)>
The dispersion liquid designed to form porous layer (J) is referred to dispersion liquid (1); the dispersion liquid designed to form porous layer (A) is referred to dispersion liquid (2); and the dispersion liquid designed to form porous layer (B) is referred to dispersion liquid (3).
[0122]
Dispersion liquid (1) to be used was prepared by mixing carbon black, namely acetylene black, and other components, namely PTFE resin dispersion, surfactant, and purified water, mixed at a carbon black/PTFE resin ratio of 75 parts by mass to 25 parts by mass with the solid components accounting for 15 mass % of the total quantity.
Dispersion liquid (1) was found to have a viscosity of 34 mPa = s when examined with a B type viscometer.
[0123]
Dispersion liquid (1) was put in a stainless steel tray and a porous carbon fiber base substrate was completely dipped in dispersion liquid (1). The liquid attached to the surface was scraped off with a stainless steel spatula and heat-drying was performed at 120 C to provide an impregnated substrate having an impregnation rate of 15 g/m2 after sintering.
[0124]
Dispersion liquid (2) to be used was prepared by mixing carbon black, namely acetylene black, and other components, namely PTFE resin dispersion, surfactant, and purified water, mixed at a carbon blacic/PTFE resin ratio of 75 parts by mass to 25 parts by mass with the solid components accounting for 22 mass % of the total quantity.
[0125]
Dispersion liquid (2) was applied to the impregnated substrate using a die coater and heat-drying was performed at 120 C to provide a coated substrate.
[0126]
The heat-dried coated substrate was heated at 380 C to prepare a gas diffusion layer including a porous carbon fiber base substrate that contains porous layer (J) in its interior and has porous layer (A) on one surface. Porous layer (A) had a mean thickness ti (j.1m) of 40 i_tm and porous layer (A) had an areal weight of 20 g/m2. It was found that porous layer (J) was exposed in some parts of the opposite surface, i.e.
surface B, of the porous carbon fiber base substrate. Those parts of porous layer (J) existing at the opposite surface, i.e. surface B, were defined as porous layer (B) with a mean thickness of t2 (p.m) of 0 gm.
[0127]

The porosity of the resulting gas diffusion layer was calculated at 31% and the percentage of void of porous layer (J) and porous layer (A) in the resulting gas diffusion layer was calculated at 52% for porous layer (J) and 75% for porous layer (A).
[0128]
Furthermore, the resulting gas diffusion layer was examined for cracks in the surface of porous layer (A), but no cracks were found.
[0129]
For the resulting gas diffusion layer, fuel cell performance was evaluated and results showed a very good anti-plugging characteristic. The output voltage was 0.38 V
(operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 91 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1.
[0130]
(Example 2) Except that porous layer (A) had a mean thickness ti (um) of 15 i.un and that porous layer (A) had an areal weight of 8 g/m2 after sintering, the same procedure as in Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)> was carried out to produce a gas diffusion layer. Evaluation results of the fuel cell performance of this gas diffusion layer showed a good anti-plugging characteristic. The output voltage was 0.37 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C
(humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1. No cracks were found in the surface of porous layer (A).

=

[0131]
(Example 3) Except that porous layer (A) had a mean thickness t 1 (1.1m) of 52 1AM and that porous layer (A) had an areal weight of 26 g/m2 after sintering, the same procedure as in Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)> was carried out to produce a gas diffusion layer. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic.
The output voltage was 0.36 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C
(humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1. One crack was found in the surface of porous layer (A).
[0132]
(Example 4) As described in Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, dispersion liquid (1) was put in a stainless steel tray and a porous carbon fiber base substrate was completely dipped in dispersion liquid (1).
Then, except that the liquid attached to the surface was not scraped off with a stainless steel spatula before heat-drying at 120 C, that porous layer (B) with a mean thickness t2 (um) of 10 um was formed over the entirety of the opposite surface, i.e. surface (B), of the porous carbon fiber base substrate, and that an impregnated substrate having an impregnation rate of 22 g/m2 (porous layer (J) 15 g/m2 + porous layer (B) 7 g/m2) after sintering was obtained, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic. The output voltage was 0.33 V
(operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 92 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1. No cracks were found in the surface of porous layer (A).
[0133]
(Example 5) In Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, dispersion liquid (1) prepared had a carbon black/PTFE resin ratio of 75 parts by mass to 25 parts by mass and a solid content of 21%. This dispersion liquid (1) = was found to have a viscosity of 46 mPa = s when examined with a B type viscometer.
This dispersion liquid (1) was put in a stainless steel tray and a porous carbon fiber base substrate was completely dipped in this dispersion liquid (1). The liquid attached to the surface was scraped off with a stainless steel spatula and heat-drying was performed at 120 C to provide an impregnated substrate having an impregnation rate of 29 g/m2 after sintering. Except for this, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. This gas diffusion layer had a porosity of 10%.
Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic. The output voltage was 0.33 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 92 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table I. No cracks were found in the surface of porous layer (A).
= [0134]
(Example 6) In Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, dispersion liquid (1) prepared had a carbon blacic/PTFE resin ratio of 75 parts by mass to 25 parts by mass and a solid content of 7%. This dispersion liquid (1) was found to have a viscosity of 16 mPa-s when examined with a B type viscometer.
This dispersion liquid (1) was put in a stainless steel tray and a porous carbon fiber base substrate was completely dipped in this dispersion liquid (1). The liquid attached to the surface was scraped off with a stainless steel spatula and heat-drying was performed at 120 C to provide an impregnated substrate having an impregnation rate of 8 g/m2 after sintering. Except for this, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. This gas diffusion layer had a porosity of 38%.
Evaluation results of the fuel cell performance of this gas diffusion layer showed a good anti-plugging characteristic. The output voltage was 0.38 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C (humidification temperatuic 70C, cuticat density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1. No cracks were found in the surface of porous layer (A).
[0135]
(Example 7) In Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, dispersion liquid (2) prepared had a carbon black/PTFE
resin/surfactant/purified water ratio of 75 parts by mass to 25 parts by mass and a solid content of 22%, and except for this, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. Porous layer (A) produced from this dispersion liquid (2) had a mean thickness ti (j.tm) of 43 m, an areal weight of 20 g/m2, and a percentage of void of 80%. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic. The output voltage was 0.39 V

(operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C (humidification temperature 70 C, current density 1.2 Akm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1. No cracks were found in the surface of porous layer (A).
[0136]
(Example 8) In Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, dispersion liquid (2) prepared had a carbon black/PTFE
resin/surfactant/purified water ratio of 75 parts by mass to 25 parts by mass and a solid content of 23%, and except for this, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. Porous layer (A) produced from this dispersion liquid (2) had a mean thickness ti (pm) of 30 p,m, an meal weight of 20 g/m2, and a percentage of void of 52%. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic. The output voltage was 0.32 V
(operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1. No cracks were found in the surface of porous layer (A).
[0137]
(Example 9) Except for decreasing the thickness setting for molding, the same procedure as in Example 1 was carried out to produce a porous carbon fiber base substrate with a thickness of 75 pm, an areal weight of 24 g/m2, and a bulk density of 0.32 g/cm3, and then hydrophobic treatment was performed as in Example 1 to provide a hydrophobic-treated substrate.
[0138]
Except that this hydrophobic-treated substrate was used and that the impregnated substrate produced according to <Formation of porous layer (A), porous layer (J), and porous layer (B)> had a porous layer (J) impregnation rate of 11 g/m2 after sintering, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. This gas diffusion layer had a porosity of 23%. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic.
The output voltage was 0.39 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C
(humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-fluoding elialactelistie and anti-dry-out characteristic as seen in Table 1. No cracks were found in the surface of porous layer (A).
[0139]
(Example 10) Except that carbon fiber paper with an areal weight of carbon fiber of 32 g/m2 was obtained in the carbon fiber papermaking process in Example 1 and that impregnation was carried out in the resin impregnation process in such a manner that the resin impregnation quantity was 290 parts by mass of phenol resin relative to 100 parts by mass of carbon fiber, the same resin impregnation procedure as in Example 1 was carried out to produce a porous carbon fiber base substrate with a thickness of 200 m, an areal weight of 80 g/m2, and a bulk density of 0.40 g/cm', followed by performing hydrophobic treatment as in Example 1 to provide a hydrophobic-treated substrate.

[0140]
Except that this hydrophobic substrate was used and that the impregnated substrate produced according to <Formation of porous layer (A), porous layer (J), and porous layer (B)> had a porous layer (J) impregnation rate of 28 g/m2 after sintering, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. This gas diffusion layer had a porosity of 37%. Evaluation results of the fuel cell performance of this gas diffusion layer showed a good anti-plugging characteristic. The output voltage was 0.32 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 92 C
(humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1. No cracks were found in the surface of porous layer (A).
[0141]
(Example 11) A porous layer was formed according to the procedure described in <Formation of porous layer> given below on a hydrophobic-treated substrate prepared in Example 1 to provide a gas diffusion layer.
[0142]
<Formation of porous layer>
The same dispersion liquid (2) as in Example 1 was applied over the above-mentioned hydrophobic-treated substrate using a die coater. In doing this, the discharge rip of the die coater was brought close to the above-mentioned hydrophobic-treated substrate to allow dispersion liquid (2) to infiltrate into the interior of the porous carbon fiber base substrate and the porosity in the CP was controlled close to the value in Example 1. After the coating, heat-drying was carried out at 120 C to =

produce a coated substrate.
[0143]
The heat-dried coated substrate was heated at 380 C to prepare a gas diffusion layer in which porous layer (A) and porous layer (J) had the same constitution. This means that both porous layer (A) and porous layer (J) were formed from dispersion liquid (2). Porous layer (A) had a mean thickness ti (um) of 19 um and porous layer (A) had an areal weight of 20 g/m2. It was found that porous layer (J) was exposed in some parts of the opposite surface, i.e. surface B, of the porous carbon fiber base substrate.
[0144]
The porosity of the resulting gas diffusion layer was calculated at 31% and the percentage of void was calculated at 75% for both porous layer (J) and porous layer (A) in the resulting gas diffusion layer.
[0145]
Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic. The output voltage was 0.39 V

(operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic;
and anti-dry-out characteristic as seen in Table 2. No cracks were found in the surface of porous layer (A).
[0146]
(Example 12) Except that the above hydrophobic-treated substrate was replaced with the hydrophobic-treated substrate obtained in Example 9 and that the coating weight was adjusted to allow the porosity in the CP to be close to the value in Example 9, the same procedure as in Example 11 was carried out to produce a gas diffusion layer.
The replacement of the porous carbon fiber base substrate resulted in porous layer (A) with a mean thickness t1 (gm) of 25 gm. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic. The output voltage was 0.39 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 2. No cracks were found in the surface of porous layer (A).
[0147]
(Example 13) Except that the hydrophobic-treated substrate obtained in Example 10 was used and thai the uuating weight was adjusted to allow the areal weight of porous layer (A) in <Formation of porous layer> to be 29 g/m2 and allow the porosity in the CP to be close to the value in Example 10, the same procedure as in Example 11 was carried out to produce a gas diffusion layer. Evaluation results of the fuel cell performance of this gas diffusion layer showed a good anti-plugging characteristic. The output voltage was 032 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 92 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and anti-dry-out characteristic as seen in Table 1. No cracks were found in the surface of porous layer (A).
[0148]
The constitutions used in Examples 1 to 13 and evaluation results are summarized in Tables 1 and 2.

, .

=
0149]
.
Table 1]
Example Example Example Example Example Example Example Example Example Example Porous carbon thickness(pm) 100 100 100 10C
100 100 100 , 100 75 200 fiber base substrate bulk density (g/cm3) 0.24 0.24 024 0.24 0.24 0.24 0.24 0.24 0.32 0.40 mean thickness t1 (m) 40 15 52 40 40 40 43 , 30 40 40 Porous layer coating weight (g/m2) 20 8 26 20 _ , (A) percentage of void in MPL (%) number of surface cracks (-) 0 0 1 0 0 . 0 0 0 0 0 impregnation weight (g/m2) 15 15 15 15 Porous layer percentage of void in MPL (%) 52 52 52 52 (J) exposed at opposite surface B yes yes yes yes yes yes yes yes yes yes .
.-..
porosity in CP (%) 31 31 31 31 10 38 31 31 23 37 .
mean thickness of t2 (um) 0 0 0 10 0 0 0 0 0 0 .
Porous layer coating weight (g/m2) 0 0 0 7 0 - .
(B) .
percentage of void in MPL (%) - - - 52 - - - - -output voltage [V]
Anti-flooding (operation temperature 65 C, 0.38 0.37 0.36 0.33 0.33 0.38 0.39 0.32 0.39 0.32 characteristic humidification temperature 70 C, current density 2.2 A/cm2) voltage drop frequency evaluation Anti-plugging humidification temperature 65 C, humidification temperature 70 C, S A S S S
A S S S A
characteristic current density 2.2 A/cm2, maintained for 30 min) upper limit temperature [ C]
Anti-dry-out (humidification temperature 70 C, 91 90 92 92 characteristic current density 1.2 A/cm2) = .

, 0150]
.
Table 2]
Example 11 Example 12 Example 13 Porous carbon fiber base thickness (urn) 100 substrate bulk density (g/cm3) 0.24 0.32 0.40 dispersion liquid (2) coating weight (gim2) 20 20 29 mean thickness ti (iim) 19 Porous layer (A) percentage of void in MPL (%) 75 number of surface cracks (-) 0 Porous layer (J) percentage of void in MPL (%) 75 (same composition exposed at opposite surface B yes yes yes as porous layer (A)) porosity in CP
(%) 31 23 37 P
mean thickness of t2 (pm) 0 0 0 .
Porous layer (B) coating weight (g/m2) 0 -...
a percentage of void in MPL (%) - .
.
output voltage [V]

Anti-flooding (operation temperature 65 C, = 8 0.39 0.39 0.32 .1 characteristic humidification temperature 70 C, current density 2.2 A/cm2) voltage decrease frequency evaluation (operation temperature 65 C, Anti-plugging humidification temperature 70 C, current S
S A
characteristic density 2.2 A/cm2, maintained for 30 min) upper limit temperature [DC]
Anti-dry-out characteristic (humidification temperature 70 C, current 90 density 1.2 A/cm2) [0151]
(Comparative example 1) Except that impregnation with dispersion liquid (1) was omitted in Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, the same procedure as in Example 1 was carried out to produce a gas diffusion layer.
Evaluation results of the fuel cell performance of this gas diffusion layer showed a largely deteriorated anti-plugging characteristic. The output voltage was 0.38 V
(operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 88 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a good anti-flooding characteristic and a deteriorated anti-dry-out characteristic as seen in Table 3. The poor high-temperature performance is attributed to the fact that the porous carbon fiber base substrate was free of porous layer (J), allowing water vapor to escape into the bipolar plate to cause the electrolyte membrane to dry significantly. No cracks were found in the surface of porous layer (A).
[0152]
(Comparative example 2) Except changing the coating weight of dispersion liquid (2) to allow porous layer (A) to have a mean thickness ti (gm) of 60 pm and allow porous layer (A) to have an areal weight of 30 g/tri.` in Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic. The output voltage was 0.29 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 86 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a deteriorated anti-flooding characteristic and anti-dry-out characteristic as seen in Table 3. The poor low-temperature performance is attributed to the fact that the increased thickness of porous layer (A) acted to prevent water vapor from being discharged from the catalyst layer while the poor high-temperature performance is attributed to the fact that the through-plane gas diffusivity in the gas diffusion layer was low to prevent fuel from being supplied sufficiently to the catalyst. Six cracks were found in the surface of porous layer (A).
[0153]
(Comparative example 3) In Example I <Formation of porous layer (A), porous layer (J), and porous layer (B)>, dispersion liquid (3) prepared had a carbon black/PTFE resin ratio of 75 parts by mass to 25 parts by mass and a solid content of 24%. In Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, impregnation with dispersion liquid (1) was omitted, but dispersion liquid (2) was applied over the surface of the porous carbon fiber base substrate as in Example 1 to prepare a coated substrate and then, dispersion liquid (3) was applied over the opposite surface, i.e.
surface B, using a die coater, followed by drying and sintering under the same conditions as in Example 1 to provide a gas diffusion layer that had porous layer (A) and porous layer (B). Porous layer (B) had a mean thickness t2 (gm) of 30 gm, an areal weight of 15 g/m2, and a percentage of void of 66%. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic.
Output voltage could not be obtained in the anti-flooding characteristic evaluation (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a largely deteriorated anti-flooding characteristic and a good anti-dry-out characteristic as seen in Table 3. The poor low-temperature performance is attributed to the thick porous layer (B) which acted to decrease the discharge of water into the bipolar plate. No cracks were found in the surface of porous layer (A).
[0154]
(Comparative example 4) In Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, dispersion liquid (1) prepared had a carbon black/PTFE resin ratio of 75 parts by mass to 25 parts by mass and a solid content of 23%. This dispersion liquid (1) was found to have a viscosity of 50 mPa = s when examined with a B type viscometer.
This dispersion liquid (1) was put in a stainless steel tray and the hydrophobic-treated substrate was completely dipped in this dispersion liquid (1). Then, except that the liquid attached to the surface was not scraped off with a stainless steel spatula before heat-drying at 120C for 10 minutes, that porous layer (B) with a mean thickness t2 (p.m) of 11 gm was formed over the entirety of the opposite surface, i.e.
surface (B), of the porous carbon fiber base substrate, and that an impregnated substrate having an impregnation rate of 43 g/m2 (porous layer (J) 35 g/m2 + porous layer (B) 8 g/m2) after sintering was obtained, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. Evaluation results of the fuel cell performance of this gas diffusion layer showed a very good anti-plugging characteristic. This gas diffusion layer had a porosity of 2%. The output voltage was 0.25 V (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 89 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a deteriorated anti-flooding characteristic and anti-dry-out characteristic as seen in Table 3. The poor low-temperature performance is attributed to the fact that the porous carbon fiber base substrate was filled with dense porous layers (J) that acted to prevent water vapor from being discharged from the catalyst layer while the poor high-temperature performance is attributed to the fact that the dense porous layers (J) acted to maintain a low through-plane gas diffusivity in the gas diffusion layer, preventing fuel from being supplied sufficiently to the catalyst. One crack was found in the surface of porous layer (A).
[0155]
(Comparative example 5) In Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)>, dispersion liquid (2) prepared had a carbon black/PTFE resin ratio of 75 parts by mass to 25 parts by mass and a solid content of 23%, and except for this, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. Porous layer (A) produced from this dispersion liquid (2) had a mean thickness ti ( m) of 25 an areal weight of 20 g/m2, and a percentage of void of 45%. Evaluation results of the fuel cell performance of this gas diffusion layer showed a good anti-plugging characteristic. Output voltage could not be obtained in the anti-flooding characteristic evaluation (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 88 t (humidification temperature 70 C, current density 1.2 A/cm2), representing a deteriorated anti-flooding characteristic and a deteriorated anti-dry-out characteristic as seen in Table 3. The poor low-temperature performance is attributed to the fact that porous layer (A) is low in percentage of void to prevent water vapor from being discharged from the catalyst layer while the poor high-temperature performance is attributed to the fact that porous layer (A) low in percentage of void acted to decrease the through-plane gas diffusivity in the gas diffusion layer, preventing fuel from being supplied sufficiently to thc catalyst. No cracks were found in the surface of porous layer (A).
[0156]
(Comparative example 6) Except that carbon fiber paper of 28 g/m2 was obtained in the carbon fiber papermaking process in Example 1 and that impregnation was subsequently carried out in the resin impregnation process in such a manner that the resin impregnation quantity was 403 parts by mass of phenol resin relative to 100 parts by mass of carbon fiber to produce resin-impregnated carbon fiber paper, followed by compressing a stack of two sheets of the resin-impregnated carbon fiber paper in a pressing process, the same resin impregnation procedure as in Example 1 was carried out to produce a porous carbon fiber base substrate with a thickness of 350 gm, an areal weight of 175 g/m2, and a bulk density of 0.50 g/cm3. Then, hydrophobic treatment was performed as in Example 1 to provide a hydrophobic-treated substrate.
[0157]
Except that by using this hydrophobic-treated substrate, the impregnated substrate produced in Example 1 <Formation of porous layer (A), porous layer (J), and porous layer (B)> had a porous layer (J) impregnation rate of 38 g/m2 after sintering, the same procedure as in Example 1 was carried out to produce a gas diffusion layer. This gas diffusion layer had a porosity of 30%. Evaluation results of the fuel cell performance of this gas diffusion layer showed a good anti-plugging characteristic.
Output voltage could not be obtained in the anti-flooding characteristic evaluation (operation temperature 65 C, humidification temperature 70 C, current density 2.2 A/cm2) and the upper limit temperature was 90 C (humidification temperature 70 C, current density 1.2 A/cm2), representing a largely deteriorated anti-flooding characteristic and a good anti-dry-out characteristic as seen in Table 3. The poor low-temperature performance is attributed to the fact that the porous carbon fiber base substrate had a large thickness and a large bulk density, which acted to decrease the discharge of water into the bipolar plate. No cracks were found in the surface of porous layer (A).
[0158]
The constitutions used in Comparative examples 1 to 6 and evaluation results are summarized in Table 3.

.
0159]
.
Table 3]
Comparative Comparative Comparative Comparative Comparative Comparative example 1 example 2 example 3 example 4 example 5 example 6 Porous carbon thickness (pm) 100 , fiber base substrate bulk density (g/cm3) 0.24 0.24 0.24 0.24 0.24 0.50 . _ mean thickness ti (pm) 35 60 coating weight (g/m2) 20 30 Porous layer (A) percentage of void in MPL (%) 75 75 number of surface cracks (-) 0 6 impregnation weight (g/m2) 0 15 0 35 15 38 ' P
percentage of void in MPL (%) - 52 - 52 52 52 .
Porous layer (J) .
exposed at opposite surface B no yes no yes yes yes g ,' porosity in CP (A) 46 31 39 2 31 30 , 40 co .., mean thickness of t2 (pm) - 0 30 11 0 0 .
In Porous layer (B) coating weight (g/m2) - 0

15 8 0 0 ' 1$
percentage of void in MPL (%) - -output voltage [V]
Anti-flooding .. (operation temperature 65 C, 0.38 0.29 - 0.25 - -characteristic humidification temperature 70 C, current density 2.2 A/cm2) , voltage decrease frequency evaluation (operation temperature 65 C, Anti-plugging humidification .
temperature 70 C, C S
S S A A
characteristic current density 2.2 Akm2, maintained for 30 min) _ upper limit temperature [ C]
Anti-dry-out characteristic 1 (humidification temperature 70 C, 88 86 I
current density 1.2 A/cm2) EXPLANATION OF NUMERALS
[0160]
1. porous layer (A) 2. porous layer (J) 3. porous layer (B) 4. carbon fiber 5. pore 6. void 7. carbonaceous particles (or hydrophobic polymer) 8. electrolyte membrane 9. catalyst layer

Claims (24)

CLAIMS:

1. A fuel cell gas diffusion layer comprising:
a porous carbon fiber base substrate comprising discontinuous carbon fibers bonded to each other with carbide, wherein the porous fiber base substrate (i) has a thickness of 60 to 300 gm and a bulk density of 0.20 to 0.45 g/cm3, (ii) is impregnated with a porous material (J) containing carbonaceous particles at least part of which is exposed at opposite surface B thereof, and (iii) has internal pores with a cross-sectional area accounting for 5% to 40% of the total cross section in a through-plane direction in the porous carbon fiber base substrate, and a porous layer (A) with a mean thickness tl of 10 to 55 gm and containing carbonaceous particles deposited on a surface A of the porous carbon fiber base substrate, wherein at least the porous layer (A) and the porous material (J) both have a percentage of void of 50% to 85%.

2. The fuel cell gas diffusion layer according to claim 1, wherein the porous layer (A) and the porous material (J) have different constitutions.

3. The fuel cell gas diffusion layer according to claim 1, wherein the porous layer (A) and the porous material (J) have the same constitution.

4. The fuel cell gas diffusion layer according to any one of claims 1 to 3, wherein the carbonaceous particles contained in the porous layer (A) or the porous material (J) account for to 95 mass%.

5. The fuel cell gas diffusion layer according to any one of claims 1 to 4, wherein the percentage of void of the porous layer (A) is higher than the percentage of void of the porous material (J).

6. The fuel cell gas diffusion layer according to any one of claims 1 to 5, wherein the porous carbon fiber base substrate, the porous material (J), and the porous layer (A) further contain a hydrophobic polymer.
Date Recue/Date Received 2022-06-17

7. The fuel cell gas diffusion layer according to claim 6, wherein the hydrophobic polymer is distributed unevenly in the porous carbon fiber base substrate, with a larger concentration near the porous layer (A).

8. The fuel cell gas diffusion layer according to any one of claims 1 to 7, wherein the carbonaceous particles of the porous material (J) and the porous layer (A) contain at least carbon black.

9. The fuel cell gas diffusion layer according to any one of claims 1 to 8, wherein the crack frequency in the porous layer (A) is smaller than the crack frequency in the porous material (J).

10. The fuel cell gas diffusion layer according to any one of claims 1 to 9, wherein the crack frequency in the porous layer (A) is one per square millimeter or less.

11. The fuel cell gas diffusion layer according to any one of claims 1 to 10 further comprising a porous layer (B) with a mean thickness t2 of 0 to 20 um deposited on the opposite surface B, the porous layer (B) containing at least carbonaceous particles.

12. The fuel cell gas diffusion layer according to any one of claims 1 to 11 wherein the porous layer (B) further contains a hydrophobic polymer.

13. The fuel cell gas diffusion layer according to claim 11 or 12, wherein the carbonaceous particles of the porous layer (B) contain at least carbon black.

14. The fuel cell gas diffusion layer according to any one of claims 11 to 13, wherein the porous layer (B) and the porous material (J) have the same constitution.

15. The fuel cell gas diffusion layer according to any one of claims 11 to 14, wherein the carbonaceous particles contained in the porous layer (B) account for 5 to 95 mass %.

16. The fuel cell gas diffusion layer according to any one of claims 11 to 15, wherein the percentage of void of the porous layer (A) is higher than the percentage of void of the porous layer (B).
Date Recue/Date Received 2022-06-17

17. A production method for the fuel cell gas diffusion layer as defined in any one of claims 1 to 10 comprising:
providing:
a precursor porous material (J) in the form of a dispersion liquid (1) that contains at least the carbonaceous particles and a dispersion medium (1), a precursor porous layer (A) in the foiin of a dispersion liquid (2) that contains at least the carbonaceous particles and a dispersion medium (2), and the porous carbon fiber base substrate, performing an impregnation process (I) to impregnate the porous carbon fiber base substrate with the dispersion liquid (1), performing a deposit process (II) to deposit the dispersion liquid (2) on the surface A of the porous carbon fiber base substrate, thereby forming the precursor porous layer (A) on the surface A of the porous carbon fiber base substrate, and subsequently heating and sintering the porous carbon fiber base substrate with the precursor porous layer (A) thereon, thereby forming the porous carbon fiber base substrate impregnated with the porous material (J) and having the porous layer (A) deposited on the surface A.

18. The production method for the fuel cell gas diffusion layer according to claim 17, further comprising, prior to the depositing of the dispersion liquid (2), heating the porous carbon fiber base substrate to remove the dispersion medium (1).

19. A production method for the fuel cell gas diffusion layer as defined in any one of claims 3 to 10 comprising:
Date Recue/Date Received 2022-06-17 providing:
a precursor porous layer (A) in the foim of a dispersion liquid (2) that contains at least the carbonaceous particles and a dispersion medium (2), and the porous carbon fiber base substrate, performing a deposit process (11-3) to deposit the dispersion liquid (2) on the surface A
of the porous carbon fiber base substrate, and infiltrating the dispersion liquid (2) into the porous carbon fiber base substrate, thereby forming a precursor porous material (J) and the precursor porous layer (A) on the surface A of the porous carbon fiber base substrate, and subsequently heating and sintering the porous carbon fiber base substrate with the precursor porous layer (A) thereon, thereby forming the porous carbon fiber base substrate impregnated with the porous material (J) and having the porous layer (A) deposited on the surface A.

20. The production method for the fuel cell gas diffusion layer according to any one of claims 17 to 19, wherein at least one of the dispersion liquid (1) and the dispersion liquid (2) further contains a hydrophobic polymer.

21. The production method for the fuel cell gas diffusion layer according to any one of claims 17 to 20, further comprising, prior to the heating and sintering, heating the porous carbon fiber base substrate to remove the dispersion medium (2).

22. A production method for the fuel cell gas diffusion layer as defined in any one of claims 11 to 16 comprising:
performing the method of any one of claims 17 to 21, wherein the providing further comprises providing:
a precursor porous layer (B) in the form of a dispersion liquid (3) that contains at least the carbonaceous particles and a dispersion medium (3), Date Recue/Date Received 2022-06-17 the method further comprising, prior to the heating and sintering, performing an opposite surface deposit process (II-2) to deposit the dispersion liquid (3) on the opposite surface B of the porous carbon fiber base substrate, wherein the heating and sintering thereby forms the porous carbon fiber base substrate further having the porous layer (B) deposited on the opposite surface B.

23. The production method for the fuel cell gas diffusion layer according to claim 22, wherein the dispersion liquid (3) further contains a hydrophobic polymer.

24. The production method for the fuel cell gas diffusion layer according to claim 22 or 23, further comprising, prior to the depositing of dispersion liquid (3), heating the porous carbon fiber base substrate to remove the dispersion medium (3).
Date Recue/Date Received 2022-06-17