CA2820465A1 - High strength and high elasticity composite materials and methods of reinforcing substrates with the same - Google Patents

Abstract

In accordance with various embodiments of the disclosed subject matter, a composite material is provided. The composite material in accordance with some embodiments of the disclosed subject matter includes a high tenacity fiber reinforced polymer fabric and a polyurea coating layer formed on at least one surface of the polymer fabric. The composite material provides significant strength, flexibility, and energy dissipation. In some embodiments, the composite material can be used to reinforce structural and non-structaral. substrates.

Description

HIGH STRENGTH AND HIGH ELASTICITY COMPOSITE MATERIALS AND
METHODS OF REINFORCING SUBSTRATES WITH THE SAME
Cross Reference to Related Applications [00011 This application claims the benefit of United States Provisional Patent Application No. 61/420,159, filed December 6, 2010, which is hereby incorporated by reference herein in its entirety.
Convridit Notice [00021 A portion of the disclosure of this patent document contains material which is subject to copyright protection. The copyright owner has no objection to the facsimile reproduction by anyone of the patent document or the patent disclosure, as it appears in the Patent and Trademark Office patent file or records, but otherwise reserves all copyright rights whatsoever.
Technical Field [00031 The disclosed subject matter relates to a composite material comprising a high tenacity fiber reinforced polymer fabric, such as a carbon fiber reinforced polymer, and a polyurea layer coated on at least one surface of the polymer fabric. The disclosed subject matter also relates to reinforcing a substrate, such as a wood, concrete, masonry, steel, or other component, with the composite material.
Background [00041 Earthquakes remain one of nature's deadliest lotus. One way in which earthquakes cause darriage is the stress they exert on buildings and other snuctures due to ground shaking and ground rupture. The damage can render buildings and other structures unusable, or at worst, cause their outright collapse, often resulting in human injuty or death.
For example, the 2010 earthquake in Haiti caused significant damage or destruction to many homes and to the health care infrastructure, resulting in over 170,000 casualties and affecting over 3 million people.

100051 Furthermore, earthquakes, such as, for example, the 19.06 San Francisco earthquake, often initiate associated fire disasters (Lee "fire fbllowing earthquake" disasters).
The earthquake-associated fires can significantly contribute to the economic.
losses and to the loss of life related to the original earthquake event. Regions of northern and southern California that lie along the San Andreas Fault and its various sister Inuits are primary candidates for a "fire following earthquake" disaster due to their population and infrastructure density. Recent modeling of present-day damage resulting from a "fire following earthquake" disaster of the same magnitude as the 1906 San Francisco earthquake and tire estimated that nearly 10 million residents of northern California would be impacted by economic, social, and mortality factors. The overall economic losses were estimated to be about Si 50 billion dollars.
100061 In addition .to earthquakes and other seismic events,. structural damage can also be caused by other natural or non-natural events that exert stresses on buildings and other structures, including, for example, hurricanes, tornados, landslides, flash flooding, tsunamis, and explosions due to Warfare or terrorism., Moreover, structural damage can occur even in the absence of a particular catastrophic event. For example, damage to structures can be caused by regular long-term use, long-term exposure to environmental factors, and/or increased use and/or loading of structures due to increasing population demands.
100071 For at least these reasons, various approaches have been made to strengthen structural elements, such as concrete slabs, walls, beams, columns, and foundations. For example, one approach for strengthening new and existing concrete structural elements is by reinforcing them with a variety of steel shapes, such as steel meshes, steel reinforcement bars, and steel grids. However, steel or other suitable metals used for reinforcing these structural elements are subject to corrosion. The products of corrosion result in an expansion of the column of the steel which causes a spalling effect, which can cause a breakup and deterioration of the concrete stsucture. In addition, .while other corrosion-resistant materials have been considered, these materials bring about other difficulties, such as delamination, less ductility, or higher cost.
10008j Accordingly, it is desirable to provide high strengthõ highly dampedõ and/or high elasticity composite materials that overcome these and other deficiencies of the prior art.
100091 For example, there is an ongoing need for protection systems to reinforce structures (e.g., buildings and other infrastructure) against damage due to torsion and/or shear and tensile stresses, such as might be experienced, for example, during structural accelerations and displacements, or to strengthen them following such damage.
In addition, thereis 'a need for materials that can also protect buildings and other infrastructurefrom fire damage and/or that can provide other additional protection, suchas from ultraviolet radiation, water damage, and/or environmental pollutants, and/or that can provide an insulative effect, e.g., to reduce heating andlor cooling costs in the reinforced structures.
Summary 10010) In accordance with Various eiribodiments:of the disclosed subject matter, a composite material is provided. The composite material in accordance with some embodiments of the disclosed subject matter includes a high tenacity fiber reinforced polymer fabric and a polyurea coating layer .formed on at least one surface of the polymer fabric.. The composite material provides significant strength, flexibility, viscous damping, and energy dissipation. hi some embodiments, the composite material can also be formed to have additional protecting properties, such as fire resistant: properties, UV
protective properties, or moisture resistant properties.
1001.1.j The composite material can be used in a variety of applications.
For exampleõ
the composite material can be used to .reinforce structural and/or non-structural substrates to protect them from damage (e.g., due to seismic or wind activity, fire, impact, loading, and/or explosive threes). In another example, the composite material can be used to strengthen structural and/or non-structural substrates following damage by forming the composite.
material on at least one surface of the substrate (e.g., tightly wrapped around the entire substrate, formed over a crack in the substrate, etc.). In yet another example, the composite material can be used to provide a particular protective property to a substrate, such as U.V.
protection, fire resistance, corrosion resistance, moisture resistance, and/or energy efficiency.
In yet another suitable example, the composite material can be used as a stand-alone structure that is strong, stiff, and provides significant damping, while also providing one or more protective properties, such as UV protection, .fire resistance, corrosion resistanceõ moisture resistance, and/or energy-efficiency.
100121 In a more particular example, the composite material can be used to provide energy dissipation and sustainable strength properties to light-frame wood.constructionõ
concrete and masonry structures, and/or steel structures to save occupant lives and protect infrastructure during extreme loading events (e.g., an earthquake or human-induced hazards having high impact loads involving ballistics or blast loads). In some embodiments, the composite material can be used for the lightweight design of vehicle components, which would improve safety, performance, and fuel efficiency.

1001.3j la:some .embodiments, the disclosed subject matter can provide a protection system that reduces structural accelerations and displacements by combining a high strength/high stiffness material with sustainable energy dissipation and ductility. .In some embodiments, this protection system can include a composite material that is tightly wrapped around or applied as a ply .to (e.g., adhered to) an exterior lace or surface of a substrate, thereby providing viscoelastic behavior properties that transition to a sustainable .elastomeric state by sustaining the interfacial interaction between the composite material and the .underlying substrate. The composite material can act as an energy-release valve by providing sustainable energy dissipation and large viscous-type damping during extreme loading events, such as during earthquakes, that minimize structural damage to the substrate. In some embodiments, the composite/substrate system can allow fOr a. change in viscous damping ratio (e.g., the composite/substrate system has a different viscous damping ratio than the substrate alone).
100141 in accordance with some embodiments of the disclosed subject matter, a composite material is provided, the composite .material comprising: a substrate; a .fiber reinforced polymer fabric layer attached to at least a portion of the substrate; and a. polyurea coating layer formed on an exposed surface of the fiber reinforced polymer fabric layer.
100151 In some embodiments, the substrate is one of: wood, masonry, concrete, steel, and a combination thereof 100161 In some embodiments, the substrate has at least one damaged portion and the fiber reinforced polymer fabric layer and the polyurea coating layer are formed on the at least one damaged portion of the substrate.
100171 .In some embodiments, the fiber reinforced. polymer fabric layer is a carbon fiber reinforced polymer fabric.
100181 In some embodiments., the polyurea. coating layer is formed by applying an elastomeric polyurea-forming component solution to the exposed surface of the fiber reinforced .polymer fabric layer, wherein the elastomeric polyurea-forming component.
solution forms an aromatic polyurea coating layer.
1001.91 In some embodiments, the polyurea further comprises an additive component, .wherein the additive component is at least one of an ultraviolet (UV) protective additive, a flame retardant, a corrosion protective additive, a moisture resistance additive, and ceramic microspberes.
100201 in accordance with some embodiments, a method for reinforcing a substrate is provided, the method comprising: providing a substrate; attaching a high tenacity .tiber reinforced polymer fabric to atleasta portion of the.substrate, applying a saturant composition to an exposed surface of the high tenacity fiber reinforced polymer fabric, wherein the saturant composition comprises a polymer resin; curing the saturant composition to ibrin a tacky surface; applying an elastomeric polyurea-forming component solution to the tacky surface; and curing the polyurea-forming component .solution to form a polyurea coating layer:
100111 :La some embodiments, the method further comprises; applying a primer layer to a surface of .the substrate; and applying another saturant composition to the primer layer.
The primer layer can be used to prepare the substrate andlor assist layers to bond with the substrate. The saturant composition can be used to bond the high tenacity fiber reinforced polymer fabric with the substrate.
100221 In some embodiments, the substrate is one of: wood, masonry, concrete, steel, and a combination thereof 100231 in some embodiments, the substrate is used in one of a newly constructed.
structure and an existing structure.
100241 In some embodiments, the method further comprises performing surface preparation on at least a portion of the substrate, wherein the surface preparation includes at least one of: smoothing the substrate, filling in one or more damaged portions of the substrate with a putty material, and cleaning the substrate, 100251 In some embodiments, the high tenacity fiber reinforced polymer fabric is wrapped around the substrate.
100261 In some embodiments, the polyurea-forming component solution comprises an isocyanate component and a polyamine component, the method further comprising mixing the isocyanate component and the polyamine component prior to applying it to the tacky surface of the saturant to form the .polyurea-forming component solution. The polyurea-forming component solution .may, in some embodiments, have an excess of the isocyanate component.
100271 In some embodiments, the method further comprises spraying the 'polyurea-forming component solution on the tacky surface.
100281 In some embodiments, the method further comprises providing an additive component into the polyurea-forming component solution, wherein the additive component is one of: an ultraviolet (DV) protective additive, a flame retardant, a corrosion protective additive, a moisture resistance additive, and ceramic microspheres, 100291 In some embodiments, the polyurea coating layer has a thickness, the .method furthetcomprising controlling the thickness 017 the polyurea coating layer.
100341 .In some embodiments, the method. further comprises applying the polyurea -forming component solution to form the polyurea coating layer alter a given time when the saturant composition on the high tenacity fiber reinforced fabric layer has become tacky and controlling the thickness of the polyurea coating layer. In some embodiments the given time is between about two hours and about five hours.
1003.11 In some embodiments, the saturant composition is cured for a first time period and wherein the .polyurea-forming component solution is cured for a. second time period, the method further comprising modifying the first time period and the second time period to obtain material properties of the polyurea coating layer on the high tenacity fiber reinforced polymer fabric.
100321 In some embodiments, a first component of the polyurea,lbrining component solution and a second component of the tacky surface of the saturant composition applied to the high tenacity fiber reinforced polymer fabric interact to form a sustainable interface between the polyurea coaling layer and the high tenacity fiber reinforced polymer fabric.
100331 In accordance with some embodiments, a method for reinforcing a substrate having damaged portions is provided, the method comprising: forming a.
polyurea-coated high tenacity fiber reinforced polymer fabric, wherein the forming comprises:
providing a high tenacity fiber reinforced polymer fabric; applying a saturant composition to a. surface of the high tenacity fiber reinforced polymer fabric, wherein the saturant composition comprises a polymer resin; curing the saturant composition to form a tacky surface;
applying an elastomeric polyurea-forming component solution to the tacky surface: and curing the polyurea-forming component solution to form a polyurea coating layer on the high tenacity fiber reinforced polymer fabric; preparing at least a portion of the substrate for reinforcement prior to positioning the polyurea-coated high tenacity fiber reinforced polymer fabric on the substrate; and attaching the polyurea-coated high tenacity -fiber reinforced polymer fithric to at least the damaged portions of the substrate.
100341 In some embodiments, the method further comprisesapplying a puny to the substrate having damaged portions to create a smooth surface on the sttbstrate.
100351 In some embodiments, the method further comprises applying another saturant composition to an interface between the substrate and the high tenacity fiber reinforced polymer Fabric.
100361 In some embodiments, the method further comprises .forming the polyurea coating layer of a thickness based at least in part onan.aSSessment of the damaged portion of the substrate.
100371 .fri some embodiments, the method, further comprises forming the polyurea coating layer after a given .time when the saturant composition on the high tenacity fiber reinforced fabric layer has become tacky and based at least in part on an assessment of the damaged portion of .the substrate.
100381 In sonic embodiments, at least a first..component.of the polyurea-forming.
component solution and a second component of the tacky surface of the saturant composition.
applied to the high tenacity fiber reinforced polymer fabric interact to form a sustainable interface between the polyurea coating layer and the high tenacity fiber reinforced polymer fabric.
100391 In some embodiments, the method further comprises .forming a plurality of polyurea-coated high tenacity fiber reinforced polymer fabrics and attaching each of the plurality of polyurea-coated high tenacity fiber reinforced polymer fabrics to a different .portion of the substrate.
Brief Description of the Drawings 100401 FIG. I is an illustrative cross-section ofa composite having at least a 'high tenacity fiber reinforced polymer fabric layer and a. polyurea coating layer formed on a surface or a substrate in accordance with some embodiments of the disclosed subject matter.
100411 FIG, 2 is an illustrative example of a process for forming a composite having at least a high tenacity fiber reinforced polymer -fabric layer and a polyurea coating, layer on a.
surface of a substrate in accordance with some embodiments of the disclosed subject matter.
100421 FIG. 3 is an illustrative example of a process for retrofitting a substrate (e.g., a damaged substrate) with a composite having at. least a high tenacity fiber reinforced polymer fabric layer and a polyurea coating layer in accordance with some embodiments of the disclosed subject matter, 100431 FIG. 4 is an illustrative graph of tensile -force versus axial displacement that compares the properties of carbon fiber reinforced polymer fabrics with the properties of .polyurea-coated carbon fiber reinthrced polymer fabrics in accordance with some embodiments of the disclosed subject matter.
100441 FIG. 5 is an illustrative graph of torque versus angle of twist that compares the.
torsion properties of a wooden rod wrapped with a carbon fiber reinforced polymer fabric with the torsion properties of a wooden rod wrapped with a polyurea-coated.
carbon fiber reinforced polymer fabric composite in accordance with some embodiments of the disclosed subject matter..
100451 FIG: 6A is an illustrative force-deflection graph showing the results of wood 'beam bending studies performed on various wood substrates in accordance with some embodiments of the disclosed subject matter.
190461 FIG. 6B is an illustrative image of testinr., equipment and a composite-wrapped wood beam during the testing that provided the results shown. in. FIG. 6A.
100471 FIG. 6C is an illustrative image of a composite-wrapped wood beam after the testing using the testing equipment shown in FIG. 6B.
[00481 FIG. 7 is an illustrative force-deflection graph showing the results of wood.
'beam bending study on a wood beam substrate that was wrapped in a composite having a reinforced polymer fabric layer and a polyurea coating layer (one eighth of an inch thick) in accordance with some embodiments of the disclosed subject matter, 100491 FIG. 8 is an illustrative graph showing the strain capacities and elastameric flow of various wood substrates in accordance with some embodiments of the disclosed subject matter..
100501 FIG. 9 is an illustrative graph showing load deflection curves for various wood substrates in accordance with some embodiments of the disclosed subject matter.
100511 FIG. WA is a mph of a simulated acceleration-time history of a two-story wooden structure wrapped with a composite in accordance with some embodiments of the disclosed subject matter.
[0052] FIG: 10B is a graph of a simulated acceleration-time history of a two-story wooden structure wrapped without a composite in accordance with some embodiments of the disclosed subject matter.
[0053] FIG, IOC are illustrative hysteresis curves of the two-story wooden structure in FIGS. WA and I OB subjected to forces similar to an earthquake in accordance with some embodiments of the disclosed subject matter.
[0054] FIG. 11A. shows illustrative images of preparing and retrofitting a damaged substrate with a polyurea-coated carbon fiber reinforced polymer fabric composite in accordance with some embodiments of the disclosed subject: matter 100551 FIG. 1 lB shows illustrative cross-sections along the retrofitted substrate in.
accordance with some embodiments of the disclosed subject matter, 100561 FIG. liC shows illustrative load deflection curves in various retrofitted steel reinforced concrete composite beams in accordance with Sonic embodiments of the disclosed subject matter.

100571 FIG. .12A. Shows illu.strative :images of preparing and retrofitting a damaged shear wall substrate with a polyareaacoated carbon -fiber reinforced polymer fabric in accordance with some embodiments of the disclosed subject matter, 1.00581 FIG. 1213 shows illustrative force deflection curves in various retrofitted shear wall substrates in accordance with some embodiments of the disclosed subject matter.
100591 FIG. 12C shows images that illustrate the increase in ductility, confinement, and compression strength for a damaged shear wall substrate retrofitted with a poly-urea--coated carbon .fiber reinforced polymer fabric composite in accordance with some embodiments of the disclosed subject matter.
I006O FiGJ3A shows images that. illustrate the results of impact testing between a foam core substrate with a carbon fiber reinforced polymer fabric and a -polyurea-coated carbon fiber reinforced polymer composite in accordance with some embodiments of the disclosed subject matter.
100611 FIG, 13B shows an illustrative force versus displacement graph during impact testing of a foam core substrate with a carbon fiber reinforced polymer fabric and a polyttrea-coated carbon fiber reinforced polymer composite in accordance with some embodiments of the disclosed subject matter..
100621 FIG. 14A shows the viscous damping properties of a thin steel beam substrate with a carbon fiber reinforced polymer fabric and a polyurea-coated carbon fiber reinforced polymer composite in accordance with some embodiments of the disclosed subject matter.
100631 Ha 14B shows the power spectrum and model properties of a thin, steel beam substrate with a. carbon fiber reinforced .polymer fabric and a polyurea-coated carbon fiber reinforced polymer composite in accordance with some embodiments of the disclosed subject matter.
100641 FIG. 15A shows the damping ratio as a. function of 'thickness of the polyarea coating layer for a thin steel beam with a polyurea-coated carbon fiber reinforced polymer.
composite, where the damping ratio of a thin steel beam with a polyurea-coated carbon .fiber reinforced polymer composite is compared. with the damping ratio of a thin steel beam and a thin steel beam with a carbon fiber reinforced polymer fabric, in accordance with some embodiments of the disclosed subject matter.
100651 FIG. 15B shows the damp*: ratio as a function of curing time for a.
ann.:steel 'beam with a polyurea-coated carbon fiber reinforced polymer composite in accordance with some embodiments of .the disclosed subject matter.
100661 FIG. 15C shows the damping ratio as a function of thickness of the pelyurea õ, , coating, layer for a polyurea-coated carbon .fiber reinforced polyiner composite by itself, where the damping ratio of the polyurea-coated carbon fiber reinforced polymer composite is compared with the damping ratio of a carbon fiber reinforced polymer fabric, in accordance with some embodiments of the disclosed subject matter.
100671 FIG. 15D shows the damping ratio as a function of curing time for a polyurea-coated carbon fiber reinforced polymer composite by itself in accordance with some embodiments of the disclosed subject matter.
Detailed .Descrintion 100681 The disclosed subject matter will now be described more fully hereinafter with reference to the accompanying examples and drawings, in which representative embodiments are shown. The presently disclosed subject matter can, howeverõ be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the embodiments to those skilled in the art.
100691 Throughout the specification and claims, a given chemical formula or name shall encompass all optical and stereoisomers, as well as racemie mixtures where such isomers and mixtures exist.
DEFINITIONS.
100701 While the following terms are believed to be well understood by one of ordinary skill in the art, the following definitions are set forth to facilitate explanation of the disclosed subject matter.
100711 Unless defined. otherwise, all technical and scientific terms used herein have the same meaning as commonly understood to one of ordinary skill in the an to which the presently disclosed subject matter belongs. Although any methods, devices, and materials similar or equivalent: to those described herein can be used in the practice or testing of the presently disclosed subject matter, representative methods, devices, and materials are now described.
100721 Following long-standing patent law convention, the terms "a," "an,"
and 'the"
refer to "one or more" when used in this application, including the claims.
Thus, for example, reference to -an additive" includes a plurality of such additives, and so forth.
100731 Unless otherwise indicated, all numbers expressing quantities of size, amount, elongation percentage, tensile strength, reaction conditions, and so forth used in the - -specification and claims are to be -understood as being modified in all instances:by the term "about." Accordingly, unless indicated to the contrary, the numerical parameters set forth in this specification and attached claims are approximations that can vary depending upon the desired properties sought to be obtained by the presently disclosed subject matter.
100741 As used herein, the term "about," when .referring to a value or to an amount of size, weight, concentration, time, or percentage is meant to encompass variations of., in some embodiments 20%, in some embodiments 10%, in some embodiments -15%, in some embodiments 11%, and in some embodiments -10.1% from the specified amount, as such VariatiODS are appropriate to perform .the disclosed methods.
100751 The .term "and/or" when used to describe two or more activities, conditions., or outcomes refers to situations wherein both of the listed conditions are included or wherein only one of the two listed conditions are included.
[00761 The term "comprising," which is synonymous with "including,"
"containing,"
or "characterized by" is inclusive or open-ended and does not exclude additional, tareeited elements or method steps, "Comprising" is a term of art used in claim language which means that the named elements are essential, but other elements can be added and still form a.
construct within the scope of the claim, 100771 As used herein, the phrase "consisting or excludes any element, step, or ingredient not specified in the claim. When the phrase "consists of' appears in a clause of the body of a claim, rather than immediately following the preamble, it limits only the element set forth in that clause; other elements are not excluded from the claim as a whole.
10078) As used herein, the phrase "consisting essentially of' limits the scope of a claim to the specified materials or steps, plus those that do not materially affect the basic and novel characteristic(s) of .the claimed subject matter.
100791 With .respect to the terms "comprising," "consisting of," and "consisting essentially of," where one of these three terms is used herein, the presently disclosed and claimed subject matter can include the use of either of the other two terms.
100801 The term "fiber" generally refers to an elongated body the length dimension of which is much greater than the transverse dimensions of width and thickness.
The term fiber includes either manufactured or natural .monofilament, multifilament, ribbon, strip, staple and other forms of chopped, cut or discontinuous fiber and the like having regular or irregular cross-section. The term "fiber" includes a plurality of any of the foregoing or a combination thereof.
100811 In some embodiments, the cross sections of the fibers may be circular, flat or oblong. They may be irregular otregulat multi-lobal cross-section having one or more regular or irregular lobes .projectinerom the linear .or longitudinal axis of the fibers.
100821 High tenacity fibers are fibers that have high ultimate tensile strength and a.
high modulus of elasticity (e,g,õ a high Young's modulus or tensile _modulus), High tenacity fibers include, but are not limited to, highly oriented, 'high molecular weight polyolefin fibers, particularly high modulus polyethylene fibers and polypropylene fibers; aramid fibers;
polybenzazole fibers such as polyhenzoxazole (PBO) and .polybenzothiazole (PBT);
polyvinyl alcohol .fibers; polyacrylonitrile fibers; liquid crystal copolyester fibers; glass fibers; carbon fibers; basalt or other mineral fibers; as well as rigid rod polymer fibers; and mixtures and 'blends thereof. In some embodiments, the high tenacity fiber is carbon fiber, glass fiber (e.q.õ e-glass or s-glass), aramid (e.gõ meta- or para-aramid), liquid crystal copolvester fiber, basalt fiber or a combination thereof.
100831 Fabrics comprising high tenacity fibers can include a network of fibers in the form of a woven, knitted or a non-woven fabric. In some embodiments, at least 50% by weight of the fibers in the fabric are high tenacity fibers. in some embodiments, at least about 75% by weight of the fibers in the fabric are high tenacity fibers. In some embodiments, substantially all of the fibers in the fabric are high tenacity fibers.
100841 The fabrics of the presently disclosed subject matter can comprise one or more different high tenacity fibers. In some embodiments, the yarns in the fabric can be essentially parallel in alignment. In some embodiments, the yarns can be twisted, over-wrapped or entangled. The fabrics of the presently disclosed subject matter can be woven with yams having different fibers in the warp and weft directions, or in other directions.
100851 As used herein, a "monomer" refers to a molecule that can undergo polymerization, thereby contributing constitutional units (i.e., an atom or group of atoms) to the essential structure of an oligomer or polymer, 100861 An "oligomer" refers to a molecule of intermediate relative molecular mass, the structure of which comprises a small plurality of units (e.g., between about 2 and about 10 repeating units) derived from molecules f lower relative molecular mass, 100871 A "polymer" refers to a molecule comprising a plurality of repeating units derived from smaller molecules (e.g., monomers or oligomers). In some embodiments, the polymer has more than 10 repeating units, more than 25 repeating units, more than 50 repeating units, or more than 100 repeating units. in some embodiments, a polymer can have more than 1,000, more than 5,000, more than 10,000, more than 50,000, more than 100,000 repeating units, or more than 250,000 repeating units.

10088l A "copolymer".refers.to a polymer derived from more than one species monomer.
100891 The term "prepolymer" refers to a monomer, oligomer or short chain polymer with reactive terminal groups (e.g., epoxy, ester, carboxylic acid (or carboxylate), hydroxyl, viol, or amine groups) that can react to form a larger (e.g., higher molecular weight) polymer or copolymer. In some embodiments, "short chain polymer" refers to a polymer with 1,000 repeating units or less (e.g., 1,000, 750, 500, 400, 300, 200, 150, 100, 75, 60, 50, 40, or 30 repeating units or less). In some embodiments, a. short chain polymer has molecular weight of less than 10,000 elmol (e.g., less than 10,000, 7,500, 5,000, 4,000, 3,000, 2,000, or 1,000 Owl).
100901 The term "resin" or "polymer resin" as used herein refers to a composition comprising one or more polymeric, oligomeric or monomeric materials that can be hardened by polymerization. Thus, in some embodiments, a resin is a viscous liquid, composition that can be polymerized to form a solid. Suitable resins include, but are not limited to, epoxy resins, vinyl ester resins, polyester resins and methylmethacrylate resins.
100911 The hardening (or further polymerization) of the resin can also be referred to as "curing." in some embodiments, the curing requires a polymerization initiator, e.g., an organic peroxide. In some embodiments, the level of curing is dependent on time and temperature. In some embodiments, "curing" refers to partial curing, e.g., wherein the further polymerization of the resin is allowed to proceed to about 10%, 20%, 30%, 40%, 50%, 60%, 70%, 80%, or 90% completion (i.e,, leaving about 90, 80, 70, 60, 50, 40, 30, 20, or about 10% unreacted polymerizable groups as compared to the percentage of polymerizable groups present in the resin prior to curing).
[0092] The term "tacky" as used herein refers to a partially cured resin., e.g., a resin or saturant wherein some level of polymerization of the original resin has occurred, but wherein there are still unreacted, polymerizable groups available.
[0093] The term "polyurea" refers to a polymer comprising multiple urea bonds (i.e., bonds having the structure ¨NR-C(=0)-NR-, wherein R is H, alkyl, or aryl).
Polyureas can be formed by the reaction of isocyanate-terminated prepolymers and amine-containing components (e.g., amine-terminated polymer resins, amine-terminated oligomers, or amine-containing monomers).
100941 The term "isoeyanate" refers to the group 100951 The term "amine" refers to the group ---NR.'R", wherein R' and R"
are independently H. alkyl, or aryl. "Primary amines" are compounds wherein both R' and R"

are ft "Secondary aminee.are compounds wherein ane of R' and R" is. H and the otheds=
.alkyl or aryl.
100961 As used herein, the term "alkyl" refers to Cl..20 inclusive, linear (i.e., "straight-chain"), branched, or cyclic, saturated or at least partially and in some cases fully unsaturated alkenyl and alkynyl) hydrocarbon chains, including for example, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, ren-butyl, pentyl, hexyl, octylõ ethenyl, propenylõ butenyl, pentenyl, hexenyl, amyl, butadienyl, propynyl, butynyl, pentynyl, hexynyl, heptynyl, and allenyl groups. "Branched" refers to an alkyl group in which a lower alkyl group, such as methyl, ethyl or propyl, is attached to a linear alkyl chain. "Lower alkyl"
refers to an alkyl group having 1 to about 8 carbon atoms (i.e., a Ci4 alkyl.), e.g., 1, 2, 3, 4, 5, 6, 7, or 8 carbon atoms. -Higher alkyl" refers to an alkyl group 'having about 10 to about 20 carbon atoms, e.g., 10, I I, 12, 13, 14, 1.5, 1.6,17, 18, 19, or 20 carbon atoms. In certain embodiments, "alkyl" refers, in particular, to Ciõ.8 straight-chain alkyls. In other embodiments, "alkyl"
refers, in particular, to Ci.s 'branched-chain alkyls.
10097j Alkyl groups can optionally be substituted with one or more alkyl group substituents, which can be the same or different. The term "alkyl group substiment" includes but is not limited to alkyl, halo, arylamino., acyl, hydroxyl, aryloxyl, alkoxyl, alkylthio, arylthio, aralkyloxyl, aralkylthio, carboxyl, alkoxycarbanyl, oxo, and cycloalkyl. There can he optionally inserted along the alkyl chain one or more oxygen, sulfur or substituted or unsubstituted nitrogen atoms, wherein the nitrogen substituent is hydrogen, lower alkyl (also referred to herein as "alkylaminoalkyl"), or aryl.
10098j The term "aryl" is used herein to refer to an aromatic substituent win& can be a single aromatic ring or multiple aromatic rings which are fused together, linked covalently, or linked to a common group such as a methylene or ethylene moiety. The common linking group can also be a carbonyl as in benzophenone or oxygen as in dipheny tether or nitrogen in diphenylamine. The aromatic ring(s) can include phenyl, naphthyl, biphenyl, diphenylether, diphenylamine and 'benzophenone among others. In particular embodinients, the term "aryl"
means a cyclic aromatic comprising about 5 to about 10 carbon atoms, including 5- and 6-membered hydrocarbon and heterocyclic aromatic rings, 100991 The aryl group can be optionally substituted with one or more aryl group substituents which can be the same or different, where "aryl group substituent" includes.
alkyl, aryl, aralkyl., hydroxy, alkoxyl, aryloxy, aralkoxyl, rarboxy, aryl, halo, nitro, alkoxycarbonylõ aryloxycarbonyl, aralkoxycarbonyt, acyloxyl, acylamino, aroy !amino, carbamoyl, alk.ylcarbamoyl, dialkylcarbamoy.1, arylthioõ alkylthio, alkylene and --NR.R.", Where R. and IC' can be each independently:hydrogen, alkyl,.aryl and aralkyl.
101.001 Specific examples:of aryl groups include but are not limited to cyclopentadienyl, phenyl, furan, thiophene, pyrrole, py.nm, pyridine, imidazole, isothiazole, isoxazole, pyrazote, pyrazine,.pyrimidine, and the like, [0101] The term "microspheres" refers to particles having at least one dimension less than about 1000 microns. In some, but .not all, embodiments, microspheres are essentially spherical and have a diameter of less than about 1000, 750, Soo, 400, 300, 200, 100, 75, 50, 25, .10, S. or 1 microns. In some embodiments, microspheres can be irregular in shape, or have a rod-like, disc, or cubic shape.
GENERAL CONSIDERATIONS
101021 Generally speaking, the disclosed stibiect matter provides a composite material that includes a high .tenacity fiber reinforced polymer fabric and a polyurea coating layer formed on the high tenacity fiber reinforced polymer fabric. The composite material can be formed on any suitable substrate .(e.g., wood, reinforced concrete, steel, any other suitable substrate, and/or any combination thereof). The composite material provides a material that integrates viscoelastic behavioral properties via sustainable interfacial interaction between the composite material and the underlying substrate, 10103] The composite material can be used in a variety of applications.
For example, the composite material can be used to reinforce structural and/or non-structural substrates to protect them from damage (e.g.., due to seismic activity, fire, impact, loading,, author explosive forces), In another example, the composite material can be used to strengthen structural and/or non-stnictural substrates following damage by forming the composite material on at least one surface of the substrate (e.g., tightly wrapped around the entire substrate, formed over a crack in the substrate, etc.). In yet another example, the composite material can be used to provide a particular protective property to a substrate, such as UV
protection, lire resistance, corrosion resistance, moisture resistance, and/or energy efficiency.
[0104] in a more particular .embodiment, the disclosed subject matter can provide a protection system that reduces structural accelerations and displacements by combining a high strength/high stiffness material with sustainable energy dissipation and ductility. In some embodiments, this protection system can include a composite material that is tightly wrapped around or applied as a ply (e.g,, adhered to) an exterior face or surface of a substrate, thereby providing viscoelastic behavior properties that transition to a sustainable elastomeric state by sustaining the interfacial interaction between the composite material and.
-the underlying substrate. The composite. material can aetas an energy-release -valve by providing sustainable energy dissipatiou and large viscous-type damping during extreme loading events, such as during earthquakes, that minimize structural damage to the substrate.
In some embodiments, the composite/substrate system can allow for a change in viscous damping ratio (e.g, the composite/substrate system has a different viscous damping ratio than the substrate alone).
10.1.05) in another suitable embodiment, the composite material of the disclosed subject matter can be used to construct a stand-alone structure having high strength, high stiffness, and provides significant damping. in addition, the composite material can provide one or more protective properties, such as UV protection, fire resistance, corrosion resistance, moisture resistance, and/or energy-efficiency. For example, the composite material can be used to manufacture automotive parts, sporting goods equipment:, and bicycle frames, among others. In a more particular example, each of these parts or structures may have a desirable set of properties, such as a damping ratio greater than a. given percentage.
As explained hereinbelowõ the composite material can be modified by varying curing dines and/or varying the thickness of the polyurea coating layer to achieve particular properties.
101061 As described herein, the composite material can include a layer of high tenacity fiber reinforced polymer .(FRP) and a layer of elastomeric polyurea formed on the layer of high tenacity fiber reinforced polymer. In a more particular embodiment, a high tenacity -fiber reinforced polymer fabric can be attached to a. substrate using a first saturant composition, a second saturant can be applied, to the exposed .surface of the high tenacity fiber reinforced polymer fabric and cured until fbrming a tacky surface, and an elastorneric polyurea can be formed on the tacky surface. Use of the polyurea coating layer can increase ductility and energy dissipation by about 1.00% in a composite as compared to that of the relatively stiff and brittle FRP alone.
101071 In some embodiments, the properties of the composite material can be described as a function of time-related ttej and volume-fraction (ho) polymeric properties.
For example, it has been determined that. time-related factors in the preparation of the composite material (e.g.., time factors related to the reaction of the precursors of the polyurea layer and the precursors of the polymer of the FRP) can affect the viscous properties and/or elongation percentage of the FRP and/or composite as a whole, thereby enabling the strength of the restating load-bearing composite to be sustained at large deformations, 101081 For example, as described herein, studies of the disclosed composites and of composite-wrapped wood-frame structures indicate that wrapping substrates with the presently diselosed composite material can synergistically confine the substrate and provide a continuous load path, for example, between the foundation of the wrapped wood-frame structure and its roof. Moreover, no de-bonding was exhibited between the individual composite wrap constituents or between the wrap and the wood frame substrate.
Accordingly, the interaction, or synergy, of the exterior composite tight-wrap and the frame can be used to replace the interaction of an exterior wood sheathing diaphragm and the .frame, for example, via the fasteners typically used in traditional wood structures.
The integration of large viscous-type damping can preclude reliance on the hysteretic damping of the shear wall fasteners, which can pull .through or withdraw from the .framing during ground motions, or the minimal viscous damping that is ordinarily provided by structural and non-structural components in traditional wood structures.
101091 In another example, as described herein, the disclosed composites can be applied to reinforced concrete beams, shear walls, and other structures:: More particularly, a:
structure or structural element can be retrofitted with the composite material. A damaged structural element having multiple cracks such that the after-test load capacity dropped. to approximately 40% of its peak value can be retrofitted with the composite material. Upon forming the composite material over portions of the damaged structural element, the reinforced structural element recovered its original load capacity and received a significant increase in the ductility of the structural element. The ductility of the composite .material thrilled on the structural element allows the structural element to experience large deformations. That is, .the energy after the formation of cracks can be readily dissipated, thus inhibiting the formation of new crack surfaces and inhibiting further damage from occurring.
101101 .In some embodiments, the composite material wrapped around a substrate can reduce accelerations and elastic displacements in wrapped substrates up until their peak loading stress via an increase in strength, stiffness and viscous properties.
During extreme loading, where an unwrapped substrate would have been loaded inelastic:ally and beyond its maximum strength, the composite wrap can provide, in some embodiments, a "sustainable negative stiffness" to help minimize damages by inducing a viscous damping mechanism to stabilize crack substrate growth (by invoking stable crack energy- release) and dissipate strain energy, allowing the wrapped substrate to sustain a high level of strength.
Models of the viscoelestie behavior of the wrapped substrates can be developed based, for example, on existing nonlinear constitutive material .models formulated on continuum mechanics theory.
Seeõ e.g., .Attard, TI et al .õ1. qf Eng. Mechanics, ASCE., 134(10), 881 (2008), Which is:
incorporated by reference herein in its entirety.

COMPOSITES
[01.111 .In some embodiments, the disclosed subject matter provides a composite comprising a fabric that is coated on at least one surface with a coating layer comprising an elastomeric polyurea, where the fabric is a high tenacity fiber reinforced by a polymer matrix (sometimes referred to herein as a fiber reinfbrced polymer (FRP) fabric). The composite is sometimes referred to herein as CarbonFlex.
[01.12) Referring to FIG. 1, a cross-section of a substrate surface reinforced with a composite in accordance with some embodiments of the disclosed .subject matter is provided.
As shown in cross-section of .FICi. 1, a substrate 1.00 can be provided. As generally described.
'herein, substrate 100 can be made of any suitable material., such as, for example, wood, masonry (eq., 'brick, stone, stucco, tile), concrete (including concrete reinforced with steel or other .metal), steel, or combinations thereof, [0113] It should be noted that the composite can be formed without a substrate. That is, the composite can be used to construct a stand-alone structure.
Alternatively, the composite can be formed without a substrate and, at a later time, attached to a substrate.
101.141 In some embodiments, substrate 100 may be damaged and include cracks, pits, chips, and/or grooves in .the surface of substrate 100. To provide a uniform and/or a smooth surface, substrate 100 can be prepared by using a putty material. As shown in FIG. 1, putty material 101 has been applied to provide a smooth surface for reinforcement with the composite. Alternatively, any suitable procedure may be performed to prepare substrate 100.
For example, abrasive blasting; can be performed to remove loose material from the surface of substrate 100. in another example, epoxy resin and/or cementitious mortars can be applied to repair portions of the surface of substrate 100.
101.151 It should be noted that putty material 105 applied to substrate 1.00 may not be used for a newly constructed structure or substrate that is generally undamaged.
[0116] in some embodiments, substrate I 0(1 (and its prepared surface) can be in contact with a primer 1.1.0 and a first saturant: composition 120. Primer 110 can be also in contact with one side of a high tenacity fiber reinforced polymer fabric 130 (e.g., the high tenacity fiber fabric with the polymeric matrix formed by curing of, for example, the first saturant composition 120). Attachment of the fiber reinforced polymer fabric 104 can be performed. such that during curing of the polymer matrix in fabric. 130 an interaction or 'bonding (eg., covalent bonding') takes place between the polymeric components of primer HD, saturant composition 1.20, and/or the fiber reinforced polymer fabric 130.
For example,.
primer .110 and/or first saturant composition '120 can improve :the bonding of the high 18..-tenacity fiber reinforced polymer fabric 130 with substrate 100. In another example, primer can improve the. bonding ffirst saturant. composition 120 with substrate 100.
In yet another example, a predetermined amount of time may elapse before forming, additional layers to allow the high tenacity fiber reinforced polymer fabric 130 to band or interact with substrate 100.
101171 In sonic embodiments, the exposed side of the fiber reinforced polymer fabric 130 can be in contact with a polyurea coating layer 150., at interface 135:=
More particularly,. a =
second saturant composition 140 can be applied to the exposed surface of the fiber reinforced polymer fabric 130. When a tacky surfiece, is formed by at least partially curing the second.
saturant composition 140 for a given period of time (e.g., about two hours to five hours), a palyurea coating layer 150 can be formed on the high tenacity fiber reinforced polymer fabric 130. Polymeric components from both fiber reinforced polymer fabric 130 with second saturant composition 140 and polyurea coating layer 140 can interact (e.g., via covalent bonding) at interface 135 to prevent separation of fiber reinforced polymer fabric. 130 and polyurea coating layer 1.40 following complete curing of the composite, it should also be noted that curing the second .saturant composition can, in some embodiments, cure the first saturant composition applied between substrate 100 and fiber reinforced polymer fabric 130.
101181 It should be noted that the thickness of the polyurea coating layer 150 can be varied based on .the desired properties of the composite-coated substrate. It should also be noted that the properties of the composite (e.g., viscous damping properties versus stiffness properties) can generally be modified by modifying time-related (tc) and volume-fraction (.hp) polymeric properties. For example, the tune related to the reaction of the precursors of the polyurea coating layer 150 and the polymer of the fiber reinforced polymer .fabric 110 can affect the viscous properties andior elongation percentage of the composite as a whole.
101191 In some embodiments, if desired, an additive layer 110 can be formed on one side of the polyurea coating layer 108. Additive layer 110 can contain, for example, ceramic mierospheres or an additional protect= layer (e.g., a moisture resistance layer, a UV
protective layer, a corrosion resistance layer, a flame retardant layer, etc.). in some embodiments, optional additive layer 1.10 is absent.
101.201 Accordingly, the interaction, or synergy. of various components within the primer layer 110, the -first saturant. composition layer 120, the fiber reinforced polymer fabric layer 130, the second saturant composition layer 140, the polyurea coating layer 150, andlor the additive layer 160 form .the composite having desirable strength., stiffness, and. damping properties. The strength, stiffness, and damping properties of the composite can be modified based on time-telated (tõ) and -volume-aaction (11v) polymeric properties.
Foreixample, time -related factors in .the preparation of the composite material (e.g.., the time to Cure the second saturant composition, w.hich creates an interaction between components of the polyurea coating layer 150 and the precursors of the polymer of the fiber reinforced polymer fabric layer 130) can affect the viscous properties and/or elongation percentage of the composite,.
thereby enabling the strength of the resulting load-bearing composite to be sustained at large deformations, (0121 j As described above, the composite or composite material can be used in a variety of applications. For example, the composite can be used to wrap substrates including 'buildings, building components and other structures and parts or elements thereof in order to reinforce the substrates following damage or to prevent damage from occurring in the future.
The composite can also be used to provide reinforcing inserts for building materials. For example, in addition to being used as a wrap for concrete structures, materials comprising the composite can be embedded within the concrete structure. In some embodiments, the composite materials can be used as a wrap for armored vehicles, such as military transport OE
weapons .vehiclesõAdditional uses also include protective clothing (e.g.., bullet proof vests and. the like) or bio-medical applications, such as in the fabrication of prosthetics or parts for prosthetics. Even further, the composite can be used in high-vibration or high impact or shock load applications, such as bicycles, 'helmets, etc. For example, the composite material can be formed around a foam core to impart impact resistance properties to the foam core.
101221 in some embodiments, the composite can be used as a building material itself.
For example, the composite can be used to construct 'bicycle frames, automotive parts, and/or protective clothing. In a more particular example, the composite can be used for the lightweight design and manufacturing of vehicle components, which would.
improve safety, performance, and fuel efficiency.
101231 It should be noted that, for the polyurea coating layer, any suitable .elastomeric polyurea can be used. The polyurea can be selected based on any suitable factors including, but not limited to, cost, abrasion resistance, flexibility, chemical resistance, toxicity/volatility of chemicals given off by the polyurea over time, UV resistance, moisture resistanceõ and the like. In some embodiments, the polyurea has an elongation (i.e., an elongation a break) of at least about 100%. In some embodiments, the polyurea can have an elongation of about 600%
or more, in some embodiments, the polyurea has a tensile strength of between about 1500 and about 2000 pounds per square inch (psi) (e.g., about 1500, about 1600, about 1700, about 1800, about 1900, or about 2000 psi). The properties of many polyureas are known in the art and/or can be measured by techniques known in the .art, such a$,ASTM D4I 2.
101241 Polyureas suitable for use in the disclosed subject matter can be prepared by mixing (e.g., reacting or polymerizing) isoeyanates and amines. In some embodiments, the isocyanate is a di-isocyanate-terminated prepoly-mer (i.e., a compound having the tOrmula 0:-C.N-R-N-C--0, wherein R can comprise aliphatic or aromatic groups and can be polymeric or non-polymeric). For example, in some embodiments, the isocyanate can be a compound based on the structure of methylene diphenyl diisocyanate. Thus, in some embodiments, the isocyanate includes, but is not limited to, 4,4'-diphenylmethane diisocyanate (MD1), p-phenylene diisocyanate (PPD1), m-phenylene diisocyanate (MPDI), toluene diisocyanate (TM), or a mixture thereof Suitable isocyanates can also comprise backbones based on .polyethers. Additional examples of suitable isocyanates are described in, for example, U.S. Patent No. 5,415,499, which is hereby incorporated by reference herein in its entirety.
101251 Typically the amine-containing: component comprises at least two reactive amine groups. The reactive amine groups can be primary or secondary amines. in some embodiments, the amine-containing component comprises an amine-terminated prepolymer, such as an amine-terminated polymer resin and/or a monomeric aliphatic or aromatic polyamine (e.g_., a diamine, triamine, tetraamine, etc.). Exemplary amine-terminated polymer resins include blends comprisMe polyoxyalkylene di- and/or triamines and aromatic polyamines, such as diethyltoluenediamine and dimethylthiotoluenediamine (aMIDA). In some embodiments, the polyurea can include an amine-containing component such as, but not limited to, amine-terminated polypropylene glycols (e.g., jEFFAMINEO
1)2000 and JEFFAMINEV T5000, available from Huntsman Corporation, The Woodlands, Texas, United States of America), diethyltoluenediamine (i.e., ETHACURE 100, available from Albemarle Corporation, Baton Rouge, Louisiana, United States of America), or a diamine comprising sec-bm,,,1 groups (e.g., LINILINK 4200TM, Dorf K.etal Chemicals LLE, Stafford, Texas, United States of America). The amine-terminated compounds suitable for use in the present subject matter generally have a mean functionality of about 2,0 to 3,0 and an average molecular weight of about 150 to 6000. Additional examples of suitable amine-containing components are described in, for example, U.S, Patent No. 5,415,499, which is incorporated by reference herein in its entirety, 101261 Thus, in some embodiments, the polyurea layer is provided by mixing and reacting an isocyanate-terminated compound or polymer with an amine-terminated polymer and/or an aliphatic or aromatic diamine compound and then essentially immediately applying the resultant rea.ctin.g mixture to the sur&ce. (e.g., of the fabric) to be coated. The mix:nig, of the two reactants can be effected directly within a spray gun used to apply the mixture (i.e., impingement mixing). Of course, mixtures of suitable isocyanate-terminated compounds and mixtures of suitable amine-terminated compounds can be used. In some ethbodiments, a slight excess of isocyanate equivalents can be used. For example, the components can be mixed such that there are slightly more reactive isocyanate groups than reactive amine groups. In some embodiments, there is between about a 1% and about a 10%
excess of isocyanate equivalents. In some embodiments, there is about a 5% excess of isocyanate equivalents.
101271 It should be noted that providing an isocyanate-rich polyurea layer (e.g., a. 5%-rich isoeyanate) can, in some ethbodiments, enhance the molecular reactivity between a component of the polyurea layer and a component of the fiber reinforced polymer layer. It should also be noted that providing an isocyanate-rich polyurea layer can, in some embodiments, create non-contaminated state, thereby creating a. no-Slip condition between the .polyurea layer and the fiber reinforced polymer layer.
101.28-1 In some embodiments, the polyurea is aromatic. Accordingly, in some embodiments, either or both of the isocyanate and amine components comprise an aromatic moiety.
101291 In some embodiments, the polyurea is a fire-resistant polyurea. Use of a fire-resistant polyurea can provide fire-resistive properties to the composite material and to substrates reinforced with the composite material. For example, use of a fire-resistant .polyttrea can reduce the intensity of heat to the polyurea and to the composite material and/or reduce toxic outgassing. In some embodiments, the tire-resistant polyurea is also intumescent. Accordingly, in some embodiments, the composite combines in a single reinforcing material, high strength, high energy dissipation, and fire-resistivity.
101301 Fire resistant properties of polyureas or other materials can be tested by methods known in the art, such as for exampleõASTM E84-05 (Standard Test Method tbr Surface Burning Characteristics of Materials). In some embodiments, the polyurea has a flame spread classification of about 50 or less and/or a smoke developed classification of about 200 or less as measured using ASTM. E84-05. in some embodiments, the polyurea has a flame spread classification of about 20 and/or a smoke developed classification of about 115. in some embodiments, the poly-urea is the polyurea sold as System 550D-FR
by Quantum Coatings (Edmonton, Alberta, Canada).
101311 In some embodiments, various additives can be included in the polyurea layer.

For example, the additives .can be added to either the isoeyanate reactants and/or the amine reactants when the polyurea is prepared. Additives includeõ for example, organic. and inorganic colorants or dyes, UV protective agents, adhesion promoters, fillers, and other processing aids or enhancers.
1.01321 UV protective agents can include hiahi stabilizers, UV absorbers, and antioxidants. Examples of suitable light stabilizers include hindered amines, such as bis-(1,2,2,6fi-pentamethy1-4-piperidinyPsebacate and bis-(22,6,6-tetramenthyl-4-piperidyPsebacate.
101331 UV absorbers can protect against photodegradation by competing with the polyurea for absorption of ultraviolet light, In some embodiments, the UV
absorber has broad absorption over the UV range from about 290 urn to about 400 ran.
Suitable UV
absorbers can include, but are not limited to, triazines, berizoxazinones, berrzotriazoles, benzophenones, benzoates, .formamidines, citinamates/propenoates, aromatic propanediones, benzimidazoles, cycloaliphatic ketones, formanilides (including oxamides), cyarionnitates, benzopyranones, and mixtures thereof.
10134-1 Antioxidants, on the other hand, can interrupt the degradation process in different ways according .to .their structure. The major classifications of antioxidants are primary antioxidants and secondary antioxidants. Primary antioxidants, such as sterically hindered phenols, react rapidly with peroxy radicals to break the degradation cycle.
Secondary antioxidants, such as arylamines, are more reactive toward oxygen-centered radicals than are hindered phenols. The secondary antioxidants react with hydroperoxide to yield non-radical, non-reactive products, and are frequently called hydroperoxide decomposers. -Multifunctional antioxidants, such as hindered amine stabilizers ('HAS"), combine the functions of primary and secondary antioxidants.
101351 Examples of adhesion promoters include, but are not. limited to, titanates and zirconates, as well as various organofunctional awes (especially the amino-functional slimes). Examples of useful fillers include, but are not limited to, zinc oxide ("Zn0"), barium sulfate, calcium oxide, calcium carbonate, and silica, as well as any salts and oxides thereof Additional fillers Imdfor additives also include, but are not limited to, foaming agents, glass, ceramic, and/Or plastic microspheres, and various metals.
101361 The various additives are amorally present (individually or as a whole) at less.
than about 10% by weight of the total polyurea composition, in some embodiments, the polyurea layer contains about 5% by weight or less of one or more additives.
In some embodiments, the po-lyurea layer contains about 1% by weight or less of one or more additives.
[01371 .In some embodiments, the properties of the composite can be controlled by controlling the thickness of the polyurea coating layer. Controlling the thickness of the coating layer can alter the volume fraction of elastomeric polyarea in the composite as a whole. Typically, the polyurett coating layer is thicker than the fabric (e.g., at least about 5, 10, 20, 30, 40, 50, 100, 250, or 500 times thicker than the fabric when the fabric thickness is measured before the application of the saturant). In some embodiments, the coating layer has a thickness of between about 1/16th of an inch (i.e,, about 0.0625 inches) and about ligth of an inch (i.e., 0.125 inches). Accordingly, in some embodiments, the coating layer has a thickness of about 0.0625, about 0.0675, about 0.0725, about 0.0775, about 0.0825, about 0.0875, about 0.0925, about 0.0975, or about 0,125 inches. In contrast, the fabric typically has a .thickness of less .than about 0,01 inches. In some embodiments, the .fabric has a thickness (prior to the addition and curing of saturant composition) of between about 0.0013 inches and. about 0,0065 inches (el., about 0.0013, about 0,0017. about 0.0021, about 0.0025, about 0.0029, about 0.0033, about 0.0037, about 0.0041, about 0.0045, about 0.0049, about 0.0053, about 0,0057, about 0.0061., of about 0.0065 inches).
101381 The fabrics of the presently disclosed composites comprise a network of high tenacity fibers. The fabric can be woven, 'knitted, or non-woven. In some embodiments, the high tenacity fibers are uni-directional such that the fibers are generally aligned in a .parallel fashion. In some embodiments, the high tenacity fibers are hi-directional such that the fibers are aligned in both parallel and perpendicular directions.
101.39) It should. be noted that any suitable high tenacitytenacity fiber or combination of fibers can be used. For example, in some embodiments, the high tenacity fiber is carbon fiber, glass fiber (e.g., e-glass or s-glass), aramid. (e.g., meta- or p.ara-aramid), crystal copolyester fiber, basalt fiber, or any suitable combination thereof. In some embodiments, the high tenacity fiber includes carbon fiber and the fabric comprises a carbon fiber reinforced polymer (CFR?) fabric, CFRPs are relatively inexpensive compared to other FRPs and. have excellent strength and durability. More particularly, suitable high tenacity fiber fabrics include, but are not limited to. MBracee cloths, commercially available from BASF
Construction Chemicals, LLC (Shakopee, Minnesota, United States of America).
101401 High tenacity fiber fabrics are generally reinforced by a thermosetting polymer matrix based on a polymeric resin, such as, but not limited to, epoxy resins, vinyl ester resins, and polyester resins. In some embodiments, the disclosed composites comprise a carbon fiber reinforced. polymer (CFRP) fabric reinforced with a polymer matrix based on an epoxy resin.
[01.41.1 The fabric can be obtained with at least some polymeric resin pre-embedded (or pre-impregnated) in the fabric and then treated further to cause curing of the resin when desired. Alternatively, the fabric can be obtained free of polymeric resin and the polymeric resin can be applied as part of a saturant composition.. Accordingly, in some embodiments, the .presently disclosed composite comprises a. CFRP fabric that has been treated with a mixture (e.g., a saturant composition) comprising a polymeric resin (e.g., an epoxy, vinyl ester, or polyester resin). The mixture can also include additional chemicals or additives, as desired, such as to promote the curing of the resin (e.g., polymerization initiators or curing accelerators) and/or a diluent, Additional additives can further include one or more of a filler, a colorant, a UV protectant, a viscosity modifier, a. defoamina aunt, and a surface drying agent: or .the like, [0142] Typically, epoxy resins can include an epoxy-terminated prepolymer (e.g.,, an epoxy-terminated .monomer, oliuomer, or short chain polymer) and a hardener comprising a .polyamine triethylenetetramine). Epoxy-terminated prepolymers can be prepared, tbr example, from the reaction of epichlorohydrin and bisphenol A. Thus, suitable epoxy resins include, but are not limited, to, glycidyl ethers .of polyvalent phenols such as bisphenol A.
epoxy resins, bisphenol F epoxy resins, bisphenol S epoxy resins, phenolic novolak epoxy resins, cresol novolak epoxy resins, brominated bisphenol A epoxy resins, and brominated phenolic novolak epoxy resins; glycidyl esters such as diglycidyl phthalate, diglycidyi hexahydrop.htbalate, diglycidyi tetrahydrophthalate, and benzoic. acid. or (limey acid glycidyl esters; heterocyclic epoxy resins such as 1,3-diglycidy1-5,5-dimethylhydantoin and triglydicyl isocyanurate; and Acyclic epoxy resins such as naphthalene-based epoxy resins and 2,2%44-tetraglycidoxybiph.enyi. These epoxy resins can be used either singly or as a mixture of two or more particular resins.
101431 In some embodiments, the epoxy resin is provided as part of a saturant composi.tion or compositions comprising, for example, Bisphenol A epoxy resin, alkyl glycidyl ether, amorphous silica, isophoron.ediamine, benzyl alcohol, and salicylic acid. In some embodiments., the epoxy resin is provided as part of a commercially available MBrace0 Saturant, such as MBracetit) Saturant LTC (available from BASE Construction Chemicals, LLC.; Shakopee, Minnesota, United States of America).
101441 Vinyl ester resins typically include an epoxy resin and a monocarboxylic acid, Examples of monocarboxyhc acids include, but are not limited to, acrylic acid, methacrylic acid, crotonic acid, cinnamic acid, sorbitanic acid, acrylic diraers, .rrionomethyl malate, .

monopropyllateõ monobutyl malate, mono(2-ethythexyl.).malate and the like:
101.45.1 Polyester resins can be prepared by the reaction of a di- or polyearboxylic acid and a polyvalent alcohol (i.e., a polyol, a compound comprising at least two hydroxyl groups). Polycarboxylic acids include, but are not limited to, lumalic acid, maleic anhydride, maleic acid, itaconic acid, isophthalic acid, terephthalic acid, tetrahydropluhalic acid, adipic acid and .sebacic acid. Polyvalent alcohols include, but are not limited to, ethylene glycol, propylene glycol, diethylene glycol, dipropylene glycol, 1,2-butanediol, 1,3-butanediol, I ,5-pentattediol, 1,6-hexanediol, 2-methyl-I ,3-propanediol, 2,2-dimethyl-1,3-propanediolõ cyclohexane-1,4-dimethanolõ ethylene oxide adducts of bisphenol A. and propylene oxide adducts of bisphenol A.
101461 In some embodiments, the polymer matrix reinforced fabric (e.g., the cured FRP in the absence of the polyurea coating layer) has an ultimate tensile strength of at least about 145 ksi (1.0 GPa) and a tensile modulus of at least about :20,000 ksi (138 GPa) measured in the direction along the length of the fabric, hi some embodiments, the fabric has an -ultimate tensile strength of at least about 500 ksi (3.45 GPa) and a tensile modulus of at least about. 30,000 ksi. (207 GPa). In some embodiments, the fabric has an ultimate tensile strength of at least about 550 ksi (3.79 GPa) and a tensile modulus of at least about 33,000 ksi (228 GPa)õ In some embodiments, the fabric has an ultimate tensile, strength of between about 1.90 GPa and about 5,74 GPii about 1..90, 2.40, 2.90, 3.40, 3.90, 4.40,4.90, 5.40, or about 5.74 GPa) with elongation percentages varying between about 0.5% and 2.0% (e.g., About 0.5, 1,0, 1.5, or about 2.0 %) beyond. yield. In some embodiments, the fabric has an ultimate tensile strength per unit width of about 3.575 kips per inch (per ply). in some embodiments, the fabric has an ultimate modulus of about 214.5 kips per inch (Per ply per .unit width). 'Tensile properties can be measured by any suitable approach known in the art, such as, for example, ASTM D3039, 101471 By combining the FRP fabric with the elastomeric polyurea layer, the elastic and inelastic properties and viscous properties of the composite material as a whole can be significantly enhanced.. In some embodiments, the composite has an elongation of about 1.00% or more (e.g., about 100%, about. 150%, about 200%, about 250%, about 300%, or about 400% or more). In some embodiments, the composite has an elongation of about.
600%.
101481 In addition to providing a combination of strength and energy dissipation, the presently disclosed composites can be free of carcinogenic toxicity, By "free of carcinogenic toxicity," it is meant .that the composites are essentially free of volatile carcinogenic chemicals and, if used in long-term proximity to humans; such as.when the composite is used.
as a wrap for a building or as protective clothing, the humans exposed to the composite do not experience a statistical increase in cancer incidence compared to humans not exposed to the composite.
191491 In some embodiments, in addition to the FRP fabric and the at least one pots/urea coating layer, the composite can .include additional components. For example, the composite can include a FRP fabric that is coated on both sides with a polyurea coating layer.
Additionally or alternatively, .the composite can be coated with an adhesive, e.g.., to enhance the attachment of the composite to various other materials.
101.501 In Wale embodiments, the composite can further include microspheres, such.
as ceramic .microspheres, that are embedded into the .polyurea coating layer or added in a separate layer on a surface of the polyurea coaling layerte.c.,n, on the surface of the polyurea coating layer not in contact with .the FRP fabric). For example, ceramic microspheres can add additional insulating properties to the composite material. Accordingly, in some embodiments, the composite can be used to increase the energy efficiency rating of a structure, for example, a wood-constructed home. In some embodiments, the use of a composite comprising ceramic microspheres can increase the energy efficiency of a structure from about 2 to about 4 times (e.g., about 2, 3, or 4 times) that of the corresponding: structure where the composite is not used.
METHODS .FOR REINFORCING SUBSTRATES
101.51) FIG. 2 is an illustrative method .for reinforcing a substrate, such as a substrate from a newly constructed structure) with a composite material that includes a high tenacity fiber reinforced polymer fabric and a polyurea layer is provided. It should be noted that, in the illustrative method of FIG. 2 and other flow Charts described herein, some steps cart be added, some steps can be omitted, the order of the steps can be re-arranged, and/or some steps can be performed simultaneously.
[01521 As shown, method 200 begins by providing a substrate at 210. It should be noted that the composite material in accordance with the disclosed subject matter can be used with any suitable substrate. Suitable substrates can include, but are not limited to, wood, masonry (e.g., brick, stone, stucco, tile), concrete (including concrete reinforced with steel or other metal), steel, or combinations thereof. Alternatively, as shown in embodiments described herein, a suitable substrate can be a foam (e.g., expanded polystyrene, expanded polyurethane, etc.) It should also be noted that the substrate can be any suitable shape (e.g., ..

a wall, a beam, a slab, a. bar, a column, 'a rod, a. support strut) or size.
For example, in. some embodiments, the substrate is a building component intended for use in new construction of a house or other 'building (e.g., an office building, a hospital, a school, a store, a. power plant, an airport, etc.), a bridge, a roadway, a dam, a tunnel, a retaining wafl, a dock, or a wharf.
101531 At 220, a first saturant composition can be applied to the surface of the substrate prior to attaching the high tenacity fiber reinforced polymer fabric. Upon applying the first saturant composition at 220, a high tenacity fiber reinforced polymer fabric can be attached to at least a portion of .the substrate at 230. As described previously, any suitable high .tenacity fiber fabric can be used. For example, in some embodiments, the fabric can include at least some carbon fibers. In a more particular embodiment, the high tenacity fiber reinforced polymer fabric is a carbon fiber .reinforced polymer fabric.
101541 Attaching the high tenacity fiber reinforced polymer fabric to the substrate can be done by any suitable method., For example, the high tenacity fiber reinforced polymer fabric, can be attached to the substrate, surface by stapling or nailing. In another suitable embodiment, the attaching can be performed by coating at least a portion of a surface of the substrate with a primer composition and/or the first saturant composition to provide a coated substrate and contacting the coated. substrate with the high tenacity fiber fabric.. The primer composition and/or the first saturant composition can comprise an adhesive and/or a polymer.
resin that can interact (e.g., via covalent bonding or non-covalent bonding) with the high tenacity .fiber reinforced polymer fabric and, in some cases, the second saturant composition.
that. is applied .to the fabric after the fabric is contacted to the coated surface.
10155j It should. be noted that any suitable polymer resin can be used in the primer or the saturant composition. Suitable polymer resins for use in the primer can include, but are not limited to, epoxy resins, vinyl ester resins, polyester resins, and methylmethacrylate resins. If a primer comprising a polymer resin is used, it can be the same resin or type of resin as the polymer resin in the saturant composition (the polymer resin in 230) or it can be a different type of polymer resin. Accordingly, in some embodiments, the polymer resin in the saturant and the polymer resin in the pruner can both be epoxy resins.
10156j At 240, a second saturant composition can be applied to an exposed surface of the fabric. As described above, the second saturant composition can comprise an adhesive and/or a polymer resin that can interact (e.g., via covalent bonding or non-covalent bonding) with the high tenacity fiber reinforced polymer fabric. After the .saturant is applied to an exposed surface of .the fabric (e.g., by painting or spraying) at 240, it can be cured. at 250 for a suitable period of time to provide a tacky surface (a tacky outer surface to the fabric). It 28..-should be noted that the time to cure the second :Wilma co.mposition can be -varied based on the chemical composition of the saturant, temperature, and/or humidity. In some embodiments, the second saturant composition can be cured for between about 2 hours and.
about 3 hours (e.g., about 120, 130, 140, 1.50, 160, 170, or about 180 minutes), In some, embodiments, the saturant composition can be partially cured. In some embodiments, the second saturant composition can be cured as long as about five hours.
101.57) When the saturant is partially cured at 250, an elastomeric poly-urea-forming component solution can be applied to the tacky surface at 260. Applying the -polyurea-forming component solution while the surface is tacky can allow for interaction (e.g., covalent or non-covalent bonding) between the chemicals or components in the polyurea-forming component solution and the resin or other components in the saturant composition.
This interaction during preparation can allow for sustained. interfacial interaction between the polyurea coating layer and the fiber reinforced polymer fabric layer when, for example, the reinforced substrate is subjected to various stresses or events. In some embodiments, the elastomeric polyurea-forming solution can be sprayed or brushed. onto the tacky surface.
101.581 In some embodiments, the polyurea-fOrming component solution comprises materials that form an aromatic polyurea layer. In some embodiments, the polyurea layer is fire-resistant. For example, the polyurea layer can have a flame spread classification as determined using ASTM E84-05 of about 50 or less (e.g., about 50, about 40, about 30, or about 20 or less). In some embodiments, the polyurea layer can have a smoke developed classification of about 200 or less (e.g., about 200, about 180, about 160, about 140, or about 120 or less) as measured by ASTME84-05. lin some embodiments, the polyurea layer has a.
flame spread classification of about 20 and a smoke developed classification of about 115. In sonic embodiments, the fire-resistant polyurea layer is intumescent A suitable fire-resistant intumescent palyurea includes, for example, the polyurea sold as System 550D-FR by Quantum Coatings (Edmonton, Alberta, Canada).
[0159] In some embodiments, the polyurea-forming component solution comprises a.
first component that is an isocyanate (e.g., an isocyanate prepoly-mer) and a second component comprising an amine (e.g., an amine-terminated prepolymer). In some embodiments, the isocyanate is a di-isocyanate-terminated prepolymer (i.e., a compound having the fermata wherein R can comprise aliphatic or aromatic groups and can be polymeric or non-polymeric). For example, in some embodiments, the isocyanate can be a compound based on the structure of methylene diphenyl diisocyanate.
Thus, in some embodiments, the isocyanate includes, but is not -limited to, 4õ4'-dipbenylmethane diisocyaniate (MD.I), p-pheny I encedifsocyanate (PPDI), m-phenylene diisocyanate (MP DI), toluene diisocyanate (1.DI), or a mixture thereof Suitable isocyanates can also comprise 'backbones based on polyethers. Additional examples of suitable isocyanates are described in, for example, U.S. Patent No, 5,415,499, which is hereby incorporated by reference herein in its entirety.
101601 The amine-terminated prepolymer can comprise at. least. two reactive amine groups. The reactive amine groups can be primary or secondary. amines. In some embodiments, the amine-terminated prepolymer comprises an amine-terminated .polymer resin and/or monomeric aliphatic or aromatic poly:Amine (e.g., a diarnine, triamine, tetraamine, etc.). Exemplary amine-terminated polymer resins can include blends comprising polyoxyalkylene di- and/or triamines and aromatic polyamines, such as diethyltoluenediamine and dimethylthiotoluenediamine (DMTDA). In some embodiments, the polyurea can include an amine-containing component such as, but not limited to, amine-terminated polypropylene glycols (e.g., JEFFAMINE0 D2000 and IEFFAMINE615000, available from Huntsman Corporation, The Woodlands, Texas, United States of America), diethyltoluenediamine (i.e., ETHACUREO 100, available from Albemarle Corporation, Baton Rouge, Louisiana, 'United States of America), or a. &amine comprising sec-butyl groups (e.g., UNIL1NK 4200.", Dorf Ketal Chemicals LLC, Stafford, Texas, United States of America). The amine-terminated compounds suitable for use in the present subject matter generally have a mean functionality of about 2.0 to 3.0 and an average molecular weight of about 150 to 6000. Additional examples of suitable amine-terminated prepolymers are described in, for example, U.S. Patent No. 5,415,499.
101.61.1 The components of the polyurea-forming component solution can be typically mixed iminediately prior .to application to the tacky surface, For example, the components can be mixed. in a spray gun as they are being sprayed. In some embodiments, the components of the polyurea-forming component solution can be mixed in a ratio where there is a slight excess of isocyanate equivalents (i.e., reactive isocyanate groups). In some embodiments, the components can be mixed such that there is between an about 1% and an about 10% excess of isocyanate equivalents (e.g., an about: 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, or 10% excess of isocyanate equivalents). In some embodiments, there is a 5%
excess of isocyanate equivalents.. In some embodiments, the use of a slight excess of isocyanate can enhance interaction of the polyurea layer with the fiber reinforced polymer fabric, due to interaction of the isocyanate component from the polyurea-forming solution.
with unreacted polymeric groups in the saturant of the fiber reinforced polymer fabric.
- 3.0 -10162j In.:some embodiments,. the polyurea-forming componentsohnion can comprise.
one or more additives to enhance the functionality or appearance of the reinforced substrate, In some embodiments, the polyurea-forming component solution can comprise a UV

protective additive, such as, but not limited to an organic pigment. In some embodiments, the polyurea-forming component solution can comprise between about 1% and about 10% by volume of the UV protective additive (e.g., about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9% or about 10%), in some embodiments, the polyurea-forming component solution can comprise about 5% by volume of the IN
protective additive.
10101 Following application of the polyurea-forming component solution, .the polyurea component solution can be allowed to cure to form a coating layer at 270, it should he noted that some polyureas can cure relatively rapidly. In some embodiments, the polyurea component solution can be allowed to cure for about 1 to 5 minutes (e.g., about 60, 90, 120, 150, 180, 210, 240, 270, or 300 seconds) and while the polyurea is still tacky, an additive is applied to the coating layer (e.g., to the exposed surface of the coating layer). In some embodiments, the additive comprises ceramic microspheres.
101.641 As described herein, properties of the composite (e.g., viscous damping properties, strength properties, and/or stiffness properties) can be modified by controlling the thickness or the polyurea coating layer. Controlling the thickness of the pialyarea coating layer can alter the volume fraction of elastomeric polyurea in the composite, which can alter the properties of the resulting composite. in another example, the time related to the reaction between .polyurea coating layer and the polymer of the fiber reinforced polymer fabric can affect the viscous properties of .the resulting; composite. Accordingly, when presented with particular material specifications (e.t.a, an installation requires a highly damped material), the composite can be made to accommodate such specifications..
101651 in some embodiments, the approach for reinforcing substrates can be applied to a previously constructed structure and, more particularly, an already damaged structure.
Referring to FIG, 3, an illustrative method for reinforcing a substrate having damaged .portions with a composite material that includes a high tenacity fiber reinforced polymer fabric and a polyurea layer is provided.
101.661 As shown, method 300 'begins by providing a substrate having damaged portions at 310, In some embodiments, the substrate can be already present in a previously constructed building or other structure. In some embodiments, the previously constructed building or other structure can be a building or other structure that has been damaged due to a catastrophic event, such as an earthquake, a fire, a tornado, a hurricane, a typhoon, -flooding, or an explosion, Alternatively, in some embodiments:, the building, or other structureis present in a region where .there is an increased likelihood of such an event.
For example, the 'building or structure can be located near a fault line, near the coastline, in a war zone, and/or he a 'building or structure having an increased risk of a terrorist attack, such as a building of economic or government, importance or a building related to high population density events (e.g., sporting arenas, theaters, etc.).
10167) in some embodiments:, the previously constructed building can be damaged or be suspected of having damage due .to normal wear and. tear and/or related to age. For example, concrete is relatively alkaline, preventing the corrosion of any reinforcing metal bass present within concrete structures. Over time, however, concrete can become neutralized due to the action of carbon dioxide in the air. Once the concrete becomes neutralized, the metal bars can become susceptible to corrosion and an increase in volume, causing cracks in the structure. In some embodiments, the concrete is already cracked, and the metal bars are susceptible to corrosion, hi some embodiments., older structures can become candidates for damage because the use of the structure changes over time. For example, bridges can become candidates of damage due to increases in traffic above levels accounted for during the design of the 'bridge. In such an embodiment, the building or other structure can be I() or more years Old (e.g., 10, 20, 30., 40, 50, 60, 70, 80, 90, or 100 or more years old).
101681 Alternatively, in some embodiments, the building or other structure can be newly constructed (e.g., within the last 10, 5, 4, 3, or 2 years.) such that the reinforcement is perthrmed .to prevent damage. In some embodiments, the newly constructed building or other structure is a structure built within the last 12 months.
101691 In some embodiments, the building or other structure is under construction or the substrate is intended for use in future construction.
[01701 With a substrate having damaged portions (or suspected damage due to, for example, wear and tear), .the substrate can be prepared at 320, This can include, for example, selecting the substrate and preparing it by one or more of cleaning the surface of the substrate, smoothing the .surface of the substrate, and filling in cracks, pits, chips, and/or grooves- in the surface of the substrate prior to attaching the fabric.
Cleaning can be done by any suitable method., such as power washing or any other method to remove surface dirt arid/or other non-substrate matter. In some embodiments, providing the substrate can comprise Idling in and/or smoothing out the surface of the substrate with a.
putty material..
- 32.-Smoothing canbe performed by sanding or any other suitable method. Cracks, pits, chips, grooves or other indentations or disfignrementsin the surface of the substrate can be filled in with any suitable material, such as, but not limited to wood filler, cement, concrete, or mortar. Generally, the fill material should be such that it does not interfere with the attachment of the fabric. Thus, in some embodiments, the fin material is a material that can interact (e.g., via covalent of non-covalent bonds) with a polymer resin applied to the surface of the substrate as part of a primer for attaching the high tenacity fiber fabric, or with a polymeric component present in or added to (e.g., in a saturant) the high tenacity fiber fabric.
[01.711 Steps 330 through 380 of Ha 3 are similar to steps 220 through 270 of FIG. 2. In particular, the composite material can be prepared by applying a first saturant.
composition to a surface of the substrate (at 330); attaching a high tenacity.
fiber reinforced fabric to at least a portion of the substrate with the use of the first saturant composition (at 340); coating the high tenacity fiber fabric with a second saturant composition comprising a .polymer resin (at 350); curina, the second saturant composition for a period of time (e.a., about two hours to five hours) to provide a tacky surface (at 350); applying an .elastomeric polyurea-forming component solution to the tacky surface (at 360); and curing the polyurea-forming component solution to provide a composite material (370), 101721 In some embodiments, the substrate can be reinforced by attaching a previously prepared composite to the substrate, wherein the previously prepared composite includes a high tenacity fiber reinforced polymer fabric and a polyurea coating layer. Thus, in some embodiments, the method of reinforcing the substrate comprises preparing a composite material and attaching the composite material to the substrate. The previously prepared composite material can be attached to the substrate via any suitable method, such as, 'but not limited to, stapling or nailing the composite material to the substrate and/or adhering the composite material to the substrate via an adhesive and/or polymeric resin coated on the substrate and/or on the composite material.
[0173] It. should be noted that reinforcing a substrate (e.g.., a wood home, a reinforced concrete bridge, a steel structure, an automobile, an aircraft structure, etc.) inhibits or reduces damage to the substrate due to seismic activity (e.g., earthquakes), tire, and/or explosive forces (e.g., due to ballistics). In some embodiments, reinforcing the substrate can also provide resistance to water damage (e.g., due to mechanical stresses from flash flooding or by reducing mold or other damage due to water saturation into the substrate), environmental pollutants and/or sun damage. In some embodiments, the protective properties can relate, at least in part, to a specific additive (e.g., a UV protectant, a flame retardant, moisture resistanceeetc..) added to the fiber reinforced polymer .Fabric Or the poly-area layer. In some embodiments, the protective property is 'related to the chemical composition of the fiber reinforced polymer fabric and/or the polyarea layer. For example, polyureas can be moisture and/or mold resistant. In some embodiments, such as when a microsphere additive is used, the rein .forcing can provide an insulative effect to the substrate, thereby making the reinforced substrate a more energy efficient building material than the non-reinforced substrate. In some embodiments, the reinfbrcing can increase the energy efficiency to between about 2 and 4 times (e.g.., about 2, 3, or 4 times) that of the non-reinforced substrate.
EXAMPLES
101741 The killowing examples further illustrate some embodiments of the present invention, but Should not be construed as in any way limiting the scope.
EXAMPLE: 1: Tensile Composite Coupon . Results 101751 Coupons of composite were prepared using MBraceg FRY cloth (about 0,068 inch thick x about I inch wide available from BASF Construction Chemicals:
LLC., Shakopee, Minnesota, United States of .America) saturated with a saturant prepared. by mixing a composition comprising Bisphenol A epoxy resin, .alkyl glycidyl ether, and amorphous silica with a composition comprising isophoronediamine, bevy1 alcohol, and salicylic acid; and coated with a non-fire resistant polyureaeforming composition. Coupons.
were prepared with two different polyurea layer thicknesses (e.g., either about one eighth of an inch thick or about one sixteenth of an inch thick), providing final composite dimensions of about: 0.19 in. thick .x about I in. wide or about 0.32 in. thick x about 1 in. wide.
101761 -FIG. 4 is an illustrative graph of tensile three versus axial displacement that compares the elastic properties of carbon fiber reinforced polymer fabrics (as indicated by CFRP - Test I carve 420 and CRFP -- Test 2 carve 430) with the elastic properties of a pol,,,urea-coated carbon fiber reinforced polymer fabric having a polyurea coating layer with a thickness of either one sixteenth of an inch (as indicated by Carbon-Flex, Ix Poly ¨ Text 1 curve 410 and Carbordlex, Ix Poly --Test 2 curve 440) or one eighth of an inch (as indicated by CarbonFlex, 2x Poly ¨ Test 1 curve 450). As shown in curves 410 and 440 of FIG. 4, the.
displacement of the polyttrea-coated tensile coupon havin Me of one inch thick polyurea.
coating layer on each side was about 3.75 times larger than that of the non-coated CFRP
coupon (as compared to curves 420 and 430). Moreover, the displacement of the polyurea-coated tensile coupon .having. a Ile of one inch -thick polyurea coating layer per side (curve 450) was about 6.25 times largerthan that of the non-coated CFRP coupon (curves 420 and 430). it should also be noted. that the continuous nature of the curves in FIG. 4 suggests that no interfacial slip had occurred between the poly-urea and the CFRP.
EXAMPLE 3: Torsion Results of Composite Wrapped Woad.
[01.77) FIG. 5 is an illustrative graph showing the results of a. torsion study that was conducted on a white pine wood rod that 12 inches long and I/2 of an inch in diameter. In this embodiment, the rod was wrapped with a polyurea coated (I/16 inch) CFRP
composite according to above-described method of the disclosed subject matter, As Shown in FIG, 5, the composite wrap was able to provide the necessary energy dissipation and strength components, as implied by the highly nonlinear response of the specimen, to enable the .polyurea-coated composite wrapped wooden structure to attain a maximum torque reading of 80,0 pound inches (lbs-in). This maximum torque reading is nearly four times the torsional strength of unwrapped white pine at about 22.9 pound inches. It should be noted that the continuity of the curve shown in FIG, 5 and visual inspection of several cross-sectioned slices of the wrapped rod indicate that no bond slip occurred between the composite and the wood structure, EXAMPLE 3: Bending Results of Composite Wrapped Wood 101.781 Three 2 x 4 wood beams of white pine, each with a 28 inch span, were subjected to wood beam bending studies. 'Each of the wood beams was prepared differently ¨
as shown in FIG. 6A, curve 610 corresponds to the wood beam by itself (labeled by Wood only), curve 620 corresponds to the wood beam wrapped with a carbon fiber reinforced polymer fabric (labeled by Wood + CFRP), and curve 630 corresponds to the wood beam.
wrapped in a polyurea-coated carbon fiber reinforced polymer composite of the disclosed subject matter. Each of these wood beams was subjected to concentrated mid-span forces as indicated on the force axis of FIG. 6A. For example, FIG. 611 shows an illustrative testing setup that subjected these wood beams to concentrated mid-span forces. 'The results, as shown in 'FIG, 6A, indicate significant increases in displacement, shear strength, and energy dissipation in the polyurea-coated carbon fiber reinforced polymer composite wrapped beam.
The .polyurea-coated carbon fiber reinforced polymer composite wrap was able to hold the damaged wood. beam .together well after the sudden strength drop, which, without being bound to any one theory, enabled the load to redistribute to the. wrap while energy was.
steadily dissipated.. Tests have shown that the displacement ductility and energy dissipation values can exceed .those of a beam wrapped only with a carbon fiber reinforced polymer fabric by more than 100%. FIG. 6C illustrates an example of Shows a Photograph of a polyurea-coated carbon fiber reinforced polymer composite wrapped .wood beam following testing; with the testing setup shown in FIG. 613.
101791 Similarly, FIG. 7 shows a. graph showing the results of a wood beam bending study of a wood beam wrapped with a polyurea-coated carbon fiber reinforced polymer composite, where .the polyurea layer is one eighth of an inch thick Also similar to FIG. 6A, the circled portion of .the graph indicates a strength drop. It should be noted that, for the wood beam wrapped with a composite comprising an eighth of an inch thick layer of polyurea, the strength drop was immediately followed by a recovery stress (hardening). This behavior is at least due in part to the viscoelastic nature of the polyurea-coated carbon fiber reinforced polymer composite and its interfacial chemical interaction, it should also be noted that the thicker coat of polyurea. (e.g., one sixteenth of an inch versus one eighth of an inch) .provides greater support and stillness to the carbon fiber reinforced polymer fabric (as well as to the entire systern),, thereby providing adjustable desirable properties upon load redistribution and greater energy dissipation and ductility.
101801 Turning to FIG. 8, FIG. 8 is a graph showing the strain capacities and elastomeric flow of polyurea-coated carbon fiber reinforced polymer fabric composites applied to a wooden substrate. As shown, curve 830 shows the data related to the strain at the interface between the polyurea and the carbon fiber reinforced polymer fabric components of the composite material, and curve 840 shows the data. related to the strain at the interface 'between the composite material and the wooden substrate. in addition, FIG. 8.
includes curve 810, Which shows the data related to the strain for a non-wrapped wooden substrate, and curve 820, which shows the data related to the strain for a wooden substrate wrapped only with a carbon fiber reinforced polymer fabric. It should be noted that, similar to FIG. '7, the open circles indicate a strength drop. It should also be noted that the closed circles indicate a yield point.
101.811 As indicated, FIG. 8 shows parallel strains on the wood and polyurea interfaces at quarter span locations, implying that there is no d.ebonding, while the negligible strain rate indicates that there is no deformation in the polyurea. Again, without being bound to any one theory, the data shown in FIG. 8 supports the existence of a purely..elastomeric poly urea-carbon fiber reinforced polymer system after the wood substrate reaches its strength.

drop and the existence of a viscoelastic energy dissipative: stem prior to that point (but after 101821 FIG. 9 shows the results of additional studies of composite wrapped wood 'beams under static load and indicates that the composite wrapped beams (curves 930 and 940) have a significant increase in ductility of 150% as compared to wood beams wrapped in carbon fiber reinforced polymer alone (curve 920). The carbon fiber reinforced polymer alone has an elongation of only 1,5%. Further, compared to the unwrapped wood beam (curve 910), the composite wrapped beams have a significant increase in ductility of 800%.
FIG. 9 shows various load-deflection curves and indicates that two composite wrapped beams (one having about 2 times the amount of polyurea by volume and/or thickness;
see CarbonFlex x Wood Bead 2xV clime 940) exhibit a sustainable negative stiffness and strength over prolonged deflections and continued substrate cracking, relative to a carbon fiber reinforced polymer-wrapped wood beam, 101831 It should be noted that the 2xV beam shown by curve 940 depicts an elastic-plastic like region after the final strength drop. Accordingly, curing time and polyurea .volume fractions can be tailored to design the tight-wrap to satisfy specific structural performance demands.
101841 In addition, a. comparison of the load-deflection curves of the lxV
and UV
'beams in FIG. 9 suggest .that the negative stiffness becomes less negative as cracks in the damaged wood member propagate and the load gradually transfers to the composite.
Following the .final, strength drop Shown in FIG. ),where the substrate fails, a strain hardening region ensues that actually restores stress_ The increasing nature of the negative slope of the stiffness indicates that the composite stabilizes wood crack growth as the composite transitions to a neatly purely viscous material.
EXAMPLE 4: Simulations of Acceleration and Hysteresis in Wrapped Wood Structure 101851 As shown in FIGS, 10A-10C, computational simulations were pert-United to compare the performance of a two-story composite wrapped wood structure (indicated by CF
in FIG, 10C) to that of a non-wrapped structure (indicated by W in FIG, 10C) subjected to conditions similar to the 1994 Northridge earthquake. Interior gypsum board wall sheathing and. stucco finishes were not included in the model, and neither was pinching of the hysterets.
The post-yield viscoelastic portiOn of the CF tight-wrap was based on previously described models (see e.g., .Attard, International Journal of Solids and Structures, 42(21-22), 5656-5668 (2005); and Attard and Mignolet. .1. Engineering Mechanics, 134(10), 881-891 (NW)) and .the sustainable negative stiffness region was modeled using a regression of experimental data. The confinement of the CF structure was modeled as a nonlinear Iight!..le element, and the viscous-plus-hysteretic damping was calculated as 44.1 32% using experimental data, with 13% calculated from viscous-type damping. For the Ws structure, 4.eq¨ 20%, of which viscous damping contributed 2%. See 'Filiatrattlt et al,, Engineering Structures, 25, 461-471 (2003.) The "deep shear" displacements were estimated as a function of a changing shear modulus in the negative stiffness region of the CF' model. The CF and Ws models were embedded into a comprehensive nonlinear time-history code, .NONLIN, See Allard. T.L,..
"Modeling of Higher-Mode Effects in 'Various Structures Using a Pushover Analysis,"
Doctoral Dissertationõ,krizona State University, Tempe, .Arizona (2003); and Allard and Fafitis. Engineering Structures, 29(8), 1977-1989 (2007), [0186I For comparison, FIG. 10A shows an illustrative graph of a simulated acceleration time-history of a two-story wooden structure that is wrapped with a polyurea-coated carbon fiber reinforced polymer fabric composite and FIG.1013 shows an illustrative graph of a simulated acceleration time-history of a two-story wooden structure without the composite described herein. An analysis of the acceleration results of the simulations in FIGS. 10A and. .10B reveals significantly larger stitThess and viscous-type damping in the CF
structure, which enabled the peak accelerations in the CIF structure to be 25%
and. 35%
smaller than those in the Ws structure on the top and bottom stories, respectively. The standard deviations of the acceleration time histories were 39% and 47%
smaller, which represent a substantial across-the-board reduction. FIG. IOC shows the hysteresis and inter-story drifts (in %) in the two structures, indicating significant reduction in building damage to the bottom story using the polyarea-coated carbon fiber reinforced polymer iiibric composite and no damage to the top story, which remained elastic, in comparison to the Ws structure, which experienced significant damage to both stories, the polyurea-coated carbon fiber reinforced polymer fabric composite wrapped structure was able to reduce the maximum post-elastic inter-story drift by 81%, where the post-elastic drift is defined here as the post-yielding drift, per cycle.
EXAMPLE 5; Retrofitting a Steel Reinforced Concrete Composite Beam (SRCC) 101871 As described herein, the approach for reinforcing substrates can be applied to a previously constructed structure and, more particularly, to an already damaged structure.
-10188j As.Sh.ownin FIG. I IA, the substrate can be prepared befOretetrofitting the substrate with the disclosed composite by, for example, re-shaping the substrate, steel shape welding, and grouting. As also shown in FIG. 11.A., in this example, two concrete beams were prepared and retrofitted --- one with only a carbon fiber reinforced polymer fabric and one with the :polyurea-coated carbon fiber reinforced polymer composite.
101891 FIG. 1. IB shows various cross-sections along the concrete beam retrofitted.
with the carbon fiber reinforced polymer fabric. For example, section Al-Al 'illustrates the three-layer bottom laminate used to carry tensile forces and section .A2-A2 illustrates the three-layer composite formed around the bottom portion of the beam and the polyurea-coated carbon fiber reinforced polymer fabric formed around all four sides of the beam. In addition, the polyurea-coated carbon fiber reinforced polymer fabric can be formed around particular portions of the beam. For example, section A3-A3 shows that polyurea-coated carbon fiber reinforced polymer fabric can be attached to opposing sides of the beam such that, in combination with the composite formed around the bottom portion of the beam, a "U" shaped composite jacket is thrilled.
[01.901 FIG. 11C shows the results of force-deflection response studies along different 'beams ¨ as shown, curve 11I0 corresponds to a steel reinforced concrete composite (SR CC) 'beam retrofitted with .polyurea-coated carbon fiber reinforced polymer composite portions (labeled B1), curve 1120 corresponds to a SRC:C beam retrofitted with only carbon .fiber reinforced polymer fabric portions (labeled 132). and curve 1.130 corresponds to a S.RCC
beam retrofitted with polyurea-coated carbon fiber reinforced polymer composite portions having no steel welded. (labeled B l). The results indicate that the use of polyurea-coated carbon fiber rein forced polymer composite portions allow the SRCC beam to experience significant increases in displacement and energy dissipation. The composite wrapped SR CC
beams in 1 110 and 1130 exhibit brae viscous damping, a sustainable negative stiffness, and strength over prolonged deflections under stabilized substrate cracking, relative to a carbon fiber reinforced polymer-wrapped wood beam in 1120.
EXAMPLE 6: R.etrofittina a Seismic .Datitaaed Reinforced Concrete Shear Wall 101.911 Similar to the above-mentioned example, the approach for reinforcing substrates can be applied to a previously constructed structure and, more particularly, to an already damaged structure. In this example, a reinforced concrete shear wall was damaged under a cyclic load. The cyclic testing resulted in severe damage to the reinforced concrete shear wall :that included a three millimeter wide cross-crack and concrete crush at two of the - 39¨

bottom corners (Jf the -wall. The after4est load capacity of the. wall dropped to approximately 40% of its peak value.
101921 As shown in portion 1210, of FIG. 12A, the shear wall substrate can be prepared. before retrofitting the substrate with the disclosed composite by, for example, grouting and crack injection. As shown in portion 1220 of FIG. 12A, various portions of the shear wall substrate, such as the cracked, crushed, and/or damaged portions of the substrate, can be retrofitted and reinforced with the polyurea-coated carbon fiber reinforced polymer composite. In particular, particular portions of the shear 'wall substrate and reinforced, with the composite before the entire substrate is wrapped around with the composite. As described previously, the composite can be prepared and then attached to the substrate or, alternatively, the composite can be formed directly on the surface of the substrate.
101931 Turning to FIGS, 1213 and I2C, the results of the Ibrce-deflection response studies along the retrofitted and reinforced shear wall indicate that the use of polyurea-coated carbon fiber reinforced polymer composite portions allow the Shear wail to recover about 80% of the shear walFs original load capacity. In addition, as shown in the illustrative images of FIG. 12C, the polyurea-coated carbon fiber reinforced polymer composite provides a substantial increase in ductility. This increase in ductility allows the reinforced concrete shear wall to experience large deformations, Where the energy dissipation properties of the polyurea-coated carbon fiber reinforced polymer composite stabilized crack growth and sustained the high strength of the structure even after the concrete was crushed. By readily dissipating the energy after the formation of cracks, the formation of new crack surfaces and/or further damage can be prevented from occurring. As also shown in the images of FIG.
12C, it should be noted that there is significant confinement and a substantial increase in compression strength in this retrofitted wall.
EXAMPLE 7: Viscous Damping and Impact Resistance of Composite Wrapped.
Substrates [019.1] In this example, foam core substrates were used, where one foam core substrate was wrapped only with a carbon fiber reinforced polymer fabric and one foam core substrate was wrapped with a polyurea-coated carbon fiber reinforced polymer composite of the disclosed subject matter. These .foam core substrates were then subjected to impact resistance testing, where a high loading speed (a shock load) or 4 meters per second was used.
101951 As shown in FIGS. 13A and 1313, the amount of load handled by the poly-urea-, coated carbon fiber reinforced polymer composite. wrapped around the foam core substrate is instark contrast to the foam core substrate wrapped with only the .catbon fiber reinfOrced polymer fabric. As shown in images 1110 and 1313, upon performing the impact test, the carbon fiber reinforced polymer fabric de-bonds from the foam core substrate.
In comparison, images 1320 and 1325 illustrate that the polyurea-coated carbon fiber reinforced.
polymer composite can absorb much more energy from the impact and dissipate the energy.
As a result, the polyurea-coated carbon fiber reinforced polymer composite allows the foam core to experience significant increases in displacement and energy dissipation. It should be .noted that there is no debonding in the foam core wrapped with the polytirea-coated carbon fiber reinforced polymer composite.
101961 Turning to FIGS. 14.A and 14B, the two thin steel beam substrates were subjected to high vibration tests. As described above, the polyurea-coated carbon fiber reinforced .polymer composite transitions from a viscoelastic material to a nearly viscous material. The composite can act as an energy-release valve by providing sustainable energy dissipation and large viscous-type damping during extreme loading events, such as during earthquakes. in some embodiments, the composite/substrate system can allow .fer a change .viscous damping ratio (e.g., the composite/substrate system has a different viscous damping ratio than the substrate alone).
101971 As shown, when comparing the results between the steel beam substrate that was wrapped only with a carbon fiber reinforced polymer fabric and the steel beam substrate that was wrapped with a polyurea-coated carbon fiber reinforced polymer composite of the disclosed subject matter, the polyurea,coated carbon fiber reinforced polymer composite provides viscous-type damping to minimize vibrations during the testing.
EXAMPLE 8: Damping Ratio of the Composite 101981 It should be noted that, in some embodiments, the properties of the composite material can be 'modified by varying time-related 00 and volume-fraction Old polymeric properties. For example, as shown in FIGS. 15A and .15C, properties of the composite, such as damping ratio, can be modified by controlling the thickness of the polyurea coatina layer.
Controlling the thickness of the polyurea coating layer can alter the volume .fraction of elastomeric polyurea in the composite, which can alter the properties of the resulting composite. In another example, as shown in FIGS. 158 and I 5D, time-related factors in the preparation of the composite material (eg., time factors related to the reaction of the precursors of the polyurea layer and the precursors of the polymer of the FRP) can affect the damping ratio of the composite as a whole, thereby enabling the strength of the resulting load-bearing composite to be sustained at large deformations Accordingly, the composite .material may be modified during the fabrication of the. composite material (e.g., method 200 of FIG. 2, method 300 of FIG. 3, etc.) to achieve desired properties.
191991 Turning to FIG. I5A, thin steel beams were used. The damping ratio determination included a steel beam by itself, a steel beam wrapped only with a carbon fiber reinforced -polymer fabric, a steel beam wrapped with a polyurea-coated carbon fiber reinforced polymer composite (where the poly-urea layer is 1132'd of an inch), and a steel beam wrapped with a polyurea-coated carbon fiber reinforced polymer composite (where the polyurea layer is 1116th of an inch). As shown in FIG. 15A, the damping ratio is significantly greater for steel beams wrapped with the polyurea-coated carbon fiber reinforced polymer composite. In addition, FIG. 15A shows that the damping ratio of a steel beam wrapped with the polyurea-coated carbon fiber reinforced polymer composite can vary as a function of the.
thickness of the polyurea layer. Increasing the thickness of the polyurea layer (e.g,, from I/32'i of an inch to 1/1(.' an inch), substantially increases the damping ratio, I0200 As shown in FIG. 158, the curing time for forming the polyurea layer on the carbon fiber reinforced polymer fabrk, where the composite was formed on a steel beam, was varied between two hours and. five hours. The damping ratio can vary as a function of time-related factors in the preparation of the composite material It should be noted, however, that other properties, such as slightly greater stiffness, may be achieved by increasing the curing time.
1024111 In this example, -these tests were conducted. with the polyurea-coated carbon fiber reinforced polymer composite by itself. This can, for example, remove any contributing effects from the thin steel beam. As shown in FIG. 15C, the damping ratio was determined for a carbon fiber reinforced polymer fabric, a polythrea-coated carbon fiber reinforced polymer composite (where the .polyurea layer is I/1 6th of an inch), and a polyurea-coated carbon fiber reinforced polymer composite (where the polyurea layer is 118th of an inch). As shown in FIG. 1 5C, the damping ratio is significantly greater lbr the polyureaecoated carbon fiber reinforced polymer composite than with the carbon fiber reinforced polymer fabric by itself. Similar to FIG. I5.A, FIG. I SC shows that the damping ratio the polyurea-coated carbon fiber reinforced polymer composite can -vary as a .function of the thickness of the polyurea layer. Increasing the thickness of the polyurea layer (e.g., from Ill 6th of an inch to 1/8th of an inch), substantially increases the damping ratio. In addition, the greater the thickness of the polyurea layer, the greater the strength and stiffness properties of the composite material, Accordingly, the thickness of the polyurea layer can be modified based.

on the desired properties of the resulting composite.
102021 Similar to FIG. 1513. FIG. 15D shows that the curing time for forming the polyurea layer on the carbon fiber reinforced polymer fabric affects the damping ratio. It should be noted, however, that although FIG. 15D Shows that damping ratio decreases as curing .time increases, caring time can be modified to achieve a composite material having a desired range of damping ratio. Again, the curing times used in making the composite .can be modified based on the desired properties of the .resulting composite.
(0203) Accordingly, high strength and high elasticity composite materials and methods of reinforcing substrates with the same are provided.
102041 Although .the invention has been described and illustrated in the foregoing illustrative embodiments, it is understood. that the present disclosure has been made only by way of example, and .that numerous changes in the details of implementation of the invention can be made without departing from the spirit and scope of the invention, which is only limited by the claims which follow. 'Features of the disclosed embodiments can be combined and rearranged in various ways.

Claims (20)

1. A composite comprising:
a substrate;
a fiber reinforced polymer fabric layer attached to at. least a portion of the substrate; and a polyurea coating layer formed on an exposed surface of the fiber reinforced polymer fabric layer.

2. The composite of claim 1, wherein the substrate is at least one of:
wood, masonry, concrete, steel, and a combination thereof,

3. The composite of claim 1 , wherein the substrate has at least one damaged portion and the fiber reinforced polymer fabric layer and the polyurea coating layer are formed on the at least one damaged portion of the substrate.

4. The composite of claim 1, wherein the fiber reinforced polymer fabric layer is a carbon fiber reinforced polymer fabric,

5. The composite of claim 1, wherein the polyurea coating layer is formed by applying an elastomeric polyurea-forming component solution to the exposed surface of the fiber reinforced polymer fabric layer, wherein the elastomeric polyurea-forming component solution forms an aromatic polyurea coating layer.

6. The composite of claim 1, wherein the polyurea further comprises an additive component, wherein the additive component is at least one of: an ultraviolet am protective additive, a flame retardant, a corrosion protective additive, a moisture resistance additive, ceramic microspheres, and a combination thereof.

7. A method for reinforcing a substrate, the method comprising:
providing a substrate;
attaching a high tenacity fiber reinforced polymer fabric to at least a portion of the substrate;
applying a saturant composition to an exposed surface of the high tenacity fiber reinforced polymer fabric, wherein the saturant composition comprises a polymer resin;
curing the saturant composition to form a tacky surface;
applying an elastomeric polyurea-forming component solution to the tacky surface; and curing the polyurea-forming component solution to form a polyurea coating layer.

8. The method of claim 7, wherein the substrate is at least one of wood, masonry, concrete, steel, and a combination thereof.

9. The method of claim 7, wherein the saturant composition is cured for a first time period and wherein the polyurea-forming component solution is cured for a second time period, the method further comprising modifying the first time period and the second time period to obtain material properties of the polyurea coating layer on the high tenacity fiber reinforced polymer fabric.

10. The method of claim 7, further comprising performing surface preparation on at least a portion of the substrate, wherein the surface preparation includes at least one of:
smoothing the substrate, tilling in one or more damaged portions of the substrate with a puny material, and cleaning the substrate.

11. The method of claim 7, wherein the high tenacity fiber reinforced polymer fabric is wrapped around the substrate.

12. The method of claim 7, wherein the polyurea-forming component solution comprises an isocyanate component and a polyamine component, the method further comprising mixing the isocyanate component and the polyamine component prior to the applying to the tacky surface to form the polyurea-forming component solution, wherein the polyurea-forming component solution has an excess of the isocyanate component.

13. The method of claim 7, further comprising spraying the polyurea-forming component solution on the tacky surface.

14. The method of claim 7, further comprising providing an additive component into the polyurea-forming component solution, wherein the additive component is at least one of: an ultraviolet (UV) protective additive, a flame retardant, a corrosion protective additive, a moisture resistance additive, ceramic microspheres, and a combination thereof.

15. The method of claim 7, wherein the polyurea coating layer has a thickness, the method further comprising controlling the thickness of the polyurea coating layer.

16. The method of claim 7, wherein at least a first component of the polyurea-forming component solution and a second component of the tacky surface of the saturant composition applied to the high tenacity fiber reinforced polymer fabric interact to form an sustainable interface between the polyurea coating layer and the high tenacity fiber reinforced.
polymer fabric.

17. A method for providing a composite, the method comprising:
forming a polyurea-coated high tenacity fiber reinforced polymer fabric, wherein the forming comprises:
providing a Web tenacity fiber reinforced polymer fabric;
applying a saturant composition to a surface of the high tenacity fiber reinforced polymer fabric, wherein the saturant composition comprises a polymer resin;
curing the saturant. composition to form a tacky surface;
applying an elastomeric polyurea-forming component solution to the tacky surface; and curing the polyurea-forming component solution to form a polyurea coating layer on the high tenacity fiber reinforced polymer fabric..

18. The method of claim 17, further comprising:
preparing at least a portion of a substrate for reinforcement prior to positioning the polyurea-coated high tenacity fiber reinforced polymer fabric on the substrate; and attaching the polyurea-coated high tenacity fiber reinforced polymer fabric to a damaged portion of the substrate.

19. The method of claim 17, wherein the saturant composition is cured for a first time period and wherein the polyurea-forming component solution is cured for a second tune period, the method further comprising modifying the first time period and the second time period to obtain the polyurea coating layer of a thickness based at least in part on an assessment of the damaged portion of the substrate.

20. The method of claim 17, wherein at least a .first component of the polyurea, forming component solution and a second component of the tacky surface of the saturant composition applied to the high tenacity fiber reinforced polymer fabric interact to form an sustainable interface between the polyurea coating layer and the high tenacity fiber reinforced polymer fabric.