CA2412415A1 - Ion conductive membrane for electrochemical application - Google Patents

Ion conductive membrane for electrochemical application Download PDF

Info

Publication number
CA2412415A1
CA2412415A1 CA002412415A CA2412415A CA2412415A1 CA 2412415 A1 CA2412415 A1 CA 2412415A1 CA 002412415 A CA002412415 A CA 002412415A CA 2412415 A CA2412415 A CA 2412415A CA 2412415 A1 CA2412415 A1 CA 2412415A1
Authority
CA
Canada
Prior art keywords
membrane
general formula
polymer
membrane according
polyimide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CA002412415A
Other languages
French (fr)
Other versions
CA2412415C (en
Inventor
Yolanda Alvarez-Gallego
Suzana Pereira Nunes
Kai Jakoby
Javier De Abajo
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GKSS Forshungszentrum Geesthacht GmbH
Original Assignee
GKSS Forshungszentrum Geesthacht GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to EP02025254A priority Critical patent/EP1420037B8/en
Application filed by GKSS Forshungszentrum Geesthacht GmbH filed Critical GKSS Forshungszentrum Geesthacht GmbH
Priority to CA002412415A priority patent/CA2412415C/en
Publication of CA2412415A1 publication Critical patent/CA2412415A1/en
Application granted granted Critical
Publication of CA2412415C publication Critical patent/CA2412415C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

An ion conductive membrane for electrochemical applications is provided for forming the membrane on the basis of a polyimide or copolyimide polymer, which contains in its structure heterocyclic groups, particularly in the form of imidazole-, pyridin or pyrimidin groups. The electrochemical applications include particularly the use of such membranes in fuel cells.

Claims (9)

1. An ion conductive membrane, for electrochemical applications, on the basis of an aromatic polyimide or co-polyimide polymer containing the same or different units of the general formula I
wherein B is a rest representing at least one aromatic heterocycle of the general formula II
with R substituted for H representing one of a phenyl rest, a phosphoric acid group and at least one chain containing a phosphoric acid group and A representing one of the following groups containing at least one napthalene unit and having the general formula and forming with the neighboring imide groups rings with 6 atoms.
2. A membrane according to claim 1, wherein said polymer is built up from recurring units of the general formula I.
3. A membrane according to claim 1, comprising at least one of the group consisting of diamine, diaminopyridin and diaminopyrimidin, which are reacted with at least one of bis(napthalene-acidanhydride) and a diacid-diakylyester or dialcylchloride-diakylester derivate of the these dianhydrides.
4. A membrane according to claim 3, wherein, as diamin, there is at least one of a 4.5-di(3 amino phenyl)imidazole and 5-(2-benzimidazole)-1.3-phenylendiamin.
5. A membrane according to claim 1, wherein said polymer is modified by introduction of another group, particularly a phosphoric acid group, and the membrane is doped with an acid or an organic modifier.
6. A membrane according to claim 1, wherein said membrane is produced by a casting solution of one of the polyimide and the copolyimide polymer.
7. The use of a membrane as defined in claim 1 for electrochemical application.
8. The use of a membrane as defined in claim 1 for installation in a fuel cell.
9
CA002412415A 2002-11-12 2002-11-20 Ion conductive membrane for electrochemical application Expired - Fee Related CA2412415C (en)