CA2361463A1 - A method of reducing wrinkles and improving feel in fabrics - Google Patents

Abstract

The present invention is directed to a method for treating a material to impart wrinkle reduction and temporary crease resistance thereto, and improve feel. The method involves:
applying to said material a solution of a treatment composition in an amount effective to impart temporary crease and stain resistance, said treatment composition contains a hydroxy urea or hydroxy amide compound; and allowing said treatment composition to dry at ambient temperature, wherein said hydroxy urea compound comprises one urea and at least one hydroxyl group and said hydroxy amide compound comprises at least one amide group and at least one hydroxyl group. The material treatment is useful in reducing wrinkles in clothing, improving the feel of fabrics, and increasing the moisture adsorbence and retention in natural and synthetic fabrics.

Description

A Method for Reducing Wrinkles and Improving Feel in Fabrics FIELD OF THE INVENTION
The present invention relates to the use of a treatment composition comprising a hydroxy urea or hydroxy amide compound in the treatment of a material to reduce wrinkles, impart temporary crease resistance and improve fabric hand (feel), and increase moisture absorbance.
More specifically, the method of the invention involves applying the hydroxy compound to a material, in a solution, neat or as a mist, and allowing the material to dry at ambient temperature, without the application of an external heat source. The treatment composition can also be included in a laundry detergent or fabric softener.
BACKGROUND OF THE INVENTION
Clothing, fabric, and other materials, free of wrinkles are viewed in a more favorable light than the same materials that are wrinkled. Thus there have been many methods developed to reduce wrinkles on clothing and other materials, and to develop materials resistant to wrinkling. The use of thermosetting resins or reactants to impart crease resistance and dimensional stability to textile materials is well-known in the art. These materials, known as "aminoplast resins", include the products of the reaction of formaldehyde with such compounds as urea, thiourea, ethylene urea, dihydroxyethylene urea, melamines or the like. A serious drawback to the use of such materials is that they contain free formaldehyde. This is present during the preparation and storage of the finishing agent and its use in treating textiles, on the treated fabric, and on the finished garments.
Also, when the fabrics or garments made therefrom are stored under humid conditions, additional free formaldehyde is produced.
The presence of even less than one percent of free formaldehyde, based on the total weight of the product, is undesirable, not only because of its unpleasant odor, but because it is an allergen and an irritant, causing severe reactions in the operators who manufacture the agent and who treat and handle the treated fabrics and to persons who handle and wear garments fabricated from the treated fabrics.

Solutions containing lubricants such as silicone compounds are known to reduce interfiber friction, allowing fibers to slide past each other and thereby reducing wrinkling. Such compounds are described in the art such as in U.S. Patent Number 5,968,404, and in WO
11/24857.
U.S. Patent Number 5,879,749 describes compositions containing a poly-functional molecule having at least two functional groups selected from carboxyl, anhydride and amine which is crosslinked using a (hydroxyalkyl)urea crosslinking agent. U.S. Patent Number 5,965,466 describes the use of hydroxyalkyl urea and/or ~-hydroxyalkylamide for imparting permanent press properties to a textile containing cellulose fibers. U.S. Patent No. 4,076,917 describes (3-hydroxyalkylamides as curing agents for polymers containing one or more carboxy or anhydride functions. These references require a heating step following application of the composition to the fabric, in order to effect a cross-linking reaction.
Treating textiles with resin compositions that do not contain or evolve formaldehyde is also known, as in U.S. Patent No. 3,260,565 which describes finishing agents formed by the reaction of alkyl or aryl ureas or thioureas with glyoxal. U.S. Patent Nos. 4,332,586 and 4,300,898 describe alkylated glyoxal/cyclic urea condensates as crosslinking agents for textiles.
U.S. Patent No.
4,295,846 describes a finishing agent for textiles which is prepared by reacting urea or symmetrically disubstituted ureas in an aqueous solution with glyoxal. These agents, however, have the disadvantage of having marginal permanent press properties. Finishing agents formed by the reaction of ethylene urea with glyoxal are described in Japanese publication No. 5 3044-567, but they too do not have satisfactory properties.
Copending U.S. application 09/456,358 describes a texile antiwrinkling composition containing polyhydroxyalkyl urea crease resistance agents having at least two urea moities.
There is a need for a material treatment composition which can be applied to a material to reduce wrinkles and impart temporary permanent press properties, without the need to follow the application with the addition of an external heat source. Ideally the treatment composition should be one which does not emit formaldehyde. Surprisingly, it has been found that a hydroxy urea or hydroxy amide compound, when applied to a fabric by means such as a spray, will reduce wrinkles, without the need for the addition of an external heat source. This method provides consumers the ability to provide crease resistance properties easily and cost-effectively to clothing at home, and even the ability to reduce wrinkles on clothing being worn. Furthermore, there is a need for anti-wrinkling treatments that do not discolor the fabric. Additionally the treatment should not negatively impact stain removal unlike the silicones that are difficult to clean because they attract oily stains. Finally, there is a need for a material that does not leave the fabric with an oily type of finish. The method of the present invention fulfills these needs.
SUMMARY OF THE INVENTION
The present invention relates to a method of treating a material which comprises applying to the material an amount of a treatment composition which is effective to impart temporary crease resistance.
The treatment composition comprises a hydroxy compound which is either a hydroxy urea or a hydroxy amide. The material treatment composition may be applied to clothing, fabric, and textiles; and without the need of an external heat source, reduce wrinkles and provide the material temporary crease resistance. In addition, there is no build-up of the composition on clothes or irons, and no residual flaking is noted, even on dark fabric. The treatment composition may also be formulated into a laundry detergent or fabric softener and thus applied to a material in the wash or rinse cycle. The treated material also has a tactile sensation of feeling soft, and increased moisture absorbance. Moreover, there is no discoloration of the fabric and the material does not hold on to oily stains unlike the silicones typically used.
DESCRIPTION OF THE INVENTION
This invention relates to a method for imparting wrinkle reduction , permanent press properties, and improved feel, and increased moisture absorbance to a material. As used herein, "crease resistance" shall be synonymous with wrinkle resistance, durable press, dimensional stability, shrinkage resistance, and wrinkle recovery. The method involves applying a treatment composition of a hydroxy compound to a material, and allowing the material to dry at ambient temperature without application of an external heat source, to impart crease resistance properties to the material. The treatment composition is essentially free of formaldehyde and may be applied in the form of a solution or neat.
The material treated by the method of the present invention consists of a natural or synthetic material. The material may be a material such a leather, or a fibrous material. Fibrous materials may be natural, synthetic, or a mixture thereof. Such material includes, but is not limited to, fabrics, textiles, non-wovens, and finished products made from these materials. The material preferably is a cellulosic fabric or textile, and may be woven or non-woven, and includes 100 percent cellulosic fabrics, for example, cotton, rayon, and linen, as well as blends, for example, polyester/cotton or polyester/rayon . The fibrous material may also be a non-cellulosic natural or synthetic fiber, such as for example nylon, silk, and polyester. Both white and colored (printed, dyed, yarn-dyed, cross-dyed, etc.) materials can be effectively treated with the material treatment composition of the present invention. The materials may comprise new or used clothing including previously worn clothing and/or laundered clothing.
The hydroxy compound is either a hydroxy urea or a hydroxy amide. The hydroxy urea useful in the present invention is one containing one urea functionality and at least one hydroxyl functionality.
The term urea, as used herein, refers to a N-CO-N moiety in which the other two bonds on each nitrogen atom form additional attachments, as for example those found in the illustrations and examples herein. The urea and hydroxyl functionalities may be separated from each other in the compound by one carbon atom. Preferably they are separated by at least two carbon atoms. The hydroxy amide useful in the invention is one containing at least one amide functionality and at least one hydroxyl functionality. Preferably the hydroxy compound should not be a formaldehyde emitter.
The preferred compounds of the invention are either a hydroxyalkyl urea, or a v-hydroxyalkyl amide, or a mixture thereof.
Preferred hydroxy urea compounds are derived from urea, and comprise only a single urea group, at least one hydroxyl group, at least two carbon atoms disposed between the urea group and each of the hydroxyl groups. The two carbons disposed between the hydroxyl and urea groups may be in linear, branched or substituted configuration. The hydroxy urea compound is represented by structure (I) as follows:
O
R3 ~ R' (I) NCN

wherein R' is C-R', Rs R2 is H or Rs, R3 is H or R5, and R4 is H, R', or Rs, wherein R$ R9 Re R9 R'°
RS is H, CH20H, CHCHOH, CHCHCHOH or C,-C4 alkyl, R8 R9 Rg R9 R'°
R6 is H, CH20H, CHCHOH, CHCHCHOH or C,-C4 alkyl, and RB R9 R8 R9 R'°
R' is H, CH20H, CHCHOH, CHCHCHOH or C,-C4 alkyl, wherein R8 is H, methyl or ethyl, R9 is H, methyl or ethyl, and R'° is H, methyl or ethyl.
Preferred hyroxy urea compounds are N-2-hydroxyethyl urea, N,N-bis(2-hydroxyethyl)urea, tetrakis(2-hydroxyethyl)urea, tris(2-hydroxyethyl)urea, N,N'-bis(2-hydroxyethyl)urea, N,N'-bis(3-hydroxypropyl)urea, N,N'-bis(4-hydroxybutyl)urea, N-methyl-D-glucourea, and 2-urea-2-ethyl-1,3-propanediol. Most preferably, the hydroxy urea compound is N,N'-bis(2-hydroxyethyl)urea.
Combinations of hydroxy urea compounds can also be used in the method of the invention.
The hydroxy urea compound is the reaction product of urea and an alkanolamine with the evolution of ammonia. Preferred alkanolamines include, but are not limited to, diethanolamine, monoethanolamine, 2-amino-2-methyl-1,3-propanediol, bis(hydroxymethyl)amino-methane, 2-methyl-3-amino-1-propanol and 2-methylaminoethanol. Processes for preparing the hydroxy urea compound is described in U.S. Patent Application Serial No. 08/783,350 which is hereby incorporated herein by reference.
Preferred hydroxy amide compounds are (3-hydroxyalkyl amide compounds represented by structure (II) as follows:
O O
[HO(R,3)2C(R,2)2C-N-C-]~ A-[-C-N-C(R,2)2C(R,s)20H]~
.
R" R"
In structure (II), A is a bond, hydrogen or a monovalent or polyvalent organic radical derived from a saturated or unsaturated alkyl radical wherein the alkyl radical contains from 1 to 60 carbon atoms, such as methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, eicosyl, triacontyl, tetracontyl, pentacontyl, hexylcontyl and the like; aryl, for example, mono-and dinuclear aryl such as phenyl, naphthyl and the like; tri-lower alkyleneamino such as trimethyleneamino, triethyleneamino and the like; or an unsaturated radical containing one or more ethylenic groups such as ethenyl, 1-methylethenyl, 3-butenyl-1,3-diyl, 2-propenyl-1,2-diyl, carboxy lower alkenyl, such as 3-carboxy-2-propenyl and the like, lower alkoxy carbonyl lower alkenyl such as 3-ethoxycarbonyl-2-propenyl and the like; R" is hydrogen, lower alkyl of from 1 to 5 carbon atoms such as methyl, ethyl, n-propyl, n-butyl, sec-butyl, tert-butyl, pentyl and the like or hydroxy lower alkyl of from 1 to 5 carbon atoms such as hydroxyethyl, 3-hydroxypropyl, 2-hydroxypropyl, 4-hydroxybutyl, 3-hydroxybutyl, 2-hydroxy-2-methylpropyl, 5-hydroxypentyl, 4-hydroxypentyl, 3-hydroxypentyl, 2-hydroxypentyl and the isomers of pentyl; R'2 and R'3 are the same or different radicals selected from hydrogen, straight or branched chain lower alkyl of from 1 to 5 carbon atoms or one of the R'2 and one of the R'3 radicals may be joined to form, together with the carbon atoms, such as cyclopentyl, cyclohexyl and the like; n is an integer having a value of 1 or 2 and n' is an integer having a value of 0 to 2 or when n' is 0.
A preferred (3-hydroxyalkyl amide compound is represented by structure (III) as follows:
R' 3 O O R' 3 . ) ) .
HO-CHCH2N-C-(CH2)m C-N-CH2-CH-OH
R" R"
In structure (III), R" is H, lower alkyl, or HO(R'3 )2C(R'2 )2C-, n and n' are each 1,-A- is -(CH2)[m]-, m is 0-8, preferably 2-8, each R'2 is H, and one of the R'3 radicals in each case is H and the other is H
or a C,-CS alkyl; that is wherein R", R'3, and m have the meanings just given.
The most preferred (3-hydroxyalkyl amide compound is represented by structure (IV) as follows:
R' 3 O O R' 3 (HO-CHCH2)2N-C-(CH2)mC-N(CH2CHOH)2 In structure (IV), R'3 is H or -CH3.
Specific examples of (3-hydroxyalkyl amide compounds are bis[N,N-di(beta-hydroxyethyl)]
adipamide, bis[N,N-di(beta-hydroxypropyl)] succinamide, bis[N,N-di(beta-hydroxyethyl)] azelamide, bis[N-N-di(beta-hydroxypropyl)] adipamide, and bis[N-methyl-N-(beta-hydroxyethyl)] oxamide.
The (3-hydroxyalkyl amide compounds are either known compounds or may be prepared by treating an ester with an amine at a temperature in the range of from about ambient to about 200°C.

Suitable esters are prepared by esterifying the corresponding acid by standard esterifying procedures.
Among the preferred acids used to prepare the (3-hydroxyalkyl amide crosslinking agents are oxalic, malonic, succinic, glutaric, adipic, pimelic, suberic, azelaic, sebacic, 1,4-cyclohexane and the like and alkyl derivatives thereof. Dimer and trimer acids may also be used. Suitable amines used to prepare the (3-hydroxyalkyl amide compounds are 2-aminoethanol; 2-methylaminoethanol;

ethylaminoethanol; 2-n-propylaminoethanol; 2,2'-iminodiethanol; 2-aminopropanol; 2,2'-iminodiisopropanol; 2-aminocyclohexanol; 2-aminocyclopentanol; 2-aminomethyl-2-methylethanol; 2-n-butylaminoethanol; 2-methylamino-1,2-dimethylethanol; 2-amino-2-methyl-1-propanol; 2-amino-2-methyl-1,3-propanediol; 2-amino-2-ethyl-1,3-propanediol and 2-amino-2-hydroxymethyl-1,3-propanediol. The [3-hydroxyalkyl amide compounds are prepared according to processes described in U.S. Patent No. 4,076,917 which is hereby incorporated herein by reference.
The treatment composition of the present invention can be used either in the neat form, or as a solution. It can also be formulated into a liquid or powder form laundry detergent or fabric softener composition. A solution can be in any solvent which forms a solution or suspension with the hydroxy compound. Examples of useful solvents include, but are not limited to, water, acetone and alcohols such as methanol, ethanol, propanols and butanols, and mixtures of such solvents. A preferred solvent is water. An aqueous solution containing the hydroxy compound preferably has a pH of from about 1 to about 12, more preferably from about 2 to about 10, and most preferably from 4 to 7.
Most preferably, an aqueous solution containing the hydroxy compound has a pH
of from about 3 to about 8. It is understood that any means of adjusting the pH of the aqueous solution may be employed in the method of the invention to achieve a desired pH. The treatment composition may contain, in addition to the hydroxy compound, one or more compounds selected from the group containing surfactants; buffers; dyes; electrolytes; builders; modified or unmodified cellulosic compounds; modified or unmodified starch; polymers which are cationic, nonionic or zwitterionic;
enzymes; cyclodextrins; silicones; and fragrances. Compositions containing a mono hydroxy alkyl urea may also be combined with anionic polymers.
Any method of applying the treatment composition to the material is acceptable. Some examples of application methods include, but are not limited to, spray or mist application, application in the laundering process wash or rinse cycle, application from a sheet of material containing the treatment compound - for example in a dryer, and immersion in a solution containing the treatment composition.
A preferred method of applying the treatment composition to a material is by spray or mist application by means of a pump or aerosol, or other methods known in the art.
One method, useful for individual use, is application from a spray or mist bottle. The treatment composition may be applied to clothing, which is being worn, as well as to clothing not being worn.
Misting can also occur in an industrial or consumer apparatus designed for such a use, such as a home valet machine or a machine for freshening clothing.
The material may be impregnated with an aqueous solution of the treatment composition. As used herein, "impregnate" refers to the penetration of the solution into the fiber matrix of the material, and to the distribution of the solution in a preferably substantially uniform manner into and through the interstices in the material. The solution therefore preferably envelopes, surrounds, and/or impregnates individual fibers substantially through the thickness of the material as opposed to only forming a surface coating on the material.
The treatment composition may be applied to the textile in a textile manufacturing process as part of the durable press finishing operation. Where the textile is not treated in a textile manufacturing process, the treatment composition may be applied in a laundering process, most preferably to rinse water in the rinse cycle of the laundering process at home or at a Laundromat.
The treatment composition may also be transferred to the material to be treated through contact with another material impregnated with the treatment composition. An example would be the addition to a dryer or tumbling device of a sheet containing the treatment composition of the invention, and the transfer of the treatment composition to laundry through contact in the dryer. Since heat is not required for the method of the present invention, this method of application is useful on no-heat or low-heat settings. Application by an impregnated sheet can also include the use of such a sheet in home dry cleaning applications.
Additionally, the treatment composition may be applied by soaking the textile in a solution containing the treatment composition.
The material treated with the treatment composition of the present invention is dried at ambient temperature, without the need for an external heat source. Application of an external heat source could speed the drying process, but is not required for the method of the present invention.
Such heat sources include, but are not limited to temperatures found in a clothes dryer.

The hydroxy compound is present in an amount sufficient to provide about 0.00001 to about percent of hydroxy compound in the material based on the oven-dry weight of the material.
Preferably, the hydroxy compound is present in an amount sufficient to provide from about 0.1 to about 5 weight percent, and more preferably from about 0.5 to about 2 weight percent of hydroxy 5 compound in the material based on the oven-dry weight of the material.
A dilute solution of the material is typically sprayed on to the fabric. The spray solution may contain 0.001 to 20 weight percent of the hydroxy urea compound, preferably 0.1 to 10 percent and most preferably 0.5 to 5 percent.
The treatment composition of the present invention may be formulated as a portion of a laundry 10 detergent or a fabric softener. The treatment composition may be formulated into both liquid and powdered or tableted detergents. The hydroxy compound is present in the detergent or fabric softener at from 0.0001 to 20, preferably from 0.1 to 10, and most preferrably from 0.5 to 5 percent. The treatment composition of the present invention may be formulated into the detergent or fabric softener using standard methods known in the art.
Application of the treatment composition to a material occurs during a normal wash and/or rinse cycle. A
laundry detergent composition containing the hydroxy compound of the present invention could also contain ingredients typically found in laundry detergents, including, but not limited to surfactants, builders and co-builders, dispersants, enzymes, fillers, and dye. Likewise, fabric softener compositions containing the hydroxy compound of the present invention also contains other ingredients typically found in a fabric softener. In addition to providing wrinkle reduction and feel improvement, the hydroxy compound of the invention also serves as a dissolution aid for detergents in the form of tablets or sachets, and will help hard ingredients to dissolve faster in detergent powders.
The hydroxy compound may be encapsulated in a material, such as a starch, modified starch, cellulosie, or modified cellulosic,for delivery onto the material to be treated.
The method of the present invention provides crease resistance properties to materials treated therewith. Moreover, the treated textiles have a tactile sensation of feeling soft and retain their smoothness even after laundering.
The following non-limiting examples illustrate further aspects of the invention.

106.2 g diethanolamine and 61.24 g urea were charged to a 250 mL flask equipped with a condenser, thermometer, stirrer, and nitrogen purge needle. The mixture was heated at 115 °C for 5 hours. A nitrogen purge was used to remove evolving ammonia. The progress of the reaction was monitored by titration of the remaining diethanolamine with 0.1 N hydrochloric acid. A clear hydroscopic liquid was obtained which contained N,N-bis(2-hydroxyethyl)urea.

The following amines were reacted with urea according to the procedure set forth in Example 1.
Wt, Urea Example Amine g g ___. _.____. ____.____ _.... __ ~: ....___ __._. __._.___ _ _.._... __..__._ _ ......_._._..
2 Ethanolamme 61 60 3 3-amino-1-propanol 150 60 4 2-amino-2-ethyl-1,3-propanediol 119 30 (AEPD) Ethanolamine 122 60 6 Diethanolamine 210 60 7 4-aminobutanol 12 4 212.4 g diethanolamine in 212.4 g of water was neutralized with 101.85 g concentrated sulfuric acid to a pH of 4. A solution of 168.99 g potassium cyanate in 260 g of water was then added and the mixture was heated to 90 °C for 3 hours. After cooling to ambient temperature, potassium sulfate precipitated and was filtered out. The filter cake was washed with 425 g of hot ethanol. The recovered ethanol was then added to the contents of the filtrate, causing the filtrate to become cloudy.
The white precipitate was removed by filtration and then the ethanol was removed by distillation to give a viscous liquid solution of N,N-bis(2-hydroxyethyl)urea. The product similarly could be obtained using other acids to neutralize the amine, e.g. sulfuric acid. Also, other cyanate salts could be used, e.g. sodium cyanate.

Following the procedure of Example 8, 195.22 g N-methyl-D-glucamine in 200 g water were reacted with 98.08 g sulfuric acid. After adjusting pH to 4, 81.11 g potassium cyanate was charged to the flask in 100 g water. The mixture was heated to 70 °C for 2 hours.
After cooling to 0 °C, the precipitated potassium sulfate byproduct was removed by filtration. The filtrate was treated with 250 mL of hot methanol and again filtered to remove any remaining salt byproduct.
The methanol was then removed by vacuum distillation to give a solution containing N-methyl-D-glucourea.

Using the procedure set forth in Example 1, the reaction can also be conducted effectively using refluxing water as a means of removing evolving ammonia. 105 g diethanolamine, 25 g water, and 60 g urea were charged in a 250 mL flask equipped with heating mantle, stirrer, and thermometer and allowed to react at 115 °C for 8 hours.

210 g diethanolamine and 90 g dimethylcarbonate were charged to a flask with a heating mantle, stirrer, and condenser. The flask contents were heated to 80 °C and allowed to stir for 3 hours.
Volatile byproducts, e.g., methanol, were removed by vacuum distillation. A
mixture containing tetrakis(2-hydroxyethyl)urea was obtained.

To a solution of 106 g of diethanolamine in 700 mL of methanol was added a solution of 99 g of n-butylisocyanate in 40 mL of tetrahydrofuran over 1 hour, holding the temperature below 30 °C. After the addition, the mixture was stirred for 1 hour and then the solvent was removed by vacuum distillation to give a white solid, N'-butyl-N,N-bis(2-hydroxyethyl)urea.

The following amines were reacted with an isocyanate according to the procedure set forth in Example 12.
Example Amine Wt. Isocyanate Wt.
(g) (g) 13 EthanOlamine 61 N-butyl isocyanate 99 14 N-methyl-D-glucoamine 196 N-butyl isocyanate 99 A 500 mL flask equipped with stirrer and condenser was charged with 145.1 g of 40% glyoxal and 90 g of urea. The temperature was held at 30 °C for 6 hours. The resultant solution contained 4,5-dihydroxyimidazolidone.

Cotton swatches, 6" by 11" were sprayed with a solution of tfie Example compounds, such that 7 x 10-4 moles of the material were delivered to the fabric. The swatches were allowed to dry overnight and then the wrinkle recovery was measured as in AATCC (American Association of Textile Chemists and Colorists) Test Method 128-1980. Instead of using the standard evaluation method found in section 6, a pairwise comparison of the wrinkled swatches was used. Less wrinkled swatches were given a score of 2, while the more wrinkled fabric was assigned a value of 1. When no difference in fabric appearance could be distinguished, a ranking of 1.5 was given to each swatch.
The totals for each swatch were added together and called "rank sum". By this method, swatches with a higher rank sum were found to be less wrinkled by the panelists.

Table 1 Swatches 5" by 5" in size were sprayed with an aqueous solution of the Example materials to give the concentrations on the swatch as shown in Table 2. The swatches were conditioned in a dessicator kept at constant humidity level to equilibrate the samples. The humidity level was controlled by saturated salt aqueous solutions. After conditioning, the cloth samples were loaded into the TGA
instrument at room temperature, equilibrated for half a minute at 25 °C, then heated to 100 °C and held at 105 °C for 10 minutes. TGA measurements were conducted under ultra pure N2. The instrument detected the sample weight loss in percentage of total starting sample weight. The experimental error was about 0.5. The weight loss was found to be due to water loss rather than to derivative decomposition. The total water loss is effectively the water uptake of the swatches at 100%
relative humidity. The total water uptake is for each of the materials is shown in Table 2. Samples, which were treated with hydroxy urea materials, were shown to absorb more water than samples with no treatment.
Table 2: Moisturizin4 Effect of Hydroxy Ureas Moles materialWater Uptake /

gram swatch 100% RH

Material(moles / g) (% mass increase) _._._~ ~~..._.____.__.~____.____.._ ~____. . ~_.._.__ ~ _...__..~.____._._......
~ 5.11 x 10 40.8 2 5.02 x 10-3 42.9 9 5.38 x 10-3 54.2 13 5.54 x 10-3 33.9 14 5.15 x 10-3 37.4 12 4.98 x 10-3 31.7 W ater 0 14.4 EXAMPLE 18 - fabric feel For the fabric feel test, 3% solutions were made of each of the following products; Example 1 (N,N-bis(2-hydroxy ethyl urea)), Example 2 (N-2-hydroxyethylurea) and Example 9 (N-methyl-D-glucourea). These solutions were sprayed for 10 seconds each onto 10 inch square swatches of cotton, 50/50 cotton polyester blend, and polyester. The swatches were then ironed dry. A panel was asked to evaluate the feel of the fabric by comparing each sample swatch to a blank swatch of the same fabric that had been sprayed with deionized water and ironed dry. Each individual decided if the sample felt better, worse or equal to the blank.
Results were tallied by allocating one point for a sample that felt better than the blank, deducting one point for a sample rated worse than the blank, and by giving zero points for samples that felt equivalent to the Fabric Feel Panel Results N

w O

Z

blank. Total points for each individual sample were then added together.
Results appear in the chart below.
Example 1 and Example 2 when applied to cotton, received the most points (four each). Example 1 also received three points on polycotton and two on polyester. Example 2 received two points each on polycotton and polyester. Example 9 performed poorly receiving two votes for polyester, one point for cotton and zero points for polycotton.
In order to decide the best overall performer, the points for a single product's use on each of the individual fabrics were added together. Example 1 had the best overall rating with nine points. Example 2 followed closely behind with eight points. Example 9 received an overall rating of three points. The maximum number of points available was eleven.
Following this evaluation, drops of water were placed on each sample and the rate of absorption was visually evaluated. There seemed to be no difference in the rate at which the water was absorbed by the various swatches but polyester samples ironed with Example 2 and Example 9 and Example 1 seemed to dry faster than the blank Cotton PolyCotton Polyester Fabric Granular Detergent Test Composition Preparation Typical heavy duty granular detergent compositions can be prepared containing one or more hydroxy compounds of this invention. These granular detergent compositions all have the following basic formula:

Com onent Wt.

C, Linear alk I benzene 9.31 sulfonate C,, alk 1 ether (0.35 12.74 EO sulfate Zeolite Builder 27.79 Sodium Carbonate 27.31 PEG 4000 1.60 Dis ersant 2.26 C _, Alcohol lEthox late 1.5 (9 EO

Sodium Perborate 1.03 Soil Release Pol mer 0.41 Enz mes 0.59 H drox com and 3.0 Perfume, Brightener, SudsBalance Suppressor, Other Minors, Moisture, Sulfate ioo%-l Liquid Detergent Test Composition Preparation Typical heavy duty liquid detergent compositions can be prepared containing one or more hydroxy compounds of this invention. These granular detergent compositions all have the following basic formula:

Com onent Wt.
%

C12-15 alk 1 ether 2.5) sulfate38 C12 lucose amide 6.86 Citric Acid 4.75 C12-14 Fatt Acid 2.00 Enz mes 1.02 MEA 1.0 Pro anediol 0.36 Borax 6.58 Dis ersant 1.48 Na Toluene Sulfonate 6.25 H drox com ound 1.0 Dye, Perfume, Brighteners, Balance Preservatives, Suds Su ressor, Other Minors, Water 100%

Granular Detergent Test Composition Preparation Typical granular detergent compositions can be prepared containing one or more hydroxy compounds of this invention. These granular detergent compositions all have the following basic formula:

Exam Com arative le Com onent _- Wt. % Wt. %

Na C,z Linear alk 1 benzene9.40 9.40 sulfonate Na C,4_,5 alk 1 sulfonate11.26 11.26 Zeolite Builder 27.79 27.29 Sodium Carbonate 27.31 27.31 PEG 4000 1.60 1.60 Dis ersant, Na of acr 2.26 2.26 late C,z_,3 alk 1 ethox late 1.5 1.5 (E9) Sodium Perborate 1.03 1.03 H drox com ound 2.0 0 Other Ad'unct in edients Balance Balance 100% 100%

Example 22 Typical dilute fabric softener formulations are listed below.

Formulations of Dilute Traditional Softeners (Single Active)a Formula A
.

_ In redient __ ( %

distearyldimethylammoniumChloride6-9 (75% active) Hydroxy compound 0.1 - 3.0 Perfume 0.2-0.5 Colorant 0.001 Water Balance Formula B

Quaternary dialkylimidazolines6-9 (75% active) Hydroxy compound 0.1 - 3.0 Perfume 0.2-0.5 Colorant 0.001 Preservative Example 23 Examples of concentrated fabric softener compositions.

Ready-to-Use Rinse Conditioners at Triple Concentration (Mixed Actives) Formula C

In redient %

distearyldimethylammonium 14 chloride 75%

hydroxy compound 3 Lanolin 2 Ethoxylated fatty acid 4 CaCl2 0.05 Water, erfume, color Balance Fomulation D

distearyldimethylammonium 5-10 chloride Amidoamine 5-10 Imidazoline 3.75-5.25 hydroxy compound 0.1 - 2.0 Electrolyte 0.05-.4 Water, erfume, color Balance Example 24 Examples of concentrated fabric softener compositions.

Examples of Concentrated Biodegradable Formulations Formulation E roduct wit h 37.5 %
actives) In redient ( %
) Amidoamine 23.45 Diester quat 14.05 Hydroxy compound 1.25 HCI 1.10 CaCl2 0.55 Emulsifier 0.5 Perfume 2 Colorant 0.03 Water Balance Formulation F

A B

Ester quat 5 2 Imidazoline-substituted 17 30 ester Isopropanol --- 1.5 Silicone 0.5 ---Hydroxy compound 0.25 0.75 Polyethylene glycol 1.2 ---Color, erfume, CaCI , Balance Balance Na citrite, water EXAMPLES OF DYER SHEET COMPOSITIONS
lO

MATERIALS IN FORMULATION G ARE COATED ON A NONWOVEN OR FABRIC SURFACE.
MATERIAL IN FORMULATION H IS AN EXAMPLE OF A FINAL USE APPLICATION.
FORMULATION G_ _ INGREDIENT %

DITALLOW DIMETHYL AMMONIUM70 22.7 METHYL SULFATE

-35.9 SORBITAN ESTER 29.1 BENTONITE CLAY 4.7 CYCLODEXTRIN STARCH 4.3 HYDROXY COMPOUND O.1 O.1 O

FORMULATION H

COMMERCIAL BOUNCE BRAND 2.S 2.S
DRYER

SHEET

HYDROXY UREA COMPOUND 1.3 0.38 RESULTS ( 1-3, LEAST 3 1 2 TO MOST

WRINKLED) ' oa number/ Numero de demande Applicati ~.I 3 Documents of poor quality scanned (request original documents in File Prep. Section on the 10'" floor) Documents de pietre qualite numerises (Pour obtenir les documents originau~c, veuillez vous adresser a la Section de preparation des dossiers, situee au l0e etage)

Claims (8)

1. A method for treating a material to impart wrinkle reduction and temporary crease resistance thereto, and improve feel, comprising:
a) applying to said material a treatment composition in an amount effective to impart temporary crease and stain resistance, said treatment composition comprising a hydroxy compound;
and b) allowing said treatment composition to dry at ambient temperature without requiring application of an external heat source, wherein said hydroxy compound comprises either:
1) a hydroxy urea comprising one urea and at least one hydroxyl moiety; or

2) a hydroxy amide comprising at least one amide and at least one hydroxyl moiety.

2. The method of claim 1 wherein said hydroxy compound comprises a (hydroxyalkyl)urea, .beta.-hydroxyalkylamide, or combinations thereof.

3. The method of claim 2 wherein a) said (hydroxyalkyl)urea has the structure wherein R2 is H or R5, R3 is H or R5, and R4 is H, R1, or R5, wherein R5 is H, CH2OH, or C1-C4 alkyl, R6 is H, CH2OH, or C1-C4 alkyl, and R7 is H, CH2OH, CHCHOH, CHCHCHOH or C1-C4 alkyl, wherein R8 is H, methyl or ethyl, R9 is H, methyl or ethyl, and R10 is H, methyl or ethyl; and b) said .beta.-hydroxyalkylamide has the structure wherein A is a bond, hydrogen, a monovalent or polyvalent organic radical derived from a saturated or unsaturated alkyl containing from 1 to 60 carbon atoms, aryl, tri-lower alkyleneamino or an ethylenically unsaturated radical; R11 is selected from the group consisting of hydrogen, lower alkyl having 1 to 5 carbon atoms, and hydroxyalkyl having from 1 to 5 carbon atoms;
R12 and R13 are independently selected from the group consisting of hydrogen, straight or branched chain lower alkyl having from 1 to 5 carbon atoms, and one of the R12 and R13 radicals joined together with the carbon atoms to which they are attached to form a cycloalkyl; n is an integer of 1 or 2 and n' is an integer of 0 to 2; n being 2 when n' is 0.

4. The method of claim 1 wherein said material is selected from the group consisting of cotton rayon, linen, leather, silk, polyester/cotton, polyester/rayon, and combinations thereof.

5. The method of Claim 2 wherein said hydroxy compound is selected from the group consisting of N,N-bis(2-hydroxyethyl)urea, tetrakis(2-hydroxyethyl)urea, tris(2-hydroxyethyl)urea, N,N'-bis(2-hydroxyethyl)urea, N,N'-bis(3-hydroxypropyl)urea, N,N'-bis(4-hydroxybutyl)urea, 2-urea-2-ethyl-1,3-propanediol, N-hydroxyethylurea, N-methyl-D-glocourea, and combinations thereof.

6. The method according to Claim 2 wherein said .beta.-hydroxyalkylamide is selected from the group consisting of bis[N,N-di(beta-hydroxyethyl)] adipamide, bis[N,N-di(beta-hydroxypropyl)]
succinamide, N-2-hydroxyethylurea, bis[N,N-di(beta-hydroxyethyl)] azelamide, bis[N-N-di(beta-hydroxypropyl)] adipamide, and bis[N-methyl-N-(beta-hydroxyethyl)] oxamide.

7. The method according to Claim 1 wherein the hydroxy compound is present in an amount sufficient to provide from about 0.00001 to about 10 weight percent of hydroxy compound in the material based on the oven-dry weight of the material.

8. A method for increasing the feel, and moisture absorption and retention of a material comprising:
b) applying to said material a treatment composition in an amount effective to impart temporary crease and stain resistance, said fabric treatment composition comprising a hydroxy compound; and c) allowing said treatment composition to dry at ambient temperature, wherein said hydroxy urea compound comprises either:
1) a hydroxy urea comprising one urea and at least one hydroxyl moiety; or 2) a hydroxy amide comprising at least one amide and at least one hydroxyl moiety.