CA2332147C - Intumescent composition - Google Patents
Intumescent composition Download PDFInfo
- Publication number
- CA2332147C CA2332147C CA2332147A CA2332147A CA2332147C CA 2332147 C CA2332147 C CA 2332147C CA 2332147 A CA2332147 A CA 2332147A CA 2332147 A CA2332147 A CA 2332147A CA 2332147 C CA2332147 C CA 2332147C
- Authority
- CA
- Canada
- Prior art keywords
- composition
- intumescent
- product
- smoke
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The composition contains exfoliating graphite and a carrier which is preferably polyvinyl chloride, polyethylene or polypropylene.
The composition can be produced by co-extrusion of a suitable mixture with a further plastics material to form composite products in continuous lengths. The products include papers, tubes, fuel, pipes, doorstrips, electrical conduit and electrical cables.
The composition can be produced by co-extrusion of a suitable mixture with a further plastics material to form composite products in continuous lengths. The products include papers, tubes, fuel, pipes, doorstrips, electrical conduit and electrical cables.
Description
INTUMESCENT COMPOSITION
This invention relates to intumescent materials which find application as fire-stop materials, for example fire penetration seals and cavity fire-stops, and otherwise.
Known intumescent fire-stop or penetration-sealing products include: sealants and mastics which comprise exfoliating graphite in a suitable carrier material;
intumescent pipe bands, collars and wraps; intumescent blocks, grills and strips; intumescent fire pillows; intumescent expansion joints; intumescent cavity and lap-jointing seals;
intumescent paints; lightweight cavity barriers; and doorstrips which comprise intumescent material. All the intumescent products mentioned may contain exfoliating graphite.
These products are incorporated into buildings at various stages and places in their construction and all have the property of intumescing when subjected to the heat of a fire and thereby closing a passageway through which the fire, flame and/or smoke would otherwise spread. The products thereby protect the elements of the building from structural collapse.
The products are however subject to disadvantages in that their incorporation into or onto the structure of a building is a time-consuming operation or, in certain cases, the products themselves (e.g. cavity seals, lap joints, lightweight cavity barriers and doorstrips) are difficult to manufacture as they consist of assemblies of two or more component parts.
According to the present invention a material comprising one or more of polyvinyl chloride, polyethylene, polypropylene, polyethylene-polypropylene copolymers, acrylic polymers and copolymers, metallocene polymers, silicone rubbers and polymers and natural and synthetic polymer and rubber latexes (preferably comprising one or more of the foregoing) is used as a carrier for exfoliating graphite in an intumescent composition.
The invention also provides an intumescent composition which comprises the said carrier material and exfoliating graphite.
Intumescent compositions according to the invention can be produced by extrusion of a mixture of the said carrier material and exfoliating graphite, the extrusion process preferably being a melt-extrusion process. The invention accordingly provides an extrudable mixture comprising the said carrier material and exfoliating graphite and a composition produced by extrusion, preferably melt-extrusion, of a mixture of the said carrier material and exfoliating graphite.
Preferably when the carrier material comprises one or more acrylic polymer or copolymer and/or one or more silicone rubber or polymer, the intumescent composition according to the invention can be produced by mixing of the carrier material (preferably in the form of a latex) with the exfoliating graphite. The invention accordingly provides such a mixture.
The amount of carrier material in the composition or extrudable mixture is preferably from 30 to 4501 by weight of the composition or mixture.
In all aspects of the invention, the amount of exfoliating graphite is preferably from 5 to 50 % by weight, more preferably 15 to 4501 by weight, most preferably 25 to 35%
by weight of the composition or mixture.
Compositions and extrudable mixtures of the invention preferably contain one or more plasticisers, at least one of which preferably has a fire-retardant effect.
The or at least one of the plasticisers is preferably a phthalate plasticiser.
The plasticiser(s) are suitably present in an amount of up to 35% by weight of the composition or mixture, preferably from 10 to 30% by weight, more preferably 20 to 30% by weight.
The compositions and extrudable mixtures of the invention preferably also contain one or more stabilisers, preferably of low toxicity, suitably in a total amount of up 0. 05% by weight of the composition or mixture, preferably 0.015 to 0.025% by weight.
Compositions and extrudable mixtures of the invention may contain an inert filler, preferably in an amount of 4 to 6%
by weight of the composition or mixture.
Suitable exfoliating graphite materials are those sold under the names "Callotek 50", "Callotek 100", "Callotek 200", "Callotek 500" and "Callotek 600" and available from P.F.C.
Surechem Limited of Davis Road, Chessington, Surrey, KT9 1TV, United Kingdom.
In another aspect, the present invention provides a composite product comprising a co-extrusion of first and second materials, the first material being an intumescent composition comprising exfoliating graphite in a carrier material.
Preferably, the carrier material is polyvinyl chloride, polyethylene, polypropylene or a polyethylene-polypropylene copolymer, the first material preferably containing from 5 to 50% by weight of exfoliating graphite, more preferably 15 to 45% by weight, most preferably 25 to 35% by weight, based on the weight of the first material.
The amount of carrier material in the first material is preferably from 30 to 45% by weight of the first material.
The first material may contain one or more plasticisers and/or one cr more stabilisers and/or an inert filler, of the types and in amounts based on the first material as stated above for the first-mentioned composition of the invention.
The second material preferably comprises one or more of polyvinyl chloride, polyethylene, polypropylene and a polyethylene-polypropylene copolymer.
Advantageously, the second material and the carrier material are chosen for compatibility with each other, particularly upon co-extrusion, and are preferably the same material, more preferably polyvinyl chloride.
The composite product of the invention may take the form of a tube of multi-layer wall construction, the outer or inner layer of the tube wall being preferably of the first material.
Another preferred product is a tube having a wall construction which comprises a layer of the second material between first and second layers of the first material.
Examples of tubes constituting composite products according to the invention are pipes for gases or liquids and electrical and cable conduits. Another example is a hose in which the second material is neoprene rubber and the carrier material is polyvinyl chloride, polyethylene, polypropylene or a polyethylene-polypropylene copolymer.
A further product according to this aspect of the invention comprises a tube of the second material which is filled completely with the first material.
Another product according to this aspect of the invention comprises a doorstrip or a door or window frame profile, in which the first material forms an intumescent element within the second element. It need not however be that the first material is fully enclosed in the extrusion of the second material: for example, U- and C-shaped and flat extrusions of the second material are also within the scope of the invention. Articles of these types all provide fire-stop 5 and/or flame- or smoke-retardant functions when used in building construction.
In all cases, the second material may be flexible or rigid according to its intended use, and may have its other physical properties also chosen to suit it to the intended use.
In all cases in which the tube wall construction comprises a layer (which may be an inner, outer or intermediate layer) of the first material, the tube, when passed through an opening, for example in a wall or floor, in a building construction, acts as a smoke-stop, flame-stop and/or fire-stop component without any additional wrapping or collar being fitted around it to form a fire-stop.
When the tube is subjected to heat, the intumescent material intumesces and acts to block the bore of the tube.
This is particularly advantageous for tubes used to convey flammable materials, for example gas pipes and fuel lines.
It is desirable for the layer containing intumescent material to form the inner layer of the pipe or tube.
In yet another aspect, the present invention provides an electrical cable of which the insulation comprises an intumescent material comprising exfoliating graphite in a carrier material. Examples of suitable cables are electrical cables generally, telecommunication cables, data transmission cables and coaxial cables.
The intumescent material preferably forms at least one tubular layer extending around at least one conductor of the cable. The conductor may be a single strand or consist of a plurality of strands. Thus, cable structures in which the intumescent material forms a tubular layer around each individual conductor, or at least those having their own insulating layers, and structures in which the intumescent material forms a tubular layer around all the conductors and within the sheathing layer of the, cable, are within the scope of the invention. Further, the invention also provides a cable in which a layer of intumescent material forms an outer tubular layer enclosing the sheathing layer of the cable.
The carrier material preferably comprises one or more of polyvinyl chloride, polyethylene, polypropylene, a polyethylene-polypropylene copolymer, an acrylic polymer or copolymer and a metallocene polymer; the insulation and sheathing layers of the cable are also preferably of one of these materials.
The amounts of carrier material and exfoliating graphite are preferably as stated above, for the carrier material and exfoliating graphite of the first-mentioned composition according to the invention.
The in;.umescent material may contain one or more plasticisers and/or one or more stabilisers and/or an inert filler of the types and in the amounts based on the carrier material stated above for the first-mentioned composition according to the invention.
In each cable according to the invention, the intumescent material swells to enlarge the cable and perform a fire-stop, anti-smoke-spread and/or anti-flame-spread function when the cable is subjected to the heat of a fire. When the cable is installed in a conduit or otherwise passes through a confined space within a building, for example through a fire wall or floor, this intumescence provides a fire-stop, anti-smoke-spread and/or anti-flame-spread, effect.
The terms "polyvinyl chloride" and "PVC" are each used throughout this specification and its claims to cover plasticised and unplasticised polyvinyl chloride and also derivatives of both those materials. Similarly the terms "polyethylene", "polypropylene" and ="polyethylene-polypropylene copolymer" are used to cover both these materials themselves and also derivatives thereof.
The invention will be described further by way of the following examples 1 to 3.
Compositions according to the invention were produced by introducing the following ingredients into the feed hopper of an extruder filled with a suitable extrusion die:
ingredient amount (g) example 1 example 2 example 3 PVC granules 380 - -PVC powder - 100 100 PVC-compatible 0.2 - -stabiliser/lubricant dioctyl phthalate 150 52 -plasticiser acrylonitrile- - - 8 butadiene-styrene impact modifier acrylic process aid - - 1.5 epoxidised soya bean - 5 1.5 oil barium-zinc - 2 -stabiliser 15 ingredient amount (g) example 1 example 2 example 3 tin stabiliser - - 2.5 fatty acid ester - - 1.2 glycerine lubricant paraf f i.n wax - - 0.4 chlorinated paraffin 110 30 -(fire retardant plasticiser) Callotek 500 310 85 50 exfoliating graphite PVC-compatible inert 49.8 - 7 filler TOTAL 1000 274 172.1 Embodiments of the invention will now be described by way of example with reference to the drawing, in which:
Figure 1 is a transverse sectional view of an electrical conduit having a twi-n-walled construction;
Figure 2 is a transverse sectional view of an electrical conduit having a triple-walled construction;
Figure 3 is a transverse sectional view of a fuel pipe having a twin-walled construction;
Figure 4 is a transverse sectional view of a filled profile member according to the invention;
Figure 5 is a transverse sectional view of a first electrical cable;
Figure 6 is a transverse sectional view of a second electrical cable;
Figure 7 is a transverse sectional view of a third electrical cable; and Figure 8 is a transverse sectional view of a coupling which can act as a fire and smoke seal where electrical cables pass through a wall or similar part of a building.
Figure 1 of the drawings shows an electrical conduit having an outer layer 10 of rigid PVC material as in a conventional electrical conduit and an inner layer 12 of a composition made in accordance with any of examples 1 to 3.
The conduit is produced by co-extrusion through an extruder fitted with a suitable extrusion die of PVC granules to form the outer layer 10 and a blend of the ingredients listed in example 1 tc form the inner layer 12.
An electrical conduit as shown in figure 1 and having an inner layer of a composition in accordance with example 1 was tested for compliance with British Standard 476, Part 20 (see British Standards Institution document UDC 614.841.332: 620.1:
69.01: 6909.81) for fire penetration. The conduit had an outside diameter of 20 mm. The inner layer was 2 mm thick.
The test involved placing the conduit between opposed panels of mineral fibre slab each 50 mm thick and coated with a 1 mm ablative coating. Heat transfer through the sample from a furnace at 1200 C heating one of the panels was measured. The sample produced an integrity rating of 186 mins, with an insulation rating of 75 mins.
Figure 2 shows a conduit having an intermediate layer 20 of the same material as the outer layer 10 of the conduit of figure 1 and inner and outer layers 22,24 of a composition made in acccrdance with any of examples 1 to 3 herein. The conduit is produced by co-extrusion as above using a suitable extrusion die.
The fue_ pipe shown in Figure 3 comprises an outer layer 30 of latex rubber and an inner layer 32 of a composition made in accordance with any of examples 1 to 3 herein. The fuel pipe is made by co-extrusion of the rubber and the ingredients listed in the example using a suitable extrusion die.
5 Figure 4 of the drawings shows a filled, profiled element produced by co-extrusion of PVC and the ingredients of any of examples 1, 2 and 3 using a suitable extrusion die. The outer part 40 of the extrusion is of circular cross-section and is filled completely with the composition of the respective 10 example. In other embodiments, the outer part can be of any desired cross-section, for example that of a door, window or cladding component, or a door or window frame. Another example is a rectangular-section which forms a doorstrip for insertion into the frame of a fire door. In all cases, the filed profiled element intumesces to produce a fire-stop effect when subjected to the heat of a fire.
The electrical cable of Figure 5 comprises insulated line and neutral conductors 50,52 and an uninsulated earth conductor 54. The three conductors 50,52,54 are encased in a sheathing 56 of PVC which is itself covered by a layer 58 of a composition made in accordance with any of examples 1, 2 and 3. The cable is produced by co-extrusion of PVC and the ingredients listed in the respective example, through a suitable extrusion die through which the conductors 50,52,54 are also fed.
The cable of Figure 6 comprises conductors 60,62,64 which correspond to the conductors 50,52,54 of the cable of Figure 5. Each of the insulated conductors 60,62 has around it a respective layer 66,68 of a composition made in accordance with example 1, 2 or 3, around which a sheathing 70 of PVC is formed. The cable is produced by co-extrusion of PVC and the ingredients listed in the respective example, through a suitable extrusion die through which the conductors 60,62,64 are also fed.
Figure 7 shows a cable which comprises insulated line and neutral conductors 72, 76 and an uninsulated earth conductor 74. The three conductors 72, 74, 76 are encased in sheathing 71 made from a composition in accordance with any of examples 1, 2 and 3. The sheathing 71 is covered by an outer layer 80 of PVC. The cable is produced by co-extrusion of the composition according to the invention and PVC through a suitable extrusion die through which the conductors 72, 74 and 76 are also fed.
An electrical cable as shown in figure 7 having a sheathing 71 of a composition in accordance with example 2 was tested.for compliance with British Standard 476, Part 20 (see British Standards 476, Part 20 (see British Standards Institution document UDC 614.841.332: 620.1: 69.01: 6909.81) for fire penetration as described above. The sample produced an integrity rating of 210 min, with an insulation rating of 45 min.
An electrical cable as shown in figure 7 having a sheathing of a composition in accordance with example 1 was tested for compliance with International Electrical Committee tests 61034, 60754-1 and 60754-2.
Test 61034, relating to measurement of smoke density of electrical cables burning under defined conditions, produced a test rating of 62%, compared with a minimum test requirement of 500.
Test 60754-1, relating to the amount of halogen gases evolved during combustion of cable materials, produced a test rating of 16, compared with a maximum test requirement of 100.
This invention relates to intumescent materials which find application as fire-stop materials, for example fire penetration seals and cavity fire-stops, and otherwise.
Known intumescent fire-stop or penetration-sealing products include: sealants and mastics which comprise exfoliating graphite in a suitable carrier material;
intumescent pipe bands, collars and wraps; intumescent blocks, grills and strips; intumescent fire pillows; intumescent expansion joints; intumescent cavity and lap-jointing seals;
intumescent paints; lightweight cavity barriers; and doorstrips which comprise intumescent material. All the intumescent products mentioned may contain exfoliating graphite.
These products are incorporated into buildings at various stages and places in their construction and all have the property of intumescing when subjected to the heat of a fire and thereby closing a passageway through which the fire, flame and/or smoke would otherwise spread. The products thereby protect the elements of the building from structural collapse.
The products are however subject to disadvantages in that their incorporation into or onto the structure of a building is a time-consuming operation or, in certain cases, the products themselves (e.g. cavity seals, lap joints, lightweight cavity barriers and doorstrips) are difficult to manufacture as they consist of assemblies of two or more component parts.
According to the present invention a material comprising one or more of polyvinyl chloride, polyethylene, polypropylene, polyethylene-polypropylene copolymers, acrylic polymers and copolymers, metallocene polymers, silicone rubbers and polymers and natural and synthetic polymer and rubber latexes (preferably comprising one or more of the foregoing) is used as a carrier for exfoliating graphite in an intumescent composition.
The invention also provides an intumescent composition which comprises the said carrier material and exfoliating graphite.
Intumescent compositions according to the invention can be produced by extrusion of a mixture of the said carrier material and exfoliating graphite, the extrusion process preferably being a melt-extrusion process. The invention accordingly provides an extrudable mixture comprising the said carrier material and exfoliating graphite and a composition produced by extrusion, preferably melt-extrusion, of a mixture of the said carrier material and exfoliating graphite.
Preferably when the carrier material comprises one or more acrylic polymer or copolymer and/or one or more silicone rubber or polymer, the intumescent composition according to the invention can be produced by mixing of the carrier material (preferably in the form of a latex) with the exfoliating graphite. The invention accordingly provides such a mixture.
The amount of carrier material in the composition or extrudable mixture is preferably from 30 to 4501 by weight of the composition or mixture.
In all aspects of the invention, the amount of exfoliating graphite is preferably from 5 to 50 % by weight, more preferably 15 to 4501 by weight, most preferably 25 to 35%
by weight of the composition or mixture.
Compositions and extrudable mixtures of the invention preferably contain one or more plasticisers, at least one of which preferably has a fire-retardant effect.
The or at least one of the plasticisers is preferably a phthalate plasticiser.
The plasticiser(s) are suitably present in an amount of up to 35% by weight of the composition or mixture, preferably from 10 to 30% by weight, more preferably 20 to 30% by weight.
The compositions and extrudable mixtures of the invention preferably also contain one or more stabilisers, preferably of low toxicity, suitably in a total amount of up 0. 05% by weight of the composition or mixture, preferably 0.015 to 0.025% by weight.
Compositions and extrudable mixtures of the invention may contain an inert filler, preferably in an amount of 4 to 6%
by weight of the composition or mixture.
Suitable exfoliating graphite materials are those sold under the names "Callotek 50", "Callotek 100", "Callotek 200", "Callotek 500" and "Callotek 600" and available from P.F.C.
Surechem Limited of Davis Road, Chessington, Surrey, KT9 1TV, United Kingdom.
In another aspect, the present invention provides a composite product comprising a co-extrusion of first and second materials, the first material being an intumescent composition comprising exfoliating graphite in a carrier material.
Preferably, the carrier material is polyvinyl chloride, polyethylene, polypropylene or a polyethylene-polypropylene copolymer, the first material preferably containing from 5 to 50% by weight of exfoliating graphite, more preferably 15 to 45% by weight, most preferably 25 to 35% by weight, based on the weight of the first material.
The amount of carrier material in the first material is preferably from 30 to 45% by weight of the first material.
The first material may contain one or more plasticisers and/or one cr more stabilisers and/or an inert filler, of the types and in amounts based on the first material as stated above for the first-mentioned composition of the invention.
The second material preferably comprises one or more of polyvinyl chloride, polyethylene, polypropylene and a polyethylene-polypropylene copolymer.
Advantageously, the second material and the carrier material are chosen for compatibility with each other, particularly upon co-extrusion, and are preferably the same material, more preferably polyvinyl chloride.
The composite product of the invention may take the form of a tube of multi-layer wall construction, the outer or inner layer of the tube wall being preferably of the first material.
Another preferred product is a tube having a wall construction which comprises a layer of the second material between first and second layers of the first material.
Examples of tubes constituting composite products according to the invention are pipes for gases or liquids and electrical and cable conduits. Another example is a hose in which the second material is neoprene rubber and the carrier material is polyvinyl chloride, polyethylene, polypropylene or a polyethylene-polypropylene copolymer.
A further product according to this aspect of the invention comprises a tube of the second material which is filled completely with the first material.
Another product according to this aspect of the invention comprises a doorstrip or a door or window frame profile, in which the first material forms an intumescent element within the second element. It need not however be that the first material is fully enclosed in the extrusion of the second material: for example, U- and C-shaped and flat extrusions of the second material are also within the scope of the invention. Articles of these types all provide fire-stop 5 and/or flame- or smoke-retardant functions when used in building construction.
In all cases, the second material may be flexible or rigid according to its intended use, and may have its other physical properties also chosen to suit it to the intended use.
In all cases in which the tube wall construction comprises a layer (which may be an inner, outer or intermediate layer) of the first material, the tube, when passed through an opening, for example in a wall or floor, in a building construction, acts as a smoke-stop, flame-stop and/or fire-stop component without any additional wrapping or collar being fitted around it to form a fire-stop.
When the tube is subjected to heat, the intumescent material intumesces and acts to block the bore of the tube.
This is particularly advantageous for tubes used to convey flammable materials, for example gas pipes and fuel lines.
It is desirable for the layer containing intumescent material to form the inner layer of the pipe or tube.
In yet another aspect, the present invention provides an electrical cable of which the insulation comprises an intumescent material comprising exfoliating graphite in a carrier material. Examples of suitable cables are electrical cables generally, telecommunication cables, data transmission cables and coaxial cables.
The intumescent material preferably forms at least one tubular layer extending around at least one conductor of the cable. The conductor may be a single strand or consist of a plurality of strands. Thus, cable structures in which the intumescent material forms a tubular layer around each individual conductor, or at least those having their own insulating layers, and structures in which the intumescent material forms a tubular layer around all the conductors and within the sheathing layer of the, cable, are within the scope of the invention. Further, the invention also provides a cable in which a layer of intumescent material forms an outer tubular layer enclosing the sheathing layer of the cable.
The carrier material preferably comprises one or more of polyvinyl chloride, polyethylene, polypropylene, a polyethylene-polypropylene copolymer, an acrylic polymer or copolymer and a metallocene polymer; the insulation and sheathing layers of the cable are also preferably of one of these materials.
The amounts of carrier material and exfoliating graphite are preferably as stated above, for the carrier material and exfoliating graphite of the first-mentioned composition according to the invention.
The in;.umescent material may contain one or more plasticisers and/or one or more stabilisers and/or an inert filler of the types and in the amounts based on the carrier material stated above for the first-mentioned composition according to the invention.
In each cable according to the invention, the intumescent material swells to enlarge the cable and perform a fire-stop, anti-smoke-spread and/or anti-flame-spread function when the cable is subjected to the heat of a fire. When the cable is installed in a conduit or otherwise passes through a confined space within a building, for example through a fire wall or floor, this intumescence provides a fire-stop, anti-smoke-spread and/or anti-flame-spread, effect.
The terms "polyvinyl chloride" and "PVC" are each used throughout this specification and its claims to cover plasticised and unplasticised polyvinyl chloride and also derivatives of both those materials. Similarly the terms "polyethylene", "polypropylene" and ="polyethylene-polypropylene copolymer" are used to cover both these materials themselves and also derivatives thereof.
The invention will be described further by way of the following examples 1 to 3.
Compositions according to the invention were produced by introducing the following ingredients into the feed hopper of an extruder filled with a suitable extrusion die:
ingredient amount (g) example 1 example 2 example 3 PVC granules 380 - -PVC powder - 100 100 PVC-compatible 0.2 - -stabiliser/lubricant dioctyl phthalate 150 52 -plasticiser acrylonitrile- - - 8 butadiene-styrene impact modifier acrylic process aid - - 1.5 epoxidised soya bean - 5 1.5 oil barium-zinc - 2 -stabiliser 15 ingredient amount (g) example 1 example 2 example 3 tin stabiliser - - 2.5 fatty acid ester - - 1.2 glycerine lubricant paraf f i.n wax - - 0.4 chlorinated paraffin 110 30 -(fire retardant plasticiser) Callotek 500 310 85 50 exfoliating graphite PVC-compatible inert 49.8 - 7 filler TOTAL 1000 274 172.1 Embodiments of the invention will now be described by way of example with reference to the drawing, in which:
Figure 1 is a transverse sectional view of an electrical conduit having a twi-n-walled construction;
Figure 2 is a transverse sectional view of an electrical conduit having a triple-walled construction;
Figure 3 is a transverse sectional view of a fuel pipe having a twin-walled construction;
Figure 4 is a transverse sectional view of a filled profile member according to the invention;
Figure 5 is a transverse sectional view of a first electrical cable;
Figure 6 is a transverse sectional view of a second electrical cable;
Figure 7 is a transverse sectional view of a third electrical cable; and Figure 8 is a transverse sectional view of a coupling which can act as a fire and smoke seal where electrical cables pass through a wall or similar part of a building.
Figure 1 of the drawings shows an electrical conduit having an outer layer 10 of rigid PVC material as in a conventional electrical conduit and an inner layer 12 of a composition made in accordance with any of examples 1 to 3.
The conduit is produced by co-extrusion through an extruder fitted with a suitable extrusion die of PVC granules to form the outer layer 10 and a blend of the ingredients listed in example 1 tc form the inner layer 12.
An electrical conduit as shown in figure 1 and having an inner layer of a composition in accordance with example 1 was tested for compliance with British Standard 476, Part 20 (see British Standards Institution document UDC 614.841.332: 620.1:
69.01: 6909.81) for fire penetration. The conduit had an outside diameter of 20 mm. The inner layer was 2 mm thick.
The test involved placing the conduit between opposed panels of mineral fibre slab each 50 mm thick and coated with a 1 mm ablative coating. Heat transfer through the sample from a furnace at 1200 C heating one of the panels was measured. The sample produced an integrity rating of 186 mins, with an insulation rating of 75 mins.
Figure 2 shows a conduit having an intermediate layer 20 of the same material as the outer layer 10 of the conduit of figure 1 and inner and outer layers 22,24 of a composition made in acccrdance with any of examples 1 to 3 herein. The conduit is produced by co-extrusion as above using a suitable extrusion die.
The fue_ pipe shown in Figure 3 comprises an outer layer 30 of latex rubber and an inner layer 32 of a composition made in accordance with any of examples 1 to 3 herein. The fuel pipe is made by co-extrusion of the rubber and the ingredients listed in the example using a suitable extrusion die.
5 Figure 4 of the drawings shows a filled, profiled element produced by co-extrusion of PVC and the ingredients of any of examples 1, 2 and 3 using a suitable extrusion die. The outer part 40 of the extrusion is of circular cross-section and is filled completely with the composition of the respective 10 example. In other embodiments, the outer part can be of any desired cross-section, for example that of a door, window or cladding component, or a door or window frame. Another example is a rectangular-section which forms a doorstrip for insertion into the frame of a fire door. In all cases, the filed profiled element intumesces to produce a fire-stop effect when subjected to the heat of a fire.
The electrical cable of Figure 5 comprises insulated line and neutral conductors 50,52 and an uninsulated earth conductor 54. The three conductors 50,52,54 are encased in a sheathing 56 of PVC which is itself covered by a layer 58 of a composition made in accordance with any of examples 1, 2 and 3. The cable is produced by co-extrusion of PVC and the ingredients listed in the respective example, through a suitable extrusion die through which the conductors 50,52,54 are also fed.
The cable of Figure 6 comprises conductors 60,62,64 which correspond to the conductors 50,52,54 of the cable of Figure 5. Each of the insulated conductors 60,62 has around it a respective layer 66,68 of a composition made in accordance with example 1, 2 or 3, around which a sheathing 70 of PVC is formed. The cable is produced by co-extrusion of PVC and the ingredients listed in the respective example, through a suitable extrusion die through which the conductors 60,62,64 are also fed.
Figure 7 shows a cable which comprises insulated line and neutral conductors 72, 76 and an uninsulated earth conductor 74. The three conductors 72, 74, 76 are encased in sheathing 71 made from a composition in accordance with any of examples 1, 2 and 3. The sheathing 71 is covered by an outer layer 80 of PVC. The cable is produced by co-extrusion of the composition according to the invention and PVC through a suitable extrusion die through which the conductors 72, 74 and 76 are also fed.
An electrical cable as shown in figure 7 having a sheathing 71 of a composition in accordance with example 2 was tested.for compliance with British Standard 476, Part 20 (see British Standards 476, Part 20 (see British Standards Institution document UDC 614.841.332: 620.1: 69.01: 6909.81) for fire penetration as described above. The sample produced an integrity rating of 210 min, with an insulation rating of 45 min.
An electrical cable as shown in figure 7 having a sheathing of a composition in accordance with example 1 was tested for compliance with International Electrical Committee tests 61034, 60754-1 and 60754-2.
Test 61034, relating to measurement of smoke density of electrical cables burning under defined conditions, produced a test rating of 62%, compared with a minimum test requirement of 500.
Test 60754-1, relating to the amount of halogen gases evolved during combustion of cable materials, produced a test rating of 16, compared with a maximum test requirement of 100.
Test 60754-2, relating to the acidity of gases evolved and the conductivity of the cable during combustion of the cable, produced a test rating OF 4.6%, compared with a minimum test requirement of 4.3%.
The coupling 82 shown in Figure 8 is made from a composition in accordance with any of examples 1, 2 and 3.
The coupling is extruded in sections of suitable length to allow coupling of conduits or pipes which are not rated for fire resistance where they pass through fire-rated walls or floors. A fire, flame and/or smoke seal is therefore produced and is effective when subjected to the heat of a fire.
The coupling 82 shown in Figure 8 is made from a composition in accordance with any of examples 1, 2 and 3.
The coupling is extruded in sections of suitable length to allow coupling of conduits or pipes which are not rated for fire resistance where they pass through fire-rated walls or floors. A fire, flame and/or smoke seal is therefore produced and is effective when subjected to the heat of a fire.
Claims (20)
1. An intumescent composition comprising a mixture of exfoliating graphite, a carrier material selected from polyvinyl chloride, polyethylene, polypropylene, polyethylene-polypropylene copolymers, acrylic polymers and copolymers, metallocene polymers, silicone rubbers and polymers and natural and synthetic polymer and rubber latexes and mixtures of any of the forgoing, and at least one plasticizer, the total amount of said plasticizer(s) comprising from 20 to 30 percent by weight of the composition.
2. A composition as claimed in claim 1 in which said exfoliating graphite comprises 25 to 35 percent by weight of said composition and said carrier comprises 30 to 45 percent by weight of said composition, and wherein said composition comprises 100% of said composition's parts.
3. A composition as claimed in claim 1 or 2 containing at least one stabilizer, the total amount of stabilizer(s) being no more than 0.05 percent by weight of the composition.
4. A composition as claimed in any one of claims 1, 2 or 3 containing at least one filler, the total amount of filler(s) being 4 to 6 percent by weight of the composition.
5. A intumescent product formed from an intumescent composition according to any one of claims 1 to 4.
6. An intumescent product as claimed in claim 5 in the form of a conduit through which fluids can flow.
7. An intumescent product as claimed in claim 5 in the form of a coupling through which fluids can flow.
8. A composite product comprising an inner layer of intumescent material formed from an intumescent composition according to any one of claims 1 to 4, covered by an outer layer of rigid material.
9. A composite product comprising a co-extrusion of a first and second material, the first material being an intumescent composition according to any one of the claims 1 to 4, and the second material comprises one or more of polyvinyl chloride polyethylene, polypropylene, polyethylene polypropylene copolymers and mixtures thereof.
10. A composite product as claimed in claim 9 in which said product comprises a conduit through which fluids can flow.
11. A composite product as claimed in claim 10 in which said conduit has an inner surface of said first material and an outer surface of said second material.
12. A composite product as claimed in claim 10 in which said conduit has an inner surface of said second material and an outer surface of said first material.
13. A composite product as claimed in claim 9 or 10 in which said product as alternating layers of said first and second materials.
14. A smoke, flame or fire stop component for providing a passageway through an opening in a wall or floor of a building through which material can be fed, said component being hollow and adapted for insertion through the opening in the wall or floor of a building to define said passageway, said component having a tubular wall formed of an intumescent composition as claimed in any one of claims 1 to 9.
15. A component as claimed in claim 14 in which said intumescent composite material comprises exfoliated graphite, a carrier material, and a plasticizer.
16. A smoke, flame or fire stop component as claimed in claim 14 or 15 in which the periphery of said component is enveloped with an outer plastic layer.
17. A smoke, flame or fire stop component as claimed in claim 16 in which said outer plastic layer is a rigid plastic.
18. A smoke, flame or fire stop component as claimed in claim 16 in which said outer plastic layer is a flexible plastic.
19. A smoke, flame or fire stop component as claimed in any one of claims 14, 15, 16, 17 or 18 comprising a pipe for delivering fluids through said opening in a wall or floor of a building.
20. A smoke, flame or fire stop component as claimed in claim 14 or 15 comprising a coupling for delivering fluids through said opening in a wall or floor of a building.