CA2309593A1 - Polyurethane binding agents having a low content of highly volatile monomers - Google Patents
Polyurethane binding agents having a low content of highly volatile monomers Download PDFInfo
- Publication number
- CA2309593A1 CA2309593A1 CA002309593A CA2309593A CA2309593A1 CA 2309593 A1 CA2309593 A1 CA 2309593A1 CA 002309593 A CA002309593 A CA 002309593A CA 2309593 A CA2309593 A CA 2309593A CA 2309593 A1 CA2309593 A1 CA 2309593A1
- Authority
- CA
- Canada
- Prior art keywords
- isocyanate
- component
- groups
- stage
- polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The invention relates to low viscosity, weak migrating polyurethane binding agents lacking highly volatile monomers which carry isocyanate groups. The invention also relates to a method for producing such polyurethane binding agents and their application for coating, especially for gluing, objects.
Description
Polyurethane Binding Agents Having a Low Content of Highly Volatile Monomers This invention relates to a polyurethane binder and to processes for producing a low-viscosity polyurethane binder containing isocyanate groups which, despite its low viscosity, only has a low content of readily volatile residual monomers and essentially forms no "migrates". The invention also relates to the use of a low-viscosity polyurethane binder containing isocyanate groups (NCO groups) in the production of adhesives, more particularly one-component and two-component adhesives, for example for bonding web-form materials of paper, plastic or aluminium or mixtures of two or more thereof, coatings, more particularly lacquers, emulsion paints and casting resins as well as moldings.
Isocyanate-terminated polyurethane prepolymers have been known for some time. They may readily be chain-extended or crosslinked with suitable hardeners, usually polyhydric alcohols, to form high molecular weight materials. Polyurethane prepolymers have acquired significance in many fields of application, including for example the production of adhesives, coatings, casting resins and moldings.
In order to obtain isocyanate-terminated polyurethane prepotymers, it is standard practice to react polyhydric alcohols with an excess of polyisocyanates, generally at least predominantly diisocyanates. Molecular weight can be controlled at least approximately through the ratio of OH
groups to isocyanate groups. Whereas a ratio of OH groups to isocyanate groups of, or approaching, 1:1 leads to generally high molecular weights, a statistical average of one diisocyanate molecule - where diisocyanates are used - is attached to each OH group where the OH : isocyanate group ratio is about 2:1, so that ideally no oligomerization or chain extension occurs in the course of the reaction.
In practice, however, chain-extending reactions are impossible to suppress with the result that, on completion of the reaction, a certain quantity of the component used in excess is left over irrespective of the reaction time. If diisocyanate, for example, is used as the excess component, a generally considerable proportion of this component remains behind in the reaction mixture for the reasons explained above.
The presence of such components is particularly problematical when they consist of readily volatile diisocyanates. The vapors of these diisocya-nates are often harmful to the skin and the application of products with a high content of such readily volatile diisocyanates requires elaborate measures on the part of the user to protect the people involved in processing the product, more particularly elaborate measures for keeping the surrounding air clean to breathe.
Since protective measures and cleaning measures generally involve considerable expense, there is a need on the part of the user for products which have a low percentage content of readily volatile diisocyanates depending on the isocyanate used.
In the context of the present invention, "readily volatile" substances are understood to be substances which have a vapor pressure at around 30°C of more than about 0.0007 mmHg or a boiling point of less than about 190°C (70 mPa).
If low-volatility diisocyanates, more particularly the widely used bicyclic diisocyanates, for example diphenyl methane diisocyanates, are used instead of the readily volatile diisocyanates, polyurethane binders with a viscosity normally outside the range suitable for simple processing methods are generally obtained. In cases such as these, the viscosity of the polyurethane prepolymers can be reduced by adding suitable solvents although this is not consistent with the absence of solvents normally demanded. Another way of reducing viscosity without solvents is to add an excess of monomeric polyisocyanates which are incorporated in the coating or bond (reactive diluent) in the course of a subsequent curinglhardening process (after the addition of a hardener or by curing under the influence of moisture).
Whereas the viscosity of the polyurethane prepolymers can actually be reduced in this way, the generally incomplete reaction of the reactive diluent often leads to the presence in the bond or coating of free monomeric polyisocyanates which are capable of "migrating", for example within the coating or bond or, in some cases, even into the coated or bonded materials themselves. Corresponding constituents of a coating or bond are often referred to among experts as "migrates". By contact with moisture, the isocyanate groups of the migrates are continuously reacted to form amino groups. The aromatic amines normally formed in this way are suspected of having a carcinogenic effect.
Migrates are often not tolerable, above all in the packaging field, because any migration of the migrates through the packaging material would result in contamination of the packaged product and the consumer would inevitably come into contact with the migrates when using the product.
Accordingly, the migrates in question are undesirable above all in the packaging field, especially in the packaging of foods.
In order to avoid the disadvantages described above, EP-A 0 118 065 proposes producing polyurethane prepolymers by a two-stage process.
In the first stage of this process, a monocyclic diisocyanate is reacted with a polyhydric alcohol in an OH group : isocyanate group ratio of <1 and, in the second step, a bicyclic diisocyanate is reacted with polyhydric alcohols in an OH group : isocyanate group ratio of <1 in the presence of the prepolymer prepared in the first step. A ratio of OH groups to isocyanate groups of 0.65 to 0.8:1 and preferably 0.7 to 0.75:1 is proposed for the second stage. The prepolymers obtainable in this way still have viscosities of 2500 mPas, 7150 mPas and 9260 mPas at high temperatures (75°C and 90°C).
DE-A 34 01 129 relates to a process for the production of mixed polyurethane prepolymers in which polyhydric alcohols are first reacted with the faster reacting isocyanate group of an asymmetrical diisocyanate, the more slowly reacting group being left intact, after which the reaction products are combined with a symmetrical diisocyanate of which the equally reactive isocyanate groups react more quickly than the slowly reacting groups of the first polyfunctional isocyanate compound mentioned.
The described polyurethane prepolymers have high viscosities and hence high processing temperatures so that they can only be used under conditions which allow high processing temperatures.
EP-A 0 019 120 relates to a two-stage process for the production of elastic weather-resistant sheet-form materials. In the first stage of this process, toluene diisocyanate (TDI) is reacted with at least equimolar quantities of a polyol and the reaction product obtained is subsequently reacted with diphenyl methane diisocyanate (MDI) and a polyol. The poly-urethane binders obtainable in this way are said to be capable of curing with water or with atmospheric moisture. Although the described process does give products with a relatively low viscosity, the content of free readily volatile diisocyanate (in the present case TDI) is still high (0.7% by weight) and can only be reduced when time-consuming and energy-intensive methods, for example thin-layer distillation, are used to remove excess readily volatile diisocyanate.
In many cases, laminated films are used in applications involving elevated temperatures, for example in the preparation of foods. Unfortu-nately, laminated films produced with conventional adhesives often under-go delamination whenever they are exposed to the temperatures normally prevailing in the preparation of foods.
Accordingly, the problem addressed by the present invention was to provide a polyurethane binder which would have a low viscosity and a low residual content of less than about 1 % by weight of readily volatile diiso-cyanates. In the case of toluene diisocyanate (TDI), the residual content of readily volatile isocyanate should be less than about 0.1 % by weight.
Another problem addressed by the present invention was to provide a polyurethane binder which would enable processing to be carried out at low temperatures.
A further problem addressed by the present invention was to provide a polyurethane binder which would have a low percentage content of "migrates", i.e. a low percentage content of monomeric polyisocyanates.
Another problem addressed by the present invention was to provide a polyurethane binder with which it would be possible to produce laminated films which would have little or no tendency to delaminate, even at high temperatures.
Finally, another problem addressed by the present invention was to provide a process for the production of a polyurethane binder having the properties mentioned above.
The present invention relates to a polyurethane binder with a low content of readily volatile isocyanate-functional monomers at least containing components A and B, in which (a) a polyurethane polymer containing at least two isocyanate groups or a mixture of two or more polyurethane prepolymers containing at least two isocyanate groups is present as component A, the polyurethane prepolymer containing two isocyanate groups or the mixture of two or more polyurethane prepolymers containing isocyanate groups containing at least two differently attached types of isocyanate groups of which at least one type has a lower reactivity to isocyanate-reactive groups than the other type(s), and (b) an at least difunctional isocyanate, of which the molecular weight is lower than the molecular weight of the polyurethane prepolymers present in component A and of which the isocyanate groups have a higher reactivity to isocyanate-reactive compounds than the type of isocyanate groups of relatively low reactivity present in component A, is present as component B.
"Low viscosity" in the context of the present invention means a (Brookfield) viscosity at 50°C of less than 5000 mPas.
In the context of the present invention, the expression "polyurethane binder" is understood to be a mixture of molecules each containing at least two isocyanate groups, in which the content of molecules with a molecular weight of more than 500 is at least about 50% by weight and preferably at least about 60% by weight or about 70% by weight.
A polyurethane prepolymer containing at least two isocyanate groups or a mixture of two or more polyurethane prepolymers containing at least two isocyanate groups, which may preferably be obtained by reacting a polyol component with an at least difunctional isocyanate, is used as component A.
In the context of the present invention, a "polyurethane prepolymer"
is understood to be the compound which is obtained, for example, when a polyol component is reacted with an at least difunctional isocyanate.
Accordingly, the expression "polyurethane prepolymer" encompasses both compounds of relatively low molecular weight, as formed for example in the reaction of a polyol with an excess of polyisocyanate, and also oligomeric or polymeric compounds. The expression "polyurethane prepolymer" also encompasses the compounds formed, for example, in the reaction of a trihydric or tetrahydric polyol with a molar excess of diisocyanates, based on the polyol. In this case, one molecule of the resulting compound carries several isocyanate groups.
Molecular weights relating to polymeric compounds represent the number average molecular weight (Mn), unless otherwise indicated.
In general, the polyurethane prepolymers used for the purposes of the present invention have a molecular weight in the range from about 500 to about 15,000 or in the range from about 500 to about 10,000, for example of the order of 5000, but especially in the range from about 700 to about 2500.
The polyurethane prepolymer containing two isocyanate groups or the mixture of two or more polyurethane prepolymers containing isocyanate groups has at least two differently attached types of isocyanate groups, of which at least one type has a lower reactivity to isocyanate-reactive groups than the other type or the other types of isocyanate groups. Isocyanate groups with a relatively low reactivity to isocyanate-reactive groups (by comparison with at least one other isocyanate group present in the poly-urethane binder) are also referred to hereinafter as "less reactive isocyanate groups" while the corresponding isocyanate group with a higher reactivity to isocyanate-reactive compounds is also referred to as the "more reactive isocyanate group".
According to the present invention, therefore, a difunctional polyurethane prepolymer for example containing two differently attached isocyanate groups, one of the isocyanate groups having a higher reactivity to isocyanate-reactive groups than the other isocyanate group, may be used as component A. A polyurethane prepolymer such as this may be obtained, for example, from the reaction of a dihydric alcohol with compounds containing two different, for example difunctional, isocyanate groups, the reaction being carried out in such a way that, on average, each molecule of the dihydric alcohol reacts with one molecule of the compounds containing different isocyanate groups.
A trifunctional or higher polyurethane prepolymer may also be used as component A, in which case one molecule of the polyurethane prepolymer for example may contain a different number of less reactive and more reactive isocyanate groups.
Mixtures of two or more polyurethane prepolymers may also be used as component A in accordance with the invention. The mixtures mentioned may be polyurethane prepolymers in which individual molecules carry identically attached isocyanate groups, at least one more reactive and one less reactive isocyanate group having to be present in the mixture as a whole. Besides molecules containing one or more identically attached isocyanate groups, the mixture may contain other molecules which carry both one or more identically attached isocyanate groups and one or more differently attached isocyanate groups.
Besides component A, the polyurethane binder according to the invention contains an at least difunctional isocyanate of which the molecular weight is lower than the molecular weight of the polyurethane prepolymers present in component A and of which the isocyanate groups have a higher reactivity to isocyanate-reactive compounds than the less reactive type of isocyanate groups present in component A.
In general, component B has a molecular weight of up to about 1000, molecular weights of up to about 720 or lower, for example of the order of 550, 500, 450, 400 or lower, being preferred. Component B may consist, for example, of low molecular weight diisocyanates with a molecular weight of up to about 300 or of the reaction products of dihydric or higher alcohols with an at least equimolar quantity of such low molecular weight diisocyanates, based on the OH groups of the dihydric or higher alcohol. Also suitable as component B are, for example, the trimerization products of difunctional isocyanates, the isocyanurates.
The polyurethane binder according to the invention contains at least 5% by weight of component B, based on the polyurethane binder as a whole.
The polyurethane binder according to the invention preferably has a content of readily volatile isocyanate-functional monomers of less than 2%
by weight or less than 1 % by weight or preferably less than 0.5% by weight.
These limits apply in particular to readily volatile isocyanate compounds which have only a limited danger potential for people involved in their processing, for example isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), tetramethyl xylylene diisocyanate (TMXDI) or cyclo-hexane diisocyanate. In the case of certain readily volatile isocyanate compounds, especially those which represent a serious risk to people involved in their processing, their content in the polyurethane binder according to the invention is preferably less than 0.3% by weight and more preferably less than 0.1 % by weight. These particular isocyanate compounds include, above all, toluene diisocyanate (TDI). In another preferred embodiment of the invention, the polyurethane binder has a TDI
and HDI content of less than 0.05% by weight.
In one preferred embodiment of the invention, the polyurethane binder according to the invention may contain an at least trifunctional isocyanate as component H in addition to components A and B.
Suitable at least trifunctional isocyanates are, for example, the trimerization and oligomerization products of the above-mentioned poly-isocyanates which can be obtained by suitably reacting polyisocyanates, preferably diisocyanates, to form isocyanurate rings. If oligomerization products are used, those which have a degree of oligomerization of on average about 3 to about 5 are particularly suitable.
Isocyanates suitable for the production of trimers are the diisocya-nates mentioned above, the trimerization products of the isocyanates HDI, MDI or IPDI being particularly preferred.
Polymeric isocyanates obtained, for example, as residue in the distillation of diisocyanates are also suitable for use as component H. The polymeric MDI obtainable from the distillation residue in the distillation of MDI is particularly suitable.
In one preferred embodiment of the invention, Desmodur N 3300, Desmodur N 100, the IPDI-trimeric isocyanurate T 1890 (products of Bayer AG) or triphenyl methane triisocyanate, for example, is used as component H.
Component H is preferably used in a quantity of about 1 to about 30% by weight and more preferably in quantity of about 5 to about 25% by weight, for example in a quantity of about 12 to about 20% by weight.
In one preferred embodiment of the invention, component A is prepared by an at least two-stage reaction in which (c) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least a first polyol component, the NCO:OH ratio being smaller than 2 and free OH groups still being present in the polyurethane prepolymer, and (d) in a second stage, another at least difunctional isocyanate is reacted with the polyurethane prepolymer from the first stage, the isocyanate groups of the isocyanate added in the second stage having a higher reactivity to isocyanate-reactive compounds than at least the predominant percentage of the isocyanate groups present in the polyurethane prepolymer from the first stage.
In another preferred embodiment, the other at least difunctional isocyanate is added in a molar excess, based on free OH groups of component A, the non-OH-reactive part of the other at least difunctional isocyanate representing component B.
In another preferred embodiment, component A is prepared by an at least two-stage reaction in which (e) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least a first polyol component, the NCO:OH ratio being smaller than 2 and free OH groups still being present in the polyurethane prepolymer, and (f) in a second stage, another at least difunctional isocyanate and another polyol component are reacted with the polyurethane prepolymer from the first stage, the isocyanate groups of the isocyanate added in the second stage having a higher reactivity to isocyanate-reactive compounds than at least the predominant percentage of the isocyanate groups present in the polyurethane prepolymer from the first stage.
In another preferred embodiment, the other at least difunctional isocyanate is added in a molar excess, based on free OH groups of component A and the other polyol component, the non-OH-reactive part of the other at least difunctional isocyanate representing component B.
According to the invention, the OH:NCO ratio in the production of component A in the second stage is preferably about 0.001 to less than 1:1 and, more particularly, 0.005 to about 0.8:1.
In one preferred embodiment of the invention, the OH:NCO ratio in the second stage is about 0.2 to 0.6:1.
In another preferred embodiment of the invention, the OH:NCO ratio in the first stage is less than 1 and, more particularly, 0.5 to 0.7:1, the described ratios optionally being maintained for the second stage also.
In the context of the present invention, the expression "polyol component" encompasses a single polyol or a mixture of two or more polyols which may be used for the production of polyurethanes. A polyol is understood to be a polyhydric alcohol, i.e. a compound containing more than one OH group in the molecule.
Various polyols may be used as the polyol component for the production of component A. They include, for example, aliphatic alcohols containing 2 to 4 OH groups per molecule. The OH groups may be both primary and secondary. Suitable aliphatic alcohols include, for example, ethylene glycol, propylene glycol, butane-1,4-diol, pentane-1,5-diol, hexane-1,6-diol, heptane-1,7-diol, octane-1,8-diol and higher homologs or isomers thereof which the expert can obtain by extending the hydrocarbon chain by one CH2 group at a time or by introducing branches into the carbon chain. Also suitable are higher alcohols such as, for example, glycerol, trimethylol propane, pentaerythritol and oligomeric ethers of the substances mentioned either individually or in the form of mixtures of two or more of the ethers mentioned with one another.
Other suitable polyol components for the production of component A
are the reaction products of low molecular weight polyhydric alcohols with alkylene oxides, so-called polyethers. The alkylene oxides preferably contain 2 to 4 carbon atoms. Suitable reaction products of the type in question are, for example, the reaction products of ethylene glycol, propylene glycol, the isomeric butane diols or hexane diols with ethylene oxide, propylene oxide or butylene oxide or mixtures of two or more thereof. The reaction products of polyhydric alcohols, such as glycerol, trimethylol ethane or trimethylol propane, pentaerythritol or sugar alcohols or mixtures of two or more thereof, with the alkylene oxides mentioned to form polyether polyols are also suitable. Polyether polyols with a molecular weight of about 100 to about 10,000 and preferably in the range from about 200 to about 5000 are particularly suitable. According to the invention, polypropylene glycol with a molecular weight of about 300 to about 2500 is most particularly preferred. Other suitable polyol components for the production of component A are polyether polyols as obtained, for example, from the polymerization of tetrahydrofuran.
The polyethers are reacted in known manner by reacting the starting compound containing a reactive hydrogen atom with alkylene oxides, for example ethylene oxide, propylene oxide, butylene oxide, styrene oxide, tetrahydrofuran or epichlorohydrin or mixtures of two or more thereof.
Suitable starting compounds are, for example, water, ethylene glycol, 1,2- or 1,3-propylene glycol, 1,4- or 1,3-butylene glycol, hexane-1,6 diol, octane-1,8-diol, neopentyl glycol, 1,4-hydroxymethyl cyclohexane, 2 methyl propane-1,3-diol, glycerol, trimethylol propane, hexane-1,2,6-triol, butane-1,2,4-triol, trimethylol ethane, pentaerythritol, mannitol, sorbitol, methyl glycosides, sugars, phenol, isononylphenol, resorcinol, hydroqui-none, 1,2,2- or 1,1,2-tris-(hydroxyphenyl)-ethane, ammonia, methyl amine, ethylenediamine, tetra- or hexamethylenediamine, triethanolamine, aniline, phenylenediamine, 2,4- and 2,6-diaminotoluene and polyphenylpolymethy-lene polyamines, which may be obtained by anilinelformaldehyde condensation, or mixtures of two or more thereof.
Polyethers modified by vinyl polymers are also suitable for use as a polyol component. Products such as these can be obtained, for example, by polymerizing styrene or acrylonitrile or mixtures thereof in the presence of polyethers.
Other suitable polyol components for the production of component A
are polyester polyols with a molecular weight of about 200 to about 10,000 For example, it is possible to use polyester polyols obtained by reacting low molecular weight alcohols, more particularly ethylene glycol, diethylene glycol, neopentyl glycol, hexanediol, butanediol, propylene glycol, glycerol or trimethylol propane, with caprolactone. Other suitable polyhydric alcohols for the production of polyester polyols are 1,4-hydroxymethyl cyclohexane, 2-methyl propane-1,3-diol, butane-1,2,4-triol, triethylene glycol, tetraethylene glycol, polyethylene glycol, dipropylene glycol, poly-propylene glycol, dibutylene glycol and polybutylene glycol.
Other suitable polyester polyols can be obtained by polycondensation. Thus, dihydric andlor trihydric alcohols may be condensed with less than the equivalent quantity of dicarboxylic acids and/or tricarboxylic acids or reactive derivatives thereof to form polyester polyols. Suitable dicarboxylic acids are, for example, succinic acid and higher homologs thereof containing up to 16 carbon atoms, unsaturated dicarboxylic acids, such as malefic acid or fumaric acid, and aromatic dicarboxylic acids, more particularly the isomeric phthalic acids, such as phthalic acid, isophthalic acid or terephthalic acid. Citric acid and trimellitic acid, for example, are also suitable tricarboxylic acids. Polyester polyols of at least one of the dicarboxylic acids mentioned and glycerol which have a residual content of OH groups are particularly suitable for the purposes of the present invention. Particularly suitable alcohols are hexanediol, ethylene glycol, diethylene glycol or neopentyl glycol or mixtures of two or more thereof. Particularly suitable acids are isophthalic acid and adipic acid and mixtures thereof.
In a particularly preferred embodiment of the invention, polyols used as polyol component for the production of component A are, for example, dipropylene glycol and/or polypropylene glycol with a molecular weight of about 400 to about 2500 and polyester polyols, preferably polyester polyols obtainable by polycondensation of hexanediol, ethylene glycol, diethylene glycol or neopentyl glycol or mixtures of two or more thereof and isophthalic acid or adipic acid or mixtures thereof.
High molecular weight polyester polyols include, for example, the reaction products of polyhydric, preferably dihydric, alcohols (optionally together with small quantities of trihydric alcohols) and polybasic, preferably dibasic, carboxylic acids. Instead of free polycarboxylic acids, the corresponding polycarboxylic anhydrides or corresponding polycar-boxylic acid esters with alcohols preferably containing 1 to 3 carbon atoms may also be used (where possible). The polycarboxylic acids may be aliphatic, cycloaliphatic, aromatic or heterocyclic or both. They may optionally be substituted, for example by alkyl groups, alkenyl groups, ether groups or halogens. Suitable polycarboxylic acids are, for example, succinic acid, adipic acid, suberic acid, azelaic acid, sebacic acid, phthalic acid, isophthalic acid, terephthalic acid, trimellitic acid, phthalic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, tetrachloro-phthalic anhydride, endomethylene tetrahydrophthalic anhydride, glutaric anhydride, malefic acid, malefic anhydride, fumaric acid, dimer fatty acid or trimer fatty acid or mixtures of two or more thereof. Small quantities of monofunctional fatty acids may optionally be present in the reaction mixture.
The polyesters may optionally contain a small percentage of terminal carboxyl groups. Polyesters obtainable from lactones, for example s-caprolactone, or hydroxycarboxylic acids, for example c~-hydroxycaproic acid, may also be used.
Polyacetals are also suitable polyol components. Polyacetals are compounds which can be obtained from glycols, for example diethylene glycol or hexanediol or mixtures thereof with formaldehyde. Polyacetals suitable for use in accordance with the invention may also be obtained by the polymerization of cyclic acetals.
Other suitable polyols for the production of components A and B are polycarbonates. Polycarbonates may be obtained, for example, by the reaction of diols, such as propylene glycol, butane-1,4-diol or hexane-1,6 diol, diethylene glycol, triethylene glycol or tetraethylene glycol or mixtures of two or more thereof, with diaryl carbonates, for example diphenyl carbonate, or phosgene.
OH-functional polyacrylates are also suitable polyol components for the production of component A. These polyacrylates are obtainable, for example, by the polymerization of ethylenically unsaturated monomers containing an OH group. Monomers such as these are obtainable, for example, by the esterification of ethylenically unsaturated carboxylic acids and dihydric alcohols, the alcohol generally being present in a slight excess. Ethylenically unsaturated carboxylic acids suitable for this purpose are, for example, acrylic acid, methacrylic acid, crotonic acid or malefic acid.
Corresponding OH-functional esters are, for example, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, 3-hydroxypropyl acrylate or 3-hydroxypropyl methacrylate or mixtures of two or more thereof.
To produce component A, the corresponding polyol component is reacted with an at least difunctional isocyanate. Suitable at least difunctional isocyanates for the production of component A are basically any isocyanates containing at least two isocyanate groups although, in general, compounds containing 2 to 4 isocyanate groups, more particularly 2 isocyanate groups, are preferred for the purposes of the present invention.
At least difunctional isocyanates suitable as the at least difunctional isocyanate for the production of component A are described in the following.
These at least difunctional isocyanates are, for example, ethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diiso-cyanate (HDI), cyclobutane-1,3-diisocyanate, cyclohexane-1,3- and -1,4-diisocyanate and mixtures of two or more thereof, 1-isocyanato-3,3,5-tri-methyl-5-isocyanatomethyl cyclohexane (isophorone diisocyanate, IPDI), 2,4- and 2,6-hexahydrotoluene diisocyanate, tetramethyl xylylene diiso-cyanate (TMXDI), 1,3- and 1,4-phenylene diisocyanate, 2,4- or 2,6-toluene diisocyanate, diphenyl methane-2,4-diisocyanate, diphenylmethane-2,2'-diisocyanate or diphenylmethane-4,4'-diisocyanate or mixtures of two or more of the diisocyanates mentioned.
According to the invention, other suitable isocyanates for the production of component A are trifunctional or higher isocyanates obtainable, for example, by oligomerization of diisocyanates. Examples of such trifunctional and higher polyisocyanates are the triisocyanurates of HDI or IPDI or mixtures thereof or mixed triisocyanurates thereof.
In one preferred embodiment of the invention, diisocyanates containing two isocyanate groups differing in their reactivity are used for the production of component A. Examples of such diisocyanates are 2,4- and 2,6-toluene diisocyanate (TDI) and isophorone diisocyanate (IPDI). With non-symmetrical diisocyanates such as these, one isocyanate group generally reacts far more quickly with isocyanate-reactive groups, for example OH groups, while the remaining isocyanate group reacts comparatively sluggishly. Accordingly, in one preferred embodiment, a monocyclic non-symmetrical diisocyanate containing two isocyanate groups differing in their reactivity, as described above, is used for the production of component A.
In one particularly preferred embodiment, 2,4- or 2,6-toluene diiso-cyanate (TDI) or a mixtures of the two isomers, but especially pure 2,4-TDI, is used for the production of component A.
Component B is produced using an at least difunctional isocyanate which ensures that at least the predominant percentage of the isocyanate groups of component B remaining after the reaction with the polyol com-ponent is more reactive than the predominant percentage of the isocyanate groups present in component A. Difunctional isocyanates of which the isocyanate groups are largely identical in their reactivity are preferably used for the production of component B. More particularly, these difunctional isocyanates are the symmetrical isocyanates, preferably the symmetrical, aromatic difunctional isocyanates. In one particularly preferred embodi-ment, the bicyclic, aromatic, symmetrical diisocyanates of the diphenyl methane series, more particularly MDI, are used for the production of component B.
A polyurethane binder with the advantages according to the invention can be produced in basically any way. However, two processes which are described hereinafter have proved to be particularly advantageous.
For example, the polyurethane binder can be directly produced by preparing component A and subsequently adding component B.
However, the compound required as component B may actually be used in the preparation of component A and may be added in such an excess that the required final content of component B is reached.
Accordingly, the present invention also relates to an at least two-stage process for the production of a low-viscosity polyurethane binder containing isocyanate groups, characterized in that (g) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least one polyol component and (h) in a second stage, another at least difunctional isocyanate or another at least difunctional isocyanate and another polyol component is/are reacted in the presence of the polyurethane prepolymer, the predominant percentage of the isocyanate groups present on completion of the first stage having a lower reactivity to isocyanate-reactive groups, more particularly to OH groups, than the isocyanate groups of the at least difunctional isocyanate added in the second stage and the OH:NCO ratio in the second stage being about 0.2 to about 0.6:1.
In principle, any of the polyols component which have already been mentioned herein may be used as the other polyol component.
In one advantageous embodiment, the OH:NCO ratio in the first stage of the process according to the invention is less than 1:1. In one preferred embodiment, the ratio of OH groups to isocyanate groups in the first stage is about 0.4 to about 0.7:1 and, more particularly, more than 0.5 to about 0.7:1.
The reaction of a polyol component with the at least difunctional isocyanate in a first stage may be carried out in any manner known to the expert under the general rules for producing polyurethanes. For example, the reaction may be carried out in the presence of solvents. Suitable solvents are, basically, any of the solvents typically used in polyurethane chemistry, more particularly esters, ketones, halogenated hydrocarbons, alkanes, alkenes and aromatic hydrocarbons. Examples of such solvents are methylene chloride, trichloroethylene, toluene, xylene, butyl acetate, amyl acetate, isobutyl acetate, methyl isobutyl ketone, methoxybutyl acetate, cyclohexane, cyclohexanone, dichlorobenzene, diethyl ketone, diisobutyl ketone, dioxane, ethyl acetate, ethylene glycol monobutyl ether acetate, ethylene glycol monoethyl acetate, 2-ethylhexyl acetate, glycol diacetate, heptane, hexane, isobutyl acetate, isooctane, isopropyl acetate, methyl ethyl ketone, tetrahydrofuran or tetrachloroethylene or mixtures of two or more of the solvents mentioned.
If the reaction components themselves are liquid or if at least one or more of the reaction components forms) a solution or dispersion of other insufficiently liquid reaction components, there is no need at all to use solvents. A solventless reaction represents a preferred embodiment of the invention.
To carry out the first stage of the process according to the invention, the polyol is introduced into a suitable vessel, optionally together with a suitable solvent, and mixed. The at least difunctional isocyanate is then added with continued mixing. To accelerate the reaction, the temperature is normally increased. In general, the reaction mixture is heated to about 40 to about 80°C. The exothermic reaction which then begins provides for an increase in the temperature. The temperature of the mixture is kept at about 70 to about 110°C, for example at about 85 to 95°C or, more parti-cularly, at about 75 to about 85°C, the temperature optionally being adjusted by suitable external measures, for example heating or cooling.
Catalysts typically used in polyurethane chemistry may optionally be added to the reaction mixture to accelerate the reaction. Dibutyl tin dilaurate or diazabicyclooctane (DABCO) is preferably added. If it is desired to use a catalyst, the catalyst is generally added to the reaction mixture in a quantity of about 0.005% by weight or about 0.01 % by weight to about 0.2% by weight, based on the mixture as a whole.
The reaction time for the first stage depends upon the polyol component used, upon the at least difunctional isocyanate used, upon the reaction temperature and upon the catalyst present, if any. The total reaction time is normally about 30 minutes to about 20 hours.
Isophorone diisocyanate (IPDI), tetramethylene xylylene diisocya-nate (TMXDI), hydrogenated diphenyl methane diisocyanate (MDIH~2) or toluene diisocyanate (TDI) or a mixture of two or more thereof is preferably used as the at least difunctional isocyanate in the first stage.
To carry out the second stage of the process according to the invention, at least one other at least difunctional isocyanate is reacted with another polyol component in admixture with component A obtained in the first stage. Any polyol from the group of polyols listed in the foregoing or a mixture of two or more thereof may be used as a constituent of the other polyol component. However, a polypropylene glycol with a molecular weight of about 400 to about 2500 or a polyester polyol with at least a high percentage and, more particularly, a predominant percentage of aliphatic dicarboxylic acids or a mixture of these polyols is preferably used as the polyol component in the second stage of the process according to the invention.
At least one polyisocyanate of which the isocyanate groups have a higher reactivity than the majority of the isocyanate groups present in the prepolymer is used as the at least difunctional isocyanate in the second stage of the process according to the invention. In other words, reactive isocyanate groups emanating from the at least difunctional isocyanate originally used for the production of prepolymer A may be present in the prepolymer, the only requirement in this connection being that the predominant percentage of the isocyanate groups present in the prepolymer A should have a lower reactivity than the isocyanate groups of the other at least difunctional isocyanate added in the second stage of the process according to the invention.
A bicyclic aromatic symmetrical diisocyanate is preferably used as the other at least difunctional isocyanate. The bicyclic isocyanates include, for example, diisocyanates of the diphenyl methane series, more particularly 2,2'-diphenyl methane diisocyanate, 2,4'-diphenyl methane diisocyanate and 4,4'-diphenyl methane diisocyanate. Of the diisocyanates mentioned, diphenyl methane diisocyanate, more particularly 4,4'-diphenyl methane diisocyanate, is particularly preferred as the other at least difunctional isocyanate for the second stage of the process according to the invention.
The other at least difunctional isocyanate is used in the second stage in a quantity of about 5 to about 95% by weight, preferably in a quantity of about 20 to about 95% by weight and more preferably in a quantity of about 40 to about 90% by weight, based on the total quantity of polyisocyanates used in all the stages of the process according to the invention.
In one preferred embodiment, the OH:NCO ratio in the second stage is about 0.2 to about 0.6:1 and, more particularly, up to about 0.5:1. By this is meant the OH:NCO ratio of the components added in the second stage excluding any isocyanate groups emanating from the prepolymer A.
However, a polyurethane binder with the advantages according to the invention can also be produced by mixing individual components C, D
and E.
Accordingly, the present invention also relates to a process for the production of a low-viscosity polyurethane binder containing isocyanate groups with a low content of readily volatile isocyanate-functional monomers by mixing three components C, D and E, characterized in that (i) an isocyanate-functional polyurethane prepolymer obtainable by reacting a polyol component with an at least difunctional isocyanate is used as component C, (j) another isocyanate-functional polyurethane prepolymer obtainable by reacting a polyol component with another at least difunctional isocyanate, of which the isocyanate groups have a higher reactivity to isocyanate-reactive groups than the isocyanate groups of component C, is used as component D
and (g) another at least difunctional isocyanate, of which the molecular weight is lower than that of components C and D and of which the isocyanate groups have a higher reactivity to isocyanate-reactive groups than the isocyanate groups of component C, is used as component E, the quantity of component E being gauged so that, on completion of mixing and after all the reactions, if any, taking place between components C, D
and E have ended, at least 5% by weight and more particularly at least 10% by weight of component E is present in the polyurethane binder.
The polyurethane binders according to the invention and the polyurethane binders produced in accordance with the invention preferably have a viscosity of less than 5000 mPas (as measured with a Brookfield RT
DVII (Thermosell), spindle 27, 20 r.p.m., 50°C).
In the context of the present invention, the expression "all the reactions, if any, taking place between components C, D and E" refers to reactions of isocyanate groups with functional groups containing isocyanate-reactive hydrogen atoms. The addition of component E, particularly when components C or D or C and D, for example, contain free OH groups, generally leads to a reaction of the isocyanate groups of component E with the free OH groups. This results in a reduction in the content of component E. Accordingly, if reactions capable of leading to a reduction in the proportion of component E are likely to occur, component E
must be added in such a quantity that, after all these reactions have ended, the required minimum quantity of component E is present in the polyure-thane binder.
Any of the polyols described above and mixtures of two or more of the polyols mentioned may be used as the polyol component for the production of components C and D in the process according to the invention. The polyol components in particular mentioned in the present specification as particularly suitable for the production of component A are also preferably used in the process according to the invention.
The foregoing observations on component B apply similarly to the at least difunctional isocyanate to be used as component E, of which the molecular weight is lower than that of components C and D and of which the isocyanate groups have a higher reactivity than the isocyanate groups of component C.
In one preferred embodiment of the invention, another at least tri-functional isocyanate may be added as component H after the two stages already described. Suitable at least trifunctional isocyanates are the poly-isocyanates containing at least three NCO groups described in the foregoing or the trimerization and polymerization products of the difunctional isocyanates mentioned above.
The polyurethane binder according to the invention and the polyure-thane binders produced in accordance with the invention are distinguished in particular by the fact that they have an extremely low content of readily volatile monomers containing isocyanate groups which is less than 2% by weight or less than 1 % by weight, less than 0.5% by weight and, more particularly, less than about 0.1 % by weight. It is particularly emphasized in this connection that the process according to the invention does not require any separate process steps for removing readily volatile diisocya-nate components.
Another advantage of the polyurethane binders produced by the process according to the invention is that they have a viscosity which lies in a very favorable range for processing. More particularly, the polyurethane binders produced by the process according to the invention have a viscosity below 5000 mPas (as measured with a Brookfield RT DVII
(Thermosell), spindle 27, 20 r.p.m., 50°C).
The polyurethane binders according to the invention are suitable for coating articles and more particularly for bonding articles either as such or in the form of solutions in organic solvents, for example in the solvents described in the foregoing.
Accordingly, the present invention also relates to the use of a polyurethane binder according to the invention or of a polyurethane binder produced by a process according to the invention in the production of adhesives, more particularly one-component and two-component adhesives, coatings, more particularly lacquers, emulsion paints and casting resins as well as moldings and for coating and, more particularly, bonding articles, more particularly for bonding films and for the production of laminated films.
The polyurethane binder according to the invention or the polyure-thane binder produced by one of the processes according to the invention is used in particular for bonding plastics and, in one particularly preferred embodiment, for laminating plastic films, plastic films metallized with metals or with metal oxides and metal foils, more particularly aluminium foils.
The curing process, i.e. the crosslinking of the individual polyure-thane binder molecules through the free isocyanate groups, may be carried out solely under the influence of atmospheric moisture, i.e. without any need to add hardeners. However, polyfunctional crosslinking agents, for example amines or, more particularly, polyfunctional alcohols, are preferably added as hardeners (two-component systems).
Film laminates made with the products produced in accordance with the invention are safe to heat-seal. This is attributable to the reduced percentage of migratable low molecular weight products in the polyure-thane binders. A favorable processing temperature for the adhesives produced in accordance with the invention in heat-sealing processes is between about 30 and about 90°C.
The present invention also relates to an adhesive containing two components F and G, (i) a polyurethane binder containing isocyanate groups according to the invention or a polyurethane binder containing isocyanate groups produced by the process according to the invention being used as component F
and (j) a compound containing at least two functional groups reactive to the isocyanate groups of component F with a molecular weight of up to 2500 or a mixture of two or more such compounds being used as component G.
Accordingly, any of the polyurethane binders according to the invention as described in the foregoing may be used as component F.
A compound containing at least two functional groups reactive to the isocyanate groups of component F with a molecular weight of up to 2500 or a mixture of two or more such compounds is preferably used as component G. The at least two functional groups reactive to the isocyanate groups of component F may be selected in particular from amino groups, mercapto groups or OH groups. Compounds suitable for use in component G may contain amino groups, mercapto groups or OH groups either individually or in admixture.
The functionality of the compounds suitable for use in component G
is generally at least about two. Component G preferably has a percentage of compounds with a higher functionality, for example with a functionality of three, four or more. The total (average) functionality of component G is for example about two (for example when only difunctional compounds are used as component G) or more, for example about 2.1, 2.2, 2.5, 2.7 or 3.
Component G may optionally have an even higher functionality, for example of about 4 or higher.
Component G preferably contains a polyol carrying at least two OH
groups. Any of the polyols mentioned in the foregoing are suitable for use in component G providing they satisfy the limiting criterion of the upper molecular weight limit.
Component G is generally used in such a quantity that the ratio of isocyanate groups of component F to functional groups reactive with isocyanate groups of component F in component G is about 5:1 to about 1:1 and, more particularly, about 2:1 to about 1:1.
The adhesive according to the invention generally has a viscosity of about 250 to about 10,000 mPas and, more particularly, in the range from about 500 to about 8000 mPas or to about 5000 mPas (Brookfield RVT
DVII, spindle 27, 20 r.p.m., 40°C).
The adhesive according to the invention may optionally contain additives. The additives may make up as much as about 30% by weight of the adhesive as a whole.
Additives suitable for use in accordance with the present invention include, for example, plasticizers, stabilizers, antioxidants, dyes, photo-stabilizers and fillers.
Suitable plasticizers are, for example, plasticizers based on phthalic acid, more particularly dialkyl phthalates, phthalic acid esters esterified with a linear alkanol containing about 6 to about 12 carbon atoms representing preferred plasticizers. Dioctyl phthalate is particularly preferred.
Other suitable plasticizers are benzoate plasticizers, for example sucrose benzoate, diethylene glycol dibenzoate and/or diethylene glycol benzoate, in which about 50 to about 95% of all the hydroxyl groups have been esterified, phosphate plasticizers, for example t-butylphenyl Biphenyl phosphate, polyethylene glycols and derivatives thereof, for example, Biphenyl ethers of polyethylene glycol), liquid resin derivatives, for example the methyl ester of hydrogenated resin, vegetable and animal oils, for example glycerol esters of fatty acids and polymerization products thereof.
Stabilizers or antioxidants suitable for use as additives in accordance with the invention include hindered phenols of high molecular weight (Mn), polyhydric phenols and sulfur- and phosphorus-containing phenols. Phenols suitable for use as additives in accordance with the invention are, for example, 1,3,5-trimethyl-2,4,6-tris-(3,5-ditert.butyl-4-hy-droxybenzyl)-benzene; pentaerythritol tetrakis-3-(3,5-ditert.butyl-4-hydroxy-phenyl)-propionate; n-octadecyl-3,5-ditert.butyl-4-hydroxyphenyl)-propion-ate; 4,4-methylene-bis-(2,6-ditert.butylphenol); 4,4-thiobis-(6-tert.butyl-o-cresol); 2,6-ditert.butylphenol; 6-(4-hydroxyphenoxy)-2,4-bis-(n-octylthio)-1,3,5-triazine; di-n-octadecyl-3,5-ditert.butyl-4-hydroxybenzyl phosphon-ates; 2-(n-octylthio)-ethyl-3,5-ditert.butyl-4-hydroxybenzoate; and sorbitol hexa-[3-(3,5-ditert.butyl-4-hydroxyphenyl)-propionate].
Suitable photostabilizers are, for example, those marketed under the name of Tinuvin~ (manufacturer: Ciba Geigy).
Other additives may be incorporated in the adhesives according to the invention in order to vary certain properties. These other additives include, for example, dyes, such as titanium dioxide, fillers, such as talcum, clay and the like. The adhesives according to the invention may optionally contain small quantities of thermoplastic polymers or copolymers, for example ethylene/vinyl acetate (EVA), ethylene/acrylic acid, ethylene/meth-acrylate and ethylene/n-butyl acrylate copolymers which optionally provide the adhesive with additional flexibility, toughness and strength. It is also possible - and preferred in accordance with the invention - to add certain hydrophilic polymers, for example polyvinyl alcohol, hydroxyethyl cellulose, hydroxypropyl cellulose, polyvinyl methyl ether, polyethylene oxide, polyvinyl pyrrolidone, polyethyl oxazolines or starch or cellulose esters, more particularly the acetates with a degree of substitution of less than 2.5, which increase the wettability of the adhesives.
The following Examples are intended to illustrate the invention without limiting it in any way.
Examples List of the abbreviations used:
DPG - dipropylene glycol PPG - polypropylene glycol TDI - toluene diisocyanate (2,4-isomer) MDI - 4,4'-diphenyl methane diisocyanate PE - polyester based on isophthalic acidladipic acid/diethylene glycolldipropylene glycol NCO - isocyanate group content OHV - OH value M - molecular weight d - day VH - laminate adhesion SNH - sealing seam adhesion OPA - oriented polyamide PEKO$$ LLDPEILDPE blend, thickness: ca. 70 pm, manufacturer:
=
Mildenberger and Willing Examples 1 to 9 were carried out by the following method:
The polyol components of the first stage were introduced first and homogeneously mixed. The isocyanate was then added and the temperature of the reaction mixture was increased to 50°C. The temperature then rose considerably as a result of the exothermic reaction between isocyanate groups and OH groups and, after reaching 90°C, was kept at that level by cooling.
The components for the second stage were added to the reaction product of the first stage and the mixture was adjusted to a temperature of 85°C, followed by stirring for another hour.
In Example 9, the first and second stages were separately produced and the resulting products were subsequently mixed.
Examples 10, 11 and 12 were carried out with isophorone diisocyanate (IPDI) as the first isocyanate component.
The results are set out in Table 1 below.
Table 1:
Examples 1 to 12 Example 1 2 3 4 5 6 O_HV Eq__u_ivalent weight 1st Stage TDI 19.0 18.1 17.1 19.6 22.0 17.1 OH:NCO ratio 0.555 0.556 0.588 0.588 0.588 0.588 Equivalents 0.218 0.208 0.196 0.2250 0.253 0.196 NCO
Equivalents 0.121 0.115 0.116 0.1323 0.149 0.116 OH
NCO:OH ratio 1.8 1.8 1.7 1.7 1.7 1.7 Final NCO 9.9 9.4 8.5 9.6 10.7 8.5 content Quantity 41.0 41.1 40.1 40.6 41.0 40.1 1st stage 2nd Stage MDI 38.8 38.3 39.7 38.6 37.1 38.2 OH: NCO ratio 0.29 0.294 0.284 0.292 0.303 0.2535 2nd stage Equivalents 0.31 0.306 0.318 0.31 0.297 0.3053 NCO 2nd stage Equivalents 0.09 0.09 0.09 0.09 0.09 0.0774 OH 2nd stage NCO:OH addition 3.44 3.40 3.53 3.43 3.29 3.94 ratio 2nd stage NCO:OH addition 2.50 2.50 2.50 2.40 2.30 - 2.60 ratio, total -Quantity, 109.8 109.3 109.8 109.2 108.1 108.2 total Final NCO 12.1 11.8 11.8 12.0 12.1 12.0 Viscos.40C: 9000 9300 5800 9370 14500 4190 Viscos.50C: 3300 3530 2220 3320 4660 1770 NCO (1d) 11.80% 12% 12.1% 12.2%
MDI 17.00% 16.0% I 17.1% 16.6%
TDI I I I 0.10% 0.10% / I 0.08% 0.09% 0.1 I I I I %1 Table 1 continued Example 7 8 911 912 913 Stage Stage Mixing SeparateSeparateof the batch batch separate batches OHV Equivalent weight 1st Stage TDI 21.7 21.7 17.1 PPG 13.5 13.5 12 PPG 25.5 25.5 8 PE 26.645 26.645 0 OH:NCO ratio 0.714 0.714 0.588 Equivalents 0.249 0.249 0.196 NCO
Equivalents 0.178 0.178 0.116 OH
NCO:OH ratio 1.4 1.4 1.77 Final NCO 3.4 3.4 8.5 content Quantity 87.3 87.3 40.1 1st stage 2nd Stage MDI 12.2 33.9 38.3 DPG 0.575 0.575 0 OH:NCO ratio 0.088 0.032 2nd stage Equivalents 0.098 0.271 0.3058 NCO 2nd stage Equivalents 0.009 0.009 0.0774 OH 2nd stage NCO:OH addition 31.67 3.95 ratio 2nd stage NCO:OH addition 2.79 3.95 ratio, total Quantity, 100.1 121.8 68.2 total Final NCO 6.7 11.5 14.1 Viscos.40C: Viscos.20000 3470 103000 1330 4600 Viscos. 50C: Viscos.7200 1420 I I 1770 NCO (1d) 7.10% 11.10% 9.00% 14.10% 12.40%
MDI I I I 28.00% 18%
TDI / / 0.80% / 0.30%
Table 1 continued Example 10 11 12 OHV Equivalent weight 1 Stage IPDI 21.1 19.3 17.1 PPG 400 256 219 10.3 10.64 10.64 PPG 1000 113 497 19.5 7.09 7.09 DPG 836 67 0 2.66 2.66 PE 218 137 410 20.4 0 0 Stanclere 0.01 0.075 0.075 TL
Equivalents 0.1905 0.1741 0.1537 NCO
Equivalents 0.1360 0.1024 0.1024 OH
Addition 1.4 1.7 1.5 ratio X:1 Final NCO 3.2 7.6 5.7 Quantity 71.3 39.7 37.4 1 st stage 2nd Stage MDI 28.1 54.6 77.1 PPG 400 0 14.4 20.304 PPG 1000 0 15.2 21.432 DPG 0.45 0 0 PE 218 0 14.9 21.009 Equivalents 0.2249 0.4371 0.6164 NCO 2nd stage Equivalents 0.0067 0.1327 0.1871 OH 2nd stage NCO:OH addition 33.56 3.29 3.30 ratio 2nd stage NCO:OH addition 2.91 2.60 2.66 ratio, total Quantity, 99.9 138.9 177.2 total Final NCO 11.5 11.4 11.4 Viscos.40C 6000 4910 5600 Viscos.50C 2800 1960 2120 NCO (24 11.55% 12.20% 12.10%
h) MDI (batch) 22.70% 20.00% 20.00%
~ IPDI (batch)~ ~ <1% ~ <1% I ~1%
~
Table 2:
Example 13 OHV Equivalent weight 1 st Stage TDI 15.7 PPG 400 265 212 9.9 PPG 1000 111 506 6.6 PPG 2000 55 1020 8.58 DPG 835 67 2.502 Equivalents NCO 0.1803 Equivalents OH 0.1054 Addition ratio X:1 1.71 Final NCO 7.3 Quantity 1 st stage 43.3 2nd Stage MDI - 31.9 PPG 400 4.104 PPG 1000 12.402 PE 218 8.208 Equivalents NCO 2nd stage 0.2552 Equivalents OH 2nd stage 0.0647 NCO:OH addition ratio 2nd 3.95 stage NCO:OH addition ratio, 2.56 total Quantity 1 st + 2nd stage 99.9 Final NCO 11.2 3rd Stage Desmodur 3300 20 Equivalents NCO 3rd stage __ 0.1026 Quantity, total 119.9 Final NCO _ ~ 12.9 Viscos. 40C 4200 mPas Color clear, yellowish Table 3: Evaluation of the lamination tests with a polyurethane binder according to Example 6.
Table 3 Laminate Quantity Web VH unprinted SNH n115 mm structure ' applied speed NI15 mm glm2 mlmin.
OPAI 1.9 100 11.6 52.1 PEKOee PE elongation Internal laminate failure OPAI 1.5 100 11.7 55.1 PEKO88 PE elongation Laminate failure in edge of sealing seam OPAI 1.1 100 11.1 55.4 PEKOeg PE elongation Laminate failure in edge of sealing seam Migration test:
The migrate content is determined as follows (see Deutsche Lebensmittel Rundschau, 87, (1991), 280-281):
A weldable laminated film bag made with the adhesive according to the invention is filled with 3% acetic acid and stored for 2 h at 70°C.
The contents of the bag are then diazotized, subjected to azo coupling with N-(1-naphthyl)-ethylenediamine and concentrated in a C~$ column. The concentration of azo dye is then photometrically determined. The results are set out in Table 4 below.
Table 4:
Results of the migration tests Migrates Laminate (after days) 01.07.97 9.7 Ng AHCU100 ml (4 days) 9.7 Ng AHCU100 ml 07.07.973.8 Ng AHCLI100 ml (10 days) 11.07.97 0.93 Ng AHCL/100 ml (14 days) 21.07.97 <0.2 Ng AHCU100 ml (24 days)
Isocyanate-terminated polyurethane prepolymers have been known for some time. They may readily be chain-extended or crosslinked with suitable hardeners, usually polyhydric alcohols, to form high molecular weight materials. Polyurethane prepolymers have acquired significance in many fields of application, including for example the production of adhesives, coatings, casting resins and moldings.
In order to obtain isocyanate-terminated polyurethane prepotymers, it is standard practice to react polyhydric alcohols with an excess of polyisocyanates, generally at least predominantly diisocyanates. Molecular weight can be controlled at least approximately through the ratio of OH
groups to isocyanate groups. Whereas a ratio of OH groups to isocyanate groups of, or approaching, 1:1 leads to generally high molecular weights, a statistical average of one diisocyanate molecule - where diisocyanates are used - is attached to each OH group where the OH : isocyanate group ratio is about 2:1, so that ideally no oligomerization or chain extension occurs in the course of the reaction.
In practice, however, chain-extending reactions are impossible to suppress with the result that, on completion of the reaction, a certain quantity of the component used in excess is left over irrespective of the reaction time. If diisocyanate, for example, is used as the excess component, a generally considerable proportion of this component remains behind in the reaction mixture for the reasons explained above.
The presence of such components is particularly problematical when they consist of readily volatile diisocyanates. The vapors of these diisocya-nates are often harmful to the skin and the application of products with a high content of such readily volatile diisocyanates requires elaborate measures on the part of the user to protect the people involved in processing the product, more particularly elaborate measures for keeping the surrounding air clean to breathe.
Since protective measures and cleaning measures generally involve considerable expense, there is a need on the part of the user for products which have a low percentage content of readily volatile diisocyanates depending on the isocyanate used.
In the context of the present invention, "readily volatile" substances are understood to be substances which have a vapor pressure at around 30°C of more than about 0.0007 mmHg or a boiling point of less than about 190°C (70 mPa).
If low-volatility diisocyanates, more particularly the widely used bicyclic diisocyanates, for example diphenyl methane diisocyanates, are used instead of the readily volatile diisocyanates, polyurethane binders with a viscosity normally outside the range suitable for simple processing methods are generally obtained. In cases such as these, the viscosity of the polyurethane prepolymers can be reduced by adding suitable solvents although this is not consistent with the absence of solvents normally demanded. Another way of reducing viscosity without solvents is to add an excess of monomeric polyisocyanates which are incorporated in the coating or bond (reactive diluent) in the course of a subsequent curinglhardening process (after the addition of a hardener or by curing under the influence of moisture).
Whereas the viscosity of the polyurethane prepolymers can actually be reduced in this way, the generally incomplete reaction of the reactive diluent often leads to the presence in the bond or coating of free monomeric polyisocyanates which are capable of "migrating", for example within the coating or bond or, in some cases, even into the coated or bonded materials themselves. Corresponding constituents of a coating or bond are often referred to among experts as "migrates". By contact with moisture, the isocyanate groups of the migrates are continuously reacted to form amino groups. The aromatic amines normally formed in this way are suspected of having a carcinogenic effect.
Migrates are often not tolerable, above all in the packaging field, because any migration of the migrates through the packaging material would result in contamination of the packaged product and the consumer would inevitably come into contact with the migrates when using the product.
Accordingly, the migrates in question are undesirable above all in the packaging field, especially in the packaging of foods.
In order to avoid the disadvantages described above, EP-A 0 118 065 proposes producing polyurethane prepolymers by a two-stage process.
In the first stage of this process, a monocyclic diisocyanate is reacted with a polyhydric alcohol in an OH group : isocyanate group ratio of <1 and, in the second step, a bicyclic diisocyanate is reacted with polyhydric alcohols in an OH group : isocyanate group ratio of <1 in the presence of the prepolymer prepared in the first step. A ratio of OH groups to isocyanate groups of 0.65 to 0.8:1 and preferably 0.7 to 0.75:1 is proposed for the second stage. The prepolymers obtainable in this way still have viscosities of 2500 mPas, 7150 mPas and 9260 mPas at high temperatures (75°C and 90°C).
DE-A 34 01 129 relates to a process for the production of mixed polyurethane prepolymers in which polyhydric alcohols are first reacted with the faster reacting isocyanate group of an asymmetrical diisocyanate, the more slowly reacting group being left intact, after which the reaction products are combined with a symmetrical diisocyanate of which the equally reactive isocyanate groups react more quickly than the slowly reacting groups of the first polyfunctional isocyanate compound mentioned.
The described polyurethane prepolymers have high viscosities and hence high processing temperatures so that they can only be used under conditions which allow high processing temperatures.
EP-A 0 019 120 relates to a two-stage process for the production of elastic weather-resistant sheet-form materials. In the first stage of this process, toluene diisocyanate (TDI) is reacted with at least equimolar quantities of a polyol and the reaction product obtained is subsequently reacted with diphenyl methane diisocyanate (MDI) and a polyol. The poly-urethane binders obtainable in this way are said to be capable of curing with water or with atmospheric moisture. Although the described process does give products with a relatively low viscosity, the content of free readily volatile diisocyanate (in the present case TDI) is still high (0.7% by weight) and can only be reduced when time-consuming and energy-intensive methods, for example thin-layer distillation, are used to remove excess readily volatile diisocyanate.
In many cases, laminated films are used in applications involving elevated temperatures, for example in the preparation of foods. Unfortu-nately, laminated films produced with conventional adhesives often under-go delamination whenever they are exposed to the temperatures normally prevailing in the preparation of foods.
Accordingly, the problem addressed by the present invention was to provide a polyurethane binder which would have a low viscosity and a low residual content of less than about 1 % by weight of readily volatile diiso-cyanates. In the case of toluene diisocyanate (TDI), the residual content of readily volatile isocyanate should be less than about 0.1 % by weight.
Another problem addressed by the present invention was to provide a polyurethane binder which would enable processing to be carried out at low temperatures.
A further problem addressed by the present invention was to provide a polyurethane binder which would have a low percentage content of "migrates", i.e. a low percentage content of monomeric polyisocyanates.
Another problem addressed by the present invention was to provide a polyurethane binder with which it would be possible to produce laminated films which would have little or no tendency to delaminate, even at high temperatures.
Finally, another problem addressed by the present invention was to provide a process for the production of a polyurethane binder having the properties mentioned above.
The present invention relates to a polyurethane binder with a low content of readily volatile isocyanate-functional monomers at least containing components A and B, in which (a) a polyurethane polymer containing at least two isocyanate groups or a mixture of two or more polyurethane prepolymers containing at least two isocyanate groups is present as component A, the polyurethane prepolymer containing two isocyanate groups or the mixture of two or more polyurethane prepolymers containing isocyanate groups containing at least two differently attached types of isocyanate groups of which at least one type has a lower reactivity to isocyanate-reactive groups than the other type(s), and (b) an at least difunctional isocyanate, of which the molecular weight is lower than the molecular weight of the polyurethane prepolymers present in component A and of which the isocyanate groups have a higher reactivity to isocyanate-reactive compounds than the type of isocyanate groups of relatively low reactivity present in component A, is present as component B.
"Low viscosity" in the context of the present invention means a (Brookfield) viscosity at 50°C of less than 5000 mPas.
In the context of the present invention, the expression "polyurethane binder" is understood to be a mixture of molecules each containing at least two isocyanate groups, in which the content of molecules with a molecular weight of more than 500 is at least about 50% by weight and preferably at least about 60% by weight or about 70% by weight.
A polyurethane prepolymer containing at least two isocyanate groups or a mixture of two or more polyurethane prepolymers containing at least two isocyanate groups, which may preferably be obtained by reacting a polyol component with an at least difunctional isocyanate, is used as component A.
In the context of the present invention, a "polyurethane prepolymer"
is understood to be the compound which is obtained, for example, when a polyol component is reacted with an at least difunctional isocyanate.
Accordingly, the expression "polyurethane prepolymer" encompasses both compounds of relatively low molecular weight, as formed for example in the reaction of a polyol with an excess of polyisocyanate, and also oligomeric or polymeric compounds. The expression "polyurethane prepolymer" also encompasses the compounds formed, for example, in the reaction of a trihydric or tetrahydric polyol with a molar excess of diisocyanates, based on the polyol. In this case, one molecule of the resulting compound carries several isocyanate groups.
Molecular weights relating to polymeric compounds represent the number average molecular weight (Mn), unless otherwise indicated.
In general, the polyurethane prepolymers used for the purposes of the present invention have a molecular weight in the range from about 500 to about 15,000 or in the range from about 500 to about 10,000, for example of the order of 5000, but especially in the range from about 700 to about 2500.
The polyurethane prepolymer containing two isocyanate groups or the mixture of two or more polyurethane prepolymers containing isocyanate groups has at least two differently attached types of isocyanate groups, of which at least one type has a lower reactivity to isocyanate-reactive groups than the other type or the other types of isocyanate groups. Isocyanate groups with a relatively low reactivity to isocyanate-reactive groups (by comparison with at least one other isocyanate group present in the poly-urethane binder) are also referred to hereinafter as "less reactive isocyanate groups" while the corresponding isocyanate group with a higher reactivity to isocyanate-reactive compounds is also referred to as the "more reactive isocyanate group".
According to the present invention, therefore, a difunctional polyurethane prepolymer for example containing two differently attached isocyanate groups, one of the isocyanate groups having a higher reactivity to isocyanate-reactive groups than the other isocyanate group, may be used as component A. A polyurethane prepolymer such as this may be obtained, for example, from the reaction of a dihydric alcohol with compounds containing two different, for example difunctional, isocyanate groups, the reaction being carried out in such a way that, on average, each molecule of the dihydric alcohol reacts with one molecule of the compounds containing different isocyanate groups.
A trifunctional or higher polyurethane prepolymer may also be used as component A, in which case one molecule of the polyurethane prepolymer for example may contain a different number of less reactive and more reactive isocyanate groups.
Mixtures of two or more polyurethane prepolymers may also be used as component A in accordance with the invention. The mixtures mentioned may be polyurethane prepolymers in which individual molecules carry identically attached isocyanate groups, at least one more reactive and one less reactive isocyanate group having to be present in the mixture as a whole. Besides molecules containing one or more identically attached isocyanate groups, the mixture may contain other molecules which carry both one or more identically attached isocyanate groups and one or more differently attached isocyanate groups.
Besides component A, the polyurethane binder according to the invention contains an at least difunctional isocyanate of which the molecular weight is lower than the molecular weight of the polyurethane prepolymers present in component A and of which the isocyanate groups have a higher reactivity to isocyanate-reactive compounds than the less reactive type of isocyanate groups present in component A.
In general, component B has a molecular weight of up to about 1000, molecular weights of up to about 720 or lower, for example of the order of 550, 500, 450, 400 or lower, being preferred. Component B may consist, for example, of low molecular weight diisocyanates with a molecular weight of up to about 300 or of the reaction products of dihydric or higher alcohols with an at least equimolar quantity of such low molecular weight diisocyanates, based on the OH groups of the dihydric or higher alcohol. Also suitable as component B are, for example, the trimerization products of difunctional isocyanates, the isocyanurates.
The polyurethane binder according to the invention contains at least 5% by weight of component B, based on the polyurethane binder as a whole.
The polyurethane binder according to the invention preferably has a content of readily volatile isocyanate-functional monomers of less than 2%
by weight or less than 1 % by weight or preferably less than 0.5% by weight.
These limits apply in particular to readily volatile isocyanate compounds which have only a limited danger potential for people involved in their processing, for example isophorone diisocyanate (IPDI), hexamethylene diisocyanate (HDI), tetramethyl xylylene diisocyanate (TMXDI) or cyclo-hexane diisocyanate. In the case of certain readily volatile isocyanate compounds, especially those which represent a serious risk to people involved in their processing, their content in the polyurethane binder according to the invention is preferably less than 0.3% by weight and more preferably less than 0.1 % by weight. These particular isocyanate compounds include, above all, toluene diisocyanate (TDI). In another preferred embodiment of the invention, the polyurethane binder has a TDI
and HDI content of less than 0.05% by weight.
In one preferred embodiment of the invention, the polyurethane binder according to the invention may contain an at least trifunctional isocyanate as component H in addition to components A and B.
Suitable at least trifunctional isocyanates are, for example, the trimerization and oligomerization products of the above-mentioned poly-isocyanates which can be obtained by suitably reacting polyisocyanates, preferably diisocyanates, to form isocyanurate rings. If oligomerization products are used, those which have a degree of oligomerization of on average about 3 to about 5 are particularly suitable.
Isocyanates suitable for the production of trimers are the diisocya-nates mentioned above, the trimerization products of the isocyanates HDI, MDI or IPDI being particularly preferred.
Polymeric isocyanates obtained, for example, as residue in the distillation of diisocyanates are also suitable for use as component H. The polymeric MDI obtainable from the distillation residue in the distillation of MDI is particularly suitable.
In one preferred embodiment of the invention, Desmodur N 3300, Desmodur N 100, the IPDI-trimeric isocyanurate T 1890 (products of Bayer AG) or triphenyl methane triisocyanate, for example, is used as component H.
Component H is preferably used in a quantity of about 1 to about 30% by weight and more preferably in quantity of about 5 to about 25% by weight, for example in a quantity of about 12 to about 20% by weight.
In one preferred embodiment of the invention, component A is prepared by an at least two-stage reaction in which (c) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least a first polyol component, the NCO:OH ratio being smaller than 2 and free OH groups still being present in the polyurethane prepolymer, and (d) in a second stage, another at least difunctional isocyanate is reacted with the polyurethane prepolymer from the first stage, the isocyanate groups of the isocyanate added in the second stage having a higher reactivity to isocyanate-reactive compounds than at least the predominant percentage of the isocyanate groups present in the polyurethane prepolymer from the first stage.
In another preferred embodiment, the other at least difunctional isocyanate is added in a molar excess, based on free OH groups of component A, the non-OH-reactive part of the other at least difunctional isocyanate representing component B.
In another preferred embodiment, component A is prepared by an at least two-stage reaction in which (e) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least a first polyol component, the NCO:OH ratio being smaller than 2 and free OH groups still being present in the polyurethane prepolymer, and (f) in a second stage, another at least difunctional isocyanate and another polyol component are reacted with the polyurethane prepolymer from the first stage, the isocyanate groups of the isocyanate added in the second stage having a higher reactivity to isocyanate-reactive compounds than at least the predominant percentage of the isocyanate groups present in the polyurethane prepolymer from the first stage.
In another preferred embodiment, the other at least difunctional isocyanate is added in a molar excess, based on free OH groups of component A and the other polyol component, the non-OH-reactive part of the other at least difunctional isocyanate representing component B.
According to the invention, the OH:NCO ratio in the production of component A in the second stage is preferably about 0.001 to less than 1:1 and, more particularly, 0.005 to about 0.8:1.
In one preferred embodiment of the invention, the OH:NCO ratio in the second stage is about 0.2 to 0.6:1.
In another preferred embodiment of the invention, the OH:NCO ratio in the first stage is less than 1 and, more particularly, 0.5 to 0.7:1, the described ratios optionally being maintained for the second stage also.
In the context of the present invention, the expression "polyol component" encompasses a single polyol or a mixture of two or more polyols which may be used for the production of polyurethanes. A polyol is understood to be a polyhydric alcohol, i.e. a compound containing more than one OH group in the molecule.
Various polyols may be used as the polyol component for the production of component A. They include, for example, aliphatic alcohols containing 2 to 4 OH groups per molecule. The OH groups may be both primary and secondary. Suitable aliphatic alcohols include, for example, ethylene glycol, propylene glycol, butane-1,4-diol, pentane-1,5-diol, hexane-1,6-diol, heptane-1,7-diol, octane-1,8-diol and higher homologs or isomers thereof which the expert can obtain by extending the hydrocarbon chain by one CH2 group at a time or by introducing branches into the carbon chain. Also suitable are higher alcohols such as, for example, glycerol, trimethylol propane, pentaerythritol and oligomeric ethers of the substances mentioned either individually or in the form of mixtures of two or more of the ethers mentioned with one another.
Other suitable polyol components for the production of component A
are the reaction products of low molecular weight polyhydric alcohols with alkylene oxides, so-called polyethers. The alkylene oxides preferably contain 2 to 4 carbon atoms. Suitable reaction products of the type in question are, for example, the reaction products of ethylene glycol, propylene glycol, the isomeric butane diols or hexane diols with ethylene oxide, propylene oxide or butylene oxide or mixtures of two or more thereof. The reaction products of polyhydric alcohols, such as glycerol, trimethylol ethane or trimethylol propane, pentaerythritol or sugar alcohols or mixtures of two or more thereof, with the alkylene oxides mentioned to form polyether polyols are also suitable. Polyether polyols with a molecular weight of about 100 to about 10,000 and preferably in the range from about 200 to about 5000 are particularly suitable. According to the invention, polypropylene glycol with a molecular weight of about 300 to about 2500 is most particularly preferred. Other suitable polyol components for the production of component A are polyether polyols as obtained, for example, from the polymerization of tetrahydrofuran.
The polyethers are reacted in known manner by reacting the starting compound containing a reactive hydrogen atom with alkylene oxides, for example ethylene oxide, propylene oxide, butylene oxide, styrene oxide, tetrahydrofuran or epichlorohydrin or mixtures of two or more thereof.
Suitable starting compounds are, for example, water, ethylene glycol, 1,2- or 1,3-propylene glycol, 1,4- or 1,3-butylene glycol, hexane-1,6 diol, octane-1,8-diol, neopentyl glycol, 1,4-hydroxymethyl cyclohexane, 2 methyl propane-1,3-diol, glycerol, trimethylol propane, hexane-1,2,6-triol, butane-1,2,4-triol, trimethylol ethane, pentaerythritol, mannitol, sorbitol, methyl glycosides, sugars, phenol, isononylphenol, resorcinol, hydroqui-none, 1,2,2- or 1,1,2-tris-(hydroxyphenyl)-ethane, ammonia, methyl amine, ethylenediamine, tetra- or hexamethylenediamine, triethanolamine, aniline, phenylenediamine, 2,4- and 2,6-diaminotoluene and polyphenylpolymethy-lene polyamines, which may be obtained by anilinelformaldehyde condensation, or mixtures of two or more thereof.
Polyethers modified by vinyl polymers are also suitable for use as a polyol component. Products such as these can be obtained, for example, by polymerizing styrene or acrylonitrile or mixtures thereof in the presence of polyethers.
Other suitable polyol components for the production of component A
are polyester polyols with a molecular weight of about 200 to about 10,000 For example, it is possible to use polyester polyols obtained by reacting low molecular weight alcohols, more particularly ethylene glycol, diethylene glycol, neopentyl glycol, hexanediol, butanediol, propylene glycol, glycerol or trimethylol propane, with caprolactone. Other suitable polyhydric alcohols for the production of polyester polyols are 1,4-hydroxymethyl cyclohexane, 2-methyl propane-1,3-diol, butane-1,2,4-triol, triethylene glycol, tetraethylene glycol, polyethylene glycol, dipropylene glycol, poly-propylene glycol, dibutylene glycol and polybutylene glycol.
Other suitable polyester polyols can be obtained by polycondensation. Thus, dihydric andlor trihydric alcohols may be condensed with less than the equivalent quantity of dicarboxylic acids and/or tricarboxylic acids or reactive derivatives thereof to form polyester polyols. Suitable dicarboxylic acids are, for example, succinic acid and higher homologs thereof containing up to 16 carbon atoms, unsaturated dicarboxylic acids, such as malefic acid or fumaric acid, and aromatic dicarboxylic acids, more particularly the isomeric phthalic acids, such as phthalic acid, isophthalic acid or terephthalic acid. Citric acid and trimellitic acid, for example, are also suitable tricarboxylic acids. Polyester polyols of at least one of the dicarboxylic acids mentioned and glycerol which have a residual content of OH groups are particularly suitable for the purposes of the present invention. Particularly suitable alcohols are hexanediol, ethylene glycol, diethylene glycol or neopentyl glycol or mixtures of two or more thereof. Particularly suitable acids are isophthalic acid and adipic acid and mixtures thereof.
In a particularly preferred embodiment of the invention, polyols used as polyol component for the production of component A are, for example, dipropylene glycol and/or polypropylene glycol with a molecular weight of about 400 to about 2500 and polyester polyols, preferably polyester polyols obtainable by polycondensation of hexanediol, ethylene glycol, diethylene glycol or neopentyl glycol or mixtures of two or more thereof and isophthalic acid or adipic acid or mixtures thereof.
High molecular weight polyester polyols include, for example, the reaction products of polyhydric, preferably dihydric, alcohols (optionally together with small quantities of trihydric alcohols) and polybasic, preferably dibasic, carboxylic acids. Instead of free polycarboxylic acids, the corresponding polycarboxylic anhydrides or corresponding polycar-boxylic acid esters with alcohols preferably containing 1 to 3 carbon atoms may also be used (where possible). The polycarboxylic acids may be aliphatic, cycloaliphatic, aromatic or heterocyclic or both. They may optionally be substituted, for example by alkyl groups, alkenyl groups, ether groups or halogens. Suitable polycarboxylic acids are, for example, succinic acid, adipic acid, suberic acid, azelaic acid, sebacic acid, phthalic acid, isophthalic acid, terephthalic acid, trimellitic acid, phthalic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, tetrachloro-phthalic anhydride, endomethylene tetrahydrophthalic anhydride, glutaric anhydride, malefic acid, malefic anhydride, fumaric acid, dimer fatty acid or trimer fatty acid or mixtures of two or more thereof. Small quantities of monofunctional fatty acids may optionally be present in the reaction mixture.
The polyesters may optionally contain a small percentage of terminal carboxyl groups. Polyesters obtainable from lactones, for example s-caprolactone, or hydroxycarboxylic acids, for example c~-hydroxycaproic acid, may also be used.
Polyacetals are also suitable polyol components. Polyacetals are compounds which can be obtained from glycols, for example diethylene glycol or hexanediol or mixtures thereof with formaldehyde. Polyacetals suitable for use in accordance with the invention may also be obtained by the polymerization of cyclic acetals.
Other suitable polyols for the production of components A and B are polycarbonates. Polycarbonates may be obtained, for example, by the reaction of diols, such as propylene glycol, butane-1,4-diol or hexane-1,6 diol, diethylene glycol, triethylene glycol or tetraethylene glycol or mixtures of two or more thereof, with diaryl carbonates, for example diphenyl carbonate, or phosgene.
OH-functional polyacrylates are also suitable polyol components for the production of component A. These polyacrylates are obtainable, for example, by the polymerization of ethylenically unsaturated monomers containing an OH group. Monomers such as these are obtainable, for example, by the esterification of ethylenically unsaturated carboxylic acids and dihydric alcohols, the alcohol generally being present in a slight excess. Ethylenically unsaturated carboxylic acids suitable for this purpose are, for example, acrylic acid, methacrylic acid, crotonic acid or malefic acid.
Corresponding OH-functional esters are, for example, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, 3-hydroxypropyl acrylate or 3-hydroxypropyl methacrylate or mixtures of two or more thereof.
To produce component A, the corresponding polyol component is reacted with an at least difunctional isocyanate. Suitable at least difunctional isocyanates for the production of component A are basically any isocyanates containing at least two isocyanate groups although, in general, compounds containing 2 to 4 isocyanate groups, more particularly 2 isocyanate groups, are preferred for the purposes of the present invention.
At least difunctional isocyanates suitable as the at least difunctional isocyanate for the production of component A are described in the following.
These at least difunctional isocyanates are, for example, ethylene diisocyanate, 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diiso-cyanate (HDI), cyclobutane-1,3-diisocyanate, cyclohexane-1,3- and -1,4-diisocyanate and mixtures of two or more thereof, 1-isocyanato-3,3,5-tri-methyl-5-isocyanatomethyl cyclohexane (isophorone diisocyanate, IPDI), 2,4- and 2,6-hexahydrotoluene diisocyanate, tetramethyl xylylene diiso-cyanate (TMXDI), 1,3- and 1,4-phenylene diisocyanate, 2,4- or 2,6-toluene diisocyanate, diphenyl methane-2,4-diisocyanate, diphenylmethane-2,2'-diisocyanate or diphenylmethane-4,4'-diisocyanate or mixtures of two or more of the diisocyanates mentioned.
According to the invention, other suitable isocyanates for the production of component A are trifunctional or higher isocyanates obtainable, for example, by oligomerization of diisocyanates. Examples of such trifunctional and higher polyisocyanates are the triisocyanurates of HDI or IPDI or mixtures thereof or mixed triisocyanurates thereof.
In one preferred embodiment of the invention, diisocyanates containing two isocyanate groups differing in their reactivity are used for the production of component A. Examples of such diisocyanates are 2,4- and 2,6-toluene diisocyanate (TDI) and isophorone diisocyanate (IPDI). With non-symmetrical diisocyanates such as these, one isocyanate group generally reacts far more quickly with isocyanate-reactive groups, for example OH groups, while the remaining isocyanate group reacts comparatively sluggishly. Accordingly, in one preferred embodiment, a monocyclic non-symmetrical diisocyanate containing two isocyanate groups differing in their reactivity, as described above, is used for the production of component A.
In one particularly preferred embodiment, 2,4- or 2,6-toluene diiso-cyanate (TDI) or a mixtures of the two isomers, but especially pure 2,4-TDI, is used for the production of component A.
Component B is produced using an at least difunctional isocyanate which ensures that at least the predominant percentage of the isocyanate groups of component B remaining after the reaction with the polyol com-ponent is more reactive than the predominant percentage of the isocyanate groups present in component A. Difunctional isocyanates of which the isocyanate groups are largely identical in their reactivity are preferably used for the production of component B. More particularly, these difunctional isocyanates are the symmetrical isocyanates, preferably the symmetrical, aromatic difunctional isocyanates. In one particularly preferred embodi-ment, the bicyclic, aromatic, symmetrical diisocyanates of the diphenyl methane series, more particularly MDI, are used for the production of component B.
A polyurethane binder with the advantages according to the invention can be produced in basically any way. However, two processes which are described hereinafter have proved to be particularly advantageous.
For example, the polyurethane binder can be directly produced by preparing component A and subsequently adding component B.
However, the compound required as component B may actually be used in the preparation of component A and may be added in such an excess that the required final content of component B is reached.
Accordingly, the present invention also relates to an at least two-stage process for the production of a low-viscosity polyurethane binder containing isocyanate groups, characterized in that (g) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least one polyol component and (h) in a second stage, another at least difunctional isocyanate or another at least difunctional isocyanate and another polyol component is/are reacted in the presence of the polyurethane prepolymer, the predominant percentage of the isocyanate groups present on completion of the first stage having a lower reactivity to isocyanate-reactive groups, more particularly to OH groups, than the isocyanate groups of the at least difunctional isocyanate added in the second stage and the OH:NCO ratio in the second stage being about 0.2 to about 0.6:1.
In principle, any of the polyols component which have already been mentioned herein may be used as the other polyol component.
In one advantageous embodiment, the OH:NCO ratio in the first stage of the process according to the invention is less than 1:1. In one preferred embodiment, the ratio of OH groups to isocyanate groups in the first stage is about 0.4 to about 0.7:1 and, more particularly, more than 0.5 to about 0.7:1.
The reaction of a polyol component with the at least difunctional isocyanate in a first stage may be carried out in any manner known to the expert under the general rules for producing polyurethanes. For example, the reaction may be carried out in the presence of solvents. Suitable solvents are, basically, any of the solvents typically used in polyurethane chemistry, more particularly esters, ketones, halogenated hydrocarbons, alkanes, alkenes and aromatic hydrocarbons. Examples of such solvents are methylene chloride, trichloroethylene, toluene, xylene, butyl acetate, amyl acetate, isobutyl acetate, methyl isobutyl ketone, methoxybutyl acetate, cyclohexane, cyclohexanone, dichlorobenzene, diethyl ketone, diisobutyl ketone, dioxane, ethyl acetate, ethylene glycol monobutyl ether acetate, ethylene glycol monoethyl acetate, 2-ethylhexyl acetate, glycol diacetate, heptane, hexane, isobutyl acetate, isooctane, isopropyl acetate, methyl ethyl ketone, tetrahydrofuran or tetrachloroethylene or mixtures of two or more of the solvents mentioned.
If the reaction components themselves are liquid or if at least one or more of the reaction components forms) a solution or dispersion of other insufficiently liquid reaction components, there is no need at all to use solvents. A solventless reaction represents a preferred embodiment of the invention.
To carry out the first stage of the process according to the invention, the polyol is introduced into a suitable vessel, optionally together with a suitable solvent, and mixed. The at least difunctional isocyanate is then added with continued mixing. To accelerate the reaction, the temperature is normally increased. In general, the reaction mixture is heated to about 40 to about 80°C. The exothermic reaction which then begins provides for an increase in the temperature. The temperature of the mixture is kept at about 70 to about 110°C, for example at about 85 to 95°C or, more parti-cularly, at about 75 to about 85°C, the temperature optionally being adjusted by suitable external measures, for example heating or cooling.
Catalysts typically used in polyurethane chemistry may optionally be added to the reaction mixture to accelerate the reaction. Dibutyl tin dilaurate or diazabicyclooctane (DABCO) is preferably added. If it is desired to use a catalyst, the catalyst is generally added to the reaction mixture in a quantity of about 0.005% by weight or about 0.01 % by weight to about 0.2% by weight, based on the mixture as a whole.
The reaction time for the first stage depends upon the polyol component used, upon the at least difunctional isocyanate used, upon the reaction temperature and upon the catalyst present, if any. The total reaction time is normally about 30 minutes to about 20 hours.
Isophorone diisocyanate (IPDI), tetramethylene xylylene diisocya-nate (TMXDI), hydrogenated diphenyl methane diisocyanate (MDIH~2) or toluene diisocyanate (TDI) or a mixture of two or more thereof is preferably used as the at least difunctional isocyanate in the first stage.
To carry out the second stage of the process according to the invention, at least one other at least difunctional isocyanate is reacted with another polyol component in admixture with component A obtained in the first stage. Any polyol from the group of polyols listed in the foregoing or a mixture of two or more thereof may be used as a constituent of the other polyol component. However, a polypropylene glycol with a molecular weight of about 400 to about 2500 or a polyester polyol with at least a high percentage and, more particularly, a predominant percentage of aliphatic dicarboxylic acids or a mixture of these polyols is preferably used as the polyol component in the second stage of the process according to the invention.
At least one polyisocyanate of which the isocyanate groups have a higher reactivity than the majority of the isocyanate groups present in the prepolymer is used as the at least difunctional isocyanate in the second stage of the process according to the invention. In other words, reactive isocyanate groups emanating from the at least difunctional isocyanate originally used for the production of prepolymer A may be present in the prepolymer, the only requirement in this connection being that the predominant percentage of the isocyanate groups present in the prepolymer A should have a lower reactivity than the isocyanate groups of the other at least difunctional isocyanate added in the second stage of the process according to the invention.
A bicyclic aromatic symmetrical diisocyanate is preferably used as the other at least difunctional isocyanate. The bicyclic isocyanates include, for example, diisocyanates of the diphenyl methane series, more particularly 2,2'-diphenyl methane diisocyanate, 2,4'-diphenyl methane diisocyanate and 4,4'-diphenyl methane diisocyanate. Of the diisocyanates mentioned, diphenyl methane diisocyanate, more particularly 4,4'-diphenyl methane diisocyanate, is particularly preferred as the other at least difunctional isocyanate for the second stage of the process according to the invention.
The other at least difunctional isocyanate is used in the second stage in a quantity of about 5 to about 95% by weight, preferably in a quantity of about 20 to about 95% by weight and more preferably in a quantity of about 40 to about 90% by weight, based on the total quantity of polyisocyanates used in all the stages of the process according to the invention.
In one preferred embodiment, the OH:NCO ratio in the second stage is about 0.2 to about 0.6:1 and, more particularly, up to about 0.5:1. By this is meant the OH:NCO ratio of the components added in the second stage excluding any isocyanate groups emanating from the prepolymer A.
However, a polyurethane binder with the advantages according to the invention can also be produced by mixing individual components C, D
and E.
Accordingly, the present invention also relates to a process for the production of a low-viscosity polyurethane binder containing isocyanate groups with a low content of readily volatile isocyanate-functional monomers by mixing three components C, D and E, characterized in that (i) an isocyanate-functional polyurethane prepolymer obtainable by reacting a polyol component with an at least difunctional isocyanate is used as component C, (j) another isocyanate-functional polyurethane prepolymer obtainable by reacting a polyol component with another at least difunctional isocyanate, of which the isocyanate groups have a higher reactivity to isocyanate-reactive groups than the isocyanate groups of component C, is used as component D
and (g) another at least difunctional isocyanate, of which the molecular weight is lower than that of components C and D and of which the isocyanate groups have a higher reactivity to isocyanate-reactive groups than the isocyanate groups of component C, is used as component E, the quantity of component E being gauged so that, on completion of mixing and after all the reactions, if any, taking place between components C, D
and E have ended, at least 5% by weight and more particularly at least 10% by weight of component E is present in the polyurethane binder.
The polyurethane binders according to the invention and the polyurethane binders produced in accordance with the invention preferably have a viscosity of less than 5000 mPas (as measured with a Brookfield RT
DVII (Thermosell), spindle 27, 20 r.p.m., 50°C).
In the context of the present invention, the expression "all the reactions, if any, taking place between components C, D and E" refers to reactions of isocyanate groups with functional groups containing isocyanate-reactive hydrogen atoms. The addition of component E, particularly when components C or D or C and D, for example, contain free OH groups, generally leads to a reaction of the isocyanate groups of component E with the free OH groups. This results in a reduction in the content of component E. Accordingly, if reactions capable of leading to a reduction in the proportion of component E are likely to occur, component E
must be added in such a quantity that, after all these reactions have ended, the required minimum quantity of component E is present in the polyure-thane binder.
Any of the polyols described above and mixtures of two or more of the polyols mentioned may be used as the polyol component for the production of components C and D in the process according to the invention. The polyol components in particular mentioned in the present specification as particularly suitable for the production of component A are also preferably used in the process according to the invention.
The foregoing observations on component B apply similarly to the at least difunctional isocyanate to be used as component E, of which the molecular weight is lower than that of components C and D and of which the isocyanate groups have a higher reactivity than the isocyanate groups of component C.
In one preferred embodiment of the invention, another at least tri-functional isocyanate may be added as component H after the two stages already described. Suitable at least trifunctional isocyanates are the poly-isocyanates containing at least three NCO groups described in the foregoing or the trimerization and polymerization products of the difunctional isocyanates mentioned above.
The polyurethane binder according to the invention and the polyure-thane binders produced in accordance with the invention are distinguished in particular by the fact that they have an extremely low content of readily volatile monomers containing isocyanate groups which is less than 2% by weight or less than 1 % by weight, less than 0.5% by weight and, more particularly, less than about 0.1 % by weight. It is particularly emphasized in this connection that the process according to the invention does not require any separate process steps for removing readily volatile diisocya-nate components.
Another advantage of the polyurethane binders produced by the process according to the invention is that they have a viscosity which lies in a very favorable range for processing. More particularly, the polyurethane binders produced by the process according to the invention have a viscosity below 5000 mPas (as measured with a Brookfield RT DVII
(Thermosell), spindle 27, 20 r.p.m., 50°C).
The polyurethane binders according to the invention are suitable for coating articles and more particularly for bonding articles either as such or in the form of solutions in organic solvents, for example in the solvents described in the foregoing.
Accordingly, the present invention also relates to the use of a polyurethane binder according to the invention or of a polyurethane binder produced by a process according to the invention in the production of adhesives, more particularly one-component and two-component adhesives, coatings, more particularly lacquers, emulsion paints and casting resins as well as moldings and for coating and, more particularly, bonding articles, more particularly for bonding films and for the production of laminated films.
The polyurethane binder according to the invention or the polyure-thane binder produced by one of the processes according to the invention is used in particular for bonding plastics and, in one particularly preferred embodiment, for laminating plastic films, plastic films metallized with metals or with metal oxides and metal foils, more particularly aluminium foils.
The curing process, i.e. the crosslinking of the individual polyure-thane binder molecules through the free isocyanate groups, may be carried out solely under the influence of atmospheric moisture, i.e. without any need to add hardeners. However, polyfunctional crosslinking agents, for example amines or, more particularly, polyfunctional alcohols, are preferably added as hardeners (two-component systems).
Film laminates made with the products produced in accordance with the invention are safe to heat-seal. This is attributable to the reduced percentage of migratable low molecular weight products in the polyure-thane binders. A favorable processing temperature for the adhesives produced in accordance with the invention in heat-sealing processes is between about 30 and about 90°C.
The present invention also relates to an adhesive containing two components F and G, (i) a polyurethane binder containing isocyanate groups according to the invention or a polyurethane binder containing isocyanate groups produced by the process according to the invention being used as component F
and (j) a compound containing at least two functional groups reactive to the isocyanate groups of component F with a molecular weight of up to 2500 or a mixture of two or more such compounds being used as component G.
Accordingly, any of the polyurethane binders according to the invention as described in the foregoing may be used as component F.
A compound containing at least two functional groups reactive to the isocyanate groups of component F with a molecular weight of up to 2500 or a mixture of two or more such compounds is preferably used as component G. The at least two functional groups reactive to the isocyanate groups of component F may be selected in particular from amino groups, mercapto groups or OH groups. Compounds suitable for use in component G may contain amino groups, mercapto groups or OH groups either individually or in admixture.
The functionality of the compounds suitable for use in component G
is generally at least about two. Component G preferably has a percentage of compounds with a higher functionality, for example with a functionality of three, four or more. The total (average) functionality of component G is for example about two (for example when only difunctional compounds are used as component G) or more, for example about 2.1, 2.2, 2.5, 2.7 or 3.
Component G may optionally have an even higher functionality, for example of about 4 or higher.
Component G preferably contains a polyol carrying at least two OH
groups. Any of the polyols mentioned in the foregoing are suitable for use in component G providing they satisfy the limiting criterion of the upper molecular weight limit.
Component G is generally used in such a quantity that the ratio of isocyanate groups of component F to functional groups reactive with isocyanate groups of component F in component G is about 5:1 to about 1:1 and, more particularly, about 2:1 to about 1:1.
The adhesive according to the invention generally has a viscosity of about 250 to about 10,000 mPas and, more particularly, in the range from about 500 to about 8000 mPas or to about 5000 mPas (Brookfield RVT
DVII, spindle 27, 20 r.p.m., 40°C).
The adhesive according to the invention may optionally contain additives. The additives may make up as much as about 30% by weight of the adhesive as a whole.
Additives suitable for use in accordance with the present invention include, for example, plasticizers, stabilizers, antioxidants, dyes, photo-stabilizers and fillers.
Suitable plasticizers are, for example, plasticizers based on phthalic acid, more particularly dialkyl phthalates, phthalic acid esters esterified with a linear alkanol containing about 6 to about 12 carbon atoms representing preferred plasticizers. Dioctyl phthalate is particularly preferred.
Other suitable plasticizers are benzoate plasticizers, for example sucrose benzoate, diethylene glycol dibenzoate and/or diethylene glycol benzoate, in which about 50 to about 95% of all the hydroxyl groups have been esterified, phosphate plasticizers, for example t-butylphenyl Biphenyl phosphate, polyethylene glycols and derivatives thereof, for example, Biphenyl ethers of polyethylene glycol), liquid resin derivatives, for example the methyl ester of hydrogenated resin, vegetable and animal oils, for example glycerol esters of fatty acids and polymerization products thereof.
Stabilizers or antioxidants suitable for use as additives in accordance with the invention include hindered phenols of high molecular weight (Mn), polyhydric phenols and sulfur- and phosphorus-containing phenols. Phenols suitable for use as additives in accordance with the invention are, for example, 1,3,5-trimethyl-2,4,6-tris-(3,5-ditert.butyl-4-hy-droxybenzyl)-benzene; pentaerythritol tetrakis-3-(3,5-ditert.butyl-4-hydroxy-phenyl)-propionate; n-octadecyl-3,5-ditert.butyl-4-hydroxyphenyl)-propion-ate; 4,4-methylene-bis-(2,6-ditert.butylphenol); 4,4-thiobis-(6-tert.butyl-o-cresol); 2,6-ditert.butylphenol; 6-(4-hydroxyphenoxy)-2,4-bis-(n-octylthio)-1,3,5-triazine; di-n-octadecyl-3,5-ditert.butyl-4-hydroxybenzyl phosphon-ates; 2-(n-octylthio)-ethyl-3,5-ditert.butyl-4-hydroxybenzoate; and sorbitol hexa-[3-(3,5-ditert.butyl-4-hydroxyphenyl)-propionate].
Suitable photostabilizers are, for example, those marketed under the name of Tinuvin~ (manufacturer: Ciba Geigy).
Other additives may be incorporated in the adhesives according to the invention in order to vary certain properties. These other additives include, for example, dyes, such as titanium dioxide, fillers, such as talcum, clay and the like. The adhesives according to the invention may optionally contain small quantities of thermoplastic polymers or copolymers, for example ethylene/vinyl acetate (EVA), ethylene/acrylic acid, ethylene/meth-acrylate and ethylene/n-butyl acrylate copolymers which optionally provide the adhesive with additional flexibility, toughness and strength. It is also possible - and preferred in accordance with the invention - to add certain hydrophilic polymers, for example polyvinyl alcohol, hydroxyethyl cellulose, hydroxypropyl cellulose, polyvinyl methyl ether, polyethylene oxide, polyvinyl pyrrolidone, polyethyl oxazolines or starch or cellulose esters, more particularly the acetates with a degree of substitution of less than 2.5, which increase the wettability of the adhesives.
The following Examples are intended to illustrate the invention without limiting it in any way.
Examples List of the abbreviations used:
DPG - dipropylene glycol PPG - polypropylene glycol TDI - toluene diisocyanate (2,4-isomer) MDI - 4,4'-diphenyl methane diisocyanate PE - polyester based on isophthalic acidladipic acid/diethylene glycolldipropylene glycol NCO - isocyanate group content OHV - OH value M - molecular weight d - day VH - laminate adhesion SNH - sealing seam adhesion OPA - oriented polyamide PEKO$$ LLDPEILDPE blend, thickness: ca. 70 pm, manufacturer:
=
Mildenberger and Willing Examples 1 to 9 were carried out by the following method:
The polyol components of the first stage were introduced first and homogeneously mixed. The isocyanate was then added and the temperature of the reaction mixture was increased to 50°C. The temperature then rose considerably as a result of the exothermic reaction between isocyanate groups and OH groups and, after reaching 90°C, was kept at that level by cooling.
The components for the second stage were added to the reaction product of the first stage and the mixture was adjusted to a temperature of 85°C, followed by stirring for another hour.
In Example 9, the first and second stages were separately produced and the resulting products were subsequently mixed.
Examples 10, 11 and 12 were carried out with isophorone diisocyanate (IPDI) as the first isocyanate component.
The results are set out in Table 1 below.
Table 1:
Examples 1 to 12 Example 1 2 3 4 5 6 O_HV Eq__u_ivalent weight 1st Stage TDI 19.0 18.1 17.1 19.6 22.0 17.1 OH:NCO ratio 0.555 0.556 0.588 0.588 0.588 0.588 Equivalents 0.218 0.208 0.196 0.2250 0.253 0.196 NCO
Equivalents 0.121 0.115 0.116 0.1323 0.149 0.116 OH
NCO:OH ratio 1.8 1.8 1.7 1.7 1.7 1.7 Final NCO 9.9 9.4 8.5 9.6 10.7 8.5 content Quantity 41.0 41.1 40.1 40.6 41.0 40.1 1st stage 2nd Stage MDI 38.8 38.3 39.7 38.6 37.1 38.2 OH: NCO ratio 0.29 0.294 0.284 0.292 0.303 0.2535 2nd stage Equivalents 0.31 0.306 0.318 0.31 0.297 0.3053 NCO 2nd stage Equivalents 0.09 0.09 0.09 0.09 0.09 0.0774 OH 2nd stage NCO:OH addition 3.44 3.40 3.53 3.43 3.29 3.94 ratio 2nd stage NCO:OH addition 2.50 2.50 2.50 2.40 2.30 - 2.60 ratio, total -Quantity, 109.8 109.3 109.8 109.2 108.1 108.2 total Final NCO 12.1 11.8 11.8 12.0 12.1 12.0 Viscos.40C: 9000 9300 5800 9370 14500 4190 Viscos.50C: 3300 3530 2220 3320 4660 1770 NCO (1d) 11.80% 12% 12.1% 12.2%
MDI 17.00% 16.0% I 17.1% 16.6%
TDI I I I 0.10% 0.10% / I 0.08% 0.09% 0.1 I I I I %1 Table 1 continued Example 7 8 911 912 913 Stage Stage Mixing SeparateSeparateof the batch batch separate batches OHV Equivalent weight 1st Stage TDI 21.7 21.7 17.1 PPG 13.5 13.5 12 PPG 25.5 25.5 8 PE 26.645 26.645 0 OH:NCO ratio 0.714 0.714 0.588 Equivalents 0.249 0.249 0.196 NCO
Equivalents 0.178 0.178 0.116 OH
NCO:OH ratio 1.4 1.4 1.77 Final NCO 3.4 3.4 8.5 content Quantity 87.3 87.3 40.1 1st stage 2nd Stage MDI 12.2 33.9 38.3 DPG 0.575 0.575 0 OH:NCO ratio 0.088 0.032 2nd stage Equivalents 0.098 0.271 0.3058 NCO 2nd stage Equivalents 0.009 0.009 0.0774 OH 2nd stage NCO:OH addition 31.67 3.95 ratio 2nd stage NCO:OH addition 2.79 3.95 ratio, total Quantity, 100.1 121.8 68.2 total Final NCO 6.7 11.5 14.1 Viscos.40C: Viscos.20000 3470 103000 1330 4600 Viscos. 50C: Viscos.7200 1420 I I 1770 NCO (1d) 7.10% 11.10% 9.00% 14.10% 12.40%
MDI I I I 28.00% 18%
TDI / / 0.80% / 0.30%
Table 1 continued Example 10 11 12 OHV Equivalent weight 1 Stage IPDI 21.1 19.3 17.1 PPG 400 256 219 10.3 10.64 10.64 PPG 1000 113 497 19.5 7.09 7.09 DPG 836 67 0 2.66 2.66 PE 218 137 410 20.4 0 0 Stanclere 0.01 0.075 0.075 TL
Equivalents 0.1905 0.1741 0.1537 NCO
Equivalents 0.1360 0.1024 0.1024 OH
Addition 1.4 1.7 1.5 ratio X:1 Final NCO 3.2 7.6 5.7 Quantity 71.3 39.7 37.4 1 st stage 2nd Stage MDI 28.1 54.6 77.1 PPG 400 0 14.4 20.304 PPG 1000 0 15.2 21.432 DPG 0.45 0 0 PE 218 0 14.9 21.009 Equivalents 0.2249 0.4371 0.6164 NCO 2nd stage Equivalents 0.0067 0.1327 0.1871 OH 2nd stage NCO:OH addition 33.56 3.29 3.30 ratio 2nd stage NCO:OH addition 2.91 2.60 2.66 ratio, total Quantity, 99.9 138.9 177.2 total Final NCO 11.5 11.4 11.4 Viscos.40C 6000 4910 5600 Viscos.50C 2800 1960 2120 NCO (24 11.55% 12.20% 12.10%
h) MDI (batch) 22.70% 20.00% 20.00%
~ IPDI (batch)~ ~ <1% ~ <1% I ~1%
~
Table 2:
Example 13 OHV Equivalent weight 1 st Stage TDI 15.7 PPG 400 265 212 9.9 PPG 1000 111 506 6.6 PPG 2000 55 1020 8.58 DPG 835 67 2.502 Equivalents NCO 0.1803 Equivalents OH 0.1054 Addition ratio X:1 1.71 Final NCO 7.3 Quantity 1 st stage 43.3 2nd Stage MDI - 31.9 PPG 400 4.104 PPG 1000 12.402 PE 218 8.208 Equivalents NCO 2nd stage 0.2552 Equivalents OH 2nd stage 0.0647 NCO:OH addition ratio 2nd 3.95 stage NCO:OH addition ratio, 2.56 total Quantity 1 st + 2nd stage 99.9 Final NCO 11.2 3rd Stage Desmodur 3300 20 Equivalents NCO 3rd stage __ 0.1026 Quantity, total 119.9 Final NCO _ ~ 12.9 Viscos. 40C 4200 mPas Color clear, yellowish Table 3: Evaluation of the lamination tests with a polyurethane binder according to Example 6.
Table 3 Laminate Quantity Web VH unprinted SNH n115 mm structure ' applied speed NI15 mm glm2 mlmin.
OPAI 1.9 100 11.6 52.1 PEKOee PE elongation Internal laminate failure OPAI 1.5 100 11.7 55.1 PEKO88 PE elongation Laminate failure in edge of sealing seam OPAI 1.1 100 11.1 55.4 PEKOeg PE elongation Laminate failure in edge of sealing seam Migration test:
The migrate content is determined as follows (see Deutsche Lebensmittel Rundschau, 87, (1991), 280-281):
A weldable laminated film bag made with the adhesive according to the invention is filled with 3% acetic acid and stored for 2 h at 70°C.
The contents of the bag are then diazotized, subjected to azo coupling with N-(1-naphthyl)-ethylenediamine and concentrated in a C~$ column. The concentration of azo dye is then photometrically determined. The results are set out in Table 4 below.
Table 4:
Results of the migration tests Migrates Laminate (after days) 01.07.97 9.7 Ng AHCU100 ml (4 days) 9.7 Ng AHCU100 ml 07.07.973.8 Ng AHCLI100 ml (10 days) 11.07.97 0.93 Ng AHCL/100 ml (14 days) 21.07.97 <0.2 Ng AHCU100 ml (24 days)
Claims (22)
1. A polyurethane binder with a low content of readily volatile isocyanate-functional monomers at least containing components A and B, characterized in that (a) a polyurethane polymer containing at least two isocyanate groups or a mixture of two or more polyurethane prepolymers containing at least two isocyanate groups is present as component A, the polyurethane prepolymer containing two isocyanate groups or the mixture of two or more polyurethane prepolymers containing isocyanate groups containing at least two differently attached types of isocyanate groups of which at least one type has a lower reactivity to isocyanate-reactive groups than the other type(s), and (b) an at least difunctional isocyanate, of which the molecular weight is lower than the molecular weight of the polyurethane prepolymers present in component A and of which the isocyanate groups have a higher reactivity to isocyanate-reactive compounds than the type of isocyanate groups of relatively low reactivity present in component A, is present as component B.
2. A polyurethane binder as claimed in claim 1, characterized in that at least 5% by weight of component B, based on the polyurethane binder as a whole, are present.
3. A polyurethane binder as claimed in claim 1 or 2, characterized in that the content of readily volatile monomers containing isocyanate groups is less than 1% by weight, the toluene diisocyanate content being less than 0.1 % by weight.
4. A polyurethane binder as claimed in any of claims 1 to 3, characterized in that an at least trifunctional isocyanate is present as component H.
5. A polyurethane binder as claimed in any of claims 1 to 4, characterized in that component A is produced by an at least two-stage reaction in which (a) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least a first polyol component, the NCO:OH ratio being smaller than 2 and free OH groups still being present in the polyurethane prepolymer, and (b) in a second stage, another at least difunctional isocyanate is reacted with the polyurethane prepolymer from the first stage, the isocyanate groups of the isocyanate added in the second stage having a higher reactivity to isocyanate-reactive compounds than at least the predominant percentage of the isocyanate groups present in the polyurethane prepolymer from the first stage.
6. A polyurethane binder as claimed in claim 5, characterized in that the other at least difunctional isocyanate is added in a molar excess, based on free OH groups of component A, the non-OH-reactive part of the other at least difunctional isocyanate representing component B.
7. A polyurethane binder as claimed in any of claims 1 to 4, characterized in that component A is produced by an at least two-stage reaction in which (c) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least a first polyol component, the NCO:OH ratio being smaller than 2 and free OH groups still being present in the polyurethane prepolymer, and (d) in a second stage, another at least difunctional isocyanate and another polyol component are reacted with the polyurethane prepolymer from the first stage, the isocyanate groups of the isocyanate added in the second stage having a higher reactivity to isocyanate-reactive compounds than at least the predominant percentage of the isocyanate groups present in the polyurethane prepolymer from the first stage.
8. A polyurethane binder as claimed in claim 7, characterized in that the other at least difunctional isocyanate is added in a molar excess, based on free OH groups of component A and the other polyol component, the non-OH-reactive part of the other at least difunctional isocyanate representing component B.
9. A polyurethane binder as claimed in any of claims 5 to 8, characterized in that the OH:NCO ratio in the second stage is 0.1:1 to less than 1:1 and, more particularly, 0.2:1 to 0.6:1.
10. A polyurethane binder as claimed in any of claims 5 to 9, characterized in that the OH:NCO ratio in the first stage is less than 1:1 and more particularly 0.5:1 to 0.7:1.
11. An at least two-stage process for the production of a low-viscosity polyurethane binder containing isocyanate groups, characterized in that (c) in a first stage, a polyurethane prepolymer is prepared from an at least difunctional isocyanate and at least one polyol component and (d) in a second stage, another at least difunctional isocyanate or another at least difunctional isocyanate and another polyol component is/are reacted in the presence of the polyurethane prepolymer, the predominant percentage of the isocyanate groups present on completion of the first stage having a lower reactivity to isocyanate-reactive groups, more particularly to OH groups, than the isocyanate groups of the at least difunctional isocyanate added in the second stage and the OH:NCO ratio in the second stage being about 0.2 to about 0.6:1.
12. A process as claimed in claim 11, characterized in that the OH:NCO
ratio in the first stage is less than 1:1 and more particularly 0.4:1 to 0.7:1.
ratio in the first stage is less than 1:1 and more particularly 0.4:1 to 0.7:1.
13. A process as claimed in claim 11 or 12, characterized in that isophorone diisocyanate (IPDI), tetramethyl xylylene diisocyanate (TMXDI), hydrogenated diphenyl methane diisocyanate (MDI H12) or toluene diisocyanate (TDI) is used as the at least difunctional isocyanate in the first stage.
14. A process as claimed in any of claims 11 to 13, characterized in that diphenyl methane diisocyanate (MD) is used as the other at least difunctional isocyanate in the second stage.
15. A process for the production of a low-viscosity polyurethane binder containing isocyanate groups with a low content of readily volatile isocyanate-functional monomers by mixing three components C, D and E, characterized in that (c) an isocyanate-functional polyurethane prepolymer obtainable by reacting a polyol component with an at least difunctional isocyanate is used as component C, (d) another isocyanate-functional polyurethane prepolymer obtainable by reacting a polyol component with another at least difunctional isocyanate, of which the isocyanate groups have a higher reactivity to isocyanate-reactive groups than the isocyanate groups of component C, is used as component D
and (g) another at least difunctional isocyanate, of which the molecular weight is lower than that of components C and D and of which the isocyanate groups have a higher reactivity to isocyanate-reactive groups than the isocyanate groups of component C, is used as component E, the quantity of component E being gauged so that, on completion of mixing and after all the reactions, if any, taking place between components C, D
and E have ended, at least 5% by weight and more particularly at least 10% by weight of component E is present in the polyurethane binder.
and (g) another at least difunctional isocyanate, of which the molecular weight is lower than that of components C and D and of which the isocyanate groups have a higher reactivity to isocyanate-reactive groups than the isocyanate groups of component C, is used as component E, the quantity of component E being gauged so that, on completion of mixing and after all the reactions, if any, taking place between components C, D
and E have ended, at least 5% by weight and more particularly at least 10% by weight of component E is present in the polyurethane binder.
16. A process as claimed in any of claims 11 to 15, characterized in that the polyurethane binder has a viscosity of less than 5000 mPas (as measured with a Brookfield RT DVII (Thermosell), spindle 27, 20 r.p.m., 50°C).
17. A process as claimed in any of claims 11 to 16, characterized in that an at least trifunctional isocyanate is added as component H in the third stage.
18. The use of the polyurethane binder claimed in any of claims 1 to 10 or produced by the process claimed in any of claims 11 to 17 in the production of adhesives, more particularly one-component and two-component adhesives, coatings, more particularly lacquers, emulsion paints and casting resins as well as moldings and for coating and, in particular, bonding articles, more particularly for bonding films and for the production of film laminates.
19. An adhesive containing two components F and G, (i) a polyurethane binder containing isocyanate groups according to any of claims 1 to 10 or a polyurethane binder containing isocyanate groups produced in accordance with any of claims 11 to 17 being used as component F
and (j) a compound containing at least two functional groups reactive to the isocyanate groups of component F with a molecular weight of up to 2500 or a mixture of two or more such compounds being used as component G.
and (j) a compound containing at least two functional groups reactive to the isocyanate groups of component F with a molecular weight of up to 2500 or a mixture of two or more such compounds being used as component G.
20. An adhesive as claimed in claim 19, characterized in that a polyol containing at least two OH groups is used as component G.
21. An adhesive as claimed in claim 19 or 20, characterized in that in that component G is used in such a quantity that the ratio of isocyanate groups of component F to functional groups reactive with isocyanate groups of component F is from 5:1 to 1:1 and more particularly from 2:1 to 1:1.
22. An adhesive as claimed in any of claims 19 to 21, characterized in that it has a viscosity of 500 to 8000 cps (Brookfield RVT DII, Spindle 27, 40°C).