CA2309233A1 - Method of making cement from tailings or rock fines containing silicate or siliceous compounds - Google Patents
Method of making cement from tailings or rock fines containing silicate or siliceous compounds Download PDFInfo
- Publication number
- CA2309233A1 CA2309233A1 CA002309233A CA2309233A CA2309233A1 CA 2309233 A1 CA2309233 A1 CA 2309233A1 CA 002309233 A CA002309233 A CA 002309233A CA 2309233 A CA2309233 A CA 2309233A CA 2309233 A1 CA2309233 A1 CA 2309233A1
- Authority
- CA
- Canada
- Prior art keywords
- tailings
- pozzolan
- cement
- portland cement
- ground
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method of making cement from tailings or rock fines containing silicate or siliceous compounds includes grinding the tailings or rock fines to a size in the range of from about -250 to about 425 mesh to produce ground pozzolan. The ground pozzolan is mixed with Type 1 normal Portland cement or Type 3 high early strength Portland cement in a ratio of at least about 0.5:1 by weight to produce a blended cement.
Description
METHOD OF MAKING CEMENT FROM TAILINGS OR ROCK FINES
CONTAINING SILICATE OR SILICEOUS COMPOUNDS
RELATED APPLICATION
This application claims priority from U.S. Provisional Patent Application No.
60/137403 filed June 1, 1999.
FIELD OF INVENTION
This invention relates to a method of making cement from tailings or rock fines containing silicate or siliceous compounds and also for recovering metals from the tailings.
BACKGROUND OF THE INVENTION
The use of supplementary cementing materials has gained wide acceptance in the construction industry since 1986. In general, supplementary cementing materials comprise natural pozzolans, fly, ash, ground granulated blast furnace slag and silica fume and they are added at the mixing plant to supplement the Portland cement in concrete.
Also, base metal (copper, nickel, lead or zinc) smelter slag can be used to produce a slag cement for use in making concrete in the manner described and claimed in US
patents 5,593,493 and 5,749,962 (Krofchak).
A natural pozzolan is a volcanic ash containing siliceous compounds. The Romans used to add burnt lime thereto to form cementitious compounds. Buildings built using such compounds still exists.
In modern times, other synthetic pozzolanic materials have been used, such as power station fly ash and silica fume from furnace operations. These materials have become so useful as supplemental additives to Portland cement that they are very sought after. Another such material is granulated blast furnace slag, Ca0 Si02, which is superior to most other pozzolanic materials.
As a result of the success of these materials, demand has created a search for further such materials. Consequently, any material having sufficient lime, alumina and silica content would be a target material for a pozzolanic supplementary material.
It has recently been realized that mine tailings have sufficient values of lime, alumina and silica, and might be a candidate as pozzolanic material. It would therefore be necessary to find a way in which mine tailings can be processed into a satisfactory pozzolanic material. If this can be accomplished, it would provide a major economic solution to dealing with mine tailings, while at the same time create a prolific source of a pozzolanic material for the cement industry.
Mine tailings or, to be more specific, mill tailings are produced by the beneficiation of ores to yield a high purity mineral for further refining. Mill tailings consist mainly of finely divided waste rock (generally siliceous compounds), usually with trace quantities of the mineral being recovered, which is too poor to be treated further, or with minerals which are uneconomical to recover. There is a danger that such minerals may have the potential of being reduced or oxidized to more hazardous materials in their finely divided state when exposed to elements in a surface disposal area.
CONTAINING SILICATE OR SILICEOUS COMPOUNDS
RELATED APPLICATION
This application claims priority from U.S. Provisional Patent Application No.
60/137403 filed June 1, 1999.
FIELD OF INVENTION
This invention relates to a method of making cement from tailings or rock fines containing silicate or siliceous compounds and also for recovering metals from the tailings.
BACKGROUND OF THE INVENTION
The use of supplementary cementing materials has gained wide acceptance in the construction industry since 1986. In general, supplementary cementing materials comprise natural pozzolans, fly, ash, ground granulated blast furnace slag and silica fume and they are added at the mixing plant to supplement the Portland cement in concrete.
Also, base metal (copper, nickel, lead or zinc) smelter slag can be used to produce a slag cement for use in making concrete in the manner described and claimed in US
patents 5,593,493 and 5,749,962 (Krofchak).
A natural pozzolan is a volcanic ash containing siliceous compounds. The Romans used to add burnt lime thereto to form cementitious compounds. Buildings built using such compounds still exists.
In modern times, other synthetic pozzolanic materials have been used, such as power station fly ash and silica fume from furnace operations. These materials have become so useful as supplemental additives to Portland cement that they are very sought after. Another such material is granulated blast furnace slag, Ca0 Si02, which is superior to most other pozzolanic materials.
As a result of the success of these materials, demand has created a search for further such materials. Consequently, any material having sufficient lime, alumina and silica content would be a target material for a pozzolanic supplementary material.
It has recently been realized that mine tailings have sufficient values of lime, alumina and silica, and might be a candidate as pozzolanic material. It would therefore be necessary to find a way in which mine tailings can be processed into a satisfactory pozzolanic material. If this can be accomplished, it would provide a major economic solution to dealing with mine tailings, while at the same time create a prolific source of a pozzolanic material for the cement industry.
Mine tailings or, to be more specific, mill tailings are produced by the beneficiation of ores to yield a high purity mineral for further refining. Mill tailings consist mainly of finely divided waste rock (generally siliceous compounds), usually with trace quantities of the mineral being recovered, which is too poor to be treated further, or with minerals which are uneconomical to recover. There is a danger that such minerals may have the potential of being reduced or oxidized to more hazardous materials in their finely divided state when exposed to elements in a surface disposal area.
The usual disposal of mill tailing comprises dumping them in slurry form into a disposal area of sufficient area to ensure that decanted water is free of suspended solids.
Over the last forty years, more and more severe restrictions on discharges from tailing disposal areas have been enacted. From essentially no restrictions, other than keeping the gangue on mine property, it is now necessary to provide an accounting of metals leaching from the tailings in parts per billion and, in some cases, in parts per million. Also, it is now sometimes required that mine/mill operations carry out water treatment on tailing discharges to meet current criteria. Of course, the above is true only of the most environmentally conscious countries, but the trend is apparent on a worldwide basis.
No one, so far as is known, has yet found a solution to the problems of the tailing ponds, and the fact that it has been found that they are leaching heavy metal values has caused mining companies to seek acceptable solutions to this growing problem.
Also, environmental authorities are requiring plans to be formulated for long-term permanent solutions.
It has now also been realized that quarry rock fines have sufficient values of lime, alumina and silica, and might be a candidate as pozzolanic material. It would therefore be necessary to find a way in which rock fines can be processed into a satisfactory pozzolanic material. If this can be accomplished, it would provide a major economic solution to dealing with waste quarry fine materials, while, at the same time, create a prolific source of a pozzolanic material for the cement industry.
Over the last forty years, more and more severe restrictions on discharges from tailing disposal areas have been enacted. From essentially no restrictions, other than keeping the gangue on mine property, it is now necessary to provide an accounting of metals leaching from the tailings in parts per billion and, in some cases, in parts per million. Also, it is now sometimes required that mine/mill operations carry out water treatment on tailing discharges to meet current criteria. Of course, the above is true only of the most environmentally conscious countries, but the trend is apparent on a worldwide basis.
No one, so far as is known, has yet found a solution to the problems of the tailing ponds, and the fact that it has been found that they are leaching heavy metal values has caused mining companies to seek acceptable solutions to this growing problem.
Also, environmental authorities are requiring plans to be formulated for long-term permanent solutions.
It has now also been realized that quarry rock fines have sufficient values of lime, alumina and silica, and might be a candidate as pozzolanic material. It would therefore be necessary to find a way in which rock fines can be processed into a satisfactory pozzolanic material. If this can be accomplished, it would provide a major economic solution to dealing with waste quarry fine materials, while, at the same time, create a prolific source of a pozzolanic material for the cement industry.
Aggregates and stones for general concrete products and other purposes such as railroad ballast or road support are provided by crushing rock from quarries.
The crushing from the host materials ends up producing as by-products fine materials (1/4"
down) that have limited uses and end up being piled beside the quarries as waste.
It is therefore an object of this invention to provide a method of using tailings or rock fines containing silicate or siliceous compounds to produce pozzolans suitable for manufacturing predictable grades of low, medium and high strength concrete for general construction purposes, including mine backfill and shotcrete, and to recover metal values from the tailings which would otherwise be lost.
SUMMARY OF INVENTION
According to the invention, a method of making cement from tailings or rock fines containing siliceous compounds comprises grinding the tailings to a size within the range of from about -250 to about 425 mesh to produce ground pozzolan, and mixing the ground pozzolan with Type 1 normal Portland cement or Type 3 high early strength Portland cement in a ratio of at least about 0.5:1 by weight to produce a blended cement.
The ground pozzolan may be mixed with the Portland cement in the range of from about 0.5:1 to about 1.75:1, preferably from about 1.25:1 to about 1.5:1. The ground pozzolan may also be mixed with the Portland cement in a ratio of up to about 2.5:1 to dispose of extra tailings or rock fines without reducing compressive strength below acceptable ASTM Standards.
The crushing from the host materials ends up producing as by-products fine materials (1/4"
down) that have limited uses and end up being piled beside the quarries as waste.
It is therefore an object of this invention to provide a method of using tailings or rock fines containing silicate or siliceous compounds to produce pozzolans suitable for manufacturing predictable grades of low, medium and high strength concrete for general construction purposes, including mine backfill and shotcrete, and to recover metal values from the tailings which would otherwise be lost.
SUMMARY OF INVENTION
According to the invention, a method of making cement from tailings or rock fines containing siliceous compounds comprises grinding the tailings to a size within the range of from about -250 to about 425 mesh to produce ground pozzolan, and mixing the ground pozzolan with Type 1 normal Portland cement or Type 3 high early strength Portland cement in a ratio of at least about 0.5:1 by weight to produce a blended cement.
The ground pozzolan may be mixed with the Portland cement in the range of from about 0.5:1 to about 1.75:1, preferably from about 1.25:1 to about 1.5:1. The ground pozzolan may also be mixed with the Portland cement in a ratio of up to about 2.5:1 to dispose of extra tailings or rock fines without reducing compressive strength below acceptable ASTM Standards.
The tailings or rock fines may contain from about 15% to about 95% Si02, from about 0 to about 35% A1203 and from about 0 to about 35% Ca0 by weight.
Appropriate amounts of sand and stone can be added in the presence of moisture to produce low, medium or high strength concrete as required. The ground pozzolan chemically reacts with calcium hydroxide released by the hydration of Portland cement to form compounds possessing cementing properties.
Metal values in ground tailing pozzolan can be separated by magnetic or gravitational separation or by other techniques known to those skilled in the art.
Such utilization of tailings to produce a pozzolan substantially completely solves the environmental disposal problem of tailings in ponds and eliminates the risk of heavy metals leaching, while at the same time providing a viable and practical use for the tailings.
Such utilization of rock fines to produce a pozzolan substantially completely solves the problem of rock fines piles, while at the same time providing a viable and practical use therefor.
Various examples of methods carried out in accordance with the present invention will now be described.
A composite sample of tailings was obtained from tailing ponds which have been accumulated for over 50 years from one of the world's largest nickel producers located in Sudbury, Ontario, Canada.
Appropriate amounts of sand and stone can be added in the presence of moisture to produce low, medium or high strength concrete as required. The ground pozzolan chemically reacts with calcium hydroxide released by the hydration of Portland cement to form compounds possessing cementing properties.
Metal values in ground tailing pozzolan can be separated by magnetic or gravitational separation or by other techniques known to those skilled in the art.
Such utilization of tailings to produce a pozzolan substantially completely solves the environmental disposal problem of tailings in ponds and eliminates the risk of heavy metals leaching, while at the same time providing a viable and practical use for the tailings.
Such utilization of rock fines to produce a pozzolan substantially completely solves the problem of rock fines piles, while at the same time providing a viable and practical use therefor.
Various examples of methods carried out in accordance with the present invention will now be described.
A composite sample of tailings was obtained from tailing ponds which have been accumulated for over 50 years from one of the world's largest nickel producers located in Sudbury, Ontario, Canada.
The sample was ground to -325 mesh to produce ground tailing pozzolan and was analyzed as follows: (by weight) Si02 49.89% Ti02 0.96% Sr (ppm) 166 AI203 12.OS% Mn0 0.17% Zr (ppm) 1?6 Fc203 18.52% P205 0.16% Co (ppm) 61 Ca0 6.21 % S 3.24% Cr (ppm) 486 Mg0 5.90% Pyrrhntite 7.14% Cu (ppm) 459 Ne20 1.74% C 0.09% Ni (ppm) 1022 1.17% Ha (ppm) 348 Zn (ppm) 24S
The ground tailing pozzolan was subjected to magnetic separation, and the pyrrhotite, which contained virtually all the metals, was recovered. The analysis of the pyrrhotite was as follows:
Si02 4.96% Ti02 0.64% Sr (ppm) 191 AI2O3 1.25% MtlO 0.05% ZT (ppm) 428 Fe2O3 77.01 % P20S 0.02% Co (ppm) 461 Ca0 0.74% Fe 53.9% Cr (ppm) 489 M$O 0.83% S 25.1% Cu (ppm) 859 Na20 0.19% Ha (ppm) 537 Ni (ppm) 7000 ~
O 0.16%
Zn (ppm) S70 The analysis of the ground tailing pozzolan after pyrrhotite removal was as follows:
Si02 53.3% Ti02 0.98% Sr (ppm) 0.003 A1203 12.89% Mn0 0.16% Zr (ppm) 0.003 Fe203 14.42% P205 0.14% Co ~) 0.001 Ca0 6.64% S 1.68% Cr Mg0 6.36% Pyrrhotite <0.002% Cu (ppm) 0.091 Na20 1.87% C 0.08% Ni (ppm) 0.02 K2O 1.2S% Ba (ppm) 0.006 Zn (ppm) 0.049 The ground tailing pozzolan, free of metals, was then blended with Type 1 normal Portland cement in different proportions and 2" concrete cubes were made in accordance with the American Society for Testing Materials (ASTM). The cubes were then tested for compressive strength at 3, 7 and 28 days and compared with the ASTM Minimum Requirements (Min. Req.).
Comprerrive Strength Test Mix Pro Com Cement onion restive In m Strea Saad t6 Tallin In s Water ri 3 da 7 do ZS
da MIe. 500 1375 -- 242.5 2103 2900 3843 Req.
#1 250 1375 250 242.5 2132 2958 4083 #2 325 1375 175 242.5 2389 3630 4701 #3 425 1375 75 242.5 2623 3927 5436 From these results, it is clear that the cubes made with the blend of the ground tailing pozzolan and Portland cement exceeded the ASTM requirements for use in concrete and mortars.
The Pozzolanic Strength Activity Index (P.S.A.L) at 28 days has to be at least 75%
of that of a control sample. The P.S.A.I. with Portland cement according to the ASTM
Standards is calculated in the following manner:
Pozzolanic Strength Activity Index with Portland cement= (A/B)x100 Where: A= average compressive strength of test mix cubes made with 80%
Portland cement and 20% by weight of the tailing cement (6163 psi) B= average compressive strength of control mix cubes (5075 psi) For the tailing cement, the P.S.A.I. = 6163/5075 x 100 = 121.4%, which is of course significantly higher than 75%.
In this example, Type 3 high early strength Portland cement was used instead of Type 1 normal Portland cement in order to obtain high strength concrete. The results are as follows:
Compraelve 9tren~th Tat Miz Pro Com reerive ortioti Strea In m h in ~1 Cement Sand Tailin Water 3 da 7 da 28 da t M~a Req.500 1375 -- 242.5 2103 2900 3843 #1 250 1375 250 242.5 2679 3277 4365 #Z 325 1375 175 242.5 3842 4637 5528 #3 425 1375 75 242.5 5029 5867 7042 Again, the results significantly exceed the ASTM requirements and show that this invention is technically very successful.
Various leach tests were carried out with broken pieces of the 2" cubes after compressive strength testing. The results are as follows:
_g_ Leach Test Tailings were leached in water/acid in accordance with the Environment Protection Agency (EPA) test standards, and the results were compared to those from the crushed cubes:
Metal Crushed cubes Tallin s Re ulations to Water Course Fe 0.006 1 _ 1.0 1 .3 1 C a 0.043 m 1 _ 0.3 1 46.02 Ni 0.011 39.01 /l 0.3 /1 Co 0.004 1 0.97 I 0.3 m 1 The tailings as they are in the lagoons showed a high leachability, while the crushed cubes made with tailing pozzolan and Portland cement leached metals safely below currently regulated limits.
A series of 300 freeze/thaw cycles were carried out on six 2" cubes having the composition of Examples 1 and 2 in order to assess their durability to resist to exposure conditions which are the most destructive factors causing deterioration of concrete. The cubes were placed in a freezer 12 hours later, i.e. thawed in water during the day and frozen in the freezer over night. After the cycles, no deterioration was visible in the form of cracking, sealing, or crumbling of the surfaces, thus demonstrating that tailing pozzolan produced concrete with good durability.
Concrete hollow blocks were made using tailing pozzolan and Type 3 high early strength Portland cement and compared with a control made with straight Type 3 high early strength Portland cement.
The results were as follows:
_ M!z , Com eve u 1 P etlon ~trrr fn l Cemeat T $and ldmeetore Watcr 1 day 9 14 x8 day doy diy in Control210 1690 11 25 501i~s2247 2451 2573 2757 Itl 178 32 1690 11 25 501itre~t2?31 2400 2563 2691 Ifl 157 53 1690 11 25 50 2159 2398 2412 2585 lions As can be seen, the concrete blocks made with a blend of tailing pozzolan and Type 3 Portland cement show comparable strength to the control.
Cylinders (4" x 8") were made for testing tailing pozzolan in mine backfill, with the following results:
Mh P ro ortlar Com h tr h realty i Strer Type 8bet TailingT1~IIInBsWater 3 day 7 day Z8 duly PortleadFWre~acePasrnleaCoawa Cee~eot~fa Coneroli167 is00 25000 11000 14 3a 7s di 133 1201 333 25000 11000 18 38 T1 The water content in the tailing was 32% in order to enable it to be pumped back to the mine without plugging the pipes, and the cement/tailing ratio was 1:15.
MI= Pro ~etlorId Cos reeelvs le t ~ Stree Type Hlast Tdilag TalNnp Water 3 y day Z8 dey 1 day p~ad Frraace PaaaoiarCoaese CenreatBla Control86 778 -- I5920 1108014 28 d3 Z
1~'t 69 622 1'f3 2'920 1108018 3D d3 The water content in the tailing was 28%, in order to enable it to be pumped to the mine without plugging the pipes, and the cement/tailing ratio was 1:30.
As can be seen, the strength results with tailing pozzolan are very satisfactory.
Various examples of rock fines from different quarries in Northern Ontario, Canada were obtained.
The samples were ground to -325 mesh and were analyzed as follows: (by weight) Si02 40-80% K20 0.5-1.5%
A1203 5-25% Ti02 0.2-2.9%
Fe203 5-20% Mn0 0.1-0.3%
Ca0 0-25% P205 0.02-0.9%
Mg0 4-12% S 0.05-1.1%
Na20 1-2% C02 0.01-2.5%
The ground rock pozzolan was then blended with Type 1 normal Portland cement and concrete prestressed slabs and pipes were made to be compared to those ones with straight Type 1 normal Portland cement.
The results were as follows:
M1: in Com t~i~, Pro sty rein Pr ~tmeedCement Sosd A~rnpt~erWater 1 d~,y p~Vp Coetrol 395 394 1184 250 6815 9937 #1 316 79 39d 1184 250 647 9895 Mi: ro Com rssalve l3trea P rtfon h in ~i In pipes Cement ~~ $aed A~re~tes Water 1 doy Z8 day p p Coptrol 198 -- 195 590 120 36x5 7395 *1 195 590 120 3590 '7302 Again the strength results between the control and the test with rock pozzolan are highly comparable.
Numerous other tests have been conducted using varying amounts of Type 1 normal Portland cement, Type 3 high early strength Portland cement, sand and different type of tailings containing siliceous compounds. Various chemical additives were also used to implement the pozzolanic properties of the tailings. All have produced satisfactory results, but more particularly, the method according to this invention has advantageously made use of the tailings to make various grades of concrete, while simultaneously solving a growing and perplexing environmental problem.
Thus, an economical and viable solution has been invented for the disposal or recycling of a waste material into a valuable raw product from which important and increasingly useful products can be made, namely concrete, shotcrete and cement for mine backfill. At the same time, the metals lost in the tailings can be recovered, thus eliminating any risk of leaching.
Other examples of the invention will be readily apparent to a person skilled in the art from the foregoing description.
U:\CLIENTS\FENICEM\H310286.CUS\04260830.OPA
April 26, 2000
The ground tailing pozzolan was subjected to magnetic separation, and the pyrrhotite, which contained virtually all the metals, was recovered. The analysis of the pyrrhotite was as follows:
Si02 4.96% Ti02 0.64% Sr (ppm) 191 AI2O3 1.25% MtlO 0.05% ZT (ppm) 428 Fe2O3 77.01 % P20S 0.02% Co (ppm) 461 Ca0 0.74% Fe 53.9% Cr (ppm) 489 M$O 0.83% S 25.1% Cu (ppm) 859 Na20 0.19% Ha (ppm) 537 Ni (ppm) 7000 ~
O 0.16%
Zn (ppm) S70 The analysis of the ground tailing pozzolan after pyrrhotite removal was as follows:
Si02 53.3% Ti02 0.98% Sr (ppm) 0.003 A1203 12.89% Mn0 0.16% Zr (ppm) 0.003 Fe203 14.42% P205 0.14% Co ~) 0.001 Ca0 6.64% S 1.68% Cr Mg0 6.36% Pyrrhotite <0.002% Cu (ppm) 0.091 Na20 1.87% C 0.08% Ni (ppm) 0.02 K2O 1.2S% Ba (ppm) 0.006 Zn (ppm) 0.049 The ground tailing pozzolan, free of metals, was then blended with Type 1 normal Portland cement in different proportions and 2" concrete cubes were made in accordance with the American Society for Testing Materials (ASTM). The cubes were then tested for compressive strength at 3, 7 and 28 days and compared with the ASTM Minimum Requirements (Min. Req.).
Comprerrive Strength Test Mix Pro Com Cement onion restive In m Strea Saad t6 Tallin In s Water ri 3 da 7 do ZS
da MIe. 500 1375 -- 242.5 2103 2900 3843 Req.
#1 250 1375 250 242.5 2132 2958 4083 #2 325 1375 175 242.5 2389 3630 4701 #3 425 1375 75 242.5 2623 3927 5436 From these results, it is clear that the cubes made with the blend of the ground tailing pozzolan and Portland cement exceeded the ASTM requirements for use in concrete and mortars.
The Pozzolanic Strength Activity Index (P.S.A.L) at 28 days has to be at least 75%
of that of a control sample. The P.S.A.I. with Portland cement according to the ASTM
Standards is calculated in the following manner:
Pozzolanic Strength Activity Index with Portland cement= (A/B)x100 Where: A= average compressive strength of test mix cubes made with 80%
Portland cement and 20% by weight of the tailing cement (6163 psi) B= average compressive strength of control mix cubes (5075 psi) For the tailing cement, the P.S.A.I. = 6163/5075 x 100 = 121.4%, which is of course significantly higher than 75%.
In this example, Type 3 high early strength Portland cement was used instead of Type 1 normal Portland cement in order to obtain high strength concrete. The results are as follows:
Compraelve 9tren~th Tat Miz Pro Com reerive ortioti Strea In m h in ~1 Cement Sand Tailin Water 3 da 7 da 28 da t M~a Req.500 1375 -- 242.5 2103 2900 3843 #1 250 1375 250 242.5 2679 3277 4365 #Z 325 1375 175 242.5 3842 4637 5528 #3 425 1375 75 242.5 5029 5867 7042 Again, the results significantly exceed the ASTM requirements and show that this invention is technically very successful.
Various leach tests were carried out with broken pieces of the 2" cubes after compressive strength testing. The results are as follows:
_g_ Leach Test Tailings were leached in water/acid in accordance with the Environment Protection Agency (EPA) test standards, and the results were compared to those from the crushed cubes:
Metal Crushed cubes Tallin s Re ulations to Water Course Fe 0.006 1 _ 1.0 1 .3 1 C a 0.043 m 1 _ 0.3 1 46.02 Ni 0.011 39.01 /l 0.3 /1 Co 0.004 1 0.97 I 0.3 m 1 The tailings as they are in the lagoons showed a high leachability, while the crushed cubes made with tailing pozzolan and Portland cement leached metals safely below currently regulated limits.
A series of 300 freeze/thaw cycles were carried out on six 2" cubes having the composition of Examples 1 and 2 in order to assess their durability to resist to exposure conditions which are the most destructive factors causing deterioration of concrete. The cubes were placed in a freezer 12 hours later, i.e. thawed in water during the day and frozen in the freezer over night. After the cycles, no deterioration was visible in the form of cracking, sealing, or crumbling of the surfaces, thus demonstrating that tailing pozzolan produced concrete with good durability.
Concrete hollow blocks were made using tailing pozzolan and Type 3 high early strength Portland cement and compared with a control made with straight Type 3 high early strength Portland cement.
The results were as follows:
_ M!z , Com eve u 1 P etlon ~trrr fn l Cemeat T $and ldmeetore Watcr 1 day 9 14 x8 day doy diy in Control210 1690 11 25 501i~s2247 2451 2573 2757 Itl 178 32 1690 11 25 501itre~t2?31 2400 2563 2691 Ifl 157 53 1690 11 25 50 2159 2398 2412 2585 lions As can be seen, the concrete blocks made with a blend of tailing pozzolan and Type 3 Portland cement show comparable strength to the control.
Cylinders (4" x 8") were made for testing tailing pozzolan in mine backfill, with the following results:
Mh P ro ortlar Com h tr h realty i Strer Type 8bet TailingT1~IIInBsWater 3 day 7 day Z8 duly PortleadFWre~acePasrnleaCoawa Cee~eot~fa Coneroli167 is00 25000 11000 14 3a 7s di 133 1201 333 25000 11000 18 38 T1 The water content in the tailing was 32% in order to enable it to be pumped back to the mine without plugging the pipes, and the cement/tailing ratio was 1:15.
MI= Pro ~etlorId Cos reeelvs le t ~ Stree Type Hlast Tdilag TalNnp Water 3 y day Z8 dey 1 day p~ad Frraace PaaaoiarCoaese CenreatBla Control86 778 -- I5920 1108014 28 d3 Z
1~'t 69 622 1'f3 2'920 1108018 3D d3 The water content in the tailing was 28%, in order to enable it to be pumped to the mine without plugging the pipes, and the cement/tailing ratio was 1:30.
As can be seen, the strength results with tailing pozzolan are very satisfactory.
Various examples of rock fines from different quarries in Northern Ontario, Canada were obtained.
The samples were ground to -325 mesh and were analyzed as follows: (by weight) Si02 40-80% K20 0.5-1.5%
A1203 5-25% Ti02 0.2-2.9%
Fe203 5-20% Mn0 0.1-0.3%
Ca0 0-25% P205 0.02-0.9%
Mg0 4-12% S 0.05-1.1%
Na20 1-2% C02 0.01-2.5%
The ground rock pozzolan was then blended with Type 1 normal Portland cement and concrete prestressed slabs and pipes were made to be compared to those ones with straight Type 1 normal Portland cement.
The results were as follows:
M1: in Com t~i~, Pro sty rein Pr ~tmeedCement Sosd A~rnpt~erWater 1 d~,y p~Vp Coetrol 395 394 1184 250 6815 9937 #1 316 79 39d 1184 250 647 9895 Mi: ro Com rssalve l3trea P rtfon h in ~i In pipes Cement ~~ $aed A~re~tes Water 1 doy Z8 day p p Coptrol 198 -- 195 590 120 36x5 7395 *1 195 590 120 3590 '7302 Again the strength results between the control and the test with rock pozzolan are highly comparable.
Numerous other tests have been conducted using varying amounts of Type 1 normal Portland cement, Type 3 high early strength Portland cement, sand and different type of tailings containing siliceous compounds. Various chemical additives were also used to implement the pozzolanic properties of the tailings. All have produced satisfactory results, but more particularly, the method according to this invention has advantageously made use of the tailings to make various grades of concrete, while simultaneously solving a growing and perplexing environmental problem.
Thus, an economical and viable solution has been invented for the disposal or recycling of a waste material into a valuable raw product from which important and increasingly useful products can be made, namely concrete, shotcrete and cement for mine backfill. At the same time, the metals lost in the tailings can be recovered, thus eliminating any risk of leaching.
Other examples of the invention will be readily apparent to a person skilled in the art from the foregoing description.
U:\CLIENTS\FENICEM\H310286.CUS\04260830.OPA
April 26, 2000
Claims (5)
1. A method of making cement from tailings or rock fines containing silicate or siliceous compounds comprising grinding the tailings or rock fines to a size in the range of from about -250 to about 425 mesh to produce ground pozzolan, and mixing the ground pozzolan with Type 1 normal Portland cement or Type 3 high early strength Portland cement in a ratio of at least about 0.5:1 by weight to produce a blended cement
2. A method according to claim 1 wherein the ground pozzolan is mixed with the Portland cement in a ratio in the range of from about 0.5:1 to about 1.75:1.
3. A method according to claim 2 wherein the ground pozzolan is mixed with a Portland cement in a ratio in the range of from about 1.25:1 to about 1.5:1.
4. A method according to claim 1 wherein the ground pozzolan is mixed with the Portland cement in a ratio of up to about 2.5:1 to dispose of extra tailings or rock fines without reducing compressive strength below acceptable ASTM Standards.
5. A method according to claim 1 wherein the tailings rock fines contain from about 15%
to about 95% SiO2, from about 0 to about 35% Al203 and from about 0 to about 35% Ca0 by weight.
7. A method according to claim 1 wherein sand, stone and water are added to the blended cement to produce concrete.
8. A method according to claim 1 including separating metal values from ground tailing pozzolan before mixing with the Portland cement.
to about 95% SiO2, from about 0 to about 35% Al203 and from about 0 to about 35% Ca0 by weight.
7. A method according to claim 1 wherein sand, stone and water are added to the blended cement to produce concrete.
8. A method according to claim 1 including separating metal values from ground tailing pozzolan before mixing with the Portland cement.