CA2289466C - Specially shaped multilayer armour - Google Patents
Specially shaped multilayer armour Download PDFInfo
- Publication number
- CA2289466C CA2289466C CA002289466A CA2289466A CA2289466C CA 2289466 C CA2289466 C CA 2289466C CA 002289466 A CA002289466 A CA 002289466A CA 2289466 A CA2289466 A CA 2289466A CA 2289466 C CA2289466 C CA 2289466C
- Authority
- CA
- Canada
- Prior art keywords
- shaped
- layers
- darts
- folded
- multilayer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Armour, in particular body armour for female wearers is made of multiple layers (30) of penetration-resistant material for example madc of polyaramid fibers, specially shaped to fit over a shaped area to be protected, e.g. the bust of a female wearer. The armour's shaped part is held in shape by a series of darts (37) in successive layers (30) of the material. Each dart in a material layer comprises a generally V-shaped section (35) whose edges (37) are joined to form the dart. The V-shaped section (35) of the material is folded on itself to form a pleat (40) which is folded over to one side of the dart (37) to form an added thickness overlaying or underlying an adjacent part of the material (30). The darts (37) are angularly offset from one another with the pleats (40) oriented in directions so that the added thickness is distributed substantially evenly, thereby avoiding bulges or stiffness and improving the wearing comfort.
Description
TITLE
SPECIALLY SHAPED MULTILAYER ARMOUR
Field of the Invention The invention relates to armour made of multiple layers of penetration-resistant material, and is particularly concerned with body armour comprising a part specially shaped to fit over a curved area of the body such as female bust, as well as its method of manufacture.
Background Art It is known to use high tenacity fibers such as polyaramid fibers in multilayer structures to provide ballistic protection in body armour. Bullet resistant vests of multilayer structure have proven very satisfactory as body armour for men and women, but difficulties have been encountered in improving comfort for female wearers by shaping the armour to adapt to the female body.
Wearer comfort and the effectiveness of the armour to prevent injury are closely related. Depending on the protection Level and the fabric type, about 10 to 50 layers of fabric are used. This produces a somewhat stiff structure that does not readily adapt to pronounced body contours, particularly over the female breast region.
If the armour does not lie in snug contact with the wearer's body, shock transmission becomes uneven and the body armour does not perform as it should. The body armour's shaped areas are particularly liable to damage by shots at a glancing angle of incidence. Moreover, female breasts are specially liable to traumatic shock injury.
Various proposals for multilayer body armour specially shaped to protect shaped areas of the body such as women's breasts have already been made. But making multilayer armour in special shapes is rendered difficult due to the fact that the layers of penetration resistant material are flexible but relatively inelastic.
Problems have therefore been encountered.
Contouring a front armour panel by joining cut panels of the fabric with overlapping seams using a special stitching pattern was proposed in U.S.
Patent 4,183,097. However, if the overlapping seams are not large enough, angle shots can penetrate the vest, whereas increasing the size of the overlapping seams creates a hard rim in a region where women need as much flexibility as possible.
U.S. Patent 4,578,821 proposed inserting a flexible multilayer ballistic panel into a front pocket of a carrier garment. This panel is held by a Velcro hook-and-pile fastener enabling adjustment to different bust sizes, but the protected area is limited and the Velcro fastener cannot ensure good ballistic performance. This system is hence suitable for low protection levels only.
U.K. Patent Specification 2,231,481 proposed a vest whose inner part has a foamed plastic material shaped to fit the breast. A shaped stiff or semi-stiff shock-absorbing sheet is added to the plastic layers and finally a multilayer ballistic pack is inserted, the entire arrangement being enclosed in a bag. With this design, the ballistic pack adapts to the shape by folding about a horizontal line. This can only be achieved by leaving large openings at the left and right sides of the chest, so protection in these side areas will be questionable. Moreover, the vest will be relatively heavy, stiff and uncomfortable to wear.
Another proposal made in U.S. Patent 5,020,157 was the use of rigid, inflexible cups made of high strength laminated polyethylene material which are worn over a woman's breast and under a conventional soft body vest to protect from injuries resulting from ballistic impact. The impact-generated pressure will nevertheless be transmitted to the cup's rim which could cause injury. In addition, the stiff cups will be uncomfortable to wear.
Shaping body armour by molding layers of aramid fabric in a PVC shell with the aid of pressure at 400-800 kPa and heat at 180-300°C has been proposed in DE-A-4423194 and in WO 96/01405. However aramid fibers have an elongation up to 4% which can lead to damage in molding. Moreover, shaping the layers stretches the fabric which would increase the gaps between the fibers and reduce ballistic efficiency. Also, this molding in a PVC shell makes the armour relatively stiff.
The above-discussed prior proposals for specially shaped multilayer body armour have therefore failed to produce a lightweight multiIayer structure which fits to the body comfortably while providing excellent ballistic protection and which can be manufactured using available equipment operating at ambient temperature.
SPECIALLY SHAPED MULTILAYER ARMOUR
Field of the Invention The invention relates to armour made of multiple layers of penetration-resistant material, and is particularly concerned with body armour comprising a part specially shaped to fit over a curved area of the body such as female bust, as well as its method of manufacture.
Background Art It is known to use high tenacity fibers such as polyaramid fibers in multilayer structures to provide ballistic protection in body armour. Bullet resistant vests of multilayer structure have proven very satisfactory as body armour for men and women, but difficulties have been encountered in improving comfort for female wearers by shaping the armour to adapt to the female body.
Wearer comfort and the effectiveness of the armour to prevent injury are closely related. Depending on the protection Level and the fabric type, about 10 to 50 layers of fabric are used. This produces a somewhat stiff structure that does not readily adapt to pronounced body contours, particularly over the female breast region.
If the armour does not lie in snug contact with the wearer's body, shock transmission becomes uneven and the body armour does not perform as it should. The body armour's shaped areas are particularly liable to damage by shots at a glancing angle of incidence. Moreover, female breasts are specially liable to traumatic shock injury.
Various proposals for multilayer body armour specially shaped to protect shaped areas of the body such as women's breasts have already been made. But making multilayer armour in special shapes is rendered difficult due to the fact that the layers of penetration resistant material are flexible but relatively inelastic.
Problems have therefore been encountered.
Contouring a front armour panel by joining cut panels of the fabric with overlapping seams using a special stitching pattern was proposed in U.S.
Patent 4,183,097. However, if the overlapping seams are not large enough, angle shots can penetrate the vest, whereas increasing the size of the overlapping seams creates a hard rim in a region where women need as much flexibility as possible.
U.S. Patent 4,578,821 proposed inserting a flexible multilayer ballistic panel into a front pocket of a carrier garment. This panel is held by a Velcro hook-and-pile fastener enabling adjustment to different bust sizes, but the protected area is limited and the Velcro fastener cannot ensure good ballistic performance. This system is hence suitable for low protection levels only.
U.K. Patent Specification 2,231,481 proposed a vest whose inner part has a foamed plastic material shaped to fit the breast. A shaped stiff or semi-stiff shock-absorbing sheet is added to the plastic layers and finally a multilayer ballistic pack is inserted, the entire arrangement being enclosed in a bag. With this design, the ballistic pack adapts to the shape by folding about a horizontal line. This can only be achieved by leaving large openings at the left and right sides of the chest, so protection in these side areas will be questionable. Moreover, the vest will be relatively heavy, stiff and uncomfortable to wear.
Another proposal made in U.S. Patent 5,020,157 was the use of rigid, inflexible cups made of high strength laminated polyethylene material which are worn over a woman's breast and under a conventional soft body vest to protect from injuries resulting from ballistic impact. The impact-generated pressure will nevertheless be transmitted to the cup's rim which could cause injury. In addition, the stiff cups will be uncomfortable to wear.
Shaping body armour by molding layers of aramid fabric in a PVC shell with the aid of pressure at 400-800 kPa and heat at 180-300°C has been proposed in DE-A-4423194 and in WO 96/01405. However aramid fibers have an elongation up to 4% which can lead to damage in molding. Moreover, shaping the layers stretches the fabric which would increase the gaps between the fibers and reduce ballistic efficiency. Also, this molding in a PVC shell makes the armour relatively stiff.
The above-discussed prior proposals for specially shaped multilayer body armour have therefore failed to produce a lightweight multiIayer structure which fits to the body comfortably while providing excellent ballistic protection and which can be manufactured using available equipment operating at ambient temperature.
,,r Summary of the Invention An object of the invention is to obviate the above-mentioned problems of the prior art and provide multilayer armour shaped specially to fit over a shaped area, which combines reliable ballistic protection and high comfort.
S It is also an object of the invention to provide a simple method for shaping such multilayer armour which does not require performance-reducing heat treatment.
These objects are achieved by a novel dart folding technique for building up layers shaped by more-or-less uniformly distributed darts in rotating (angularly offset) sequence, as described below.
The invention proposes armour, in particular body armour, which is made of multiple layers of flexible relatively inelastic penetration-resistant material specially shaped to fit over a shaped area to be protected.
By "specially shaped" is meant out-of plane parts of a three dimensional structure such as a garment.
According to the invention, the layers are held in shape by a plurality of darts in successive layers of the material. Each dart in a layer comprises a generally V-shaped section whose edges are joined to form the dart, with the V-shaped section folded on itself and folded over to one side of the dart to form an added thickness overlaying or underlying an adjacent part of the layer.
Also according to the invention, the darts are angularly offset from one another with the folded V-shaped sections oriented so that said added thickness is distributed substantially evenly.
The resulting specially shaped lightweight armour is comfortable to wear without compromising the ballistic protection. The absence of cuts in the darts means that no lines of weakness are created that could allow penetration of projectiles.
The additional thickness of the folded parts of the V-shaped sections, which is distributed substantially evenly around the shaped area, provides extra protective layers over these shaped parts where projectiles are more likely to hit at a glancing angle and cause injury. However, the excellent ballistic protection does not result from these thickened parts, but is due mainly to the fact that the design produces no weaknesses that would reduce the ballistic effectiveness of the main layers.
The shape produced this way enables a better fit to the body contour while imposing no restrictions on the extent of the protection provided by the multilayer structure. Due to their even distribution, the folded-over parts do not adversely ai~ect the flexibility and comfort of the armour. Moreover, the extra weight of the folded parts is insignificant. The body armour thus remains lightweight and comfortable to wear leading to enhanced protection against injury.
The folded V-shaped sections of material form pleats which can all be oriented in the same direction, i.e. folded to the same side. However, usually these pleats are oriented in different directions. In a preferred embodiment, pairs of the layers of material have darts at the same angular location, with their pleats oriented in opposite directions so they do not overlay one another. The layers of material forming these pairs can be adjacent to one another, but are advantageously alternate layers as this improves flexibility and comfort by avoiding jamming of the pleats that could lead to stiffness or bulges.
Angular gaps can be left between the darts where convenient so that corresponding angular gaps may be left between some or all of the angularly adjacent pleats of different layers. This can contribute to the flexibility of the shaped part, without reducing security. What is important is to angularly distribute the pleats in such a way that the extra thickness is evenly distributed, avoiding bulges or stiffness that could reduce comfort and safety.
In principle, the darts extend generally radially from at least one point or area of convergence. Usually, the darts are angularly staggered from one another around the point or area of convergence by an angle which is equal to or greater than the angle of the V-shaped sections before folding. This avoids unwanted overlapping of the edges of the folded pleats.
Each layer of material normally has one dart, or in the case of women's specially-shaped body armour, two darts arranged symmetrically on either side of the two points or areas of convergence. It is however possible for each layer of material to have more darts, for example four darts on either side of and extending above and below the two points or areas of convergence.
,., A main application of the specially shaped armour of the invention is as body armour comprising at least one part specially shaped to fit over a shaped part of the body such as a torso, a neck and/or collar area, a shoulder area, or an elbow, knee or other joint area. The body armour can be soft or relatively stiff or hard armour in the form of vests or arm or leg protection and similar apparel.
A particular application is as body armour specially shaped to fit over the bust of a female wearer, having two laterally-spaced internally concave recessed parts corresponding to the bust. In this embodiment, the darts are angularly offset around each of the two laterally-spaced recessed parts about which said added thickness is distributed substantially evenly.
In this women's specially-shaped body armour, the two laterally-spaced concave recessed parts corresponding to the bust are usually formed by darts around the upper, lower and outer edges of the recessed parts, defining a continuously shaped bust ("mono-cup") receiving the two breasts.
1 S Alternatively, two breast cups can be provided, but this is not necessary.
In this case, it would be possible to provide enough darts angularly staggered from one another so that the pleats cover substantially an entire circular area around each laterally-spaced recessed part.
The darts of this women's specially-shaped body armour extend radially from two laterally-spaced points or areas of convergence corresponding to the centers of the recessed parts, above and below the two points or areas of convergence, and preferably extending over an angle of at least about 180 degrees.
Body armour according to the invention in the form of a vest typically has front and rear panels permanently joined together or releasably secured for example by Velcro fasteners, the front panel for example being shaped to fit over the bust of a female wearer by the described novel arrangement of darts. The invention concerns both the entire vest and the front panel, which may be sold separately.
The angle of the V-shaped sections of flexible material depends on the degree of curvature required for any particular application. For most applications, the V-shaped sections will each make an angle of about 10 to 40 degrees.
For women's specially-shaped body armour, an angle of about 15 to 30 degrees, conveniently 20 to 25 degrees, is preferred as this provides the recessed parts with a shape that is suitable for most female breasts.
V-shaped sections having an angle less than 10° are possible for neck shapes, for example. When small angles are employed, special care will be taken to properly fold and position the relatively narrow pleats (half the angle of the V) to avoid creating bulges.
V-shaped sections having an angle more than 40° may be needed for elbow shapes, for example.
Usually, the assembled layers of material have at least three dart locations about each of the two laterally-spaced recessed parts. However, for some applications, two dart locations may suffice, wherein the pleats in different layers at each dart location are folded in opposite directions to spread the extra thickness of the pleats as much as possible.
An arrangement with six dart locations about each of the two laterally-spaced recessed parts has proven very satisfactory for women's vests. The maximum number of dart locations will be determined by the envisaged application and by manufacturing considerations.
The shape produced by the special arrangement of darts according to the invention can be symmetrical or asymmetrical about one or more points or areas of convergence. An asymmetric shape can be provided by an asymmetric distribution of the dart locations, and/or could involve using V-shaped sections {in the same or different layers) having different angles, or by asymmetric folding of the pleats.
As discussed in detail below, the penetration-resistant material is advantageously made of polyaramid fibers and, to improve the penetration resistance and reduce backface deformation, one or more of the layers (typically only the back andlor front layer) may be bonded to a polymer. It is also possible for the body armour to include one or more front pockets for receiving ballistic panels, or to be associated with other protective layers, to improve the ballistic performance and/or reduce back-face deformation where needed. For example, a rigid or semi-rigid front layer could be fitted.
b r ... i , The Penetration-Resistant Material Various types of fibers can be applied in the penetration-resistant material used in the multilayer body armour according to the invention such as fibers comprising a polyolefin, e.g. polyethylene, polyimide, polyester or polyaramid usually having a tenacity at least 900 MPa according to ASTM D-885, which equals approximately 7 grams/denier. To provide superior penetration-resistance, preferably the tenacity of the fibers is at least 2000 MPa according to ASTM D-885.
Polyaramid fibers are preferred because they can have the required tenacity, even surpassing the preferred 2000 MPa limit and, in addition have good chemical resistance.
The fibers can be present in the material in many forms, preferably as a knitted fabric, a woven fabric, as a uniweave structure, unidirectional structure or muiti-directional sheet {e.g. having fibers crossing over at an angle between 20 and degrees) or as a non-woven (e.g. felt) layer. Film-like sheets of penetration-resistant material are also possible.
Far reasons of manufacturing efficiency, availability and geometric strength (well defined stable structure) a woven fabric of high tenacity fibers is preferred.
The fabric construction can suitably be a plain weave made up typically from 42 x or 28 x 28 ends/cm, or 14 x 14 or 6.7 x 6.7 ends/cm, although other woven structures can equally well be used, depending on the use requirements.
The specific weight of such fabrics is generally from 0.02 to 0.5 kg/m2, preferably from 0.05 to 0.5 kg/m2 and more preferably from 0.08 to 0.3 kg/m2 in order to obtain a balance between penetration resistance and specific weight.
If the specific weight below is 0.02 kg/m2 the ballistic resistance of the fabric, even when made from polyaramid fibers, is generally unacceptable whereas if the specific weight is above 0.5 kglm2, the use of a plurality of fabric layers becomes impractical, due to weight constraints.
The fibers used have a suitable denier number (defined as the weight in grams of 9000 meters of yarn) from 0.1 to 3500, and suitably from 10 to 3500, depending on the required fabric weight/ballistic performance ratio. A fiber with a denier from 1000 to 3000 is used for less demanding applications, while for high performance/low specific weight applications, a fiber with a denier from 1 to 1000, and more particular from 50 to 1000 is preferred.
In many cases, a denier range from I to 3000 for the fibers is excellent.
The fbers can be present in uncoated form, or coated or otherwise pretreated (e.g.
pre-stretched ar meat-Heated). In case polyaratrtid fiber is used, it is generally not necessary to coat or otherwise pre-treat the, fiber other than arranging it in the appropriate woven or non-woven laye , however, in Borne cases a coating might be applied to t~.e fibers for e. temple in order to increase their bonding to a polymeric continuum.
To improve the penetration resistance and reduce backface deformation, one or more ofthe layers of the above-described fabric, typically only the back andlor fxont layer, may be bonded to s polymer layer or impregnated with a polymer in order to make use of both the properties of the Ethers and the polymeric continuum.
Such a composite described in 1?P 0 862 722 B 1 published on January 30, 2002 includes a layer carnposed of fibers having a tenacity of at feast 900 Mfa (7 gldenier} according to ASTM
D-885 bonded to a polymeric continuum having a flexural rnodulus of 42 to 1,000 MPa according to ASTM D-790, a tensile strength at break of at Least 10 MPa according to ASTM D-638 and an elongation to break of at least 100 % according to ASTM D-538.
In such composites, preferably a thermoplastic polymer is used. Suitable polymers include specifc polyethylenes, polyimide, golytther etherketonc, ionomeric resins, phenolic-modified resins, poiyescers.
Preferably the thermoplastic polymer is an ionomcric resin, more preferably an ionomeric resin containing rations selected from the group consisting of Lithium, Sodium and Zinc, in particular from 0.1 to 3°/p by weight of such eations.
Altezaatively, the thermoplastic polymer is a phenolic modified resin, in particular a phenolic-polyvinylbutyral resin.
The poiymedc ovntinuum should preferably have a tensile strength at break of at least 20 MPa and an elongation to break of at least 200°!u, more preferably aE least 300%, bout according to ASTM D-638.
The flexibility of the polymeric layer is an important factor for both the penetratiott~resistance of the composite an;d the wearing comfort of body armour incorporating one of more of the composite sheets.
'Ihe flexural modulus of the polymer is preferably between ~2 and 1000 MPa, according to ASTM D-790, in particular between 50 and 804 Ml'a.
A flexural modulus higher than 100D MPa indicates a polymer that is too Stiff to effectively withstand puncture or be worn comfortably as body armour, whereas a flexural modulus of less than 4Z MPa u~diestes a material which is too flexible to' provide any effeciive stiffness to the eotnposition for anti-stab purposes, Ari additiazlal advantage of body armow comprising; such a polymer is the reduced backfact deformation attained when a bullet hiu the body armour, Another significant property of the polymer layer is the density thereof, in particular in view of a desirable low specific weight (expressed in kg/m2 composite) for ease o_ f wear of body armour and for ease of handling and efficient engin~ring with the aim of weight reduction.
Preferably the density of the layer comprising the polymeric compound is below 2,504 kg/m3, and in particular below 1,500 kg/rn3; ionomeric polymer layers are particularly pre~etred in this respect if their density is less than 1,004 kglm3.
The polymeric continuum can be suitably applied as a layer which can be bonded at one side or at both sides to a fiber-containing .layer, depending vn the application, and in mare practical terms, on the availability of the appropriate manufacturing process. In a preferred embodiment, the fiber-containing Iayer is embedded in the polymeric continuum in order to immobilize the fibers, resulting in an extremely strong composition. The polymer and fiber layers can be bonded in a batch or continuous process, by any means known in the art, such as calendering, extrusion coating, gluing, impregnation, thermally bonding, other forms of laminating Iayexs of two different materials, or even in-situ polymerization thus forming a polymer continuum with the fibers. ' Although the continuum has been described a:~ a polymeric continuum, it is understood that such continuum serves as a reinforcement and can be a polymeric film or coating layer, a metal foil or a sheet of rubber or elastomer.
A preferred method of bonding a fiber/polymer .composite layer is thermal bonding 34 such as molding in the form of a batch process, or in the form of a continuous process, in particular by means of a belt press or calender.
When layers of such composite fiberlpolymer are included in the shaped body armour accdrding to the invention, such sheets caa he shaped using darts and folded pleats as described herein; there is no need for the application of heat dutxng this shaping process. However, it would be possible to include one or more layers of a fiberlpolymer composite pre~haped by molding.
Method of Manufacture According to another aspect of the invention, a method of manufacturing multilayer specially-shaped armour begins by providing multiple layers of flexible relatively inelastic penetration-resistant material to be assembled into the shaped armour. Each layer has fold lines defining at least one dart comprising a generally V-shaped section of the material, the darts of the different layers being angularly offset from one another around at least one point or area of convergence.
Firstly, the edges of the V-shaped sections are joined to form the darts in each layer, the layers with formed darts all having substantially the same peripheral shape for assembly into the body armour.
Usually, all of these layers are identical in shape and size. However, sometimes it may be convenient to arrange the layers with slightly different shapes or sizes, for example in order to accommodate for progressive shaping as the layers build up.
Then the multiple layers are assembled to form the shaped part with the darts of different layers angularly offset to one another and with the V-shaped sections of material folded in directions to distribute the added thickness substantially evenly around the shaped part.
This forming operation is carned out on a suitable support. To form a vest for example, the layers can be built up on a bust.
Lastly, the thus-shaped multiple layers are assembled to form the armour.
The gradual build-up of angularly offset ("rotated") darts with folded pleats in the progressive layers (from layer number 2) can be referred to as progressive contouring, as the contouring progresses during the subsequent layers up to 30, 50 or even more layers.
in this way, armour can be tailored by building it up in anatomically correct fashion. Each single layer of relatively inelastic penetration-resistant material can be shaped by folding, joining the dart, folding the pleat and building up the successive layers.
....... . . r .. . i On the one hand, it is possible to tailor garments such as vests to the measurements of individual wearers. On the other hand, shaped garments such as vests can be made so they can be adapted to fit different wearers.
The folding and fastening technique does not require special equipment or tools, but can be handled by existing procedures of modern textile cutting techniques.
An advantage of this assembly technique is that multilayer shapes can conveniently be made using relatively thin layers of the penetration-resistant material built up to a very large number of layers, say 50 layers or more. It is well known than the ballistic performance improves with the number of layers, even for the same overall thickness.
Preferably pairs of the layers of material have darts at the same angular location, and the V-shaped parts of these layers are folded in opposite directions so they do not overlay one another, the pairs of layers with darts at the same angular location preferably being assembled in alternate layers.
By this novel technique of building thick protection layers, layers are gained (at overlaps where the pleats are folded over) that provide additional protection against ballistic impact, valuable especially at shaped areas where bullets or fragments hit at an angle (non-perpendicular impact).
The edges of the V-shaped sections can be sewed together to form the darts, preferably using a polyarimid yarn. Alternatively, these edges could be joined by other means such as staples or rivets of polyaramid, or by gluing. The layers of impact-resistant material are conveniently joined by sewing.
When the layers of material are attached together, care is taken to maintain the shape and to avoid the formation of air pockets. The front panel of the body armour can be made by joining together two or more packs of layers of the penetration-resistant material shaped by assembling layers with angularly offset darts as just described.
Brief Description of the Drawings The invention will be further described by way of example with reference to the drawings, wherein:
Fig. 1 is a front perspective view of a bullet-resistant vest having a front panel specially shaped according to the invention for the vest to be worn by a female;
Figs. 2-1 to 2-12 are schematic plan views each showing one half of one layer of material, the twelve layers of Figs. 2-1 to 2-12 being shown before assembly of the successive layers to form the shaped front panel of the bullet-resistant vest of Fig.
1;
Fig. 3 illustrates the formation of a dart in one of these layers;
Figs. 4-1 to 4-4 illustrate folding of the darts of four successive layers before (or during) assembly of the layers;
Fig. 5 is a schematic plan view illustrating the angular distribution of the folded pleats; and Fig. 6 is a schematic plan view illustrating how the back panel of the body armour of Fig. 1 may be assembled.
Detailed Description Fig. 1 shows a lightweight bullet-resistant vest comprising a front panel 10, which is specially shaped to fit over the bust of a female wearer, and a back panel 20, each made from an assembly of layers of penetration-resistant material. The front panel 10 has a top breast section 14 and a lower breast section 15 shaped to form inside two laterally-spaced internally concave recessed parts corresponding to the bust. The internal layers of penetration-resistant material making up the front panel 10 are shaped by a series of anguiarly-offset darts, as will be described with reference to Figs. 2 to 4.
As shown in Fig. 1, the front and back panels 10,20 of the vest are releasably secured together by a series of Velcro fasteners, namely Velcro pile fasteners 11 at the top sides of front panel 10 that cooperate with Velcro hook fasteners carried by shoulder straps 21 fitted to back panel 20, and Velcro pile fasteners 12 at the bottom sides of front panel I O that cooperate with Velcro hook fasteners carried by side straps 22 fitted to the lower part of back panel 20. These side straps 22 carry an additional Velcro cross-piece 23 and, for added security, a belt 24 with Velcro fasteners is provided.
,,, The layers of penetration-resistant material making up the front panel 10 are enclosed between an outer cover sheet and a lining of non-penetration-resistant material. To conform this outer sheet to the shape of the front panel 10, seams 17 which extend up to and over the level of the bust are provided. However, it is emphasized that according to the invention the inside layers of penetration-resistant material have no cuts, but are assembled by a series of anguiarly-offset darts having folded pleats, as described below with reference to Figs. 2 to 4.
If desired, the outside cover sheet can have a dart with a folded pleat, like those of the inside layers of penetration-resistant material.
Figs. 2-1 to 2-I2 each show the right-hand half of one of twelve layers 30 of penetration-resistant material before assembly of the successive layers to form the shaped front panel 10 of the bullet-resistant vest of Fig. 1. The other half of each layer 30 is a mirror image about the line X. The lines shown inside the perimeter of each layer 30 are only indications serving to locate the folding and joining lines.
Each layer 30 has two side extensions 31 (corresponding to the parts of the front panel 10 that fit around the wearer's waist), side recesses 32 (corresponding to the parts of the front panel I 0 that fit under the wearer's arms), rounded upper parts 33 (corresponding to the parts of the front panel 10 that cover the wearer's upper breast, i.e. where the fasteners I 1 are attached), and a concave top 34 (corresponding to the part of the front panel 10 that fits around the wearer's neck).
Each half of the layer 30 also has a V-shaped section 35 having a central fold line 36 about which it can be folded and joined to form a dart as illustrated in Fig. 3.
This Figure shows a layer corresponding to that of Fig. 2-1 or Fig. 2-3. As shown, the layer 30 is folded about a vertical fold line 38 coincident with the fold line 36, whereupon the layer 30 can be joined by sewing or stapling along the lines 37 defining the V-shaped section 35, to form a dart along the joined lines 37, leaving a pleat 40 which consists of the V-shaped section 35 folded over on itself.
As shown for the layers 30 of Figs. 4-1 to 4-4, when two darts 37 are formed in the right and left parts of each layer 30, the outer perimeter of the layer 30 adopts a shape which is essentially the same for all of the layers and corresponds to the peripheral shape of the front panel 10. The successive layers 30 can however have different sizes and shapes as a function of the shape to be built up.
By comparing Figs. 2-1 to 2-I2, it can be seen that the successive layers have darts 37 which are angularly offset from one another around a point of convergence 39, each sheet 30 having two laterally-spaced points of convergence 39 corresponding to the centers of the recessed parts in the front panel 10 that are adapted to receive the wearer's breast. These points of convergence 39 are approximately at the same locations for all twelve layers 30. It is understood that the pointed ends of the darts 37 could be distributed around an area of convergence, e.g. a circular area that as a result is not folded. Such area will be sufficiently large to avoid twisting and unwanted "doubling up" at a point of convergence.
I O Alternate pairs of the layers 30 of material - namely those of Figs. 2-1 and 2-3; 2-2 and 2-4; 2-5 and 2-7; 2-6 and 2-8; 2-9 and 2-11; 2-10 and 2-12 - are identical so the darts 37 of the layers of each pair are located at the same angular location.
The darts 37 of the successive layers (Figs. 2-1, 2-2, 2-3 and so on) are angularly offset to one another. Those of Figs. 2-1, 2-2 and Figs. 2-3, 2-4 are at 180 degrees to one another; those of the other successive layers are at different angles represented on Figs. 2-5 to 2-12 by the fold lines 36. Generally, the darts 37 in the odd-numbered layers are located on the upper part and those in the even-numbered layers are located on the lower part of its layer 30, except for the layer 30 of Fig. 2-10 where the dart is located in the middle.
In this given example, the angle of the V between the lines 37 forming each dart is about 22.5 degrees, so the six darts placed side by side would extend over 135 degrees. However, it can be seen that overall the darts 37 extend over an angle of about 195 degrees, starting at one extremity at the top from the darts 37 of Figs. 2-9 and 2-I 1, to the darts 37 of Figs. 2-2 and 2-4 at the other extremity at the bottom, there being a gap between the other darts 37 - see Fig. S.
As illustrated in Figs. 4-1 to 4-4, the pleats 40 associated with darts 37 are folded in alternate directions in order to achieve the best possible distribution of their extra thickness when the layers 30 are assembled. Each pleat 40 occupies 1/2 the width of the V-shaped sections and these pleats 40 are selectively folded in alternate directions.
In Fig. 4-1 the left pleat 40 in the top of the frst layer 30 is folded to the right and the right pleat 40 is folded to the left. Likewise, in Fig. 4-2, the left pleat 40 in the lower part of the second layer 30 is folded to the right and the right pleat 40 is folded to the left.
For the corresponding next two layers of Figs. 4-3 and 4-4, the folding of the con esponding pleats 40 is inverted, i.e. for the third and fourth layers 30 the left pleats 40 are folded to the left and the right pleats 40 are folded to the right.
The same pattern of inverting the folding of the pleats 40 is followed in the S subsequent groups of pairs of layers 30. The principle is that the pleats 40 in darts 37 located at the same location in alternating layers - like those in Figs. 2-S and 2-7 and in Figs. 2-6 and 2-8 for example - will be folded in opposite directions so that when the layers 30 are assembled these pleats 40 will not overlay one another (see Fig. S). This folding of the pleats 40 can be done when the darts 37 are formed, or when the layers 30 are being assembled.
The layers 30 with their darts 37 are then assembled successively on a bust, with the pleats 40 of the successive layers folded as described above. Each layer 30 is adjusted onto the next (or previous) one by means of needles. The same process is repeated for all twelve layers 30, laying the pleats 40 in the selected directions on 1 S top of the layer 30, except for the last layer where the pleats can be turned inside to have a smooth outer surface.
The assembled and shaped layers 30 are held in clamps and sewed (or otherwise secured together) around their periphery, taking care to maintain the shape during sewing and pressing out air to avoid the formation of air pockets. For this, it is preferable not to sew continuously around the periphery, but to sew peripheral sections one at a time, starting at the rounded upper parts 33 and finishing at the lower corners. If desired, the part corresponding to the waist can be taken in to provide a better shape.
Thanks to the darts 37, the assembled layers 30 are shaped to form two laterally-2S spaced recessed parts in a mono-cup configuration adapted to fit over the wearer's breasts, and the pleats 40 in the various layers 30 are oriented in directions so that the added thickness is distributed substantially evenly around the shaped parts, avoiding any bulges or stiffness.
Fig. S schematically illustrates the angular distribution of the pleats 40 in the assembled pack. In this Figure the pleats 40 are identified by the number L1 to L12 of their respective layer 30 conesponding to Figs. 2-1 to 2-12. In this example, proceeding clockwise, the pleats L 11-L9, L3-L 1, L7-LS, L 12-L 10, L6-L8 and L4 are arranged together in pairs folded in opposite directions about the lines forming their darts 37. The pleats L1-L7, LS-L12, L10-L6 and L8-L2 are all IS
angularly spaced apart from one another by expanses of the layer 30 that are not covered by pleats.
Due to the angular staggering of the darts 37 and the selective orientation of the pleats 40, no pleats in the pack overlap one another. Moreover, pleats 40 whose external edges coincide angularly with one another - in this example L3 and L9 -are separated by a non-pleated part of at least one intermediate layer 30 -namely layers L4-L8 - so there is no risk of interference between pleats 40 that could cause jamming or bulge formation.
In the final assembly, the pleats 40 are evenly distributed around the outer parts of the mono-cup recesses, providing two extra protective layers in this sensitive zone in the locations covered by the pleats 40.
If it is desired to have two extra protective areas over the uncovered areas in Fig. 5, this can be achieved simply by including extra layers in the pack with darts at the desired extra locations.
The front panel i 0 of Fig. 1 can be made by fitting together a chosen number of packs of the twelve layers 30 assembled as described, e.g, two packs making up a 24-layer panel or three packs making up a 36-layer panel, and so on. It is also possible to make fractional assemblies, e.g. two and a half packs making up a layer panel.
Fig. 6 shows how layers of penetration-resistant material can be assembled to form the back panel 20 of Fig. 1. Here, layers 50 shaped to form the back panel 20 are placed together, curved to the back's shape then sewn or otherwise attached together. All layers 50 except the last five are sewed together around their periphery at 51 and crosswise at 52. The last five layers 50 (which will be those closest the body} are sewed together only around the periphery at 51. Then the packs are stitched together only in the top and side regions of the periphery 51.
The front and back panels 10,20 are then enclosed in their respective cover layer and lining, and the Velcro fasteners and straps fitted.
Example The shaped front panel of a bullet-resistant vest was manufactured as described above with 30 layers of Kevlar~ Style 363F fabric sewed using 930 dtex Kevlar~
__.._... ~.._. ........ ...._. ~ . ~ , ~
sewing yarn. Kevlar~ is a DuPont Registered Trademark. The layers were assembled on a bust measuring 94-64-97 cm (size 42). The finished shaped front panel was mounted on a Plastilina backing material and subjected to standard ballistic tests. Bullets were aimed at the tip, flank and border of the curved breast part under standard conditions. All bullets were stopped within the first half of the pack, which is an indication of good ballistic design. Moreover, the backface deformation on the Plastilina was satisfactory.
Legend L 1-L 12 Layers 10 front panel 11 Velcro pile fastener 12 Velcro pile fastener 14 top breast section 15 lower breast section 16 side extension 17 seam back panel 15 21 top straps 22 Iower straps 23 cross-piece 24 belt 30 Iayer of material cut to shape 31 side extension 32 arm recess 33 upper breast cover 34 neck V-shaped section of material 36 fold line 37 joining line 38 vertical fold line 30 39 point or area of convergence V-shaped pleat (folded over) back layer 51 periphery 35 52 crosswise sewing FIG.1 FIG. 2-1 FIG. 2-2 FIG. 2-3 FIG.2-4 FIG. 2-5 FIG. 2-6 FIG. 2-7 FIG. 2-8 FIG.2-9 FIG. 2-10 FIG. 2-11 FIG. 2-12 FIG. 3 FIG.4-1 FIG. 4-2 FIG. 4-3 FIG. 4-4 FIG. 5 FIG. 6
S It is also an object of the invention to provide a simple method for shaping such multilayer armour which does not require performance-reducing heat treatment.
These objects are achieved by a novel dart folding technique for building up layers shaped by more-or-less uniformly distributed darts in rotating (angularly offset) sequence, as described below.
The invention proposes armour, in particular body armour, which is made of multiple layers of flexible relatively inelastic penetration-resistant material specially shaped to fit over a shaped area to be protected.
By "specially shaped" is meant out-of plane parts of a three dimensional structure such as a garment.
According to the invention, the layers are held in shape by a plurality of darts in successive layers of the material. Each dart in a layer comprises a generally V-shaped section whose edges are joined to form the dart, with the V-shaped section folded on itself and folded over to one side of the dart to form an added thickness overlaying or underlying an adjacent part of the layer.
Also according to the invention, the darts are angularly offset from one another with the folded V-shaped sections oriented so that said added thickness is distributed substantially evenly.
The resulting specially shaped lightweight armour is comfortable to wear without compromising the ballistic protection. The absence of cuts in the darts means that no lines of weakness are created that could allow penetration of projectiles.
The additional thickness of the folded parts of the V-shaped sections, which is distributed substantially evenly around the shaped area, provides extra protective layers over these shaped parts where projectiles are more likely to hit at a glancing angle and cause injury. However, the excellent ballistic protection does not result from these thickened parts, but is due mainly to the fact that the design produces no weaknesses that would reduce the ballistic effectiveness of the main layers.
The shape produced this way enables a better fit to the body contour while imposing no restrictions on the extent of the protection provided by the multilayer structure. Due to their even distribution, the folded-over parts do not adversely ai~ect the flexibility and comfort of the armour. Moreover, the extra weight of the folded parts is insignificant. The body armour thus remains lightweight and comfortable to wear leading to enhanced protection against injury.
The folded V-shaped sections of material form pleats which can all be oriented in the same direction, i.e. folded to the same side. However, usually these pleats are oriented in different directions. In a preferred embodiment, pairs of the layers of material have darts at the same angular location, with their pleats oriented in opposite directions so they do not overlay one another. The layers of material forming these pairs can be adjacent to one another, but are advantageously alternate layers as this improves flexibility and comfort by avoiding jamming of the pleats that could lead to stiffness or bulges.
Angular gaps can be left between the darts where convenient so that corresponding angular gaps may be left between some or all of the angularly adjacent pleats of different layers. This can contribute to the flexibility of the shaped part, without reducing security. What is important is to angularly distribute the pleats in such a way that the extra thickness is evenly distributed, avoiding bulges or stiffness that could reduce comfort and safety.
In principle, the darts extend generally radially from at least one point or area of convergence. Usually, the darts are angularly staggered from one another around the point or area of convergence by an angle which is equal to or greater than the angle of the V-shaped sections before folding. This avoids unwanted overlapping of the edges of the folded pleats.
Each layer of material normally has one dart, or in the case of women's specially-shaped body armour, two darts arranged symmetrically on either side of the two points or areas of convergence. It is however possible for each layer of material to have more darts, for example four darts on either side of and extending above and below the two points or areas of convergence.
,., A main application of the specially shaped armour of the invention is as body armour comprising at least one part specially shaped to fit over a shaped part of the body such as a torso, a neck and/or collar area, a shoulder area, or an elbow, knee or other joint area. The body armour can be soft or relatively stiff or hard armour in the form of vests or arm or leg protection and similar apparel.
A particular application is as body armour specially shaped to fit over the bust of a female wearer, having two laterally-spaced internally concave recessed parts corresponding to the bust. In this embodiment, the darts are angularly offset around each of the two laterally-spaced recessed parts about which said added thickness is distributed substantially evenly.
In this women's specially-shaped body armour, the two laterally-spaced concave recessed parts corresponding to the bust are usually formed by darts around the upper, lower and outer edges of the recessed parts, defining a continuously shaped bust ("mono-cup") receiving the two breasts.
1 S Alternatively, two breast cups can be provided, but this is not necessary.
In this case, it would be possible to provide enough darts angularly staggered from one another so that the pleats cover substantially an entire circular area around each laterally-spaced recessed part.
The darts of this women's specially-shaped body armour extend radially from two laterally-spaced points or areas of convergence corresponding to the centers of the recessed parts, above and below the two points or areas of convergence, and preferably extending over an angle of at least about 180 degrees.
Body armour according to the invention in the form of a vest typically has front and rear panels permanently joined together or releasably secured for example by Velcro fasteners, the front panel for example being shaped to fit over the bust of a female wearer by the described novel arrangement of darts. The invention concerns both the entire vest and the front panel, which may be sold separately.
The angle of the V-shaped sections of flexible material depends on the degree of curvature required for any particular application. For most applications, the V-shaped sections will each make an angle of about 10 to 40 degrees.
For women's specially-shaped body armour, an angle of about 15 to 30 degrees, conveniently 20 to 25 degrees, is preferred as this provides the recessed parts with a shape that is suitable for most female breasts.
V-shaped sections having an angle less than 10° are possible for neck shapes, for example. When small angles are employed, special care will be taken to properly fold and position the relatively narrow pleats (half the angle of the V) to avoid creating bulges.
V-shaped sections having an angle more than 40° may be needed for elbow shapes, for example.
Usually, the assembled layers of material have at least three dart locations about each of the two laterally-spaced recessed parts. However, for some applications, two dart locations may suffice, wherein the pleats in different layers at each dart location are folded in opposite directions to spread the extra thickness of the pleats as much as possible.
An arrangement with six dart locations about each of the two laterally-spaced recessed parts has proven very satisfactory for women's vests. The maximum number of dart locations will be determined by the envisaged application and by manufacturing considerations.
The shape produced by the special arrangement of darts according to the invention can be symmetrical or asymmetrical about one or more points or areas of convergence. An asymmetric shape can be provided by an asymmetric distribution of the dart locations, and/or could involve using V-shaped sections {in the same or different layers) having different angles, or by asymmetric folding of the pleats.
As discussed in detail below, the penetration-resistant material is advantageously made of polyaramid fibers and, to improve the penetration resistance and reduce backface deformation, one or more of the layers (typically only the back andlor front layer) may be bonded to a polymer. It is also possible for the body armour to include one or more front pockets for receiving ballistic panels, or to be associated with other protective layers, to improve the ballistic performance and/or reduce back-face deformation where needed. For example, a rigid or semi-rigid front layer could be fitted.
b r ... i , The Penetration-Resistant Material Various types of fibers can be applied in the penetration-resistant material used in the multilayer body armour according to the invention such as fibers comprising a polyolefin, e.g. polyethylene, polyimide, polyester or polyaramid usually having a tenacity at least 900 MPa according to ASTM D-885, which equals approximately 7 grams/denier. To provide superior penetration-resistance, preferably the tenacity of the fibers is at least 2000 MPa according to ASTM D-885.
Polyaramid fibers are preferred because they can have the required tenacity, even surpassing the preferred 2000 MPa limit and, in addition have good chemical resistance.
The fibers can be present in the material in many forms, preferably as a knitted fabric, a woven fabric, as a uniweave structure, unidirectional structure or muiti-directional sheet {e.g. having fibers crossing over at an angle between 20 and degrees) or as a non-woven (e.g. felt) layer. Film-like sheets of penetration-resistant material are also possible.
Far reasons of manufacturing efficiency, availability and geometric strength (well defined stable structure) a woven fabric of high tenacity fibers is preferred.
The fabric construction can suitably be a plain weave made up typically from 42 x or 28 x 28 ends/cm, or 14 x 14 or 6.7 x 6.7 ends/cm, although other woven structures can equally well be used, depending on the use requirements.
The specific weight of such fabrics is generally from 0.02 to 0.5 kg/m2, preferably from 0.05 to 0.5 kg/m2 and more preferably from 0.08 to 0.3 kg/m2 in order to obtain a balance between penetration resistance and specific weight.
If the specific weight below is 0.02 kg/m2 the ballistic resistance of the fabric, even when made from polyaramid fibers, is generally unacceptable whereas if the specific weight is above 0.5 kglm2, the use of a plurality of fabric layers becomes impractical, due to weight constraints.
The fibers used have a suitable denier number (defined as the weight in grams of 9000 meters of yarn) from 0.1 to 3500, and suitably from 10 to 3500, depending on the required fabric weight/ballistic performance ratio. A fiber with a denier from 1000 to 3000 is used for less demanding applications, while for high performance/low specific weight applications, a fiber with a denier from 1 to 1000, and more particular from 50 to 1000 is preferred.
In many cases, a denier range from I to 3000 for the fibers is excellent.
The fbers can be present in uncoated form, or coated or otherwise pretreated (e.g.
pre-stretched ar meat-Heated). In case polyaratrtid fiber is used, it is generally not necessary to coat or otherwise pre-treat the, fiber other than arranging it in the appropriate woven or non-woven laye , however, in Borne cases a coating might be applied to t~.e fibers for e. temple in order to increase their bonding to a polymeric continuum.
To improve the penetration resistance and reduce backface deformation, one or more ofthe layers of the above-described fabric, typically only the back andlor fxont layer, may be bonded to s polymer layer or impregnated with a polymer in order to make use of both the properties of the Ethers and the polymeric continuum.
Such a composite described in 1?P 0 862 722 B 1 published on January 30, 2002 includes a layer carnposed of fibers having a tenacity of at feast 900 Mfa (7 gldenier} according to ASTM
D-885 bonded to a polymeric continuum having a flexural rnodulus of 42 to 1,000 MPa according to ASTM D-790, a tensile strength at break of at Least 10 MPa according to ASTM D-638 and an elongation to break of at least 100 % according to ASTM D-538.
In such composites, preferably a thermoplastic polymer is used. Suitable polymers include specifc polyethylenes, polyimide, golytther etherketonc, ionomeric resins, phenolic-modified resins, poiyescers.
Preferably the thermoplastic polymer is an ionomcric resin, more preferably an ionomeric resin containing rations selected from the group consisting of Lithium, Sodium and Zinc, in particular from 0.1 to 3°/p by weight of such eations.
Altezaatively, the thermoplastic polymer is a phenolic modified resin, in particular a phenolic-polyvinylbutyral resin.
The poiymedc ovntinuum should preferably have a tensile strength at break of at least 20 MPa and an elongation to break of at least 200°!u, more preferably aE least 300%, bout according to ASTM D-638.
The flexibility of the polymeric layer is an important factor for both the penetratiott~resistance of the composite an;d the wearing comfort of body armour incorporating one of more of the composite sheets.
'Ihe flexural modulus of the polymer is preferably between ~2 and 1000 MPa, according to ASTM D-790, in particular between 50 and 804 Ml'a.
A flexural modulus higher than 100D MPa indicates a polymer that is too Stiff to effectively withstand puncture or be worn comfortably as body armour, whereas a flexural modulus of less than 4Z MPa u~diestes a material which is too flexible to' provide any effeciive stiffness to the eotnposition for anti-stab purposes, Ari additiazlal advantage of body armow comprising; such a polymer is the reduced backfact deformation attained when a bullet hiu the body armour, Another significant property of the polymer layer is the density thereof, in particular in view of a desirable low specific weight (expressed in kg/m2 composite) for ease o_ f wear of body armour and for ease of handling and efficient engin~ring with the aim of weight reduction.
Preferably the density of the layer comprising the polymeric compound is below 2,504 kg/m3, and in particular below 1,500 kg/rn3; ionomeric polymer layers are particularly pre~etred in this respect if their density is less than 1,004 kglm3.
The polymeric continuum can be suitably applied as a layer which can be bonded at one side or at both sides to a fiber-containing .layer, depending vn the application, and in mare practical terms, on the availability of the appropriate manufacturing process. In a preferred embodiment, the fiber-containing Iayer is embedded in the polymeric continuum in order to immobilize the fibers, resulting in an extremely strong composition. The polymer and fiber layers can be bonded in a batch or continuous process, by any means known in the art, such as calendering, extrusion coating, gluing, impregnation, thermally bonding, other forms of laminating Iayexs of two different materials, or even in-situ polymerization thus forming a polymer continuum with the fibers. ' Although the continuum has been described a:~ a polymeric continuum, it is understood that such continuum serves as a reinforcement and can be a polymeric film or coating layer, a metal foil or a sheet of rubber or elastomer.
A preferred method of bonding a fiber/polymer .composite layer is thermal bonding 34 such as molding in the form of a batch process, or in the form of a continuous process, in particular by means of a belt press or calender.
When layers of such composite fiberlpolymer are included in the shaped body armour accdrding to the invention, such sheets caa he shaped using darts and folded pleats as described herein; there is no need for the application of heat dutxng this shaping process. However, it would be possible to include one or more layers of a fiberlpolymer composite pre~haped by molding.
Method of Manufacture According to another aspect of the invention, a method of manufacturing multilayer specially-shaped armour begins by providing multiple layers of flexible relatively inelastic penetration-resistant material to be assembled into the shaped armour. Each layer has fold lines defining at least one dart comprising a generally V-shaped section of the material, the darts of the different layers being angularly offset from one another around at least one point or area of convergence.
Firstly, the edges of the V-shaped sections are joined to form the darts in each layer, the layers with formed darts all having substantially the same peripheral shape for assembly into the body armour.
Usually, all of these layers are identical in shape and size. However, sometimes it may be convenient to arrange the layers with slightly different shapes or sizes, for example in order to accommodate for progressive shaping as the layers build up.
Then the multiple layers are assembled to form the shaped part with the darts of different layers angularly offset to one another and with the V-shaped sections of material folded in directions to distribute the added thickness substantially evenly around the shaped part.
This forming operation is carned out on a suitable support. To form a vest for example, the layers can be built up on a bust.
Lastly, the thus-shaped multiple layers are assembled to form the armour.
The gradual build-up of angularly offset ("rotated") darts with folded pleats in the progressive layers (from layer number 2) can be referred to as progressive contouring, as the contouring progresses during the subsequent layers up to 30, 50 or even more layers.
in this way, armour can be tailored by building it up in anatomically correct fashion. Each single layer of relatively inelastic penetration-resistant material can be shaped by folding, joining the dart, folding the pleat and building up the successive layers.
....... . . r .. . i On the one hand, it is possible to tailor garments such as vests to the measurements of individual wearers. On the other hand, shaped garments such as vests can be made so they can be adapted to fit different wearers.
The folding and fastening technique does not require special equipment or tools, but can be handled by existing procedures of modern textile cutting techniques.
An advantage of this assembly technique is that multilayer shapes can conveniently be made using relatively thin layers of the penetration-resistant material built up to a very large number of layers, say 50 layers or more. It is well known than the ballistic performance improves with the number of layers, even for the same overall thickness.
Preferably pairs of the layers of material have darts at the same angular location, and the V-shaped parts of these layers are folded in opposite directions so they do not overlay one another, the pairs of layers with darts at the same angular location preferably being assembled in alternate layers.
By this novel technique of building thick protection layers, layers are gained (at overlaps where the pleats are folded over) that provide additional protection against ballistic impact, valuable especially at shaped areas where bullets or fragments hit at an angle (non-perpendicular impact).
The edges of the V-shaped sections can be sewed together to form the darts, preferably using a polyarimid yarn. Alternatively, these edges could be joined by other means such as staples or rivets of polyaramid, or by gluing. The layers of impact-resistant material are conveniently joined by sewing.
When the layers of material are attached together, care is taken to maintain the shape and to avoid the formation of air pockets. The front panel of the body armour can be made by joining together two or more packs of layers of the penetration-resistant material shaped by assembling layers with angularly offset darts as just described.
Brief Description of the Drawings The invention will be further described by way of example with reference to the drawings, wherein:
Fig. 1 is a front perspective view of a bullet-resistant vest having a front panel specially shaped according to the invention for the vest to be worn by a female;
Figs. 2-1 to 2-12 are schematic plan views each showing one half of one layer of material, the twelve layers of Figs. 2-1 to 2-12 being shown before assembly of the successive layers to form the shaped front panel of the bullet-resistant vest of Fig.
1;
Fig. 3 illustrates the formation of a dart in one of these layers;
Figs. 4-1 to 4-4 illustrate folding of the darts of four successive layers before (or during) assembly of the layers;
Fig. 5 is a schematic plan view illustrating the angular distribution of the folded pleats; and Fig. 6 is a schematic plan view illustrating how the back panel of the body armour of Fig. 1 may be assembled.
Detailed Description Fig. 1 shows a lightweight bullet-resistant vest comprising a front panel 10, which is specially shaped to fit over the bust of a female wearer, and a back panel 20, each made from an assembly of layers of penetration-resistant material. The front panel 10 has a top breast section 14 and a lower breast section 15 shaped to form inside two laterally-spaced internally concave recessed parts corresponding to the bust. The internal layers of penetration-resistant material making up the front panel 10 are shaped by a series of anguiarly-offset darts, as will be described with reference to Figs. 2 to 4.
As shown in Fig. 1, the front and back panels 10,20 of the vest are releasably secured together by a series of Velcro fasteners, namely Velcro pile fasteners 11 at the top sides of front panel 10 that cooperate with Velcro hook fasteners carried by shoulder straps 21 fitted to back panel 20, and Velcro pile fasteners 12 at the bottom sides of front panel I O that cooperate with Velcro hook fasteners carried by side straps 22 fitted to the lower part of back panel 20. These side straps 22 carry an additional Velcro cross-piece 23 and, for added security, a belt 24 with Velcro fasteners is provided.
,,, The layers of penetration-resistant material making up the front panel 10 are enclosed between an outer cover sheet and a lining of non-penetration-resistant material. To conform this outer sheet to the shape of the front panel 10, seams 17 which extend up to and over the level of the bust are provided. However, it is emphasized that according to the invention the inside layers of penetration-resistant material have no cuts, but are assembled by a series of anguiarly-offset darts having folded pleats, as described below with reference to Figs. 2 to 4.
If desired, the outside cover sheet can have a dart with a folded pleat, like those of the inside layers of penetration-resistant material.
Figs. 2-1 to 2-I2 each show the right-hand half of one of twelve layers 30 of penetration-resistant material before assembly of the successive layers to form the shaped front panel 10 of the bullet-resistant vest of Fig. 1. The other half of each layer 30 is a mirror image about the line X. The lines shown inside the perimeter of each layer 30 are only indications serving to locate the folding and joining lines.
Each layer 30 has two side extensions 31 (corresponding to the parts of the front panel 10 that fit around the wearer's waist), side recesses 32 (corresponding to the parts of the front panel I 0 that fit under the wearer's arms), rounded upper parts 33 (corresponding to the parts of the front panel 10 that cover the wearer's upper breast, i.e. where the fasteners I 1 are attached), and a concave top 34 (corresponding to the part of the front panel 10 that fits around the wearer's neck).
Each half of the layer 30 also has a V-shaped section 35 having a central fold line 36 about which it can be folded and joined to form a dart as illustrated in Fig. 3.
This Figure shows a layer corresponding to that of Fig. 2-1 or Fig. 2-3. As shown, the layer 30 is folded about a vertical fold line 38 coincident with the fold line 36, whereupon the layer 30 can be joined by sewing or stapling along the lines 37 defining the V-shaped section 35, to form a dart along the joined lines 37, leaving a pleat 40 which consists of the V-shaped section 35 folded over on itself.
As shown for the layers 30 of Figs. 4-1 to 4-4, when two darts 37 are formed in the right and left parts of each layer 30, the outer perimeter of the layer 30 adopts a shape which is essentially the same for all of the layers and corresponds to the peripheral shape of the front panel 10. The successive layers 30 can however have different sizes and shapes as a function of the shape to be built up.
By comparing Figs. 2-1 to 2-I2, it can be seen that the successive layers have darts 37 which are angularly offset from one another around a point of convergence 39, each sheet 30 having two laterally-spaced points of convergence 39 corresponding to the centers of the recessed parts in the front panel 10 that are adapted to receive the wearer's breast. These points of convergence 39 are approximately at the same locations for all twelve layers 30. It is understood that the pointed ends of the darts 37 could be distributed around an area of convergence, e.g. a circular area that as a result is not folded. Such area will be sufficiently large to avoid twisting and unwanted "doubling up" at a point of convergence.
I O Alternate pairs of the layers 30 of material - namely those of Figs. 2-1 and 2-3; 2-2 and 2-4; 2-5 and 2-7; 2-6 and 2-8; 2-9 and 2-11; 2-10 and 2-12 - are identical so the darts 37 of the layers of each pair are located at the same angular location.
The darts 37 of the successive layers (Figs. 2-1, 2-2, 2-3 and so on) are angularly offset to one another. Those of Figs. 2-1, 2-2 and Figs. 2-3, 2-4 are at 180 degrees to one another; those of the other successive layers are at different angles represented on Figs. 2-5 to 2-12 by the fold lines 36. Generally, the darts 37 in the odd-numbered layers are located on the upper part and those in the even-numbered layers are located on the lower part of its layer 30, except for the layer 30 of Fig. 2-10 where the dart is located in the middle.
In this given example, the angle of the V between the lines 37 forming each dart is about 22.5 degrees, so the six darts placed side by side would extend over 135 degrees. However, it can be seen that overall the darts 37 extend over an angle of about 195 degrees, starting at one extremity at the top from the darts 37 of Figs. 2-9 and 2-I 1, to the darts 37 of Figs. 2-2 and 2-4 at the other extremity at the bottom, there being a gap between the other darts 37 - see Fig. S.
As illustrated in Figs. 4-1 to 4-4, the pleats 40 associated with darts 37 are folded in alternate directions in order to achieve the best possible distribution of their extra thickness when the layers 30 are assembled. Each pleat 40 occupies 1/2 the width of the V-shaped sections and these pleats 40 are selectively folded in alternate directions.
In Fig. 4-1 the left pleat 40 in the top of the frst layer 30 is folded to the right and the right pleat 40 is folded to the left. Likewise, in Fig. 4-2, the left pleat 40 in the lower part of the second layer 30 is folded to the right and the right pleat 40 is folded to the left.
For the corresponding next two layers of Figs. 4-3 and 4-4, the folding of the con esponding pleats 40 is inverted, i.e. for the third and fourth layers 30 the left pleats 40 are folded to the left and the right pleats 40 are folded to the right.
The same pattern of inverting the folding of the pleats 40 is followed in the S subsequent groups of pairs of layers 30. The principle is that the pleats 40 in darts 37 located at the same location in alternating layers - like those in Figs. 2-S and 2-7 and in Figs. 2-6 and 2-8 for example - will be folded in opposite directions so that when the layers 30 are assembled these pleats 40 will not overlay one another (see Fig. S). This folding of the pleats 40 can be done when the darts 37 are formed, or when the layers 30 are being assembled.
The layers 30 with their darts 37 are then assembled successively on a bust, with the pleats 40 of the successive layers folded as described above. Each layer 30 is adjusted onto the next (or previous) one by means of needles. The same process is repeated for all twelve layers 30, laying the pleats 40 in the selected directions on 1 S top of the layer 30, except for the last layer where the pleats can be turned inside to have a smooth outer surface.
The assembled and shaped layers 30 are held in clamps and sewed (or otherwise secured together) around their periphery, taking care to maintain the shape during sewing and pressing out air to avoid the formation of air pockets. For this, it is preferable not to sew continuously around the periphery, but to sew peripheral sections one at a time, starting at the rounded upper parts 33 and finishing at the lower corners. If desired, the part corresponding to the waist can be taken in to provide a better shape.
Thanks to the darts 37, the assembled layers 30 are shaped to form two laterally-2S spaced recessed parts in a mono-cup configuration adapted to fit over the wearer's breasts, and the pleats 40 in the various layers 30 are oriented in directions so that the added thickness is distributed substantially evenly around the shaped parts, avoiding any bulges or stiffness.
Fig. S schematically illustrates the angular distribution of the pleats 40 in the assembled pack. In this Figure the pleats 40 are identified by the number L1 to L12 of their respective layer 30 conesponding to Figs. 2-1 to 2-12. In this example, proceeding clockwise, the pleats L 11-L9, L3-L 1, L7-LS, L 12-L 10, L6-L8 and L4 are arranged together in pairs folded in opposite directions about the lines forming their darts 37. The pleats L1-L7, LS-L12, L10-L6 and L8-L2 are all IS
angularly spaced apart from one another by expanses of the layer 30 that are not covered by pleats.
Due to the angular staggering of the darts 37 and the selective orientation of the pleats 40, no pleats in the pack overlap one another. Moreover, pleats 40 whose external edges coincide angularly with one another - in this example L3 and L9 -are separated by a non-pleated part of at least one intermediate layer 30 -namely layers L4-L8 - so there is no risk of interference between pleats 40 that could cause jamming or bulge formation.
In the final assembly, the pleats 40 are evenly distributed around the outer parts of the mono-cup recesses, providing two extra protective layers in this sensitive zone in the locations covered by the pleats 40.
If it is desired to have two extra protective areas over the uncovered areas in Fig. 5, this can be achieved simply by including extra layers in the pack with darts at the desired extra locations.
The front panel i 0 of Fig. 1 can be made by fitting together a chosen number of packs of the twelve layers 30 assembled as described, e.g, two packs making up a 24-layer panel or three packs making up a 36-layer panel, and so on. It is also possible to make fractional assemblies, e.g. two and a half packs making up a layer panel.
Fig. 6 shows how layers of penetration-resistant material can be assembled to form the back panel 20 of Fig. 1. Here, layers 50 shaped to form the back panel 20 are placed together, curved to the back's shape then sewn or otherwise attached together. All layers 50 except the last five are sewed together around their periphery at 51 and crosswise at 52. The last five layers 50 (which will be those closest the body} are sewed together only around the periphery at 51. Then the packs are stitched together only in the top and side regions of the periphery 51.
The front and back panels 10,20 are then enclosed in their respective cover layer and lining, and the Velcro fasteners and straps fitted.
Example The shaped front panel of a bullet-resistant vest was manufactured as described above with 30 layers of Kevlar~ Style 363F fabric sewed using 930 dtex Kevlar~
__.._... ~.._. ........ ...._. ~ . ~ , ~
sewing yarn. Kevlar~ is a DuPont Registered Trademark. The layers were assembled on a bust measuring 94-64-97 cm (size 42). The finished shaped front panel was mounted on a Plastilina backing material and subjected to standard ballistic tests. Bullets were aimed at the tip, flank and border of the curved breast part under standard conditions. All bullets were stopped within the first half of the pack, which is an indication of good ballistic design. Moreover, the backface deformation on the Plastilina was satisfactory.
Legend L 1-L 12 Layers 10 front panel 11 Velcro pile fastener 12 Velcro pile fastener 14 top breast section 15 lower breast section 16 side extension 17 seam back panel 15 21 top straps 22 Iower straps 23 cross-piece 24 belt 30 Iayer of material cut to shape 31 side extension 32 arm recess 33 upper breast cover 34 neck V-shaped section of material 36 fold line 37 joining line 38 vertical fold line 30 39 point or area of convergence V-shaped pleat (folded over) back layer 51 periphery 35 52 crosswise sewing FIG.1 FIG. 2-1 FIG. 2-2 FIG. 2-3 FIG.2-4 FIG. 2-5 FIG. 2-6 FIG. 2-7 FIG. 2-8 FIG.2-9 FIG. 2-10 FIG. 2-11 FIG. 2-12 FIG. 3 FIG.4-1 FIG. 4-2 FIG. 4-3 FIG. 4-4 FIG. 5 FIG. 6
Claims (24)
1. Armor made of multiple layers of flexible relatively inelastic penetration-resistant material shaped to fit over a shaped area to be protected, wherein the layers are held by a plurality of darts in successive layers of the material, each of said layers of material having et least one dart and each dart in a layer comprising a generally V-shaped section where edges era joined to form the dart, with the V-shaped section folded on itself and folded over to one side to form an added thickness overlaying err underlying an adjacent part of the layer, the darts in said multiple layers being angularly offset from one another with the folded V-shaped sections oriented so that raid added thickness is distributed substantially evenly around said shaped area et least one of the layers of penetration-resistant material comprising a fabric bonded to err coated with a reinforcing continuum which extends over a selected arcs to be protected of said at least one layer, wish the exception of the or each folded-over V-shaped section forming the or each dart, said folded-over V-shaped section consisting of fabric only.
2. Multilayer shaped armor according to claim 1 in which the folded V-shaped sections are oriented in different directions.
3. Multilayer shaped armor according to clam a in which pairs of the layers of material have dams at the same angular location with their folded V-shaped parts oriented in opposite directions so they do net overlay one another.
4. Multilayer shaped armor according to claim 3 in which the layers forming said pairs with darts at the same angular location are alternate layers.
5. Multilayer shaped armor according to claim 1 in which the darts extend radially from at least one point of convergence.
6. Multilayer shaped armor according to claim 5 in which the darts are angularly staggered from one another around s point of convergence by an angle which is equal to or greater than the angle of the V-shaped sections.
7. Multilayer shaped armor according to claim 1 which is body armor comprising at least one part shaped to fit over a shaped part of the body.
8. Multilayer shaped armor according to claim 7 which is shaped to fit over the bust of a female wearer, having two laterally-spaced internally concave recessed parts corresponding to the bust, in which the darts are angularly offset around each of the two laterally-spaced recessed parts about which said added thickness is distributed substantially evenly.
9. Multilayer shaped armor according to claim 8 is which said two laterally-spaced concave recessed parts corresponding to the bust are formed by darts around the upper, lower and outer edges of the recessed parts, defining a continuous shaped bust for receiving the two breasts.
10. Multilayer shaped armor according to claim 8 or 9 in which the darts extend radially from two laterally-spaced paints of convergence corresponding to the centers of said recessed parts, the darts extending above and below the two points of convergence over an overall angle of at least about 180 degrees.
11. Multilayer shape armor according to claim 1, in which the V-shaped sections each make an angle of 10 to 40 degrees.
12. Multilayer shaped armor according to claim 1 comprising darts in at least three angularly offset positions about a point of convergence.
13. Multilayer shaped armor according to claim 12 comprising darts in at least six angularly offset positions about a point of convergence.
14. Multilayer shaped armor according to claim 1 in which the layers of penetration-resistant material comprise polyaramid fibers.
15. Multilayer shaped armor according to claim 1 in which there are discontinuities in the reinforcing continuum in the area of the folded oven darts, said discontinuities being covered by the folded over layers of the fabric forming the darts, the angular offsetting of said darts distributing the darts and said discontinuities in the reinforcing continuum of the different layers to avoid bulges and excessive stiffness.
16. Multilayer shaped armor according to claim 1 in which said reinforcing continuum is a polymeric film or coating layer, a metal foil or a sheet of rubber or elastomer.
17. Multilayer shaped armor according to claim 1 in which at least two successive layers of penetration-resistant material are glued or bonded together as a sandwich.
18. A method of manufacturing multilayer shaped armor as defined in claim 1, comprising:
providing multiple layers of flexible relatively inelastic penetration-resistant material to be assembled into the shaped armor, each layer having fold lines defining at least one dart comprising a generally V-shaped section of the material, the darts of the different layers being angularly offset from one another around at least one point of convergence, at least one of the layers of penetration-resistant material comprising a fabric bonded to or coated with a reinforcing continuum which extends over a selected area to be protected of said at least one layer with the exception of the or each folded-over V-shaped section forming the err each dart, said folded-over V-shaped section consisting of fabric only;
- joining the edges of the V-shaped sections to form the dart(s) in each layer, the layers with formed darts all having substantially the same peripheral shape for assembly into the shaped armor;
- assembling the multiple layers to form the shaped part, with darts of different layers angularly offset to one another and with the V-shaped sections of fabric folded in directions to distribute the added thickness substantially evenly;
and - attaching the shaped multiple layers to form the armor.
providing multiple layers of flexible relatively inelastic penetration-resistant material to be assembled into the shaped armor, each layer having fold lines defining at least one dart comprising a generally V-shaped section of the material, the darts of the different layers being angularly offset from one another around at least one point of convergence, at least one of the layers of penetration-resistant material comprising a fabric bonded to or coated with a reinforcing continuum which extends over a selected area to be protected of said at least one layer with the exception of the or each folded-over V-shaped section forming the err each dart, said folded-over V-shaped section consisting of fabric only;
- joining the edges of the V-shaped sections to form the dart(s) in each layer, the layers with formed darts all having substantially the same peripheral shape for assembly into the shaped armor;
- assembling the multiple layers to form the shaped part, with darts of different layers angularly offset to one another and with the V-shaped sections of fabric folded in directions to distribute the added thickness substantially evenly;
and - attaching the shaped multiple layers to form the armor.
19. The method according to claim 18 in which pairs of the layers of material have darts at the same angular location, the V-shaved sections of these layers being folded in apposite directions so they do not overlay one another.
20. The method according to claim 19 in which the pairs of layers with darts at the same angular location are assembled in alternate layers.
21. The method according to claim 18 in which the reinforcing continuum is applied to the fabric, with the application of bast and pressure, before folding the darts.
22. The method according to claim 18 in which the reinforcing continuum is applied to the fabric after folding of the dart(s).
23. The method of claim 18 ins which a peripheral edge part of the fabric is free from the reinforcing continuum, and the successive layers are joined by around said peripheral edge part of the fabric.
24. The method according to claim 18, 19 or 20 in which the edges of the V-shaped sections are joined to form the darts by sewing, stapling, riveting or gluing.