CA2245894A1 - Hot-dip zn-al-mg plated steel sheet good in corrosion resistance and surface appearance and method of producing the same - Google Patents
Hot-dip zn-al-mg plated steel sheet good in corrosion resistance and surface appearance and method of producing the sameInfo
- Publication number
- CA2245894A1 CA2245894A1 CA 2245894 CA2245894A CA2245894A1 CA 2245894 A1 CA2245894 A1 CA 2245894A1 CA 2245894 CA2245894 CA 2245894 CA 2245894 A CA2245894 A CA 2245894A CA 2245894 A1 CA2245894 A1 CA 2245894A1
- Authority
- CA
- Canada
- Prior art keywords
- coating layer
- plating bath
- steel sheet
- phase
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A steel sheet having on the surface thereof a coating layer which is formed by hot dipping and which consists of 4.0 to 10 wt.% of Al, 1.0 to 4.0 wt.% of Mg and the balance consisting of Zn and unavoidable impurities, the coating layer having a metallic structure in which a proeutectic Al phase or both of a proeutectic Al phase and a single Zn phase are dispersed in a matrix of an Al/Zn/Zn2 Mg ternary eutectic structure. The coating layer having such a metallic structure can be formed by properly controlling the rate of cooling the coating layer adhering to the steel strip pulled up from a plating bath in continuous plating equipment and the temperature of the plating bath and/or by adding proper amounts of Ti and B into the plating bath. The streaking inherent in such a coated steel sheets is inhibited by controlling the configuration of a magnesium-containing film generated until the solidification of the coating layer or by the addition of a proper amount of Be into the plating bath.
Applications Claiming Priority (9)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP35246796 | 1996-12-13 | ||
JP8/352467 | 1996-12-13 | ||
JP9/63923 | 1997-03-04 | ||
JP6392397 | 1997-03-04 | ||
JP9-162035 | 1997-06-05 | ||
JP16203597 | 1997-06-05 | ||
JP9/316631 | 1997-11-04 | ||
JP31663197A JP3201469B2 (en) | 1997-11-04 | 1997-11-04 | Mg-containing hot-dip Zn-base plated steel sheet |
PCT/JP1997/004594 WO1998026103A1 (en) | 1996-12-13 | 1997-12-12 | HOT-DIP Zn-Al-Mg COATED STEEL SHEET EXCELLENT IN CORROSION RESISTANCE AND SURFACE APPEARANCE AND PROCESS FOR THE PRODUCTION THEREOF |
Publications (2)
Publication Number | Publication Date |
---|---|
CA2245894A1 true CA2245894A1 (en) | 1998-06-18 |
CA2245894C CA2245894C (en) | 2006-01-17 |
Family
ID=29424799
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
CA 2245894 Expired - Lifetime CA2245894C (en) | 1996-12-13 | 1997-12-12 | Hot-dip zn-al-mg plated steel sheet good in corrosion resistance and surface appearance and method of producing the same |
Country Status (1)
Country | Link |
---|---|
CA (1) | CA2245894C (en) |
-
1997
- 1997-12-12 CA CA 2245894 patent/CA2245894C/en not_active Expired - Lifetime
Also Published As
Publication number | Publication date |
---|---|
CA2245894C (en) | 2006-01-17 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
TW363088B (en) | Molten Zn-Al-Mg plated steel sheet of good corrosion resistance and good appearance, and process | |
US3505043A (en) | Al-mg-zn alloy coated ferrous metal sheet | |
ES8501449A1 (en) | Ferrous product having an alloy coating thereon of aluminium-zinc-magnesium-silicon, and method. | |
US4029478A (en) | Zn-Al hot-dip coated ferrous sheet | |
CA2358442A1 (en) | Plated steel wire with high corrosion resistance and excellent workability, and process for its manufacture | |
JPS648702B2 (en) | ||
CA2040376A1 (en) | Process for continuous dip coating of a steel strip | |
KR900700648A (en) | Hot-dip zinc-aluminum alloy plated steel sheet for prepainted steel sheet, preparation method thereof and prepainted steel sheet | |
JPS6223976A (en) | Steel sheet coated with zn-al alloy by hot dipping and having superior paintability | |
US5470667A (en) | Coated metal strip | |
CA2290073A1 (en) | Galvannealed steel sheet and manufacturing method | |
JP2754126B2 (en) | Hot-dip Zn-Al plated steel sheet with excellent appearance, blackening resistance over time and corrosion resistance | |
JP3718479B2 (en) | Hot-dip Zn-Al-Cr alloy-plated steel with excellent corrosion resistance | |
US5489490A (en) | Coated metal strip | |
JPS56152955A (en) | Hot dipping composition for steel sheet coated with zinc alloy by hot dipping | |
CA2245894A1 (en) | Hot-dip zn-al-mg plated steel sheet good in corrosion resistance and surface appearance and method of producing the same | |
JPH02175852A (en) | Production of hot dip zinc-aluminum alloy plated steel sheet having superior surface smoothness and high corrosion resistance | |
JP2627788B2 (en) | High corrosion resistance hot-dip zinc-aluminum alloy coated steel sheet with excellent surface smoothness | |
JP2704816B2 (en) | Hot-dip Zn-Al plated steel sheet with excellent appearance, blackening resistance over time and corrosion resistance | |
WO2002033140A2 (en) | Process and alloy for decorative galvanizing of steel | |
KR950018601A (en) | Manufacturing method of hot-dip galvanized steel sheet excellent in corrosion resistance and plating adhesion | |
CA2092079A1 (en) | Aluminum alloy sheet with improved formability and method of production | |
CA1065204A (en) | Zinc-aluminum eutectic alloy coating process and article | |
JP2001107212A (en) | HIGH CORROSION RESISTANT HOT-DIP Zn-Al-Mg BASE COATED STEEL SHEET EXCELLENT IN SURFACE CHARACTERISTIC | |
Horton | Aluminum-zinc alloys as sacrificial coatings |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
EEER | Examination request | ||
MKEX | Expiry |
Effective date: 20171212 |