CA2147687A1 - Method of treating papermaking fibers for making tissue - Google Patents
Method of treating papermaking fibers for making tissueInfo
- Publication number
- CA2147687A1 CA2147687A1 CA 2147687 CA2147687A CA2147687A1 CA 2147687 A1 CA2147687 A1 CA 2147687A1 CA 2147687 CA2147687 CA 2147687 CA 2147687 A CA2147687 A CA 2147687A CA 2147687 A1 CA2147687 A1 CA 2147687A1
- Authority
- CA
- Canada
- Prior art keywords
- fibers
- index
- disperser
- tissue
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The throughdryability of dewatered, but wet, sheets made from papermaking fibers can be significantly increased by subjecting an aqueous suspension of the fibers at high consistency to elevated temperatures with sufficient working of the fibers. Such a treatment is particularly effective for improving the efficiency of throughdrying processes used in the manufacture of certain products, such as tissues and paper towels, made from furnishes having a significant amount of secondary or recycled fibers.
Description
METHOD OF TREATING PAPERMAKING FIBERS FOR MAKING TISSUE
Background of the Invention In the manufacture of certain paper sheet products, such as tissue and paper towels, one method of drying the sheet after formation and dewatering is to pass heated air through the wet sheet in a process well known in the papermaking art as throughdrying.
Throughdrying is advantageous in that it minimizes compaction of the web and thereby produces a bulkier product compared to conventional wet press manufacturing processes, which rely on high levels of compression of the wet web and on a Yankee dryer to dry the web.
However, throughdrying has some disadvantages in that it requires a substantial amount of expensive equipment and energy to carry out the drying process. In particular, the drying efficiency of the throughdrying process is in large part dependent upon the air permeability of the wet sheet which permits the hot air to pass therethrough. Air permeability is especially a problem for sheets made from fiber furnishes containing secondary (recycled) fibers, which inherently impart poor air permeability to the wet sheets into which they are incorporated. With the continual efforts to utilize more secondary fibers in paper products for environmental reasons, there is a need to improve the throughdryability of secondary papermaking fibers.
SummarY of the Invention It has been surprisingly discovered that the ease in which secondary papermaking fibers can be throughdried can be improved by pre-treating the fibers of the papermaking furnish in a wet mechanical process in which the fibers are appropriately worked while suspended in a high consistency aqueous slurry. The effectiveness of the pretreatment is manifested by an increase of the Throughdryability Index (hereinafter defined and referred to as the ~TD Index") of the fibers. An increase in the TD Index translates into faster throughdrying machine speeds for a given furnish and 21 ~ 7687 basis weight, which results in improved operating efficiency. The method of this invention can be utilized for any papermaking fibers, but is especially advantageous for improving the TD Index of secondary fiber furnishes and furnishes containing a significant amount of fines and/or short fibers, such as hardwood fibers. (As used herein, "short fibers" are fibers having a population average length of from 0.5 to about 1 millimeter as determined by using a Kajaani FS-200 fiber length analyzer.) In some cases, the TD Index of secondary fiber furnishes can be surprisingly improved beyond that of untreated virgin furnishes. As used herein, ~fines~ are particles that pass through a 200 mesh screen having a 76 micrometer diameter opening. They can be measured in accordance with TAPPI Test Method T261 pm-80 (1989).
In addition, while the fiber treatment of this invention is particularly advantageous for throughdrying processes and products, product improvements can also be realized when the treated fibers of this invention are used for making wet pressed tissue products as well. More specifically, it has been found that substituting the treated fibers of this invention for a portion of the fibers of a given tissue furnish, the softness of the resulting tissue can be increased without loss of strength. This is especially effective when treating hardwood fibers and combining the treated hardwood fibers with other fibers, such as untreated softwood fibers, either bler,ded or layered. The treated hardwood fibers improve the softness of the resulting product while the untreated softwood fibers retain the strength. Softness can be further enhanced by adding a softening agent to the treated fibers either before treatment or after treatment. Certain softening agents also provide an unexpected increase in bulk as well as enhancing the softness of the tissue.
Hence in one aspect, the invention resides in a method of making a tissue comprising: (a) forming an aqueous suspension of papermaking fibers having a consistency (dry weight percent fibers in the aqueous suspension) of about 20 or greater; (b) passing the aqueous suspension through a shaft disperser at a temperature of 150-F. or greater with a power input of at least about 1 horsepower-day per ton of dry fiber, wherein the TD Index of the fibers is increased about 25 percent or greater, preferably about 50 percent or greater, and 2I~7687 more preferably about 75 percent or greater; (c) feeding the fibers through a tissue making headbox to form a wet web; and (d) drying the web, such as by throughdrying, to form a dried tissue.
In another aspect, the invention resides in a method of making tissue comprising: (a) forming an aqueous suspension of papermaking fibers having a consistency of about 20 or greater; (b) passing the aqueous suspension through a shaft disperser at a temperature of 150F. or greater with a power input of at least about 1 horsepower-day per ton of dry fiber, wherein the TD Index of the fibers is about 0.15 or greater, preferably about 0.2 or greater, more preferably about 0.3 or greater, and most preferably about 0.5 or greater;
(c) feeding the fibers through a tissue making headbox to form a wet web; and (d) drying the web, such as by throughdrying, to form a dried tissue.
In a further aspect, the invention resides in a throughdried sheet made from a furnish comprising at least about 25 dry weight percent secondary fibers, and/or having at least about 7 weight percent fines and/or having at least about 20 percent short fibers, said furnish having a TD Index of about 0.15 or greater, preferably about 0.20 or greater, more preferably about 0.30 or greater, and most preferably about 0.5 or greater. If present, the amount of secondary fibers in the furnish can be anywhere within the range of about 25 to about 50, 75, or 100 dry weight percent. In general, secondary fibers inherently have a high proportion of fines and/or short fibers. If present, the amount of fines can be about 7 weight percent or greater, more particularly about 10 weight percent or greater, still more particularly from about 10 to about 25 weight percent. If present, the amount of short fibers can be about 20 weight percent or greater, more specifically about 50 weight percent or greater, still more specifically about 75 percent or greater.
Papermaking fibers useful for purposes of this invention include any cellulosic fibers which are known to be useful for making paper, particularly those fibers useful for making relatively low density tissue papers such as facial tissue, bath tissue, dinner napkins, paper towels, and the like. As used herein, the term ~tissue" is used generically and is intended to include all such products. Such ~1~7687 products can be creped or uncreped. The most common papermaking fibers include virgin softwood and hardwood fibers, as well as secondary or recycled cellulosic fibers. As used herein, "secondary fiber" means any cellulosic fiber which has previously been isolated from its original matrix via physical, chemical or mechanical means and, further, has been formed into a fiber web, dried to a moisture content of about 10 weight percent or less and subsequently reisolated from its web matrix by some physical, chemical, or mechanical means. Fibers which have been passed through a shaft disperser as described herein are sometimes referred to as ~dispersed fibers".
The basis weight of the throughdried sheet can be from about 5 to about 50, preferably from about 10 to about 40, and more preferably from about 20 to about 30 grams per square meter. It will be appreciated that lower basis weight sheets inherently have greater permeability for a given furnish. Hence the greatest advantage of this invention is obtained with relatively higher basis weights where the sheets are normally more difficult to throughdry. The invention is particularly suitable for making throughdried single-ply bath tissue having a basis weight of about 25 grams per square meter.
The consistency of the aqueous suspension which is subjected to the treatment of this invention must be high enough to provide significant fiber-to-fiber contact or working which will alter the surface properties of the treated fibers. Specifically, the consistency can be at least about 20, more preferably from about 20 to about 60, and most preferably from about 30 to about 50 dry weight percent. The consistency will be primarily dictated by the kind of machine used to treat the fibers. For some rotating shaft dispersers, for example, there is a risk of plugging the machine at consistencies above about 40 dry weight percent. For other types of shaft dispersers, such as the Bivis machine (commercially available from Clextral Company, Firminy Cedex, France), consistencies greater than 50 can be utilized without plugging. It is desirable to utilize a consistency which is as high as possible for the particular machine used.
The temperature of the fibrous suspension can preferably be about 150F. or greater, more preferably about 210-F. or greater, and 2147fi~7 more preferably about 220F. or greater. In general, higher temperatures are better for increasing the TD Index. The upper limit on the temperature is dictated by whether or not the disperser is pressurized, since the aqueous fibrous suspensions within apparatus operating at atmospheric pressure cannot be heated beyond the boiling point of water. A suitable temperature range is from about 170-F. to about 220-F.
The amount of power applied to the fibrous suspension also impacts the resulting TD Index. In general, increasing the power input will increase the TD Index. However, it has also been found that the improvement (increasing) of the TD Index falls off upon reaching a power input of about 2 horsepower-days per ton (HPD/T) of dry fiber in suspension. A preferred range of power input is from about 1 to about 3 HPD/T, more preferably about 2 HPD/T or greater.
In working the fibers within the disperser, such as by shearing and compression, it is necessary that the fibers experience substantial fiber-to-fiber contact by rubbing or shearing in addition to rubbing or shearing contact with the surfaces of the mechanical devices used to treat the fibers. Some compression, which means pressing the fibers into themselves, is also desireable to enhance or magnify the effect of the rubbing or shearing of the fibers. The desired fiber-to-fiber contact can in part be characterized by apparatus having a relatively high volume-to-working surface area ratio which increases the likelihood of fiber-to-fiber contact. The working surface for purposes herein is defined as that surface of the apparatus which contacts the majority of the fibers passing through.
For example, disc refiners have a very low volume-to-working surface area (approximately 0.05 centimeters) because there is a relatively small volume or space between the opposed rotating discs (working surfaces). Such devices work the fibers primarily by contact between the working surfaces and the fibers. However, the apparatus particularly useful for purposes of this invention, such as the various types of shaft dispersers, have a much higher volume-to-working surface area. Such volume-to-working surface area ratios can be about 1 centimeter or greater, preferably about 3 centimeters or greater, and more specifically from about 5 to about 10 centimeters.
21~ 76~ 7 These ratios are orders of magnitude greater than those of disc refiners.
The measure of the appropriate amount of shearing and compression to be used lies in the end result, which is the achievement of an increased TD Index. A number of shaft dispersers or equivalent mechanical devices known in the papermaking industry can be used to achieve varying degrees of the desired results.
Suitable shaft dispersers include, without limitation, nonpressurized shaft dispersers, such as the Maule shaft disperser, and pressurized shaft dispersers, such as the Bivis machines and the like.
If softening agents are used to enhance the softness of the final tissue product, suitable agents include, without limitation, fatty acids, waxes, quaternary ammonium salts, dimethyl dihydrogenated tallow ammonium chloride, quaternary ammonium methyl sulfate, carboxylated polyethylene, cocamide diethanol amine, coco betaine, sodium lauroyl sarcosinate, partly ethoxylated quaternary ammonium salt, distearyl dimethyl ammonium chloride, and the like.
Examples of suitable commercially available chemical softening agents include, without limitation, Berocell 564 and 584 manufactured by Eka Nobel Inc., Adogen 442 manufactured by Whitco Sherex Chemical Company, Quasoft 203 manufactured by Quaker Chemical Company, and Arquad 2HT-75, manufactured by Akzo Chemical Company.
Brief DescriDtion of the Drawinq Figure 1 is a schematic flow diagram of the apparatus used for determining the TD Index.
Figure 2 is an exploded perspective view of the sample holder of the apparatus of Figure 1, including the sliding sample tray used to place the sample holder into the drying apparatus.
Figure 3 is a representative depiction of a typical plot of pressure drop versus moisture ratio as generated while testing a sample using the apparatus described in Figure 1 above.
Figure 4 is a schematic process flow diagram of a method of treating fibers in accordance with this invention using a shaft disperser to work the fibers.
Figure 5 is a cut-away perspective view of the shaft disperser of Figure 4.
21476~7 Figure 6 is an alternative schematic process flow diagram of a method in accordance with this invention using a pair of Bivis shaft dispersers in series.
Figure 7 is a sectional view of a Bivis shaft disperser useful for purposes of this invention.
Figure 8 is a sectional view, viewed in the axial direction, of the reverse-flighted screws of the Bivis shaft disperser, illustrating the cut-out notches in the flights.
Figure 9 is a sectional view, viewed in the axial direction, of the forward-flighted screws.
Figure 10 is a sectional view of a reversed-flighted section of the machine, illustrating the flow of the fibrous suspension.
Detailed Description of the Invention The ThroughdrYabilitY Index During throughdrying, it is generally understood that the drying rate is high and relatively constant at high moisture ratios (constant rate period). The drying rate begins decreasing rather rapidly after reaching a certain critical moisture ratio (falling rate period) in the sheet. If a constant air permeation rate is maintained throughout the-drying period, the pressure drop is also expected to decrease as the moisture ratio decreases (or as the drying process continues). The manner in which the pressure drop varies during the throughdrying process under a constant air permeation rate is of primary interest for purposes of this invention because it provides a quantitative means for measuring the air permeability of the sheet while being dried. If one can accurately measure the instantaneous absolute humidity of the outlet air after drying a tissue sample, one can readily calculate the instantaneous moisture ratio from the humidity of the outlet air and the initial and the final moisture ratios of the tissue sample as shown below:
Xm(t) = Xo~ (Xo~Xend) ~out(t) ~in~ dt wherein ~XoN= the moisture ratio of the test sample at the beginning of the test, expressed as kilograms of water per kilogram of bone dry fiber;
21476~7 "Xend~= the moisture ratio of the test sample at the end of the test, expressed as kilograms of water per kilogram of bone dry fiber;
~Xmll= the instantaneous moisture ratio of the test sample, expressed as kilograms of water per kilogram of bone dry fiber;
"Yjnn= the humidity of the drying air immediately prior to reaching the sample, expressed as kilograms of water per kilogram of dry air;
"Y~t"= the humidity of the drying air immediately after passing through the sample, expressed as kilograms of water per kilogram of dry air; and "t"= elapsed time, expressed in seconds.
Calculating the moisture ratio X~ from the humidity data for the entire drying period data enables one to plot pressure drop as a function of the instantaneous moisture ratio. The inverse of the area under the resulting curve is referred to herein as the TD Index, expressed as kilopascals-~. This index is a measure of the air permeability of the wet sheet and reflects the ease in which a paper sheet made from a particular furnish can be throughdried. Higher TD
Index values reflect greater ease in throughdrying, whereas lower values reflect greater difficulty in throughdrying.
As will be described below, measurement of the TD Index requires that the fibers in question be formed into a handsheet having a basis weight of 24 grams per square meter. This is accomplished by diluting a fiber sample in water to a consistency of 2.5 weight percent in a British Pulp Disintegrator and allowing the dispersed sample to soak for 5 minutes. The sample is then pulped for 10 minutes at ambient temperature, diluted to 0.04 percent consistency, and formed into a handsheet on a British Handsheet Mold (The Hermann Mfg. Co., Lancaster, Ohio). The handsheet is couched off of the mold by hand using a blotter without applying any pressure. The handsheet is dried for 2 minutes to absolute dryness using a Valley steam hotplate and a standard weighted canvas cover having a lead filled (4.75 pounds) brass tube at one end to maintain uniform tension. The TD Index for the resulting dried handsheet is then determined as described herein and the measured TD Index value 21~687 is assigned to the fibers or furnish from which the handsheet was made.
Referring now to Figure 1, the apparatus for determining the TD
Index will be described in greater detail. Unless otherwise specified, conduit in the mainstream of air flow has a 1.5 inch inside diameter. Air for drying the samples is provided by two "oil free" compressors 1, each rated for 29.9 cubic feet per minute at 90 psi. (Model DN 1024H-3DF, Atlas Copco, Cleveland, Ohio). The outlet of the compressors is suitably connected to the inlet of a condensed water separator 2 (Model WS0-08-000, Wilkerson, Engelwood, Colorado), which serves to remove any liquid water entrained in the air stream. The outlet of the separator is suitably connected to the inlet of a molecular sieve 3 (Model M530, Wilkerson) which serves to eliminate particulate matter in the air having a particle size greater than about 0.05 microns. The outlet of the molecular sieve is suitably connected to a compressed air dryer 4 (Wilkerson model DHA-AE-000) with an outlet flow of 49 cubic feet per minute. The outlet of the dryer is connected to the inlet of a surge tank 5 (approximately 75 cubic feet capacity). The outlet of the surge tank is suitably connected to two additional oil heat exchangers 6 and 7 (5 liter capacity/250-C. max. temp./6 bar max. pressure, Apparatebau Wiesloch GmbH, Weisloch, Germany) in series which serve to further heat the air to the desired throughdrying temperature. In between the surge tank and the two heat exchangers are a moisture monitor 8 (Aquanel, Gerhard GmbH, Blankebach, Germany), a gate-type control valve 9 (DIN R65, 1.5 inch, PN 16, Henose, Hamburg, Germany) for controlling the flow rate of the air, an orifice plate 10 (25 millimeter diameter opening, RST 37-2 PN6 DIN 2527-32-5784, University of Karlsruhe, Karlsruhe, Germany), and a manometer 11 (Betz, Gottingen, Germany), which together are used to determine the air flow rate. Other valves and piping (not shown) which are not essential to the operation of the apparatus can be present for convenience at various places to isolate or by-pass gauges and other devices. The outlet of the second heat exchanger is directly connected to a sample housing 12, which is designed to receive and hold a slidable sample tray 13 (see Figure 2) into which a sample holder (see Figure 2) is placed. All of the air passes through the sample placed in the sample holder. An inflatable gasket mounted within the sample housing assures a positive seal between the sample housing and the slidable sample tray when the gasket is activated. A
diffuser 14 is suitably connected to the outlet of the sample housing such that the cross-sectional flow area is expanded to 11,600 square millimeters in order to slow down the air flow to facilitate more accurate moisture measurement. The diffuser is suitably connected to a vent tube which carries the air to a suitable exhaust system. A
differential temperature sensor 16 (resistance type differentiation) is suitably connected to measure the temperature of the air before and after the sample. A differential pressure sensor 17 (PU 1000, 0-1000 millibar, llOV AC) is suitably connected to measure the pressure drop across the sample. A second, more sensitive moisture monitor 18 (infrared; twenty-five measurements per second; made by Paderborn University, Paderborn, Germany) measures the moisture content of the air leaving the sample. All three sensors are linked to a Schlumberger data acquisition system 19 which is linked to a computer 20 (RMC 80286 processor) for correlating the data.
Figure 2 illustrates the sample holder and the manner in which the sample is mounted within the sample holder, including the sliding sample tray 13 adapted to hold the sample holder and slide it in and out of the sample housing. Shown in Figure 2 is the top of the sample holder 21, which is the upstream portion, and the bottom of the sample holder 22, which is the downstream portion. The bottom of the sample holder contains a support fabric 23 (Asten 937, Asten Corporation, Appleton, WI) upon which the sample rests. Sandwiched in between the top and bottom is the handsheet sample 24 which has been cut to the appropriate size. A thin line of grease (not visible in this view) positioned around the inside edge of the top of the sample holder provides a seal between the sample and the top of the sample holder when the sample is secured. The top of the sample holder contains two registration pins 25 which become inserted into registration holes 26 in the bottom of the sample holder and the two halves are secured by means of six screws 27 with appropriate threaded holes.
Having identified the apparatus for determining the TD Index, the procedure for determining the TD Index can now be described.
21~7687 Generally speaking, to determine the TD Index for a given test sample (24 gsm handsheet), the sample is carefully wetted to a particular moisture level and dried in the apparatus described above under controlled conditions of constant air mass flow rate. The moisture level in the sample is continuously calculated by a computer, based on the humidity measurements of the air before and after the sample during the test. The measured pressure drop across the sample is plotted as a function of the calculated moisture level of the sample, and the area under the curve is the TD Index.
More specifically, the handsheet sample to be tested is cut into a 10.25 centimeter diameter circle which fits into the sample holder of the apparatus and is only slightly larger than the sample holder opening. During the test, only a 10 centimeter diameter circle of the sample is exposed to air flow. Accordingly, the portion of the circular sample outside the sample holder opening is impregnated with grease (Compound 111 Valve Lubricant and Sealant, Dow Corning Corporation, Midland, Michigan) before being wetted for the test to prevent any moisture from being wicked outside the circle as well as establishing a more positive seal between the sample and the sample holder. This is accomplished by applying and rubbing the grease around the inside edge of the top half (upstream half) of the sample holder. The sample is then placed onto the bottom half of the sample holder which contains a piece of throughdrying fabric (Asten 937) for supporting the sample. The top half of the sample holder is then clamped onto the bottom half of the sample holder, thereby impregnating the outer edge of the sample with the grease. The supported sample is then wetted by spraying with a fine mist until a moisture level of 3.0 kilograms of water per kilogram of bone dry fiber is reached. During spraying, a cover guard should be placed over the sample holder to prevent the sample holder from being sprayed and to keep all of the sprayed water directed at the 10 centimeter circle. The moisture in the sample is accurately determined by the weight difference before and after wetting.
While the sample is being prepared, the air system is turned on at a predetermined constant flow rate of 3.0 kilograms per square meter per second and heated to a temperature of 175C. When steady state is reached, the air temperature will be steady and constant, 21~ 7~87 the humidity will be zero, and the pressure drop will be zero. After the reference steady state conditions are achieved, the sample holder with the wetted test sample is placed into the sliding sample tray and slid into the sample housing of the apparatus. The humidity and the pressure drop are continuously monitored by the instruments and the computer, which provides a plot of pressure drop versus moisture ratio. A typical plot is illustrated in Figure 3. (Note that time increases from right to left in this plot.) As shown, the pressure drop shows a very rapid initial increase and thereafter quickly starts decreasing, typically reaching a constant level in about four or five seconds. The computer then integrates the inverse of the area under the curve and calculates the TD Index as earlier described.
Figure 4 is a block flow diagram illustrating overall process steps for treating fibers in accordance with this invention. Shown is the paper furnish 28 to be treated being fed to a high consistency pulper 29 (Model ST6C-W, Bird Escher Wyss, Mansfield, MA) with the addition of dilution water 30 to reach a consistency of about 15 percent. Prior to being pumped out of the pulper, the stock is diluted to a consistency of about 6 percent. The pulped fibers are fed to a scalping screen 31 (Fiberizer Model FT-E, Bird Escher Wyss) with additional dilution water in order to remove large contaminants.
The input consistency to the scalping screen is about 4 percent. The rejects from the scalping screen are directed to waste disposal 32.
The accepts from the scalping screen are fed to a high density cleaner 33 (Cyclone Model 7 inch size, Bird Escher Wyss) in order to remove heavy contaminants which have escaped the scalping screen.
The rejects from the high density cleaner are directed to waste disposal. The accepts from the high density cleaner are fed to a fine screen 34A (Centrisorter Model 200, Bird Escher Wyss) to further remove smaller contaminants. Dilution water is added to the fine screen feed stream to achieve a feed consistency of about 2 percent.
Rejects from the fine screen are directed to a second fine screen 34B
(Axiguard, Model 1, Bird Escher Wyss) to remove additional contaminants. The accepts are recycled to the feed stream to the fine screen 34A and the rejects are directed to waste disposal. The accepts from the fine screen, with the addition of dilution water to 2l 476~7 reach a consistency of about 1 percent, are then passed to a series of four flotation cells 35, 36, 37 and 38 (Aerator Model CF1, Bird Escher Wyss) to remove ink particles and stickies. Rejects from each of the flotation cells are directed to waste disposal. The accepts from the last flotation cell are fed to a washer 39 (Double Nip Thickener Model 100, Black Clawson Co., Middletown, OH) to remove very small ink particles and increase the consistency to about 10 percent. Rejects from the washer are directed to waste disposal.
The accepts from the washer are fed to a belt press 40 (Arus-Andritz Belt Filter Press Model CPF 20 inches, Andritz-Ruthner Inc., Arlington, TX) to reduce the water content to about 70 percent.
Pressate is directed to waste disposal. The resulting partially dewatered fibrous material is then fed to a shaft disperser 41 (GR II, Ing. S. Maule & C. S.p.A., Torino, Italy), described in detail in Figure 5, in order to work the fibers to increase the TD
Index in accordance with this invention. Steam 42 is added to the disperser feed stream to elevate the temperature of the feed material. The resulting treated fibers 43 can be directly used as feedstock for papermaking or otherwise further treated as desired.
Figure 5 is a cut-away perspective view of a preferred apparatus for treating fibers in accordance with this invention as illustrated in Figure 4. The particular apparatus is a shaft disperser, type GR II, manufactured by Ing. S. Maule & C. S.p.A., Torino, Italy.
This apparatus has a volume-to-working surface area of about 8.5 centimeters. Shown is an upper cylindrical housing 51 and a lower cylindrical housing 52 which, when closed, enclose a rotating shaft 53 having a multiplicity of arms 54. The upper housing contains two rows of knurled fingers 55 and three inspection ports 56. At one end of the upper housing is an inlet port 57. At the inlet end of the rotating shaft is drive motor 58 for turning the shaft. At the outlet end of the rotating shaft is a bearing housing 59 which supports the rotating shaft. The inlet end of the rotating shaft contains a screw feed section 60 which is positioned directly below the inlet and serves to urge the feed material through the disperser. The outlet 61 of the disperser comprises a hinged flap 62 having a lever 63 which, when the disperser is closed up, is engaged by hydraulic air bags 63 mounted on the upper housing. The air bags provide controllable resistance to the rotation of the hinged flap and hence provide a means of controlling the back pressure within the disperser. Increasing the back pressure increases the degree to which the fibers are worked and thereby increases the TD Index.
During operation, the knurled fingers interdigitate with the arms of the rotating shaft to work the feed material therebetween.
Figure 6 is a block flow diagram of an alternative process of this invention utilizing a pair of Bivis shaft dispersers. As illustrated, papermaking pulp, preferably secondary fiber pulp, at a consistency of about 50 percent, is fed to a screw feeder. The screw feeder meters the feedstock to the first of two Bivis shaft dispersers in series. Each Bivis shaft disperser typically has three or four compression/expansion zones. Steam is injected into the first Bivis shaft disperser to raise the temperature of the fibers to about 212-F. The worked pulp is transferred to the second Bivis shaft disperser operating at the same conditions as the first disperser. The worked pulp from the second machine can be quenched by dropping it into a cold water bath and thereafter dewatered to a suitable consistency.
Figure 7 is a sectional elevational view of a twin screw Bivis shaft disperser useful for purposes of this invention. Shown are the inlet 71, feed screw 72, forward flighted screws 73, 74, 75, and 76, reverse-flighted screws 77, 78, 79 and 80, outlet 81, injection ports 82, 83, 84 and 85, optional extraction ports 86, 87, 88 and 89, and thermocouples 90. In operation, pulp is introduced into the Bivis through the inlet. The pulp then encounters the short feed screw, which serves to introduce the pulp into the first working zone. The working zones consist of a pair of slightly overlapping screws encased in cylinders with less than 1 millimeter clearance between the screw flights and the cylinder walls. The twin screws rotate in the same direction, and at the same speed. Shaft rotation transports the pulp axially through the machine. Key to the fiber property modification within the machine are the reverse-flighted screw sections which have small slots machined into the flights and are positioned periodically along the length of both screws. These reverse-flighted sections serve to reverse the flow of stock through the machine, thereby introducing backpressure to the stock stream.
Thus the stock travels forward axially until it encounters a backpressure zone. The pressure builds in this zone, but because of the slots in the reverse flights, the pressure behind is greater than the pressure ahead. In this manner the stock is forced through the slots where it encounters the next (lower pressure) forward-flighted section of the screws. It is theorized that this compression/expansion action further enhances the modification of fiber properties. Typically the Bivis shaft disperser is set up to include three or four working zones. The injection ports can be used to inject different chemicals into each of the individual working zones. The extraction ports associated with each working zone can be used to extract liquid if desired. Although-not measured, the volume-to-surface area ratio of the Bivis shaft disperser is believed to be slightly less than that of the Maule shaft disperser.
Figure 8 is an axial view of a reverse-flighted section of the twin screws of the apparatus of Figure 7. Shown are screws 92 and 93, each having slots 94 machined out of their flights. As shown, the flights of each screw overlap.
Figure 9 is an axial view of a forward-flighted section of the twin screws of the apparatus of Figure 7, illustrating the overlap of the screw flights 95 and 96.
Figure 10 is an expanded sectional view of a working zone of the apparatus of Figure 7, showing the upstream forward-flighted screw section "AH, the reverse-flighted screw section "B~, and the downstream forward-flighted screw section HCn. This figure serves to illustrate the flow of stock (represented by the arrows) through the reverse-flighted screw section.
EXAMPLES
Having described the TD Index and the method of carrying out this invention, the invention will now be further described in detail with reference to the following examples.
ExamDle 1.
Secondary fiber (office waste grade) was treated by the process described in Figure 4. Specifically, the secondary fiber was repulped at a consistency of 15%, cleaned, pressed to a pre-disperser 2147fi87 consistency of 22.9%, then fed to a Maule shaft disperser as illustrated in Figure 5. The fines content of the pulp fed to disperser was 8.5 weight percent. The disperser was maintained at a temperature of 175-F. Power input to the disperser was approximately 1.39 horsepower-day per ton of fiber (HPD/T). Pre- and post-disperser samples were taken and made into dry 24 gsm. handsheets per the previously defined method. Measurement of the TD Index was carried out as previously described. The results are set forth in Table 1 below. (The ~TD~ is the Throughdryability Index, expressed as kilopascals ~. The "Tensile" is the tensile strength, expressed as grams per inch of sample width. The "Tear" is the Elmendorf tear strength, expressed as grams-force per four sheets. The "Caliper~ is thickness, expressed as inches. The "TEA" is the tensile energy absorbed, expressed as gram-centimeters per square centimeter.) Sample TDTensile Tear Caliper TEA
Pre-disperser 0.111274 18.0 0.0058 8.1 Post-disperser 0.30739 17.2 0.0076 3.8 Example 2.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 175-F., the pre-disperser consistency was 34.7 percent, and the power input to the disperser was 2.12 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as previously described. The pre-disperser fines content was 7.4 weight percent. The results~are set forth in Table 2.
TDTensile Tear Caliper TEA
Pre-disperser 0.121278 18.0 0.0060 6.6 Post-disperser 0.53585 14.0 0.0082 2.5 Example 3.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 150-F., the pre-disperser consistency was 34.6%, and the power input to the disperser 2l~7687 was 2.15 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as previously described. The results are set forth in Table 3.
TD Tensile Tear Caliper TEA
Pre-disperser 0.14 1334 19.2 .0060 7.9 Post-disperser 0.37 884 18.0 .0070 4.9 10Example 4.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 81-F., the pre-disperser consistency was 26.8% and the power input to the disperser was 2.44 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as previously described. The pre-disperser fines content was 7.2 weight percent. The results are set forth in Table 4.
TD Tensile Tear Caliper TEA
Pre-disperser 0.10 1409 19.6 .0055 8.3 Post-disperser 0.17 1125 20.0 .0062 6.7 Example 5.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 79-F., the pre-disperser consistency was 34.6% and the power input to the disperser was 1.18 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as prev;ously described. The pre-disperser fines content was 6.9 weight percent. The results are set forth in Table 5.
TD Tensile Tear CaliDer TEA
Pre-disperser 0.10 1322 - .0055 5.7 35Post-disperser 0.14 1189 22.4 .0060 6.7 21~7687 Example 6.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 78-F., the pre-disperser consistency was 37.1% and the power input to the disperser was 2.95 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as previously described. The pre-disperser fines content was 7.8 percent. The results are set forth in Table 6.
TD Tensile Tear CaliDer TEA
Pre-disperser 0.10 1435 20.0 .0055 8.1 Post-disperser 0.19 1155 21.6 .0064 6.1 ExamDle 7.
Well-washed secondary fiber at approximately 50% consistency was fed in crumb form to a Bivis twin screw shaft disperser (Clextral Company, Firminy Cedex, France) via a screw feeder as illustrated in Figures 7-10. The fines content of the washed fiber was 5.2 weight percent. Steam was introduced into the interior compartment to raise the pulp temperature to approximately 220-F. (105-C.J. The product from the first Bivis disperser was sent to a second Bivis disperser operated under the same conditions. From the second disperser, the pulp was sent to a quench tank at 10-C. The pulp was then gravity dewatered and made into 24 gsm handsheets as previously described and the TD Index was determined as previously described. The results are set forth in Table 7.
TD Tensile Tear Caliper TEA
Pre-Bivis 0.08 1072 18.5 .0061 5.65 Post-Bivis 0.71 388 10.5 .0079 1.28 The results from the foregoing examples illustrate that the Throughdryability Index of secondary fibers can be dramatically increased (and hence the throughdrying behavior of the fibers can be improved) by subjecting the fibers to appropriate working forces at high consistency and high temperature in a shaft disperser. Also, the application of high consistency working forces improves the tissue making character of the fibers by decreasing the tensile and tearing strengths while increasing bulk.
ExamPle 8 Cenibra eucalyptus fibers were pulped for 15 minutes at 10%
consistency and dewatered to 30% consistency. A softening agent (Berocell 584) was added to the pulp in the amount of 10 lb. Berocell per ton dry fiber, and the pulp was then fed to a Maule shaft disperser as illustrated in Figure 5. The disperser was operated at 160-F with a power input of 2.2 HPD/T.
The resulting dispersed eucalyptus fibers were made into a two-layered tissue having a softwood fiber layer and a eucalyptus fiber layer. Prior to formation, the northern kraft softwood fibers (LongLac-l9) were pulped for 60 minutes at 4% consistency, while the dispersed eucalyptus fibers were pulped for 2 minutes at 4%
consistency. Each layer was independently formed on separate forming fabrics at 0.05% consistency at a speed of about 50 feet per minute and the resulting two webs were couched together at approximately 10%
consistency to form a two-layered web. The resulting layered web was transferred to a papermaking felt and thereafter pressed onto the surface of a Yankee dryer, where the web was dried and creped at a 1.3 crepe ratio. The dryer side of the layered web was composed entirely of the softwood fibers and had a basis weight of 7.25 lb./2880 ftZ (dryer basis weight). The air side of the layered web was composed entirely of the dispersed eucalyptus fibers of equal basis weight. After creping, the tissue was wound into bath rolls under minimum draw.
The resulting tissue had the following properties: tensile strength = 858 grams per 3 inches width (machine direction) and 488 grams per 3 inches width (cross-machine direction); stretch = 30.4%
(machine direction) and 5.8% (cross-machine direction); Panel Softness = 7.70. (Panel Softness is determined by a trained sensory panel which rates tissues for softness on a scale of from 0 to about 9.5.) For comparison, a typical softness value for throughdried material at similar strength is 7.15.
21~75~7 ExamPle 9 Southern hardwood kraft fibers (Coosa River-59) were pulped for 15 minutes at 10% consistency and dewatered to 28% consistency. A
debonder (Berocell 584) was added to the pulp in the amount of 10 lb.
Berocell per ton dry fiber. The pulp was then fed to a Maule shaft disperser. The disperser was operated at 160-F with a power input of 2.2 HPD/T.
The resulting dispersed hardwood fibers were made into a two-layered tissue having a softwood layer and a hardwood layer.
Specifically, northern softwood kraft fibers (LongLac-l9) were pulped for 60 minutes at 4% consistency, while the dispersed hardwood fibers were pulped for 2 minutes at 4% consistency. Each layer was independently formed on separate forming fabrics at 0.05% consistency and the resulting webs were couched together at about 50 feet per minute at approximately 10% consistency to form a single layered web.
The resulting layered web was transferred to a papermaking felt and thereafter pressed onto the surface of a Yankee dryer, where the web was dried and creped at a 1.3 crepe ratio. The dryer side of the layered web was composed entirely of softwood fibers and had a basis weight of 7.25 lb./2880 ft2 (dryer basis weight). The air side of the web was composed entirely of the dispersed hardwood fibers of equal basis weight. After creping, the tissue was wound into bath tissue rolls under minimum draw.
The resulting tissue had the following properties: tensile strength = 689 grams per 3 inches width (machine direction) and 466 grams per 3 inches width (cross-machine direction); stretch = 32%
(machine direction) and 5.6% (cross-machine direction); Panel Softness = 7.65. For comparison, a typical softness value for throughdried material at similar strength is 7.30.
Examples 8 and 9 both illustrate the softness advantages of treating virgin hardwood fibers with a disperser in accordance with the method of this invention for making wet-pressed tissues.
Example 10 A secondary fiber blend (45 percent laser ledger, 45 percent laser computer print-out, 10 percent white ledger) was pulped for 15 minutes at 40- C and 15 percent consistency. The resultant slurry 21476~7 was screened at ambient temperature and 3.0 percent consistency. The slurry was then dehydrated to 30 percent consistency using a belt press and screw fed directly to a shaft disperser (J. M. Voith GmbH, Heidenheim, Germany) similar to that illustrated in Figure 5. The disperser was maintained at a temperature of 176- F. Power input to the disperser was approximately 4.17 HPD/T. Pre- and post-disperser samples were taken and made into 24 gsm handsheets per the previously defined method. As the improvement in TD Index occurs under all drying conditions, the TD Index of this sample was measured under different flow conditions than the previous examples. Specifically, the air flow rate was 1.0 kg./m2 sec., the air temperature was 90 C, and the initial moisture ratio was 3.5. Since each of these factors affects the TD Index, the TD Index values in this example are not directly relatable to those of the previous examples. Still, the 15 improvement in the TD Index is readily apparent. The results are set forth in Table 8 below.
Table 8 Sample TD Fines Pre-disperser 0.07 22.0 Post-disperser 0.18 23.3 Example 11 The same secondary fiber blend was treated as described in Example 10, except the disperser was maintained at a temperature of 166- F and the power input to the disperser was approximately 5.28 HPD/T. Pre- and post-disperser samples were taken and made into 24 gsm handsheets as previously described. Measurement of the TD
Index was carried out as for Example 10. The results are set forth in Table 9 below.
Table 9 SamDle TD Fines Pre-disperser 0.07 22.0 Post-disperser 0.18 20.6 21~7fi87 Example 11 The same secondary fiber blend was treated as described in Example 10, except the disperser was maintained at a temperature of 147 F and the power input to the disperser was approximately 5.55 HPD/T. Pre- and post-disperser samples were taken and made into 24 gsm handsheets as previously described. Measurement of the TD
Index was carried out as for Example 10. The results are set forth in Table 10 below:
Table 10 Sample TD Fines Pre-disperser 0.07 22.0 Post-disperser 0.17 20.6 As illustrated by Examples 10, 11 and 12, the method of this invention greatly improves the TD Index even at very high fines levels.
It will be appreciated that the foregoing examples, given for purposes of illustration, are not to be construed as limiting the scope of this invention, which is defined by the following claims and all equivalents thereto.
Background of the Invention In the manufacture of certain paper sheet products, such as tissue and paper towels, one method of drying the sheet after formation and dewatering is to pass heated air through the wet sheet in a process well known in the papermaking art as throughdrying.
Throughdrying is advantageous in that it minimizes compaction of the web and thereby produces a bulkier product compared to conventional wet press manufacturing processes, which rely on high levels of compression of the wet web and on a Yankee dryer to dry the web.
However, throughdrying has some disadvantages in that it requires a substantial amount of expensive equipment and energy to carry out the drying process. In particular, the drying efficiency of the throughdrying process is in large part dependent upon the air permeability of the wet sheet which permits the hot air to pass therethrough. Air permeability is especially a problem for sheets made from fiber furnishes containing secondary (recycled) fibers, which inherently impart poor air permeability to the wet sheets into which they are incorporated. With the continual efforts to utilize more secondary fibers in paper products for environmental reasons, there is a need to improve the throughdryability of secondary papermaking fibers.
SummarY of the Invention It has been surprisingly discovered that the ease in which secondary papermaking fibers can be throughdried can be improved by pre-treating the fibers of the papermaking furnish in a wet mechanical process in which the fibers are appropriately worked while suspended in a high consistency aqueous slurry. The effectiveness of the pretreatment is manifested by an increase of the Throughdryability Index (hereinafter defined and referred to as the ~TD Index") of the fibers. An increase in the TD Index translates into faster throughdrying machine speeds for a given furnish and 21 ~ 7687 basis weight, which results in improved operating efficiency. The method of this invention can be utilized for any papermaking fibers, but is especially advantageous for improving the TD Index of secondary fiber furnishes and furnishes containing a significant amount of fines and/or short fibers, such as hardwood fibers. (As used herein, "short fibers" are fibers having a population average length of from 0.5 to about 1 millimeter as determined by using a Kajaani FS-200 fiber length analyzer.) In some cases, the TD Index of secondary fiber furnishes can be surprisingly improved beyond that of untreated virgin furnishes. As used herein, ~fines~ are particles that pass through a 200 mesh screen having a 76 micrometer diameter opening. They can be measured in accordance with TAPPI Test Method T261 pm-80 (1989).
In addition, while the fiber treatment of this invention is particularly advantageous for throughdrying processes and products, product improvements can also be realized when the treated fibers of this invention are used for making wet pressed tissue products as well. More specifically, it has been found that substituting the treated fibers of this invention for a portion of the fibers of a given tissue furnish, the softness of the resulting tissue can be increased without loss of strength. This is especially effective when treating hardwood fibers and combining the treated hardwood fibers with other fibers, such as untreated softwood fibers, either bler,ded or layered. The treated hardwood fibers improve the softness of the resulting product while the untreated softwood fibers retain the strength. Softness can be further enhanced by adding a softening agent to the treated fibers either before treatment or after treatment. Certain softening agents also provide an unexpected increase in bulk as well as enhancing the softness of the tissue.
Hence in one aspect, the invention resides in a method of making a tissue comprising: (a) forming an aqueous suspension of papermaking fibers having a consistency (dry weight percent fibers in the aqueous suspension) of about 20 or greater; (b) passing the aqueous suspension through a shaft disperser at a temperature of 150-F. or greater with a power input of at least about 1 horsepower-day per ton of dry fiber, wherein the TD Index of the fibers is increased about 25 percent or greater, preferably about 50 percent or greater, and 2I~7687 more preferably about 75 percent or greater; (c) feeding the fibers through a tissue making headbox to form a wet web; and (d) drying the web, such as by throughdrying, to form a dried tissue.
In another aspect, the invention resides in a method of making tissue comprising: (a) forming an aqueous suspension of papermaking fibers having a consistency of about 20 or greater; (b) passing the aqueous suspension through a shaft disperser at a temperature of 150F. or greater with a power input of at least about 1 horsepower-day per ton of dry fiber, wherein the TD Index of the fibers is about 0.15 or greater, preferably about 0.2 or greater, more preferably about 0.3 or greater, and most preferably about 0.5 or greater;
(c) feeding the fibers through a tissue making headbox to form a wet web; and (d) drying the web, such as by throughdrying, to form a dried tissue.
In a further aspect, the invention resides in a throughdried sheet made from a furnish comprising at least about 25 dry weight percent secondary fibers, and/or having at least about 7 weight percent fines and/or having at least about 20 percent short fibers, said furnish having a TD Index of about 0.15 or greater, preferably about 0.20 or greater, more preferably about 0.30 or greater, and most preferably about 0.5 or greater. If present, the amount of secondary fibers in the furnish can be anywhere within the range of about 25 to about 50, 75, or 100 dry weight percent. In general, secondary fibers inherently have a high proportion of fines and/or short fibers. If present, the amount of fines can be about 7 weight percent or greater, more particularly about 10 weight percent or greater, still more particularly from about 10 to about 25 weight percent. If present, the amount of short fibers can be about 20 weight percent or greater, more specifically about 50 weight percent or greater, still more specifically about 75 percent or greater.
Papermaking fibers useful for purposes of this invention include any cellulosic fibers which are known to be useful for making paper, particularly those fibers useful for making relatively low density tissue papers such as facial tissue, bath tissue, dinner napkins, paper towels, and the like. As used herein, the term ~tissue" is used generically and is intended to include all such products. Such ~1~7687 products can be creped or uncreped. The most common papermaking fibers include virgin softwood and hardwood fibers, as well as secondary or recycled cellulosic fibers. As used herein, "secondary fiber" means any cellulosic fiber which has previously been isolated from its original matrix via physical, chemical or mechanical means and, further, has been formed into a fiber web, dried to a moisture content of about 10 weight percent or less and subsequently reisolated from its web matrix by some physical, chemical, or mechanical means. Fibers which have been passed through a shaft disperser as described herein are sometimes referred to as ~dispersed fibers".
The basis weight of the throughdried sheet can be from about 5 to about 50, preferably from about 10 to about 40, and more preferably from about 20 to about 30 grams per square meter. It will be appreciated that lower basis weight sheets inherently have greater permeability for a given furnish. Hence the greatest advantage of this invention is obtained with relatively higher basis weights where the sheets are normally more difficult to throughdry. The invention is particularly suitable for making throughdried single-ply bath tissue having a basis weight of about 25 grams per square meter.
The consistency of the aqueous suspension which is subjected to the treatment of this invention must be high enough to provide significant fiber-to-fiber contact or working which will alter the surface properties of the treated fibers. Specifically, the consistency can be at least about 20, more preferably from about 20 to about 60, and most preferably from about 30 to about 50 dry weight percent. The consistency will be primarily dictated by the kind of machine used to treat the fibers. For some rotating shaft dispersers, for example, there is a risk of plugging the machine at consistencies above about 40 dry weight percent. For other types of shaft dispersers, such as the Bivis machine (commercially available from Clextral Company, Firminy Cedex, France), consistencies greater than 50 can be utilized without plugging. It is desirable to utilize a consistency which is as high as possible for the particular machine used.
The temperature of the fibrous suspension can preferably be about 150F. or greater, more preferably about 210-F. or greater, and 2147fi~7 more preferably about 220F. or greater. In general, higher temperatures are better for increasing the TD Index. The upper limit on the temperature is dictated by whether or not the disperser is pressurized, since the aqueous fibrous suspensions within apparatus operating at atmospheric pressure cannot be heated beyond the boiling point of water. A suitable temperature range is from about 170-F. to about 220-F.
The amount of power applied to the fibrous suspension also impacts the resulting TD Index. In general, increasing the power input will increase the TD Index. However, it has also been found that the improvement (increasing) of the TD Index falls off upon reaching a power input of about 2 horsepower-days per ton (HPD/T) of dry fiber in suspension. A preferred range of power input is from about 1 to about 3 HPD/T, more preferably about 2 HPD/T or greater.
In working the fibers within the disperser, such as by shearing and compression, it is necessary that the fibers experience substantial fiber-to-fiber contact by rubbing or shearing in addition to rubbing or shearing contact with the surfaces of the mechanical devices used to treat the fibers. Some compression, which means pressing the fibers into themselves, is also desireable to enhance or magnify the effect of the rubbing or shearing of the fibers. The desired fiber-to-fiber contact can in part be characterized by apparatus having a relatively high volume-to-working surface area ratio which increases the likelihood of fiber-to-fiber contact. The working surface for purposes herein is defined as that surface of the apparatus which contacts the majority of the fibers passing through.
For example, disc refiners have a very low volume-to-working surface area (approximately 0.05 centimeters) because there is a relatively small volume or space between the opposed rotating discs (working surfaces). Such devices work the fibers primarily by contact between the working surfaces and the fibers. However, the apparatus particularly useful for purposes of this invention, such as the various types of shaft dispersers, have a much higher volume-to-working surface area. Such volume-to-working surface area ratios can be about 1 centimeter or greater, preferably about 3 centimeters or greater, and more specifically from about 5 to about 10 centimeters.
21~ 76~ 7 These ratios are orders of magnitude greater than those of disc refiners.
The measure of the appropriate amount of shearing and compression to be used lies in the end result, which is the achievement of an increased TD Index. A number of shaft dispersers or equivalent mechanical devices known in the papermaking industry can be used to achieve varying degrees of the desired results.
Suitable shaft dispersers include, without limitation, nonpressurized shaft dispersers, such as the Maule shaft disperser, and pressurized shaft dispersers, such as the Bivis machines and the like.
If softening agents are used to enhance the softness of the final tissue product, suitable agents include, without limitation, fatty acids, waxes, quaternary ammonium salts, dimethyl dihydrogenated tallow ammonium chloride, quaternary ammonium methyl sulfate, carboxylated polyethylene, cocamide diethanol amine, coco betaine, sodium lauroyl sarcosinate, partly ethoxylated quaternary ammonium salt, distearyl dimethyl ammonium chloride, and the like.
Examples of suitable commercially available chemical softening agents include, without limitation, Berocell 564 and 584 manufactured by Eka Nobel Inc., Adogen 442 manufactured by Whitco Sherex Chemical Company, Quasoft 203 manufactured by Quaker Chemical Company, and Arquad 2HT-75, manufactured by Akzo Chemical Company.
Brief DescriDtion of the Drawinq Figure 1 is a schematic flow diagram of the apparatus used for determining the TD Index.
Figure 2 is an exploded perspective view of the sample holder of the apparatus of Figure 1, including the sliding sample tray used to place the sample holder into the drying apparatus.
Figure 3 is a representative depiction of a typical plot of pressure drop versus moisture ratio as generated while testing a sample using the apparatus described in Figure 1 above.
Figure 4 is a schematic process flow diagram of a method of treating fibers in accordance with this invention using a shaft disperser to work the fibers.
Figure 5 is a cut-away perspective view of the shaft disperser of Figure 4.
21476~7 Figure 6 is an alternative schematic process flow diagram of a method in accordance with this invention using a pair of Bivis shaft dispersers in series.
Figure 7 is a sectional view of a Bivis shaft disperser useful for purposes of this invention.
Figure 8 is a sectional view, viewed in the axial direction, of the reverse-flighted screws of the Bivis shaft disperser, illustrating the cut-out notches in the flights.
Figure 9 is a sectional view, viewed in the axial direction, of the forward-flighted screws.
Figure 10 is a sectional view of a reversed-flighted section of the machine, illustrating the flow of the fibrous suspension.
Detailed Description of the Invention The ThroughdrYabilitY Index During throughdrying, it is generally understood that the drying rate is high and relatively constant at high moisture ratios (constant rate period). The drying rate begins decreasing rather rapidly after reaching a certain critical moisture ratio (falling rate period) in the sheet. If a constant air permeation rate is maintained throughout the-drying period, the pressure drop is also expected to decrease as the moisture ratio decreases (or as the drying process continues). The manner in which the pressure drop varies during the throughdrying process under a constant air permeation rate is of primary interest for purposes of this invention because it provides a quantitative means for measuring the air permeability of the sheet while being dried. If one can accurately measure the instantaneous absolute humidity of the outlet air after drying a tissue sample, one can readily calculate the instantaneous moisture ratio from the humidity of the outlet air and the initial and the final moisture ratios of the tissue sample as shown below:
Xm(t) = Xo~ (Xo~Xend) ~out(t) ~in~ dt wherein ~XoN= the moisture ratio of the test sample at the beginning of the test, expressed as kilograms of water per kilogram of bone dry fiber;
21476~7 "Xend~= the moisture ratio of the test sample at the end of the test, expressed as kilograms of water per kilogram of bone dry fiber;
~Xmll= the instantaneous moisture ratio of the test sample, expressed as kilograms of water per kilogram of bone dry fiber;
"Yjnn= the humidity of the drying air immediately prior to reaching the sample, expressed as kilograms of water per kilogram of dry air;
"Y~t"= the humidity of the drying air immediately after passing through the sample, expressed as kilograms of water per kilogram of dry air; and "t"= elapsed time, expressed in seconds.
Calculating the moisture ratio X~ from the humidity data for the entire drying period data enables one to plot pressure drop as a function of the instantaneous moisture ratio. The inverse of the area under the resulting curve is referred to herein as the TD Index, expressed as kilopascals-~. This index is a measure of the air permeability of the wet sheet and reflects the ease in which a paper sheet made from a particular furnish can be throughdried. Higher TD
Index values reflect greater ease in throughdrying, whereas lower values reflect greater difficulty in throughdrying.
As will be described below, measurement of the TD Index requires that the fibers in question be formed into a handsheet having a basis weight of 24 grams per square meter. This is accomplished by diluting a fiber sample in water to a consistency of 2.5 weight percent in a British Pulp Disintegrator and allowing the dispersed sample to soak for 5 minutes. The sample is then pulped for 10 minutes at ambient temperature, diluted to 0.04 percent consistency, and formed into a handsheet on a British Handsheet Mold (The Hermann Mfg. Co., Lancaster, Ohio). The handsheet is couched off of the mold by hand using a blotter without applying any pressure. The handsheet is dried for 2 minutes to absolute dryness using a Valley steam hotplate and a standard weighted canvas cover having a lead filled (4.75 pounds) brass tube at one end to maintain uniform tension. The TD Index for the resulting dried handsheet is then determined as described herein and the measured TD Index value 21~687 is assigned to the fibers or furnish from which the handsheet was made.
Referring now to Figure 1, the apparatus for determining the TD
Index will be described in greater detail. Unless otherwise specified, conduit in the mainstream of air flow has a 1.5 inch inside diameter. Air for drying the samples is provided by two "oil free" compressors 1, each rated for 29.9 cubic feet per minute at 90 psi. (Model DN 1024H-3DF, Atlas Copco, Cleveland, Ohio). The outlet of the compressors is suitably connected to the inlet of a condensed water separator 2 (Model WS0-08-000, Wilkerson, Engelwood, Colorado), which serves to remove any liquid water entrained in the air stream. The outlet of the separator is suitably connected to the inlet of a molecular sieve 3 (Model M530, Wilkerson) which serves to eliminate particulate matter in the air having a particle size greater than about 0.05 microns. The outlet of the molecular sieve is suitably connected to a compressed air dryer 4 (Wilkerson model DHA-AE-000) with an outlet flow of 49 cubic feet per minute. The outlet of the dryer is connected to the inlet of a surge tank 5 (approximately 75 cubic feet capacity). The outlet of the surge tank is suitably connected to two additional oil heat exchangers 6 and 7 (5 liter capacity/250-C. max. temp./6 bar max. pressure, Apparatebau Wiesloch GmbH, Weisloch, Germany) in series which serve to further heat the air to the desired throughdrying temperature. In between the surge tank and the two heat exchangers are a moisture monitor 8 (Aquanel, Gerhard GmbH, Blankebach, Germany), a gate-type control valve 9 (DIN R65, 1.5 inch, PN 16, Henose, Hamburg, Germany) for controlling the flow rate of the air, an orifice plate 10 (25 millimeter diameter opening, RST 37-2 PN6 DIN 2527-32-5784, University of Karlsruhe, Karlsruhe, Germany), and a manometer 11 (Betz, Gottingen, Germany), which together are used to determine the air flow rate. Other valves and piping (not shown) which are not essential to the operation of the apparatus can be present for convenience at various places to isolate or by-pass gauges and other devices. The outlet of the second heat exchanger is directly connected to a sample housing 12, which is designed to receive and hold a slidable sample tray 13 (see Figure 2) into which a sample holder (see Figure 2) is placed. All of the air passes through the sample placed in the sample holder. An inflatable gasket mounted within the sample housing assures a positive seal between the sample housing and the slidable sample tray when the gasket is activated. A
diffuser 14 is suitably connected to the outlet of the sample housing such that the cross-sectional flow area is expanded to 11,600 square millimeters in order to slow down the air flow to facilitate more accurate moisture measurement. The diffuser is suitably connected to a vent tube which carries the air to a suitable exhaust system. A
differential temperature sensor 16 (resistance type differentiation) is suitably connected to measure the temperature of the air before and after the sample. A differential pressure sensor 17 (PU 1000, 0-1000 millibar, llOV AC) is suitably connected to measure the pressure drop across the sample. A second, more sensitive moisture monitor 18 (infrared; twenty-five measurements per second; made by Paderborn University, Paderborn, Germany) measures the moisture content of the air leaving the sample. All three sensors are linked to a Schlumberger data acquisition system 19 which is linked to a computer 20 (RMC 80286 processor) for correlating the data.
Figure 2 illustrates the sample holder and the manner in which the sample is mounted within the sample holder, including the sliding sample tray 13 adapted to hold the sample holder and slide it in and out of the sample housing. Shown in Figure 2 is the top of the sample holder 21, which is the upstream portion, and the bottom of the sample holder 22, which is the downstream portion. The bottom of the sample holder contains a support fabric 23 (Asten 937, Asten Corporation, Appleton, WI) upon which the sample rests. Sandwiched in between the top and bottom is the handsheet sample 24 which has been cut to the appropriate size. A thin line of grease (not visible in this view) positioned around the inside edge of the top of the sample holder provides a seal between the sample and the top of the sample holder when the sample is secured. The top of the sample holder contains two registration pins 25 which become inserted into registration holes 26 in the bottom of the sample holder and the two halves are secured by means of six screws 27 with appropriate threaded holes.
Having identified the apparatus for determining the TD Index, the procedure for determining the TD Index can now be described.
21~7687 Generally speaking, to determine the TD Index for a given test sample (24 gsm handsheet), the sample is carefully wetted to a particular moisture level and dried in the apparatus described above under controlled conditions of constant air mass flow rate. The moisture level in the sample is continuously calculated by a computer, based on the humidity measurements of the air before and after the sample during the test. The measured pressure drop across the sample is plotted as a function of the calculated moisture level of the sample, and the area under the curve is the TD Index.
More specifically, the handsheet sample to be tested is cut into a 10.25 centimeter diameter circle which fits into the sample holder of the apparatus and is only slightly larger than the sample holder opening. During the test, only a 10 centimeter diameter circle of the sample is exposed to air flow. Accordingly, the portion of the circular sample outside the sample holder opening is impregnated with grease (Compound 111 Valve Lubricant and Sealant, Dow Corning Corporation, Midland, Michigan) before being wetted for the test to prevent any moisture from being wicked outside the circle as well as establishing a more positive seal between the sample and the sample holder. This is accomplished by applying and rubbing the grease around the inside edge of the top half (upstream half) of the sample holder. The sample is then placed onto the bottom half of the sample holder which contains a piece of throughdrying fabric (Asten 937) for supporting the sample. The top half of the sample holder is then clamped onto the bottom half of the sample holder, thereby impregnating the outer edge of the sample with the grease. The supported sample is then wetted by spraying with a fine mist until a moisture level of 3.0 kilograms of water per kilogram of bone dry fiber is reached. During spraying, a cover guard should be placed over the sample holder to prevent the sample holder from being sprayed and to keep all of the sprayed water directed at the 10 centimeter circle. The moisture in the sample is accurately determined by the weight difference before and after wetting.
While the sample is being prepared, the air system is turned on at a predetermined constant flow rate of 3.0 kilograms per square meter per second and heated to a temperature of 175C. When steady state is reached, the air temperature will be steady and constant, 21~ 7~87 the humidity will be zero, and the pressure drop will be zero. After the reference steady state conditions are achieved, the sample holder with the wetted test sample is placed into the sliding sample tray and slid into the sample housing of the apparatus. The humidity and the pressure drop are continuously monitored by the instruments and the computer, which provides a plot of pressure drop versus moisture ratio. A typical plot is illustrated in Figure 3. (Note that time increases from right to left in this plot.) As shown, the pressure drop shows a very rapid initial increase and thereafter quickly starts decreasing, typically reaching a constant level in about four or five seconds. The computer then integrates the inverse of the area under the curve and calculates the TD Index as earlier described.
Figure 4 is a block flow diagram illustrating overall process steps for treating fibers in accordance with this invention. Shown is the paper furnish 28 to be treated being fed to a high consistency pulper 29 (Model ST6C-W, Bird Escher Wyss, Mansfield, MA) with the addition of dilution water 30 to reach a consistency of about 15 percent. Prior to being pumped out of the pulper, the stock is diluted to a consistency of about 6 percent. The pulped fibers are fed to a scalping screen 31 (Fiberizer Model FT-E, Bird Escher Wyss) with additional dilution water in order to remove large contaminants.
The input consistency to the scalping screen is about 4 percent. The rejects from the scalping screen are directed to waste disposal 32.
The accepts from the scalping screen are fed to a high density cleaner 33 (Cyclone Model 7 inch size, Bird Escher Wyss) in order to remove heavy contaminants which have escaped the scalping screen.
The rejects from the high density cleaner are directed to waste disposal. The accepts from the high density cleaner are fed to a fine screen 34A (Centrisorter Model 200, Bird Escher Wyss) to further remove smaller contaminants. Dilution water is added to the fine screen feed stream to achieve a feed consistency of about 2 percent.
Rejects from the fine screen are directed to a second fine screen 34B
(Axiguard, Model 1, Bird Escher Wyss) to remove additional contaminants. The accepts are recycled to the feed stream to the fine screen 34A and the rejects are directed to waste disposal. The accepts from the fine screen, with the addition of dilution water to 2l 476~7 reach a consistency of about 1 percent, are then passed to a series of four flotation cells 35, 36, 37 and 38 (Aerator Model CF1, Bird Escher Wyss) to remove ink particles and stickies. Rejects from each of the flotation cells are directed to waste disposal. The accepts from the last flotation cell are fed to a washer 39 (Double Nip Thickener Model 100, Black Clawson Co., Middletown, OH) to remove very small ink particles and increase the consistency to about 10 percent. Rejects from the washer are directed to waste disposal.
The accepts from the washer are fed to a belt press 40 (Arus-Andritz Belt Filter Press Model CPF 20 inches, Andritz-Ruthner Inc., Arlington, TX) to reduce the water content to about 70 percent.
Pressate is directed to waste disposal. The resulting partially dewatered fibrous material is then fed to a shaft disperser 41 (GR II, Ing. S. Maule & C. S.p.A., Torino, Italy), described in detail in Figure 5, in order to work the fibers to increase the TD
Index in accordance with this invention. Steam 42 is added to the disperser feed stream to elevate the temperature of the feed material. The resulting treated fibers 43 can be directly used as feedstock for papermaking or otherwise further treated as desired.
Figure 5 is a cut-away perspective view of a preferred apparatus for treating fibers in accordance with this invention as illustrated in Figure 4. The particular apparatus is a shaft disperser, type GR II, manufactured by Ing. S. Maule & C. S.p.A., Torino, Italy.
This apparatus has a volume-to-working surface area of about 8.5 centimeters. Shown is an upper cylindrical housing 51 and a lower cylindrical housing 52 which, when closed, enclose a rotating shaft 53 having a multiplicity of arms 54. The upper housing contains two rows of knurled fingers 55 and three inspection ports 56. At one end of the upper housing is an inlet port 57. At the inlet end of the rotating shaft is drive motor 58 for turning the shaft. At the outlet end of the rotating shaft is a bearing housing 59 which supports the rotating shaft. The inlet end of the rotating shaft contains a screw feed section 60 which is positioned directly below the inlet and serves to urge the feed material through the disperser. The outlet 61 of the disperser comprises a hinged flap 62 having a lever 63 which, when the disperser is closed up, is engaged by hydraulic air bags 63 mounted on the upper housing. The air bags provide controllable resistance to the rotation of the hinged flap and hence provide a means of controlling the back pressure within the disperser. Increasing the back pressure increases the degree to which the fibers are worked and thereby increases the TD Index.
During operation, the knurled fingers interdigitate with the arms of the rotating shaft to work the feed material therebetween.
Figure 6 is a block flow diagram of an alternative process of this invention utilizing a pair of Bivis shaft dispersers. As illustrated, papermaking pulp, preferably secondary fiber pulp, at a consistency of about 50 percent, is fed to a screw feeder. The screw feeder meters the feedstock to the first of two Bivis shaft dispersers in series. Each Bivis shaft disperser typically has three or four compression/expansion zones. Steam is injected into the first Bivis shaft disperser to raise the temperature of the fibers to about 212-F. The worked pulp is transferred to the second Bivis shaft disperser operating at the same conditions as the first disperser. The worked pulp from the second machine can be quenched by dropping it into a cold water bath and thereafter dewatered to a suitable consistency.
Figure 7 is a sectional elevational view of a twin screw Bivis shaft disperser useful for purposes of this invention. Shown are the inlet 71, feed screw 72, forward flighted screws 73, 74, 75, and 76, reverse-flighted screws 77, 78, 79 and 80, outlet 81, injection ports 82, 83, 84 and 85, optional extraction ports 86, 87, 88 and 89, and thermocouples 90. In operation, pulp is introduced into the Bivis through the inlet. The pulp then encounters the short feed screw, which serves to introduce the pulp into the first working zone. The working zones consist of a pair of slightly overlapping screws encased in cylinders with less than 1 millimeter clearance between the screw flights and the cylinder walls. The twin screws rotate in the same direction, and at the same speed. Shaft rotation transports the pulp axially through the machine. Key to the fiber property modification within the machine are the reverse-flighted screw sections which have small slots machined into the flights and are positioned periodically along the length of both screws. These reverse-flighted sections serve to reverse the flow of stock through the machine, thereby introducing backpressure to the stock stream.
Thus the stock travels forward axially until it encounters a backpressure zone. The pressure builds in this zone, but because of the slots in the reverse flights, the pressure behind is greater than the pressure ahead. In this manner the stock is forced through the slots where it encounters the next (lower pressure) forward-flighted section of the screws. It is theorized that this compression/expansion action further enhances the modification of fiber properties. Typically the Bivis shaft disperser is set up to include three or four working zones. The injection ports can be used to inject different chemicals into each of the individual working zones. The extraction ports associated with each working zone can be used to extract liquid if desired. Although-not measured, the volume-to-surface area ratio of the Bivis shaft disperser is believed to be slightly less than that of the Maule shaft disperser.
Figure 8 is an axial view of a reverse-flighted section of the twin screws of the apparatus of Figure 7. Shown are screws 92 and 93, each having slots 94 machined out of their flights. As shown, the flights of each screw overlap.
Figure 9 is an axial view of a forward-flighted section of the twin screws of the apparatus of Figure 7, illustrating the overlap of the screw flights 95 and 96.
Figure 10 is an expanded sectional view of a working zone of the apparatus of Figure 7, showing the upstream forward-flighted screw section "AH, the reverse-flighted screw section "B~, and the downstream forward-flighted screw section HCn. This figure serves to illustrate the flow of stock (represented by the arrows) through the reverse-flighted screw section.
EXAMPLES
Having described the TD Index and the method of carrying out this invention, the invention will now be further described in detail with reference to the following examples.
ExamDle 1.
Secondary fiber (office waste grade) was treated by the process described in Figure 4. Specifically, the secondary fiber was repulped at a consistency of 15%, cleaned, pressed to a pre-disperser 2147fi87 consistency of 22.9%, then fed to a Maule shaft disperser as illustrated in Figure 5. The fines content of the pulp fed to disperser was 8.5 weight percent. The disperser was maintained at a temperature of 175-F. Power input to the disperser was approximately 1.39 horsepower-day per ton of fiber (HPD/T). Pre- and post-disperser samples were taken and made into dry 24 gsm. handsheets per the previously defined method. Measurement of the TD Index was carried out as previously described. The results are set forth in Table 1 below. (The ~TD~ is the Throughdryability Index, expressed as kilopascals ~. The "Tensile" is the tensile strength, expressed as grams per inch of sample width. The "Tear" is the Elmendorf tear strength, expressed as grams-force per four sheets. The "Caliper~ is thickness, expressed as inches. The "TEA" is the tensile energy absorbed, expressed as gram-centimeters per square centimeter.) Sample TDTensile Tear Caliper TEA
Pre-disperser 0.111274 18.0 0.0058 8.1 Post-disperser 0.30739 17.2 0.0076 3.8 Example 2.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 175-F., the pre-disperser consistency was 34.7 percent, and the power input to the disperser was 2.12 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as previously described. The pre-disperser fines content was 7.4 weight percent. The results~are set forth in Table 2.
TDTensile Tear Caliper TEA
Pre-disperser 0.121278 18.0 0.0060 6.6 Post-disperser 0.53585 14.0 0.0082 2.5 Example 3.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 150-F., the pre-disperser consistency was 34.6%, and the power input to the disperser 2l~7687 was 2.15 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as previously described. The results are set forth in Table 3.
TD Tensile Tear Caliper TEA
Pre-disperser 0.14 1334 19.2 .0060 7.9 Post-disperser 0.37 884 18.0 .0070 4.9 10Example 4.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 81-F., the pre-disperser consistency was 26.8% and the power input to the disperser was 2.44 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as previously described. The pre-disperser fines content was 7.2 weight percent. The results are set forth in Table 4.
TD Tensile Tear Caliper TEA
Pre-disperser 0.10 1409 19.6 .0055 8.3 Post-disperser 0.17 1125 20.0 .0062 6.7 Example 5.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 79-F., the pre-disperser consistency was 34.6% and the power input to the disperser was 1.18 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as prev;ously described. The pre-disperser fines content was 6.9 weight percent. The results are set forth in Table 5.
TD Tensile Tear CaliDer TEA
Pre-disperser 0.10 1322 - .0055 5.7 35Post-disperser 0.14 1189 22.4 .0060 6.7 21~7687 Example 6.
The same secondary fiber material was treated as described in Example 1, except the disperser temperature was 78-F., the pre-disperser consistency was 37.1% and the power input to the disperser was 2.95 HPD/T. Pre- and post-disperser samples were taken as before and formed into handsheets as previously described. The pre-disperser fines content was 7.8 percent. The results are set forth in Table 6.
TD Tensile Tear CaliDer TEA
Pre-disperser 0.10 1435 20.0 .0055 8.1 Post-disperser 0.19 1155 21.6 .0064 6.1 ExamDle 7.
Well-washed secondary fiber at approximately 50% consistency was fed in crumb form to a Bivis twin screw shaft disperser (Clextral Company, Firminy Cedex, France) via a screw feeder as illustrated in Figures 7-10. The fines content of the washed fiber was 5.2 weight percent. Steam was introduced into the interior compartment to raise the pulp temperature to approximately 220-F. (105-C.J. The product from the first Bivis disperser was sent to a second Bivis disperser operated under the same conditions. From the second disperser, the pulp was sent to a quench tank at 10-C. The pulp was then gravity dewatered and made into 24 gsm handsheets as previously described and the TD Index was determined as previously described. The results are set forth in Table 7.
TD Tensile Tear Caliper TEA
Pre-Bivis 0.08 1072 18.5 .0061 5.65 Post-Bivis 0.71 388 10.5 .0079 1.28 The results from the foregoing examples illustrate that the Throughdryability Index of secondary fibers can be dramatically increased (and hence the throughdrying behavior of the fibers can be improved) by subjecting the fibers to appropriate working forces at high consistency and high temperature in a shaft disperser. Also, the application of high consistency working forces improves the tissue making character of the fibers by decreasing the tensile and tearing strengths while increasing bulk.
ExamPle 8 Cenibra eucalyptus fibers were pulped for 15 minutes at 10%
consistency and dewatered to 30% consistency. A softening agent (Berocell 584) was added to the pulp in the amount of 10 lb. Berocell per ton dry fiber, and the pulp was then fed to a Maule shaft disperser as illustrated in Figure 5. The disperser was operated at 160-F with a power input of 2.2 HPD/T.
The resulting dispersed eucalyptus fibers were made into a two-layered tissue having a softwood fiber layer and a eucalyptus fiber layer. Prior to formation, the northern kraft softwood fibers (LongLac-l9) were pulped for 60 minutes at 4% consistency, while the dispersed eucalyptus fibers were pulped for 2 minutes at 4%
consistency. Each layer was independently formed on separate forming fabrics at 0.05% consistency at a speed of about 50 feet per minute and the resulting two webs were couched together at approximately 10%
consistency to form a two-layered web. The resulting layered web was transferred to a papermaking felt and thereafter pressed onto the surface of a Yankee dryer, where the web was dried and creped at a 1.3 crepe ratio. The dryer side of the layered web was composed entirely of the softwood fibers and had a basis weight of 7.25 lb./2880 ftZ (dryer basis weight). The air side of the layered web was composed entirely of the dispersed eucalyptus fibers of equal basis weight. After creping, the tissue was wound into bath rolls under minimum draw.
The resulting tissue had the following properties: tensile strength = 858 grams per 3 inches width (machine direction) and 488 grams per 3 inches width (cross-machine direction); stretch = 30.4%
(machine direction) and 5.8% (cross-machine direction); Panel Softness = 7.70. (Panel Softness is determined by a trained sensory panel which rates tissues for softness on a scale of from 0 to about 9.5.) For comparison, a typical softness value for throughdried material at similar strength is 7.15.
21~75~7 ExamPle 9 Southern hardwood kraft fibers (Coosa River-59) were pulped for 15 minutes at 10% consistency and dewatered to 28% consistency. A
debonder (Berocell 584) was added to the pulp in the amount of 10 lb.
Berocell per ton dry fiber. The pulp was then fed to a Maule shaft disperser. The disperser was operated at 160-F with a power input of 2.2 HPD/T.
The resulting dispersed hardwood fibers were made into a two-layered tissue having a softwood layer and a hardwood layer.
Specifically, northern softwood kraft fibers (LongLac-l9) were pulped for 60 minutes at 4% consistency, while the dispersed hardwood fibers were pulped for 2 minutes at 4% consistency. Each layer was independently formed on separate forming fabrics at 0.05% consistency and the resulting webs were couched together at about 50 feet per minute at approximately 10% consistency to form a single layered web.
The resulting layered web was transferred to a papermaking felt and thereafter pressed onto the surface of a Yankee dryer, where the web was dried and creped at a 1.3 crepe ratio. The dryer side of the layered web was composed entirely of softwood fibers and had a basis weight of 7.25 lb./2880 ft2 (dryer basis weight). The air side of the web was composed entirely of the dispersed hardwood fibers of equal basis weight. After creping, the tissue was wound into bath tissue rolls under minimum draw.
The resulting tissue had the following properties: tensile strength = 689 grams per 3 inches width (machine direction) and 466 grams per 3 inches width (cross-machine direction); stretch = 32%
(machine direction) and 5.6% (cross-machine direction); Panel Softness = 7.65. For comparison, a typical softness value for throughdried material at similar strength is 7.30.
Examples 8 and 9 both illustrate the softness advantages of treating virgin hardwood fibers with a disperser in accordance with the method of this invention for making wet-pressed tissues.
Example 10 A secondary fiber blend (45 percent laser ledger, 45 percent laser computer print-out, 10 percent white ledger) was pulped for 15 minutes at 40- C and 15 percent consistency. The resultant slurry 21476~7 was screened at ambient temperature and 3.0 percent consistency. The slurry was then dehydrated to 30 percent consistency using a belt press and screw fed directly to a shaft disperser (J. M. Voith GmbH, Heidenheim, Germany) similar to that illustrated in Figure 5. The disperser was maintained at a temperature of 176- F. Power input to the disperser was approximately 4.17 HPD/T. Pre- and post-disperser samples were taken and made into 24 gsm handsheets per the previously defined method. As the improvement in TD Index occurs under all drying conditions, the TD Index of this sample was measured under different flow conditions than the previous examples. Specifically, the air flow rate was 1.0 kg./m2 sec., the air temperature was 90 C, and the initial moisture ratio was 3.5. Since each of these factors affects the TD Index, the TD Index values in this example are not directly relatable to those of the previous examples. Still, the 15 improvement in the TD Index is readily apparent. The results are set forth in Table 8 below.
Table 8 Sample TD Fines Pre-disperser 0.07 22.0 Post-disperser 0.18 23.3 Example 11 The same secondary fiber blend was treated as described in Example 10, except the disperser was maintained at a temperature of 166- F and the power input to the disperser was approximately 5.28 HPD/T. Pre- and post-disperser samples were taken and made into 24 gsm handsheets as previously described. Measurement of the TD
Index was carried out as for Example 10. The results are set forth in Table 9 below.
Table 9 SamDle TD Fines Pre-disperser 0.07 22.0 Post-disperser 0.18 20.6 21~7fi87 Example 11 The same secondary fiber blend was treated as described in Example 10, except the disperser was maintained at a temperature of 147 F and the power input to the disperser was approximately 5.55 HPD/T. Pre- and post-disperser samples were taken and made into 24 gsm handsheets as previously described. Measurement of the TD
Index was carried out as for Example 10. The results are set forth in Table 10 below:
Table 10 Sample TD Fines Pre-disperser 0.07 22.0 Post-disperser 0.17 20.6 As illustrated by Examples 10, 11 and 12, the method of this invention greatly improves the TD Index even at very high fines levels.
It will be appreciated that the foregoing examples, given for purposes of illustration, are not to be construed as limiting the scope of this invention, which is defined by the following claims and all equivalents thereto.
Claims (56)
1. A method for making tissue comprising (a) forming an aqueous suspension of papermaking fibers comprising at least 25 weight percent secondary fibers and having a consistency of about 20 or greater; (b) passing the aqueous suspension through a shaft disperser at a temperature of 150°F. or greater with a power input of about 1 horsepower-day per ton of dry fiber or greater, wherein the TD Index of the fibers is increased about 25 percent or greater; (c) feeding the fibers through a tissue making headbox to form a wet web; and (d) drying the web to form a dried tissue.
2. The method of Claim 1 wherein the TD Index is increased about 50 percent or greater.
3. The method of Claim 1 wherein the TD Index is increased about 75 percent or greater.
4. The method of Claim 1 wherein the temperature is about 210°F. or greater.
5. The method of Claim 1 wherein the temperature is about 220°F. or greater.
6. The method of Claim 1 wherein the temperature is from about 170°F. to about 220°F.
7. The method of Claim 1 wherein the amount of secondary fibers is about 50 weight percent or greater.
8. The method of Claim 1 wherein the amount of secondary fibers is about 75 weight percent or greater.
9. The method of Claim 1 wherein the shaft disperser has a volume-to-working surface area ratio of about 1 centimeter or greater.
10. The method of Claim 1 wherein the shaft disperser has a volume-to-working surface area ratio of about 3 centimeters or greater.
11. The method of Claim 1 wherein the shaft disperser has a volume-to-working surface area ratio of from about 5 to about 10 centimeters.
12. The method of Claim 1 wherein the consistency is from about 20 to about 60 weight percent.
13. The method of Claim 1 wherein the consistency is from about 30 to about 50 weight percent.
14. The method of Claim 1 wherein a softening agent is added to the papermaking fibers prior to passing the fibers through the shaft disperser.
15. The method of Claim 1 wherein a softening agent is added to the papermaking fibers while the fibers are passing through the shaft disperser.
16. The method of Claim 1 wherein a softening agent is added to the fibers after the fibers have passed through the shaft disperser.
17. The method of Claim 1 wherein the wet web is throughdried.
18. A method for making tissue comprising: (a) forming an aqueous suspension of papermaking fibers having a consistency of about 20 percent or greater, said fibers containing about 7 weight percent fines or greater; (b) passing the aqueous suspension through a shaft disperser at a temperature of 150°F. or greater with a power input of at least about 1 horsepower-day per ton of dry fiber, wherein the TD Index of the fibers is increased about 25 percent or greater; (c) feeding the fibers through a tissue making headbox to form a wet web; and (d) drying the web to form a dried tissue.
19. The method of Claim 18 wherein the TD Index is increased about 50 percent or greater.
20. The method of Claim 18 wherein the TD Index is increased about 75 percent or greater.
21. The method of Claim 18 wherein the temperature is about 210°F.
or greater.
or greater.
22. The method of Claim 18 wherein the temperature is about 220°F.
or greater.
or greater.
23. The method of Claim 18 wherein the temperature is from about 170°F. to about 220°F.
24. The method of Claim 18 wherein the shaft disperser has a volume-to-working surface area ratio of about 1 centimeter or greater.
25. The method of Claim 18 wherein the shaft disperser has a volume-to-working surface area ratio of about 3 centimeters or greater.
26. The method of Claim 18 wherein the shaft disperser has a volume-to-working surface area ratio of from about 5 to about 10 centimeters.
27. The method of Claim 18 wherein the amount of fines is about 10 weight percent or greater.
28. The method of Claim 18 wherein the amount of fines is from about 10 to about 25 weight percent.
29. The method of Claim 18 wherein a softening agent is added to the fibers prior to passing the fibers through the shaft disperser.
30. The method of Claim 18 wherein a softening agent is added to the fibers while the fibers are passing through the shaft disperser.
31. The method of Claim 18 wherein a softening agent is added to the fibers after the fibers have passed through the shaft disperser.
32. A method of making tissue comprising (a) forming an aqueous suspension of papermaking fibers comprising at least about 20 weight percent short fibers; (b) passing the aqueous suspension through a shaft disperser at a temperature of 150°F. or greater with a power input of about 1 horsepower-day per ton of dry fiber or greater, wherein the TD Index of the fibers is increased about 25 percent or greater; (c) feeding the fibers through a tissue making headbox to form a wet web; and (d) drying the web to form a dried tissue.
33. The method of Claim 32 wherein the TD Index is increased about 50 percent or greater.
34. The method of Claim 32 wherein the TD Index is increased about 75 percent or greater.
35. The method of Claim 32 wherein the temperature is about 210°F.
or greater.
or greater.
36. The method of Claim 32 wherein the temperature is from about 170°F. to about 220°F.
37. The method of Claim 32 wherein the amount of short fibers is about 50 percent or greater.
38. The method of Claim 32 wherein the amount of short fibers is about 75 percent or greater.
39. The method of Claim 32 wherein the short fibers are virgin hardwood fibers.
40. The method of Claim 32 wherein the shaft disperser has a volume-to-working surface area ratio of about 1 centimeter or greater.
41. The method of Claim 32 wherein the shaft disperser has a volume-to-working surface area ratio of about 3 centimeters or greater.
42. The method of Claim 32 wherein the shaft disperser has a volume-to-working surface area ratio of from about 5 to about 10 centimeters.
43. A tissue made by the method of Claims 1, 18 or 32.
44. A tissue sheet made from a furnish comprising at least about 25 dry weight percent dispersed secondary fibers, said furnish having a TD Index of about 0.15 or greater.
45. The tissue sheet of Claim 44 wherein the furnish has a TD Index of about 0.2 or greater.
46. The tissue sheet of Claim 44 wherein the furnish has a TD Index of about 0.3 or greater.
47. The tissue sheet of Claim 44 wherein the furnish has a TD Index of about 0.5 or greater.
48. The tissue sheet of Claim 44 wherein the furnish has a TD Index of from about 0.2 to about 0.5.
49. The tissue sheet of Claim 44 made from a furnish having at least about 50 dry weight percent secondary fibers.
50. The tissue sheet of Claim 44 made from a furnish having at least about 75 dry weight percent secondary fibers.
51. A tissue sheet made from a furnish comprising at least about 20 weight percent dispersed hardwood fibers, said furnish having a TD Index of about 0.15 or greater.
52. The tissue sheet of Claim 51 wherein the furnish has a TD Index of about 0.2 or greater.
53. The tissue sheet of Claim 51 wherein the furnish has a TD Index of about 0.3 or greater.
54. The tissue sheet of Claim 51 wherein the furnish has a TD Index of about 0.5 or greater.
55. The tissue sheet of Claim 51 wherein the furnish has a TD Index of from about 0.2 to about 0.5.
56. The tissue sheet of Claim 51 wherein the amount of hardwood fibers is about 50 weight percent or greater.